Made available in DSpace on 2017-07-24T19:22:08Z (GMT). No. of bitstreams: 1 Shelon Cristina Souza Pinto.pdf: 1676066 bytes, checksum: 976186479b1c0d4721c391d1a3411ea9 (MD5) Previous issue date: 2008-02-18 / The aim of this study was to evaluate the physico-chemical characteristics of dentifrices with desensitizing agents as well as their capability for obliterate dentinal tubules. In vitro study: Physical and chemical properties were analyzed using the loss desiccation test, pH analysis, microbiologic test, scanning electronic microscopy (SEM) and energy dispersive x ray (EDX). The dentifrices were: Sensodyne original® (GSO); Colgate sensitive branqueador® (GCS) and Sensodyne Proteção Total® (GSPT). In vivo study: Forty rats with 90 days and weighing 200-270 grams were divided into the following groups: GSO: (n=10) strontium chloride (Sensodyne original®); GCS- (n=10) potassium citrate (Colgate sensitive whitening®), GSPT- (n=10) potassium nitrate (Sensodyne Protector Total®) and GAD- (n=10) distilled water (Control). Upper and lower incisors had dentinal tubules exposed with cervical abrasion in superficial (0.2 mm) and deep dentin (0.4mm). Smear layer was removed by actively etched with a 24% EDTA gel per 3 minutes, after samples were toothbrushed (15 movements) daily, for 4 days. After each treatment, 5 μl of Evans blue dye solution was applied to the teeth. The samples were prepared to dentin permeability, scanning electron microscopy (SEM) and energy-dispersive X-ray (EDX) analysis. Physico-chemical dentifrices characterization results: GSO (64.34±0.85) showing a higher solid residue and GCS (40.08±1.71) the lower. Basic pH were observed (GSO- 7.81±0.011, GCS- 8.00±0.043, GSPT- 8.36±0.055). Dentifrices not showed bacterial growth or fungal. SEM analysis showed inorganic particles. Exception fluoride, desensitizing agents’ chemicals elements were detected by EDX analysis. In vivo study: There was significant difference among test groups and control for dentin permeability (p<0.001). Superficial and deep dentin had similar dentinal tubules number per mm2, statistical difference was observed in deep dentin between GSO and GAD (p>0.05). The dentinal tubules area and diameter were similar in test groups, but these had a significant difference (p<0.001) with control group (higher area and diameter). GSO, GCS e GSPT (superficial and deep dentin) showed open and partial obliterated tubules. Most opened tubules were observed on GAD. EDX showed a low quantity of desensitizing agents’ elements. According to the methodology used was possible to conclude that the dentifrices had different physico-chemical characteristics, suggesting different abrasive pattern. All agents tested were able to decrease dentine permeability and partial obliteration of dentinal tubules. / O objetivo deste estudo foi avaliar as características físico-químicas e a obliteração de túbulos dentinários por dentifrícios incorporados com agentes dessensibilizantes. Estudo in vitro: Para a caracterização físico-química foram realizados os testes de perda por dessecação, análise de pH, avaliação microbiológica e análise por microscopia eletrônica de varredura (MEV) e energia dispersiva de raio x (EDX). Os dentifrícios testados foram: Sensodyne original® (GSO); Colgate sensitive branqueador® (GCS) e Sensodyne Proteção Total® (GSPT). Estudo in vivo: 40 ratos com 90 dias e peso entre 200-270 gramas, divididos em 4 grupos: GSO- (n=10) cloreto de estrôncio; GCS- (n=10) citrato de potássio, GSPT- (n=10) nitrato de potássio e GAD- (n=10) água destilada (Controle). Para exposição dos túbulos dentinários, em dentina superficial (0,2mm) e profunda (0,4mm), foram realizados desgastes no esmalte da face vestibular dos incisivos superiores e inferiores ao nível da margem gengival. Smear layer foi removida através do condicionamento ativo com gel de EDTA por 3 minutos, e posteriormente, escovadas (15 movimentos) diariamente, durante 4 dias. Após cada tratamento 5μl de solução de Azul de Evans foi aplicado sobre os dentes. As amostras foram preparadas para análise da permeabilidade dentinária, MEV e EDX. Os resultados da caracterização físicoquímica dos dentifrícios mostraram com o teste de perda por dessecação, maior quantidade de resíduo sólido no GSO (64,34±0,85) e a menor no GCS (40,08±1,71). O pH dos dentifrícios se apresentou básico (GSO- 7,81±0,011, GCS- 8,00±0,043, GSPT- 8,36±0,055). Nenhum dentifrício apresentou crescimento bacteriano ou fúngico. A análise em MEV apresentou partículas inorgânicas homogêneas e o EDX identificou os elementos químicos presentes nas formulações, com exceção do flúor. Estudo in vivo: a avaliação da permeabilidade dentinária mostrou diferenças estatísticas entre os grupos teste e o controle (p<0,001). O número de túbulos dentinários por mm2 foi similar para dentina superficial e profunda, existindo diferenças significativas apenas entre GSO e GAD em dentina profunda (p>0,05). A área e o diâmetro dos túbulos dentinários foram semelhantes entre os grupos testes, com diferenças significativas (p<0,001) em relação ao grupo controle, que se apresentou com maior área e maior diâmetro. GSO, GCS e GSPT (dentina superficial e profunda) mostraram túbulos abertos e parcialmente obliterados. GAD apresentou a maioria dos túbulos abertos. EDX mostrou pequena quantidade dos elementos presentes nos agentes dessensibilizantes. De acordo com a metodologia utilizada foi possível concluir que os dentifrícios apresentaram diferentes características físico-químicas, sugerindo diferentes padrões de abrasividade. Todas as substâncias testadas foram capazes de reduzir a permeabilidade dentinária com obliteração parcial dos túbulos dentinários.

