Made available in DSpace on 2016-06-02T19:12:38Z (GMT). No. of bitstreams: 1 6196.pdf: 3158389 bytes, checksum: ecb1f1518baa3ec332ed2c07679038a2 (MD5) Previous issue date: 2014-07-25 / The application of polymeric fibers as reinforcement in cement based composites is a highly developed technology in various applications in construction. The use of polypropylene fibers have been widely used, but with some technological limitations, mainly because of them present low interaction with the cement matrix when compared with other polymeric fibers. For this work, we sought to evaluate polypropylene fibers doped with surface modifiers, with emphasis on mechanical and microstructural characteristics of composites. Different amounts of fiber with and without surface modifying additives in matrices of Portland cement mortar after 35 days of age were evaluated. The physic-chemical interactions of the fiber with the matrix were evaluated by pullout tests and through reviews of scanning electron microscopy. Some specimens were subjected to accelerated aging tests and these samples were analyzed by electron microscopy to observe the behavior of the interaction of the fiber with the additive, but also for assessing the behavior of the fiber with the matrix after exposure to aging. The results obtained by the mechanical resistance measures uniaxial compression and scanning electron microscopy showed that a mechanical reinforcement occurs independent of incorporation of additives in fiber to additions of 1.2 kg/m3. On the other hand, the surface-treated fiber exhibited higher degree of adhesion to the matrix. / A aplicação de fibras poliméricas como reforço em compósitos de matriz cimentícia é uma tecnologia bastante desenvolvida em diversas aplicações em construção civil. A utilização de fibras de polipropileno tem sido bastante utilizada, porém com algumas limitações tecnológicas, principalmente pelo fato delas apresentarem baixa interação com a matriz cimentícia, quando comparadas com outras fibras poliméricas. Para este trabalho, buscou-se a avaliação de fibras de polipropileno aditivadas com modificadores de superfície, com ênfase nas características mecânicas e microestruturais dos compósitos. Foram avaliados diferentes teores de fibras sem e com aditivos modificadores de superfície em matrizes de cimento Portland e argamassas após 35 dias de idade. As interações físico-químicas da fibra com a matriz foram avaliadas através de ensaios de pullout e através de avaliações de microscopia eletrônica de varredura. Alguns corpos de prova foram submetidos a ensaios de envelhecimento acelerado e estas amostras foram analisadas por microscópio eletrônico para observação do comportamento da interação da fibra com o aditivo, como também para a avaliação do comportamento da fibra com a matriz após a exposição ao envelhecimento. Os resultados obtidos por medidas de resistência mecânica à compressão uniaxial e microscopia eletrônica de varredura mostraram que ocorre um reforço mecânico independente da incorporação de aditivos na fibra até adições de 1,2 kg/m3. Por outro lado, as fibras tratadas superficialmente apresentaram maior grau de aderência com a matriz.

