Made available in DSpace on 2014-08-20T14:30:07Z (GMT). No. of bitstreams: 1 Dissertacao_giana_da_silveira_lima.pdf: 1493174 bytes, checksum: 68e4c67538ad95eba022c0a0e790d4b8 (MD5) Previous issue date: 2007-12-21 / To investigate the influence of different water concentrations in self-etching primers solvents on microtensile bond strength (μTBS) of an experimental adhesive system. Five experimental self-etching primers with 0, 5, 10, 20 and 40 water concentration (wt %) in solvent, were synthesized. Clearfil SE Bond (CSEB) was used as commercial adhesive. Sixty bovine incisive were randomize separated in six groups (n=20). Vestibular enamel was removed to expose the superficial coronal dentin, this surface was polished wet to create a standardized smear layer. After rinsing, water was removed, leaving the surface visibly dried. The dentin surfaces were etched with primer and air-dried, after coating adhesive resin was applied and photo-activated, following the composite resin restoration was accomplished. After storage for 24 hours, the specimens were sectioned with a refrigerated diamond saw at low-speed. Microtensile bond strength were measured and data were analyzed by one-way ANOVA/Tukey s test (α=0.05). Analysis of variance showed that primer composition was a significant factor for bond strength. There was not difference on bond strength of the primers with water concentration: 40% (53.9 ± 12.7 MPa), 20% (51.1 ± 11.5 MPa) and 10% (47.5 ± 11.4 MPa) and CSEB (52.44 ± 13.27 MPa). The group with 5% (38.6 ± 12.9 MPa) and 0% (31.5 ± 7.5 MPa), present similar bond strength amongst themselves but statistically smaller that the other groups. The water concentration, present in the primer solvent, exercise significant influence on the bond strength of this experimental self-etching adhesive system / Este estudo avaliou a influência de diferentes concentrações de água no solvente de um primer autocondicionante de um sistema adesivo dentinário experimental. Foram formulados cinco primers experimentais com diferentes concentrações, 0; 5; 10; 20; 40%, de água em massa e Clearfil SE Bond (CSEB) foi utilizado como referência comercial. Foram utilizados 60 incisivos bovinos, distribuídos aleatoriamente entre 6 grupos (n= 20). Na face vestibular dos dentes foi realizado desgaste com lixas até a exposição de dentina com lixa d água 600. O primer foi aplicado sobre a dentina previamente seca com papel absorvente, sendo aplicado jato de ar e em seguida o adesivo foi aplicado e foto-ativado com aparelho fotopolimerizador LED SDI Radii®. A restauração foi confeccionada utilizando 2 incrementos, fotoativados de acordo com as recomendações do fabricante. Após armazenagem por 24 horas em água destilada à 37°C, os dentes foram seccionados em cortadeira de precisão e a resistência de união mensurada, através de ensaio de microtração em uma máquina de ensaios mecânicos. Análise de Variância segundo um critério e teste complementar de Tukey foram utilizados na análise estatística (α=5%). Não houve diferença na resistência de união de P40 (53,9 ±12,7 MPa) P20 (51,1 ±11,5 MPa) e P10 (47,5 ±11,4 MPa) e CB (52,44 ±13,27 MPa). Os grupos P5 (38,6 ±12,9 MPa) e P0 (31.5 ±7.5 MPa) não apresentaram diferença estatística entre si, mas seus valores de adesão dentinária foram menores que os demais grupos (p<0,05). A resistência de união dentinária do sistema adesivo experimental testado sofre influência da concentração de água presente no solvente do primer autocondicionante

