Made available in DSpace on 2014-10-09T12:26:37Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:04:21Z (GMT). No. of bitstreams: 0 / Dissertacao (Mestrado Profissionalizante em Lasers em Odontologia) / IPEN/D-MPLO / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP; Faculdade de Odontologia, Universidade de Sao Paulo, Sao Paulo

Made available in DSpace on 2014-10-09T12:32:57Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:06:10Z (GMT). No. of bitstreams: 1 17894.pdf: 2451441 bytes, checksum: a74787cbf4366c714393f0684a412955 (MD5) / Dissertacao (Mestrado Profissionalizante em Lasers em Odontologia) / IPEN/D-MPLO / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP; Faculdade de Odontologia, Universidade de São Paulo, São Paulo

Submitted by Lana Kei Yamamoto de Almeida null (lanakei@yahoo.com.br) on 2018-02-19T02:56:34Z No. of bitstreams: 1 Dissertação_Lana Kei Y. Almeida.pdf: 1649494 bytes, checksum: cf989b1c447cf66da3c31a3a2e9896fc (MD5) / Approved for entry into archive by Ana Cristina Jorge null (anacris@fclar.unesp.br) on 2018-02-19T18:54:54Z (GMT) No. of bitstreams: 1 almeida_lky_me__arafo_ int.pdf: 1535802 bytes, checksum: a92c9105082146daf4863bcb47d187ac (MD5) / Made available in DSpace on 2018-02-19T18:54:54Z (GMT). No. of bitstreams: 1 almeida_lky_me__arafo_ int.pdf: 1535802 bytes, checksum: a92c9105082146daf4863bcb47d187ac (MD5) Previous issue date: 2018-02-05 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Os defeitos de esmalte são alterações pouco estudadas na dentição decídua, apesar de acarretarem problemas como sensibilidade dentária, estética indesejável e aumento do risco ao desenvolvimento da cárie dentária. O objetivo deste estudo foi identificar a prevalência de defeitos no esmalte dentário na dentição decídua de escolares de Araraquara/SP. Foi realizado o exame clínico em crianças de 4 anos (n=656), para o registro dos seguintes índices: fluorose dentária (FD) (TF, 1978), cárie dentária (OMS, 1997), hipomineralização de molar decíduo (HMD) (Elfrink et al., 2012), defeitos de desenvolvimento de esmalte não-fluoróticos (FDI, 1992), erosão dentária (Bartlett et al., 2008) e atrição dentária (Pullinger e Seligman, 1993). Dois questionários estruturados foram respondidos pelos pais/responsáveis dos escolares, com intuito de identificar a condição socioeconômica, o histórico médico/odontológico, além do histórico comportamental e de hábitos alimentares. Os dados foram coletados no período de março a novembro/2017 e foram analisados por meio do programa SPSS 17.0 for Windows. A estatística descritiva foi utilizada para verificar a prevalência dos defeitos de esmalte e a relação com as outras variáveis propostas através do teste Qui-quadrado, ao nível de significância de 0,05, sendo as associações verificadas pelo Odds Ratio. Os resultados deste estudo mostraram que, dentre os defeitos de desenvolvimento do esmalte dentário, a FD foi a mais prevalente (6,1%, n=40), seguida pela HMD (5,6%, n=37) e Opacidade localizada (4,1%, n=27). Dentre os defeitos adquiridos, a atrição foi a lesão mais prevalente (36,9%, n=242), seguida pela erosão (2,4%, n=16). Ao avaliar os fatores etiológicos relacionados à manifestação dos defeitos de desenvolvimento dentário nas crianças, as seguintes variáveis apresentaram associação: amamentação não exclusiva pelo leite materno (p=0,003) e icterícia ao nascimento (p<0,001). Com relação aos defeitos de esmalte adquiridos e seus fatores relacionados, verificou-se uma associação