Orientador: Antonio Felipe P. F. Wouk / Dissertação (mestrado) - Universidade Federal do Parana, Setor de Ciencias Agrarias, Curso de Pós-Graduação em Ciencia Veterinarias. Defesa: Curitiba, 14/05/1991 / Resumo: Foi realizado um experimento para demonstrar a utilidade da fibra de carbono no processo cicatricial do tendão calcâneo comum de cão. Foram utilizados doze câes sem raça definida clinicamente sadios e quatro destes foram utilizados como controle. Filamentos de fibra de carbono foram utilizados como prótese cirúrgica após tenotomia e tenorrafia do tendão calcâneo comum direito do cão. Foram também realizados tenotomia e tenorrafia nos grupos controle, os quais não sofreram implante. A tenorrafia foi realizada com fio de sutura de ácido poliglicólico. Foram constituido quatro grupos experimentais de três cães. O primeiro grupo foi sacrificado aos trinta dias, o segundo aos sessenta dias, o terceiro aos noventa dias e o quarto aos cento e vinte dias após o ato cirúrgico e a correspondente implantação com fibra de carbono. Os tendões foram analisados clinica e his tologicamente. Os cães implantados demonstraram sinais de deambulação nor mal mais precocemente, apresentando os tendões mais espessados em relação aos animais controle. Foram encontradas microparticulas de fibra de carbo no no linfonodo popliteo já aos trinta dias após o implante. Devido uma intensa proliferação tissular encontrada em torno dos filamentos e da fibra de carbono, admite-se que o material implantado atuou como um promotor de cr~scimehto para o·tecido neo-formado. Desta forma o novotecido obedece as linhas biomecânicas do-tendão. Uma pesquisa com duração de um periodo de tempo mais longo está realizada no Serviço de Cirurgia Veterinária da Universidade Federal do. Paraná para observações mais detalhadas' da mígração das microparticulas de fibra de carbono via linfática. / Abstract: An experiment was carried out in order to demonstrate the usefulness of carbon fiber in the process of healing of the dogs calcaneal tendon. Twelve healthy mongrel dogs and four of them were used as control. Carbon fiber filaments were experimentally inserted by means of a surgical prothesis after a tenontoplasty of the right common calcaneal tendon has been performed. Tenotomy and tenontoplasty were also carried out in the control group, wich, in the other hand, was not implanted with carbon fiber. After the tenotomy, tenontoplasty was performed using poliglycolic acid suture. Four experimental, groups of three dogs each were used. The first group was killed at 30 days; the second group at 60 days, the third at 90 days and the fourth, at 120 days after surgery and the corresponding implantation of the carbon fiber. A clinical survey of the tendons has been carried out wich was followed by histological analysis. The implanted dogs showed earlier signs of normal walking when compared to the behaviour of the control animals. Furthermore macroscopically thicker tendons were observed as compared with the control animals. Microparticles of carbon fiber.were already found in the popliteous limph nodes after 30 days of implantation. Due to the high tissue proliferation around the carbon fiber filaments,', it has been admited thaltv the implanted material acts as a scaffold to the newly formed tissue. In regard to this feature, the new tissue follows the biomechanical lines of the tendon. A further study is being on the way in the Veterinary Surgical Service of Federal University of Parana with the goal to obtain more details about carbon fiber micropar tides limphatic migration in the implanted animals.

O entendimento das características de compósitos com fibras naturais pode promover o seu uso a ponto de sugerir sua aplicação no lugar de compósitos reforçados com fibras sintéticas. Este trabalho busca embasar essa alternativa através da comparação do comportamento mecânico de compósitos unidirecionais de matriz poliéster isoftálica reforçada com fibras de curauá e reforçada com fibras de vidro. Os compósitos foram produzidos na forma de lâminas finas com teor de fibra de 20% onde se variou o ângulo do reforço (0º, 15º, 30º, 45º, 60º, 75º e 90º) com o objetivo de estudar o efeito de orientação da fibra nas suas propriedades. Foram moldados compósitos variando-se o teor volumétrico de fibras (10 %, 20 %, 30 %, 40 % e 50 %) a fim de avaliar a quantidade ótima de reforço em cada lâmina; a eficiência de um tratamento alcalino (5 % em peso de NaOH) na superfície das fibras de curauá também foi avaliada afim de se observar o ganho em resistência