The effect of using variable curing light types and intensities on the parameters of a mathematical model that predicts the depth of cure of light- activated dental compositesRidha, Hashem January 2009 (has links)
Indiana University-Purdue University Indianapolis (IUPUI) / The purpose of this study is to further investigate the effect of using six different light source
types with different light output intensities on the parameters of a mathematical model that predicts
the DOC in VLDC’s. In this equation: D = Dp In(E0/Ec), D is the depth of cure in millimeters, E is
the curing energy in J/cm2, Ec is the critical curing energy for the composite to reach a gel layer, and
Dp is a characteristic coefficient.
Three LED and three halogen dental curing units with different light output intensities were
used to cure three shades (B1, A3, D3) of a hybrid resin composite. The exposure duration was at
the intervals of 10, 20, 30, and 40 seconds for each sample setting. ISO scraping technique was
performed to measure the depth of cure of each sample. Regression analysis was used to assess the
fit of the proposed mathematical model D = Dp In(E0/Ec) to the experimental data obtained in this
study.
72
For all the shade-light combinations; A3, B1, and D3 had significantly different regression
lines (P < 0.05) with significantly higher Dp and Ec for B1 than A3 and D3. The only exceptions
were for the Ec values between B1 and D3 in Allegro, Astralis 5, and Visilux 2 groups; and the Ec
between A3 and B1 in Allegro group. The Dp and Ec parameters didn’t show significant differences
between A3 and D3 shades in all the groups. Also, most of the significant differences for Dp values
occurred in the B1 shade-light combinations; however, none of the D3 shade-light combinations
showed significant differences for Dp.
Several factors play combined influential effects on the kinetics of polymerization and depth of
cure in VLDC’s. The shade has a more dominant effect on both parameters Dp and Ec than the
curing light type or source output intensity. As we cure lighter shades “B1,” the effect of using
different lights with different output intensities on the two parameters Dp and Ec will be greater and
more significant than for darker shades “A3 or D3.” The clinical significance drawn from this study
is that clinicians should recognize that using curing lights w/ increased output intensities doesn’t
absolutely increase the DOC of VLDC’s especially with the darker shades.
|
2 |
Influência da temperatura sobre a microdureza de uma resina composta fotoativada com luz halógena e LedsCáceres Benítez, Pablino [UNESP] 31 August 2004 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0
Previous issue date: 2004-08-31Bitstream added on 2014-06-13T19:51:22Z : No. of bitstreams: 1
caceresbenitez_p_me_arafo.pdf: 539913 bytes, checksum: 4b2674880d3cfaa5af955bceb1ed75eb (MD5) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / O objetivo desta pesquisa foi avaliar a influência de várias temperaturas sobre os valores de microdureza de topo e base de uma resina composta fotopolimerizável comercialmente disponível, variando o tipo de fonte de luz (LEDs e lâmpada halógena). As temperaturas testadas foram 25, 35, 45, 55, 65, 80, 90 e 100º C. A resina composta utilizada foi a Z100 (3M). Com o auxílio de uma matriz metálica foram confeccionados 3 corpos-de-prova de 2 mm de espessura e 9,8 mm de diâmetro para cada temperatura. Os corpos-de-prova foram polimerizadas LEDs (60 s) ou lâmpada halógena (40 s) enquanto eram submetidas às diferentes temperaturas, após a polimerização as amostras foram armazenadas a seco, em estufa a 37º C. Após 24 horas as amostras foram submetidas ao teste de microdureza Vickers no topo e na base. Baseados nos resultados conclui-se que com a elevação da temperatura aumentou o valor da dureza Vickers com correlação linear positiva e com ambos aparelhos; o valor da dureza de topo foi sempre superior à dureza de base independentemente da fonte de luz ou temperaturas empregadas; o aparelho de luz halógena só se mostrou superior à fonte de LEDs na região de base dos corpos-de-prova. / The aim of this research was to evaluate the influence of several temperatures on the microhardness values of top and base of a light curing composites resin commercially available, varying the type of light source (LEDs and halogen lamp). The tested temperatures were 25, 35, 45, 55, 65, 80, 90 and 100º C. The composite resin used was Z100 (3M). With the aid of a metallic mould were made three samples of 2 mm of thickness and 9,8 m diameter for each temperature. The samples were light cure while they where submitted to the different temperatures with LEDs (60 s) and halogen lamp (40 s), after the polymerization the samples were dry stored in a stove at 37º C. After 24 hours, the samples were submitted to the Vickers microhardness test in the top and in the base. Based on the results it was concluded that with the elevation of the temperature increased the Vickers hardness value with positive linear correlation on both devices. The hardness value of the top was always superior to the base hardness, independently of the light source or used temperatures. The halogen lamp source was superior to the source of LEDs in the area of base of the samples.
