Made available in DSpace on 2017-07-21T20:42:27Z (GMT). No. of bitstreams: 1 Simone Maruchin.pdf: 886299 bytes, checksum: fdac9ee5e7e61bca17d63292c58ddb90 (MD5) Previous issue date: 2007-04-27 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / A industrial composition was utilized for comparison with compositions contaiining 4, 6,8 and 10% of talc, that was prepared to study the influence of this new material in a porcelainized gres composition. This study concerns talc due to the following reasons: Ponta Grossa and Castro are near to Campo Largo´s ceramics pole: the increasing use of this material in products of technological interest; and its increasing acceptance in the market. The importance of a more detailed study was made necessary because talc is a relatively cheap product and with large reserves in the state of Paraná. The study was carried out using different levels of talc purity and varying its proportion to values higher than the ones found in the literature, aiming a larger use of this product. Firstly, the raw materials were characterized according to the chemical and mineralogical compositon as well as the particles size. The compositions were defined by the mineralogical compositions. Every composition had its barbotin done, dried, the proof bodies were shaped and sintherized using different temperatures. Analyses of the shaped samples were carried out according to the proof bodies mechanical characterization. The advantage of using a larger percentage of talc in the porcelainizes gres compositions was assessed according to these results. / Em uma composição utilizada industrialmente foi introduzido talco nas proporções de 0,4,6 e 8% para estudar a influência desse material em uma composição de grês porcelanato. O principal motivo do estudo do talco se prende ao fato da região de Ponta Grossa e Castro estarem proximos ao pólo cerâmico de Campo Largo e a possibilidade de utilização desse material em um produto de grande interesse tecnológico e de aceitação cada vez maior no mercado. Pelo fato do talco ser um produto relativamente barato e com grades reservas no Estado do Paraná, vislumbrou-se a importância de um estudo mais detalhado, utilizando talcos de diferentes purezas, variando sua proporção para valores superiores aos encontrados na literatura e aos praticados atualmente, visando um maior aproveitamento desse produto. Inicialmente as matérias-primas foram caracterizadas quanto à composição química, mineralógica e tamanho das partículas. Foram definidas as composiçõs através das composições químicas e mineralógicas. Foi feita a barbotina de cada composição, secada, conformado os corpos de prova e sinterizados a diferentes temperaturas. Dos corpos de prova das amostras conformadas foram ralizados ensaios de caracterização cerâmica. Com base nesses resultados foi avaliada a possibilidade e vantagem de utilizar-se maior porcentagem de talco nas composições de grês porcelanato.

O trabalho apresenta o estado-da-arte das fachadas-cortina executadas com placas de grês porcelanato, discutindo os principais parâmetros para a elaboração de projetos e produção desta tipologia de revestimentos. Acredita-se ser este um dos primeiros trabalhos acadêmicos elaborados no Brasil sobre o assunto, pretendendo-se contribuir quando da implantação desse sistema no país. Procura-se estabelecer os principais conceitos e definições sobre as fachadas-cortina e fachadas ventiladas, objetivando fundamentar a utilização desses termos que vêm sendo empregados sem precisão pelo meio técnico brasileiro. São abordadas as principais características e propriedades dos componentes, elementos construtivos e dispositivos empregados, como também os principais requisitos a serem considerados quando da elaboração do projeto. São destacadas as vantagens relativas desta tecnologia construtiva quando comparada aos revestimentos tradicionais aderidos, ressaltando-se sua importância como alternativa e potencialidades quando comercializado como um sistema de produção. / This report approaches the state-of-art of the porcelain tiles curtain wall. Both design and installations methods are discussed, including main features and properties of the components, elements and devices necessary. Main requirements considered to the design process are also take into consideration. It is believed that this study is one of the first academic studies developed in Brazil concerning this theme, and it is intended to contribute to the implementation of this system in the country. It aims at establishing the main concepts and the definitions on the curtain walls and ventilated facades. The prime objective is to base the correct use of these terms, since they have been used without accuracy by the Brazilian technicians. main features and properties of the components, elements and devices necessary. Main requirements considered to the design process are also take into consideration. Several advantages concerning this type of cladding are emphasized when compared with traditional coverings, standing out the comportance of the method as an interesting technology alternative.

