RF-sputtered CoCr films have been characterized for a variety of deposition conditions, and the most effective parameters which bring about perpendicular anisotropy have been evaluated. In particular bias sputtering has been noted for its role in improving the crystallographic orientation and magnetic properties when applied to the substrate at certain values, hence the root mechanism of the observed improvement has been, as far as possible , investigated . These investigations have, in particular, focused on the extent to which impurity gases are likely to effect the magnetic properties of sputtered films, as well as quantifying the gas contents of the films using as yet unexploited (in this area) method of thermal desorption experiments. In a further attempt to quantify tolerable level of impurity species in the sputtering environment , impurity gases of nitrogen, oxygen and hydrogen, which are commonly present even in high vacuum systems, were intentionally introduced in the sputtering chamber and their effects on both magnetic and crystallographic properties of CoCr were noted . To measure the perpendicular and in-plane magnetic properties of CoCr , a combined polar-transverse Kerr magneto- optic system was costructed , through which direct magnetic measurement of CoCr/NiFe becomes feasible . This method was further exploited to compare volume and surface magnetic properties of CoCr , as measured using a V.S.M and this M-O system. Finally , a CoCr/NiFe W1nchester disc was fabricated on which a recording experiment was successfully performed.

Estudou-se a caracterização de blocos sinterizados à base de Co-Cr-Mo visando a obtenção de próteses odontológicas por fresagem CAD/CAM. O processo de sinterização foi estudado e ocorreu através do transporte difusional de massa e calor no estado sólido, denominado sinterização no estado sólido. Esse fenômeno produz uma forte união entre as partículas devido ao transporte de massa, em escala atômica, sob condições controladas de tempo, temperatura e atmosfera. Foram realizadas sinterizações interrompidas a 800, 1000, 1200 e 1300°C nos tempos de 15 minutos, 1 hora e 4 horas. A liga foi caracterizada nas condições recebida e sinterizadas em termos de composição química, propriedades mecânicas e caracterização microestrutural. Para isto, utilizou-se fluorescência de raios X, dilatometria, ensaios de Arquimedes, ensaios de dureza, ensaios de compressão, microscopia eletrônica de varredura (MEV), microscopia óptica e microanálise eletrônica dispersiva (EDS). Os resultados composicionais indicam que a liga se encontrava dentro da faixa de composição química estabelecida pelo manual do fabricante e pela norma ASTM 1537. As partículas analisadas na condição pré-sinterizada exibiram formato esférico, indicando uma provável utilização de pós atomizados. A estimativa do levantamento da distribuição do tamanho das partículas foi realizado utilizando o programa de computador ImageJ, e a distribuição foi caracterizada como assimétrica positiva. O material no estado recebido se apresentou monofásico. A fase presente encontrada foi ?Co com estrutura cristalina CFC. Em contrapartida, as amostras sinterizadas apresentaram porções de fase ?Co, com estrutura cristalina hexagonal, fase esta formada a partir da transformação ?Co <-> ?Co, na qual, a energia armazenada na forma de defeitos é a força motriz da transformação. E sugere que a transformação ocorreu durante resfriamento. A amostra sinterizada por quatro horas em 1200°C apresentou-se no estágio final de sinterização, dado que os poros encontrados tinham aspecto arredondado e com densificação maior que 90%. Os resultados de compressão indicam tensão média de ruptura de 2523 ± 168 MPa. / This work studied the characterization of Co-Cr-Mo sintered blocks in order to obtain dental prosthesis by prototyping CAD/CAM. The sintering process was studied through diffusional mass transport in solid state, termed solid state sintering. This phenomenon produces a strong bond between the particles due to mass transport, at the atomic scale, under controlled conditions of time, temperature and atmosphere. The interrupted sintering was performed at 800, 1000, 1200 and 1300 ° C in times to 15 minutes, 1 hour and 4 hours. The alloy was characterized in conditions as received and sintered in terms of chemical composition, mechanical properties and microstructural characterization. For this, we used X-ray fluorescence, dilatometry, Archimedes tests, hardness tests, compression tests, scanning electron microscopy (SEM), optical microscopy and dispersive electron microanalysis (EDS). The results indicate that the alloy was within the chemical composition range established by the manufacturer and ASTM 1537. The particles analyzed in the pre-sintered condition showed spherical shape, indicating a likely use of atomized powders. The estimate of the particle size distribution was performed using ImageJ software, and the distribution is characterized as positive asymmetric. The samples in the received state were monophasic. This phase was found ?Co with FCC crystal structure. On the order hand, the sintered samples showed ?Co phase portions with hexagonal crystal structure, phase formed from the transformation ?Co <-> ?Co, in which the energy stored in the form of defects is the driving force of transformation and suggests that transformation occurred during the cooling. Sample sintered during four hours at 1200°C was in the final stages of sintering, since the pores were found aspect rounded and densification above 90%. The compression results indicate rupture stress at 2523 ± 168 MPa.

