Thesis (M.S.)--West Virginia University, 2005. / Title from document title page. Document formatted into pages; contains vii, 96 p. : ill. (some col.). Includes abstract. Includes bibliographical references (p. 77-79).

Thesis--University of Wisconsin--Madison. / Vita. Photocopy of typescript. Ann Arbor, Mich. : University of Microfilms International, 1979. -- 21 cm. eContent provider-neutral record in process. Description based on print version record. Includes bibliographical references (leaves 175-179).

Thesis (M.S.)--University of Alabama at Birmingham, 2009. / Title from PDF t.p. (viewed June 30, 2010). Additional advisors: Derrick R. Dean, Selvum Pillay, Alan M. Shih. Includes bibliographical references (p. 80-83).

Thesis (M.Phil.)--Hong Kong University of Science and Technology, 2007. / Includes bibliographical references. Also available in electronic version.

Advanced composite materials possessing high specific stiffness and strength have been successfully employed as structural materials in the aerospace, military and automotive industries. Despite the advantages that composites have over other materials, further development has been restricted by their brittleness. The aim of this research project was to improve the energy absorbing capabilities of unidirectional glass fibre epoxy resin composites by coating the fibres with an interlayer. UHMWPE was used as the interlayer because of its outstanding toughness while EPDM of low modulus was used to assess the difference between energy absorption through plastic deformations (UHMWPE) and highly elastic deformations (EPDM).

No description available.

Made available in DSpace on 2014-06-11T19:32:10Z (GMT). No. of bitstreams: 0 Previous issue date: 2012-03-28Bitstream added on 2014-06-13T19:21:28Z : No. of bitstreams: 1 monteiro_aa_dr_ilha.pdf: 1046450 bytes, checksum: 560e13ad3cb62b69f71f9251e2750311 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Neste trabalho de doutoramento é proposto um novo modelo estrutural que explica satisfatoriamente como a estrutura dos vidros do sistema Li2O-TeO2-WO3 responde a estímulos ópticos e elétricos. Esse modelo afirma que a estrutura vítrea é formada basicamente por uma rede composta por poliedros TeO4 na fase α-TeO2 e por ilhas estruturais, as quais são compostas por poliedros TeO4 nas fases α-TeO2 e γ-TeO2 e por pirâmides trigonais O=TeO2. Contudo, dependendo da composição da amostra a estrutura dessas ilhas também pode conter os poliedros: O=WO2, O=WO5 e/ou 2[O=WO5]. Estas são as responsáveis pelas características excepcionais dos teluritos (por exemplo, altos índices de refração) devido sua alta polarizabilidade contribuir com a hiperpolarizabilidade de toda amostra. Os vidros do sistema 80TeO2-(20-x)Li2O-xWO3 para x = 0, 5, 10, 15 e 20 % mol, foram pesquisados por meio das seguintes técnicas experimentais: espectroscopia no infravermelho com transformada de Fourier, espalhamento Raman, espectroscopia de absorção no ultravioleta – visível, difração de raios – X, z-scan, além disso, obteve-se o índice de refração linear na região do visível e na região espectral de teraHertz. A técnica de espectroscopia em teraHertz possibilitou obter os espectros de absorção dessas amostras vítreas os quais mostraram que essa é uma região de alta absorção e como previsto pelo modelo alta magnitude do índice de refração / This doctoral study proposes a new structural model of the glass system Li2O-TeO2-WO3 which satisfactorily explains how the structure responds to optical and electrical stimuli. This model says that the glass structure is basically formed by a network of polyhedral TeO4 in α- TeO2 phase and by clusters which are composed of polyhedra TeO4 in both α- TeO2 and γ-TeO2 phases and by the trigonal pyramids O=TeO2. However, depending on the composition of the sample the structure of the cluster may also contain the polyhedra, O=WO2, O = WO5 and / or 2[O=WO5]. The clusters are responsible for the exceptional characteristics of tellurite (eg, high refractive index) due to its high polarizability sustain the hyperpolarizability of the whole sample. The glass system 80TeO2-(20-x) Li2O-xWO3 for x = 0, 5, 10, 15 and 20 mol%, were studied by the following experimental techniques: infrared spectroscopy, Raman spectroscopy, absorption spectroscopy in the ultraviolet – visible, X-ray diffraction, z-scan, in addition, we obtained the linear refractive index in the visible and in the teraHertz range. The teraHertz spectroscopy technique allowed to obtain the absorption spectra of these samples which showed that this is a region of high absorption and high magnitudes of the refractive index as predicted by the model