Made available in DSpace on 2014-08-20T14:30:10Z (GMT). No. of bitstreams: 1 Dissertacao_Francine_Cardozo_Madruga.pdf: 401845 bytes, checksum: 455f72341e671454f219f56884bf2224 (MD5) Previous issue date: 2006-12-21 / The aim of this study was to investigate the influence of different functional monomer concentrations/HEMA in self-etching primers solvents on microtensile bond strength (μTBS) of an experimental adhesive system. Seventy bonive incisors were allocated in seven groups (n=20). Six experimental self-etching primers were synthesized with different concentratios of acidic monomer (MPF); 0, 15, 30, 50, 70 and 100 (wt %)(Groups EMa0, EMa15, EMa30, EMa50, EMa70, EMa100 respectively). Adhesive system Clearfil SE Bond (CSEB, Kuraray) was used as control. Coating adhesive resin AP-50 was prepared Seventy bovine incisors were randomized and allocate in seven groups. Vestibular enamel was grounded to expose the superficial coronal dentin, witch that was polished wet to create a standardized smear layer with 600 grit silicon paper. After rinsing, water was removed with a piece of absorbent paper, leaving the surface visibly dried. The prepared dentin surfaces were etched with primer and air-dried, after coating adhesive resin was applied and light activated with LED SDI Radii® (1400mW/cm2). The composite resin was inserted in two increments and were ligth activated for 20 s each. After storage for 24 hours, the specimens were sectioned with a refrigerated diamond saw at low-speed. To investigate immediate microtensile bond strength (μTBS) statistical analysis were performed (one-way ANOVA plus Tukey s post-hoc test, α=0.05). Fractographic analysis were performed using optical microscopy to describe failure patterns. The group EMa50 showed statistically higher (p<0.05) microtensile bond strength (55.1MPa) than others experimental groups but was similar with control (50.7MPa). Due total premature failure groups EMa0 and EMa100 were exclude form statistics. Groups EMa15, EMa30 and EMa70 were similar but different that control. Was possible conclude that concentration of acidic monomer/HEMA affects microtensile bond strength of self-etching adhesive systems. Primer composition of 50%MPF-20%HEMA- 30% water showed satisfactory microtensile bond strength as a self-etching adhesive system. / O objetivo deste estudo foi avaliar a influência de diferentes composições variando as concentrações de monômero ácido/HEMA em primer autocondicionante de sistema adesivo dentinário experimental. Foram utilizados 70 incisivos bovinos, distribuídos aleatoriamente entre 7 grupos (n=20). Foram formulados seis primers experimentais com concentrações de 0; 15; 30; 50; 70%; e 100% de monômero ácido (MPF) em massa (Grupos EMa0, EMa15, EMa30, EMa50, EMa70, EMa100 respectivamente). O sistema adesivo Clearfil SE Bond (CSEB, Kuraray) foi utilizado como controle. Na face vestibular dos dentes foi realizado desgaste até a exposição de dentina com lixa d água granulação até 600. O primer foi aplicado vigorosamente sobre a dentina previamente seca com papel absorvente, sendo aplicado jato de ar e em seguida o adesivo foi aplicado e foto-ativado com aparelho fotopolimerizador LED SDI Radii® (1400mW/cm2). A restauração foi confeccionada utilizando 2 incrementos de 2 mm de compósito,fotoativados de acordo com as recomendações do fabricante. Após armazenagem por 24 horas em água destilada a 37°C, os dentes foram seccionados em cortadeira de precisão e a resistência de união (MPa) mensurada através do ensaio de microtração em uma máquina de ensaios mecânicos. As amostras fraturadas do ensaio de microtração foram avaliadas por microscopia óptica e classificadas quanto ao modo de fratura. Análise de Variância segundo um critério e teste complementar de Tukey foram utilizados para detectar diferenças entre médias (α=5%). O grupo EMa50 apresentou o maior valor (p<0,05) de resistência de união à microtração em dentina (55,1MPa) entre os primers experimentais, sendo esse valor semelhante ao encontrado no controle comercial (50,7MPa). Os grupos EMa0 e EMa100 demostraram-se inviáveis por apresentarem totalidade de falhas prematuras e foram excluídos da estatística, os grupos EMa15, EMa30e EMa70 foram semelhantes e estatisticamente inferiores ao controle. Baseado na metodologia do presente estudo foi possível concluir que variações de concentração de monômero ácido/HEMA na composição de sistemas adesivos autocondicionantes afetam os valores de resistência de união à dentina sendo que a composição 50%MPF-20%HEMA-30%Água demonstrou valores iniciais satisfatórios de resistência de união para o desenvolvimento de um sistema adesivo experimental autocondicionante.