Estudou-se a caracterização de blocos sinterizados à base de Co-Cr-Mo visando a obtenção de próteses odontológicas por fresagem CAD/CAM. O processo de sinterização foi estudado e ocorreu através do transporte difusional de massa e calor no estado sólido, denominado sinterização no estado sólido. Esse fenômeno produz uma forte união entre as partículas devido ao transporte de massa, em escala atômica, sob condições controladas de tempo, temperatura e atmosfera. Foram realizadas sinterizações interrompidas a 800, 1000, 1200 e 1300°C nos tempos de 15 minutos, 1 hora e 4 horas. A liga foi caracterizada nas condições recebida e sinterizadas em termos de composição química, propriedades mecânicas e caracterização microestrutural. Para isto, utilizou-se fluorescência de raios X, dilatometria, ensaios de Arquimedes, ensaios de dureza, ensaios de compressão, microscopia eletrônica de varredura (MEV), microscopia óptica e microanálise eletrônica dispersiva (EDS). Os resultados composicionais indicam que a liga se encontrava dentro da faixa de composição química estabelecida pelo manual do fabricante e pela norma ASTM 1537. As partículas analisadas na condição pré-sinterizada exibiram formato esférico, indicando uma provável utilização de pós atomizados. A estimativa do levantamento da distribuição do tamanho das partículas foi realizado utilizando o programa de computador ImageJ, e a distribuição foi caracterizada como assimétrica positiva. O material no estado recebido se apresentou monofásico. A fase presente encontrada foi ?Co com estrutura cristalina CFC. Em contrapartida, as amostras sinterizadas apresentaram porções de fase ?Co, com estrutura cristalina hexagonal, fase esta formada a partir da transformação ?Co <-> ?Co, na qual, a energia armazenada na forma de defeitos é a força motriz da transformação. E sugere que a transformação ocorreu durante resfriamento. A amostra sinterizada por quatro horas em 1200°C apresentou-se no estágio final de sinterização, dado que os poros encontrados tinham aspecto arredondado e com densificação maior que 90%. Os resultados de compressão indicam tensão média de ruptura de 2523 ± 168 MPa. / This work studied the characterization of Co-Cr-Mo sintered blocks in order to obtain dental prosthesis by prototyping CAD/CAM. The sintering process was studied through diffusional mass transport in solid state, termed solid state sintering. This phenomenon produces a strong bond between the particles due to mass transport, at the atomic scale, under controlled conditions of time, temperature and atmosphere. The interrupted sintering was performed at 800, 1000, 1200 and 1300 ° C in times to 15 minutes, 1 hour and 4 hours. The alloy was characterized in conditions as received and sintered in terms of chemical composition, mechanical properties and microstructural characterization. For this, we used X-ray fluorescence, dilatometry, Archimedes tests, hardness tests, compression tests, scanning electron microscopy (SEM), optical microscopy and dispersive electron microanalysis (EDS). The results indicate that the alloy was within the chemical composition range established by the manufacturer and ASTM 1537. The particles analyzed in the pre-sintered condition showed spherical shape, indicating a likely use of atomized powders. The estimate of the particle size distribution was performed using ImageJ software, and the distribution is characterized as positive asymmetric. The samples in the received state were monophasic. This phase was found ?Co with FCC crystal structure. On the order hand, the sintered samples showed ?Co phase portions with hexagonal crystal structure, phase formed from the transformation ?Co <-> ?Co, in which the energy stored in the form of defects is the driving force of transformation and suggests that transformation occurred during the cooling. Sample sintered during four hours at 1200°C was in the final stages of sintering, since the pores were found aspect rounded and densification above 90%. The compression results indicate rupture stress at 2523 ± 168 MPa.