Made available in DSpace on 2017-07-24T19:22:15Z (GMT). No. of bitstreams: 1 Juliana Aparecida de Campos Lawder.pdf: 4443458 bytes, checksum: 1e068fa2b364b7ffd6181e9bfa9ad613 (MD5) Previous issue date: 2010-08-30 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Aiming to check the pH values and ability to seven drinks previously selected, the action beverage on the structure of bovine enamel and dentin and the effect of brushing with dentifrices one of which is indicated for lesions of acid erosion a study was conducted in vitro. We obtained 36 fragments of bovine teeth, with 18 enamel and dentin of 18, which remained immersed in grape juice for 10 minutes and then immersed in artificial saliva for 60 minutes. This cycle was repeated 4 times every 6 hours. After acid challenge, bodies were prepared with proof-of-four fragments each (2 of 2 enamel and dentin). Six specimens used in ev ence were submitted to 16,000 brushing cycles using soft bristle brushes and toothpaste solution / distilled water or distilled water only. The brushing was performed with two dentifrices, diluted in ratio 1:2, and only distilled water (control). The change in surface roughness and hardness were determined by the difference between roughness obtained after erosion (erosive) and after brushing (toothpaste, water). Moreover, we observed in SEM images of enamel and dentin subjected to erosion and brushing. The results were subjected to statistical tests (ANOVA, Bonferroni test (p ≤ 0.05) and t-student test) which showed: soaking in grape juice caused higher roughness on the surfaces when compared to immersion in artificial saliva (p = 0.0058) with higher amount of crystals when the surfaces were brushed with the toothpaste when compared to brushing with distilled water and a correlation between surface roughness, soaking in acid beverage and brushing. Through the results obtained, it can be concluded that there was loss of tooth structure when it was subjected to immersion in acid beverage. The variations in structure loss was dependent on whether there is brushing with toothpaste after exposure and both dentifrices tested were able to accelerate the wear of tooth surfaces subject to erosion. / Com o objetivo de verificar os valores de pH e capacidade de sete bebidas previamente selecionadas, a ação de uma bebida ácida sobre a estrutura do esmalte e da dentina bovina e o efeito da escovação simulada com dois dentifrícios, sendo um deles indicado para lesões de erosão ácida, foi realizado um estudo in vitro. Foram obtidos 36 fragmentos de dentes bovinos, sendo 18 de esmalte e 18 de dentina, os quais permaneceram imersos em suco de uva durante 10 minutos e depois mergulhados em saliva artificial por 60 minutos. Este ciclo foi repetido 4 vezes, a cada 6 horas. Após desafio ácido, foram confeccionados corpos-de-prova com 4 fragmentos cada (2 de esmalte e 2 de dentina). Seis corpos-de-prova foram submetidos a 16.000 ciclos de escovação, utilizando escovas de cerdas macias e solução creme dental/água destilada ou apenas água destilada. A escovação simulada foi realizada com 2 dentifrícios, diluídos na proporção 1:2, e somente água destilada (controle). A alteração de rugosidade superficial e microdureza foram determinadas pela diferença entre rugosidade obtida após erosão (bebida ácida) e após escovação (dentifrícios e água). Além disto, foram observadas imagens em MEV das superfícies de esmalte e de dentina submetidas à erosão e escovação. Os resultados foram submetidos aos testes estatísticos (ANOVA, teste de Bonferroni (p≤0,05) e teste t-student), os quais demonstraram: a imersão em suco de uva causou maior rugosidade nas superfícies quando comparado à imersão em saliva artificial (p=0,0058); houve maior quantidade de cristais quando as superfícies foram escovadas com os dentifrícios quando comparados à escovação com água destilada e houve correlação entre rugosidade superficial, imersão em bebida ácida e escovação simulada. Através dos resultados obtidos, pode-se concluir que houve perda de estrutura dentária quando esta foi submetida à imersão em bebida ácida. As variações da perda da estrutura foi dependente de haver ou não escovação com dentifrício após a exposição e ambos os dentifrícios testados foram capazes de acelerar o desgaste da superfície dentária submetida à erosão.