|
3 |
Resistência de união e da microinfiltração marginal em restaurações fotopolimerizadas com LED e luz halógena associadas a três modos de aplicação de um sistema adesivo universal: estudo in vitro / Bond strength and marginal microleakage restorations cured with LED and halogen dental curing light associated to three modes of application of a universal adhesive system: in vitro studyRicardi, Felipe de Brum 02 March 2017 (has links)
Submitted by Edineia Teixeira (edineia.teixeira@unioeste.br) on 2018-04-13T17:05:10Z
No. of bitstreams: 2
Felipe_Ricardi2017.pdf: 1032662 bytes, checksum: 6aaca7ee5122dd1349c2efde06964976 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2018-04-13T17:05:10Z (GMT). No. of bitstreams: 2
Felipe_Ricardi2017.pdf: 1032662 bytes, checksum: 6aaca7ee5122dd1349c2efde06964976 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Previous issue date: 2017-03-02 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The objective was to evaluate the bond strength and marginal microleakage in composite resin restorations, using Universal Single Bond adhesive system associated with Ultralux (halogen) and Bluephase (LED) photoactivators.
For bond strength, eighty healthy human third molars were divided: Halogen (n = 40); LED (n = 40), subdivided according to the technique of application of the adhesive system: self-etch – enamel; etch-and-rinse – enamel, self-etch – dentin; etch-and-rinse – dentin. The teeth were submitted to the Tensile Bond Strength test and the fracture pattern was observed under an optical microscope - 40X magnification, analyzed by the ANOVA, Tukey and Fisher tests (5%). For the marginal microleakage assay, 120 class II cavities were prepared in sixty healthy, randomly divided third human molars: Halogen (n = 30); LED (n = 30) and subdivided according to the application technique of the adhesive system: self-etch; selective-etch; etch-and-rinse. The teeth were thermocycled 2000 times (± 5 / 55ºC), stained in 5% basic fuchsin and sectioned for qualitative and quantitative evaluations, analyzed by the Kruskall-Wallis and Dunn tests (5%).
For bond strength in enamel and dentin, the adhesive application with prior acid etching was better than the etch-and-rinse (p <0.0001), regardless of the type of photoactivator used (p <0.05). The self-etch showed the lowest values of microleakage, (p <0.0001).
The self-etch, obtained the best results in relation to the other techniques of application of the adhesive system in both tests, regardless of the type of photoactivating apparatus. / O objetivo foi avaliar a resistência de união e microinfiltração marginal em restaurações de resina composta, utilizando sistema adesivo Single Bond Universal associado com fotoativadores Ultralux (halógeno) e Bluephase (LED).