Este trabalho tem por objetivo estudar as propriedades mecânicas e a caracterização microestrutural de espécimes da liga de Co-Cr-Mo obtidos por manufatura aditiva fusão seletiva a laser (do inglês Selective Laser Melting SLM) e por fundição de precisão, visando a confecção de próteses odontológicas. A partir de pós de Co-Cr-Mo atomizados a gás foram realizadas as seguintes etapas: 1) investigação das propriedades físicas, químicas e térmicas dos pós atomizados em diferentes faixas granulométricas (denominadas: D1 < 15 &mu;m, D2 de 20-50 &mu;m e D3 > 75 &mu;m); 2) confecção de espécimes, em dimensões padronizadas, por meio das técnicas de consolidação; 3) caracterização dos consolidados por análise de: citotoxicidade, porosidade, difração de raios X e dilatometria; 4) caracterização mecânica de tração, flexão em três pontos, dureza (macro e micro Vickers) e caracterização microestrutural (microscopia óptica e eletrônica de varredura). De modo geral, os resultados obtidos foram: a granulometria D2 (20-50 &mu;m) é a que melhor se enquadra nas análises de empacotamento para a consolidação por meio de SLM; a biocompatibilidade das amostras obteve resultado positivo para ambas técnicas de processamento; a avaliação mecânica dos espécimes evidencia que a técnica de fusão seletiva a laser propicia propriedades mecânicas (tensão de escoamento, tensão de ruptura, tensão máxima, alongamento e dureza) superiores as obtidas pela técnica de fundição de precisão; a microestrutura obtida pelo processo SLM é composta por grãos ultrafinos e de elevada homogeneidade química. Conclui-se que, o desenvolvimento do presente estudo evidenciou que na fabricação de componentes odontológicos customizados (coroas) a técnica SLM apresenta qualidade superior quando comparada a fundição de precisão. / The objective of this work was to study the mechanical properties and microstructural characterization of specimens of the Co-Cr-Mo alloy obtained by additive manufacturing -selective laser melting (SLM) and precision casting aiming at the manufacture of dental prostheses. The following steps were carried out on Co-Cr-Mo gas-atomized powders: 1) investigation of the physical, chemical and thermal properties of atomized powders in different grain sizes (denominated: D1 <15 &mu;m, D2 20-50 &mu;m and D3 > 75 &mu;m); 2) the consolidation of standard specimens via consolidation techniques; 3) characterization of consolidated by analysis of: cytotoxicity, porosity, X ray diffraction and dilatometry; 4) mechanical characterization of tensile, 3 point bending, hardness (macro and micro Vickers) tests and microstructural characterization (optical and scanning electron microscopy). In general, the results observed were: the grain size D2 (20-50 &mu;m) is the one that best fits in the analysis of packaging, for the consolidation by SLM; the biocompatibility of the samples obtained a positive result for both processing techniques; the mechanical evaluation of the specimens shows that the SLM technique provides superior mechanical properties (yield stress, rupture stress, maximum stress, elongation and hardness), compared to those obtained by the precision casting technique; the microstructure obtained by the SLM process results in an ultrafine grains with high chemical homogeneity, differentiated by the gross dendritic microstructure in the casting process. In this way, the development of the present study evidenced superior quality in manufacturing customized dental components (copings) by SLM technique compared to precision casting.

