Dissertação (mestrado) - Pontifícia Universidade Católica do Paraná, Curitiba, 2009 / Inclui bibliografias / Num total de 112 ratos machos Wistar foram induzidas úlceras com hidróxido de sódio (NaOH) 40%, por 07 dias. Os animais, aleatoriamente, foram divididos em 4 grupos (n=28) e tratados com os fármacos: G1 - Salina, G2 - Peróxido de carbamida 16%, G3 - Gel d / In a total of 112 male Wistar rats, ulcers were induced with 40% sodium hydroxide (NaOH), for 07 days. The animals were randomly divided into 4 groups (n=28) and treated with the following manipulated drugs: G1 - Saline, G2 - 16% Carbamide peroxide, G3 -

CAPES / A técnica de clareamento dentário tem sido uma das modalidades estéticas mais utilizadas na atualidade, em prol da busca do "sorriso branco". No entanto, a escolha da técnica, agente clareador e freqüência de utilização do mesmo têm de ser feitas de forma adequada para evitar danos ou alterações na estrutura dental. Este trabalho teve por objetivo avaliar os efeitos dos clareadores na estrutura dental. Foram selecionados 90 dentes de humanos, para preparo de 6 grupos de 15 dentes cada, que foram transformados em 90 corpos-de-prova para os testes. As amostras foram submetidas a testes de microdureza Vickers e análise de impedância, ante e após cada uma das 3 sessões de clareamento realizadas. Foram utilizados 6 tipos diferentes de clareadores disponíveis comercialmente para serem aplicados em consultório ou administrados pelo paciente (caseiro). Os resultados obtidos mostram que, se for considerado os valores médios das microdurezas ante e após a última sessão de clareamento, nas amostras 1 a 60, que foram submetidas aos clareadores utilizados em consultório, foi observada uma diminuição de aproximadamente 2 % na microdureza. Já nas amostras 61 a 90, que foram submetidas aos clareadores caseiros, a diminuição na microdureza foi de aproximadamente 24%. O dados foram analisado-se o teste One-way ANOVA e os resultados mostraram-se significativos para os testes de microdureza realizados com as amostras nas quais foram aplicados os clareadores do tipo caseiro. Os resultados obtidos no trabalho permitem concluir que o uso indiscriminado de clareadores pode provocar danos à estrutura dental. / Techniques for teeth whitening have been largely used as aesthetic procedures. However, the choice of the bleaching agent, the method and the frequency that it will be applied to the patient has to be done properly in order to avoid damage or changes to the tooth structure. This study aimed to evaluate the effects of bleaching techniques on tooth structure. It was selected 90 samples of human teeth to be evaluated considering the Vickers microhardness and impedance analysis, before and after the use of bleaching techniques. The samples were divided into 6 groups of 15 teeth each and 6 different types of commercially available bleaches to be applied at dental offices or at home were used in the tests. The results have shown a decreasing of approximately 24 % in the microhardness after the use of bleaching agents at home (samples 61-90), and only 2 % for those used at dental offices (samples 1-60). The data were analysed using the One-Way ANOVA and the statistical analysis for the Vickers microhardness after the use of bleaching agents at home have shown significant results. Thus, it was possible to conclude that the indiscriminate use of bleaching agents can damage the tooth structure. / 5000

Orientador: Giselle Maria Marchi Baron / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T09:17:29Z (GMT). No. of bitstreams: 1 Silva_AnaPaulaBritoda_M.pdf: 2693552 bytes, checksum: b8df241111c3d0d8f3d4ba79d1bf4688 (MD5) Previous issue date: 2005 / Resumo: O objetivo deste estudo in vitro foi avaliar o efeito de um gel de ascorbato de sódio estabilizado a 3% (AE) e de sistemas adesivos, contendo diferentes solventes orgânicos (acetona ou álcool), sobre a resistência de união ao esmalte humano tratado previamente com peróxido de carbamida a 10% (PC), estabelecendo o padrão de fratura através de microscopia eletrônica de varredura. Quarenta terceiros molares humanos foram selecionados, limpos e armazenados em solução salina de timol a 0,1%. Oitenta fragmentos de 16mm2 foram obtidos das superfícies vestibular e lingual, utilizando-se discos diamantados de dupla-face, em baixa rotação, sob constante irrigação. Os fragmentos foram cobertos com fina camada de cera no7 e embebidos em cilíndro por resina autopolimerizável de poliestireno. Posteriormente, foram divididos aleatoriamente em quatro grupos de acordo com o tipo de tratamento a ser submetido (G1- Saliva, durante todo o experimento; G2- PC, 