Thesis (M.S.)--University of Michigan, 1987.

Thesis (M.S.)--University of Michigan, 1990.

Thesis (M.S.)--University of Michigan, 1987.

Thesis (Ph.D.)--York University, 2009. Graduate Programme in Earth and Space Science. / Typescript. Includes bibliographical references (leaves 168-181). Also available on the Internet. MODE OF ACCESS via web browser by entering the following URL: http://gateway.proquest.com/openurl?url_ver=Z39.88-2004&res_dat=xri:pqdiss&rft_val_fmt=info:ofi/fmt:kev:mtx:dissertation&rft_dat=xri:pqdiss:NR51751

Thesis (Ph. D.)--University of Iowa, 2000. / Supervisor: Clark M. Stanford. Title-page, preliminaries, Certificate of approval, Table of contents and Project summary issued in paper (xii, 13 leaves ; 28 cm.). Includes bibliographical references. Also issued on CD-ROM (144 files, 33.7 megabytes).

Made available in DSpace on 2014-06-11T19:35:02Z (GMT). No. of bitstreams: 0 Previous issue date: 2001-10-01Bitstream added on 2014-06-13T20:25:47Z : No. of bitstreams: 1 fonseca_rg_dr_arafo.pdf: 347306 bytes, checksum: 7bab875463a1706adf2e01435b649315 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Foram avaliados grau de polimerização de cimentos resinosos em função de diferentes intensidades de luz, por meio de ensaio de dureza, e resistência à remoção por tração de coroas cimentadas em troquéis com determinados cimentos. A primeira etapa foi realizada submetendo-se ou não os cimentos resinosos Panavia F, Scothbond Resin Cement, Enforce e Cement-It à fotoativação, tendo as leituras sido realizadas nos tempos imediato, 1 hora, 2 horas, 24 horas e 7 dias após espatulação dos materiais. No segundo ensaio, foram confeccionados troquéis e coroas, ambos em liga de NiCr, os quais, após jateamento e aplicação do agente catalisador do sistema adesivo Scotchbond Multi Uso Plus (3M) em suas superfícies, foram cimentados aos pares com os materiais descritos anteriormente, além do cimento de fosfato de zinco. A análise dos resultados revelou que os cimentos resinosos alcançaram maior dureza nos grupos fotoativados em todos os tempos analisados, com exceção apenas do Scotchbond Resin Cement e Enforce que, aos 7 dias, mostraram igualdade estatística entre os tratamentos. Todos os materiais apresentaram progressão de polimerização em função do tempo na ausência de luz, com diferentes velocidades. Os cimentos Panavia F e Fosfato de Zinco apresentaram, respectivamente, a maior e a menor força de remoção por tração, tendo o Scotchbond Resin Cement, Enforce e Cement-It ficado em posição intermediária, diferenciando-se significativamente dos demais materiais, porém não entre si. / The purpose of this study was to evaluate plymerization degree of resin cements subjected to various light exposures, by hardness test, and bond strength of crowns luted to dies using five luting agents. Panavia F, Scothbond Resin Cement, Enforce and Cement-It were exposed or not to light and measurements were taken at baseline, 1 hour, 1 hours and 7 days after mixing. For the second evaluation, dies and crowns were obtained with NiCr alloys and after sandblasting and treatment with catalyzer agent of Scotchbond Multi Uso Plus adhesive system (3M) at both surfaces, cementation was done with the luting agents described before, besides zinc phosphate cement. Statistical analysis revealed greater hardness for photopolymerized groups in all times, excepting Scotchbond Resin Cement and Enforce that, at 7 days, showed no statistical difference between treatments. All cements had polymerization progression with time at light absence, with different speeds. Panavia F and zinc phosphate showed, respectively, the greatest and smallest bond strength, while Scotchbond Resin Cement, Enforce and Cement-It were in a intermediate position, differing significantly of the other cements, but not between theirserlves.