Este trabalho tem por objetivo estudar as propriedades mecânicas e a caracterização microestrutural de espécimes da liga de Co-Cr-Mo obtidos por manufatura aditiva fusão seletiva a laser (do inglês Selective Laser Melting SLM) e por fundição de precisão, visando a confecção de próteses odontológicas. A partir de pós de Co-Cr-Mo atomizados a gás foram realizadas as seguintes etapas: 1) investigação das propriedades físicas, químicas e térmicas dos pós atomizados em diferentes faixas granulométricas (denominadas: D1 < 15 &mu;m, D2 de 20-50 &mu;m e D3 > 75 &mu;m); 2) confecção de espécimes, em dimensões padronizadas, por meio das técnicas de consolidação; 3) caracterização dos consolidados por análise de: citotoxicidade, porosidade, difração de raios X e dilatometria; 4) caracterização mecânica de tração, flexão em três pontos, dureza (macro e micro Vickers) e caracterização microestrutural (microscopia óptica e eletrônica de varredura). De modo geral, os resultados obtidos foram: a granulometria D2 (20-50 &mu;m) é a que melhor se enquadra nas análises de empacotamento para a consolidação por meio de SLM; a biocompatibilidade das amostras obteve resultado positivo para ambas técnicas de processamento; a avaliação mecânica dos espécimes evidencia que a técnica de fusão seletiva a laser propicia propriedades mecânicas (tensão de escoamento, tensão de ruptura, tensão máxima, alongamento e dureza) superiores as obtidas pela técnica de fundição de precisão; a microestrutura obtida pelo processo SLM é composta por grãos ultrafinos e de elevada homogeneidade química. Conclui-se que, o desenvolvimento do presente estudo evidenciou que na fabricação de componentes odontológicos customizados (coroas) a técnica SLM apresenta qualidade superior quando comparada a fundição de precisão. / The objective of this work was to study the mechanical properties and microstructural characterization of specimens of the Co-Cr-Mo alloy obtained by additive manufacturing -selective laser melting (SLM) and precision casting aiming at the manufacture of dental prostheses. The following steps were carried out on Co-Cr-Mo gas-atomized powders: 1) investigation of the physical, chemical and thermal properties of atomized powders in different grain sizes (denominated: D1 <15 &mu;m, D2 20-50 &mu;m and D3 > 75 &mu;m); 2) the consolidation of standard specimens via consolidation techniques; 3) characterization of consolidated by analysis of: cytotoxicity, porosity, X ray diffraction and dilatometry; 4) mechanical characterization of tensile, 3 point bending, hardness (macro and micro Vickers) tests and microstructural characterization (optical and scanning electron microscopy). In general, the results observed were: the grain size D2 (20-50 &mu;m) is the one that best fits in the analysis of packaging, for the consolidation by SLM; the biocompatibility of the samples obtained a positive result for both processing techniques; the mechanical evaluation of the specimens shows that the SLM technique provides superior mechanical properties (yield stress, rupture stress, maximum stress, elongation and hardness), compared to those obtained by the precision casting technique; the microstructure obtained by the SLM process results in an ultrafine grains with high chemical homogeneity, differentiated by the gross dendritic microstructure in the casting process. In this way, the development of the present study evidenced superior quality in manufacturing customized dental components (copings) by SLM technique compared to precision casting.

