Spelling suggestions: "subject:"dentinbonding dagents"" "subject:"dentinbonding angents""
1 |
Efeito da quantidade de primer na adaptação marginal, nanoinfiltração e resistência à união de sistemas adesivos após envelhecimento termomecânico = Effects of primer amount on marginal adaptation, nano leakage and bond strength of adhesive systems after thermomechanical aging / Effects of primer amount on marginal adaptation, nano leakage and bond strength of adhesive systems after thermomechanical agingBarreto, Suelem Chasse, 1987- 26 August 2018 (has links)
Orientador: Luis Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-26T22:01:59Z (GMT). No. of bitstreams: 1
Barreto_SuelemChasse_M.pdf: 116094135 bytes, checksum: 14295d9814cd8a3d1872c717dd154522 (MD5)
Previous issue date: 2015 / Resumo: O estudo teve como objetivo avaliar a influência da quantidade de primer usada na hibridização do substrato na resistência de união por microtração, nanoinfiltração e adaptação marginal em restaurações com sistemas adesivos e resina composta após envelhecimento termomecânico. Foram selecionados 48 molares hígidos que foram restaurados em uma cavidade tipo classe I pela técnica incremental com sistema adesivo convencional de três passos (Adper Scotchbond Multiuso - 3M ESPE) e sistema autocondicionante de dois passos (Clearfill SE bond - Kuraray). Para o sistema adesivo convencional foi realizado o condicionamento ácido total e para o sistema adesivo autocondicionante, o condicionamento ácido foi seletivo no ângulo cavosuperficial em esmalte. Em seguida, os dentes foram alocados aleatoriamente em 6 grupos resultantes da interação da aplicação de uma quantidade padronizada de 1, 2 ou 3 gotas de primer e sistema adesivo. Todos os dentes foram restaurados com a resina composta microhíbrida Charisma (Heraeus Kulzer). Após o polimento das restaurações, estas foram moldadas com polivinilsiloxano e as réplicas foram obtidas em resina epóxica. Em seguida, os espécimes foram levados à máquina de ciclagem termomecânica ERIOS 37000 (ERIOS, São Paulo, Brasil), na qual realizou-se o envelhecimento artificial da restauração através de 200.000 ciclos com carga de 86 N a uma frequência de 2 Hz associados a ciclos térmicos com a temperatura variando entre 5ºC, 37ºC e 55ºC, a cada 30 segundos. Terminado o envelhecimento, obteve-se novas réplicas que foram levadas ao microscópio eletrônico de varredura (MEV) para análise de fendas em comparação com as imagens iniciais. Em seguida os dentes foram submetidos ao ensaio mecânico de resistência de união à microtração por meio de palitos obtidos da interface vestibular, e, posteriormente, avaliou-se o padrão de fratura usando MEV. Para análise de nanoinfiltração, oito palitos de cada grupo foram separados, aleatoriamente, para se avaliar a infiltração de íons de nitrato de prata em MEV. Após o teste termomecânico, os dados foram submetidos à Análise de Variância dois fatores e teste de Tukey com ?= 0,05. Quando o excesso de primer na camada adesiva foi avaliado, o sistema adesivo convencional de três passos apresentou melhores resultados de resistência à união quando comparado ao sistema adesivo autocondicionante de dois passos (?= 0,0015). A quantidade de gotas influenciou a resistência de união à microtração (?= 0,0057). A nanoinfiltração foi maior quando se utilizou maior quantidade de primer e o envelhecimento termomecânico aumentou a formação de fendas marginais. O uso de primer em excesso não é recomendado pois reduz a resistência de união à microtração e forma uma camada híbrida de baixa qualidade / Abstract: This study aimed to evaluate the effects of the amount of primer used in the tooth substrate hybridization on the microtensile bond strength (?TBs), nanoleakage and marginal sealing in dental restorations with adhesive systems and composite resin after thermomechanical aging. A total of 48 human molars were restored class I cavities with incremental technique with a three-step etchand- rinse adhesive system (Adper Scotchbond Multipurpose, 3M ESPE) and twostep self-etching adhesive system (Clearfill SE Bond, Kuraray), For three-step etch-and-rinse adhesive system used total acid etching and for the two-step selfetching system adhesive only enamel cavosurface was acid etching. Then, the teeth were aleatory alocated in 6 groups resulted the interaction between the factors application of standard quantity of primer (1, 2 or 3 drops) and adhesive systems. Afterward a standardized amount of each primer was applied (1, 2, or 3 drops of primer). All teeth were restored with microhybrid composite resin (Charisma, Heraeus Kulzer). After polishing of restorations, they were molded with polyvinylsiloxane and replicas were obtained with epoxy resin. Then the specimens were taken to thermomechanical cycling machine (model 37000 ERIOS), which carried out the artificial aging of restoration through 200,000 cycles with 86 N load at a frequency of 2 Hz associated with thermal cycling and temperature ranging from 5, 37and 55°C every 30 seconds. After aging, new replicas were obtained and images were taken by scanning electron microscope (SEM) to analyze gaps. These images were compared to the initial ones. Then the teeth were subjected to ?TBs testing through beams obtained from buccal interface, and fracture pattern was evaluated using SEM. For nanoleakage analysis, eight beams of each group were randomly separated to assess infiltration with silver nitrate ions and subsequently evaluated by SEM. After the mechanical test, the data were subjected to statistical analysis using two-way Analysis of Variance and Tukey's test (? = 0.05). When primer excess was evaluated at the adhesive layer, the three-step etch-and-rinse adhesive system showed higher bond strength results x when compared to two-step self-etching adhesive system (? = 0.0015). The primer excess influenced ?TBS (? = 0.0057). Nanoleakage was higher when using larger amount of primer was used. Thermomechanical aging increased the formation of marginal gaps. The use of primer in excess is not recommended, because the excess reduces the ?TBs and creates an unsatisfactory hybrid layer on tooth substrate / Mestrado / Dentística / Mestra em Clínica Odontológica
|
2 |