Este estudo objetivou avaliar a resistência máxima às forças de compressão entre dois grupos diferentes de coroas em porcelanas livres de metal cimentadas sobre dentes naturais e um grupo formado por dentes caninos naturais hígidos e comparar os resultados obtidos com os de (Chaves, 2001), em seu trabalho de Doutorado onde também se avaliou a resistência máxima às forças de compressão entre coroa metalo cerâmica fraturada e reparada com resina composta com coroa metalo cerâmica integra e dente natural permanente. No presente estudo foram feitos vinte preparos para coroa total em dentes naturais caninos e divididos em dois grupos para confecção de dez coroas do sistema cerâmico aluminizado infiltrado por vidro (Angelus Brasil) e dez coroas em porcelana feldspática Noritake ® (Noritake Kisai CO. Cada grupo de coroas foi cimentado com cimento resinoso auto adesivo RelyX Unicem ® , (3M ESPE, Brasil) com o objetivo de aumentar a resistência da porcelana frente às forças de compressão. O teste de compressão foi realizado em uma máquina de ensaio universal KRATOS, através de uma carga aplicada axialmente no ápice da borda incisal de cada espécime até a fratura. Os dados foram submetidos à análise de Variância ANOVA (p < 0,05) e teste de Tukey para comparação entre grupos. Os resultados mostraram que não houve diferença estatisticamente significante entre a coroa de porcelana aluminizada infiltrada por vidro e o dente natural. A coroa de porcelana feldspática apresentou-se menos resistente com relação ao dente natural e coroa de porcelana aluminizada infiltrada por vidro. / The objective of this study is evaluate the maximum load resistance between two different groups of porcelain metal free crown seated on natural teeth and a group of natural canine and to compare the results gotten with the ones of (Chaves, 2001), in its work of Doutorado where also the ultimate strength to the forces of compression between metalo ceramic broken and repaired with composite resin with ceramic crown metaloceramic integrates and permanent natural tooth. In the present study twenty natural canine teeth were prepared for crown canines and divided in two groups: aluminized porcelain crown infiltrated for glass (Angelus Brazil) and feldspathic Noritake Kisai Noritake (co). Crowns were seated using self adhesive resin cement RelyX Unicem (3M ESPE, Brazil) Compression testing was performed by a universal testing machine (KRATOS) by a load applied axially in incisal of each specimen until occurs the fracture. The data were analyzed by one way analyses of variance (ANOVA) and Tukey test for comparison between groups. The results showed that it did not have statistical significant difference between aluminized porcelain crown infiltrated by glass and natural tooth. The feldspathic porcelain crown presented less resistant than natural tooth and aluminized porcelain crown infiltrated by glass. .

A incompatibilidade entre o módulo de elasticidade (E) do endentador e dos materiais cerâmicos durante os testes de fadiga tem gerado controvérsias. Foram testadas as hipóteses que coroas totalmente cerâmicas apresentarão confiabilidade à fadiga acelerada progressiva do tipo step-stress (hipótese 1) e modos de falha (hipótese 2) similares, quando dois endentadores, um à base de carboneto de tungstênio (WC, E = 600 GPa) e outro de cerâmica esteatite [SB, E = 90 GPa] forem utilizados para transferir a carga. Para avaliar o efeito dos endentadores, um preparo para coroa total em um molar inferior foi realizado. A partir deste modelo mestre, 42 coroas à base de Y-TZP e 42 réplicas em resina composta foram produzidas. As réplicas em resina foram envelhecidas por 30 dias. Todas as coroas foram cimentadas sobre estas réplicas com cimento autoadesivo (Rely X Unicem - 3M/ESPE, St. Paul, EUA) e divididas em dois grupos de acordo com o endentador (WC ou SB). As coroas foram submetidas tanto ao teste de resistência à fratura (n = 3 por grupo), empregado para determinar os perfis de carga (leve, moderado e agressivo) quanto à fadiga (n = 18 por grupo), utilizando um endentador novo para cada coroa. Impressões de todas as coroas e endentadores submetidos ao perfil leve foram obtidas, em pontos específicos do perfil (0, 40k, e, 80k 120k, 160k), vazadas com resina epóxi e avaliadas sob MEV, com a finalidade de inspecionar a morfologia e medir a área endentada. O Use level Probability mostrou sobreposição entre os intervalos de confiança, indicando que não houve diferença significante entre os grupos, independente do critério de falha. O módulo de Weibull Beta (&#x3B2;) calculado para IA (análise inicial) foi de 1,99 e 1,67 para SB e WC, respectivamente, apontando que a fadiga acelerou o fracasso em ambos os grupos. Este não foi o caso para os valores de &#x3B2; para a análise de FA (análise final) (SB = 1,1 e WC = 0,72), revelando que a carga pode ter influenciado sozinha o mecanismo de falha. Ambos os endentadores produziram padrões semelhantes de desgaste/danos nas coroas. A análise fractográfica revelou modos de falhas concorrentes, mas as trincas tipo cone parciais foram as mais dominantes em ambos os grupos. As medições das áreas endentadas mostraram diferença estatística entre os grupos (SB vs. WC) (p <0,05). No geral, o endentador WC exibiu área maior do que a produzida pelo SB. O endentador mais compatível (SB) com a superfície cerâmica produziu confiabilidade e modos de falhas semelhantes ao ser comparada com o WC; assim, as hipóteses 1 e 2 foram aceitas. / Concerns about elastic modulus (E) mismatch between indenter and ceramic materials during fatigue testing have generated controversy. We hypothesized that all-ceramic crowns will exhibit similar step-stress sliding contact fatigue reliability (hypothesis 1) and failure characteristics (hypothesis 2) when using high stiffness tungsten carbide (WC, E = 600 GPa) vs enamel like steatite (SB, E = 90 GPa) indenters. To evaluate the effect of indenters, a preparation for a full crown was made on a first lower molar. From this master die 42 Y-TZPveneered all-ceramic crowns and 42 tooth-resin réplicas were made. Crowns were cemented onto the aged (30 days) tooth-resin réplicas with self-adhesive resin-based cement (Rely X UniCem - 3M/ESPE, St. Paul, USA). After, crowns were divided into two groups according to indenter (WC or SB). Specimens were subject to single-load to fracture (n = 3 per indenter type) to determine the step-stress profiles (mild, moderate, and aggressive) and to mouthmotion step-stress fatigue-tested (n = 18 per indenter type). Two failure modes were determined (inital analysis [IA] and final analysis [FA]). For each crown, a new indenter was used and labelled accordingly for surface damage evaluation. Impressions from all crowns subjected to mild profile were taken following a pre-arranged number of cycles (0, 40k, 80k, 120k e, 160k), poured with epoxy resin and SEM evaluated to inspect the morphology and to measure the indented area. The use level probability plots of the fatigue data showed overlap between the 2-sided 90% confidence bounds. The calculated Weibull Beta (&#x3B2;) for IA was 1.99 and 1.67 for SB and WC, respectively, pointing out that fatigue accelerated the failure in both groups. This was not the case for the &#x3B2; values for the FA analysis (SB = 1.1 and WC = 0.72), revealing tha the load alone dicted the failure mechanism. Both indenters produced similar pattern of wear on crown surfaces. Fractographic landmarks showed competing failure modes, but partial cone cracks were the most dominant for both groups. The indented area measurements showed statistical difference between groups (SB vs WC) (p < .05). Overall, the WC indenter displayed the largest area than SB, except when 120k was taken into account. The more compliant SB indenter led to similar reliability and failure modes to WC (hypotheses 1 and 2 accepted).