The functional performance of joint implants is largely determined by the surface layer properties in contact. Wear/debris-induced osteolysis and aseptic loosening has been identified as the major cause of failure of metal-on-metal joint implants. A crucial requirement for the long-term stability of the artificial joint is to minimize the release of debris particles. Severe plastic deformation (SPD) processes have been used to modify the surface integrity properties by generating ultrafine, or even nano-sized grains and grain size gradients in the surface region of many materials. These fine grained materials often exhibit enhanced surface integrity properties and improved functional performance (wear resistance, corrosion resistance, fatigue life, etc.) compared with their conventional coarse grained counterparts. The aim of the present work is to investigate the effect of a SPD process, cryogenic burnishing, on the surface integrity modifications of a Co-Cr-Mo alloy, and the resulting wear performance of this alloy due to the burnishing-induced surface integrity properties. A systematic experimental study was conducted to investigate the influence of different burnishing parameters on distribution of grain size, phase structure and residual stresses of the processed material. The wear performance of the processed Co-Cr-Mo alloy was tested via pin-on-disk wear tests. The results from this work show that the cryogenic burnishing can significant improve the surface integrity of the Co-Cr-Mo alloy which would finally lead to advanced wear performance due to refined microstructure, high hardness, compressive residual stresses and favorable phase structure on the surface layer. A finite element model (FEM) was developed for predicting the grain size changes during burnishing of Co-Cr-Mo alloy under both dry and cryogenic conditions. A new material model was used for incorporating flow stress softening and associated grain size refinement caused by the dynamic recrystallization (DRX). The new material model was implemented in a commercial FEM software as a customized user subroutine. Good agreement between predictions and experimental observations was achieved. Encouraging trends are revealed with great potential for application in industry.

La aleación biomédica CoCrMo se emplea en la elaboración de prótesis de sustituciones articulares totales o parciales de cadera y rodilla debido a su biocompatibilidad y a sus buenas propiedades mecánicas entre las que destacan su elevada resistencia a la corrosión y al desgaste. La superficie del biomaterial CoCrMo reacciona de manera espontánea con el medio que la rodea formando una capa pasiva de óxidos metálicos que auto-protege a la aleación del medio y condiciona su comportamiento frente a la corrosión. Hay que tener en cuenta que el medio en el que trabajan estas prótesis es uno de los más agresivos que se conocen lo que agrava el proceso de corrosión. Dicho proceso contribuye a la liberación de iones metálicos dentro del cuerpo humano acelerando el deterioro de dichas prótesis y problemas clínicos en los pacientes. En este contexto, la presente Tesis Doctoral pretende estudiar los mecanismos de biocorrosión que determinan la degradación de la aleación CoCrMo en condiciones fisiológicas. Para ello, en primer lugar se ha realizado la caracterización electroquímica del biomaterial en diferentes condiciones físico-químicas de relevancia biológica (composición química del fluido simulado, pH, contenido en oxígeno y potencial aplicado) las cuales influyen notablemente en las reacciones electroquímicas que tienen lugar en la interfase biometerial/medio. Posteriormente, se ha estudiado cómo influye la adsorción de albúmina (proteína modelo y mayoritaria en el cuerpo humano) en el comportamiento electroquímico de la aleación en función de la concentración de proteína y la temperatura del medio. Este estudio se ha llevado a cabo desde el punto de vista termodinámico y se ha demostrado que el proceso de adsorción de la proteína sobre la superficie de la aleación CoCrMo ocurre de manera espontánea por quimisorción modelándose correctamente mediante la Isoterma de Langmuir. Finalmente, se han estudiado las cinéticas de pasivación y de adsorción de proteína mediante la p / Valero Vidal, C. (2012). Study of the degradation mechanisms of the CoCrMo biomedical alloy in physiological media by electrochemical techniques and surface analysis [Tesis doctoral no publicada]. Universitat Politècnica de València. https://doi.org/10.4995/Thesis/10251/16881 / Palancia

The thermodynamic properties of the Co-Cr-Mo ternary system have been described. Available experimental data on the system have been assessed and applied to optimize the parameters used in the thermodynamic models within the Calphad method. Meanwhile, samples were made by the powder metallurgical process and heat treated (sintered) at 1573 K to investigate the phase diagram data related to the intermetallic phases, such as σ, μ and R phases present in the system. With the optimized thermodynamic description, we are able to fit most of the experimental data in the literature and from this work. However, the one phase field of R is too narrow in the present description. Furthermore, at 1573 K the extension of the phase boundary of σ toward the Co corner needs to be improved. In addition, the calculated phase diagram at 1573 K shows a fcc-bcc-σ three-phase equilibrium near the Co-Cr binary side. This is not shown in the experimentally determined ternary phase diagram but is necessary in order to match the recent data on the Co-Cr binary system.