Para resistência de união, oitenta terceiros molares humanos hígidos foram divididos: Halógena (n=40); LED (n=40), sendo subdivididos de acordo com a técnica de aplicação do sistema adesivo: condicionamento total-esmalte; autocondicionante-esmalte; condicionamento total-dentina; autocondicionante-dentina. Os dentes foram submetidos ao teste de microtração e o padrão de fratura foi observado em microscópio ótico – 40X de aumento, analisadas pelos testes ANOVA, Tukey e Fisher (5%). Para o ensaio de microinfiltração marginal, 120 cavidades classe II foram preparadas em sessenta terceiros molares humanos hígidos, aleatoriamente divididos: Halógena (n=30); LED (n=30) e subdivididos de acordo com a técnica de aplicação do sistema adesivo: condicionamento total; condicionamento seletivo; autocondicionante. Os dentes foram termociclados 2000 vezes (±5/55ºC), corados em fucsina básica 5% e seccionados para avaliações qualitativa e quantitativa, analisados pelos testes Kruskall-Wallis e Dunn (5%).
Para resistência de união em esmalte e dentina, a aplicação do adesivo com condicionamento ácido prévio, foi melhor que o autocondicionante (p<0.0001), independentemente do tipo de fotoativador utilizado (p<0.05). O condicionamento total mostrou os menores valores de microinfiltração, (p<0.0001).
O condicionamento total, obteve os melhores resultados em relação às outras técnicas de aplicação do sistema adesivo em ambos os testes, independentemente do tipo de aparelho fotoativador.
|
4 |
Influência da potência de fotoativação e de técnicas de inserção na retenção da restauração de resina composta em raiz fragilizada / Influence of curing light intensity and insertion techniques for composite resin restoration retention in weakened rootsMendonça, Isabela Lima de 26 January 2016 (has links)
O objetivo deste estudo ex vivo foi avaliar, por meio de teste de pull out, a influência de diferentes potências de fotoativação, associadas a diferentes técnicas de inserção, na retenção da restauração de resina composta em raízes fragilizadas. Foram utilizadas quarenta raízes de caninos superiores humanos padronizadas em 15 mm de comprimento, que foram submetidas à fragilização por meio de brocas 718PM; 730PM e 720PM, com auxílio de paralelômetro numa extensão de 8 mm. O tratamento endodôntico foi realizado por meio de instrumentos manuais tipo K, apenas no remanescente radicular não tocado pela fragilização. A obturação foi realizada pela técnica de condensação lateral com cimento AH Plus, seguida de corte dos cones, no comprimento correspondente à área da fragilização, e toalete da cavidade. Os espécimes foram distribuídos em quatro grupos (n= 10) de acordo com a técnica de inserção e a potência de fotoativação: Grupo I, resina composta inserida em incremento único; Grupo II, resina composta inserida em dois incrementos. Estes grupos foram fotoativados em baixa potência (500 mW/cm²); Grupo III, resina composta inserida em incremento único; Grupo IV, resina composta inserida em dois incrementos. Estes grupos foram fotoativados em alta potência (1200 mW/cm²). Em todos os grupos as raízes foram restauradas internamente com resina composta fotopolimerizável Z100, com fotoativação auxiliada por pinos plásticos fototransmissores, no comprimento de 8 mm, removidos após a polimerização, para a cimentação dos pinos metálicos pré-fabricados Reforpost com cimento resinoso Relyx ARC, o que proporcionou a obtenção do reforço radicular (resina composta + pino metálico). As raízes foram submetidas ao teste de pull out numa máquina universal de ensaios (Intron 3345) à velocidade de 1mm/min até deslocamento do reforço radicular. Os valores de resistência à tração foram expressos em MPa e submetidos à Análise de Variância dois fatores (α=0,05). A resistência à tração foi influenciada pela potência de fotoativação (P<0,05), mas não pela técnica de inserção da resina composta e nem pela interação dos fatores em estudo (P>0,05). A fotoativação em alta potência apresentou altos valores de resistência à tração (4,38±1,57) em comparação com a fotoativação em baixa potência (2,19±0,82), enquanto que a técnica de inserção em incremento único (3,62±1,60) ou dois incrementos (2,95±1,70) apresentou valores estatisticamente semelhantes. Concluiu-se que o aumento da potência de fotoativação influenciou positivamente na retenção da