significante com episódios frequentes de vômitos (p=0,037). Nenhuma associação foi observada com relação aos fatores socioeconômicos. Conclui-se que a prevalência geral dos defeitos de esmalte na dentição decídua na cidade de Araraquara-SP foi de 48,6%, sendo considerado um valor relevante, visto que o conhecimento destes dados possibilita a instituição de uma conduta preventiva ao paciente afetado por essas alterações. / Enamel defects are alterations that have not been extensively studied in primary dentition, in spite of causing problems such as tooth sensitivity, undesirable esthetic appearance and increased risk for developing dental caries. The aim of this study was to identify the prevalence of tooth enamel defects in primary dentition of schoolchildren in Araraquara, SP, Brazil. Clinical exams were performed in 4-year-old children (n=656), to record the following indexes: dental fluorosis (DF) (TF, 1978), dental caries (WHO, 1997), deciduous molar hypomineralization (DMH) (Elfrink et al., 2012), developmental enamel defects not related to fluorosis (FDI, 1992), tooth erosion (Bartlett et al., 2008) and dental attrition (Pullinger and Seligman, 1993). Two structured questionnaires were answered by the parents/guardians of the schoolchildren, with the purpose of identifying their socioeconomic condition, medical/dental history, behavioral history and dietary habits. The data were collected in the period from March to November 2017, and were analyzed by means of the program SPSS 17.0 for Windows. Descriptive statistics were used to verify the prevalence of enamel defects and the relationship with the other variables proposed, by means of the Chi-square test, at the level of significance of 0.05, with the associations being verified by the Odds Ratio. The results of this study showed that among the developmental dental enamel defects, DF was the most prevalent (6.1%, n=40), followed by DMH (5.6%, n=37) and localized opacity (4.1%, n=27). Among the acquired defects, attrition was the most prevalent lesion (36.9%, n=242), followed by erosion (2.4%, n=16). When evaluating the etiologic factors related to the manifestation of developmental dental defects in the children, the following variables presented association: not being exclusively breastfeeding (p=0.003) and jaundice at birth (p<0.001). As regards acquired enamel defects and their related factors, a significant association was verified with frequent episodes of vomiting (p=0.037). No association with socioeconomic factors was observed. The authors concluded that the general prevalence of enamel defects in primary dentition in the city of Araraquara, SP was 48.6%. This was considered a relevant value, considering that the knowledge of these data made it possible to institute preventive measures for the patients affected by these alterations.

Submitted by JOSÉ GUILHERME NEVES null (zehgui@hotmail.com) on 2016-07-06T19:38:02Z No. of bitstreams: 1 3 Dissertaçao Guilherme.pdf: 1305881 bytes, checksum: 91f920277ae6853940c08ab27482fc12 (MD5) / Approved for entry into archive by Ana Paula Grisoto (grisotoana@reitoria.unesp.br) on 2016-07-06T20:00:11Z (GMT) No. of bitstreams: 1 neves_jg_me_araca.pdf: 1305881 bytes, checksum: 91f920277ae6853940c08ab27482fc12 (MD5) / Made available in DSpace on 2016-07-06T20:00:11Z (GMT). No. of bitstreams: 1 neves_jg_me_araca.pdf: 1305881 bytes, checksum: 91f920277ae6853940c08ab27482fc12 (MD5) Previous issue date: 2016-07-04 / Objetivo: Esse estudou avaliou