Korozijai ir karščiui atsparaus plieno standaus apkrovimo ciklinių deformavimo parametrų nustatymas / Evaluation of cyclic properties by static characterristics for structural materialsKopūstienė, Diana 13 June 2005 (has links)
It is impossible to improve the quality of the machines, to increase their reliability and lifetime if the working conditions and the properties of the material are not analyzed. We must know the type of the material (hardening, softening or cyclically stabile), what is chosen for the constructions in low cycle loading, because strain and stress change during the exploitation and depend on this type. If we know the type of the material, we can determine the possibility of its application in concrete exploitation conditions. Real working conditions of the most constructions are close to loading with limited strain (hard straining), because elastic and plastic deformation is met in the zones of crack and stress concentration, that are surrounded with elastically deformed material.
The low cycle loading curves parameters A, and are used for the computation of elastic plastic strain curves. These parameters are obtained from the soft low cycle loading results in many cases. The other possible ways for the determination of parameters A, and are shown in this work.
The most investigated materials had the initial instability in the interval . For more objective evaluation of stress strain curves parameters A, and , all values of width of hysteresis loop up to semicycle were rejected as insignificant in comparison with the rest lifetime in cycles range . The parameter for the evaluation of hardening (softening) intensity was determined, when the values of... [to full text]
|
2 |
Analyses multi-échelles du comportement et la durée de vie d’aciers inoxydables 304L sous sollicitations cycliques avec pré-écrouissage / Multi-scale analysis of behavior and fatigue life of 304L stainless under cyclic loading with pre-hardeningBelattar, Adel 11 February 2013 (has links)
Le travail s’intéresse aux effets d’un pré-écrouissage cyclique axial ou en torsion sur le comportement cyclique et la durée de vie en fatigue sous sollicitation axiale à température ambiante d’un acier inoxydable austénitique 304L. Les essais cycliques séquentiels à amplitude de déformation croissante ou décroissante montrent que la courbe cyclique du 304L est non-unique. Cette caractéristique est liée à la persistance de l’état microstructural généré pendant les cycles d’amplitude de déformation maximale de la première séquence. En augmentant le nombre des séquences, l’acier 304L montre une tendance vers une courbe cyclique asymptotique, l’écrouissage semble se stabiliser. Des essais de fatigue sous chargement axial ont été réalisés sur des éprouvettes vierges ou pré-écrouies en traction-compression ou en torsion. Les durées de vie ont été sensiblement réduites pour les éprouvettes pré-écrouies. Ce phénomène est lié à la formation de structures de dislocations denses héritées de la phase de pré-écrouissage. Cependant, l’augmentation de l’amplitude de déformation en fatigue réduit l’effet du pré-écrouissage. / This study investigates the effects of loading history on the cyclic stress-strain curve and fatigue behavior of 304L stainless steel at room temperature. Tension-compression tests were performed ont the same specimen under controlled strain, using several loading sequences of increasing or decreasing amplitude. The results showed that fatigue life is significantly reduced by the previous loading history. A previously developed method for determining the effect of prehardening was evaluated. Microstructural analyses were also performed; the microstructures after preloading and their evolution during the fatigue cycles were characterized by TEM. The results of these analyses improve our understanding of the macroscopic properties of 304L stainless steel and can help us identify the causes of failure and lifetime reduction.
|
3 |
Effet du pré-écrouissage sur la durée de vie d'aciers austénitiques de type 304L / Effect of pre-harding on the lifetime of type 304L austenitic stainless steelsKpodekon, Crescent 30 April 2010 (has links)
Le travail s’intéresse aux effets de l’histoire de chargement sur le comportement et la durée de vie en fatigue de deux nuances (THYSSEN et CLI)d’un acier inoxydable austénitique 304L à la température ambiante. Les essais ont été réalisés en utilisant deux catégories d’éprouvettes. Les éprouvettes de la première catégorie (vierges) ont été soumises à des essais classiques de fatigue,alors que celles de la deuxième ont subi, avant les essais de fatigue, un pré-écrouissage monotone ou cyclique en déformation imposée. Les éprouvettes vierges manifestent un adoucissement cyclique suivi d’un durcissement cyclique alors que les éprouvettes pré-écrouies ne présentent qu’un durcissement cyclique. Les résultats montrent une grande influence du pré-écrouissage qui semble bénéfique en contrainte imposée, mais néfaste en déformation imposée,même en présence d'une contrainte moyenne de compression. Ces résultats sont discutés en termes d'évolution cyclique du module d'élasticité, des écrouissages isotropes et cinématiques, et de la densité d’énergie absorbées par cycle, dans différentes configurations : avec ou sans pré-écrouissage, en contrainte ou déformation imposées... / This study deals with the effect of the loading history on the cyclic behavior and the fatigue life of two kinds (THYSSEN and CLI) of 304L stainless steel at room temperature. The experiments have been performed using two specimens’ categories. The first one (virgin) has been submitted to only classical fatigue tests while in the second category, prior to the fatigue test, the specimen is subjected to a pre-hardening process under either monotonic or cyclic strain control. Cyclic softening followed by cyclic hardening are observed for the virgin specimens while only cyclic softening is exhibited by the pre-hardened specimens. The obtained results show that fatigue life is strongly influenced by the pre-hardening: it seems beneficial under stress control but detrimental under strain control, even in the presence of a compressive mean stress. The results are discussed regarding the cyclic evolution of the elastic modulus aswell as the isotropic and kinematic parts of the strain hardening, and strain energy density per cycle, in different configurations: with or without prehardening,stress or strain control...