Made available in DSpace on 2017-07-24T19:22:30Z (GMT). No. of bitstreams: 1 Marcio Cristiano de Souza Rastelli.pdf: 5926309 bytes, checksum: 1a36673541f01b28c69af14ba60a3af8 (MD5) Previous issue date: 2012-12-14 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Desensitizing toothpastes that occlude dentinal tubules were shown to be effective in the treatment of dentinal hypersensitivity. The aim of this study was to develop and evaluate a desensitizing toothpaste containing hydroxyapatite nanoparticles. The in vitro study was performed in three steps: synthesis and characterization of hydroxyapatite nanoparticles, formulation and characterization of toothpastes and assessing the potential for occlusion of dentinal tubules. Hydroxyapatite nanoparticles were obtained by wet chemical synthesis at 37 º C, and from that it was developed the WCS nanoparticle hydroxyapatite and hydrothermal synthesis at 180 ° C (HS). The characterization was performed using scanning electron microscopy (SEM), microanalysis by energy dispersive spectroscopy, X-ray diffraction, spectroscopy in the infrared Fourier transform and micro-Raman, thermal analysis, and assessment of cytotoxicity. Four experimental toothpastes were formulated and compared to two commercially available ones. We carried out the characterization and quality control of these toothpastes by evaluating pH, consistency, density, analysis of loss on drying and incineration by SEM and EDS. The evaluation of the potential occlusion of dentinal tubules was performed using samples obtained from bovine teeth that were prepared to present exposure of the root dentin. 84 samples were used and divided according to the type of dentifrice used: Groups with negative control toothpaste without abrasive (DCNS), negative control toothpaste with abrasive (DCNC), experimental WCS (DEW), experimental HS (DEH), commercial toothpaste Colgate Sensitive Pro Relief™ (DCPA) and Sensodyne Fast Relief ™ toothpaste (DSRA). All samples were their own controls since the tests were performed before and after simulated toothbrushing. Tests of surface roughness, dentin permeability, X-ray diffraction, micro-Raman spectroscopy, atomic force microscopy and scanning electron microscopy and microanalysis by energy dispersive spectroscopy were performed. Characterization of hydroxyapatite nanoparticles showed that they were nanosized particles and presented chemical properties consistent with those of hydroxyapatite. These particles were not cytotoxic to human gingival fibroblasts when at low concentrations. The dentifrices showed adequate values of pH, consistency, density and loss on drying. The analysis of the residue showed that the toothpaste had the chemical components used in the formulations. Surface roughness was statistically different between DEW and DSRA group (p < 0.05), but no group showed a high value of surface roughness, which was demonstrated by atomic force microscopy. The dentin permeability was significantly reduced (p ˂ 0.05) for groups DEW, DEH and DSRA. The X-ray diffraction showed peaks for DEH crystallinity of greater intensity corresponding to calcium spectroscopy. The micro-Raman microanalysis and EDS showed that the toothpaste had the chemical components used in its formulation, being found in the same sample surfaces after brushing. The SEM images showed that there were variations on the dentin surface morphology, in which occlusion of dentinal tubules occured, being the DSRA the only group to show total occlusion. The experimental dentifrices showed potential for occlusion of dentinal tubules similar to those of commercially available produc ts. / Dentifrícios dessensibilizantes que promovem a oclusão dos túbulos dentinários mostraram-se eficazes no tratamento da hipersensibilidade dentinária. O objetivo deste trabalho foi desenvolver e avaliar dentifrícios dessensibilizantes contendo nanopartículas de hidroxiapatita. O estudo in vitro foi realizado em três etapas: síntese e caracterização das nanopartículas de hidroxiapatita; formulação e caracterização dos dentifrícios e avaliação do potencial da oclusão dos túbulos dentinários. A obtenção das nanopartículas de hidroxiapatita foi feita por meio da síntese química por via úmida a 37º C, com a qual se elaborou a nanopartícula de hidroxiapatita WCS e síntese hidrotérmica a 180º C (HS). A caracterização foi realizada por meio de microscopia eletrônica de varredura, microanálise por espectroscopia por dispersão de energia, difração de raio-X, espectroscopias na região do infravermelho com transformada de Fourier e micro-Raman, análise térmica, avaliação de citotoxicidade. Foram formulados quatro dentifrícios experimentais e comparados com dois comerciais. Realizou-se a caracterização e controle de qualidade destes dentifrícios por meio da avaliação do pH, da consistência, densidade, análise da perda por dessecação e incineração e por MEV e EDS. A avaliação do potencial de oclusão dos túbulos dentinários foi realizada usando-se amostras obtidas de dentes bovinos que foram preparadas para apresentarem exposição da dentina radicular. Foram usadas 84 amostras que foram divididas de acordo com o tipo de dentifrício utilizado: Grupos com dentifrício controle negativo sem abrasivo (DCNS), controle negativo com abrasivo (DCNC), experimental WCS (DEW), experimental HS (DEH), dentifrício comercial Colgate® Sensitive Pró Alívio™ (DCPA) e dentifrício comercial Sensodyne® Rápido Alívio™ (DSRA). Todas as amostras foram seus próprios controles já que foram realizados os testes antes e após escovação simulada. Foram realizados testes de rugosidade superficial, permeabilidade dentinária, difração de raio-X, espectroscopia micro-Raman, microscopia de força atômica e eletrônica de varredura e microanálise espectroscopia por dispersão de energia. A caracterização das nanopartículas de hidroxiapatita mostrou que se tratava de partículas nanométricas e com propriedades químicas compatíveis com hidroxiapatita. Estas partículas não foram citotóxicas a fibroblastos gengivais humanos quando em baixas concentrações. Os dentifrícios apresentaram valores adequados de pH, consistência, densidade e perda por dessecação. A análise dos resíduos demonstrou que os dentifrícios apresentaram os componentes químicos usados nas formulações. A rugosidade superficial foi diferente estatisticamente (p˂0,05) entre o grupo DEW e DSRA, porém nenhum grupo apresentou alto valor de rugosidade superficial, o que se comprovou com a microscopia de força atômica. A permeabilidade dentinária foi reduzida significativamente (p˂0,05) para os grupos DEW, DEH e DSRA. A difração de raio-X apresentou para o DEH os picos de maior intensidade de cristalinidade correspondentes ao cálcio. A espectroscopia micro-Raman e a microanálise por EDS mostraram que os dentifrícios apresentavam os componentes químicos usados em sua formulação, sendo os mesmo encontrados nas superfícies das amostras após a escovação. As imagens de MEV mostraram que houve variações morfológicas sobre a superfície dentinária, nas quais houve oclusão de túbulos dentinários, sendo o DSRA o único a apresentar oclusão total. Os dentifrícios experimentais apresentaram potencial de oclusão de túbulos dentinários semelhantes aos produtos comerciais.

