La demanda de la vivienda en el Perú ha ido en aumento considerablemente en los últimos años. El auge que experimenta actualmente la construcción debido a la estabilidad económica del país, hace que las familias de toda condición tengan la posibilidad y condiciones de adquirir la vivienda propia.

Made available in DSpace on 2014-06-12T17:40:33Z (GMT). No. of bitstreams: 2 arquivo6222_1.pdf: 2048858 bytes, checksum: dff2a3e3553d7a5ebf4027040397c020 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2006 / O concreto auto-adensável (CAA) pode ser definido como um concreto especial caracterizado principalmente pela sua capacidade de se mover no interior das fôrmas, preenchendo todos os espaços existentes entre as armaduras, o que é conseguido exclusivamente pela ação de seu peso próprio. Esta capacidade de preenchimento, ou deformabilidade, do CAA é governada pela fluidez e coesão da mistura. Quando a coesão é insuficiente pode haver separação entre a pasta de cimento e os agregados durante as etapas de transporte e espalhamento do concreto, o que caracteriza a ocorrência de segregação. A dosagem do concreto dessa dissertação foi baseada no método proposto por Gomes (2002). Segundo este método, a dosagem é dividida em etapas distintas. Na primeira otimizase a pasta, buscando uma dosagem ideal de superplastificante e uma relação adequada entre as adições e o cimento, partindo-se de uma relação água/cimento pré-estabelecida. Outra etapa distinta é a otimização do esqueleto granular, onde se encontra uma relação ideal entre a areia e os agregados graúdos, buscando a redução do índice de vazios. Uma última etapa consiste em produzir concretos com diferentes volumes de pasta. O concreto com mínimo volume de pasta que atingir os requisitos de auto-adensabilidade e alta resistência à compressão será selecionado como ideal. Esta pesquisa tem por objetivo dosar concretos auto-adensáveis (CAA), utilizando como adições o metacaulim e rejeitos como fíler para melhorar a coesão da mistura e reduzir o impacto ambiental. E também fornecer maiores informações sobre o CAA, como por exemplo: as metodologias de dosagem existentes na literatura e como os materiais constituintes do CAA podem influenciá- loObservou-se que com o uso do metacaulim e do pó de pedra disponíveis na região do Recife é possível dosar concretos auto-adensáveis utilizando a metodologia de dosagem proposta por Gomes (2002). Os resultados das dosagens satisfizeram todas as propriedades de auto-compactabilidade alcançando valores de resistência aos 7 dias de 49,3 MPa aos 28 dias de 58,3 MPa

Made available in DSpace on 2014-06-12T17:41:49Z (GMT). No. of bitstreams: 2 arquivo6555_1.pdf: 2048858 bytes, checksum: dff2a3e3553d7a5ebf4027040397c020 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2006 / O concreto auto-adensável (CAA) pode ser definido como um concreto especial caracterizado principalmente pela sua capacidade de se mover no interior das fôrmas, preenchendo todos os espaços existentes entre as armaduras, o que é conseguido exclusivamente pela ação de seu peso próprio. Esta capacidade de preenchimento, ou deformabilidade, do CAA é governada pela fluidez e coesão da mistura. Quando a coesão é insuficiente pode haver separação entre a pasta de cimento e os agregados durante as etapas de transporte e espalhamento do concreto, o que caracteriza a ocorrência de segregação. A dosagem do concreto dessa dissertação foi baseada no método proposto por Gomes (2002). Segundo este método, a dosagem é dividida em etapas distintas. Na primeira otimizase a pasta, buscando uma dosagem ideal de superplastificante e uma relação adequada entre as adições e o cimento, partindo-se de uma relação água/cimento pré-estabelecida. Outra etapa distinta é a otimização do esqueleto granular, onde se encontra uma relação ideal entre a areia e os agregados graúdos, buscando a redução do índice de vazios. Uma última etapa consiste em produzir concretos com diferentes volumes de pasta. O concreto com mínimo volume de pasta que atingir os requisitos de auto-adensabilidade e alta resistência à compressão será selecionado como ideal. Esta pesquisa tem por objetivo dosar concretos auto-adensáveis (CAA), utilizando como adições o metacaulim e rejeitos como fíler para melhorar a coesão da mistura e reduzir o impacto ambiental. E também fornecer maiores informações sobre o CAA, como por exemplo: as metodologias de dosagem existentes na literatura e como os materiais constituintes do CAA podem influenciá- lo.Observou-se que com o uso do metacaulim e do pó de pedra disponíveis na região do Recife é possível dosar concretos auto-adensáveis utilizando a metodologia de dosagem proposta por Gomes (2002). Os resultados das dosagens satisfizeram todas as propriedades de auto-compactabilidade alcançando valores de resistência aos 7 dias de 49,3 MPa aos 28 dias de 58,3 MPa