a capacidade de adsorção do hexametafosfato de sódio (HMP) em diferentes concentrações no esmalte dentário. Desenho: Blocos de esmalte bovino (4 mm x 4 mm, n=144, 12/grupo) foram selecionados e divididos em 12 grupos: 0%; 0,25%; 0,5%; e 1% HMP, e essas concentrações de HMP seguida da aplicação em solução contendo Ca ou Ca-PO4 Os tratamentos foram realizados por 1 min (1 mL/bloco), e a seguir expostos ao ar para que houvesse a formação de película. A energia livre de superfície (mN/m) foi calculada pela medida dos ângulos de contato de três líquidos sondas: água deionizada, diiodometano e etileno glicol; determinando os componentes polar e apolar da superfície do esmalte. Analisaram-se as concentrações de cálcio (Ca), fosfato (PO4) e HMP nas soluções, antes e após os tratamentos. Os dados apresentaram distribuição normal (Kolmogorov-Smirnov) e homogênea (Cochran) e a seguir foram submetidos a ANOVA seguido pelo teste Student-Newman Keuls (p<0,05). Resultado: Quanto maior a % de HMP nas soluções maior a adsorção de HMP e a eletronegatividade na superfície do esmalte (p<0,05). A adsorção de Ca foi maior com o aumento da % de HMP na solução (p<0,05) reduzindo a eletronegatividade na superfície do esmalte. Maior adsorção de Ca e PO4 ocorreu com 0,5% HMP e 1% HMP após o tratamento com solução Ca-PO4, deixando a superfície menos eletronegativa quando comparado aos demais tratamentos (p<0,05). Conclusão: Conclui-se que o HMP promove uma superfície de esmalte mais eletronegativa favorecendo uma maior adsorção dos íons Ca e PO4. / Objective: This study evaluated the sodium hexametaphosphate (HMP) capacity adsorption at different concentrations in the dental enamel. Design: Bovine enamel blocks (4 mm x 4 mm, n = 144, 12 group) were selected and divided into 12 groups: 0%; 0.25%; 0.5%; and 1% HMP, and these HMP concentrations followed by the application solution containing Ca or Ca-PO4. The treatments were performed for 1 min (1 ml /block), and then exposed to air so that there was the formation of a pelicle. The surface free energy (mN/m) was calculated by measuring the contact angles of liquids three probes: deionized water, diiodomethane and ethylene glycol; determining the polar and nonpolar components of the enamel surface. It was analyzed the calcium (Ca), phosphate (PO4) and HMP in the solutions, before and after treatment. The data were normally distributed (Kolmogorov-Smirnov) and homogeneous (Cochran) and then were subjected to ANOVA followed by Student-Newman Keuls test (p <0.05). Results: The greater HMP % in solutions, the greater adsorption of HMP and electronegative surface enamel (p<0.05). The Ca adsorption was higher with HMP % increasin in the solution (p<0.05) reducing enamel surface electronegativity. Increased adsorption of Ca and PO4 occurred in 0.5% and 1% HMP and HMP after treatment with Ca-PO4 solution, leaving the less electronegative surface when compared to the other treatments (P<0.05). Results: The higher HMP% solutions was greater HMP adsorption and electronegative surface enamel (p<0.05). The Ca adsorption was higher with increasing HMP % in the solution (p<0.05) in reducing electronegativity enamel surface. Increased adsorption of Ca and PO4 occurred in 0.5% and 1% HMP HMP after treatment with Ca-PO4 solution, leaving the less electronegative surface when compared to the other treatments (P <0.05). Conclusion: The HMP promotes more electronegative in enamel surface, achieving greater adsorption of Ca and PO4 ions.