resina composta utilizada na restauração de raízes fragilizadas, independente da quantidade de incrementos utilizados / The aim of this ex vivo study was to evaluate by pull out test the influence of different curing light intensities, associated to different insertion techniques on the composite resin restoration retention of weakened roots. For this purpose forty maxillary human roots were used. The minimum length was standardized at 15 mm. The roots were weakened using 718PM; 730PM e 720PM drills with the aid of a parallelometer up to a depth of 8mm. Endodontic treatment was performed with K-type hand files only in the root section unreached by the weakening. Root canal filling was performed according to the lateral condensation technique using AHPlus sealer. Then cones were cut up to weakening length and cavity was cleaned.. The samples were assigned to four groups (n= 10) according to the insertion technique and curing light intensity: Group I, composite resin placed in bulk placement; Group II, composite resin placed in two increments. These groups were photoactivated with low intensity curing light (500 mW/cm²); Group III, composite resin placed in bulk placement; Group IV, composite resin placed in two increments. These groups were photoactivated with higth intensity curing light (1200 mW/cm²). In all groups the roots were restored internally with Z100 light-cured composite resin and photoactivated using light-transmitting plastic posts up to a depth of 8 mm. After polymerization the light-transmitting posts were removed. Then prefabricated metal posts were cemented with Relyx ARC resin-based cement, which provided the achieviment of root reinforcement (composite resin + metal post). The roots were subjected to pull out test by a universal testing machine (Intron 3345) at a speed of 1 mm/min until the root reinforcement was dislodged. Resistance values were expressed in Mpa and were subjected by 2-way Analysis of Variance (α=0,05). Curing light intensity influenced the tensile strength (p<0,05), however for composite resin insertion technique and for interaction between factors under study (P>0,05) no influence was found. Higth intensity curing light showed high tensile strength values (4,38±1,57) compared with low intensity curing light (2,19±0,82) whereas composite resin insertion technique using bulk placement (3,62±1,60) or two increments (2,95±1,70) showed similar values. Increasing the curing light intensity had positive influences on composite resin restoration retention in weakened roots, regardless of the amount of increments used.
|
5 |
Influência da temperatura sobre a microdureza de uma resina composta fotoativada com luz halógena e Leds /Cáceres Benítez, Pablino. January 2004 (has links)
Resumo: O objetivo desta pesquisa foi avaliar a influência de várias temperaturas sobre os valores de microdureza de topo e base de uma resina composta fotopolimerizável comercialmente disponível, variando o tipo de fonte de luz (LEDs e lâmpada halógena). As temperaturas testadas foram 25, 35, 45, 55, 65, 80, 90 e 100º C. A resina composta utilizada foi a Z100 (3M). Com o auxílio de uma matriz metálica foram confeccionados 3 corpos-de-prova de 2 mm de espessura e 9,8 mm de diâmetro para cada temperatura. Os corpos-de-prova foram polimerizadas LEDs (60 s) ou lâmpada halógena (40 s) enquanto eram submetidas às diferentes temperaturas, após a polimerização as amostras foram armazenadas a seco, em estufa a 37º C. Após 24 horas as amostras foram submetidas ao teste de microdureza Vickers no topo e na base. Baseados nos resultados conclui-se que com a elevação da temperatura aumentou o valor da dureza Vickers com correlação linear positiva e com ambos aparelhos; o valor da dureza de topo foi sempre superior à dureza de base independentemente da fonte de luz ou temperaturas empregadas; o aparelho de luz halógena só se mostrou superior à fonte de LEDs na região de base dos corpos-de-prova. / Abstract: The aim of this research was to evaluate the influence of several temperatures on the microhardness values of top and base of a light curing composites resin commercially available, varying the type of light source (LEDs and halogen lamp). The tested temperatures were 25, 35, 45, 55, 65, 80, 90 and 100º C. The composite resin used was Z100 (3M). With the aid of a metallic mould were