O trabalho apresenta o estado-da-arte das fachadas-cortina executadas com placas de grês porcelanato, discutindo os principais parâmetros para a elaboração de projetos e produção desta tipologia de revestimentos. Acredita-se ser este um dos primeiros trabalhos acadêmicos elaborados no Brasil sobre o assunto, pretendendo-se contribuir quando da implantação desse sistema no país. Procura-se estabelecer os principais conceitos e definições sobre as fachadas-cortina e fachadas ventiladas, objetivando fundamentar a utilização desses termos que vêm sendo empregados sem precisão pelo meio técnico brasileiro. São abordadas as principais características e propriedades dos componentes, elementos construtivos e dispositivos empregados, como também os principais requisitos a serem considerados quando da elaboração do projeto. São destacadas as vantagens relativas desta tecnologia construtiva quando comparada aos revestimentos tradicionais aderidos, ressaltando-se sua importância como alternativa e potencialidades quando comercializado como um sistema de produção. / This report approaches the state-of-art of the porcelain tiles curtain wall. Both design and installations methods are discussed, including main features and properties of the components, elements and devices necessary. Main requirements considered to the design process are also take into consideration. It is believed that this study is one of the first academic studies developed in Brazil concerning this theme, and it is intended to contribute to the implementation of this system in the country. It aims at establishing the main concepts and the definitions on the curtain walls and ventilated facades. The prime objective is to base the correct use of these terms, since they have been used without accuracy by the Brazilian technicians. main features and properties of the components, elements and devices necessary. Main requirements considered to the design process are also take into consideration. Several advantages concerning this type of cladding are emphasized when compared with traditional coverings, standing out the comportance of the method as an interesting technology alternative.

Made available in DSpace on 2016-06-02T19:11:58Z (GMT). No. of bitstreams: 1 DissCG.pdf: 2415650 bytes, checksum: 6d4f3400b231efd1461031a9b05312e8 (MD5) Previous issue date: 2004-08-27 / Universidade Federal de Minas Gerais / Amongst the various types of ceramic tiles, the porcelainized stoneware tile stands out due to its technical properties (low water absorption, high mechanical strength and high abrasion, chemical attack and frost resistance). In this work, five compositions prepared by mixing ball clay, kaolin, feldspar, quartz and talc (a typical porcelainized stoneware tile composition, as found in the literature, and three new compositions) were studied, to observe the effect on the phase formation and final characteristics, of partial and total replacement of the feldspar by a lab-made vitreous phase former (flux agent). Samples were characterized in terms of physical properties (firing shrinkage, water absorption and flexural strength). The results obtained show that a typical porcelainized stoneware product can be made by replacing the feldspar by the alternative flux agent: partial replacement led to rather satisfying results in terms of apparent porosity, water absorption and mechanical strength; total replacement led to low apparent porosity and water absorption, and high flexural strength. These are very promising results, as they mean a 50 ºC reduction in the firing temperature (relative to the average 1200 ºC, commonly used in industrial practice), which translates into reduced energy consumption. Furthermore, a costly raw material the feldspar could be replaced by a lab-made inert vitreous phase former, with no sacrifice to the processing or the physical and aesthetical properties of the final product. / Dentre os vários tipos de placas para revestimentos cerâmicos, o grês porcelanato se destaca devido às suas propriedades técnicas (baixa absorção de água, alta resistência mecânica e à abrasão, elevada resistência química e ao gelo). Neste trabalho, foram preparadas cinco composições a partir da mistura de argila plástica, caulim, feldspato, quartzo e talco (uma composição típica de grês porcelanato, encontrada em literatura, uma composição obtida a partir da análise química de um produto comercial e três novas composições) com a finalidade de se estudar o efeito na formação de fases e características finais, da substituição parcial e total do feldspato por uma fase vítrea previamente obtida (fluxo). A caracterização das amostras foi realizada por análises físicas (retração linear de queima, absorção de água, resistência mecânica à flexão e à abrasão profunda). Os resultados obtidos mostram que um grês porcelanato típico pode ser produzido a partir da substituição do feldspato por um fundente alternativo: a substituição parcial permite a obtenção de resultados satisfatórios em termos da porosidade aparente, absorção de água e resistência mecânica; a substituição total resulta em uma baixa porosidade e baixa absorção de água e alta resistência mecânica à flexão. Os resultados foram muito promissores, pois se referem a uma diminuição de 50 ºC na temperatura de queima (relativamente a 1200 ºC, a temperatura genérica utilizada industrialmente), com a conseqüente redução no consumo de energia. Alem disso, a matéria-prima de maior custo o feldspato pode assim ser substituída por uma fase vítrea aparentemente inerte, sem comprometimento do processamento nem das propriedades físicas e estéticas do produto final.

