No description available.

Unique physical properties such as small effective mass, high electron drift velocities, high electron mobility and small band gap energy make InN a candidate for applications in high-speed microelectronic and optoelectronic devices. The aim of this research is to understand the surface properties, desorption kinetics and thermal stability of InN epilayers that affect the growth processes and determine film quality as well as device performance and life time. We have investigated the structural properties, the surface desorption kinetics, and the thermal stability using Auger electron spectroscopy (AES), x-ray diffraction (XRD), Raman spectroscopy, atomic force microscopy (AFM), high resolution electron energy loss spectroscopy (HREELS), and temperature programmed desorption (TPD). Investigations on high pressure chemical vapor deposition (HPCVD)-grown InN samples revealed the presence of tilted crystallites, which were attributed to high group V/III flux ratio and lattice mismatch. A study of the thermal stability of HPCVD-grown InN epilayers revealed that the activation energy for nitrogen desorption was 1.6±0.2 eV, independent of the group V/III flux ratio. Initial investigations on the ternary alloy In0.96Ga0.04N showed single-phase, N-polar epilayers using XRD and HREELS, while a thermal desorption study revealed an activation energy for nitrogen desorption of 1.14 ± 0.06 eV. HREELS investigations of atomic layer epitaxy (ALE)-grown InN revealed vibrational modes assigned to N-N vibrations. The atomic hydrogen cleaned InN surface also exhibited modes assigned to surface N-H without showing In-H species, which indicated N-polar InN. Complete desorption of hydrogen from the InN surface was best described by the first-order desorption kinetics with an activation energy of 0.88 ± 0.06 eV and pre-exponential factor of (1.5 ± 0.5) ×105 s-1. Overall, we have used a number of techniques to characterize the structure, surface bonding configuration, thermal stability and hydrogen desorption kinetics of InN and In0.96Ga0.04N epilayers grown by HPCVD and ALE. High group V/III precursors ratio and lattice mismatch have a crucial influence on the film orientation. The effects of hydrogen on the decomposition add to the wide variation in the activation energy of nitrogen desorption. Presence of surface defects lowers the activation energy for hydrogen desorption from the surface.

Esta dissertação teve como objetivo o desenvolvimento da técnica de síntese por combustão em solução para obtenção de nanocristais de espinélio MgAl2O4, e a caracterização desse material por diferentes técnicas. O estudo da obtenção incluiu o cálculo termodinâmico das reações envolvidas e a influência da razão combustível-oxidante no tamanho de cristalito. A síntese de espinélio MgAl2O4 por combustão foi realizada a partir do trio precursor químico sacarose, nitrato de alumínio e nitrato de magnésio em água, para diferentes razões combustível-oxidante, temperaturas de chama e número total de moles gasosos, relacionando esses parâmetros com tamanho de cristalito do pó, deformação de rede e área superficial. As reações químicas de combustão em solução resultaram na formação in situ de fases amorfas de MgAl2O4 para o pó como-sintetizado. A fase cristalina somente foi obtida após um tratamento térmico a 900°C do pó como-sintetizado. O cálculo termodinâmico da reação de combustão em solução mostrou que quando a razão combustível-oxidante aumenta, obtém-se uma elevação da temperatura de chama adiabática e da quantidade de gás produzida, definindo características do particulado como morfologia, tamanho de cristalito, área superficial e nível de agregação. Para a caracterização do pó utilizaram-se técnicas como análise termodiferencial (ATD) e termogravimétrica (ATG), granulometria por dispersão de laser (GDL), BET para análise de área superficial, análise cristalográfica por difração de raios X (DRX), microestrutura por microscopia eletrônica de varredura (MEV) e microscopia eletrônica de transmissão (MET). Os pós de espinélio MgAl2O4 obtidos apresentaram-se como constituídos de cristalitos nanométricos, dispostos na forma de agregados de tamanho micrométrico. O tamanho de cristalito médio, calculado pelo método Single Line, a partir de dados de análises por DRX, foi de 21,57 nm, e deformação média calculada de 1,99 x 10-³ nm. Por análise granulométrica constatou-se um tamanho de aglomerado médio de 27,27 µm, com distribuição trimodal. As análises por MEV e MET confirmaram a agregação das partículas do pó sintetizado, a partir de partículas com morfologia irregular e do tamanho nanométrico dos cristalitos. / The goals of the dissertation were to investigate and develop the solution combustion synthesis technique in order to obtain nanocrystalline spinel MgAl2O4 powders and characterize them by different techniques. This study has also included thermodynamic calculation for reactions, which have been investigated and the influence of fuel-to-oxidant ratio on crystallite size. The combustion synthesis of MgAl2O4 spinel was performed by a trio of chemical precursor sucrose, aluminum nitrate and magnesium nitrate in water, for different fuel-to-oxidant ratios, flame temperatures and total mol number of gases, correlating these parameters with