Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This research aimed at investigating the influence of the positioning of Eucalyptus saligna and Pinus taeda wood veneers on the layers composing the Laminated Veneer Lumber (LVL) structural panels. The panels were manufactured in six different combinations of five veneers of 3,2 mm, glued with phenol-formaldehyde, resulting in treatments constituted of wood of the same species or with a composition of the two wood types. The evaluation of the proposed combinations was performed under the characterization of physical properties (moisture content, density, water absortion, thickness swelling and volumetric expansion) and mechanical properties verified in flatwise and edgewise static bending (modulus of elasticity, stress at the proportional limit and modulus of rupture). The quality of the adhesive wood bonding was evaluated through the glue line shear strength by compression loading and the percentage of wood failure. Wood bonding tests were done with wood of the same species and wood of two studied types. The results obtained indicated that, in most situations, the different positionings of the veneers with larger density (in the outer, intermediate and inner layers) influenced the mechanical properties of the panels. The influence detected was varied, especially for MOE and MOR when comparing the flatwise and edgewise experimented positions. In certain positions, in the layers of the LVL compositions, the presence of eucalypt veneers resulted in stiffness and strength increases. In dry shear the resistances of the joints were shown to be equivalent; after boiling, the joints in eucalypt veneers presented larger strength. The percentage of wood failure was above 80% (in eucalypt veneers) and above 90% (in pine and mixed veneers) and maintained stable after boiling, indicating good gluing quality for all the tested wood bondings. However, it was verified that the adhesive wood bonding of eucalypt and pine was shown more reliable than the bonding between eucalypt veneers. Therefore, the treatments formed by interposed veneers of eucalypt and pine presented a better combination of performance and reliability for the properties of stiffness, strength and adherence. / Investigou-se a influência do posicionamento de lâminas de madeira de Eucalyptus saligna e Pinus taeda nas camadas componentes de painéis estruturais Laminated Veneer Lumber (LVL). Os painéis foram manufaturados em seis diferentes combinações de cinco lâminas de 3,2 mm de espessura, coladas com adesivo fenolformaldeído, resultando em tratamentos constituídos de madeira de uma mesma espécie e outros com mistura de madeira das duas espécies. A avaliação das combinações propostas foi realizada mediante a caracterização de propriedades físicas (teor de umidade, massa específica, absorção de água, inchamento em espessura e expansão volumétrica) e propriedades mecânicas, verificadas em ensaios de flexão estática flatwise e edgewise (módulo de elasticidade, tensão no limite proporcional e módulo de ruptura). A qualidade da colagem foi avaliada por meio da resistência ao cisalhamento na linha de cola por ensaio de compressão e do percentual de falha na madeira. Foram testadas colagens de madeira de mesma espécie e entre madeiras das duas espécies estudadas. Os resultados obtidos indicaram que, na maior parte das vezes, os diferentes posicionamentos das lâminas de maior massa específica (nas camadas externas, intermediárias e de miolo) influíram nas propriedades mecânicas dos painéis. A influência constatada mostrouse variada, em especial para MOE e MOR, quando comparados os valores para as posições de ensaio flatwise e edgewise. Em determinadas posições, nas camadas das composições LVL, a presença de lâminas de eucalipto resultou em aumentos de rigidez e resistência. Em cisalhamento a seco, as resistências das juntas se mostraram equivalentes; entretanto, após fervura, as juntas entre lâminas de eucalipto apresentaram maior resistência. Os percentuais de falha na madeira foram superiores a 80% (entre lâminas de eucalipto) e a 90% (entre lâminas de pinus e em juntas mistas) e se mantiveram estáveis após a fervura, indicando boa qualidade de adesão para todas as colagens testadas. Entretanto, a colagem entre eucalipto e pinus mostrou-se mais confiável que a colagem entre lâminas de eucalipto. Contudo, os tratamentos formados por lâminas intercaladas de eucalipto e pinus apresentaram uma melhor combinação de performance e confiabilidade para as propriedades de rigidez, resistência e aderência.