Made available in DSpace on 2016-12-09T13:52:17Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-09-12. Added 1 bitstream(s) on 2016-12-09T13:55:20Z : No. of bitstreams: 1 000867947.pdf: 1292588 bytes, checksum: 47ef895e165a944d27f706ca2af29339 (MD5) / A cor que percebemos do dente é considerada um fenômeno complexo e um crescente número de estudos tem investigado formas de avaliação de cor com o intuito de tornar o procedimento mais preciso e objetivo. Este estudo avaliou a confiabilidade das medidas efetuadas em espectrofotômetro para análise de cor in vitro em esmalte e dentina bovinos. Realizou-se um ensaio laboratorial, duplo-cego. As variáveis dependentes avaliadas foram as coordenadas colorimétricas L*, a* e b*. Essas medidas foram realizadas por um único examinador, em dois momentos distintos. Foram utilizados 100 dentes bovinos por tipo de superfície (esmalte e dentina). Foram construídos gráficos de dispersão do tipo Bland-Altman. A reprodutibilidade intra-examinador das medidas foi estimada por meio do Coeficiente de Correlação Intraclasse (CCI) e seu Intervalo de Confiança (IC95%). A reprodutibilidade intra-examinador mostrou valores de CCI classificados como Muito Bom (CCI ≥ 0,91) para as todas as coordenadas nos dois tipos de espécimes, com exceção da coordenada a* em esmalte bovino, que foi considerada Boa (0,71≤CCI>0,91). Foi possível observar que as leituras relacionadas à luminosidade mostraram menor concordância entre as medidas, seguida da coordenada b* e da a*. Para os parâmetros L* e b*, os limites de concordância foram mais amplos na análise em dentina. Conclui-se que a técnica utilizada para medição de cor em esmalte e dentina de dentes bovinos possuiu adequada confiabilidade, mas sugere-se que estudos nessa área busquem a padronização das amostras e realizem calibração para as leituras. / The tooth color is considered a complex phenomenon and a growing number of studies have investigated ways of evaluating color in order to make this procedure more precise and objective. This study evaluated the reliability of the spectrophotometer measurements for color analysis in vitro on bovine enamel and dentin. It was a laboratory double-blind trial and the dependent variables were the colorimetric coordinates L*, a* and b*. These measurements were performed by a single examiner at two different times. 100 bovine teeth were used for each type of surface (enamel and dentin). Bland-Altman plots were used to analyze agreement. Intra-examiner reproducibility of the measurements was estimated by the Intraclass Correlation Coefficient (ICC) and its confidence interval (CI95%). Intra-examiner reliability showed ICC values classified as Very Good (ICC ≥ 0.91) for all coordinates in both types of specimens, with the exception of coordinated a* in enamel, which was considered Good (0,71 ≤CCI> 0.91). It was observed that the L* readings showed less agreement between measurements, followed by the coordinate b* and a*. For L* and b* parameters, limits of agreement were wider in dentin. We conclude that the technique used for measuring color in enamel and dentin of bovine teeth showed adequate reliability, but it is suggested that studies in this area should standardize the samples and perform calibration before the readings.

Made available in DSpace on 2014-06-11T19:29:32Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-03-06Bitstream added on 2014-06-13T19:17:50Z : No. of bitstreams: 1 000738501.pdf: 2167689 bytes, checksum: ca5a906678957479e48f0ebe5bdfe7ed (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Há evidência de que a suplementação de soluções de bochecho, dentifrícios e vernizes fluoretados com hexametafosfato de sódio (HMP) resulta em um menor desgaste do esmalte dental após um desafio erosivo. Uma vez que a associação entre flúor (F) e HMP ainda não foi testada em géis, o objetivo do presente estudo foi avaliar a ação de géis fluoretados, suplementados ou não com HMP, na erosão do esmalte dentário, associada ou não a abrasão in situ. Voluntários adultos jovens saudáveis (n=12) foram aleatoriamente divididos em 4 grupos, de acordo com os seguintes géis: Placebo (sem F ou HMP), NaF 1%, NaF 2% e NaF 1% + HMP 9%. Os voluntários fizeram