Made available in DSpace on 2014-06-11T19:32:10Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-03-22Bitstream added on 2014-06-13T18:43:09Z : No. of bitstreams: 1 figueiredo_ms_dr_ilha.pdf: 1006805 bytes, checksum: 5c550a3c14783fc554cc37dba6517cff (MD5) / No presente trabalho foram sintetizados vidros Te-Li-Ti (TLT) dopados com Er3+ e também codopados com Er3+/Yb3+ para o estudo das propriedades da emissão em 1,5m do íon. Inicialmente foi estudado um conjunto com diferentes concentrações de Er3+ para ver a dependência com a concentração de dopante da eficiência quântica de emissão (). Foi empregado como método experimental de análise a técnica de lente térmica (LT) e os resultados foram confrontados com os determinados usando dados espectroscópicos combinados com a teoria de Judd-Ofelt. Embora sejam fortemente dependentes com a concentração, os valores de  para as concentrações mais baixas de dopante (~76% para o vidro TLT: 0,05% molar de Er2O3) são maiores que os valores reportados na literatura para o mesmo íon em outras matrizes teluritos. Adicionalmente, o sistema codopado com Er3+/Yb3+ foi estudo a fim de avaliar se a adição do Yb3+ na matriz promove o aumento da emissão do érbio em 1,5 m, excitando o nível emissor via Yb3+. Os resultados mostraram que há um eficiente mecanismo de transferência de energia do Yb3+ para o Er3+ de maneira que a intensidade de emissão no infravermelho foi aumentada. Ademais, avaliou-se a existência ou não da emissão “downconversion” em 980 nm do itérbio mediante excitação do Er3+ no visível. Do ponto de vista do “downconversion”, que é interessante para aplicação do material em placas solares à base de silício, os resultados mostraram, pela primeira vez em um vidro telurito, que o efeito ocorre com uma eficiência na transferência de energia do Er3+ para o Yb3+ de 56%, indicando que o material tem boa perspectiva para utilização comercial / In this paper Er3+ doped and Yb3+/ Er3+codoped Te-Li-Ti (TLT) glasses were synthesized to study the properties of the emission at 1.5 m. One set was initially studied with different Er3+ concentrations to see the dependence of emission quantum efficiency () with the dopant concentration. The thermal lens spectrometry (TL) was employed as the method of experimental analysis and the results were compared with those determined using spectroscopic data combined with the Judd-Ofelt theory. Although they are highly dependent on the concentration, the  values for the lower dopant concentrations (~ 76% for the TLT glass doped with 0.05 mol% Er2O3) are higher than those reported in literature for the same ion at tellurite other matrices. Additionally, the Er3+ / Yb3+ codopado system was studied to evaluate the increased emission of erbium at 1.5 m as a function of Yb3+ increment by excitation in the metastable state in Yb3+. The results show that there is an efficient transfer of energy from Yb3+ to Er3+, so that the infrared emission of Er3+ was increased, as was desired. Furthermore, we assessed whether or not the issue ytterbium downconversion emission at 980 nm upon excitation visible in the Er3+. From the viewpoint of the downconversion mechanism, which is interesting for application of the material in solar cells based on silicon, the results showed for the first time in a glass tellurite, which effect occurs with efficiency in energy transfer from Er3+ Yb3+ to 56%, indicating that the material has good prospects for commercial use