14 dias/6h, G3- PC, 14dias/6horas + AE após o clareamento, 4dias/7horas e G4- PC, 14dias/6h e AE, durante o clareamento, 2horas). Iniciou-se o tratamento clareador no G3, 4 dias antes dos demais. Os quatro grupos foram subdivididos em oito grupos de acordo com o tratamento restaurador (G1SB, G2SB, G3SB e G4SB- Single Bond + TPH e G1NT, G2NT, G3NT e G4NT- Prime&BondNT + TPH). Finalizado o tratamento restaurador, os fragmentos foram imediatamente preparados para o ensaio de microtração. Cortes seriados foram realizados em cada amostra para obtenção de duas fatias centralizadas de, aproximadamente, 1mm de espessura. Posteriormente, com auxílio de uma broca 1093FF, foi confeccionado em cada fatia, uma constricção, com área adesiva de, aproximadamente, 1mm2, em forma de ampulheta. Os testes de microtração foram realizados em máquina de ensaio Universal, com velocidade de 0,5mm/min. ANOVA e teste de Tukey indicaram que não houve diferença estatística entre os grupos não clareados e os clareados tratados com ascorbato de sódio estabilizado a 3%. Entretanto, para o grupo clareado apenas, a resistência de união foi significantemente diminuída. Para o fator adesivo, não houve diferença estatisticamente significante entre Single Bond e Prime&BondNT. Nas observações em MEV, foi verificada presença de bolhas no adesivo Prime&BondNT do grupo clareado. Os padrões de fratura demonstraram maior número de falhas coesivas nos materiais resinosos submetidos ao clareamento. O gel de ascorbato de sódio estabilizado a 3%, independente da técnica de uso, foi capaz de melhorar os valores de resistência de união ao esmalte clareado / Abstract: The purpose of this in vitro study was to evaluate the effect of a 3% sodium ascorbate gel stabilized (AE) as well as of adhesive organic solvents derived from alcohol or acetone onto the bond strength to human enamel previously treated with carbamide peroxide at 10%, defining the fracture pattern by electronic scanning microscopy. Forty human third molars were selected, cleaned, and kept in saline solution of timol at 0,1%. Eighty fragments of 16mm2 were obtained by the use of double-face diamond discs, in low rotation, under constant irrigation, perpendicularly to buccal and lingual surfaces. The fragments were relieved with a thin layer of wax n° 7 and steep in a cylinder by a self-curing polyester resin. Afterwards, they were random divided into four groups according to the type of bleaching technique to be employed (G1-saliva, G2-PC for 14 days, G3-PC + AE after bleaching for 7 daily hours, during 4 days and G4- PC and AE during bleaching, daily during 2 hours). The four groups were subdivided into eight groups according to the restorative technique (G1A, G2A, G3A and G4A - Single Bond (SB) + TPH and G1B, G2B, G3B and G4B - Prime&BondNT (NT) + TPH). Bleaching treatment was started in the G3, four days before the other groups. Concluded the restorative treatment, the fragments were immediately prepared for micro-traction procedure. Serial cuts were performed in each sample to obtain two centralized slices 1mm thick. Afterwards, using a 1093 FF drill, an hour-glass was done in each slice, with adhesive area of approximately 1mm2. The microtensile tests were performed in an Universal essay machine, at 0,5 mm/min speed. ANOVA and Tukey test indicated that there wasn¿t statistical difference between non-bleached groups and the bleached ones treated with sodium ascorbate at 3%. However, for the group just bleached, the bond strength was significantly decreased. Regarding the adhesive factor, there was not statistically significant difference between SB and NT. On Electronic Scanning Microscopy observations, it was detected the presence of bubbles in the adhesive NT of the bleached group. The fracture standards demonstrated higher number of cohesive failures in the resinous materials undergone to bleaching / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Marcelo Giannini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T05:38:41Z (GMT). No. of bitstreams: 1 Berger_SandrineBittencourt_M.pdf: 5356625 bytes, checksum: 1b4907c704681cbb071f3574823129e2 (MD5) Previous issue date: 2007 / Resumo: Vários estudos têm se preocupado com os efeitos adversos produzidos pelos agentes clareadores de uso caseiro e de consultório. Este estudo tem como objetivo avaliar os efeitos de agentes clareadores de alta concentração (peróxido de hidrogênio a 35%) utilizados em consultório na dureza, composição química e estrutural do esmalte humano. Sessenta e cinco terceiros molares humanos hígidos foram utilizados. Dois fragmentos de esmalte (4x4x3mm) foram removidos das faces