Nanoinfiltração e resistência da união de sistemas adesivos avaliados sob pressão pulpar simulada / Nanoleakage and bond strenght of adhesive systems evaluated under sumulated pulpar pressureFeitosa, Victor Pinheiro, 1987- 11 September 2018 (has links)
Orientadores: Américo Bortolazzo Correr, Mário Alexandre Coelho Sinhoreti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-09-11T21:16:44Z (GMT). No. of bitstreams: 1
Feitosa_VictorPinheiro_M.pdf: 1748839 bytes, checksum: 19481c535f5edd50191d7995d2529e9f (MD5)
Previous issue date: 2011 / Resumo: O objetivo neste estudo foi avaliar o efeito do tempo de fotoativação de adesivos de passo único e da pressão pulpar simulada na resistência da união e nanoinfiltração de compósitos resinosos à dentina humana. Este estudo foi separado em 2 Capítulos. No Capítulo 1 verificada a influência do aumento do tempo de fotoativação para um sistema adesivo autocondicionante de passo único (Clearfil S3 Bond) submetido ou não à pressão intrapulpar simulada. Foram obtidas superfícies planas em dentina profunda de terceiros molares, os quais foram separados em quatro grupos (n=5). O adesivo foi aplicado seguindo a recomendação do fabricante e fotoativado por 10 segundos (recomendação fabricante) ou 40 segundos (tempo de fotoativação aumentado). A fotoativação realizada com o aparelho de luz de lâmpada halógena XL-2500 com irradiância de 600 mW/cm². Os dentes foram restaurados com o compósito nanoparticulado Filtek Z350. Metade dos grupos foi armazenada sob pressão pulpar simulada e a outra metade armazenada em água, sem pressão pulpar simulada. Após 24 horas, os dentes foram cortados em palitos e submetidos ao teste de resistência da união por microtração. Os dados foram submetidos à análise de variância dois fatores e teste de Tukey (p<0.05). resultados mostraram que a pressão pulpar diminuiu significativamente a resistência união para ambos os tempos de fotoativação. O aumento do tempo de fotoativação de 40s resultou em significante aumento de resistência para os grupos com pressão pulpar; entretanto, não foi significativo para os grupos sem pressão. Pode ser concluído que pressão pulpar simulada diminuiu a resistência da união, mas o aumento do tempo fotoativação melhorou a resistência da união a dentina nos grupos armazenados sob pressão pulpar. No Capítulo 2 o objetivo foi avaliar in vitro uma nova metodologia para simular pressão pulpar comparada à metodologia tradicional. Foram utilizados quatro sistemas adesivos (Clearfil S3 Bond, Clearfil SE Bond, Adper Single Bond Plus, and Scotchbond Multi-Purpose), que foram aplicados em superfícies planas de dentina profunda de terceiros molares. Após a restauração com compósito as amostras foram armazenadas em água sem pressão pulpar, submetidas à pressão pulpar convencional ou pela nova metodologia pressão pulpar. Após 24 horas, os dentes foram cortados em palitos e submetidos ao teste de resistência da união por microtração. Os dados foram submetidos à análise de variância dois fatores e teste de Tukey (p<0.05). Os resultados mostraram que os adesivos simplificados (autocondicionante de passo único e de técnica úmida de dois passos) foram negativamente influenciados pela pressão pulpar, mas não houve diferença significativa entre as duas metodologias de simulação da pressão pulpar. Os adesivos autocondicionante de dois passos e de técnica úmida de três passos não foram afetados pela simulação pressão pulpar (p>0,05). O padrão de nanoinfiltração mostrou similaridade entre as duas metodologias. Os maiores valores de resistência da união foram apresentados pelo Scotchbond Multi-Purpose e os menores pelo adesivo Clearfil S3 Bond. Pode ser concluído que ambas as metodologias diminuíram a resistência da união dos adesivos de técnica simplificada, sem haver diferença entre a metodologia experimental e a metodologia convencional para resistência da união e padrão de nanoinfiltração. Conclui-se que aumento do tempo de fotoativação melhorou a união nos adesivos autocondicionante simplificados sob pressão pulpar simulada. Além disso, a metodologia experimental simulação da pressão pulpar pode ser utilizada em substituição a metodologia tradicional. / Abstract: The aim of this study was to evaluate the extended photoactivation time for one-step self-etch adhesives and the simulated pulpal pressure applied into two methods on bond strength of direct restoration of composite resin to human dentin. This work was divided into two Chapters. The Chapter 1 analyzed the influence of extended photoactivation time of one-step self-etch adhesive Clearfil S3 Bond with and without conventional simulated pulpal pressure. It was obtained flat surfaces in deep dentin from extracted third molars and they were divided randomly in four groups (n=5). The adhesive was used in agreement with manufacturer's recommendation (photoactivation time 10s) and with the extended photoactivation time to 40s, after the composite restoration was built up with nanofilled composite resin Filtek Z350. The photoactivation procedures were realized with quartz-tungsten halogen lamp XL-2500 with a standard irradiance of 600mW/cm². Half of the samples were submitted to simulated pulpal pressure and the other half was stored in water without pulpal pressure. After 24 hours, the samples were cut into sticks and the microtensile bond strength test was performed. The results were submitted to two-way ANOVA and Tukey's test (p<0.05). Pulpal pressure decreased bond strength for both photoactivation times and the extended photoactivation time showed significant increase in bond strength for groups with simulated pulpal pressure, however the increase was not statistically significant for groups without pulpal pressure. It can be concluded that simulated pulpal pressure decreased bond strength, however the extended photoactivation time improved the bonding under pulpal pressure simulation. In Chapter 2, a new methodology to simulate pulpal pressure was tested in comparison with the traditional methodology and control groups without pulpal pressure. One adhesive system of each of the four approaches was applied in flat surfaces in deep dentin of extracted molars as in Chapter 1. After the composite was built up, samples were stored in water storage without pulpal pressure, under conventional simulated pulpal pressure or under the new methodology to simulate pulpal pressure. After microtensile test, the results showed no differences between two methodologies of simulated pulpal pressure (p<0.05) and nanoleakage patterns were similar for both methods. Simplified adhesives were more influenced by pulpal pressure than multi-step adhesives, showing significant decrease in bond strength. The highest bond strength values were obtained by the three-step adhesive Scotchbond Multi-Purpose and the lowest were obtained by the one-step adhesive Clearfil S3 Bond. In conclusion, the extended photoactivation time improves bonding for one-step self-etch adhesives under simulated pulpal pressure. In addition, the experimental methodology to simulate pulpal pressure can be used in replacing the conventional methodology. / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários
