21 |
Mode I Interlaminar Fracture Properties of Oxide and Non-Oxide Ceramic Matrix CompositesMansour, Rabih January 2017 (has links)
No description available.
|
22 |
Fracture properties of balsa wood and balsa core sandwich compositesShir Mohammadi, Meisam 14 June 2012 (has links)
Favorable properties of Balsa wood make it an interesting alternative in a number of
applications including thermal insulation or as a lightweight core material in
sandwich composites. Increasing use in construction necessitates a better
understanding of its mechanical and failure properties. In the present work, mode I
and mode II fracture toughness for different types of balsa wood and a sandwich
structure (balsa as core and fiber glass as skin layer) are studied experimentally by
using load-displacement diagrams and visually acquired crack growth data. / Graduation date: 2013
|
23 |
Caracterizacao microestrutural do aco maraging de grau 400 de resistencia mecanica ultra-elevadaPADIAL, ARMANDO G.F. 09 October 2014 (has links)
Made available in DSpace on 2014-10-09T12:46:42Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T13:56:09Z (GMT). No. of bitstreams: 1
07613.pdf: 5555459 bytes, checksum: 0047c9f052248797761d648268e841ba (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP
|
24 |
Desenvolvimento, processamento e caracterizacao de compositos ceramicos Sisub(3)Nsub(4)-SiCsub(w)BALDACIM, SANDRO A. 09 October 2014 (has links)
Made available in DSpace on 2014-10-09T12:45:01Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:03:20Z (GMT). No. of bitstreams: 1
07007.pdf: 10191940 bytes, checksum: 90f949a8767cea7a6c8e8cc3d2aee4ee (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP
|
25 |
Procedimento analitico para previsao do comportamento estrutural de componentes truncadosCRUZ, JULIO R.B. 09 October 2014 (has links)
Made available in DSpace on 2014-10-09T12:42:51Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:07:05Z (GMT). No. of bitstreams: 1
06110.pdf: 5239500 bytes, checksum: 175d6a6c784cd8fbadb485e4c6d90285 (MD5) / Tese(Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP
|
26 |
Caracterizacao microestrutural do aco maraging de grau 400 de resistencia mecanica ultra-elevadaPADIAL, ARMANDO G.F. 09 October 2014 (has links)
Made available in DSpace on 2014-10-09T12:46:42Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T13:56:09Z (GMT). No. of bitstreams: 1
07613.pdf: 5555459 bytes, checksum: 0047c9f052248797761d648268e841ba (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP
|
27 |
Desenvolvimento, processamento e caracterizacao de compositos ceramicos Sisub(3)Nsub(4)-SiCsub(w)BALDACIM, SANDRO A. 09 October 2014 (has links)
Made available in DSpace on 2014-10-09T12:45:01Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:03:20Z (GMT). No. of bitstreams: 1
07007.pdf: 10191940 bytes, checksum: 90f949a8767cea7a6c8e8cc3d2aee4ee (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP
|
28 |
Procedimento analitico para previsao do comportamento estrutural de componentes truncadosCRUZ, JULIO R.B. 09 October 2014 (has links)
Made available in DSpace on 2014-10-09T12:42:51Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:07:05Z (GMT). No. of bitstreams: 1
06110.pdf: 5239500 bytes, checksum: 175d6a6c784cd8fbadb485e4c6d90285 (MD5) / Tese(Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP
|
29 |
Soldagem de chapas grossas em aço baixa liga temperado e revenido ASTM A514 com aço carbono ASTM A36 pelo processo arame tubular / Welding of ASTM A514 quenched and tempered low alloy steel thick plates with ASTM A36 carbon steel by FCAW processFERRARI, MARCELLO 09 October 2017 (has links)
Submitted by Pedro Silva Filho (pfsilva@ipen.br) on 2017-10-09T18:35:29Z
No. of bitstreams: 0 / Made available in DSpace on 2017-10-09T18:35:29Z (GMT). No. of bitstreams: 0 / Neste trabalho foram determinadas as condições para a soldagem de chapas grossas de aço carbono ASTM A36 com aço baixo-liga temperado e revenido ASTM A514 Grau Q empregando-se o processo arame tubular. Para tanto foram soldadas diversas peças de testes com o intuito de se avaliar as condições mais adequadas de preparação e soldagem de juntas dissimilares destes materiais. A preparação foi realizada por meio de corte térmico. A temperatura de preaquecimento foi determinada através de modelos matemáticos, pelas recomendações das normas AWS D1.1 e DIN EN 1011-2 sendo posteriormente avaliada por intermédio do teste de soldabilidade tipo CTS Controlled Thermal Severity. Os parâmetros de soldagem foram determinados a partir da qualificação de um procedimento de soldagem, conforme a norma AWS D1.1. Foram avaliadas as consequências do emprego do tratamento térmico de alívio de tensões após soldagem (TTAT), pelos testes de dureza Vickers e impacto Charpy. A caracterização microestrutural foi realizada por meio de microscopia óptica e microscopia eletrônica de varredura. A caracterização das superfícies oxicortadas evidenciou os efeitos da descarbonetação e também da carbonetação. A temperatura de pré-aquecimento de 160°C determinada por meio da metodologia recomendada pelas normas AWS D1.1 e DIN EN 1011-2 mostrou-se satisfatória nos testes de soldabilidade. Foi possível a qualificação do procedimento de soldagem (EPS) com requisitos de impacto na condição "como soldado", porém na condição "após TTAT", os baixos valores de tenacidade obtidos no metal de solda, inferiores a 27J, não permitiram a qualificação de uma EPS com requisitos de impacto. Foi observada a ausência de trincas intergranulares tanto na zona afetada pelo calor quanto no metal de base ASTM A514, porém foi revelada a presença de microfases frágeis no metal de solda na condição "como soldado", especificamente na região da raiz, intensificadas pelo efeito da diluição. O aumento do teor de carbono na raiz, a presença de microfases frágeis, a grande fração de grãos colunares e de ferrita proeutetóide combinados com a baixa fração de ferrita acicular no metal de solda contribuíram para os baixos valores de tenacidade encontrados na condição "como soldado". Após o TTAT observou-se uma queda acentuada da tenacidade, inferior a 27J, do metal de solda devido à fragilização provocada pela precipitação e coalescimento de carbonetos de ferro. / Dissertação (Mestrado em Tecnologia Nuclear) / IPEN/D / Instituto de Pesquisas Energéticas e Nucleares - IPEN-CNEN/SP
|
30 |
Estudo do compósito 3Y-TZP/Sisub(2)Nsub(2)O obtido por sinterização sem pressãoSANTOS, CARLOS A.X. 09 October 2014 (has links)
Made available in DSpace on 2014-10-09T12:51:50Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:08:58Z (GMT). No. of bitstreams: 0 / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP
|