Orientador: Wilkens Aurelio Buarque e Silva / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-24T18:40:10Z (GMT). No. of bitstreams: 1 Lameira_DeborahPacheco_D.pdf: 11244410 bytes, checksum: 54506eb4da406d4e27116632cc014de5 (MD5) Previous issue date: 2014 / Resumo: O objetivo deste estudo foi avaliar a resistência à fratura de coroas monolíticas e bicamada a base de zircônia, após envelhecimento artificial. Para este estudo, foram utilizados 32 incisivos bovinos onde foram feitos preparos de coroa total. Estes foram escaneados para a confecção de coroas a base de a zircônia tetragonal parcialmente estabilizada por ítrio (yttrium partially stabilized tetragonal zirconia polycrystalline Y-TZP), por um sistema CAD/CAM (computer-aided design and computer-aided manufacturing). As coroas foram fabricadas de acordo com os grupos experimentais (n=10/grupo): Coroa monolítica de zircônia polida PM (1.5mm de espessura); Coroa monolítica de zircônia com aplicação de glaze GM (1.5mm de espessura); Coroa bicamada com coping de zircônia BL (0.8mm de espessura) com cerâmica de cobertura (0.7mm de espessura). As coroas foram cimentadas nos respectivos preparos com cimento resinoso (RelyX Unicem-2, 3M-ESPE). Após a cimentação, as amostras foram submetidas ao envelhecimento artificial em uma simuladora de mastigação (2,5 milhões de ciclos/3Hz de frequência/8kg) em saliva artificial a 37°C, em seguida foi efetuado o teste de resistência à fratura em maquina Instron, com velocidade de 0,5 mm/min. Duas coroas remanescentes referente a PM e GM foram submetidas a análise estrutural Electron probe microanalysis (EPMA), para medir o nível de ítrio após o envelhecimento. Os resultados foram submetidos a Análise de Variância e teste de Tukey (p=0.05). O modo de fratura foi avaliado por meio de Microscopia Eletrônica de Varredura (MEV). As coroas de zircônia monolíticas apresentaram resultados semelhantes de resistência à fratura (PM = 3476,2N ± 791,7; GM = 3561,5N ± 991,6), que foram maiores (p=0,02) do que os resultados para as coroas bicamada (BL = 2060,4N ± 810,6). Não houve diferença significativa na quantidade de ítrio entre as superfícies oclusais desgastas (PM, GM), e na superfície não desgastada de PM. Destes modo, a resistência à fratura de coroas monolíticas foi maior do que de coroas na configuração bicamada / Abstract: The purpose of this study was to evaluate the fracture strength and failure mode of zirconia crowns in monolithic or bi-layer configuration after artificial aging. Thirty-two bovine incisors received crown preparation and were scanned for the manufacturing of Y-TZP crowns using CAD/CAM technique. Crowns were fabricated according to the following groups (n=10/group): PM polished monolithic zirconia crowns of 1.5mm uniform thickness; GM glazed monolithic zirconia crowns of 1.5mm uniform thickness; BL bi-layer crowns with 0.8mm zirconia core and 0.7mm of veneered porcelain. All crowns were cemented on each respective tooth with resin cement (RelyX Unicem-2, 3M-ESPE). After the cementation, specimens were submitted to artificial aging in a chewing simulator (2.5 million cycles/ 3Hz frequency/8kg) in artificial saliva at 37°C, then the samples were submitted to fracture strength test (Instron) at a crosshead speed of 0.5mm/min. Two remaining crowns referring to PM and GM were submitted to Electron probe microanalysis (EPMA), to measure the yttrium levels after aging. One-way ANOVA and Tukey¿s test (p=0.05) were employed for analysis of the results. The fracture mode was evaluated with Scanning Electron Microscope (SEM). Monolithic zirconia crowns presented similar fracture strength results (PM= 3476.2N ± 791.7; GM= 3561.5N ± 991.6), which were higher (p=0.02) than the results for the bi-layer crowns (BL= 2060.4N ± 810.6). There was no significant difference in the yttrium content among worn occlusal surfaces (PM, GM) and undamaged surface in PM. Thus, the fracture strength of monolithic zirconia crowns was higher than bi-layer configuration / Doutorado / Protese Dental / Doutora em Clínica Odontológica