Orientador: Alberto Carlos Botazzo Delbem / Banca: Paulo Carvalho Tobias Duarte / Banca: Adelisa Rodolfo Ferreira Tiveron / Banca: Cristina Duque / Banca: Marcelle Danelon / Resumo: O objetivo deste estudo foi avaliar a capacidade de dentifrícios convencionais (1100 ppm F) suplementados com hexametafosfato de sódio (HMP), em reduzir a desmineralização do esmalte in vitro e in situ. No estudo in vitro blocos de esmalte bovino (n = 60) selecionados pela dureza de superfície inicial (SHi) foram divididos em cinco grupos de dentifrícios (n = 12): sem fluoreto e sem HMP (Placebo); um convencional de 1100 ppm F (1100F); 1100 ppm F associado 0.5% de HMP (1100FHMP0.5%), 1100 ppm F associado a 1% de HMP (1100FHMP1%) e 1100 ppm F associado a 2% HMP (1100FHMP2%). Os blocos foram submetidos a ciclagem de pH durante cinco dias, sendo o tratamento com os respectivos dentifrícios realizados 2x/dia. A seguir, determinou-se a dureza de superfície final (SHf) e a perda de dureza de superfície (%SH), perda da dureza integrada de subsuperfície (ΔKHN), a dureza diferencial integrada (ΔIH) e fluoreto (F) no esmalte. Os resultados foram submetidos à análise de variância seguida pelo teste Student-Newman-Keuls (p < 0,001). O grupo 1100FHMP1% apresentou a menor perda mineral (%SH, ΔKHN e ΔIH) seguido pelo grupo 1100FHMP0.5% (p < 0,001). O grupo 1100FHMP1% apresentou a mesma concentração de F no esmalte do grupo 1100. Para o estudo in situ, blocos de esmalte bovinos (n = 144) foram selecionados pela dureza de superfície e divididos em três grupos experimentais: Placebo (placebo), 1100 ppm F (1100F), 1100 ppm F associado a 1% de HMP (1100FHMP1%). Doze voluntários utilizaram dispositivos palatinos, com quatro blocos de esmalte, durante sete dias para cada fase, sendo a escovação realizada 3x/dia com o dispositivo palatino no interior da cavidade bucal e o desafio cariogênico com sacarose 30% em horários pré-estabelecidos. Após o período de 7 dias determinou-se %SH, ΔKHN e os níveis de fluoreto (F), cálcio (Ca) e fósforo (P) no esmalte... / Abstract: The objective of this study was to evaluate the ability of conventional dentifrices (1100 ppm F) supplemented with sodium hexametaphosphate (HMP), in reducing enamel demineralization in vitro and in situ. In the study of demineralization of bovine enamel blocks (n = 60) selected by the initial surface hardness (SHI) were divided into five groups of dentifrices (n = 12) without fluoride and HMP without (Placebo); conventional dentifrice 1100 ppm F (1100F); 1100 ppm F associated 0.5% of HMP (1100FHMP0.5%), 1100 ppm F associated 1% of HMP (1100FHMP1%) and 1100 ppm F associated 2% of HMP (1100FHMP2%). The blocks were subjected to pH cycling for five days, and then treatment performed with the respective dentifrices 2x / day. Next, we determined final surface hardness (SHf), surface hardness loss (% SH), integrated differential hardness (ΔIH) and integrated loss of subsurface hardness (ΔKHN) and fluoride (F) in the enamel. The results were submitted to one-way ANOVA followed by the Student-Newman-Keuls test (p <0.001). The group 1100FHMP1% had the lowest mineral loss (SH%, ΔKHN and ΔIH) followed in 1100FHMP0.5% (p <0.001). 1100FHMP1% group had the same concentration of 1100 ppm F in group F. For the study of enamel in situ bovine enamel blocks (n = 144) were selected for the surface hardness and divided into three groups: Placebo (placebo), 1100 ppm F (1100F), 1100 ppm F associated 1% of HMP (1100FHMP1%). Twelve volunteers wore palatal appliances with four enamel blocks for seven days, and brushing performed 3x / day with the palatal device within the oral cavity and the cariogenic challenge with sucrose 30% at pre-established times. After 7 days, SH% was determined, ΔKHN and fluoride (F), calcium (Ca) and phosphorus (P) in enamel. The biofilms formed were analyzed for the concentration of F, Ca, P and extracellular polysaccharide (EPS)... / Doutor

Orientador: Alberto Carlos Botazzo Delbem / Banca: Cinthia Pereira Machado / Banca: Marília Afonso Rabelo Buzalaf / Banca: Alberto Carlos Botazzo Delbem / Resumo: Dentifrícios com concentração reduzida de flúor podem oferecer menor risco à fluorose dentária, porém sua efetividade deve ser mantida. O objetivo deste estudo in vitro foi avaliar o potencial anticárie a abrasividade de dentifrícios fluoretados com pH ácido. Para isso, foram utilizados 240 blocos de esmalte bovino, selecionados pela microdureza de superfície e dentifrícios experimentais contendo 0 (placebo), 275, 412, 550 e 1100 mg F/g (pH 7,0 e 4,5) e comerciais Crest® (1100 mg F/g, padrão) e Colgate Baby® (500 mg F/g). Blocos de esmalte (n=120) foram submetidos à ciclagem de pH e ao tratamento (2x/dia) com suspensão de dentifrícios. Em seguida, calculou-se a variação da microdureza de superfície, o conteúdo mineral e a quantidade de