Made available in DSpace on 2016-12-12T20:12:30Z (GMT). No. of bitstreams: 1 PGEF14MA026.pdf: 1971973 bytes, checksum: e7806baddd2385da2fbe8f6b2b96ca89 (MD5) Previous issue date: 2014-05-30 / The present study aimed to evaluate technically the feasibility of production of oriented strand board (OSB) of Eucalyptus benthamii Maiden et Cambage 13 years of age through different levels of resin and compositions of particles between the layers of the mattress. Therefore, the characterization of density and dimensional stability of solid wood by NBR 7190 (1997) was performed. The experimental design for the study on the OSB consisted of 8 treatments with four different compositions between the layers (30:40:30 , 20:60:20 , 25:50:20 and 100%) and two percentages resin (4 and 6%). Three panels were produced by treatment with dimensions of 49 x 42 x 1.5 cm, which were subjected to a cycle of hot pressing temperature 180 °C, pressure of 40 kgf/cm2 for a time of 8 minutes. The technological tests on panels were made according to the procedures of ASTM D1037 (1996) and DIN 52362 (1982). The statistical analysis used was a Factorial Analysis and Tukey Test at 95% probability, as well as the comparison with the minimum values specified in the standard CSA 0437 (1993). The results for the physical properties of solid wood, it has been density of 0.53 g/cm3 with mean value and the realization of high dimensional stability of the parts analyzed. Regarding physical properties of the panels, it was found that the average density was 0.63 g/cm3 and swells for 2 hours and 24 hours were 12,35 % and 34,43 %, respectively , which overcomes the maximum setting of 10 % to 24 hours of immersion in the standard CSA 0437 (1993). For mechanical testing bending strength uniformity were observed values of rupture and elastic modulus in the direction parallel module, however, in perpendicular direction, an increase of the values of strength and stiffness as it increased the amount of particles in the inner layer of the mattress. For internal bond, there was a strong influence of the increase in the percentage of resin, with an average value of 0.36 MPa, thus, only treatments with 6% resin reached the minimum values established by the referenced standard. The results of this study indicate that Eucalyptus benthamii can be an alternative for the production of oriented strand board (OSB), through adjustments to be made in the production process / O presente estudo teve por objetivo avaliar tecnicamente a viabilidade da produção de painéis OSB a partir de toras de Eucalyptus benthamii com 13 anos de idade por meio de diferentes teores de resina e composições de partículas entre as camadas do colchão. Para tanto, foi realizada a caracterização da massa específica e da estabilidade dimensional da madeira sólida por meio da NBR 7190(1997). O delineamento experimental para o estudo relativo aos painéis OSB foi composto por 8 tratamentos, com 4 diferentes composições entre as camadas (30:40:30, 20:60:20, 25:50:20 e 100%) e duas porcentagens de resina (4 e 6%). Foram produzidos 3 painéis por tratamento com dimensões de 49 X 42 X 1,5 cm, os quais foram submetidos a um ciclo de prensagem à quente de 180oC de temperatura, 40 kgf/cm2 de pressão por um tempo de 8 minutos. Os ensaios tecnológicos dos painéis foram feitos de acordo com os procedimentos da ASTM D1037 (1996) e da DIN 52362 (1982). A análise estatística adotada foi a Análise Fatorial e Teste de Tukey a 95% de probabilidade, bem como a comparação com os valores mínimos especificados na norma CSA 0437 (1993). Como resultado para as propriedades físicas da madeira sólida, tem-se a massa específica aparente básica com 0,53 g/cm3 de valor médio e a constatação da alta instabilidade dimensional das peças analisadas. Quanto às propriedades físicas dos painéis, constatou-se que a massa específica média foi de 0,63 g/cm3 e os inchamentos para 2 horas e 24 horas foram de 12,35% e 34,43%, respectivamente, o que supera o parâmetro máximo de 10% para 24 horas de imersão pela norma CSA 0437 (1993). Para os ensaios mecânicos de flexão estática, observou-se uma homogeneidade dos valores de módulo de ruptura e de módulo de elasticidade no sentido paralelo, no entanto, no sentido perpendicular, houve um aumento nos valores de resistência e rigidez à medida que se aumentava a quantidade de partículas na camada interna do colchão. Para ligação interna, verificou-se uma forte influência do aumento da porcentagem de resina nos resultados apresentados, com valor médio de 0,36 MPa, assim, somente os tratamentos com 6% de resina atingiram os valores mínimos estabelecidos pela norma referenciada. Os resultados deste estudo indicam que a madeira de Eucalyptus benthamii pode ser uma alternativa para a produção de painéis de partículas orientadas (OSB), mediante ajustes a serem realizados no processo produtivo