|
3 |
Avaliação da adaptação à dentina de vários agentes de proteção com ou sem sistemarestaurador adesivo, em função de diferentes tratamentos da superfície dentinária. / Evaluation of the marginal finishing of cavity preparations in relation to different instrumentation methods.Coutinho, Margareth da Silva 05 April 2000 (has links)
Este estudo quantificou micrometricamente o índice de adaptação à dentina (presença ou ausência de fenda interfacial) de vários agentes protetores à base de hidróxido de cálcio de ativação química - Dycal e de luz visível - Prisma VLC Dycal e Ultra-Blend® plus e cimento de ionômero de vidro convencional - Ketac Bond e fotoativado - Vitrebond; associados a diferentes tratamentos de superfície dentinária, com e sem a presença de sistema restaurador adesivo (Primer & Bond 2.1 + TPH Spectrum). Os tratamentos dentinários foram jatos de ar/água, condicionamento com ácido poliacrílico a 25% por 10s e ácido fosfórico a 37% por 15s. Foram utilizados 200 dentes, os quais numa metade foi desgastado o esmalte e os preparos realizados em dentina e na outra metade repetiu-se o preparo cavitário envolvendo esmalte e dentina. Cavidades tipo classe V foram realizadas com 3mm de diâmetro e 0,8mm de profundidade em dentina e 0,8mm quando envolvido o esmalte. Após o preenchimento da cavidade, os corpos-de-prova foram incluídos em resina epóxica e seccionados longitudinalmente no sentido vestíbulo-lingual. Foram obtidas réplicas em negativo utilizando-se material de moldagem à base de polivinil siloxana (Aquasil), para a avaliação da desadaptação à dentina, por meio de microscópia de luz refletida em campo escuro. Os dados obtidos microscopicamente foram submetidos aos Testes de Kruskal-Wallis e as comparações múltiplas pelo Teste de Dunn. Os resultados demonstraram que quando comparados o comprimento e a largura da desadaptação à dentina dos agentes protetores, entre as condições experimentais com e sem a presença do sistema restaurador adesivo, o cimento de ionômero de vidro fotopolimerizável Vitrebond obteve os melhores resultados, sobrepujando, inclusive, o Ketac Bond ativado quimicamente. Numa posição intermediária vêm o Ultra-Blend® plus e o cimento de hidróxido de cálcio auto-ativado Dycal e, por último, o cimento de hidróxido de cálcio fotopolimerizável Prisma VLC Dycal, que apresentou a maior desadaptação. / The present study evaluated the length and width of interface gaps between dentin and the following lining materials: chemically cured Dycal Advanced Formula II and light cured Prisma VLC Dycal and Ultra-Blend® plus calcium hydroxide bases; chemically cured Ketac Bond and light cured Vitrebond glass ionomer cements. Dentin cavities prepared in human teeth were pre-treated with only an air/water Spray or with a 25% Polyacrylic acid solution for 10s, or a 37% Phosphoric acid solution for 15s. One half of cavities were prepared in dentin (3mm wide, 0.8mm deep) and have been filled with only the linning materials. The other half of the cavities were enamel dentin cavities had a 0.8mm with enamel layer, 3mm wide, 0.8mm deep below the dentinoenamel junction. Theses cavities received a layer of lining material have then been treated with an adhesive system an restored with a composite resin. In order to access the dentinal interfacial adaptation, the specimens were sectioned longitudinally in buccal to lingual direction thorough the center of the restorations. Low viscosity polyvinyl siloxane impression material (Aquasil) was used to obtain negative replicas. The replicas were examined with a Zeiss Photomicroscope and the length and width of the gaps were measured. The values were submitted to Kruskall Wallis Test and Multiple Comparation Dunn Test. Results demonstrated that, on the experimental conditions used, the glass ionomer cements obtained the best results, specially the Vitrebond. The Ultra-Blend plus and Dycal, showed an intermediary position. Prisma VLC Dycal showed the powerest adaptation.
|
4 |
Efeito de diferentes soluções de clorexidina na produção e estabilidade mecânica da união resina-dentina afetada por cárieRicci, Hérica Adad [UNESP] 31 January 2012 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:33:01Z (GMT). No. of bitstreams: 0
Previous issue date: 2012-01-31Bitstream added on 2014-06-13T20:44:35Z : No. of bitstreams: 1
ricci_ha_dr_arafo.pdf: 2721593 bytes, checksum: 4217c4bca9ee0836b6bc0623a2ea8400 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo geral deste trabalho, o qual foi dividido em três estudos, foi avaliar o efeito da clorexidina (CLX) em diferentes excipientes, etanol e água, na produção e estabilidade mecânica da união resina-dentina afetada por cárie. Materiais e Métodos. No primeiro estudo foi avaliada a influência da CLX em solução aquosa ou alcoólica na umectabilidade da dentina hígida e afetada por cárie por um sistema adesivo. Foram preparadas superfícies planas de dentina em 100 terceiros molares hígidos, das quais 50 foram submetidas ao processo microbiológico de indução de cárie. Dentro de cada condição de substrato, hígido e afetado por cárie, as superfícies foram divididas em 5 grupos (n=10): com smear layer (SL), sem smear layer impregnada com água, sem smear layer impregnada com CLX em água, sem smear layer impregnada com etanol e sem smear layer impregnada com CLX em etanol. Ângulos de contato entre a superfície de dentina e o sistema adesivo Single Bond 2 foram