Avalia??o de aditivos qu?micos alternativos para aplica??o em cimenta??es de po?os de petr?leo HPHTDantas, Tancredo 04 October 2016 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-12-04T21:21:09Z
No. of bitstreams: 1
TancredoDantas_DISSERT.pdf: 2256850 bytes, checksum: 1e1c2e473307cb7d65b98c24ec08c412 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-12-09T00:15:43Z (GMT) No. of bitstreams: 1
TancredoDantas_DISSERT.pdf: 2256850 bytes, checksum: 1e1c2e473307cb7d65b98c24ec08c412 (MD5) / Made available in DSpace on 2017-12-09T00:15:43Z (GMT). No. of bitstreams: 1
TancredoDantas_DISSERT.pdf: 2256850 bytes, checksum: 1e1c2e473307cb7d65b98c24ec08c412 (MD5)
Previous issue date: 2016-10-04 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / A ind?stria da constru??o civil emprega uma grande diversidade de aditivos desenvolvidos
para uso em concretos e argamassas e que apresentam excelente desempenho na modifica??o
do comportamento do cimento Portland. Algumas dessas propriedades encontram fun??es
an?logas ou similares na engenharia de po?os de petr?leo, como por exemplo, os
antiespumantes, dispersantes ou redutores de fric??o, controladores de filtrado e retardadores
de pega. Este estudo foi desenvolvido com o objetivo de avaliar e especificar produtos
qu?micos alternativos para compor sistemas de aditivos adequados ? formula??o de pastas de
cimento para aplica??o em po?os de petr?leo onshore caracterizados por temperaturas a partir
de 180?F (82?C), po?os depletados e po?os sujeito ? inje??o de vapor. Durante o per?odo de
execu??o do estudo, foram selecionados produtos qu?micos de acordo com sua fun??o. Estes
produtos foram especificados segundo normas internas da Petrobras e os testes foram
realizados de acordo com a norma API RP 10B. Alguns dos aditivos apresentaram grande
potencial para aplica??o em pastas de cimento para temperaturas elevadas, incluindo
antiespumantes, controladores de filtrado, dispersantes e retardadores de pega. / The civil construction industry employs a wide diversity of admixtures developed to
use in concrete and mortars, but that exhibits excellent performance for oilwell slurries. Some
properties meet analogous functions, for example, antifoam, dispersants or friction reducers,
fluid loss control agent and set retarders. This study was developed with the objective to
evaluate and specify alternative chemical products to be used as admixtures for the
formulation of cement slurries for application in onshore oil wells, characterized by
temperatures of 180?F (82?C), mature wells and wells subjected to steam injection. During
the study, chemical products were selected according its functions. These additives were
specified according to PETROBRAS internal standards and the tests were realized according
to API RP 10B standards. Some additives presented great potential for application in cement
slurries for high temperatures, including antifoams, fluid loss control agents, dispersants and
setting retarders.
|
2 |
Adi??o de superplastificante e anti-segregante ? base de CMC em pastas de cimento para Po?os de Petr?leoJacinto, T?lio W?gner Batista 29 February 2008 (has links)
Made available in DSpace on 2014-12-17T14:06:44Z (GMT). No. of bitstreams: 1
TulioWBJ.pdf: 572575 bytes, checksum: 5effde52c942d11015aa333c7bd07b5f (MD5)
Previous issue date: 2008-02-29 / Oil well cementing materials consist of slurries of Special class Portland cement dispersed in water. Admixtures can be used to provide the necessary fluidity, so the material can be efficiently pumped down as well as penetrate porous rocks with controlled filter loss. Construction admixtures can be used to modify the properties of oil well cements provided they can withstand and hold their properties at the higher than ambient temperatures usually encountered in oil fields. In civil construction, superplasticizer play the role of dispersants that reduce the facto r of water cement improve mechanical properties and fluidity of the cement, whereas anti-segregation agents improve the workability of the slurry. In the present study, oil well cement slurries were produced adding both a dispersant and an anti-segregation agent conventionally used in Portland CPII-Z-32 RS cement aiming at materials for primary cementing and squeeze operations. Three basic aspects were evaluated: fluidity, filter loss and the synergetic effect of the admixtures at two temperatures, i.e., 27?C and 56?C, following API RP 10B practical recommendations. The slurries were prepared using admixture concentrations varying from 2.60 Kgf/m3 (0.02 gallft3) to 5.82 Kgf/m3 (0.045 galJft3) BWOC. The density of the slurries was set to 1.89 g/cm3