uso de dispositivos palatinos contendo 4 discos de esmalte bovino, selecionados após polimento e análise de dureza de superfície. Os discos foram tratados uma única vez com os respectivos géis antes de cada período experimental, os quais tiveram duração de 5 dias, com intervalo de 7 dias entre cada período, seguindo um protocolo duplo-cego e cruzado. O desafio erosivo (ERO) foi realizado nos 4 discos de esmalte, por imersão ex vivo do dispositivo palatino em ácido cítrico pH 3,2 (4x/dia, 5 minutos cada). O desafio abrasivo foi produzido em apenas 2 blocos, imediatamente após os desafios erosivos (ERO+ABR), por meio de escovação com dentifrício fluoretado durante 30 segundos. O desgaste dos blocos foi analisado por perfilometria, enquanto que a perda mineral foi avaliada por meio de análise de dureza de superfície e em secção longitudinal. Os resultados foram analisados por ANOVA a 2 critérios e teste de Student-Newman-Keuls (p<0,05). O gel NaF 1% + HMP 9% promoveu desgaste significativamente menor para ERO em comparação aos demais grupos, sendo estatisticamente menor que os grupos NaF 1% e Placebo para ERO+ABR. Com relação à perda mineral, os menores valores de área integrada da lesão... / There is evidence that the addition of sodium hexametaphosphate (HMP) to fluoridated mouthwashes, toothpastes and varnishes promotes lower enamel wear after erosive challenges. Since the association of fluoride (F) and HMP has not been tested in gels, the aim of this study was to evaluate the effects of fluoride gels, supplemented or not with HMP, on the erosion of tooth enamel, followed or not by abrasion in situ. Twelve healthy young adult volunteers were randomly divided into 4 groups according to the following gels: Placebo (no F or HMP), 1% NaF, 2% NaF, and 1% NaF + 9% HMP. Volunteers wore palatal appliances containing 4 bovine enamel discs, which were selected after polishing and surface hardness analysis. The discs were treated only once with the respective gels prior to each experimental phase, which lasted for five days, with an interval of 7 days between each period. The erosive challenge (ERO) was performed on the 4 enamel discs by ex vivo immersion of the device in citric acid, pH 3.2 (4 times/day, 5 min each). The abrasive challenge was produced in only two blocks immediately after the erosive challenges (ERO+ABR) by brushing the discs for 30 seconds. Enamel wear was analyzed by profilometry, while the mineral loss was assessed by surface and cross-sectional hardness analysis. The results were analyzed by 2-way ANOVA, followed by Student-Newman-Keuls tests (p<0.05). The fluoridated gel supplemented with HMP promoted significantly lower enamel wear for ERO when compared to the other groups, and statistically lower than 1% NaF and Placebo for ERO+ABR. Regarding mineral loss, the lowest values of integrated area of the lesion were found for the 1% NaF + 9% HMP and 2% NaF, respectively for ERO and ERO+ABR. It was concluded that the addition of HMP to the 1% NaF gel led to a higher protective effect against ERO and ERO+ABR when compared to the gel with same F content without HMP. This effect was similar or superior to the 2% NaF gel.

Orientador: Alessandra Bühler Borges / Co-orientador: Carlos Rocha Gomes Torres / Banca: Daniela Rios Honório / Banca: Rebeca Di Nicoló / Banca: Sérgio Eduardo de Paiva Gonçalves / Banca: Valério Costa / Resumo: O objetivo deste estudo foi avaliar os efeitos da escovação, utilizando dentifrícios com diferentes graus de abrasividade após a exposição ao agente clareador peróxido de hidrogênio (PH) 7,5% com ou sem a adição de gluconato de cálcio em diferentes intervalos de tempo (imediatamente e após 1 h). Foi analisada a alteração no tecido dental decorrente destas interações no desgaste de superfície do esmalte. Neste estudo foram utilizados 144 espécimes de esmalte bovino, os quais foram distribuídos em 12 grupos (n = 12) de acordo com o gel clareador utilizado (com e sem cálcio), o grau de abrasividade (alto ou baixo) e o intervalo de tempo decorrido após a utilização do gel clareador (imediatamente e após 1 h). Para o controle, 4 grupos não foram expostos ao gel clareador, apenas passaram pelos ciclos de abrasão, de acordo com