vestibular e lingual de cada dente. As amostras foram divididas em 10 grupos (n=10). Antes do clareamento, foram polidas e submetidas ao teste de microdureza Knoop (KHN) e análise em Espectroscopia Raman Transformada de Fourier (ERTF) para determinação da relação de fosfato (PO4) e carbonato (CO3) presente no esmalte não tratado. O grupo controle (GC) não foi submetido ao tratamento clareador. Nos grupos experimentais foram utilizados três diferentes agentes clareadores (Whiteness HP Maxx - W; Pola Office ¿ P e Opalescence Xtra - O) bem como três formas de irradiação (sem irradiação - SI; irradiação com lâmpada halógena ¿ LH, irradiação com LED + Laser Diodo - L). Após os tratamentos, os géis clareadores foram coletados com a solução de enxágüe para avaliação da concentração de cálcio, utilizando espectrofometria de absorção atômica. Em seguida, as amostras foram submetidas à ERTF, ao teste de microdureza superficial e interna, observadas em microscopia eletrônica de varredura para analisar as alterações na superfície e avaliadas em microscopia de luz polarizada para analisar os efeitos das técnicas de clareamento na desmineralização superficial do esmalte. As médias de microdureza superficial variaram de 297,48±16,29 (O-SI) a 317,86±9,62 (P-L) antes do tratamento clareador e 260,94±17,17 (OSI) a 291,68±16,20 (W-LH, pós-clareamento). Para a microdureza interna as médias variaram de 69,55±42,02 (O-L, 20ìm) a 288,13±53,16 (GC, 80ìm). Na determinação da composição química do esmalte através de ERTF, para o fosfato a média da área do pico de fosfato variou entre 14,50± 0,32 (O-SI) a 14,90 ± 0,28 (P-LH) antes do tratamento, sendo que após o tratamento variaram entre 14,24 ± 0,72 (P-L) a 15,03 ± 0,23 (P-LH). Para o carbonato valores de: 3,60 ± 0,52 (W-LH) a 4,41 ± 0,67 (P-SI) antes do tratamento foram encontrados. Após o tratamento variaram entre: 3,69 ± 0,29 (GC) a 4,41 ± 0,13 (P-LH). A concentração de cálcio presente na solução de enxágüe variou entre 0,32 (W-SI) a 1,61 (O-L). Na microscopia eletrônica de varredura, com exceção do grupo controle, todos os grupos apresentaram alterações morfológicas na superfície. Em microscopia de luz polarizada, os grupos Whiteness sem irradiação, com luz halógena e LED/laser, Pola Office com LED/laser e Opalescence com luz halógena e LED/laser apresentaram desmineralização em profundidade. Observamos alterações no conteúdo mineral pela diminuição significativa dos valores de microdureza, perda de cálcio e desmineralização visualizada em microscopia de luz polarizada, além de alterações morfológicas na superfície do esmalte visualizadas em microscopia eletrônica de varredura. Concluímos que a utilização do peróxido de hidrogênio a 35% empregado no tratamento clareador em consultório requer cautela uma vez que, causa alterações na estrutura do esmalte como mostrado no presente estudo / Abstract: Several studies have been concerned with the adverse effects produced by home applied and in-office bleaching treatments. The aim of this study is to evaluate the effects of highconcentrated bleaching agents (35% hydrogen peroxide) on human enamel microhardness, chemical and structural composition. Sixty and five human third molars human were used. Two enamel blocks (4x4x3mm) were obtained from bucal and lingual surfaces of each tooth. The samples were divided in 10 groups (n=10). Before the bleaching treatment, samples were polished and submitted to microhardness test (Knoop) and Fourier Transform Raman Spectroscopy (FTRS) analysis in order to determine the concentration of phosphate (PO4) and carbonate (CO3) present the enamel. Control group (CG) was not submitted to the bleaching treatment. In the remaining experimental groups three different bleaching agents were used (Whiteness HP Maxx - W; Pola Office ¿ P and Opalescence Xtra - O) and three ways of irradiation (no light irradiation - N; irradiation with halogen light - HL and irradiation with LED + Diode Laser - L). After the treatments, the rinsing water solution was to evaluate the concentration of calcium, by means of atomic absorption spectrometry analysis. Afterwards, the samples were re-submitted to FTRS and to surface and cross-sectional microhardness measurement. Samples were observed in scanning electron microscopy to observe surface alterations and in polarized light microscopy to examine the effects of the bleaching techniques in the demineralization of the enamel. The average surface microhardness values microhardness ranged from 297.48±16.29 (O-N) to 317.86±9.62 (P-L) before the bleaching treatment and 260.94±17.17 (O-N) to 291.68±16.20 (W-HL) after bleaching. The mean values obtained after