mensurados por meio de um goniômetro, e os dados submetidos aos testes de ANOVA e Tukey ( =0,05). No segundo estudo foi avaliado o efeito da solução de CLX em diferentes excipientes, etanol ou água, na presença de colágeno exposto na união resina-dentina hígida e dentina afetada por cárie. Foram produzidas superfícies planas de dentina em 24 molares humanos hígidos, sendo metade delas cariadas artificialmente. Os dentes foram divididos em 8 grupos (n=3) segundo o tratamento da dentina após o condicionamento ácido (CLX associada a etanol, CLX associada a água, somente etanol ou somente água) e segundo o tipo de substrato utilizado para a adesão. Espécimes foram produzidos de cada dente e preparados histologicamente para coloração com tricrômico de Goldner. A zona de colágeno exposta (ZC) foi quantificada (μm) em... / Purpose. The overall purpose of this work, divided into three studies, was to evaluate the effect of chlorhexidine (CHX) in different excipients, ethanol and water, on the production and mechanical stability of resin-caries affected dentin bonds. Materials and Methods. In the first study, it was evaluated the influence of aqueous and alcoholic solution of CHX on the wettability of noncarious and caries-affected dentin by an adhesive system. Flat dentin surfaces (n=100) were produced, and 50 were submitted to a biological method of artificial caries induction. Within each type of substrate, noncarious and caries-affected dentin, the surfaces were divided into 5 groups (n=10): with smear layer, smear layer-free impregnated with water, smear layer-free impregnated with CHX in water, smear layer-free impregnated with ethanol and smear layer-free impregnated with CHX in ethanol. Contact angles between the dentin surface and the adhesive system Single Bond Plus were measured by using a goniometer and the data were submitted to ANOVA and Tukey tests ( =0.05). In the second study, it was evaluated the effect of CHX in different excipients, ethanol or water, on the collagen exposure in interfaces produced on noncarious and caries-affected dentin. Flat dentin surfaces were prepared in 24 noncarious human molars, and half of them were artificially decayed. The surfaces were divided into 8 groups (n=3) according to the treatment of the dentin after its conditioning with phosphoric acid (CHX in ethanol, CHX in water, water and ethanol) and to the type of substrate used for the adhesive procedures. Specimens were produced from each tooth and histologically prepared to be stained by Goldner’s trichrome. The zone of exposed collagen (CZ) was quantified (μm) under a light microscope and the data submitted to... (Complete abstract click electronic access below)
|
5 |
Influência de diferentes fontes de luz e distâncias de ativação no grau de conversão e propriedades mecânicas de sistemas adesivos / Influence of different light sources and distances of light curing tip on the degree of conversion and mechanical properties of dental adhesive systemsGaglianone, Lívia Aguilera, 1985- 17 August 2018 (has links)
Orientador: Giselle Maria Marchi Baron / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T23:11:15Z (GMT). No. of bitstreams: 1
Gaglianone_LiviaAguilera_M.pdf: 1613279 bytes, checksum: 151e990585e268deef7fdff242461689 (MD5)
Previous issue date: 2011 / Resumo: O objetivo do presente trabalho foi avaliar a influência de diferentes fontes de luz e distâncias de ativação no grau de conversão (GC) e nas propriedades mecânicas (módulo de elasticidade - ME e resistência à flexão - RF) de cinco sistemas adesivos (Scotchbond MP Plus - SBMP; Single Bond 2 - SB2; One-up Bond F Plus - OUP; Clearfil Protect Bond - CP, e P90 System Adhesive: primer - P90P e adesivo - P90B). Para realização dos testes, no experimento 1, as amostras de cada sistema adesivo foram divididas em três grupos (n=5), de acordo com as distâncias de ativação (2, 4 e 6 mm), enquanto que, no experimento 2, os espécimes foram divididos em dois grupos (n=5), dependendo da fonte de luz utilizada: halógena de quartzo-tungstênio (QTH) ou luz emitida por diodo (LED). Todos os adesivos foram fotoativados por 10s, exceto OUP cujo tempo de polimerização foi aumentado para 30s. Para avaliação das propriedades mecânicas, foram confeccionadas barras (7 mm X 2 mm X 1 mm) a partir de matrizes de silicone. Após 24 horas, o teste de três pontos foi realizado em Máquina de Ensaio Universal, com velocidade de 0,5 mm/min. O GC dos espécimes foi mensurado através do espectrômetro de raios infra-vermelhos transformada de Fourier (FTIR) e calculado comparando os espectros não-polimerizados e polimerizados dos sistemas adesivos. Os dados obtidos para ambos os experimentos foram analisados estatisticamente através de ANOVA 2-critérios e teste de Tukey (p?0,05). No experimento 1, avaliando GC, SB2, P90P e OUP (10s) mostraram diferença significante entre as distâncias testadas. Em todas as condições experimentais, SB2 obteve os melhores resultados de GC e OUP (10s), os piores valores. Contudo, analisando ME e RF, o melhor desempenho foi observado para o SBMP e P90B aos 2, 4 e 6 mm; SB2 foi inferior a todos os demais adesivos. Não houve diferença entre as distâncias de ativação para RF. No experimento 2, SB2, P90P e OUP (30s) mostraram melhor GC com QTH, já com LED, SB2 e P90P obtiveram os piores resultados de GC. Apenas P90B e OUP (30s) não apresentaram diferença estatística entre as fontes de luz. Avaliando ME, somente SBMP e CP mostraram significância estatística entre QTH e LED, enquanto que não houve diferença entre as fontes de luz para RF. Adesivos hidrófobos (SBMP, CP e P90B) obtiveram melhores valores de ME e RF, independentemente da fonte de luz testada. Dessa forma, pode-se concluir que o grau de conversão e as propriedades mecânicas dos sistemas adesivos são influenciados pelos fatores "distâncias de ativação" e "fonte de luz". Entretanto, essa interferência no comportamento do material depende da composição e características de cada sistema adesivo / Abstract: The aim of the present study was to evaluate the influence of different light curing units (LCUs) and distances of light curing tip on the degree of conversion (DC) and mechanical properties (elastic modulus - E and flexural strength - FS) of five adhesive systems (Scotchbond MP