o tipo de abrasivo e o intervalo de tempo. O gel clareador foi aplicado por 1 h e após este período, os grupos que foram escovados imediatamente, passaram para o ciclo de abrasão e os do intervalo de 1 h permaneceram na saliva artificial antes da realização dos ciclos abrasivos. Os espécimes foram submetidos a 45 ciclos de escovação, correspondentes a 3x ao dia (135 ciclos por dia - 1 min e 30 s). Estes procedimentos foram repetidos por 7 dias, totalizando 945 ciclos ao final do estudo. O desgaste da superfície do esmalte foi medido (μm) por perfilometria. Para verificação dos resultados foi aplicado o teste ANOVA três fatores e o teste de Tukey. O nível de significância foi de 5%. Foram observadas diferenças estatisticamente significantes (p=0,0001) para os três fatores testados. Os valores de média (± DP) e os resultados do teste de Tukey para o fator clareamento foram: SC- 0,45(± 0,01)a, PH+Ca- 0,51(± 0,03)b, PH- 0,82(± 0,01)c. Para o fator abrasivo, foram: Baixo- 0,44(± 0,01)a e Alto- 0,74(± 0,05)b e para o intervalo de tem... / Abstract: The objective of this study was to evaluate the effects of brushing, using toothpastes with different degrees of abrasiveness after exposure to bleaching agent hydrogen peroxide (HP) 7.5% with or without the addition of calcium gluconate in different time intervals (immediately and after 1 h). The alteration in dental tissue resulting from these interactions on enamel surface wear was analyzed. In this study 144 bovine enamel specimens were divided into 12 groups (n = 12) according to the whitening gel used (with and without calcium), the grade of abrasive (high or low) and the time interval elapsed after use of the bleaching gel (immediately and after 1h). For the control, four groups were not exposed to the bleaching gel and were just submitted to abrasion cycles according to the type of abrasive and the time interval. The bleaching gel was applied for 1 h and after this period, the groups that were brushed immediately were submitted to abrasion cycle, and the ones tested after 1h, remained in artificial saliva before the performance of abrasive cycles. The specimens were subjected to 45 cycles of brushing, corresponding to 3x a day (135 cycles per day - 1 min 30 s). These procedures were repeated for 7 days, totaling 945 cycles at the end of the study. The enamel wear was measured (μm) by profilometry. To check the results, three-way ANOVA and Tukey's test was applied. The significance level was 5%. Statistically significant differences (p =0.0001) for the three tested factors were observed. Mean values (± SD) and results of Tukey test for whitening factor were: NB- 0.45(± 0.01)a, HP+Ca- 0.51(± 0.03)b, HP - 0.82(± 0.01)c. For the abrasive factor were: Low- 0.44(± 0.01)a and High- 0.74(± 0.05)b and for the time interval, were: 1h- 0.41(± 0.01)a, immediately- 0.77(± 0.05) b. It can be concluded that: a) HP 7.5% bleaching increased the enamel susceptibility to abrasion, b) the... / Doutor

Orientador: Alberto Carlos Botazzo Delbem / Banca: Denise Pedrini Ostini / Banca: Heitor Marques Honório / Resumo: A proposta deste trabalho foi avaliar in vitro a ação de vernizes com diferentes concentrações de fluoretos e suplementado com trimetafosfato de sódio (TMP) sobre a erosão associada ou não à abrasão. Blocos de esmalte bovino foram selecionados e divididos em 12 grupos de acordo com o número de dias de tratamento (3 e 5 dias) e o tipo de verniz utilizado: placebo (sem flúor), NaF 5%, NaF 2,5%, NaF 2,5% TMP 3,5%, NaF 2,5% TMP 5%, NaF 2,5% TMP 10%. O desafio erosivo foi produzido com Sprite Zero® por 5 minutos (4x ao dia) e o erosivo/abrasivo pela escovação mecânica por 15 segundos. Após os desafios, determinou-se a dureza de superfície (SHf), o desgaste do esmalte (μm) e a dureza em secção longitudinal (KHN). Os resultados foram submetidos a Análise de Variância e ao teste de Tukey (p<0,05). Os vernizes com 2,5% de fluoreto e TMP (3,5; 5 e 10%) apresentaram os menores desgaste e perda de dureza (KHN) do que os outros vernizes (p<0,05), independente do desafio. Observou-se correlação positiva entre os resultados de desgaste e KHN. Não houve relação dose-resposta entre a concentração do TMP e o desgaste e a dureza. Maiores