Un aditivo superplastificante se caracteriza por su superior capacidad reductora de agua, también por qué en su síntesis pueden modificarse secuencias que permiten modular propiedades como el mantenimiento de consistencia (persistencia del efecto dispersante), la evolución de resistencia inicial y, lo más importante, adaptar la compatibilidad del aditivo a cada cemento en particular. Rheobuild 1000 es un aditivo que, gracias a su composición química, permite reducir el agua de amasado de concreto decididamente más marcada en comparación con el resto de superplastificantes de la línea Rheobuild y así aumentar en gran medida la especialmente el desarrollo de la resistencia mecánica y retención del asentamiento del concreto. / Tesis

La presente tesis realizó el estudio de la dosificación del concreto utilizando agregados de la cantera Figueroa en Huánuco con aditivo superplastificante Sika Viscocrete 3330 tercera generación. El objetivo principal fue el de determinar la dosificación del concreto de mediana resistencia para optimizar la calidad del concreto, y así tener un concreto en condiciones óptimas y resistencias a la compresión considerables. Para lo cual se basó en investigaciones pasadas referidas a concretos utilizando superplastificante, también se utilizó como fuente una investigación parecida perteneciente a la misma región del presente estudio. Todo ello aporto a dar opciones de solución en concretos de mediana resistencia utilizando aditivos superplastificantes, ya que el problema para esta región es la poca información en cuanto al uso de aditivos en concretos de mediana resistencia. El tipo de investigación es un análisis mixto, el nivel de investigación es descriptivo correlacional, porque especifica propiedades y características del concreto de mediana resistencia, asocia variables mediante un patrón para una determinada población. Concluida la investigación se obtuvieron resultados favorables del concreto de mediana resistencia, ya que el diseño patrón de menor relación agua/cemento presento una mejor resistencia a la compresión obteniendo un incremento del 21.13% de resistencia a la compresión, los demás diseños también tuvieron un incremento significativo de resistencia a la compresión los cuales se mencionaran en las conclusiones de esta investigación. This thesis conducted the study using dosage of concrete aggregates quarry in Huanuco Figueroa with Sika ViscoCrete superplasticizer additive 3330 third generation. The main objective was to determine the dosage of the particular medium strength to optimize the quality of the concrete, and thus have a particular under optimal conditions and considerable resistance to compression. For which it relies on past investigations into concrete using superplasticizer, also used a similar research as a source belonging to the same region of the study. I bring all this to give possible solutions in medium strength concrete using superplasticizers, because the problem in this region is the lack of information on the use of additives in concrete of medium strength. The research is a joint analysis, the level of research is descriptive correlational, for specific properties and characteristics of the particular medium strength, variables associated with a pattern for a given population. The investigation favorable results of the specific medium strength, since the design pattern of lower water / cement ratio is obtained I present a better compressive strength obtaining an increase of 21.13% of compressive strength, other designs also had an increase significant compressive strength which were mentioned in the conclusions of this investigation.

