Made available in DSpace on 2014-12-17T14:58:13Z (GMT). No. of bitstreams: 1 AlcioneOG_DISSERT.pdf: 4986234 bytes, checksum: d81c2eeeb91a55690b1f5b9671a9a5e3 (MD5) Previous issue date: 2011-08-26 / Use of natural fibres as a reinforcement material in the manufacture of composites show a series of advantages: availability, biodegradability, low weight and regeneration in relation to synthetic fibres, thus justifying its utilization. In the present research work, composites were developed with chicken feathers (KF), using unsaturated polyester resin as matrix, for diversified applications, mainly in the furniture/timber industry.At present, in Brazil the chicken feathers are used as part of the animal feed, even though this material possesses low aggregated value. The chicken feathers are hollow, light and resistant. After washing with water at room temperature, a part of the chicken feathers were treated with 2% NaOH. Composites were manufactured using treated and untreated chicken feathers with unsaturated orthothalic polyester resin and 1% peroxide as catalyser, obtained in the commerce. Samples with size 150x25x3 mm for mechanical tests were cut by laser in the composite plate. Mechanical analyses were carried out in the Laborat?rio de Metais e Ensaios Mec?nicos UFRN. All the analyses were in accordance with ASTM standards. SEM analyses were also carried out on the samples.In the analyses of the results obtained, it was observed that the composites made with untreated chicken feathers showed better results (Traction 11.406 MPa and 9.107 MPa Bending 34.947 and 20.918 MPa for samples with and without treatment respectively) compared to the composite with treated feathers. Very low values of the water absorption results, evidenced the impermeability characteristic of the feathers. From the SEM images, the structure, fracture and the fibre/matrix adsorption can be evidenced. In the flammability test, it was observed that despite the feathers having sulfur as a constituent, natural inhibitor of flame, no burning support of the composites, because the manufacturing process of the composite / O uso de fibras naturais como refor?o em comp?sitos apresenta uma s?rie de vantagens: abund?ncia, biodegradabilidade, baixo peso e regenerabilidade em rela??o ?s fibras sint?ticas, justificando sua utiliza??o. Na presente pesquisa foram desenvolvidos comp?sitos com penas de frango (KF), utilizando resina de poli?ster n?o-saturado como matriz. Atualmente, no Brasil, as penas de frango s?o utilizadas como parte de ra??o animal, por?m este produto possui um baixo valor agregado. As penas s?o um material oco, leve e resistente. Ap?s a lavagem com ?gua em temperatura ambiente uma parte das penas foi tratada com 2% de NaOH. Foram fabricados dois comp?sitos, um com as penas tratadas e outro sem tratamento, usando o processo de molde fechado por compress?o, utilizando a resina de poli?ster ortoft?lica e 1% de per?xido MEK (per?xido de metil etil cetona) como iniciador, adquiridos no com?rcio local. As amostras com 150x25x3 mm de tamanho para os ensaios mec?nicos foram cortadas a laser na placa do comp?sito. Os ensaios de tra??o e flex?o em tr?s pontos foram realizados no Laborat?rio de Metais e Ensaios Mec?nicos - UFRN. Todas as an?lises estavam de acordo com as normas da ASTM. As amostras resultantes dos ensaios mec?nicas foram avaliadas no MEV. Com base nas observa??es dos resultados nos ensaios mec?nicos, (Tra??o 11,2 Mpa e 8,3 Mpa; Flex?o 34,9 Mpa e 22,9 MPa para as amostras sem e com tratamento respectivamente) observou-se que os comp?sitos refor?ados com as penas sem tratamento apresentaram um melhor comportamento quando foram expostos a carregamentos tanto de tra??o quanto de flex?o. O ensaio de absor??o evidenciou nos valores de absor??o de ?gua, uma das caracter?sticas da prote?na existente nas penas, a queratina, a sua capaciade de impermiabiliza??o a ?gua. Nas imagens do MEV foi poss?vel verificar a estrutura da pena, as regi?es de ruptura do comp?sito e a ades?o fibra/matriz. No ensaio de inflamabilidade, observou-se que apesar das penas terem como constituinte o enxofre, inibidor natural de chama, n?o houve a susten??o da queima nos comp?sitos, devido o processo de fabrica??o do comp?sito

Made available in DSpace on 2014-12-17T14:58:14Z (GMT). No. of bitstreams: 1 JoaoPMS_DISSERT.pdf: 2368005 bytes, checksum: d7875a294c5267dc99db89f3b20a7106 (MD5) Previous issue date: 2012-03-14 / In the present work, three composites with distinct reinforcements (polyester, modal e polyester + modal), all if a unsaturated orthophthalic polyester resin as matrix were used, in order to conduct a comparative study by mechanical tests and water absorption. The fibre mats were prepared in a mat preparatory by immersion developed in the Textile Engineering Laboratory. The composites were manufactured using a closed mould process by compression using an unsaturated orthophthalic polyester resin as matrix and 1% MEK (methyl ethyl ketone peroxide) as an initiator. In each composite twelve samples with the dimensions of 150x25x3 mm were cut randomly for the mechanical analysis (tension x extension, three points bending and water absorption and Scanning Electron Micsroscopy). The mechanical tests were carried out in the Laborat?rio de Metais e Ensaios Mec?nicos UFRN . All the analyses were carried out according to the ASTM norms. The resultant samples from the mechanical analysis were subjected for the Scanning Electron Microscopy analysis. Based on the results obtained, it was observed that the reinforced composite with two fibres (modal + polyester) presented better results in comparison to the other two composites both in the tension/extension as well on the three point bending tests. In the water absorption test, it was possible to observe an equilibrium in the water absorption by the modal and polyester composite, due to the union of the two fibres. In the SEM images, the regions of rupture in the composites as well as the adsorption between the fiber and the matrix could be observed / No presente trabalho foram fabricados tr?s comp?sitos com refor?os distintos (poli?ster, modal e poli?ster + modal), todos com uma matriz de resina de poli?ster ortofit?lico n?o saturado, com o objetivo de realizar um estudo comparativo atrav?s de ensaios mec?nicos e absor??o d ?gua. As mantas de fibras foram preparadas num preparador de manta por imers?o desenvolvido no Laborat?rio de Engenharia T?xtil da UFRN. Os comp?sitos foram fabricados usando o processo de molde fechado por compress?o, utilizando a resina de poli?ster ortoft?lica e 1% de per?xido MEK (per?xido de metil etil cetona) como iniciador. Em cada comp?sito foram cortadas doze amostras aleatoriamente, com as dimens?es 150x25x3 mm, para avalia??o atrav?s de ensaios mec?nicos (resist?ncia ? tra??o e ? flex?o, absor??o d agua e microscopia eletr?nica de varredura). Os ensaios de tra??o e flex?o em tr?s pontos foram realizados no Laborat?rio de Metais e Ensaios Mec?nicos - UFRN. Todas as an?lises estavam de acordo com as normas da ASTM. As amostras resultantes dos ensaios mec?nicas foram avaliadas no MEV. Com base nos resultados dos ensaios mec?nicos, observou-se que o comp?sito refor?ado com as duas fibras em conjunto (poli?ster+modal) apresentou um melhor comportamento quando foram expostos a carregamentos tanto de tra??o quanto de flex?o. No ensaio de absor??o d agua foi poss?vel observar um equilibribio na absor??o de umidade do comp?sito com modal e poli?ster, devido a uni?o das duas fibras. Nas imagens do MEV foi poss?vel ver as regi?es de ruptura do comp?sito e a ades?o entre a fibra e a matriz