flúor, cálcio e fósforo no esmalte e nas soluções após a ciclagem. Para o teste de abrasividade (n=120) dos dentifricios utilizou-se maquina de escovacao e posterior analise perfilometrica. Os blocos de esmalte tratados com dentifricios acidos apresentaram menor perda mineral (ANOVA; p<0,05) quando comparados aos neutros. Os dentifricios 412 e 550 uÊg F/g acidos apresentaram resultados semelhantes (p>0,05) aos dos dentifricios 1100 uÊg F/g neutro e Crest. Houve correlacao positiva (Pearson; p<0,05) entre as concentracoes de fluor nos dentifricios, no esmalte e nas solucoes, com tambem com o fosforo presente nas solucoes. A abrasividade dos dentifricios acidos foi semelhante (p>0,05) a dos neutros e os comerciais apresentaram menor abrasao (p<0,05). Conclui-se que os dentifricios com 412 e 550 mg F/g acidos possuem acao anticariogenica semelhante a do Crest e que o pH nao influência a abrasividade dos dentifrícios. / Abstract: Low-fluoride dentifrices may reduce the risk to enamel fluorosis; however, their effectiveness must be maintained. This in vitro study evaluated the anticariogenic potential and abrasiveness of acidic fluoride dentifrices. Enamel bovine blocks (n=240) were selected according to their surface microhardness and divided into groups containing 0 (placebo), 275, 412, 550 and 1,100 mg F/g (pH 4.5 or 7.0). Two commercial dentifrices were also studied: Crest (positive control) and Colgate Baby (500 mg F/g). Enamel blocks (n=120) were submitted to pH cycling and treatment (2 times/day) with dentifrice slurries. Variations in surface microhardness, mineral content and amount of fluoride, calcium and phosphate in enamel and slurries after pH cycling were calculated. Enamel blocks (n=120) and an automated toothbrushing machine were used to test dentifrice abrasiveness, which was evaluated by profilometry. Enamel blocks treated with acidic dentifrices exhibited less mineral loss compared to those exposed to neutral dentifrices (ANOVA; p<0.05). Acidic dentifrices with 412 and 550 ìg F/g presented similar outcomes (p>0.05) as neutral dentifrice with 1100 ìg F/g and Crest. Positive correlation (Pearson; p<0.05) was found between fluoride concentration in dentifrices and in enamel and slurry, as well as phosphate in slurries. The abrasiveness of acidic dentifrices was similar (p>0,05) to the neutral, whereas commercial dentifrices yielded lower abrasion (p<0.05). It was concluded that acidic dentifrices with 412 and 550 ìg F/g had the same anticariogenic action as the positive control. The pH had no influence on dentifrice abrasiveness. / Mestre

Orientador: Denise Pedrini / Coorientador: Alberto Carlos Botazzo Delben / Banca: Cristiane Duque / Banca: Robson Frederico Cunha / Banca: Carla Oliveira Favretto / Banca: Mariana Emi Nagata / Resumo: Este estudo in vitro avaliou o efeito de dentifrício fluoretado (F) contendo ou não hexametafosfato de sódio (HMP) em inibir ou reparar a erosão inicial do esmalte. Blocos de esmalte bovino hígido (n=48) e desmineralizado (n=48) foram selecionados por dureza superficial inicial e submetidos a 4 grupos experimentais (12 blocos/grupo): Placebo (sem F e HMP), 1100 ppm F, 1% HMP e 1100 ppm F + 1% HMP. Para a análise do efeito protetor, os blocos de esmalte hígido foram imersos uma única vez em solução de dentifrícios com saliva humana por 2 minutos. Em seguida, os blocos foram submetidos a 4 desafios erosivos com ácido cítrico (0,75%, pH 3,5) por 1 minuto, sob agitação. A percentagem de variação da dureza superficial (%SH) foi calculada após os tratamentos e pós desafios ácidos de 1, 2, 3 e 4 minutos. Para a análise do efeito reparador, o esmalte desmineralizado foi tratado e submetido aos mesmos desafios erosivos, como descritos anteriormente. A partir de então, %SH foi calculada após a desmineralização, tratamentos e desafios ácidos de 1, 2, 3 e 4 minutos. Experimento adicional foi realizado para análise da deposição de precipitados por microscopia eletrônica de varredura (MEV) em esmalte desmineralizado. Os dados foram submetidos à análise de variância de medidas repetidas a dois critérios, seguida pelo teste de Student-Newman-Keuls (p<0,05). Os resultados mostraram que o grupo placebo apresentou a menor capacidade de inibir e reparar a erosão do esmalte (p<0,001). A perda de ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: This in vitrostudy evaluated the effect of fluoride (F) toothpaste containing or not sodium hexametaphosphate (HMP) in inhibit or repair initial enamel erosion. Sound (n=48) and demineralized (n=48) bovine enamel blocks were selected by initial surface hardness and subjected to 4 experimental groups(12 blocks/group): Placebo (without F and HMP), 1100 ppm F, 1% HMP and 1100 ppm F + 1% HMP. For the analysis of the protective effect, sound enamel were immersed in toothpaste slurry in human saliva once