Plus - SBMP; Single Bond 2 - SB2; One-up Bond F Plus - OUP; Clearfil Protect Bond - CP, and P90 System Adhesive: primer - P90P and bond - P90B). To perform the tests, in experiment 1, samples of each adhesive were divided into three groups (n=5), according to light tip distance (2, 4 and 6 mm), whereas, in experiment 2, specimens were divided into two groups (n=5), depending on LCU evaluated: quartz tungsten halogen (QTH) and blue light emitting diode (LED). All adhesive systems were irradiated for 10s, except for OUP which had its activation time increased to 30s. For evaluation of mechanical properties, specimens were prepared using bar silicon molds (7 mm X 2 mm X 1 mm). After storage for 24h, the three-point flexural test was performed, at a crosshead speed of 0,5 mm/min, using a universal testing machine. DC was measured using Fourier Transform infrared spectroscopy (FTIR) and it was calculated by comparing the polymerized and unpolymerized spectra obtained from adhesive resins. The data were statistically analyzed (p?0.05) using a two-way ANOVA and Tukey's test. In experiment 1, DC was affected by distances of light curing tip and adhesive system. The distances were statistically significant for SB2, P90P and OUP (10s). For all distances tested, SB2 showed the best DC values and OUP (10s), the worst ones. However, for E and FS, better performance was obtained for SBMP and P90B at 2, 4 and 6mm, while SB2 presented the lowest values. For FS, there was no difference between distances tested. In Experiment 2, DC was also affected by LCUs and adhesive system. SB2, P90P and OUP (30s) showed better DC values for QTH, and with LED, SB2 and P90P presented the worst ones. Only P90B and OUP (30s) were not statistically significant among LCUs. For E, only SBMP and CP showed difference between QTH and LED, whereas, for FS, there was no difference among light sources. Non-solvated adhesives (SBMP, CP and P90B) presented the best E and FS values, regardless of light sources tested. It can be concluded that DC and mechanical properties of adhesive systems are influenced by factors "distances of light curing tip" and "light sources". Nevertheless, this interference is material dependent / Mestrado / Dentística / Mestre em Clínica Odontológica
|
6 |
Determinação do numero de dentes, palitos e influencia da localização dos palitos na dentina para o ensaio de microtração / Determination of sample size, plot size and beams location on the dentin surface for microtensile test methodArias, Vanessa Gallego 16 February 2007 (has links)
Orientadores: Luiz Andre Freire Pimenta, Glaucia Bovi Ambrosano / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T12:07:02Z (GMT). No. of bitstreams: 1
Arias_VanessaGallego_D.pdf: 611326 bytes, checksum: ec27b51bc2f986d28374469ca93f8730 (MD5)
Previous issue date: 2007 / Resumo: Os objetivos deste trabalho foram determinar o número ótimo de dentes (tamanho da amostra), número de palitos (tamanho da parcela) e a influência da localização dos palitos na dentina para o ensaio de Microtração. Foram utilizados 80 dentes bovinos, os quais apresentaram as superfÃcies vestibulares coronárias desgastadas, para a exposição dentinária. Os dentes foram divididos, aleatoriamente, em dois grupos (n=40). Os sistemas adesivos utilizados foram o Single Bond (SB- G1) e Tyrian SPE /One Step Plus (TY- G2). Os dentes foram restaurados com resina composta Filtek Z-250, formando um bloco com dimensões de 4 mm de largura, 6 mm de comprimento e 4 mm de altura, sendo posteriormente seccionados em cortadeira metalográfica, obtendo-se palitos com aproximadamente 0.8 mm2 de área de interface adesiva (dente/resina), totalizando 12 palitos por dente. Os palitos foram fixados a uma máquina Universal de Ensaio para a obtenção dos valores de união, em MPa, com velocidade de avanço de 0,5mm/min. A partir do delineamento inteiramente ao acaso, com 40 repetições por sistema adesivo e 12 palitos por dente, a análise de variância foi realizada e os cálculos das respectivas médias e desvios-padrão. Para a determinação do número de repetições (dentes), o poder do teste foi calculado em função do número de dentes. Adicionalmente, diferentes tabelas foram obtidas através da simulação da variação entre as médias dos grupos, adotando-se 5, 10, 15, 20, 25, 30, 35 e 40% de variação inter-grupos. Também foi estipulado o Coeficiente de Variação do experimento, ou variação intra-grupos, em 10, 20 e 30% e o mesmo procedimento, citado acima, foi realizado. Para a determinação do número de palitos por dente (tamanho da parcela), 12 diferentes simulações (tamanhos) foram criados a partir dos valores originais, através da exclusão aleatória de 1 palito a cada vez que a ANOVA foi realizada até a permanência de apenas 1 palito por dente. O ponto de máxima curvatura modificado, proposto por Méier & Lessman (1971) foi calculado. Adicionalmente, a mesma metodologia foi aplicada, utilizando-se 20 e 10 dentes por grupo. Já para a análise da região dentinária foi aplicada a Análise de Variância em parcela subdividida e teste de Tukey, para a verificação das possÃveis diferenças regionais e suas interações. Os resultados demonstraram que a utilização de 6 dentes por grupo presentou um poder de 88%. Entretanto, este número pode variar em função do CV e da diferença entre as médias dos grupos. Já para o tamanho ideal de parcela obtido foi de 7 palitos por dente, independente do número de unidades experimentais. Com relação à localização dos palitos na dentina, os resultados demonstraram diferença estatÃstica entre os palitos nas diferentes linhas (p=0,005) e entre as colunas (p=0,00001). Também houve a interação entre sistema adesivo e linha (p=0,019). O teste de Tukey demonstrou que tanto para o sistema adesivo SB quanto para o TY os melhores resultados foram encontrados nos palitos centrais. Concluiu-se o número mÃnimo de dentes foi de 6 com 7 palitos por dente, utilizando os palitos centrais da área de união / Abstract: The objectives of this study were to determine the ideal number of teeth (sample size), number of beams per tooth (plot size) and the influence of the beams location on the dentin surface for microtensile testing-MT. Eighty bovine teeth were selected and the dentin was flat exposed. The teeth were randomly divided in two groups (n=40), using the adhesive systems: Single Bond (SB- G1) and Tyrian/One Step Plus (TY- G2). A â?