|
4 |
Stanovení zkrácených cyklických deformačních křivek superslitiny Inconel 738LC při zvýšených teplotách / Determination of Shortcut Cyclic Stress-strain Curves of Superalloy Inconel 738LC at Elevated TemperaturesŠmíd, Miroslav January 2008 (has links)
Multiple step tests under cyclic strain control have been performed using cylindrical specimens of cast polycrystalline Inconel 738LC superalloy at 23, 700, 500, 800 and 900 °C in laboratory atmosphere to obtain cyclic stress-strain curves. During cyclic straining of specimen were obtained cyclic hardening-softening curves. Their progress changed with temperature and strain amplitude. Evaluated cyclic stress-strain curves are shifted to lower stresses with increasing temperature. Surface relief was observed in fatigued specimens under SEM and metalography under optic microscopy. Slip markings were studied on specimen surface fatigued at 700 °C .Stress-strain response is compared and discussed in relation to the surface observations - persistent slip markings.
|
5 |
Deformation History and Load Sequence Effects on Cumulative Fatigue Damage and Life PredictionsColin, Julie Anne January 2009 (has links)
No description available.
|
6 |
Verformungsverfestigung bei zyklisch inkrementeller Torsion von Reineisen und dem Stahl 42CrMo4N / Strain hardening of pure iron and steel 42CrMo4N under cyclic incremental torsionKuprin, Corinna 12 February 2013 (has links) (PDF)
Die Arbeit widmet sich dem Fließverhalten von Stählen bei zyklisch inkrementeller Torsion. Dazu werden vergleichend Reineisen und der ferritisch-perlitische Stahl 42CrMo4N bei unterschiedlichen Verformungspfaden betrachtet. Vor allem in zyklischen Torsionsversuchen mit bleibendem Verformungsinkrement je Zyklus werden Fließkurvenverläufe und Verformungsverfestigung analysiert.
Die Ergebnisse belegen den Einfluss des lamellaren Zementit auf das Fließverhalten des Stahls 42CrMo4N, während die Eigenschaften des Reineisens von der entstehenden Versetzungszellstruktur bestimmt werden. Die Richtungsabhängigkeit der Fließspannung und die Verläufe der Fließkurven unterscheiden sich für die betrachteten Werkstoffe deutlich.
Fließortkurven dienen der quantitativen Beschreibung der Verfestigung. Die Vorgehensweise zu ihrer Ermittlung und ihre Abhängigkeit von den Versuchsbedingungen und den Verformungszuständen werden gezeigt. Bei Reineisen dominieren isotrope, bei dem Stahl 42CrMo4N kinematische Verfestigungsanteile das Fließverhalten. / Ferritic-pearlitic steel 42CrMo4N and pure iron under different strain paths are compared regarding their flow behaviour. Mainly in cyclic torsion tests with resulting strain increment per cycle shear stresses and strain hardening are analysed.
The results show, that the cementite lamellae determine the flow behaviour of the steel 42CrMo4N, whereas the properties of pure iron are governed by the evolving dislocation cell structure. The dependency of flow stress on the strain direction is different for the two materials.
Yield surfaces describe strain hardening quantitatively. The procedure for yield point detection and the dependency of subsequent yield surfaces on experimental conditions and strain states is shown. For pure iron isotropic hardening, for steel 42CrMo4N kinematic strain hardening dominates the flow behaviour.
|
7 |
Verformungsverfestigung bei zyklisch inkrementeller Torsion von Reineisen und dem Stahl 42CrMo4NKuprin, Corinna 04 October 2012 (has links)
Die Arbeit widmet sich dem Fließverhalten von Stählen bei zyklisch inkrementeller Torsion. Dazu werden vergleichend Reineisen und der ferritisch-perlitische Stahl 42CrMo4N bei unterschiedlichen Verformungspfaden betrachtet. Vor allem in zyklischen Torsionsversuchen mit bleibendem Verformungsinkrement je Zyklus werden Fließkurvenverläufe und Verformungsverfestigung analysiert.
Die Ergebnisse belegen den Einfluss des lamellaren Zementit auf das Fließverhalten des Stahls 42CrMo4N, während die Eigenschaften des Reineisens von der entstehenden Versetzungszellstruktur bestimmt werden. Die Richtungsabhängigkeit der Fließspannung und die Verläufe der Fließkurven unterscheiden sich für die betrachteten Werkstoffe deutlich.
Fließortkurven dienen der quantitativen Beschreibung der Verfestigung. Die Vorgehensweise zu ihrer Ermittlung und ihre Abhängigkeit von den Versuchsbedingungen und den Verformungszuständen werden gezeigt. Bei Reineisen dominieren isotrope, bei dem Stahl 42CrMo4N kinematische Verfestigungsanteile das Fließverhalten. / Ferritic-pearlitic steel 42CrMo4N and pure iron under different strain paths are compared regarding their flow behaviour. Mainly in cyclic torsion tests with resulting strain increment per cycle shear stresses and strain hardening are analysed.
The results show, that the cementite lamellae determine the flow behaviour of the steel 42CrMo4N, whereas the properties of pure iron are governed by the evolving dislocation cell structure. The dependency of flow stress on the strain direction is different for the two materials.
Yield surfaces describe strain hardening quantitatively. The procedure for yield point detection and the dependency of subsequent yield surfaces on experimental conditions and strain states is shown. For pure iron isotropic hardening, for steel 42CrMo4N kinematic strain hardening dominates the flow behaviour.
|