Resumo: Este trabalho teve por objetivo principal a preparação de vitrocerâmicas transparentes no sistema PbGeO3-PbF2-CdF2 e a determinação do domínio vítreo no diagrama de composições para este sistema. Observou-se que a introdução dos óxidos de germânio e chumbo na forma de metagermanato de chumbo (PbGeO3) propiciou a diminuição da perda de íons fluoreto durante a síntese das amostras. Foram obtidos vidros bastante estáveis frente a ristalização, com boa qualidade óptica contendo alta concentração de metais pesados. A estrutura local nos vidros foi determinada utilizando-se as técnicas espectroscópicas vibracionais (IV e Raman) e absorção de raios X (EXAFS). Foi possível observar que os vidros possuem unidades estruturais formadas por tetraedros [GeO4] semelhantes àquelas presentes no composto cristalino PbGeO3. Para identificar as fases cristalinas e acompanhar o processo de cristalização em diferentes temperaturas definidas acima da temperatura de transição vítrea, Tg, nas amostras vítreas, foram utilizadas as técnicas de difração raios X, ressonância magnética nuclear de flúor (RMN-19F) e espectroscopia vibracional (IV e Raman). Observou-se que para todas as amostras a primeira fase a cristalizar é o ß-PbF2. Tratamentos térmicos realizados em temperaturas relacionadas ao processo exotérmico denominado pico de "ceramização" possibilitaram a obtenção de vitrocerâmicas transparentes contendo 0,5% em mol de íons Er3+ ou Eu3+. Através das técnicas de microscopia eletrônica de transmissão (MET), espectroscopia eletrônica de emissão dos íons lantanídios foi possível a identificação de cristais de ß-PbF2:Er3+,Eu3+ da ordem de 6 nm. / Abstract: In the present study the glass domain in the PbGeO3-PbF2-CdF2 system is reported. Volatile fluoride loss may be diminished by usage of stoichiometric germanate glass, PbGeO3, instead of introducing individual oxides. Homogeneous glasses with good optical quality were obtained. The structural features in these glasses have been determined by vibrational spectroscopy and X-ray absorption spectroscopy (EXAFS). Tetrahedral structural units [GeO4] similar to those found in PbGeO3 crystal were identified. Crystallization process have been studied at differents temperatures above glass transition temperature, Tg, using X ray diffraction, nuclear magnetic resonance (NMR-19F) and vibrational spectroscopy (IR and Raman) techniques to identify the crystalline phases. Crystalline ß-PbF2 phase have been observed in all glass samples. Transparent glass ceramics were obtained by appropriate heat treatments above glass transition temperature (Tg). Glass composition 60PbGeO3-10PbF2-30CdF2 doped with lanthanide ions Er3+ or Eu3+ are suggest as new infrared emitting devices. By using transmission electronic microscopy (TEM) and X-ray diffraction was possible to identified ß-PbF2 crystals size around 6 nm. Spectroscopy measurements suggest that lanthanide ions concentrate in the crystalline domain. / Orientador: Sidney José Lima Ribeiro / Coorientador: Younès Messaddeq / Banca: Antônio Eduardo Mauro / Banca: Edgar Dutra Zanoto / Mestre

Orientador: Keizo Yukimitu / Banca: Eudes Borges de Araujo / Banca: Ségio Carlos Zilio / Banca: Mauro Luciano Baesso / Banca: Sidney José Lima Ribeiro / Resumo: Neste trabalho de doutoramento é proposto um novo modelo estrutural que explica satisfatoriamente como a estrutura dos vidros do sistema Li2O-TeO2-WO3 responde a estímulos ópticos e elétricos. Esse modelo afirma que a estrutura vítrea é formada basicamente por uma rede composta por poliedros TeO4 na fase α-TeO2 e por ilhas estruturais, as quais são compostas por poliedros TeO4 nas fases α-TeO2 e γ-TeO2 e por pirâmides trigonais O=TeO2. Contudo, dependendo da composição da amostra a estrutura dessas ilhas também pode conter os poliedros: O=WO2, O=WO5 e/ou 2[O=WO5]. Estas são as responsáveis pelas características excepcionais dos teluritos (por exemplo, altos índices de refração) devido sua alta polarizabilidade contribuir com a hiperpolarizabilidade de toda amostra. Os vidros do sistema 80TeO2-(20-x)Li2O-xWO3 para x = 0, 5, 10, 15 e 20 % mol, foram pesquisados por meio das seguintes técnicas experimentais: espectroscopia no infravermelho com transformada de Fourier, espalhamento Raman, espectroscopia de absorção no ultravioleta - visível, difração de raios - X, z-scan, além disso, obteve-se o índice de refração linear na região do visível e na região espectral de teraHertz. A técnica de espectroscopia em teraHertz possibilitou obter os espectros de absorção dessas amostras vítreas os quais mostraram que essa é uma região de alta absorção e como previsto pelo modelo alta magnitude do índice de refração / Abstract: This doctoral study proposes a new structural model of the glass system Li2O-TeO2-WO3 which satisfactorily explains how the structure responds to optical and electrical stimuli. This model says that the glass structure is basically formed by a network of polyhedral TeO4 in α- TeO2 phase and by clusters which are composed of polyhedra TeO4 in both α- TeO2 and γ-TeO2 phases and by the trigonal pyramids O=TeO2. However, depending on the composition of the sample the structure of the cluster may also contain the polyhedra, O=WO2, O = WO5 and / or 2[O=WO5]. The clusters are responsible for the exceptional characteristics of tellurite (eg, high refractive index) due to its high polarizability sustain the hyperpolarizability of the whole sample. The glass system 80TeO2-(20-x) Li2O-xWO3 for x = 0, 5, 10, 15 and 20 mol%, were studied by the following experimental techniques: infrared spectroscopy, Raman spectroscopy, absorption spectroscopy in the ultraviolet - visible, X-ray diffraction, z-scan, in addition, we obtained the linear refractive index in the visible and in the teraHertz range. The teraHertz spectroscopy technique allowed to obtain the absorption spectra of these samples which showed that this is a region of high absorption and high magnitudes of the refractive index as predicted by the model / Doutor