cross-sectional microhardness measurement ranged from 69.55±42.02 (O-L, 20µm) to 288.13±53.16 (CG, 80 µm). The phosphate concentration on enamel determined by means of FTRS ranged from 14.50±0.32 (O-N) to 14.90±0.28 (P-HL) before the treatment. After the treatment the phosphate concentration ranged from 14.24±0.72 (P-L) to 15.03±0.23 (P-HL). The concentration of carbonate present on treated enamel ranged from 3.60±0.52 (WHL) to 4.41±0.67 (P-N) before the treatment and after the treatment, the concentration varied from 3.69±0.29 (CG) to 4.41±0.13 (P-LH). The concentration of calcium in the rinsing water solution ranged from 0.32 (W-N) to 1.61 (O-L). The scanning electron microscopy showed that all groups presented morphologic alterations in the surface, except for the control group. The images obtained after polarized light microscopy showed that Whiteness without irradiation, with halogen light and LED/diode laser, Pola Office with LED/diode laser and Opalescence with halogen light and LED/diode laser presented demineralization. Alterations on enamel mineral content, significant decrease of enamel microhardness and calcium concentration, demineralization observed by means of polarized light microscopy and morphological alterations on enamel observed by means of scanning electron microscopy were observed in the present study. In conclusion, the use of the 35% hydrogen peroxide as a bleaching agent in clinical situations requires caution, since it may cause alterations on enamel structure as observed in the present study / Mestrado / Mestre em Materiais Dentários

Orientador: Giselle Maria Marchi Baron / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T12:14:43Z (GMT). No. of bitstreams: 1 Silva_AnaPaulaBritoda_M.pdf: 4666067 bytes, checksum: 6eaa4a564293d2a7a9e71635aad24d2f (MD5) Previous issue date: 2006 / Resumo: O objetivo deste estudo in vitro foi avaliar o efeito do tempo de aplicação de gel de ascorbil a 3% (AE) sobre a resistência de união ao esmalte bovino tratado previamente com peróxido de carbamida a 10% (PC), estabelecendo o padrão de fratura através de microscopia eletrônica de varredura (MEV). Sessenta incisivos bovinos foram selecionados, limpos e armazenados em solução salina de timol a 0,1%. Sessenta fragmentos de 25mm2 foram obtidos da superfície vestibular, utilizando-se discos diamantados de dupla-face, em baixa rotação, sob constante irrigação. Os fragmentos foram cobertos com fina camada de cera 7 e embebidos em cilíndro por resina autopolimerizável de poliestireno. Posteriormente, foram divididos aleatoriamente em seis grupos, sendo dois controles: GS (saliva, durante todo o experimento) e GP (PC, por seis horas, durante 14 dias) e quatro experimentais, que após a utilização diária do PC, foram submetidos à aplicação de gel antioxidante por 15, 30, 60 ou 120 minutos, respectivamente (GPA15, GPA30, GPA60 e GPA120). Imediatamente após o tratamento, os fragmentos foram condicionados com ácido fosfórico a 37% (Dentsply) e restaurados com sistema adesivo Adper Single Bond (3M-ESPE) e três incrementos horizontais de resina TPH (Dentsply). Finalizado o tratamento restaurador, os fragmentos foram preparados para o ensaio de microtração. Cortes seriados foram realizados em cada amostra para obtenção de duas fatias centralizadas de, aproximadamente, 1mm de espessura. Posteriormente, com auxílio de uma broca 1093FF, foi confeccionado em cada fatia, uma constrição, com área adesiva de, aproximadamente, 1mm2, em forma de ampulheta. Os testes de microtração foram realizados em máquina de ensaio EMIC, com velocidade de 0,5mm/min. A ANOVA e o Teste de Dunnet indicaram haver diferença estatisticamente significativa entre os grupos testados. Comparando-se o controle positivo (GS) com os demais, verificou-se que apenas o controle negativo (GP) diferiu estatisticamente. Quando se comparou o GP com os outros grupos, foi observada diferença estatística com o GS e o GPA120. Para comparação apenas entre os grupos experimentais (GPA15, GPA30, GPA60 e GPA120), foi aplicado o teste ANOVA e análise de regressão polinomial, que revelaram não haver diferença estatisticamente significativa para o fator tempo, de forma isolada. Foi detectada, através de observações em microscopia eletrônica de varredura, presença de pequenas bolhas no grupo clareado. Os padrões de fratura demonstraram maior número de falhas mistas, para todos os grupos testados. O gel de ascorbil a 3%, aplicado no tempo de duas horas, parece ser o mais indicado, para recuperar os valores de resistência de união ao esmalte clareado com peróxido de carbamida a 10% / Abstract: The purpose of this in vitro study was to evaluate