for 2 minutes. Hereafter, enamel blocks were submitted to 4 erosive challenges in citric acid (0.75%, pH 3.5) by 1 minute, under stirring. Percentage of surface hardness change (%SH) was calculated after treatmentsand 1, 2, 3 and 4 minutes. For the analysis of the repair effect, demineralized enamel were treated and submitted to erosive challenges as describe previously. Hereafter, %SH was calculated after demineralization, treatmentsand 1, 2, 3 and 4 minutes. Additional experimental was performed to analysis the deposition ofprecipitates by scanning electronic microscopy (SEM) on demineralized enamel. Variables were submitted to two-way repeated measures analysis of variance followed by Student-Newman-Keuls test (p<0.05). The results showed that the Placebo group had the lowest capacity to inhibit and repair enamel erosion (p<0.001). Hardness loss increased during repeated acid challenges for all groups; however the effect against erosion of F/HMP toothpaste proved to be more resi... (Complete abstract click electronic access below) / Doutor

Made available in DSpace on 2014-06-11T19:23:33Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-05-06Bitstream added on 2014-06-13T19:09:25Z : No. of bitstreams: 1 cordeiro_chg_me_arafcf.pdf: 668360 bytes, checksum: 6006843241d7fb47bcd17a5594004e3c (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Universidade Estadual Paulista (UNESP) / A utilização de produtos naturais na medicina popular é milenar e persiste até os dias atuais. Sua abrangência é vasta e engloba fins variados, inclusive em relação à saúde bucal. O controle do biofilme bacteriano dentro das diversas especialidades odontológicas é de grande importância, pois aponta para a prevenção de várias afecções bucais. Quando a remoção mecânica do biofilme é deficiente, podem ocorrer lesões de tecido duro (cáries) e/ou mole (doenças periodontais). A eficácia de plantas medicinais, tanto em dentifrícios como em enxagüatórios bucais, tem sido investigada. Os resultados têm sugerido que os componentes de origem vegetal podem ser empregados como apoio à terapia das doenças periodontais e como profilaxia de rotina. Este trabalho teve como objetivos avaliar a ação biológica de formulações para higiene bucal, contendo, em associação, extratos hidroalcoólicos das espécies vegetais Nasturtium officinale (agrião), Rosmarinus officinalis (alecrim), Tabebuia impetiginosa (ipê roxo), Achillea millefolium (mil-folhas) e Plantago major (tanchagem). Trabalhos anteriores sugerem possível efeito antiinflamatório e alteração da qualidade do biofilme dento-bacteriano, devido as substâncias ativas desses vegetais. Após os estudos de pré-formulação e obtenção do gel dentifrício e do enxagüatório bucal, foram realizadas avaliações da atividade antibacteriana (frente à Staphylococcus aureus, Bacillus subtilis, Escherichia coli, Enterococcus faecalis e Pseudomonas aeruginosa), atividade antiinflamatória e imunológica, para os extratos vegetais e para as formulações. E foram ainda realizados estudos clínicos iniciais, considerando-se os parâmetros odontológicos para a avaliação do Índice de placa, Índice Gengival, Recessão Gengival e... . / The use of natural resources in popular medicine is a millenary practice and it persists until nowadays. This habit is embracing and wide and it conglomerates multiple purposes, included those related to oral health. It’s very important to control bacterial film in many odontologic specialties, because this control helps to prevent several oral diseases. When the mechanical removal of the bacterial film is inefficient, there can occur hard tissue lesions (carious lesions) and/or soft tissue lesions (periodontal diseases) The effectiveness of medicinal herbs in dentifrices, as well as in mouthwashs have been investigated. The results have suggested that the herbs components can be utilized as a support in the periodontal diseases therapies and in the routine prophylaxis. It was the purpose of the present study to evaluate the biological action of various formulations to bucal hygiene, containing, in association, hidroalcoholic extracts from the following species: Nasturtium officinale, Rosmarinus officinalis, Tabebuia impetiginosa, Achillea millefolium and Plantago major. Previous works suggested that there are possible anti-inflammatory effects and an alteration of the bacterial dental film quality, due to the active substances of these herbs. After studying a previous formulation and obtaining the dentifrice and the mouthrinse, it was evaluated the bacterial activity (related to Staphylococcus aureus, Bacillus subtilis, Escherichia coli, Enterococcus faecalis and Pseudomonas aeruginosa), the antiinflammatory and the immunological activities, for the herbs extracts and for the formulations... (Complete abstract, click electronic address below).