¿crownâ?? was done with composite resin Filtek Z-250, presenting 4 mm width, 6 mm length and 4 mm high. The specimens were sectioned, at a metalographic machine, in 12 beams with 0,8mm2 area interface (dentin/resin). The beams were attached in a Universal Machine and the MT was performed (0.5mm/min) and the bond strength values expressed in MPa. Using the study design random model, with 40 repetitions per group and 12 beams per tooth, the one-way ANOVA was applied and the means and standard deviation were obtained. To determine the optimal sample size, the powerâ?¿s test was calculated. Additional values were simulated decreasing the difference between the groups means, using 5, 10, 15, 20, 25, 30, 35 and 40% (inter-tooth variability). Different CV were used (10, 20 and 30%) and the same procedures describes above were performed. For the analysis of the plot size, 12 different experimental unit sizes were created from the original
values by excluding randomly 1 beam every time when one-way ANOVA was performed until only 1 beam per tooth was left, using 40, 20 and 10 teeth per group (EU). The experimental coefficients of variation (CVexp) were calculated and a regression function was estimated. The maximum curvature point was calculated from the formula proposed by Meier & Lessman (1971). For the dentin region, the Split pot analysis and Tukeyâ?¿s test were applied to analyze the regional influence and the possible interactions. The results demonstrated that using 6 teeth, the power arranged 88%. But this number may variety depending CV and the means between groups. The optimal plot size was obtained with 7 beams per tooth independently of the EU. The regional analysis demonstrated statistical significant differences between rows (p=0.005) and columns (p=0.00001). The interaction between adhesive system and rows was statistical significant (p=0.019). The Tukeyâ?¿s test demonstrated that highest bond strength values were to the central beams for both adhesive systems. The conclusion of the study was the optimal sample size was 6 teeth per group, presenting 7 beams per tooth, using the central beams / Doutorado / Dentística / Doutor em Clínica Odontológica
|
7 |
Avaliação da adaptação à dentina de vários agentes de proteção com ou sem sistemarestaurador adesivo, em função de diferentes tratamentos da superfície dentinária. / Evaluation of the marginal finishing of cavity preparations in relation to different instrumentation methods.Margareth da Silva Coutinho 05 April 2000 (has links)
Este estudo quantificou micrometricamente o índice de adaptação à dentina (presença ou ausência de fenda interfacial) de vários agentes protetores à base de hidróxido de cálcio de ativação química - Dycal e de luz visível - Prisma VLC Dycal e Ultra-Blend® plus e cimento de ionômero de vidro convencional - Ketac Bond e fotoativado - Vitrebond; associados a diferentes tratamentos de superfície dentinária, com e sem a presença de sistema restaurador adesivo (Primer & Bond 2.1 + TPH Spectrum). Os tratamentos dentinários foram jatos de ar/água, condicionamento com ácido poliacrílico a 25% por 10s e ácido fosfórico a 37% por 15s. Foram utilizados 200 dentes, os quais numa metade foi desgastado o esmalte e os preparos realizados em dentina e na outra metade repetiu-se o preparo cavitário envolvendo esmalte e dentina. Cavidades tipo classe V foram realizadas com 3mm de diâmetro e 0,8mm de profundidade em dentina e 0,8mm quando envolvido o esmalte. Após o preenchimento da cavidade, os corpos-de-prova foram incluídos em resina epóxica e seccionados longitudinalmente no sentido vestíbulo-lingual. Foram obtidas réplicas em negativo utilizando-se material de moldagem à base de polivinil siloxana (Aquasil), para a avaliação da desadaptação à dentina, por meio de microscópia de luz refletida em campo escuro. Os dados obtidos microscopicamente foram submetidos aos Testes de Kruskal-Wallis e as comparações múltiplas pelo Teste de Dunn. Os resultados demonstraram que quando comparados o comprimento e a largura da desadaptação à dentina dos agentes protetores, entre as condições experimentais com e sem a presença do sistema restaurador adesivo, o cimento de ionômero de vidro fotopolimerizável Vitrebond obteve os melhores resultados, sobrepujando, inclusive, o Ketac Bond ativado quimicamente. Numa posição intermediária vêm o Ultra-Blend® plus e o cimento de hidróxido de cálcio auto-ativado Dycal e, por último, o cimento de hidróxido de cálcio fotopolimerizável Prisma VLC Dycal, que apresentou a maior desadaptação. / The present study evaluated the length and width of interface gaps between dentin and the following lining materials: chemically cured Dycal Advanced Formula II and light cured Prisma VLC Dycal and Ultra-Blend® plus calcium hydroxide bases; chemically cured Ketac Bond and light cured Vitrebond glass ionomer cements. Dentin cavities prepared in human teeth were pre-treated with only an air/water Spray or with a 25% Polyacrylic acid solution for 10s, or a 37% Phosphoric acid solution for 15s. One half of cavities were prepared in dentin (3mm wide, 0.8mm deep) and have been filled with only the linning materials. The other half of the cavities were enamel dentin cavities had a 0.8mm with enamel layer, 3mm wide, 0.8mm deep below the dentinoenamel junction. Theses cavities received a layer of lining material have then been treated with an adhesive system an restored with a composite resin. In order to access the dentinal interfacial adaptation, the specimens were sectioned longitudinally in buccal to lingual direction thorough the center of the restorations. Low viscosity polyvinyl siloxane impression material (Aquasil) was used to obtain negative replicas. The replicas were examined with a Zeiss Photomicroscope and the length and width of the gaps were measured. The values were submitted to Kruskall Wallis Test and Multiple Comparation Dunn Test. Results demonstrated that, on the experimental conditions used, the glass ionomer cements obtained the best results, specially the Vitrebond. The Ultra-Blend plus and Dycal, showed an intermediary position. Prisma VLC Dycal showed the powerest adaptation.