(15.8 Ib/gal). 0.30 to 0.60% BWOC of a CMC-based anti-segregation agent was
added to the cement to control the filter loss. The results showed that the addition of anti-segregation at concentrations above 0.55% by weight of cement resulted in the increased viscosity of the folders in temperatures evaluated. The increasing the temperature of the tests led to a reduction in the performance of anti-segregation. At concentrations of 5.20 kgf/m3 (0,040 gallft3) and 5.82 Kgf/m3 (0,045 gal/ft 3) observed a better performance of the properties evaluated in the proposed system. At low temperature was observed instability in the readings of rheology for all concentrations of anti-segregation. Contents that increasing the concentration of anti?-segregation is limited concentrations greater than 0.55 % BWOC of the CMC in temperature analyzed. The use of the system with CMC promoted a good performance against the properties evaluated. The principal function of anti?-segregation was optimized with increasing concentration of superplasticizer, at temperatures above the 2rC. The study of the behaviour of systemic additives, resulting in slurries of cement, which can be optimized face studies of other intrinsic properties in oil fields / A pasta de cimento Portland ? uma mistura de part?culas s?lidas de cimento dispersas em ?gua. Tal sistema deve possuir fluidez suficiente para penetrar de forma eficiente em meio poroso, al?m de proporcionar controle na ?gua perdida por filtrado na forma??o, garantindo o sucesso da opera??o de bombeio. Em determinados campos as condi??es geol?gicas das forma??es, bem como a profundidade das faces explorat?rias do po?o podem favorecer ao acr?scimo de temperatura. Na constru??o civil os superplastificantes reduzem o fator ?gua cimento das argamassas proporcionando aumento de propriedades como resist?ncia mec?nica e fluidez, j? o anti-segregante proporciona uma melhor trabalhabilidade das argamassas. Sistemas com a adi??o de dispersantes e anti?segregante utilizados convencionalmente em cimento Portland CPII-Z-32 RS foram analisados em pastas de cimento Portland Especial, utilizadas para opera??es de squeeze e cimenta??o em po?os petrol?feros, com ?nfase em tr?s aspectos: fluidez, perda do volume de filtrado e efeito sinerg?tico. Os par?metros analisados foram estudados por meio de ensaios de desempenho nas temperaturas de 2rC e 56?C, seguindo as recomenda??es pr?ticas da norma API RP 108. Para o estudo foram selecionados materiais com car?ter dispersante como superplastificantes. e preparadas pastas com concentra??es variando de 2,60 Kgf/m3 (0,02 gal/p?3) a 5,82 Kgf/m3 (0,045 gal/p?3) em peso de cimento, com densidade constante de 1,89 g/cm3 (15,8 Ib/gal). Para o controle da ?gua perdida por filtra??o foi utilizado um agente anti-segregante a base de CMC com concentra??es variando de 0,30 % a 0,60 % em peso de cimento. Os resultados mostraram que a adi??o do anti-segregante em concentra??es acima de 0,55 % em peso de cimento resultou no aumento da viscosidade das pastas nas temperaturas avaliadas. Foi verificado que o aumento da temperatura dos testes provocou uma redu??o no desempenho do anti-segregante. Nas concentra??es de 5,20 kgf/m3 (0,040 gal/p?3) e 5,82 Kgf/m3 (0,045 gal/p?3) observou-se um melhor desempenho das propriedades avaliadas no sistema proposto. Na temperatura ambiente foi verificado instabilidade nas leituras de reologia para todas as concentra??es do anti-segregante. Foi verificado que o aumento da concentra??o de anti-segregante ? limitada as concentra??es superior a 0,55 % em peso de cimento nas temperaturas analisadas. O uso do sistema contendo superplastificante, aliado ao anti-segregante promoveu um bom desempenho face ?s propriedades reol?gicas e de controle de filtrado das pastas. A fun??o principal do anti-segregante foi otimizada com o aumento da concentra??o do superplastificante, a temperaturas acima da ambiente. Por?m o aumento da concentra??o do agente dispersante nas pastas de cimento pode provocar o retardamento das pastas em temperaturas pr?ximas da ambiente. O estudo do comportamento sist?mico dos aditivos resultou na obten??o de pastas de cimento, que podem ser otimizadas face estudos de outras propriedades intr?nsecas a sua utiliza??o nas opera??es em campos petrol?feros
|