mecânica dos compósitos. Todos os compósitos unidirecionais foram caracterizados por meio de ensaios de tração, flexão e cisalhamento short-beam. As propriedades das lâminas reforçadas com fibra de curauá ou com fibra de vidro também foram estudadas utilizando-se as teorias da micromecânica disponíveis em softwares comerciais. As fibras de curauá tratadas com a solução alcalina produziram compósitos com maior resistência à tração quando comparados aos compósitos de curauá sem o tratamento devido a melhor interação com a matriz. A variação do ângulo de reforço mostrou o quão dependente são a resistência e o módulo dos compósitos reforçados com fibra de curauá ou vidro em relação à orientação das fibras. O efeito da orientação da fibra foi mais pronunciado em compósitos reforçados com fibra de vidro. Por último, embora os compósitos reforçados com fibra de vidro sejam mais resistentes que aqueles com fibra de curauá, os resultados para ângulos maiores que 45° foram considerados similares, equiparando as duas fibras nessas condições. / The understanding of natural fibers composites can promote its use. This work aims in compare the behavior of unidirectional polyester matrix composites reinforced with curaua fibers and reinforced with glass fiber. The composites were produced in the shape of a thin sheet where was varied the reinforcement angle (0°, 15°, 30°, 45°, 60°, 75° and 90°) with the objective of studying the fiber orientation effect on composite properties. For this study was also mold composites varying the fiber volume fraction (10 %, 20 %, 30 %, 40 % and 50 %) in order to evaluate the best amout of reinforcement in each composite sheet and the efficiency of an alkaline treatment (5 % NaOH) at the curaua fiber surface. All the unidirectional composites were characterized using tensile, flexural and short-beam tests according to ASTM standards. The composites reinforced sheet properties with either glass or curaua fibers were also studied using theoretical micromechanical approach available in commercial software. Curaua fibers treated with alkaline solution produced higher tensile strength results compared with untreated fibers. As expected, the increase in reinforcement angle significantly decreased strength and modulus of curaua reinforcement composites as in glass reinforcement composites. The effect of fiber orientation was more relevant in the glass fiber composites. At last, although the glass fiber composites indicate higher strenght than curaua fiber composites, the results for higher angles (> 45°) were considered similar for both fibers in this conditions.

Tese (doutorado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Civil e Ambiental, 2014. / Submitted by Laura Conceição (laurinha.to@gmail.com) on 2014-11-20T17:45:39Z No. of bitstreams: 1 2014_JulianoRodriguesdaSilva.pdf: 17019257 bytes, checksum: fa5c90bc697415ed248a800d49563bd2 (MD5) / Approved for entry into archive by Patrícia Nunes da Silva(patricia@bce.unb.br) on 2014-11-26T13:20:47Z (GMT) No. of bitstreams: 1 2014_JulianoRodriguesdaSilva.pdf: 17019257 bytes, checksum: fa5c90bc697415ed248a800d49563bd2 (MD5) / Made available in DSpace on 2014-11-26T13:20:47Z (GMT). No. of bitstreams: 1 2014_JulianoRodriguesdaSilva.pdf: 17019257 bytes, checksum: fa5c90bc697415ed248a800d49563bd2 (MD5) / Esta tese descreve uma pesquisa experimental sobre reforço à flexão de vigas de concreto armado com seção transversal “T” com a colagem de materiais compósitos de fibras de carbono (PRFC) e de vidro (PRFV) na superfície do concreto. Foram ensaiadas 14 vigas “T” simplesmente apoiadas, divididas em três grupos. Essas vigas, com um vão livre de 4,00 m e com taxa de armadura de 0,63%, foram submetidas a duas cargas concentradas aplicadas a 1,50 m dos apoios. As vigas foram dimensionadas para trabalhar entre os domínios dois e três (subarmadas). Duas vigas sem reforço foram ensaiadas como referência e doze vigas foram reforçadas, sendo o grupo A com duas camadas de PRF, o grupo B com três camadas e o grupo C com duas camadas e com pré-carregamento. A análise do comportamento das vigas foi realizada com os resultados das cargas e modos de ruptura, deformação específica das armaduras de flexão e de cisalhamento, deformação específica do concreto, deformação específica do reforço, deslocamento vertical das vigas e o desenvolvimento das fissuras. Os resultados experimentais foram comparados entre si e com as estimativas prescritas pelas normas técnicas Boletim 14 fib (2001), ACI 440.2R (2008) e ABNT NBR 6118 (2014) com adaptações