desgaste foram observados com 5 dias de experimento e maiores valores de SHf com o desafio erosivo/abrasivo. Os vernizes placebo, NaF 2,5% e NaF 5% apresentaram desgastes similares (p>0,05). Concluiu-se que os vernizes fluoretados suplementados com TMP apresentaram maior efeito contra a erosão e erosão/abrasão do esmalte e menor amolecimentos do esmalte / Abstract: The purpose of this study was to evaluate in vitro the action of varnishes with different concentrations of fluoride and supplemented with trimetaphosphate (TMP) on erosion with or without abrasion. Bovine enamel blocks were selected and divided into 12 groups according to the number of treatment days (3 and 5 days) and type of varnish used: placebo (no fluoride), NaF 5%, NaF 2.5%, NaF 2.5% TMP 3.5%, NaF 2.5% TMP 5%, NaF 2.5% TMP 10%. The erosive challenge was made with Sprite Zero ® for 5 minutes (4x daily) and erosive / abrasive by mechanical brushing for 15 seconds. After the challenges, we determined the surface hardness (SHf), the enamel wear (μm) in longitudinal section and hardness (KHN). The results were submitted to ANOVA and Tukey test (p<0.05). The varnish fluoride and 2.5% TMP (3.5, 5 and 10%) showed the lowest wear loss and hardness (KHN) than other coatings (p <0.05), regardless of the challenge. We observed a positive correlation between the results of wear and KHN. There was no dose-response relationship between the concentration of TMP and the wear and hardness. Greater wear was observed with 5 days of experiment and higher values of SHf with the challenge erosive / abrasive. The placebo varnish, NaF 2.5% and NaF 5% showed similar wear (p> 0.05). It was concluded that fluoride varnish supplemented with TMP had higher effect against erosion and erosion / abrasion of enamel and less softening of the enamel / Mestre

Orientador: Ana Paula Martins Gomes / Banca: Maria Ângela Pita Sobral / Banca: Priscila Christiane Suzy Ciporoni / Banca: Cláudio Antonio Talge Carvalho / Banca: José Benedicto de Mello / Resumo: O presente estudo teve como objetivo avaliar as alterações de cor, as diferenças quanto ao tempo de clareamento e a susceptibilidade ao manchamento em fragmentos dentais bovinos. Foram analisadas também as alterações morfológicas e minerais do esmalte submetido ou não, à imersão em bebida pigmentante e, após o protocolo de clareamento dental, com peróxido de hidrogênio a 35% e 38%, através de dois métodos de análise: fotorreflectância e espectroscopia FT- Raman. Foram utilizados 60 fragmentos dentais bovinos nas dimensões de 4x4x4mm. Para todos os grupos experimentais realizou-se uma leitura inicial que teve como objetivo constituir os grupos controle. Os 60 espécimes foram divididos aleatoriamente em seis grupos experimentais: (G1- Whiteness Maxx + manchamento com Coca-Cola Light Lemon; G2- Whiteness Maxx sem manchamento; G3- Opalescence Xtra Boost + manchamento com Coca-Cola Light Lemon; G4- Opalescence Xtra Boost sem manchamento; G5- Gel manipulado + manchamento com Coca-Cola Light Lemon; G6- Gel manipulado sem manchamento). O clareamento foi realizado seguindo as recomendações de cada fabricante durante duas semanas. Os espécimes foram mantidos em 2ml de saliva artificial durante toda a fase experimental. Após os registros, os dados foram encaminhados para análise estatística e os resultados demonstraram que os agentes clareadores utilizados foram capazes de promover o branqueamento dos espécimes manchados e não manchados; houve perda mineral do esmalte após imersão em Coca-Cola Light Lemon nos espécimes clareados com Whiteness HP Maxx e o agente Opalescence Xtra Boost proporcionou maior perda mineral que os demais agentes. / Abstract: The purpose of this study was to evaluate the color change, the difference on bleaching time and the staining on bovine dental enamel samples. Morphologic and mineral changes on enamel were also evaluated, on every samples (whith or without immersion on Coca-Cola drink and after the dental bleaching protocol with hydrogen peroxide 35 and 38%, throught two analysis, photoreflectance and FT-Raman espectroscopy. Sixty samples were cutted on the standardized dimensions of 4x4x4mm followed by their distribution on six experimental groups (G1- Whiteness