Made available in DSpace on 2015-05-14T12:09:06Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 2185418 bytes, checksum: 8edee78b6cc4067e1c81e1ad8e74a457 (MD5) Previous issue date: 2010-09-30 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Self-compacting concrete (SCC), considered one of the greatest advances in concrete technology, is characterized by its special capacity of filling ability, passing ability and resistance to segregation by the action of its own weight without the presence of other external forces. Taking into consideration the numerous cities and their industries that have caused a considerable increase in the production of solid waste, including industrial waste in SCC has brought about significant environmental benefits. This study aimed to develop a SCC with inclusion of waste from the manufacturing of kaolin, specifically from what is called birra and borra . The most common producers of SCC used limestone filler. In the production of SCC the mix-design method Tutikian (2007) and Gomes (2002) were used as a base, the Marsh funnel and miniature slump tests for paste composition and the compactability test of materials for the fabrication of granulometric skeletons. In order to evaluate the properties of SCC in fresh state tests, the slump flow test, slump flow test T50cm, V-funnel, V-funnel 5min, L-box, U-box and J-ring were used. The possibility of using waste from the kaolin beneficiation in a SCC was proven, where the borra was used as fine material and birra as a replacement for aggregates. In the hardened state, testing of compressive strength were carried out on the 7th and 28th days, resulting in resistance rate of approximately 20 to 40MPa. / O concreto auto-adensável (CAA), considerado como um dos maiores avanços na tecnologia do concreto, é caracterizado por suas capacidades especiais de preenchimento, habilidade de passagem e resistência à segregação pela ação do seu próprio peso sem que existam outras forças externas. Diante do panorama em que as cidades e suas indústrias têm provocado um considerável aumento na produção dos resíduos sólidos, incluir resíduos industriais ao CAA traz benefícios ambientais significativos. Assim, este trabalho teve por objetivo desenvolver um CAA com inserção de resíduos provenientes da fabricação de caulim, mais especificamente a birra e a borra. No CAA de referência foi utilizado o fíler calcário. Na confecção do CAA foram utilizados como base os métodos de dosagem Tutikian (2007) e Gomes (2002), sendo realizados os testes do Funil de Marsh e mini-cone para composição da pasta e os testes de compacidade dos materiais para confecção dos esqueletos granulométricos. Para avaliar as propriedades do CAA no estado fresco foram executados os testes do espalhamento, espalhamento T50cm, funil-V, funil V 5min, caixa-L, caixa-U e anel-J. Foi constatada a possibilidade de utilizar resíduos provenientes do beneficiamento de caulim em um CAA, a borra como material fino e a birra em substituição de parte dos agregados. No estado endurecido, foram executados testes de resistência à compressão aos 7 e 28 dias, obtendo resistências na faixa aproximada de 20 MPa a 40 MPa.

Made available in DSpace on 2014-12-17T14:06:44Z (GMT). No. of bitstreams: 1 TulioWBJ.pdf: 572575 bytes, checksum: 5effde52c942d11015aa333c7bd07b5f (MD5) Previous issue date: 2008-02-29 / Oil well cementing materials consist of slurries of Special class Portland cement dispersed in water. Admixtures can be used to provide the necessary fluidity, so the material can be efficiently pumped down as well as penetrate porous rocks with controlled filter loss. Construction admixtures can be used to modify the properties of oil well cements provided they can withstand and hold their properties at the higher than ambient temperatures usually encountered in oil fields. In civil construction, superplasticizer play the role of dispersants that reduce the facto r of water cement improve mechanical properties and fluidity of the cement, whereas anti-segregation agents improve the workability of the slurry. In the present study, oil well cement slurries were produced adding both a dispersant and an anti-segregation agent conventionally used in Portland CPII-Z-32 RS cement aiming at materials for primary cementing and squeeze operations. Three basic aspects were evaluated: fluidity, filter loss and the synergetic effect of the admixtures at two temperatures, i.e., 27?C and 56?C, following API RP 10B practical recommendations. The slurries were prepared using admixture concentrations varying from 2.60 Kgf/m3 (0.02 gallft3) to 5.82 Kgf/m3 (0.045 galJft3) BWOC. The density of the slurries was set to 1.89 g/cm3 (15.8 Ib/gal). 