Orientador: Rafael Leonardo Xediek Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-24T03:25:43Z (GMT). No. of bitstreams: 1 Carvalho_BrenoCarnevalliFrancode_D.pdf: 2254429 bytes, checksum: 0864903c9e5a5e409b843fd792284ecc (MD5) Previous issue date: 2013 / Resumo: Implantes curtos são utilizados em situações clínicas quando a altura e/ou a espessura óssea são insuficientes. A proposta neste estudo foi verificar por meio da análise de tensão fotoelástica a influência exercida pela altura e largura da coroa protética na força transmitida aos implantes curto (7 mm) e longo (13 mm) quando o carregamento foi efetuado no centro ou na extremidade das coroas. As dimensões da altura e da largura da coroa simulada foram estabelecidas com base nas dimensões de dentes pré-molar e molar inferiores humanos e a espessura estabelecida em 6 mm. O corpo-de-prova de resina fotoelástica foi feito com o sistema bi componente à base de resina epóxi modificada e endurecedor. Os carregamentos foram de 0,4 kgf no centro e de 0,3 kgf numa das extremidade da coroa. A análise fotoelástica avaliando as ordens de franjas ao redor dos implantes foi feita com polariscópio de transmissão. Cada fotografia foi analisada três vezes no programa Fringes para ordens de franja de 0 a 4, considerando as médias da ordem das franjas e da tensão cisalhante para cada ponto estabelecido no modelo. Os dados foram submetidos à ANOVA dois fatores e diferenças estatísticas comparadas pelo teste t de Student em nível de significância de 5%. Os resultados mostraram que não houve diferença entre os níveis de tensões gerados pela altura e largura das coroas protéticas sobre os implantes curto e longo, quando os carregamentos foram feitos tanto no centro como na extremidade das coroas. Concluiu-se que as tensões geradas sobre os implantes curto e longo foram similares qualquer que fosse o tamanho e o local dos carregamentos aplicados sobre as coroas; houve diferença na magnitude da tensão exercida sobre os implantes curto e longo, sendo maior para o implante curto / Abstract: Short implants are used in clinical situations when the mass of bone is deficient in height and/or thickness. The purpose of this study was to verify the height and width crown influence in the stress transmission in short (7mm) and long (13mm) implants when loaded at center and edge of the crown. The simulated crown dimensions were established using a natural premolar and molar crown dimensions and the thickness was 6 mm. The photoelastic models were made using a dual system based on modified epoxi resin and catalyser. The crowns were loaded with 0,4 kgf at the center and 0,3 kgf at the edge. The photoelastic analysis for fringe order around the implants was made using a transmission polariscope. The maximum shear stress and the fringe values from 0 to 4 were determined in each photography measured three times using Fringes software. Two-way ANOVA and t Student test at 5% significance were perfomed. The results showed no difference in the stress levels produced by different height and width crown over the short and long implants when loaded both center and edge of the crowns. In conclusion, the results showed similar stress on the short and long implants regardless the size and the loaded crown area; however, there was statistical difference in the stress level on the implants being higher for the short implant / Doutorado / Protese Dental / Doutor em Clínica Odontológica