Made available in DSpace on 2015-04-01T12:17:41Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 2182019 bytes, checksum: f16ae6c6befcaa27f593134ca7fa0f5d (MD5) Previous issue date: 2013-08-23 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Brazil is one of the references in the world market of ceramic tiles, ranking second in production and consumption. Only in 2012 were produced 865.9 million square feet, for a total installed capacity of 1.004 million square meters. An important aspect of the ceramic industry in the global context, is the continuous technological development, the widespread use of ceramics in various applications and environments and the increasing incorporation of waste from other sectors, giving sustainability concepts in the industry. Brazil produces on average 980 000 tonnes of glass packaging a year and has about a recycling rate of 47%. This study aimed to present one more option to the use of waste glass, which is still poorly recycled in Brazil, analyzing the influence of the replacement of feldspar in a ceramic, for residue from glass bottles are not returnable to the market. We tested three different percentages of glass waste, but also the influence on the behavior of the residue the technological properties with variation of firing temperature. Previously, all materials used in this work were characterized by the techniques of X-ray fluorescence, X-ray diffraction, thermal analysis and particle size. After established formulations, manufacturing and burning the bodies of the test piece, checked the technological properties and microstructure of established formulations. The results indicate that the glass waste has the potential to be used as a flux alternative to replace feldspar in the production of ceramic tiles for different purposes, according to NBR 13817/1997. / O Brasil é uma das referências no mercado mundial de revestimentos cerâmicos, ocupando a segunda posição em produção e consumo. Só no ano de 2012 foram produzidos 865,9 milhões de metros quadrados, para uma capacidade instalada de 1.004 milhões de metros quadrados. Um aspecto importante da indústria cerâmica, no contexto mundial, é o contínuo desenvolvimento tecnológico, a disseminação do uso de cerâmica em diferentes aplicações e ambientes e a crescente incorporação de resíduos provenientes de outros setores, dando conceitos de sustentabilidade no setor. O Brasil produz em média 980 mil toneladas de embalagens de vidro por ano e possui, aproximadamente, um índice de reciclagem de 47%. Este trabalho teve como objetivo apresentar mais uma opção para o aproveitamento do resíduo de vidro, que ainda é pouco reciclado no Brasil,analisando a influência da substituição do feldspato, em uma massa cerâmica, por resíduo de vidro proveniente de garrafas não retornáveis ao mercado. Foram testadas três diferentes percentuais de resíduo de vidro, como também a influência no comportamento do resíduo nas propriedades tecnológicas com a variação de temperatura de queima. Previamente, todos os materiais utilizados no trabalho foram caracterizados pelas técnicas de fluorescência de raios X, difração de raios X, análise térmica e granulométrica. Após estabelecidas as formulações, confecção e queima dos corpos-de-prova, foram verificadas as propriedades tecnológicas e microestruturais das formulações estabelecidas. Os resultados obtidos apontam que o resíduo de vidro apresentou potencial de ser utilizado como fundente alternativo em substituição ao feldspato, na produção de revestimentos cerâmicos para diferentes finalidades, de acordo com a norma NBR 13817/1997.