the effect that elapsed time (15 min, 30 min, 1 hour e 2 hours) of a 3% ascorbil gel (AE) onto the bond strength to bovine enamel previously treated with carbamide peroxide at 10%, defining the fracture pattern through electronic scanning microscopy. Sixty bovine incisors were selected, cleaned, and stored in saline solution of timol at 0.1%. Sixty fragments of 25mm2 were obtained by the use of double-face diamond discs, in low rotation, under constant irrigation, perpendicularly to buccal surfaces. The fragments were relieved with a thin layer of wax n° 7 and steep in a cylinder by a self-curing polyester resin. Afterwards, they were random divided into six groups according to the type of treatment to be employed (GS- Positive Control- Saliva, during experiment; GP- Negative Control- PC, 14 days/6hours, GPA15- PC, 14days/6hours + AE, 15 min; GPA30- PC, 14days/6hours + AE, 30 min; GPA60-PC, 14days/6hours + AE, 1 hour; GPA120- PC, 14days/6hours + AE, 2 hours). After treatments, the groups were etched with fosforic acid 35% (Dentsply) and restored with adhesive system Adaper Single Bond (3M-ESPE) and three horizontal increments of resin TPH (Dentsply). Concluded the restorative treatment, the fragments were immediately prepared for microtensile procedure. Serial cuts were performed in each sample to obtain two centralized slices 1mm thick. Afterwards, using a 1093 FF drill, an hourglass was done in each slice, with adhesive area of approximately 1mm2. The microtensile tests were performed in an mechanical test machine, at 0.5 mm/min speed. ANOVA and Dunnett test indicated that there was statistical difference between groups tested. When compared positive control group (GS) with the other groups, it was observed that only the negative control group (GP) was statistically different. These results were confirmed, when the negative control group was compared with others, in which it was observed statistic diference to GS and GPA120. When the experimental groups were compared though regressive polinominal analise it was not found statistical difference only to the time factor. On Electronic Scanning Microscopy observations, were detected the presence of bubbles of the bleached group. The fracture standards demonstrated higher number of mixed failures to all the groups. The 3% ascorbil gel (AE) used for two hours seems to be the most recommended to reverse the strength to bleached enamel with carbamide peroxide 10% / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientadores: José Roberto Lovadino, Débora Alves Nunes Leite Lima / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T14:49:11Z (GMT). No. of bitstreams: 1 Vieira_HenriqueHeringer_M.pdf: 2738449 bytes, checksum: 3bff0e9a86d6f5de5afbaa869d38e4a8 (MD5) Previous issue date: 2013 / Resumo: Este trabalho divido em dois estudos teve como objetivos: 1 - Avaliar através de microcisalhamento a influência de três tipos de matrizes para confecção dos cilindros de resina composta sobre a resistência de união a dentina, 2- Avaliar a aplicação de um agente antioxidante experimental, antes e durante o procedimento adesivo, sobre a resistência de união aos substratos dentais clareados. Todas as amostras foram feitas com adesivo simplificado convencional (Single Bond / 3M ESPE) e resina fluida de nanopartículas (Filtek Z 350 Flow / 3M ESPE). Para o estudo 1 vinte dentes bovinos foram cortados, lixados e planificados, a fim de expor a dentina coronária. Em cada fragmento dental foram confeccionados três cilindros, cada feito com um tipo diferente de matriz: 1 - matriz de silicone, 2 - matriz experimental de macarrão e 3 - matriz de Tygon. A remoção dos tipos 1 e 3 de matrizes se fez pelo corte da matriz, e do tipo 2 por imersão em água até que o macarrão se soltasse do espécime. As amostras foram submetidas ao microcisalhamento. Os dados foram analisados através de análise unidirecional de variância (ANOVA) (? = 0,05). Não houve diferença estatística entre os diferentes tipos de matrizes estudadas. Para o estudo 2 foram utilizados 100 fragmentos de dentes bovinos, medindo 6x6x1mm de espessura. Os fragmentos foram distribuídos em 10 grupos, variando o substrato dental (esmalte e dentina) e tratamento a ser realizado: controle (sem tratamento), clareamento (peróxido de hidrogênio 35%) sem aplicação do agente antioxidante, clareamento com aplicação do agente antioxidante por 10 minutos antes do procedimento restaurador, clareamento com aplicação do agente antioxidante por 10 minutos após o condicionamento ácido, clareamento com aplicação do agente antioxidante por 30 minutos antes do condicionamento ácido. Após um período de 24 horas armazenado