made three samples of 2 mm of thickness and 9,8 m diameter for each temperature. The samples were light cure while they where submitted to the different temperatures with LEDs (60 s) and halogen lamp (40 s), after the polymerization the samples were dry stored in a stove at 37º C. After 24 hours, the samples were submitted to the Vickers microhardness test in the top and in the base. Based on the results it was concluded that with the elevation of the temperature increased the Vickers hardness value with positive linear correlation on both devices. The hardness value of the top was always superior to the base hardness, independently of the light source or used temperatures. The halogen lamp source was superior to the source of LEDs in the area of base of the samples. / Orientador: Osmir Batista de Oliveira Junior / Coorientador: Vanderlei Salvador Bagnato / Banca: Sizenando de Toledo Porto Neto / Banca: Marcelo Giannini / Mestre
|
6 |
Influência da potência de fotoativação e de técnicas de inserção na retenção da restauração de resina composta em raiz fragilizada / Influence of curing light intensity and insertion techniques for composite resin restoration retention in weakened rootsIsabela Lima de Mendonça 26 January 2016 (has links)
O objetivo deste estudo ex vivo foi avaliar, por meio de teste de pull out, a influência de diferentes potências de fotoativação, associadas a diferentes técnicas de inserção, na retenção da restauração de resina composta em raízes fragilizadas. Foram utilizadas quarenta raízes de caninos superiores humanos padronizadas em 15 mm de comprimento, que foram submetidas à fragilização por meio de brocas 718PM; 730PM e 720PM, com auxílio de paralelômetro numa extensão de 8 mm. O tratamento endodôntico foi realizado por meio de instrumentos manuais tipo K, apenas no remanescente radicular não tocado pela fragilização. A obturação foi realizada pela técnica de condensação lateral com cimento AH Plus, seguida de corte dos cones, no comprimento correspondente à área da fragilização, e toalete da cavidade. Os espécimes foram distribuídos em quatro grupos (n= 10) de acordo com a técnica de inserção e a potência de fotoativação: Grupo I, resina composta inserida em incremento único; Grupo II, resina composta inserida em dois incrementos. Estes grupos foram fotoativados em baixa potência (500 mW/cm²); Grupo III, resina composta inserida em incremento único; Grupo IV, resina composta inserida em dois incrementos. Estes grupos foram fotoativados em alta potência (1200 mW/cm²). Em todos os grupos as raízes foram restauradas internamente com resina composta fotopolimerizável Z100, com fotoativação auxiliada por pinos plásticos fototransmissores, no comprimento de 8 mm, removidos após a polimerização, para a cimentação dos pinos metálicos pré-fabricados Reforpost com cimento resinoso Relyx ARC, o que proporcionou a obtenção do reforço radicular (resina composta + pino metálico). As raízes foram submetidas ao teste de pull out numa máquina universal de ensaios (Intron 3345) à velocidade de 1mm/min até deslocamento do reforço radicular. Os valores de resistência à tração foram expressos em MPa e submetidos à Análise de Variância dois fatores (α=0,05). A resistência à tração foi influenciada pela potência de fotoativação (P<0,05), mas não pela técnica de inserção da resina composta e nem pela interação dos fatores em estudo (P>0,05). A fotoativação em alta potência apresentou altos valores de resistência à tração (4,38±1,57) em comparação com a fotoativação em baixa potência (2,19±0,82), enquanto que a técnica de inserção em incremento único (3,62±1,60) ou dois incrementos (2,95±1,70) apresentou valores estatisticamente semelhantes. Concluiu-se que o aumento da potência de fotoativação influenciou positivamente na retenção da resina composta utilizada na restauração de raízes fragilizadas, independente da quantidade de incrementos utilizados / The aim of this ex vivo study was to evaluate by pull out test the influence of different curing light intensities, associated to different insertion techniques on the composite resin restoration retention of weakened roots. For this purpose forty maxillary human roots were used. The minimum length was standardized at 15 mm. The roots were weakened using 718PM; 730PM e 720PM drills with the aid of a parallelometer up to a