Orientadora: Marcelle Danelon / Coorientador: Alberto Carlos Botazzo Delbem / Banca: Gustavo Sivieri de Araújo / Banca: Sandra Maria Herondina Coelho Avila de Aguiar / Banca: Francisco Nunes de Souza Neto / Banca: Daniela Coêlho de Lima / Resumo: O objetivo geral deste estudo foi avaliar o efeito de um dentifrício fluoretado convencional (1100 ppm F), contendo nanopartículas de hexametafosfato de sódio (HMPnano) sobre a remineralização de lesões artificiais de cárie e desmineralização do esmalte in situ e biofilme. O estudo de remineralização, foi duplo-cego cruzado, realizado em quatro fases de três dias cada. Voluntários (n=12) usaram dispositivos palatinos contendo quatro blocos de esmalte bovino com lesões artificiais de cárie. A seguir foram distribuídos aleatoriamente nos seguintes grupos de tratamento: sem F/HMP/HMPnano (Placebo); 1100 ppm F (1100F); 1100F associado a 0,5% HMP microparticulado e nanoparticulado (1100F/HMP; 1100F/HMPnano). Os voluntários foram instruídos a escovar seus dentes naturais com os dispositivos palatinos na boca durante 1 min (3x/dia), de modo que os blocos foram tratados com slurry de dentifrícios. Após cada fase, determinou-se a porcentagem de recuperação de dureza de superfície (%SHR), recuperação integrada de dureza de subsuperfície (ΔIHR), recuperação mineral integrada (ΔIMR) e concentração de fluoreto (F) no esmalte. Os resultados foram submetidos a análise de variância de medidas repetidas seguido pelo teste Student-Newman-Keuls (p < 0,001). A superfície do esmalte tornou-se 68% mais remineralizada quando tratada com 1100F/HMPnano em comparação com 1100F (p < 0,001). O tratamento com 1100F/HMP e 1100F/HMPnano promoveu um aumento em ~ 23% e ~ 87% da ΔIHR quando comparado ao 1100F... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to evaluate the effect of a conventional fluoride toothpaste (1100 ppm F) containing nano-sizeds of sodium hexametaphosphate (HMPnano) on the remineralization of artificial caries lesions and enamel demineralization and biofilm in situ. The remineralization study was double-blinded crossed, performed in 4 phases of 3 days each. Volunteers (n = 12) used palatal devices containing four blocks of bovine enamel with artificial lesions of caries. They were then randomly assigned to the following treatment groups: without F/ HMP/HMPnano (Placebo); 1100 ppm F (1100F); 1100F associated with 0.5% HMP microparticulate and nano-sized (1100F/HMP; 1100F/ HMPnano). The volunteers were instructed to brush their natural teeth with the palatine devices in the mouth for 1 min (3x/day), so that the blocks were treated with slurry of toothpastes. After each phase, the percentage of surface hardness recovery (%SHR), integrated recovery of subsurface hardness (ΔIHR), integrated mineral recovery (ΔIMR) and fluoride (F) concentration in the enamel were determined. The results were subjected to analysis of variance of repeated measures followed by Student-Newman-Keuls test (p < 0.001). The enamel surface became 68% more remineralized when treated with 1100F/ HMPnano compared to 1100F (p < 0.001). Treatment with 1100F/HMP and 1100F/ HMPnano promoted an increase in ~ 23% and ~ 87% of ΔIHR when compared to 1100F (p < 0.001). In addition, ΔIMR was ~ 75% and ~ 33% higher for 1100F/HMPnano when compared to 1100F and 1100F/HMP, respectively (p < 0.001). The study of demineralization was double-blinded crossed, and consisted of four phases (7 days each). Volunteers (n = 12) used palatal appliances containing four blocks of bovine enamel. The cariogenic challenge was accomplished by the solution of sucrose 30% (6x/day). Treatments with the toothpaste (3x/day) were... / Doutor

Orientador : Alberto Carlos Botazzo Delbem / Resumo: O objetivo do presente trabalho foi verificar o efeito da saliva artificial como meio de diluição dos dentifrícios em ciclagem de pH, para validar a comparação entre dentifrícios experimentais e dentifrícios suplementados com cálcio e fosforo e, em seguida, avaliar a efetividade de dentifrícios suplementados com cálcio e fosforo e com concentração baixa de flúor utilizando um modelo de ciclagem de pH. Na primeira parte do trabalho realizou-se 2 ciclagens de pH: uma onde os dentifrícios foram diluidos em água destilada/deionizada e, na outra em saliva artificial. Os blocos de esmalte, previamente selecionados através de microdureza de superfície, foram submetidos ao tratamento diário, na segunda parte do trabalho, com dentifrício placebo, 275, 550, 450-s, 1100, 1000-s ppm F e Crest, sendo estes diluidos em saliva artificial e submetidos a ciclagem de pH. Em seguida, realizou-se o calculo da variação da microdureza de superfície, percentagem de volume mineral e flúor presente no esmalte...