em saliva, os corpos de prova foram submetidos ao teste de microcisalhamento. Então foi aplicada análise de variância (ANOVA) "1 way" e teste de Tukey, considerando o nível de significância 5%, e análise do padrão de fratura. Não foi encontrada diferença estatística na resistência de união para o esmalte. Em dentina os grupos que receberam tratamento com antioxidante apresentaram valores de resistência de união intermediários aos grupos controle e sem tratamento antioxidante. Pode-se concluir que o tipo de matriz não interferiu nos resultados de resistência de união a dentina, e que o agente antioxidante apresentou bom comportamento por elevar os valores de resistência de união à dentina clareada / Abstract: This work divided in two studies aimed to: 1 - Evaluate through microshear the influence of three types of matrices for the fabrication of composite resin cylinders on the bond strength to dentin; 2 - Evaluate the application of an experimental antioxidant, before and during the adhesive procedure on the bond strength to dental substrates bleached. All samples were made with conventional simplified adhesive (Single Bond / 3M ESPE) and nanoparticles flow composite (Filtek Z 350 Flow / 3M ESPE). For the first study twenty bovine incisors were cuted, grinded and planned in order to expose coronal dentin. Each dental fragment received three cylinders, each one made with a different type of matrix: 1 - silicone matrix, 2 - experimental matrix and 3 - Tygon matrix. Removal of the 1 and 3 matrix types were made by cutting the matrix, and type 2 by immersion in water until the noodle let out of the specimen. Samples were so subjected to microshear. Data were analyzed using one-way analysis of variance (ANOVA) and Tukey's test (? = 0.05). There was no statistical difference between the matrices studied. For study 2 one hundred fragments of bovine incisors were used, measuring 6x6 mm and height of enamel and dentin 1mm each. The fragments were distributed into 10 groups, varying the dental substrate (enamel and dentin) and treatment to be performed: Control (no treatment), bleaching (hydrogen peroxide 35%) without application of antioxidant, bleaching agent application antioxidant for 10 minutes before the restorative procedure, bleaching with agent application antioxidant for 10 minutes after the acid etching, bleaching with agent application antioxidant for 30 minutes before etching. After a period of 24 hours stored in saliva, the samples passed by microshear test. So was applied one way ANOVA, considered the 5% significance level, and analysis of the fracture pattern. There was no statistical difference in enamel. In dentin the groups that received treatment with antioxidant, showed intermediate values compared with untreated and control groups. Can be concluded that the type of matrix does not affect the results of bond strength to dentin, and that the antioxidant showed good behavior by raising the values of bond strength to bleached dentin / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Debora Alves Nunes Leite Lima / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-26T22:07:33Z (GMT). No. of bitstreams: 1 Zeczkowski_Marilia_M.pdf: 2124378 bytes, checksum: 1b6ef98933934bf726e1ed6cae6d4587 (MD5) Previous issue date: 2015 / Resumo: O clareamento dental é realizado através do peróxido de hidrogênio que se difunde pela estrutura dentária produzindo radicais livres, que por sua vez quebram as moléculas de pigmento no interior dente fazendo com que o mesmo tenha aparência mais clara. Apesar de o clareamento ser um procedimento efetivo, não há consenso na literatura em relação aos efeitos adversos que ele pode causar na estrutura dentária. Este conflito entre os resultados pode ser devido ao modo como estes estudos são realizados no que se refere ao meio de armazenamento das amostras. O objetivo deste estudo foi avaliar o efeito de diferentes meios de armazenamento in vitro e in situ na estrutura do esmalte clareado, por meio da microdureza knoop (KHN) e análise da variação de cor. Para isso, foram utilizados 48 blocos dentais bovinos aleatoriamente divididos em quatro grupos (n=12), de acordo com o meio de armazenamento: água purificada (PW), saliva artificial (AS), saliva natural (NS), in situ (IS). Foram realizadas três sessões de clareamento com peróxido de hidrogênio a 35%, com intervalo de sete dias entre elas. Cada sessão consistiu em três aplicações de 15 minutos de gel clareador, totalizando 45 minutos. As leituras de cor e KHN foram realizadas antes das amostras serem colocadas no meio de armazenamento (t1), depois de 24h no meio de armazenamento (t2) e após 24h ao término do tratamento clareador (t3). Ao final do clareamento, duas amostras extras de cada grupo foram analisadas em microscópio eletrônico de varredura (SEM). Os resultados KHN foram analisados pelo modelo de medidas repetidas PROC-MIXED, teste de Tukey-Kramer com nível de significância de 5%. A análise da variação de cor, ?L, ?a, ?b, ?E entre os diferentes tempos ?1 (t1-t2) e ?2 (t2-t3) foi realizada através do teste de Kruskal-Wallis, seguido pelo teste de Dunn (?