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-02-29T21:36:02Z No. of bitstreams: 1 RaimundoJorgeSantosParanhos_TESE.pdf: 4812222 bytes, checksum: a3fafdef35f0753c7d1a15d6d7faed55 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-03-01T00:42:05Z (GMT) No. of bitstreams: 1 RaimundoJorgeSantosParanhos_TESE.pdf: 4812222 bytes, checksum: a3fafdef35f0753c7d1a15d6d7faed55 (MD5) / Made available in DSpace on 2016-03-01T00:42:05Z (GMT). No. of bitstreams: 1 RaimundoJorgeSantosParanhos_TESE.pdf: 4812222 bytes, checksum: a3fafdef35f0753c7d1a15d6d7faed55 (MD5) Previous issue date: 2015-02-23 / O presente estudo tem como objetivo avaliar a potencialidade da utiliza??o das cinzas do baga?o da cana-de-a??car (CBC) como fundente, em substitui??o ao filito e/ou ao feldspato na massa padr?o para produ??o industrial de porcelanato esmaltado, verificando a possibilidade de as CBC contribu?rem para a redu??o do coeficiente de expans?o t?rmica global da massa cer?mica. Para isso, como um resultado da pesquisa, foram caracterizadas as mat?rias-primas componentes da massa padr?o (argila, filito, caulim, feldspato, quartzo e talco) e o res?duo das CBC, por meio de ensaios por FRX, DRX, AG, ATD e ATG. Foram confeccionados corpos de prova (CDP) nas dimens?es de 100 mm x 50 mm x 8 mm em matriz uniaxial, sob press?o de compacta??o de 33 MPa, reunidos em lotes de 3 unidades, posteriormente sinterizados nas temperaturas de 1150 ?C ? 1210 ?C variando a escala de avalia??o em 10 ?C, rampa de aquecimento e resfriamento de 50 ?C/min e 25 ?C/min, com tempo de patamares de 1 min, 3 min, 5 min, 8 min, 10 min, 15 min, 30 min e 60 min., analisando os resultados das propriedades f?sicas de absor??o de ?gua (AA), retra??o linear de queima (RLq), an?lise dilatom?trica (ADT), tens?o de resist?ncia ? flex?o (TRF) e MEV dos corpos sinterizados, a fim de verificar a adequa??o dos CDP ?s normas ISO 13006, ISO 10545, NBR 13816; NBR 13817 e NBR 13818. O estudo mostrou que as formula??es que mais atendem aos requisitos das normas s?o: a G4 ? na qual se aplicou 10% de CBC em substitui??o ao filito, temperatura de sinteriza??o de 1210 ?C e tempo de patamar de 10 min., e F3 ? com aplica??o de 7,5% de CBC em substitui??o ao feldspato, nas temperaturas de sinteriza??o de 1190 ?C, 1200 ?C e 1210 ?C e tempo de patamar de 10 min. Essas formula??es apresentaram melhor desempenho quanto ? forma??o de cristais de mulita, com redu??o consider?vel de trincas e poros, atendendo aos pr?- requisitos das normas para porcelanato esmaltado. A an?lise dos resultados comprova que a utiliza??o da CBC como fundente na prepara??o de massa para porcelanato atende aos par?metros normalizados para fabrica??o desse produto, e, com isso, pode-se reduzir o impacto ambiental e o custo de produ??o. Portanto, ? recomendada a utiliza??o desse res?duo na ind?stria ceramista, por conta de sua viabilidade industrial, comercial e colaborativa para a sustentabilidade. / The present study aims to evaluate the potential use of bagasse ash from sugar cane (CBC) as a flux, replacing phyllite and/or feldspar in standard industrial mass production of enameled porcelain, verifying the possibility of the CBC contribute to the overall reduction of the coefficient of thermal expansion of the ceramic mass. To this end, as a result of the research, we characterized the raw material components of the standard mass (clay, phyllite, kaolin, feldspar, quartz and talc) and the residue of BCC, by testing by XRF, XRD, AG, DTA and ATG. Specimens (CDP) were manufactured in the dimensions of 100 mm x 50 mm x 8 mm in uniaxial matrix under compaction pressure of 33 MPa, assembled in batches of 3 units subsequently sintered at temperatures of 1150?C to 1210?C by varying the Rating Scale at 10?C, heating and cooling ramp of 50?C/min and 25?C/min, with levels of 1 min, 3 min, 5 min, 8 min, 10 min, 15 min, 30 min and 60 min. analyzing the results of the physical properties of water absorption (WA), linear firing shrinkage (LFS), dilatometric analysis (DTA), flexural strain (SFT) and SEM of the sintered bodies in order to verify the adequacy of CDP to ISO 13006, ISO 10545, NBR 13816 standards; NBR 13817 and NBR 13818. The study showed that the formulations that best suit the requirements of the standards are:. G4 - which was applied in 10% of replacing the CBC phyllite, sintering temperature 1210 ? C for 10 min and porch, and F3 - with application of 7.5% of CBC to replace the feldspar in the sintering temperatures of 1190?C, 1200?C and 1210?C for 10 min and porch. These formulations showed better performance regarding the formation of primary and secondary mullite, with considerable reduction of cracks and pores, meeting the prerequisites of standards for glazed porcelain. The results shows that the use of the CBC as a flux in the preparation of porcelain mass meets standard parameters for the manufacture of the product, and thereby can reduce environmental impact and the cost of production. Therefore, it is recommended to use this residue in the ceramics industry, due to its industrial, commercial and collaborative viability for sustainability.