crystallite size, strain, surface area and total porosity. The chemical reactions of solution combustion resulted on amorphous phase formation of MgAl2O4 in situ for as-synthesized powder. The crystalline phase formation of spinel MgAl2O4 was only succeeded obtained after a thermal treatment of as-synthesized powder under 900°C. The thermodynamic calculation of the combustion reaction of the combustion reaction shows that as fuel-to-oxidant ratio increases the amount of gas produced and adiabatic flame temperature also increases. Powder characteristics as morphology, crystallite size, surface area and aggregation degree are mainly governed by the flame temperature and generation of gases. The techniques used for powder characterization included differential thermal analyzer (DTA), thermogravimetric analyzer (TGA), particles size analyzer (PSA), surface area by BET analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The spinel MgAl2O4 powders obtained were composed of nano-size crystallites, but in micrometer-sized aggregates. The mean particle size calculated, via Single Line method, using XRD was 21.57 nm and the mean strain calculated was 1.99 x 10-³ nm. PSA indicated that the synthesized powders contain a mean aggregates size with a tri mode distribution of around 27.27 µm. TEM and SEM analyses confirmed that the as-synthesized powders are composed of particles aggregation. They have an irregular morphology and nano-size crystallites.

Este trabalho teve por objetivo investigar a obtenção de espinélio MgAl2O4 nanoestruturado através da síntese contínua por combustão em solução e sua caracterização por diferentes técnicas. Incluso neste estudo a influência do tipo de combustível e a razão combustível-oxidante no tamanho do cristalito. As partículas de espinélio MgAl2O4 foram sintetizadas utilizando-se os precursores químicos nitrato de alumínio e nitrato de magnésio como fonte dos cátions metálicos. Uréia, glicina e sacarose foram empregadas como agentes redutores, com diferentes valores da razão combustível-oxidante para a sacarose. Estes parâmetros foram relacionados com sua influência no tamanho de cristalito, tamanho de partícula e área superficial. Na caracterização do pó obtido, foram utilizadas técnicas como análise termodiferencial (ATD) e termogravimétrica (ATG), granulometria por difração de laser (GDL), análise de área superficial (BET), análise cristalográfica por difração de raios X (DRX), morfologia por microscopia eletrônica de varredura (MEV). As reações químicas da síntese contínua por combustão em solução resultaram na formação in situ de fases cristalinas para reações estequiométricas de uréia, glicina e sacarose e as deficientes de sacarose. Preponderância de fase amorfa ocorreu nas reações com excesso de sacarose para o pó como-sintetizado. A totalidade de fase cristalina foi obtida após um tratamento térmico a 900°C do pó como-sintetizado. Os pós de espinélio MgAl2O4 obtidos apresentaram-se como constituídos de cristalitos nanométricos, dispostos na forma de agregados de tamanho micrométrico. O tamanho de cristalito médio, calculado pelo método Single Line, a partir de dados de análises por DRX, foi de 13 nm. A área superficial média dos pós calcinados medida pelo método BET foi de 54 g/m2 Por análise granulométrica constatou-se um Tamanho de partícula médio de 17 μm para o pó como-sintetizado e 17,1 μm para o calcinado a 900ºC. As análises por MEV confirmaram a agregação das partículas do pó sintetizado, a partir de partículas preponderantemente esféricas e algumas com morfologia irregular. / This study has investigated a continuous solution combustion synthesis technique to obtain the nanostructured MgAl2O4 spinel powder and their characterize them by different tecniques. This study has also included the investigation of the influence of different kinds of fuel and fuel-to-oxidant ratio on crystallite size. The MgAl2O4 spinel powder was performed using aluminum nitrate and magnesium nitrate to obtain the metallic ions. Urea, glycine and sucrose were used like fuel, with several fuel-to-oxidant ratio. These parameters were correlating with powders characteristics, like crystallite size, particle size and superficial area. The techniques used for powder characterization included differential thermal analyzer (DTA), thermogravimetric analyzer (TGA), particles size analyzer (PSA), surface area by BET analysis, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The chemical reactions of solution combustion resulted on crystalline phase to the reactions with urea, glycine and sucrose (to desabilites on fuel and stoichiometric) and amorphous phase formation of MgAl2O4 in situ for as-synthesized powder. The crystalline phase formation of spinel MgAl2O4 was only succeeded obtained after a thermal treatment of as-synthesized powder under 900°C.The spinel MgAl2O4 powders obtained were composed of nano-size crystallites, but in micrometer-sized aggregates. The mean particle size calculated, via Single Line method, using XRD was 13 nm. PSA indicated that the synthesized powders contain a mean aggregates size with a tri mode distribution of around 17.1 μm. SEM analyses confirmed that the as-synthesized powders are composed of particles aggregation. They have an irregular morphology and nano-size crystallites.