depth of 8mm. Endodontic treatment was performed with K-type hand files only in the root section unreached by the weakening. Root canal filling was performed according to the lateral condensation technique using AHPlus sealer. Then cones were cut up to weakening length and cavity was cleaned.. The samples were assigned to four groups (n= 10) according to the insertion technique and curing light intensity: Group I, composite resin placed in bulk placement; Group II, composite resin placed in two increments. These groups were photoactivated with low intensity curing light (500 mW/cm²); Group III, composite resin placed in bulk placement; Group IV, composite resin placed in two increments. These groups were photoactivated with higth intensity curing light (1200 mW/cm²). In all groups the roots were restored internally with Z100 light-cured composite resin and photoactivated using light-transmitting plastic posts up to a depth of 8 mm. After polymerization the light-transmitting posts were removed. Then prefabricated metal posts were cemented with Relyx ARC resin-based cement, which provided the achieviment of root reinforcement (composite resin + metal post). The roots were subjected to pull out test by a universal testing machine (Intron 3345) at a speed of 1 mm/min until the root reinforcement was dislodged. Resistance values were expressed in Mpa and were subjected by 2-way Analysis of Variance (α=0,05). Curing light intensity influenced the tensile strength (p<0,05), however for composite resin insertion technique and for interaction between factors under study (P>0,05) no influence was found. Higth intensity curing light showed high tensile strength values (4,38±1,57) compared with low intensity curing light (2,19±0,82) whereas composite resin insertion technique using bulk placement (3,62±1,60) or two increments (2,95±1,70) showed similar values. Increasing the curing light intensity had positive influences on composite resin restoration retention in weakened roots, regardless of the amount of increments used.
|
7 |
CORRELAÇÃO ENTRE GRAU DE CONVERSÃO E RESISTÊNCIA DE UNIÃO DE SISTEMAS ADESIVOS AUTOCONDICIONANTES / CORRELATION BETWEEN DEGREE OF CONVERSION AND BOND STRENGTH OF THE SELF-ETCHING ADHESIVE SYSTEMBorges, Marciano de Freitas 24 February 2010 (has links)
Objective: The aim of this study was to analyses the relationship between the degree of conversion of double bonds of self-etching adhesives and microshear bond strength on dentin. Materials and methods: For microshear testing twenty third molar caries free were selected. They had their crowns sectioned longitudinally so as to obtain slices that were randomly chosen and divided into four groups according to the adhesive system, Single Bond
(SB), Clearfil SEBond (CL) , Adhese (AD) and Gbond (GB). The slices were included into epoxy resin, and then cylindrical restorations were built with an area of 1.0 mm in diameter and 2.0 mm in height, around ten restorations per group, using a starch matrix. After 24 hours the specimens were tested for bond strength. To analyze the degree of conversion of these systems, a drop of adhesive was dispensed on a glass plate and after 20 seconds polymerized, forming a film of adhesive. After 24 hours, these films were pulverized and mixed with potassium bromide, pressed in a hydraulic press to form an insert for analysis with the spectrophotometer - FT-IR. The data of shear bond strength and degree of conversion of each
specimen were submitted to ANOVA and Tukey s test (p = 0.05). Results: The SB adhesive system had mean values of bond strength statistically higher than AD and GB, but no
statistical difference was found with Cl. Among the self-etching systems, the highest average shear bond strength was achieved with the application of the union CL, followed by GB and AD systems, which were not statistically different. Regarding the degree of conversion, similar statistical results were found for the systems SB and CL, and despite the SB had a higher average it, did not differ from CL. The adhesive system SB and CL showed higher values in AD and GB. The AD, showed values higher than the GB. Conclusion: The degree of conversion is affected by several factors related to the complex mixture of adhesive systems, which somehow contribute to their bond strength. / Objetivo: O objetivo desse estudo foi avaliar o grau de conversão de sistemas adesivos autocondiconantes em dentina e correlacioná-los com a resistência ao teste de