Maxx + staining with Coca-Cola Light Lemon; G2- Whiteness Maxx without staining; G3- Opalescence Xtra Boost + staining with Coca-Cola Light Lemon; G4- Opalescence Xtra Boost without staining; G5- Manipulated bleaching agent + staining with Coca-Cola Light Lemon; G6- Manipulated bleaching agent without staining). All the samples received initial register to obtain the control group. The bleaching was done following each manufactures recommendations during two weeks. The samples were kept in artificial saliva during all the research. After the registers, the data were directed to statistics analysis and the results showed that all the tested agents were capable to promove the bleaching of the samples; agents were efficient on bleaching of stained teeth; a mineral lost were detected after the immersion of the samples on Coca-Cola Light Lemon on the group bleached with Whiteness HP Maxx, and Opalescence xtra boost promove higher mineral lost than other bleaching agents. / Doutor

Orientador: Lívia Nordi Dovigo / Banca: Andrea Abi Rached Dantas / Banca: Hérica Adad Ricci / Banca: Juliana Alvares Duarte Bonini Campos / Banca: Mariana Montenegro Silva / Resumo: A cor que percebemos do dente é considerada um fenômeno complexo e um crescente número de estudos tem investigado formas de avaliação de cor com o intuito de tornar o procedimento mais preciso e objetivo. Este estudo avaliou a confiabilidade das medidas efetuadas em espectrofotômetro para análise de cor in vitro em esmalte e dentina bovinos. Realizou-se um ensaio laboratorial, duplo-cego. As variáveis dependentes avaliadas foram as coordenadas colorimétricas L*, a* e b*. Essas medidas foram realizadas por um único examinador, em dois momentos distintos. Foram utilizados 100 dentes bovinos por tipo de superfície (esmalte e dentina). Foram construídos gráficos de dispersão do tipo Bland-Altman. A reprodutibilidade intra-examinador das medidas foi estimada por meio do Coeficiente de Correlação Intraclasse (CCI) e seu Intervalo de Confiança (IC95%). A reprodutibilidade intra-examinador mostrou valores de CCI classificados como "Muito Bom" (CCI ≥ 0,91) para as todas as coordenadas nos dois tipos de espécimes, com exceção da coordenada a* em esmalte bovino, que foi considerada "Boa" (0,71≤CCI>0,91). Foi possível observar que as leituras relacionadas à luminosidade mostraram menor concordância entre as medidas, seguida da coordenada b* e da a*. Para os parâmetros L* e b*, os limites de concordância foram mais amplos na análise em dentina. Conclui-se que a técnica utilizada para medição de cor em esmalte e dentina de dentes bovinos possuiu adequada confiabilidade, mas sugere-se que estudos nessa área busquem a padronização das amostras e realizem calibração para as leituras. / Abstract: The tooth color is considered a complex phenomenon and a growing number of studies have investigated ways of evaluating color in order to make this procedure more precise and objective. This study evaluated the reliability of the spectrophotometer measurements for color analysis in vitro on bovine enamel and dentin. It was a laboratory double-blind trial and the dependent variables were the colorimetric coordinates L*, a* and b*. These measurements were performed by a single examiner at two different times. 100 bovine teeth were used for each type of surface (enamel and dentin). Bland-Altman plots were used to analyze agreement. Intra-examiner reproducibility of the measurements was estimated by the Intraclass Correlation Coefficient (ICC) and its confidence interval (CI95%). Intra-examiner reliability showed ICC values classified as "Very Good" (ICC ≥ 0.91) for all coordinates in both types of specimens, with the exception of coordinated a* in enamel, which was considered "Good" (0,71 ≤CCI> 0.91). It was observed that the L* readings showed less agreement between measurements, followed by the coordinate b* and a*. For L* and b* parameters, limits of agreement were wider in dentin. We conclude that the technique used for measuring color in enamel and dentin of bovine teeth showed adequate reliability, but it is suggested that studies in this area should standardize the samples and perform calibration before the readings. / Mestre