Esta dissertação teve como objetivo o desenvolvimento da técnica de síntese por combustão em solução para obtenção de nanocristais de espinélio MgAl2O4, e a caracterização desse material por diferentes técnicas. O estudo da obtenção incluiu o cálculo termodinâmico das reações envolvidas e a influência da razão combustível-oxidante no tamanho de cristalito. A síntese de espinélio MgAl2O4 por combustão foi realizada a partir do trio precursor químico sacarose, nitrato de alumínio e nitrato de magnésio em água, para diferentes razões combustível-oxidante, temperaturas de chama e número total de moles gasosos, relacionando esses parâmetros com tamanho de cristalito do pó, deformação de rede e área superficial. As reações químicas de combustão em solução resultaram na formação in situ de fases amorfas de MgAl2O4 para o pó como-sintetizado. A fase cristalina somente foi obtida após um tratamento térmico a 900°C do pó como-sintetizado. O cálculo termodinâmico da reação de combustão em solução mostrou que quando a razão combustível-oxidante aumenta, obtém-se uma elevação da temperatura de chama adiabática e da quantidade de gás produzida, definindo características do particulado como morfologia, tamanho de cristalito, área superficial e nível de agregação. Para a caracterização do pó utilizaram-se técnicas como análise termodiferencial (ATD) e termogravimétrica (ATG), granulometria por dispersão de laser (GDL), BET para análise de área superficial, análise cristalográfica por difração de raios X (DRX), microestrutura por microscopia eletrônica de varredura (MEV) e microscopia eletrônica de transmissão (MET). Os pós de espinélio MgAl2O4 obtidos apresentaram-se como constituídos de cristalitos nanométricos, dispostos na forma de agregados de tamanho micrométrico. O tamanho de cristalito médio, calculado pelo método Single Line, a partir de dados de análises por DRX, foi de 21,57 nm, e deformação média calculada de 1,99 x 10-³ nm. Por análise granulométrica constatou-se um tamanho de aglomerado médio de 27,27 µm, com distribuição trimodal. As análises por MEV e MET confirmaram a agregação das partículas do pó sintetizado, a partir de partículas com morfologia irregular e do tamanho nanométrico dos cristalitos. / The goals of the dissertation were to investigate and develop the solution combustion synthesis technique in order to obtain nanocrystalline spinel MgAl2O4 powders and characterize them by different techniques. This study has also included thermodynamic calculation for reactions, which have been investigated and the influence of fuel-to-oxidant ratio on crystallite size. The combustion synthesis of MgAl2O4 spinel was performed by a trio of chemical precursor sucrose, aluminum nitrate and magnesium nitrate in water, for different fuel-to-oxidant ratios, flame temperatures and total mol number of gases, correlating these parameters with crystallite size, strain, surface area and total porosity. The chemical reactions of solution combustion resulted on amorphous phase formation of MgAl2O4 in situ for as-synthesized powder. The crystalline phase formation of spinel MgAl2O4 was only succeeded obtained after a thermal treatment of as-synthesized powder under 900°C. The thermodynamic calculation of the combustion reaction of the combustion reaction shows that as fuel-to-oxidant ratio increases the amount of gas produced and adiabatic flame temperature also increases. Powder characteristics as morphology, crystallite size, surface area and aggregation degree are mainly governed by the flame temperature and generation of gases. The techniques used for powder characterization included differential thermal analyzer (DTA), thermogravimetric analyzer (TGA), particles size analyzer (PSA), surface area by BET analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The spinel MgAl2O4 powders obtained were composed of nano-size crystallites, but in micrometer-sized aggregates. The mean particle size calculated, via Single Line method, using XRD was 21.57 nm and the mean strain calculated was 1.99 x 10-³ nm. PSA indicated that the synthesized powders contain a mean aggregates size with a tri mode distribution of around 27.27 µm. TEM and SEM analyses confirmed that the as-synthesized powders are composed of particles aggregation. They have an irregular morphology and nano-size crystallites.