para o cálculo da carga última das vigas com reforço híbrido. O reforço executado com a técnica de Colagem na Superfície do Concreto (CSC) mostrou-se eficiente. Em todos os grupos pesquisados as vigas com reforço híbrido tiveram desempenho superior ao das vigas com reforço simples. O incremento da carga última das vigas com reforço híbridas em relação à viga de referência variou entre 20,3 % e 21,5 %. A viga que apresentou o melhor resultado foi a reforçada com a primeira camada de PRFV e depois com uma camada de PRFC. Os modos de ruptura apresentados nas vigas reforçadas foram descolamento do PRF (primeira camada de PRFC) e destacamento do cobrimento (primeira camada de PRFV). Estes resultados mostram a influência da sequência de colagem do PRF no comportamento das vigas. Além disso, esta tese apresenta uma adaptação do método de cálculo de vigas com reforço híbrido à flexão colado na superfície do concreto. ______________________________________________________________________________ ABSTRACT / This thesis describes an experimental research on reinforced concrete "T" beams strengthened with carbon fiber (CFRP) and glass fiber (GFRP) composites bonded to the concrete surface. 14 "T" beams were simply supported and divided into three groups in order to be tested. These beams with a span of 4.00 m and reinforcement ratio of 0.63 % were subjected to two concentrated loads, applied 1.50 m from the support. The beams were designed to work between domains two and three (under-reinforced). Two beams without FRP reinforcement were tested as reference and twelve beams were strengthened: group A with two layers of FRP, group B with three layers and group C with two layers and with preloading. The analysis was performed with the results of loads and failure modes, flexural and shear reinforcement strain, concrete strain, FRP strain, vertical displacement and cracking development. The experimental results were compared to each other and to the estimates described in Bulletin 14 fib (2001), ACI 440.2R (2008) and ABNT NBR 6118 (2014) with adaptations for calculating the ultimate load of beams with hybrid strengthening. The use of hybrid strengthening with Externally Bonded Reinforcement (EBR) showed efficiency. In all surveyed groups the beams with hybrid strengthening exhibited superior performance in relation to the beams with single strengthening. The increase of the ultimate load of the hybrid beams relative to the reference beam varied between 20.3% and 21.5 %. The beam with the best result was the one reinforced first with a layer of GFRP and then with a layer of CFRP. The failure modes of the strengthened beams presented were detachment of PRF (first layer of CFRP) and delamination (first layer of GFRP). These results show the influence of the sequence of bonding the FRP in the behavior of the beams. Moreover, this thesis also presents an adaptation for the analysis of beams with hybrid strengthening externally bonded to the concrete surface.

Esse trabalho aborda a questão de materiais compósitos reforçados com fibras (fiber reinforced concrete) com enfoque em matrizes cimentícias reforçadas com fibra de aramida Kevlar. O objetivo é caracterizar o potencial da fibra de aramida Kevlar como elemento de reforço a ser adicionado ao concreto. O trabalho busca caracterizar o desempenho dos compósitos formados, identificando as alterações decorrentes da incorporação em função do comportamento mecânico e da resistência ao impacto. Os objetivos são verificar a potencialidade de utilização dessa fibra em termos de trabalhabilidade e resistência mecânica; definir como deve ser a forma de incorporação, verificar a aderência da fibra à matriz através de microscopia eletrônica de varredura por elétrons secundários e determinar a resistência ao impacto, comparando matrizes sem adição de fibra com corpos-de-prova moldados com vários tipos e teores de fibra (aço, sisal, vidro, polipropileno e aramida). Como vantagens da incorporação das fibras de aramida Kevlar, constata-se um incremento na resistência à compressão dos compósitos aos 28 dias em relação aos espécimes sem adição de fibra. Observam-se, também, reduções na massa específica e na trabalhabilidade dos espécimes com adição de fibra de aramida Kevlar em comparação aos sem adição. Em relação à resistência ao impacto, conclui-se que os compósitos com adição de fibra de aço e fibra de aramida são os que apresentaram melhor comportamento dinâmico em relação a energia de ruptura acumulada e à energia para aparecimento da primeira fissura, respectivamente.

