In this thesis, we investigated charge carrier properties of two series of organic semiconductors with time of flight measurement. Charge carrier mobility is calculated in different electron filed and fitted to Poole-Frenkel model. In the first part, we investigated carrier properties of pyrrole derivatives .The mea- surement result of pyrrole derivatives with different functional group indicate that trans- port properties may effected by this different functional group and the bonding position. There have two different type of transport properties that is single transport and bipolar transport. In addition, carrier mobility have more than two order difference with this different functional group. Finally, we investigated carrier properties of anthracene derivatives. The measure- ment result indicate that the intermolecular aggregation can be solved by synthesizing another functional group to form polymer. This method not only perform excellent thin film stability but also keep bipolar transport property after synthesizing.

<p>Over the last few decades, bulk-heterojunction organic photovoltaic devices comprising an intimately mixed donor-acceptor blend have gained serious attention due to their potential for being cheap, light weight, flexible and environmentally friendly. In this thesis, APFO-3/PCBM bulk-heterojunction based organic photovoltaic devices with an inverted layer sequence were investigated systematically. Doctor blade coating is a technique that is roll-to-roll compatible and cost efficient and has been used to fabricate the solar cells.</p><p>Initial studies focused on optimization of the electrodes. A thin film of the conductive polymer PEDOT:PSS was chosen to be the transparent anode. Different PEDOT:PSS films with respect to the film thickness and deposition temperature were characterized in terms of conductivity and transmission. Decent conductance and transmittance were obtained in the films deposited with wet film thickness setting of 35 μm, The cathode was fabricated from a metal bilayer comprising Al and Ti with an area about 1 cm², and the best-working cathodes contained a 70 nm thick Al layer covered by a thin Ti layer of about 10 -15 nm.</p><p>Optimized coating temperature and wet film thickness settings for the active layer and PEDOT:PSS layer were experimentally determined. The highest efficiency of the APFO-3/PCBM based inverted solar cells fabricated by doctor blading was 0.69%, which exceeded the efficiency of spin-coated inverted cells.</p><p>A higher efficiency (0.8 %) was achieved by adding a small amount of high molecular weight polystyrene to the active layer. Morphological changes after adding of the polystyrene were observed by optical microscopy and AFM. A coating temperature dependent phase separation of the APFO-3/PCBM/polystyrene blend was found.</p><p> </p>

Over the last few decades, bulk-heterojunction organic photovoltaic devices comprising an intimately mixed donor-acceptor blend have gained serious attention due to their potential for being cheap, light weight, flexible and environmentally friendly. In this thesis, APFO-3/PCBM bulk-heterojunction based organic photovoltaic devices with an inverted layer sequence were investigated systematically. Doctor blade coating is a technique that is roll-to-roll compatible and cost efficient and has been used to fabricate the solar cells. Initial studies focused on optimization of the electrodes. A thin film of the conductive polymer PEDOT:PSS was chosen to be the transparent anode. Different PEDOT:PSS films with respect to the film thickness and deposition temperature were characterized in terms of conductivity and transmission. Decent conductance and transmittance were obtained in the films deposited with wet film thickness setting of 35 μm, The cathode was fabricated from a metal bilayer comprising Al and Ti with an area about 1 cm2, and the best-working cathodes contained a 70 nm thick Al layer covered by a thin Ti layer of about 10 -15 nm. Optimized coating temperature and wet film thickness settings for the active layer and PEDOT:PSS layer were experimentally determined. The highest efficiency of the APFO-3/PCBM based inverted solar cells fabricated by doctor blading was 0.69%, which exceeded the efficiency of spin-coated inverted cells. A higher efficiency (0.8 %) was achieved by adding a small amount of high molecular weight polystyrene to the active layer. Morphological changes after adding of the polystyrene were observed by optical microscopy and AFM. A coating temperature dependent phase separation of the APFO-3/PCBM/polystyrene blend was found.

Planetary ball milling (PBM) is a well-known technique for efficient size reduction and homogenization of materials that has been used for many decades in various engineering and industrial processes. More recently, it has emerged as a unique top-down nanofabrication approach for nanomaterials based on nanoscale grinding. However, its potential application in nanostructured thin film fabrication has not been fully explored, as only a limited number of studies have been carried out. In this work, the effects of different grinding parameters (speed, time and solvents) were used to create previously unstudied nanoscale grinding conditions for nanostructured thin film materials via PBM with distinct and novel properties: Nanoparticles of silicon, titanium disilicide (TiSi2) and zinc oxide (ZnO) ground in different solvents (deionized (DI) water/ ethylene glycol (EG)/isopropyl alcohol) resulted in colloidal suspensions (or nanoinks) that could be used to coat various substrates (wafers, glass, flexible substrates, etc.) via drop casting, doctor blading or dip coating. Thin film properties such as wettability, electrical conductivity and gas sensing behavior are studied. The fabricated thin film coating properties could be tuned depending on the combination of starting powder materials, grinding parameters and resulting nanoparticle size/geometry: The influence of surface chemistry, solvent type, particle geometry, surface roughness and defects was shown to alter the conductivity and surface wettability of the resultant films. Thus, thin films formed using PBM nanoinks allow varied and tunable properties for advanced multi-functional coatings and devices. To demonstrate the feasibility of PBM nanoinks for thin film device applications, ZnO nanoinks were used to create chemiresistive gas sensors that operate at room temperature. By varying grinding parameters (speed, time and solvent) thin film sensors with differing particle sizes and porosity were produced and tested with air/oxygen against hydrogen, argon and methane target gas species, in addition to relative humidity. Grinding speeds of up to 1000 rpm produced particle sizes and RMS thin film roughness below 100 nm, as measured by atomic force microscopy and scanning electron microscopy. Raman spectroscopy, photoluminescence and x-ray analysis confirmed the purity and structure of resulting films. The peak gas sensor response was found for grinding parameters of 400 rpm (average particle size 275 nm) and 30 minutes (average particle size 225 nm) in EG and DI water, respectively, which could be correlated to an increased film porosity and an enhanced electron concentration resulting from adsorption/desorption of oxygen ions on the surface of ZnO nanoparticles. Similarly, gas response and dynamic behavior were found to improve as the operating temperature was increased between 100 and 150 °C. These results demonstrate the use of low-cost PBM nanoinks to optimize the active materials for solution-processed thin film gas/humidity sensors that can operate at room temperature for use in environmental, medical, food packaging, laboratory, and industrial applications. Overall, the nanogrinding technique can produce large amounts of nanoparticle suspension with variable particle sizes for creating thin films with tunable properties. By adjusting grinding parameters, the nanoparticle shape/size and properties can be varied resulting in nanoparticle inks for inexpensive coatings on various substrates and for use in different applications. / Graduate