Este trabalho teve por objetivo investigar a obtenção de espinélio MgAl2O4 nanoestruturado através da síntese contínua por combustão em solução e sua caracterização por diferentes técnicas. Incluso neste estudo a influência do tipo de combustível e a razão combustível-oxidante no tamanho do cristalito. As partículas de espinélio MgAl2O4 foram sintetizadas utilizando-se os precursores químicos nitrato de alumínio e nitrato de magnésio como fonte dos cátions metálicos. Uréia, glicina e sacarose foram empregadas como agentes redutores, com diferentes valores da razão combustível-oxidante para a sacarose. Estes parâmetros foram relacionados com sua influência no tamanho de cristalito, tamanho de partícula e área superficial. Na caracterização do pó obtido, foram utilizadas técnicas como análise termodiferencial (ATD) e termogravimétrica (ATG), granulometria por difração de laser (GDL), análise de área superficial (BET), análise cristalográfica por difração de raios X (DRX), morfologia por microscopia eletrônica de varredura (MEV). As reações químicas da síntese contínua por combustão em solução resultaram na formação in situ de fases cristalinas para reações estequiométricas de uréia, glicina e sacarose e as deficientes de sacarose. Preponderância de fase amorfa ocorreu nas reações com excesso de sacarose para o pó como-sintetizado. A totalidade de fase cristalina foi obtida após um tratamento térmico a 900°C do pó como-sintetizado. Os pós de espinélio MgAl2O4 obtidos apresentaram-se como constituídos de cristalitos nanométricos, dispostos na forma de agregados de tamanho micrométrico. O tamanho de cristalito médio, calculado pelo método Single Line, a partir de dados de análises por DRX, foi de 13 nm. A área superficial média dos pós calcinados medida pelo método BET foi de 54 g/m2 Por análise granulométrica constatou-se um Tamanho de partícula médio de 17 μm para o pó como-sintetizado e 17,1 μm para o calcinado a 900ºC. As análises por MEV confirmaram a agregação das partículas do pó sintetizado, a partir de partículas preponderantemente esféricas e algumas com morfologia irregular. / This study has investigated a continuous solution combustion synthesis technique to obtain the nanostructured MgAl2O4 spinel powder and their characterize them by different tecniques. This study has also included the investigation of the influence of different kinds of fuel and fuel-to-oxidant ratio on crystallite size. The MgAl2O4 spinel powder was performed using aluminum nitrate and magnesium nitrate to obtain the metallic ions. Urea, glycine and sucrose were used like fuel, with several fuel-to-oxidant ratio. These parameters were correlating with powders characteristics, like crystallite size, particle size and superficial area. The techniques used for powder characterization included differential thermal analyzer (DTA), thermogravimetric analyzer (TGA), particles size analyzer (PSA), surface area by BET analysis, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The chemical reactions of solution combustion resulted on crystalline phase to the reactions with urea, glycine and sucrose (to desabilites on fuel and stoichiometric) and amorphous phase formation of MgAl2O4 in situ for as-synthesized powder. The crystalline phase formation of spinel MgAl2O4 was only succeeded obtained after a thermal treatment of as-synthesized powder under 900°C.The spinel MgAl2O4 powders obtained were composed of nano-size crystallites, but in micrometer-sized aggregates. The mean particle size calculated, via Single Line method, using XRD was 13 nm. PSA indicated that the synthesized powders contain a mean aggregates size with a tri mode distribution of around 17.1 μm. SEM analyses confirmed that the as-synthesized powders are composed of particles aggregation. They have an irregular morphology and nano-size crystallites.