Made available in DSpace on 2017-07-21T20:42:45Z (GMT). No. of bitstreams: 1 Karine Coelho Correa.pdf: 9563905 bytes, checksum: 8a65961fdf0ee9c5473b25bbc4f19942 (MD5) Previous issue date: 2007-05-31 / The knowledge of the microstructures and final properties of ceramic masses allow to determine the advantages and limitations of its application in specific conditions. This work had for objective to study the microstructural development of a known mass of porcelainized stoneware formulated with raw materials from south Brazil, especially the formation of the phase mulita, and its influence on the mechanical properties. For so many different amounts of kaolin were added (it already leaves constituent of the mass), to obtain a variation of the amount of phase mulita, and each obtained composition was sintering in 4 different times (30, 60, 120, 240 minutes), being compared the mechanical properties and microstructures obtained in each case. It was verified that as larger the burning time, larger the resistance of the stoneware ceramic. With the kaolin addition the resistance increases to certain point, producing inverse effect for larger amounts than 24% in the ceramic mass in the temperatures of sintering from 120 to 240 minutes. The largest resistance value was 67,54 MPa, obtained in the composition with addition of 24% of kaolin and sintered for 240 minutes. It was observed that the porosity and the absorption of the samples decrease significantly with the increase of the kaolin contents and increase of the temperature. The compositions were analyzed by X ray diffractometry, Scanning Electronic Microscopy, rupture module and physical characterization of samples. / O conhecimento das microestruturas e propriedades finais de massas cerâmicas permite determinar as vantagens e limitações de seu emprego em condições específicas. Este trabalho teve por objetivo estudar o desenvolvimento microestrutural de uma massa conhecida de grês porcelanato formulada com matérias-primas da região, em especial a formação da fase mulita, e sua influência nas propriedades mecânicas. Para tanto foram adicionadas diferentes quantidades de caulim (parte já constituinte da massa), para se obter uma variação da quantidade de fase mulita, e cada composição foi sinterizada em 4 tempos diferentes (30, 60, 120, 240 minutos), sendo comparadas as propriedades mecânicas e microestruturais obtidas em cada caso. Verificou-se que quanto maior o tempo de queima, maior a resistência do grês porcelanato. Com a adição de caulim a resistência aumenta até certo ponto, produzindo efeito inverso para quantidades maiores de 24% na massa cerâmica nos tempos de sinterização de 120 e 240 minutos. O maior valor de resistência foi de 67,54 MPa, obtida na composição com adição de 24% de caulim e sinterizado durante 240 minutos. Observou-se que a porosidade e a absorção das amostras diminuem significativamente com o aumento do teor de caulim e aumento da temperatura. As composições foram analisadas por microscopia eletrônica de varredura (MEV), microanálise por energia dispersiva (EDS), análise qualitativa das fases presentes por difração de raio-X, módulo de ruptura por flexão em três pontos e caracterização física das amostras.