Made available in DSpace on 2014-12-17T14:07:17Z (GMT). No. of bitstreams: 1 EduardoJVD_TESE.pdf: 12520494 bytes, checksum: 33cb961e885b2677da82d2f828a92417 (MD5) Previous issue date: 2013-05-23 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / To produce porcelain tiles fluxing agents are used in order to obtain a liquid phase during firing. This liquid phase fills the pores decreasing porosity, water absorption and contributes to material densification. In the porcelain tiles industry, feldspar is the main flux material used, with quantities ranging between 35 and 50%. Studies focus on the discovery of materials with flux characteristics that can reduce the consumption of feldspar by porcelain tiles industry. In this context, the coffee husk ashes, a residue obtained when coffee husks are burned to produce heat for the dryers during the processing of the green fruit, have as main chemical constituents potassium, calcium and magnesium, giving them characteristics of fluxing material. Brazil is the largest coffee producer in the world and is responsible for over 30% of the world s production. In this work a physical treatment of coffee husk ash was carried out in order to eliminate the organic matter and, after this, two by-products were obtained: residual wastes R1 and R2. Both residues were added separately as single fluxes and also in association with feldspar in mixtures with raw materials collected in a porcelain industry located in Dias d ?vila-Ba. The addition of these residues aimed to contribute to the reduction of the consumption of feldspar in the production of porcelain tiles. Specimens were produced with dimensions of 60 mm x 20 mm x 6 mm in an uniaxial die with compacting pressure of 45 MPa. The samples were heated to a temperature of 1200 ?C, for 8 minutes. Tests were performed to characterize the raw materials by XRF, XRD, particle size analysis, DTA and TGA and, additionally, the results of the physical properties of water absorption, apparent porosity, linear shrinkage, density, dilatometry, flexural strength and SEM of sintered body were analyzed. Additions of less than 8% of the residue R1 contributed to the decrease of porosity, but the mechanical strength of the samples was not satisfactory. Additions of 5% the R2 residue contributed significantly to decrease the water absorption and apparent porosity, and also to increase the mechanical strength. Samples with addition of feldspar associated with the R2 residue, in proportions of 6.7% of R2 and 6.7% of feldspar, led to results of water absorption of 0.12% and mechanical strength of 46 MPa, having parameters normalized to the manufacture of porcelain stoneware tiles / Na fabrica??o de porcelanatos s?o utilizados fundentes com a finalidade de obter fase l?quida durante a queima que, por sua vez, preenche os poros diminuindo a porosidade, a absor??o de ?gua, e contribui para a densifica??o do material. Na ind?stria de porcelanatos o feldspato ? o principal material fundente utilizado, com percentuais que variam entre 35 e 50% em massa. Pesquisas s?o direcionadas para a descoberta de materiais com caracter?sticas fundentes que possam diminuir o consumo de feldspato. Nesse contexto, a cinza da casca de caf?, res?duo obtido quando cascas de caf? s?o queimadas a fim de produzir calor para os secadores mec?nicos durante o beneficiamento do fruto, possuem como principais elementos o pot?ssio, c?lcio e magn?sio, conferindo-lhe caracter?sticas de material fundente. O Brasil ? o maior produtor de caf? do mundo, respons?vel por mais de 30% da produ??o mundial. Nesse trabalho, foi realizado um tratamento f?sico na cinza de caf? com a finalidade de eliminar parte do material carbonizado e, ap?s este, foram obtidos dois subprodutos: res?duo R1 e res?duo R2. Ambos os res?duos foram adicionados, separadamente, como ?nicos fundentes, e tamb?m associados ao feldspato, em massas com mat?rias primas coletadas em uma f?brica de porcelanatos localizada no munic?pio de Dias d ?vila-Ba. A adi??o desses res?duos teve o objetivo de verificar a possibilidade de reduzir o consumo de feldspato na produ??o de porcelanatos. Foram confeccionados corpos de prova com dimens?es de 60 mm x 20 mm x 6 mm em matriz uniaxial, com