Made available in DSpace on 2014-08-20T14:30:11Z (GMT). No. of bitstreams: 1 Tese_Cesar_Henrique_Zanchi.pdf: 1068579 bytes, checksum: 8e2ef86f128f91b16a71c1a2e41952f6 (MD5) Previous issue date: 2010-05-07 / This study evaluated the influence of surfactant dimethacrylates (SD) on the resin-to-dentin immediate and long term microtensile bond strength (μTBS) and characterized the interfacial micromorphology of hybrid layer of the experimental HEMA-free self-etching systems. Five experimental HEMA-free two step self-etching systems containing different surfactant dimetacrylates (SD) (Bis-EMA 10, Bis-EMA 30, PEG 400, PEG 1000 and PEG 400 UDMA) and a HEMA-containing systems (control) were formulated. Sixty bovine incisors were allocated into six groups according each experimental adhesive system used. The teeth had the superficial coronal dentins exposed and were restored and sectioned to obtain sticks randomly allocated into 3 storage periods: 24h, 6 and 12 months. Thereafter the specimens were subjected to the μTBS test. Immediate μTBS data were analyzed by One-way ANOVA and Tukey s test. Long term μTBS data were analyzed by Kruskall-Wallis and Dunn test (α = 0.05). Analysis of the adhesive-dentin interfaces were performed through scanning electron microscopy. Between the HEMA-free groups, the adhesive system formulated with PEG 400 UDMA produced the highest μTBS and was similar to HEMA-containing group. Specimens of the 24 hours of storage were statistically higher for all groups tested when compared those after 6 and 12 months storage. None difference was found between 6 months and 12 months storage for each group. All the adhesives systems presented similar partially demineralized hybrid layer (1.5-3.0 μm thickness) with well formed resin tags. All SD present reasonable μTBS, being the PEG 400 UDMA a promising monomer to be considered as HEMA substitute in adhesive systems compositions. / Este estudo avaliou a influência de dimetacrilatos surfactantes (DS) na resistência de união à dentina por microtração (RU), imediata e após armazenagem, além de caracterizar a micromorfologia da camada híbrida de sistemas adesivos experimentais autocondicionantes livres de HEMA. Foram formulados cinco sistemas adesivos autocondicionantes de dois passos livres de HEMA contendo diferentes DS (Bis-EMA 10, Bis-EMA 30, PEG 400, PEG 1000 and PEG 400 UDMA) e um sistema contendo HEMA, empregado como controle. Foi realizada a exposição da dentina superficial de sessenta incisivos bovinos posteriormente alocados em seis grupos experimentais de acordo com o sistema adesivo empregado. Os dentes foram restaurados e seccionados para obter espécimes (palitos) posteriormente divididos em três períodos de armazenagem: 24h, 6 e 12 meses. Após, os espécimes foram sujeitos ao teste de RU. Resultados de RU imediata foram analisados por ANOVA 1-fator e teste complementar de Tukey. Resultados de RU após envelhecimento foram analisados por Kruskall-Wallis e teste de Dunn (α = 0.05). Analises das interfaces de união dente-restauração foram realizadas através de microscopia eletrônica de varredura. Entre os grupos livres de HEMA, o sistema adesivo formulado com PEG 400 UDMA produziu maior RU e foi estatisticamente similar ao grupo controle contendo HEMA. Os espécimes testados após 24 horas de armazenamento apresentaram RU estatisticamente maior para todos os grupos quando comparados os espécimes testados após 6 e 12 meses de armazenagem. Não foram observadas diferenças significativas entre os grupos testados após 6 e 12 meses. Todos os sistemas adesivos apresentaram camada hibrida parcialmente desmineralizada (1.5-3 μm de espessura) com formação de prolongamentos resinosos. Em geral os sistemas adesivos demonstraram valores de RU satisfatórios, sendo o PEG 400 UDMA um monômero promissor para o desenvolvimento de sistemas adesivos livres de HEMA.