Neste trabalho foi estudado o crescimento de fibras monocristalinas de LiYF4 (YLF) dopadas com Er3+ ou Nd3+ pelo método de micro-pulling-down (-PD) no modo resistivo. Para otimização do processo de crescimento foi, desenvolvida nova metodologia de confecção de cadinhos, de forma a torná-los mais rígidos permitindo sua utilização em mais de uma experiência, aumentando a reprodutibilidade do processo. A câmara de crescimento também foi modificada para obtenção de vácuo da ordem de 10-7 torr. Devido ao tratamento térmico do sistema sob alto vácuo, antes da fusão do material, não foram observados transientes iniciais no processo de puxamento das fibras de YLF dopadas. Foram crescidas fibras de YLF:Nd com concentrações de 0,5, 1 e 1,5 mol% e fibras de YLF:Er com 1, 10, 20 mol %, com diâmetros da ordem de 0,7 mm e comprimentos de até 120mm. Devido a problemas mecânicos do sistema, o ancoramento das fibras, ou seja, o equilíbrio na interface sólidoliquido, mostrou-se muito difícil, sendo necessárias várias correções nos parâmetros de crescimento para estabilização da interface sólido-líquido resultando na formação de defeitos, principalmente na superfície, em regiões ao longo das fibras. Nas condições do presente estudo, o uso de uma atmosfera estática mostrou-se desfavorável. Testes de ganho efetuados com a fibra de YLF:Nd dopada com 1,5mol%, mostraram um ganho superior às perdas comprovando seu potencial para ação laser. / In the present work, we studied the growth of single crystal fibers of LiYF4 (YLF) doped with Er3+ or Nd3+ by the resistive micro-pulling-down (-PD) tecnhique. A new method for crucible preparation was developed to improve the growth process. The use of better-built crucibles allows their use in more than one experiment, increasing the process reproducibility. The growth chamber was also modified to achieve vacuum of approximately 10-7 torr. The previous thermal treatment under high vacuum before charge melting eliminate the initial transient reported in previous works of YLF doped fibers growth. Single crystal fibers of YLF:Nd (0.5, 1 e 1.5 mol%) and YLF:Er (1, 10 and 20 mol %), with 0.7 mm diameters and up to 120mm of length were grown. Mechanical problems in the micro-PD system equipment made difficult the control of the solid-liquid interface, and several corrections on the experimental parameters were necessary during the growth process, resulting in defects formation, mainly on the fibers surface. In the experimental conditions of this work, the use of a static atmosphere showed not appropriate for elimination of spurious contamination from ambient atmosphere. The Nd:YLF (1.5mol%) fiber demonstrated a gain higher that the losses, demonstrating the viability for laser action.

En la presente tesis se hacen referencias de los materiales empleados, sus características y otros, cabe indicar, a su vez, los resultados de los ensayos para determinar el diseño de mezcla, así como, la de las variables evaluadas como f’c en un periodo de 7, 14, 21 y 28 días y el módulo de rotura en las vigas ensayadas. Se hace un enfoque especial al comportamiento del concreto reforzado con fibra viendo como influye su presencia en el concreto, aumentando o mejorando su capacidad para controlar las fisuras y otras variables que se pudieran presentar ante factores extremos. Finalmente realizamos ensayos de concreto con fibra en diferentes periodos de tiempo comparado con concreto normal, obteniendo así las conclusiones y recomendaciones que se detallan al final de la tesis en mención, mediante los resultados de las variables evaluadas y un análisis económico.