Esta dissertação teve como objetivo o desenvolvimento da técnica de síntese por combustão em solução para obtenção de nanocristais de espinélio MgAl2O4, e a caracterização desse material por diferentes técnicas. O estudo da obtenção incluiu o cálculo termodinâmico das reações envolvidas e a influência da razão combustível-oxidante no tamanho de cristalito. A síntese de espinélio MgAl2O4 por combustão foi realizada a partir do trio precursor químico sacarose, nitrato de alumínio e nitrato de magnésio em água, para diferentes razões combustível-oxidante, temperaturas de chama e número total de moles gasosos, relacionando esses parâmetros com tamanho de cristalito do pó, deformação de rede e área superficial. As reações químicas de combustão em solução resultaram na formação in situ de fases amorfas de MgAl2O4 para o pó como-sintetizado. A fase cristalina somente foi obtida após um tratamento térmico a 900°C do pó como-sintetizado. O cálculo termodinâmico da reação de combustão em solução mostrou que quando a razão combustível-oxidante aumenta, obtém-se uma elevação da temperatura de chama adiabática e da quantidade de gás produzida, definindo características do particulado como morfologia, tamanho de cristalito, área superficial e nível de agregação. Para a caracterização do pó utilizaram-se técnicas como análise termodiferencial (ATD) e termogravimétrica (ATG), granulometria por dispersão de laser (GDL), BET para análise de área superficial, análise cristalográfica por difração de raios X (DRX), microestrutura por microscopia eletrônica de varredura (MEV) e microscopia eletrônica de transmissão (MET). Os pós de espinélio MgAl2O4 obtidos apresentaram-se como constituídos de cristalitos nanométricos, dispostos na forma de agregados de tamanho micrométrico. O tamanho de cristalito médio, calculado pelo método Single Line, a partir de dados de análises por DRX, foi de 21,57 nm, e deformação média calculada de 1,99 x 10-³ nm. Por análise granulométrica constatou-se um tamanho de aglomerado médio de 27,27 µm, com distribuição trimodal. As análises por MEV e MET confirmaram a agregação das partículas do pó sintetizado, a partir de partículas com morfologia irregular e do tamanho nanométrico dos cristalitos. / The goals of the dissertation were to investigate and develop the solution combustion synthesis technique in order to obtain nanocrystalline spinel MgAl2O4 powders and characterize them by different techniques. This study has also included thermodynamic calculation for reactions, which have been investigated and the influence of fuel-to-oxidant ratio on crystallite size. The combustion synthesis of MgAl2O4 spinel was performed by a trio of chemical precursor sucrose, aluminum nitrate and magnesium nitrate in water, for different fuel-to-oxidant ratios, flame temperatures and total mol number of gases, correlating these parameters with crystallite size, strain, surface area and total porosity. The chemical reactions of solution combustion resulted on amorphous phase formation of MgAl2O4 in situ for as-synthesized powder. The crystalline phase formation of spinel MgAl2O4 was only succeeded obtained after a thermal treatment of as-synthesized powder under 900°C. The thermodynamic calculation of the combustion reaction of the combustion reaction shows that as fuel-to-oxidant ratio increases the amount of gas produced and adiabatic flame temperature also increases. Powder characteristics as morphology, crystallite size, surface area and aggregation degree are mainly governed by the flame temperature and generation of gases. The techniques used for powder characterization included differential thermal analyzer (DTA), thermogravimetric analyzer (TGA), particles size analyzer (PSA), surface area by BET analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The spinel MgAl2O4 powders obtained were composed of nano-size crystallites, but in micrometer-sized aggregates. The mean particle size calculated, via Single Line method, using XRD was 21.57 nm and the mean strain calculated was 1.99 x 10-³ nm. PSA indicated that the synthesized powders contain a mean aggregates size with a tri mode distribution of around 27.27 µm. TEM and SEM analyses confirmed that the as-synthesized powders are composed of particles aggregation. They have an irregular morphology and nano-size crystallites.