=0,05). Não houve diferença estatisticamente significante na KHN em t1 e t2. Em t3 o grupo PW apresentou valores significativamente menores que outros grupos. Na análise de cor ?E2, IS apresentou menores valores diferindo estatisticamente de AS. Em ?b1 o grupo IS apresentou valores mais elevados em relação aos outros grupos, enquanto em ?b2, IS obteve menores valores, diferindo apenas de AS. Em ?L1 não houve diferença entre os grupos, entretanto em ?L2, PW e AS diferiram estatisticamente de IS, e NS mostrou valores similares a IS. SEM mostrou alteração na superfície de esmalte em PW. As condições de armazenamento apresentaram diferentes efeitos nas propriedades físicas do esmalte. A saliva natural foi a única que apresentou, em todos os parâmetros avaliados, comportamento semelhante ao armazenamento in situ / Abstract: Tooth bleaching is performed through hydrogen peroxide which diffuses through dental structure producing free radicals which in turn break the dye molecules inside the tooth causing it to have a clearer appearance. Despite bleaching being an effective procedure, there is no consensus in literature regarding the adverse effects it may have on tooth structure. This lack of consensus among the results may be due to how these studies are conducted with regard to the means of storage of the samples. The aim of this study was to assess the effect of different conditions of in vitro storage vs. in situ, in bleached enamel structure by Knoop microhardness (KHN), and color analysis variation. To this end, 48 bovine tooth blocks were used randomly divided into four groups (n = 12) according to the storage medium: purified water (PW), artificial saliva (AS), natural saliva (NS), in situ (IS). Three whitening sessions were carried out using hydrogen peroxide at 35%, with an interval of seven days between the sessions. Each session consists in three applications of 15 minutes of bleaching gel, totaling 45 minutes. Color and KHN measurements were taken before the samples had been placed in the storage medium (t1), after 24h on the storage medium (t2), and after 24h at the end of the bleaching treatment (t3). At the end of bleaching, two extra samples of each group were analyzed by scanning electron microscope (SEM). The KHN results were analyzed by models for repeated measures PROC MIXED, Tukey Kramer test at 5% significance level. The analysis of color change, ?L, ?a, ?b, ?E between the different times ?1 (t1-t2) and ?2 (t2-t3) was performed using the Kruskal-Wallis test followed by Dunn's test (? = 0.05). There was no significant statistical difference in KHN in t1 and t2. In t3, PW group showed lower values significantly differing from the other groups. In ?E2 color analysis, IS showed lower values differing statistically from AS. In ?b1 the IS group showed higher values as compared to the other groups, while in ?b2, IS had lower values, differing only from AS. In ?L1 there was no difference between the groups, however in ?L2, PW and AS statistically differed from IS, and NS showed similar values to IS. SEM showed change in the enamel surface in PW. The storage conditions had different effects on the physical properties of the enamel. Natural saliva, was the only one that showed in all the evaluated parameters, similar behavior to in situ storage / Mestrado / Dentística / Mestra em Clínica Odontológica

Orientador: Flávio Henrique Baggio Aguiar / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-19T14:51:35Z (GMT). No. of bitstreams: 1 Sasaki_RobsonTetsuo_M.pdf: 2754665 bytes, checksum: 23869c9999ee4e3552517da97aa3f84e (MD5) Previous issue date: 2012 / Resumo: O objetivo deste estudo in vitro foi determinar a microdureza, rugosidade superficial, micromorfologia e alterações de cor de esmalte dental humano submetido a tratamentos clareadores caseiros com peróxidos de hidrogênio a 7,5% (PH) adicionados de cálcio, fosfato de cálcio amorfo (ACP), flúor e/ou hidroxiapatita (HA). Três agentes de tratamento comerciais: (Pola Day 7,5% (PD), Day White ACP 7,5% (DW), White Class Calcium 7,5% (WC)), três agentes clareadores experimentais (PH 7,5% + NaF (PHF), PH 7,5% + HA (PHH) e PH 7,5% + NaF + HA (PHFH)) e os grupos