press?o de compacta??o de 45 MPa. Os corpos de prova foram sinterizados na temperatura de 1200 ?C com patamar de 8 minutos. Foram realizados ensaios para caracteriza??o das mat?riasprimas por FRX, DRX, AG, ATD e ATG, e analisados os resultados das propriedades f?sicas de absor??o de ?gua, porosidade aparente, retra??o linear, MEA, an?lise dilatom?trica, resist?ncia ? flex?o e MEV do corpo sinterizado. A adi??o de at? 8% do res?duo R1 contribuiu para a diminui??o da porosidade aparente, por?m a resist?ncia mec?nica das amostras n?o foi satisfat?ria. A adi??o de 5% de res?duo R2 contribuiu significativamente para diminuir absor??o de ?gua e porosidade aparente, e tamb?m, para o aumento da resist?ncia mec?nica ? flex?o. As amostras com adi??o do res?duo R2 associado ao feldspato, nas propor??es de 6,7% de R2 e 6,7% de feldspato, obtiveram resultados de absor??o de ?gua de 0,12% e resist?ncia mec?nica ? flex?o de 46 MPa, atendendo aos par?metros normalizados para fabrica??o de porcelanatos

Made available in DSpace on 2014-12-17T14:57:59Z (GMT). No. of bitstreams: 1 EduardoJVD_DISSERT.pdf: 2741868 bytes, checksum: 97ddceb816029ff94f808bc361679f56 (MD5) Previous issue date: 2010-01-12 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Brazil is the world s leading coffee producer. In 2008, 45.99 million of 60 kg bags of benefited coffee were produced. In the process of improvement 50% is grain and 50% is husk, thus, 1.38 million tons of coffee husk are produced annually. The husk is used as combustible in the drying and improvement ovens in the coffee farms, generating ash as residue. These ashes contain a high concentration of alkaline metals and earth metals, mainly K2O and CaO. This work studies the use of this residue in the ceramic tiles industry, as fluxing agents in substitution to the feldspar. Ten mixtures with equal ratios of clay and kaolin, proceeding from Bahia and the residue (varying from 30 to 5%) were defined and produced in uniaxial tool die of 60x20mm with approximately 5 mm of thickness and 45MPa compacting pressure. The samples were fired in four different temperatures: 1100 ?C, 1150 ?C, 1185 ?C and 1200 ?C during 60 minutes and characterized by means of X-ray fluorescence, X-ray diffraction, gravimetric thermal analysis and differential thermal analysis. The results of water absorption, apparent porosity, linear shrinkage, XRD, dilatometry, flexural strength and SEM were also analysed. The test specimen with addition of 10% of ash fired in 1200 ?C resulted in 0.18% water absorption and 40.77 MPa flexural strength, being classified as porcelain stoneware tiles according to ABNT, UNI and ISO norms / O Brasil ? o maior produtor mundial de caf?. Em 2008 foram produzidas 45,99 milh?es de sacas, de 60 Kg, de caf? beneficiado. No processo de beneficiamento 50% ? gr?o e 50% ? casca. Assim, 1,38 milh?es de toneladas de cascas de caf? s?o produzidas anualmente. A casca ? utilizada como combust?vel nos fornos de secagem e beneficiamento nas fazendas de caf?, gerando uma cinza como res?duo. As cinzas da casca de caf? apresentam altas concentra??es de metais alcalinos e alcalinos-terrosos, principalmente K2O e CaO. Este trabalho estuda a utiliza??o deste res?duo na ind?stria de placas cer?micas para revestimentos, como fundente, em substitui??o ao feldspato. Foram definidas 10 formula??es com iguais propor??es de argila e caulim provenientes da Bahia, e o res?duo (variando de 30 a 5%), e confeccionados corpos-de-prova em matriz uniaxial de 60x20mm com aproximadamente 5 mm de espessura, com press?o de compacta??o de 45Mpa. As amostras foram sinterizadas em quatros patamares de temperatura, 1100 ?C, 1150 ?C, 1185 ?C e 1200 ?C durante 60 minutos. Foram realizados ensaios para caracteriza??o das mat?rias-primas por fluoresc?ncia de raios-X, difra??o de raios-X, AG, ATD e ATG e analisados os resultados de absor??o de ?gua, porosidade aparente, retra??o linear, DRX, an?lise dilatom?trica, resist?ncia ? flex?o e MEV. Os corpos de prova com adi??o de 10% da cinza e sinterizados a 1200 ?C obtiveram resultados de absor??o de ?gua de 0,18% e resist?ncia ? flex?o de 40,77 MPa, o que segundo as normas ABNT, UNI e ISO podem ser classificados como gr?s porcelanato