microcisalhamento. Materiais e Métodos: Para o ensaio de microcisalhamento foram selecionados vinte terceiros molares livres de cárie, os quais tiveram suas coroas seccionadas
longitudinalmente de modo a se obter fatias, que, aleatoriamente, foram divididas em quatro grupos, de acordo com o sistema adesivo uilizado, Single Bond (SB), Clearfil SE Bond (CL), Adhese (AD) e Gbond (GB). As fatias foram incluídas em tubos de PVC com resina acrílica e, em seguida, foram construídas restaurações cilíndricas com uma área de 1,0 mm de diâmetro e 2,0 mm de altura, em torno de dez restaurações por grupo, por meio de uma matriz de amido. Após 24 horas, os corpos de prova foram submetidos ao ensaio de microcisalhamento. Para análise do grau de conversão desses sistemas, uma gota do adesivo foi dispensada sobre uma placa de vidro e, após 20 segundos, foram fotopolimerizadas, formando uma película de adesivo. Após 24h, essas películas foram pulverizadas e misturadas
com brometo de potássio, prensadas em prensa hidráulica de modo a formar uma pastilha para análise no espectofotômetro - FT-IR. Os dados obtidos da resistência de união e do grau de conversão foram submetidos à análise de variância e teste de Tukey (p = 0.05). Resultados: O
sistema de união SB apresentou valores médios de resistência de união ao microcisalhamento estatisticamente superior AD e GB, mas não apresentou diferença estatística em relação ao
sistema Cl. Dentre os sistemas autocondicionantes, as maiores médias no ensaio mecânico foram obtidas com a aplicação do sistema de união CL, seguido pelos sistemas AD e GB, que não foram estatisticamente diferentes entre si. Em relação ao grau de conversão, resultados estatísticos semelhantes foram encontrados para os sistemas SB e CL, que, apesar do SB apresentar uma maior média, não diferiu do CL. O sistema adesivo SB e CL apresentaram valores médios superiores ao AD e GB. O AD, que por sua vez, apresentou valores médios maiores que o GB. Conclusão: O grau de conversão é afetado por diversos fatores relacionados à mistura complexa dos sistemas adesivos, que, de certo modo, repercutirá na sua resistência de união.
|
8 |
Shear bond strength of metallic brackets using a 6 and 12 second curing time with high power monowave and polywave LED unitsMcCarthy, Shannon 01 January 2013 (has links)
A thesis submitted to the College of Dental Medicine of Nova Southeastern University of the degree of Master of Science in Dentistry.
Objectives: To date, the literature has shown that a 10 second curing time is necessary to consistently achieve effective shear bond strengths (SBS) of greater than 10 MPa. Recently, several manufacturers have developed high power curing lights that claim only a 6 second cure time is needed. The purpose of this study was to evaluate the shear bond strength of orthodontic brackets when using two new high power LED curing lights after a 6 and 12 second light curing time. Methods: 120 extracted premolars were divided into 6 groups (n=20). Metallic brackets were bonded using Transbond XT (3M-Unitek) and cured for 6 or 12 seconds using two high power LED curing lights (Ortholux Luminous LED, 3M-Unitek; OrthoValo, Ultradent) and one control LED unit (Ortholux LED, 3M-Unitek). The samples were stored in distilled water for 24 hours at 37°C, thermocycled and then debonded using an Instron Universal Testing Machine at a crosshead speed of 5mm/min. Bond failure was evaluated under optical microscopy using a modified adhesive remnant index (ARI). Results: All sample groups produced mean SBS higher than 10MPa. Significant reductions in SBS were observed with the Ortholux LED when the curing time was reduced from 12 to 6 seconds. The OrthoValo had significantly higher SBS than the Ortholux LED and the Ortholux Luminous LED at 6 seconds. At 12 seconds, OrthoValo SBS were significantly higher than Ortholux LED only. A higher frequency of enamel damage occurred in the OrthoValo group (28.2%) compared to the Ortholux LED (12.5%) and Ortholux Luminous LED (7.5%). No significant correlation was found between ARI score and SBS. Conclusions: Higher SBS were obtained in the OrthoValo group. This coincided with a higher frequency of enamel damage.
|