Este trabalho teve por objetivo investigar a obtenção de espinélio MgAl2O4 nanoestruturado através da síntese contínua por combustão em solução e sua caracterização por diferentes técnicas. Incluso neste estudo a influência do tipo de combustível e a razão combustível-oxidante no tamanho do cristalito. As partículas de espinélio MgAl2O4 foram sintetizadas utilizando-se os precursores químicos nitrato de alumínio e nitrato de magnésio como fonte dos cátions metálicos. Uréia, glicina e sacarose foram empregadas como agentes redutores, com diferentes valores da razão combustível-oxidante para a sacarose. Estes parâmetros foram relacionados com sua influência no tamanho de cristalito, tamanho de partícula e área superficial. Na caracterização do pó obtido, foram utilizadas técnicas como análise termodiferencial (ATD) e termogravimétrica (ATG), granulometria por difração de laser (GDL), análise de área superficial (BET), análise cristalográfica por difração de raios X (DRX), morfologia por microscopia eletrônica de varredura (MEV). As reações químicas da síntese contínua por combustão em solução resultaram na formação in situ de fases cristalinas para reações estequiométricas de uréia, glicina e sacarose e as deficientes de sacarose. Preponderância de fase amorfa ocorreu nas reações com excesso de sacarose para o pó como-sintetizado. A totalidade de fase cristalina foi obtida após um tratamento térmico a 900°C do pó como-sintetizado. Os pós de espinélio MgAl2O4 obtidos apresentaram-se como constituídos de cristalitos nanométricos, dispostos na forma de agregados de tamanho micrométrico. O tamanho de cristalito médio, calculado pelo método Single Line, a partir de dados de análises por DRX, foi de 13 nm. A área superficial média dos pós calcinados medida pelo método BET foi de 54 g/m2 Por análise granulométrica constatou-se um Tamanho de partícula médio de 17 μm para o pó como-sintetizado e 17,1 μm para o calcinado a 900ºC. As análises por MEV confirmaram a agregação das partículas do pó sintetizado, a partir de partículas preponderantemente esféricas e algumas com morfologia irregular. / This study has investigated a continuous solution combustion synthesis technique to obtain the nanostructured MgAl2O4 spinel powder and their characterize them by different tecniques. This study has also included the investigation of the influence of different kinds of fuel and fuel-to-oxidant ratio on crystallite size. The MgAl2O4 spinel powder was performed using aluminum nitrate and magnesium nitrate to obtain the metallic ions. Urea, glycine and sucrose were used like fuel, with several fuel-to-oxidant ratio. These parameters were correlating with powders characteristics, like crystallite size, particle size and superficial area. The techniques used for powder characterization included differential thermal analyzer (DTA), thermogravimetric analyzer (TGA), particles size analyzer (PSA), surface area by BET analysis, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The chemical reactions of solution combustion resulted on crystalline phase to the reactions with urea, glycine and sucrose (to desabilites on fuel and stoichiometric) and amorphous phase formation of MgAl2O4 in situ for as-synthesized powder. The crystalline phase formation of spinel MgAl2O4 was only succeeded obtained after a thermal treatment of as-synthesized powder under 900°C.The spinel MgAl2O4 powders obtained were composed of nano-size crystallites, but in micrometer-sized aggregates. The mean particle size calculated, via Single Line method, using XRD was 13 nm. PSA indicated that the synthesized powders contain a mean aggregates size with a tri mode distribution of around 17.1 μm. SEM analyses confirmed that the as-synthesized powders are composed of particles aggregation. They have an irregular morphology and nano-size crystallites.

Many applications of metal-organic frameworks (MOFs) are highly dependent on their structures. The type and consistency of structure inform their properties. Zinc-based MOFs are applicable in different fields because of the low toxicity of zinc materials and are therefore also useful for catalysis. While MOF-5, a zinc-based MOF with carboxylate linkers is moisture intolerant, a variant of this is moisture tolerant. The introduction of a nitrogen-based linker in the zinc MOF which renders the structure moisture-tolerant. This material has not been explored as much, despite its multifunctional properties. Furthermore, the growth of Zn-based bimetallics of this MOF has not yet been explored. In this work, I studied the synthesis of this zinc-based moisture-tolerant MOF-5 as a thin film using a simple, fast, and cost-effective layer-by-layer wet synthesis method on different substrate surfaces. I successfully synthesized a series of bimetallics of this MOF as thin films on an untreated silicon wafer substrate. The successful synthesis of these materials was confirmed using X-ray photoelectron spectroscopy, X-ray diffraction, and Raman spectroscopy techniques. Additionally, some software data analysis tools were used for the characterization of the surface of the thin films to quantify the chemical composition. Future applications of these materials will be as sorbent materials for the capture of CO2 and its subsequent conversion to CO which is a synthesis gas for different useful materials like fuel and other chemical materials.

No description available.