|
8 |
Avaliação in vitro do tiossulfato de sódio, em diferentes concentrações e tempos de aplicação, na resistência de união à dentina intracoronária tratada com hipoclorito de sódio / In vitro evaluation of sodium thiosulfate, at different concentrations and times of application, in the bond strength to intracoronary dentin treated with sodium hypochloriteCorrêa, Ana Carolina Pimentel, 1989- 22 August 2018 (has links)
Orientador: Caio Cezar Randi Ferraz / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T00:11:16Z (GMT). No. of bitstreams: 1
Correa_AnaCarolinaPimentel_M.pdf: 2431017 bytes, checksum: 0e40b6c1be77015400d7410e76397857 (MD5)
Previous issue date: 2013 / Resumo: A resistência de união de sistemas adesivos à dentina é comprometida quando esta é tratada com hipoclorito de sódio (NaOCl). Soluções antioxidantes têm sido propostas a fim de restabelecer os valores de adesão. Embora vários estudos tenham avaliado a eficiência do ascorbato de sódio, outras substâncias devem ser pesquisadas. O objetivo deste estudo foi avaliar a eficácia do tiossulfato de sódio (Na2S2O3), em diferentes tempos e concentrações, no restabelecimento da resistência de união à dentina tratada com NaOCl. Coroas de dentes bovinos foram cortadas de forma a expor a dentina da câmara pulpar. As superfícies dentinárias foram tratadas como se segue: grupo 1- cloreto de sódio a 0,9% durante 30 min.; grupo 2: NaOCl a 5,25% durante 30 min., EDTA a 17% durante 3 minutos e mais NaOCl a 5,25% durante 1 min.; nos grupos 3, 4, 5, 6, 7 e 8 foi realizado o mesmo protocolo do grupo 2, porém seguido da aplicação de Na2S2O3 a 0,5% por 1 min. (grupo 3), 5 min. (grupo 4) e 10 min. (grupo 5) e de Na2S2O3 a 5% por 1 min. (grupo 6), 5 min. (grupo 7) e 10 min. (grupo 8); grupo 9- imersão em cloreto de sódio a 0,9% por 10 min., após o mesmo tratamento realizado no grupo 2. Depois disso, o sistema adesivo Scotchbond Multipurpose foi aplicado na dentina da câmara pulpar, seguido da resina composta Z250. Após armazenamento em 100% de umidade por 24 horas a 37 ºC, 25 palitos foram obtidos a partir das amostras de cada grupo e submetidos ao ensaio de microtração. Os dados convertidos em MPa foram analisados por ANOVA e teste de Fisher (p <0,05). Os grupos 2 e 9 apresentaram resistência de união significativamente mais baixa do que a do controle (grupo 1). Não houve diferença estatisticamente significativa entre a aplicação da solução de Na2S2O3 a 0,5% ou 5%, durante 5 ou 10 min., para aumentar a resistência de união à dentina comprometida pelo tratamento com NaOCl (p> 0,05). Não houve diferença estatisticamente significativa entre os grupos 1 e 8 (p = 0,944), mas ambos são estatisticamente diferentes dos grupos 2, 3 e 9. Todos os grupos estudados apresentaram dois ou mais padrões de fratura, sendo que o predominante foi o coesivo em camada híbrida. Observou-se que os grupos que apresentaram maior resistência de união (Grupos 1 e 8) foram os que apresentaram o maior percentual de fraturas do tipo coesiva em resina ou dentina. Pode-se concluir que o NaOCl reduziu significativamente a resistência de união à dentina da câmara pulpar. O restabelecimento da resistência de união à dentina comprometida pelo tratamento com NaOCl não dependeu da concentração do Na2S2O3, quando este foi usado por 5 ou 10 min. Depois de aplicar por 1min, o Na2S2O3 a 5% é capaz de restaurar a resistência de união à dentina tratada com NaOCl / Abstract: The bond strength to dentin is compromised when it is treated with sodium hypochlorite. Several antioxidant solutions have been proposed in order to reestablish the adhesion values. Although several studies have evaluated the efficiency of sodium ascorbate, other substances should be assessed. The purpose of this study was to evaluate the antioxidant efficiency of sodium thiosulfate (Na2S2O3), at different times and concentrations, in reestablishing the adhesive bond strength to sodium hypochlorite-treated dentin. Crowns of bovine incisors were cut to expose the pulp chamber. The dentin surfaces were treated as follows: group 1: 0.9% sodium chloride for 30 min; group 2: treated with 5.25% sodium hypochlorite (NaOCl) for 30 min, 17% EDTA for 3 min and additional 5.25% NaOCl for 1 min; groups 3, 4, 5, 6, 7 and 8: followed the same treatment performed in group 2, adding the final applications of 0.5% sodium thiosulfate solution for 1 min (group 3), 5 min (group 4) and 10 min (group 5) or applications of 5% sodium thiosulfate solution for 1 (group 6), 5 (group 7) and 10 min (group 8); group 9: immersion in 0.9% sodium chloride for 10 min after the same treatment performed in group 2. After that, Scotchbond Multipurpose adhesive system was applied to pulp chamber dentin, followed by Filtek Z250 composite. After storage in water for 24h at 37oC, twenty-five rectangular sticks were obtained from the specimens of each group and subjected to the microtensile bond test. The data converted to MPa were analyzed by one-way ANOVA and Fisher's test (p<0.05). The groups 2 and 9 had significantly lower bond strength than the control (group 1). There was no statistically difference between application of 0.5% or 5% sodium thiosulfate solution for 5 or 10 min to increase the compromised bonding to NaOCl-treated dentin (p>0.05). There was no statistically significant difference between groups 1 and 8 (p = 0.944), but both are statistically different from the groups 2, 3 and 9. All groups studied presented two or more failure mode and the fractures predominating are the cohesive in the hybrid layer. It was observed that the groups that showed the highest bond strength (Groups 1 and 8) were the ones with the highest percentage of cohesive resin / dentin fractures type. It was concluded that sodium hypochlorite significantly reduced the bond strength to pulp chamber dentin. The bond strength reestablishment on compromised NaOCl-treated dentin do not depended on the sodium thiosulfate concentration when it is used for 5 and 10 min. After applied for 1min, 5% sodium thiosulfate is able to restore the bond strengths to NaOCl-treated dentin / Mestrado / Endodontia / Mestra em Clínica Odontológica
|
9 |
Influence of Erosive and Abrasive Cycling on Bonding of Diferent Adhesive Systems Enamel: An in situ studyCiccone Giacomini,Marina, Casas-Apayco, Leslie, Moreira Machado,Camila, Carvalho de Almendra Freitas,Maria Cristina, Atta,Maria Teresa, Wang, Linda January 1900 (has links)