Duas técnicas invasivas para o tratamento da doença aterosclerótica coronariana oclusiva firmaram-se ao longo dos anos: revascularização cirúrgica do miocárdio e angioplastia transcutânea com stents metálicos. O estudo visa comparar as alterações histopatológicas causadas por stents metálicos coronarianos fabricados com a superliga de composição química em porcentagem em peso cromo 20%, tungstênio 15%, níquel 10% e cobalto restante, designada ASTM F.90, revestidos, ou não, com carbeto de silício pelo processo de asperção térmica originando uma superfície hidrofílica. Stents com espessura das hastes entre 80 a 90 nm, área das células entre 1,4 a 2,1 mm² e relação metal-artéria de 13 a 19%, em pacientes reestenosantes que sofreram posteriormente revascularização cirúrgica do miocárdio, com aqueles não submetidos à angioplastia prévia. Foram determinados dois grupos: grupo I ou grupo controle, pacientes que sofreram revascularização cirúrgica do miocárdio sem angioplastia prévia de qualquer natureza; grupo II pacientes submetidos à revascularização cirúrgica do miocárdio, após reestenose intra-stent coronariana. Pacientes de ambos os grupos foram avaliados rotineiramente quanto à indicação e risco cirúrgico e durante o procedimento convencional da revascularização cirúrgica do miocárdio utilizando circulação extracorpórea, antes de realizar a anastomose do enxerto vascular na coronária, amostras contendo pequenos fragmentos de endotélio foram retiradas juntamente com fragmentos dos stents, enviadas para análise histopatológica e produção de laminas coradas com H-E. Observou-se a presença de arterite crônica caracterizada por infiltrado mononuclear em conjunto com fenômeno de proliferação fibroblástica e de musculatura lisa naqueles pacientes que apresentavam reestenose intra-stent, sendo mais intenso no local do stent. A visualização das superfícies dos stents em escala nanometrica (MFA) é de suma importância para análise estrutural das próteses, avaliando irregularidades nas superfícies recobertas das hastes dos stents. A persistência de arterite crônica coronariana avaliada por infiltrado linfomononuclear e proliferação de fibrocolágeno foi constatada em pacientes reestenosantes. / Two invasive techniques for the treatment of occlusive coronary atherosclerosis disease were signed over the years: coronary artery bypass surgery and transcutaneous angioplasty with bare metal stent. The study attempts to compare the histopathological abnormality caused in patients with implantation of bare metal stent in coronary made with: Chromium 20%, Tungsten 15%, Nickel 10% and Cobalt remainder, ASTM F.90 alloy for surgical implant applications, and covered with a thin layer of amorphous silicon carbide, or not, and its total or partial obstruction, after undergoing coronary artery bypass grafting, with those who had coronary artery bypass surgery with no previous angioplasty. Two groups were studied: group I, or control group, patients who underwent coronary artery bypass grafting without previous angioplasty of any kind; group II of patients undergoing coronary artery bypass surgery after coronary-stent restenosis. Patients in both groups were evaluated for the indication and surgical risk; was done routinely during the procedure of conventional coronary artery bypass grafting with cardiopulmonary bypass. Before performing the anastomosis in coronary vascular graft, a small fragment of the endothelium was removed along whit a fragment of the stent, and sent for analysis with hematoxilin-eosin. The presence of chronic inflammatory coronary reaction was detected, mediated by mononuclear cells with phenomenon of fibroblast and smooth muscle proliferation in patients presenting in-stent restenosis. It w coronary reaction as also observed that the inflammatory and proliferative process is more intense at the site of stent implantation. The analysis of surface of the stents used atomic force microscopy proved to be an important method for the surface analysis for stents, and showed on nanometric scale an irregular coverage of silicon carbide. In conclusion, in the patients with restenosis in-stent occurs persistence of chronic inflammation with mononuclear cells and process of fibroblast proliferation.