controle positivo (gel de peróxido de hidrogênio a 7,5% - PC) e controle negativo (gel sem peróxido de hidrogênio a 7,5% - NC), foram avaliados (n=10). Os agentes de tratamento comerciais foram aplicados pelo prazo recomendado pelos fabricantes e os agentes experimentais por 1,5 hora por dia. Todas as amostras foram imersas em solução de saliva artificial pelo resto do dia, num total de 21 dias de tratamento. Após, ficaram armazenados em saliva artificial por 14 dias. Ensaios de microdureza, rugosidade superficial, micromorfologia do esmalte e análise de alteração de cor foram realizados nos tempos baseline, 7, 14, 21 dias de tratamento, 7 e 14 dias de pós-tratamento. Para análise estatística, as médias foram comparadas utilizando o teste de Tukey-Kramer com um nível de significância de 5%. Como resultados, no teste de rugosidade superficial (Ra) foi observado aumento em todos os grupos experimentais (PHF, PHH e PHFH) e nos grupos comerciais DW e WC ao longo do tempo. No teste de microdureza (KHN) observou-se um aumento significativo para o grupo PHH e redução significativa do grupo DW, enquanto os outros grupos não apresentaram alteração significativa ao longo do tempo de estudo. Para o teste de análise de alteração de cor, todos os agentes apresentaram efeito clareador, exceto o grupo NC, sendo que o grupo PHH foi o único que apresentou valores similares aos agentes clareadores comerciais em todos os tempos de estudo. Na análise morfológica observou-se alterações como a presença de porosidades na maioria dos grupos, exceto no grupo NC, além de deposição de cristais de hidroxiapatita nos grupos PHH e PHFH. Concluiu-se que o tratamento clareador contendo hidroxiapatita proporcionou alterações de cor similares aos agentes clareadores comerciais, foi capaz de aumentar a microdureza, e que quando este componente é formulado com ou sem flúor, pode levar a um aumento da rugosidade superficial, devido a deposição de cristais de hidroxiapatita na superfície de esmalte, como observado pela análise de microscopia eletrônica de varredura / Abstract: The aim of this in vitro study was to determine the microhardness, surface roughness, micromorphology and color change analysis of enamel submitted to with home-use bleaching treatment 7.5% hydrogen peroxide (HP) added with calcium, amorphous calcium phosphate (ACP), fluoride and/or hydroxyapatite (HA). Three commercial treatment agents: (Pola Day 7.5% (PD), Day White ACP 7.5% (DW), White Class 7.5% Calcium (WC)), three experimental bleaching agents (7.5% HP + NaF (PHF), HP + 7.5% HA (PHH) and PH + 7.5% NaF + HA (PHFH)), a negative control (Gel without 7.5% hydrogen peroxide - NC) and a positive control (Gel with 7.5% hydrogen peroxide - PC) groups were evaluated (n=10). The treatment agents were applied according to the manufacturer's recommendation and experimental agents were applied for 1,5 hour daily. Then all the specimens were immersed in artificial saliva for the rest of the day, in a total of 21 days of treatment. After the treatment phase, the specimens were stored in artificial saliva for 14 days. Microhardness tests, surface roughness, micromorphology of the enamel and color change analysis were performed at baseline, 7, 14, 21 days of treatment, 7 and 14 days post-treatment. For the statistical analysis, means were compared using the Tukey-Kramer test at a significance level of 5%. As results, the surface roughness test (Ra) presented increase in all experimental groups (PHF, PHH and PHFH) and commercial groups DW and WC in function of time. The microhardness test (KHN) showed a significant increase for the group PHH and a significant reduction on DW group, while the other groups did not show statistical difference in function of timespan study. For the color change analysis test, all the groups presented bleaching effectiveness, except the group NC, and the PHH group was the only one that showed similar values compared to the commercial bleaching agents at all times of study. In the morphological analysis, changes were observed as the presence of porosities in most groups, except on NC group, and deposition of hydroxyapatite crystals on groups PHH and PHFH. It was concluded that the bleaching treatment containing hydroxyapatite provided color changes similar to commercial bleaching agents, was able to increase the microhardness values, and that when this component is formulated with or without fluoride, it can lead to an increase in surface roughness due to deposition of hydroxyapatite crystals over the enamel surface, as observed by analysis of scanning electron microscopy / Mestrado / Dentística / Mestre em Clínica Odontológica