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The object of this study was to check the effect of the artificial saliva as a means of diluting the dentifrices in pH cycling, to validate the comparison among the experimental dentifrices and dentifrices supplemented with calcium and phosphate, and then, to assess the effectiveness of dentifrices supplemented with calcium and phosphate and with a low fluoride concentration, using a pH cycling model. In the first part of the study, 2 pH cyclings were performed: one in which the dentifrices were diluted in distilled/deionized water, and in the other, in artificial saliva. The enamel blocks, previously selected through surface microhardness, were submitted to daily treatment in the second part of the study, with dentifrice placebo 275, 550, 450-S, 1100, 1000-S ppm F and Crest, and these were diluted in artificial saliva and submitted to pH cycling. Next, the calculation was made of the variation in surface microhardness, percentage of mineral volume and fluoride present in the enamel. Parametric and non-parametric tests and regression analyses were used to determine the difference (p<0.05) and the dose-response...(Complete abstract click electronic access below) / Doutor

Submitted by GIOVANNA DALPASQUALE null (gidalpasquale@hotmail.com) on 2016-03-09T22:35:34Z No. of bitstreams: 1 Dissertação Giovanna orginal 20.02.16.pdf: 1617739 bytes, checksum: e6b4c4a1b128f5c70b099c958cbd5ddf (MD5) / Approved for entry into archive by Juliano Benedito Ferreira (julianoferreira@reitoria.unesp.br) on 2016-03-10T19:54:27Z (GMT) No. of bitstreams: 1 dalpasquale_g_me_araca.pdf: 1617739 bytes, checksum: e6b4c4a1b128f5c70b099c958cbd5ddf (MD5) / Made available in DSpace on 2016-03-10T19:54:27Z (GMT). No. of bitstreams: 1 dalpasquale_g_me_araca.pdf: 1617739 bytes, checksum: e6b4c4a1b128f5c70b099c958cbd5ddf (MD5) Previous issue date: 2016-02-19 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Objetivo: Este estudo avaliou o efeito de dentifrícios contendo 1100 ppm F associado a nanopartículas de hexametafosfato de sódio (HMPnano) sobre a desmineralização do esmalte in vitro, utilizando um modelo de ciclagem de pH. Desenho: Blocos de esmalte bovino (4 mm x 4 mm, n=72) selecionados pela dureza de superfície inicial (SHi), foram alocados em seis grupos (n=12), de acordo com os dentifrícios teste: sem flúor ou HMPnano (Placebo), 550 ppm F (550F), 1100 ppm F (1100F), 1100F acrescido de HMPnano nas concentrações de 0,25% (1100F/0,25%HMPnano), 0,5% (1100F/0,5%HMPnano), e 1,0% (1100F/1,0%HMPnano). Blocos foram tratados 2x/dia com suspensões de dentífricios e submetidos a cinco ciclagens de pH (soluções desmineralizante/remineralizante) a 37 °C. A seguir, dureza de superfície final (SHF), perda integrada de dureza de subsuperfície (ΔKHN), concentração mineral (gHAp×cm-3) e concentração de fluoreto (F) no esmalte foram determinadas. Os dados foram submetidos à ANOVA seguido pelo teste Student-Newman-Keuls (p < 0,001). Resultados: Dentifrício com 1100F/0,5%HMPnano levou à menor perda mineral e maior concentração mineral em relação aos demais grupos (p < 0,001), que foram de 26% (SHF) e 21% (ΔKHN) inferior e ~ 58% maior (gHAp × cm-3) quando comparado ao 1100F (p < 0,001). Foram observados valores similares de F no esmalte para todos os dentifrícios fluoretados (p > 0,001). Conclusão: A adição de 0,5%HMPnano ao dentifrício 1100F aumenta significativamente os seus efeitos anticárie quando comparado com o seu equivalente sem HMPnano. / This study evaluated the effect of toothpastes containing 1100 ppm F associated with nano-sized sodium hexametaphosphate (HMPnano) on enamel demineralization in vitro, using a pH-cycling model. Design: Bovine enamel blocks (4 mm x 4 mm, n=72) selected by the initial surface hardness (SHi) were allocated into six groups (n=12), according to the test toothpastes: without fluoride or HMPnano (Placebo), 550 ppm F (550F), 1100 ppm F (1100F), 1100F plus HMPnano at concentrations of 0.25% (1100F/0.25%HMPnano), 0.5% (1100F/0.5%HMPnano), and 1.0% (1100F/1.0%HMPnano). Blocks were treated 2x/day with slurries of toothpastes and submitted to five pH cycles (demineralizing/remineralizing solutions) at 37 °C. Next, final surface hardness (SHf), integrated loss subsurface hardness (ΔKHN), enamel mineral concentration (gHAp×cm-3 ) and enamel fluoride (F) concentration were determined. Data were analyzed by ANOVA and Student-Newman-Keuls’ test (p < 0.001). Results: Toothpaste with 1100F/0.5%HMPnano led to the lowest mineral loss and the highest mineral concentration among all groups, which were 26% (SHf) and 21% (ΔKHN) lower and ~58% higher (gHAp×cm-3 ) when compared to 1100F (p < 0.001). Similar values of enamel F were observed for all fluoridated toothpastes (p > 0.001). Conclusion: The addition of 0.5%HMPnano to a 1100F toothpaste significantly enhances its anticaries effects when compared to its counterpart without HMPnano.