Duas técnicas invasivas para o tratamento da doença aterosclerótica coronariana oclusiva firmaram-se ao longo dos anos: revascularização cirúrgica do miocárdio e angioplastia transcutânea com stents metálicos. O estudo visa comparar as alterações histopatológicas causadas por stents metálicos coronarianos fabricados com a superliga de composição química em porcentagem em peso cromo 20%, tungstênio 15%, níquel 10% e cobalto restante, designada ASTM F.90, revestidos, ou não, com carbeto de silício pelo processo de asperção térmica originando uma superfície hidrofílica. Stents com espessura das hastes entre 80 a 90 nm, área das células entre 1,4 a 2,1 mm² e relação metal-artéria de 13 a 19%, em pacientes reestenosantes que sofreram posteriormente revascularização cirúrgica do miocárdio, com aqueles não submetidos à angioplastia prévia. Foram determinados dois grupos: grupo I ou grupo controle, pacientes que sofreram revascularização cirúrgica do miocárdio sem angioplastia prévia de qualquer natureza; grupo II pacientes submetidos à revascularização cirúrgica do miocárdio, após reestenose intra-stent coronariana. Pacientes de ambos os grupos foram avaliados rotineiramente quanto à indicação e risco cirúrgico e durante o procedimento convencional da revascularização cirúrgica do miocárdio utilizando circulação extracorpórea, antes de realizar a anastomose do enxerto vascular na coronária, amostras contendo pequenos fragmentos de endotélio foram retiradas juntamente com fragmentos dos stents, enviadas para análise histopatológica e produção de laminas coradas com H-E. Observou-se a presença de arterite crônica caracterizada por infiltrado mononuclear em conjunto com fenômeno de proliferação fibroblástica e de musculatura lisa naqueles pacientes que apresentavam reestenose intra-stent, sendo mais intenso no local do stent. A visualização das superfícies dos stents em escala nanometrica (MFA) é de suma importância para análise estrutural das próteses, avaliando irregularidades nas superfícies recobertas das hastes dos stents. A persistência de arterite crônica coronariana avaliada por infiltrado linfomononuclear e proliferação de fibrocolágeno foi constatada em pacientes reestenosantes. / Two invasive techniques for the treatment of occlusive coronary atherosclerosis disease were signed over the years: coronary artery bypass surgery and transcutaneous angioplasty with bare metal stent. The study attempts to compare the histopathological abnormality caused in patients with implantation of bare metal stent in coronary made with: Chromium 20%, Tungsten 15%, Nickel 10% and Cobalt remainder, ASTM F.90 alloy for surgical implant applications, and covered with a thin layer of amorphous silicon carbide, or not, and its total or partial obstruction, after undergoing coronary artery bypass grafting, with those who had coronary artery bypass surgery with no previous angioplasty. Two groups were studied: group I, or control group, patients who underwent coronary artery bypass grafting without previous angioplasty of any kind; group II of patients undergoing coronary artery bypass surgery after coronary-stent restenosis. Patients in both groups were evaluated for the indication and surgical risk; was done routinely during the procedure of conventional coronary artery bypass grafting with cardiopulmonary bypass. Before performing the anastomosis in coronary vascular graft, a small fragment of the endothelium was removed along whit a fragment of the stent, and sent for analysis with hematoxilin-eosin. The presence of chronic inflammatory coronary reaction was detected, mediated by mononuclear cells with phenomenon of fibroblast and smooth muscle proliferation in patients presenting in-stent restenosis. It w coronary reaction as also observed that the inflammatory and proliferative process is more intense at the site of stent implantation. The analysis of surface of the stents used atomic force microscopy proved to be an important method for the surface analysis for stents, and showed on nanometric scale an irregular coverage of silicon carbide. In conclusion, in the patients with restenosis in-stent occurs persistence of chronic inflammation with mononuclear cells and process of fibroblast proliferation.