Tesis para optar al grado de Magíster en Administración / Autor no envía autorización del documento (Parte I) Autor no autoriza el acceso a texto completo de su documento (Parte II) / [Erazo R., José Alejandro Parte I]: Estratégico y de mercado -- [Bernaschina C., Tomás Parte II]: Organizativo - Financiero. / Hoy en día existen diversos servicios que requieren de conexiones de internet de alta velocidad, como video por internet de Netflix o juegos en línea de consolas como Play Station y Xbox. La oferta de internet actual no permite disfrutar al 100% estos servicios, ya que la velocidad ofertada por las empresas actuales no es asegurada en los momentos de mayor tráfico y el ancho de banda es compartido incluso hasta por 63 clientes. Considerando, adicionalmente, que en un futuro próximo, todo tipo de comunicaciones en el hogar se basará en la conectividad en internet y debido al crecimiento de las soluciones en la nube y la tendencia a la automatización de todos los procesos mediante softwares especializados, es cada vez más importante disponer de conexiones fiables y de gran velocidad tanto en los hogares como en las empresas. El objetivo es ofrecer un servicio de internet totalmente diferenciado, enfocándose en dos pilares:  Internet de alta velocidad, por medio de una conexión de fibra óptica.  Con servidores de contenidos próximos a Chile que permiten disfrutar de una mejor experiencia de navegación, tanto para usuarios particulares como para empresas. La propuesta de valor estará enfocada en 2 tipos de clientes, con estrategias diferenciadas para cada uno:  Comunidades existentes: edificios, condominios u otros, donde la diferenciación, además de la velocidad, será por los contenidos próximos a Chile.  Empresas e Institucionales: La oferta es simple, conexión de alta velocidad y disponibilidad de contenido a un buen precio. Adicionalmente, contenido próximo de aplicaciones en la nube, HTTPS y actualización de software en general. El modelo de negocios se basa en tercerizar todos los servicios de la operación:  Instalación de la red  Mantención  Posventa La venta, desarrollo e implementación del producto y la coordinación de los servicios externalizados, serán las funciones propias de la empresa.

Neste trabalho foram estudadas a propagação de ondas ópticas e acústicas em fibras ópticas e a interação acusto-óptica em fibras ópticas, com o objetivo de se implementar um deslocador de freqüências ópticas via efeito acusto-óptico em fibras bimodais. No estudo da propagação de ondas ópticas e acústicas em fibras, ênfase especial foi dada aos dois primeiros modos ópticos de propagação na fibra (LP01 e LP11) e ao modo acústico flexural de ordem mais baixa (sem freqüência de corte), onde procurou-se introduzir uma padronização de nomenclatura, visando a utilização das definições e expressões envolvidas, em ambas as áreas, no estudo da interação acusto-óptica em fibras. A seguir foram mostrados o princípio de operação e o projeto do deslocador de freqüências em fibra óptica bimodal. Finalizando o trabalho, foram implementados e caracterizados dois protótipos do deslocador de freqüências estudado.

Esta dissertação apresenta o desenvolvimento inicial de um acelerômetro angular de um eixo utilizando-se grades de Bragg em fibras ópticas como elementos sensores. Para tanto, são apresentados os seguintes tópicos: conceitos de um sistema de navegação a partir da análise de uma Unidade de Medidas Inerciais (UMI) comercial; teoria de grades de Bragg a fibra óptica, incluindo-se a análise de alteração de suas propriedades quando submetida à tração; detalhamento da topologia do acelerômetro proposto, incluindo-se o dimensionamento da massa inercial e da estrutura mecânica; projetos da fonte de luz, do sistema interrogador e da eletrônica de apoio, bem como a integração dos sistemas; ensaios realizados, incluindo ensaio estático sem excitação, ensaio de oscilação senoidal, ensaio com velocidade angular constante, ensaio com variações da posição angular intercaladas por repouso, e ensaio de inclinação; análise dos resultados e propostas de trabalhos futuros. O desenvolvimento do acelerômetro angular aqui proposto é fundamental para que se possa obter, em um futuro próximo, acelerômetros lineares e angulares de seis graus de liberdade (medição de três acelerações lineares ortogonais e de três acelerações angulares ortogonais), idéia essa que se encontra em processo de proteção de propriedade intelectual, por meio de depósito de pedido nacional de patente sob número BR 10 2012 016704-2. Além desse depósito de pedido nacional de patente, este trabalho gerou, ainda, 1 (uma) trabalho de Iniciação Científica CNPq para a aluna Thabata Ferreira Ganga (UNIFESP), 2 (duas) publicações em congressos internacionais, 3 (três) publicações em eventos nacionais e 1 (uma) submissão de proposta de Capítulo de Livro.