Made available in DSpace on 2014-08-20T14:30:19Z (GMT). No. of bitstreams: 1 Dissertacao_eliseu_aldrighi_munchow.pdf: 1202368 bytes, checksum: 1ae7600de25d0a152376ee755126653c (MD5) Previous issue date: 2014-03-13 / The aim of this study was to synthesize a new acidic monomer (polypropylene glycol methacrylate phosphorous Poly-P) to constitute an experimental two-step self-etch adhesive system and to evaluate its influence on the pH of different self-primers and on the microshear bond strength (&#956;SBS) to enamel. Four experimental self-etch primers containing Poly-P (10, 15, 30 or 50 wt%), 2-hydroxyethyl methacrylate (HEMA), ethanol and water were formulated. A control primer (referential) and a commercial one (Clearfill SE Bond) were also used. The self-primers were allocated in two subgroups according to a buffered and a non-buffered pH. A microshear bond strength (&#956;SBS) test protocol was performed at the enamel substrate, followed by the mechanical testing (EMIC). Scanning Electron Microscopy (SEM) was performed in the enamel surfaces after the self-primers application. The &#956;SBS results were analyzed by One-Way Kruskall-Wallis test and Student-Newman-Keuls as post hoc test (p<0.05). As greater the Poly-P concentration, the lower the pH of the self-primers. The self-primers with a buffered pH resulted in the lowest &#956;SBS values, while the non-buffered self-primers with Poly-P amount higher than 15 wt% showed the highest bond strength results, and similar to the control/referential adhesive systems used. The SEM images demonstrated that the self-primers with high Poly-P content (30 and 50 wt%) resulted a Type 1 etching pattern in the enamel surface. The pH of the self-primer was directly influenced by the acidic monomer concentration, which has directly affected the enamel bond strength results. The Poly-P is a potential monomer to be used in the formulation of self-etch dental adhesive systems / O objetivo deste estudo foi sintetizar um novo monômero ácido (metacrilato de polipropileno glicol fosfatado (Poli-P) para constituir um sistema adesivo autocondicionante experimental e para avaliar a sua influência no pH de diferentes primers autocondicionantes e na resistência de união ao esmalte. Quatro primers autocondicionantes experimentais contendo Poli-P (10, 15, 30 ou 50% em massa), metacrilato de 2-hidroxietila (HEMA), etanol e água foram formulados. Um primer controle (referencial) e um primer comercial (Clearfill SE Bond) também foram utilizados. Os primers foram divididos em dois grupos de acordo com o pH: um grupo com pH tamponado (=2,0) e o outro sem. Um protocolo para o teste de resistência de união ao microcisalhamento (RM) foi realizado em esmalte humano, seguido do teste mecânico (EMIC). Microscopia Eletrônica de Varredura (MEV) foi realizada nas superfícies de esmalte após a aplicação dos primers autocondicionantes, para caracterização do padrão de condicionamento. Os dados foram analisados com Kruskal-Wallis uma via e o teste complementar de Student Newman Keuls (p<0,05). Quanto maior a concentração de Poli-P, menor o pH dos primers. Os primers com pH tamponado resultaram nos menores valores de RM, enquanto que os primers sem tamponamento e com concentração superior a 15% de Poli-P mostraram os maiores valores de união, e similares aos grupos controles. As imagens em MEV demonstraram que os primers com elevado conteúdo de Poli-P (30 e 50%) resultaram em um padrão do tipo 1 de condicionamento da superfície do esmalte. O pH dos primers autocondicionantes foi influenciado diretamente pela concentração do monômero ácido, o qual foi afetado diretamente pelos resultados de resistência de união. O Poli-P é um novo monômero com potencial utilização na formulação de sistemas adesivos dentários autocondicionantes