0.30 to 0.60% BWOC of a CMC-based anti-segregation agent was added to the cement to control the filter loss. The results showed that the addition of anti-segregation at concentrations above 0.55% by weight of cement resulted in the increased viscosity of the folders in temperatures evaluated. The increasing the temperature of the tests led to a reduction in the performance of anti-segregation. At concentrations of 5.20 kgf/m3 (0,040 gallft3) and 5.82 Kgf/m3 (0,045 gal/ft 3) observed a better performance of the properties evaluated in the proposed system. At low temperature was observed instability in the readings of rheology for all concentrations of anti-segregation. Contents that increasing the concentration of anti?-segregation is limited concentrations greater than 0.55 % BWOC of the CMC in temperature analyzed. The use of the system with CMC promoted a good performance against the properties evaluated. The principal function of anti?-segregation was optimized with increasing concentration of superplasticizer, at temperatures above the 2rC. The study of the behaviour of systemic additives, resulting in slurries of cement, which can be optimized face studies of other intrinsic properties in oil fields / A pasta de cimento Portland ? uma mistura de part?culas s?lidas de cimento dispersas em ?gua. Tal sistema deve possuir fluidez suficiente para penetrar de forma eficiente em meio poroso, al?m de proporcionar controle na ?gua perdida por filtrado na forma??o, garantindo o sucesso da opera??o de bombeio. Em determinados campos as condi??es geol?gicas das forma??es, bem como a profundidade das faces explorat?rias do po?o podem favorecer ao acr?scimo de temperatura. Na constru??o civil os superplastificantes reduzem o fator ?gua cimento das argamassas proporcionando aumento de propriedades como resist?ncia mec?nica e fluidez, j? o anti-segregante proporciona uma melhor trabalhabilidade das argamassas. Sistemas com a adi??o de dispersantes e anti?segregante utilizados convencionalmente em cimento Portland CPII-Z-32 RS foram analisados em pastas de cimento Portland Especial, utilizadas para opera??es de squeeze e cimenta??o em po?os petrol?feros, com ?nfase em tr?s aspectos: fluidez, perda do volume de filtrado e efeito sinerg?tico. Os par?metros analisados foram estudados por meio de ensaios de desempenho nas temperaturas de 2rC e 56?C, seguindo as recomenda??es pr?ticas da norma API RP 108. Para o estudo foram selecionados materiais com car?ter dispersante como superplastificantes. e preparadas pastas com concentra??es variando de 2,60 Kgf/m3 (0,02 gal/p?3) a 5,82 Kgf/m3 (0,045 gal/p?3) em peso de cimento, com densidade constante de 1,89 g/cm3 (15,8 Ib/gal). Para o controle da ?gua perdida por filtra??o foi utilizado um agente anti-segregante a base de CMC com concentra??es variando de 0,30 % a 0,60 % em peso de cimento. Os resultados mostraram que a adi??o do anti-segregante em concentra??es acima de 0,55 % em peso de cimento resultou no aumento da viscosidade das pastas nas temperaturas avaliadas. Foi verificado que o aumento da temperatura dos testes provocou uma redu??o no desempenho do anti-segregante. Nas concentra??es de 5,20 kgf/m3 (0,040 gal/p?3) e 5,82 Kgf/m3 (0,045 gal/p?3) observou-se um melhor desempenho das propriedades avaliadas no sistema proposto. Na temperatura ambiente foi verificado instabilidade nas leituras de reologia para todas as concentra??es do anti-segregante. Foi verificado que o aumento da concentra??o de anti-segregante ? limitada as concentra??es superior a 0,55 % em peso de cimento nas temperaturas analisadas. O uso do sistema contendo superplastificante, aliado ao anti-segregante promoveu um bom desempenho face ?s propriedades reol?gicas e de controle de filtrado das pastas. A fun??o principal do anti-segregante foi otimizada com o aumento da concentra??o do superplastificante, a temperaturas acima da ambiente. Por?m o aumento da concentra??o do agente dispersante nas pastas de cimento pode provocar o retardamento das pastas em temperaturas pr?ximas da ambiente. O estudo do comportamento sist?mico dos aditivos resultou na obten??o de pastas de cimento, que podem ser otimizadas face estudos de outras propriedades intr?nsecas a sua utiliza??o nas opera??es em campos petrol?feros