This study evaluated the impact of orange juice on the bond strength (BS) of dentin bonding systems (DBSs) to enamel surface after simulation with an in situ/ ex vivo erosive cycling. One hundred and ninety two bovine enamel fragments (4x4x2 mm) were obtained and randomized regarding superficial microhardness and distributed to palatal devices for 8 volunteers, in three phases (one for each DBS), containing 8 blocks, which were, allocated in 4 pairs. Daily, these pairs were subjected extraorally to the following conditions: CONTneither erosive nor abrasive challenge; ERO- erosive challenge only; ABR- abrasive challenge only and ERO + ABR- with erosive and abrasive challenges. Erosive cycles (immersion in orange juice, 3 times/day/5 min/5 days) or/and abrasive challenges (electric toothbrush, 3 times/day/1 min/5 days) were performed. After these cycles, all specimens were restored with the adhesive systems Adper Scotchbond Multi Purpose (MP), Adper Single Bond 2 (SB) or Clearfil SE Bond (SE), and the composite resin Filtek Z250. After 7 days, sticks (area ≅1 mm2) were obtained and subjected to the microtensile bond strength test (μTBS) at 0.5 mm/min. Data was statistically analyzed by ANOVA and Tukey tests (a=0.05). Failure modes were determined using a digital microscope (40×). DBS was the only statistical significant factor. SE was the unique DBS not affected in any challenge, whereas MP and SB performed according to the scenario. The adhesive and mixed failures were predominant in all groups. Overall performance suggested that BS to enamel after erosive /abrasive challenged by orange juice was not affected and it was material-dependent
|
10 |
Estudo in vitro do efeito da clorexidina e do etanol na dentina em diferentes condições do substrato dentinário e tempos de armazenagem : Study in vitro the effect of chlorhexidine and ethanol on dentin in different conditions of the dentin substrate and storage times / Study in vitro the effect of chlorhexidine and ethanol on dentin in different conditions of the dentin substrate and storage timesCosta, Ana Rosa, 1977- 05 October 2018 (has links)
Orientador: Regina Maria Puppin Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-10-05T18:49:21Z (GMT). No. of bitstreams: 1
Correr_AnaRosaCosta_D.pdf: 3218831 bytes, checksum: f30505368b581fed81781723b234fbd9 (MD5)
Previous issue date: 2013 / Resumo: O propósito deste estudo foi avaliar a influencia de diferentes tipos de substrato (Capitulo 1) e tratamento com etanol 100% (Capitulo 2) ou digluconato de clorexidina a 2% (CHX) (Capitulo 3) na resistência e longevidade da união compósito/dentina, apos diferentes períodos de armazenagem. Os dentes humanos hígidos foram divididos em 3 grupos, de acordo com o substrato dentinario: (Sd) dentina hígida, (Ci) dentina infectada (manutenção da carie) e (Ca) dentina afetada (remoção parcial de carie). As superfícies oclusais de terceiros molares hígidos foram removidas com disco diamantado dupla face sob refrigeração, a fim de expor a superfície plana dentinaria hígida, a qual foi submetida ao desenvolvimento da lesão de carie artificial com S. mutans. Brocas esféricas foram usadas para remover parcialmente o tecido cariado pigmentado, ate que permanecesse apenas a dentina levemente corada (Ca). Em seguida, os dentes foram novamente subdivididos, de acordo com o tratamento da superfície: Grupo Controle (Ct) - nenhum tratamento (Capitulo 1); Ct e (Et) - aplicação de etanol 100% (Capitulo 2); e, Ct e (CHX) - aplicação de digluconato de clorexidina a 2% (Capitulo 3). O substrato foi condicionado com acido fosfórico a 35% por 15 s, lavado por 30 s e seco com leve jato de ar. CHX ou Et foram aplicados apos o condicionamento acido. O sistema adesivo Adper Single Bond 2 (3M ESPE) foi aplicado de acordo com as recomendações do fabricante e fotoativado por 20 s com a fonte de aparelho de luz XL 2500. Sobre a superfície de união foram inseridos incrementos de 2 mm do compósito Z350 (3M ESPE), polimerizados usando a fonte de luz XL 2500 por 40 s, ate confeccionar um bloco com 6 mm de altura. As amostras foram armazenadas em água destilada a 37o C por 24 horas. Apos, os dentes foram seccionados perpendicularmente a área de união, de modo a obter palitos com área de secção transversal de 1mm2. Os palitos foram armazenadas em três períodos: 24 horas, 6 meses e 1 ano. Em seguida, as amostras foram submetidas ao ensaio de resistência de união a microtração usando a maquina de ensaio EZ test (EZS, Shimadzu) a velocidade de 0,5 mm/minuto. Os dados foram submetidos a Analise de Variância e ao teste de Tukey HSD (?=0,05). A união em Sd mostrou valores de resistência de união significativamente maior quando comparado a Ca e Ci. As amostras armazenadas nos períodos de 6 meses e 1 ano resultou na diminuição da resistência de união, independente do tipo de substrato e/ou tratamento. O etanol não foi efetivo em melhorar a resistência de união para os três substratos de dentina avaliados. A clorexidina não influenciou na resistência de união nos períodos de armazenagem avaliados, independente dos substratos / Abstract: The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) and 100% ethanol wet-bonding (Et) on the degradation of the adhesive system bond strength in sound or artificial caries-affected/infected dentin after different storage times under microtensile test (_TBS). The sound teeth were divided into 3 groups, according to dentin substrates: sound dentin, caries-infected dentin (maintained of caries) and caries-affected dentin (partial removal of caries). Non-carious human third molars had their occlusal enamel removed with a slow speed diamond saw, under copious water-cooling to expose a flat-surfaced sound dentin, which was submitted to the microbiological challenge (S. mutans) for the development of artificial caries. Spherical drill was used to remove soft pigmented carious tissue till hard and slightly pigmented dentin remains (Ca). After, the teeth will be assigned into 3 subgroups according to surface treatment: water wet- bonding (Ct) (Chapter 1); Ct and 100% ethanol application (Et) (Chapter 2); and, Ct and chlorhexidine digluconate 2% application (CHX) (Chapter 3). The substrate will was etched with 35% phosphoric acid gel for 15 s, rinsed for 30 s with tap water and dried with oil/water-free air. The CHX or Et was applied for 60 s, just after etching with 35% phosphoric acid gel. The adhesive system Adper Single Bond 2 (3M ESPE) was applied according to the manufacturer's instruction and polymerized for 10 s by a light-curing unit XL 2500. The bonded surfaces were coupled with a composite resin Filtek Z350 (3M ESPE) applied in 2 mm increments and polymerized using a curing unit XL 2500 (3M ESPE) for 40 s for each increment and to build 6 mm thick block. The restored teeth were stored in distilled water at 37o C for 24 h. After this period, the restored teeth were longitudinally sectioned across the bonded interface to produce a series of 1.0mm2 beams. The specimens were then submitted to three storage periods: 24 hours, 6 months, or 1 year. Afterwards, the storage periods, the specimens were submitted to a microtensile bond strength (_TBS) using EZ test machine (EZS, Shimadzu) at a crosshead speed of 0.5 mm/min until failure. Data were submitted to ANOVA and Tukey's HSD test (?=0.05). The bonding with sound dentin showed _TBS values significant higher when compared to caries-affected and caries-infected dentin. The 6 months and 1 year storage periods resulted in decreased bond strengths for all dentin conditions and/or treatment. The ethanol was not effective to improve the _TBS for the three dentin substrates evaluated. The CHX did not affect the 24- hour, 6 and 12 months _TBS, independent of the tested dentin substrates / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários
|