Thesis (Ph. D.)--Drexel University, 2006. / Includes abstract and vita. Includes bibliographical references (leaves 170-193).

Thesis (Ph. D.)--University of Washington, 2007. / Vita. Includes bibliographical references (leaves 51-60).

Diss. (sammanfattning) Göteborg : Göteborgs universitet, 2009. / Härtill 5 uppsatser.

Thesis (M.S.)--University of Texas at Dallas, 2008. / Includes vita. Includes bibliographical references (leaves 80-81)

Made available in DSpace on 2014-08-13T14:50:36Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-09-27Bitstream added on 2014-08-13T18:01:09Z : No. of bitstreams: 1 000737238_20161112.pdf: 71790 bytes, checksum: ac49347ad2d2e7e3dbce398517d332eb (MD5) Bitstreams deleted on 2016-11-16T11:41:26Z: 000737238_20161112.pdf,. Added 1 bitstream(s) on 2016-11-16T12:24:07Z : No. of bitstreams: 1 000737238.pdf: 704035 bytes, checksum: 4766cab07b8f809edd53eff6a1f90da3 (MD5) / Estudos pré-clínicos e clínicos têm demonstrado que algumas condições sistêmicas como o Diabetes mellitus podem alterar o processo de reparo ósseo. Na cavidade bucal, o diabetes pode estar associado à deficiência na osseointegração e pior prognóstico no tratamento com implantes dentais. Assim, modificações na superfície dos implantes que favoreçam a reparação do tecido ósseo poderiam ajudar a compensar as influências deletérias relacionadas ao diabetes. Este estudo tem por objetivo avaliar, em animais diabéticos, a influência de uma superfície modificada por fluoretos na osseointegração. A amostra consistiu de 180 ratos (90 para teste biomecânico e 90 para histometria) aleatoriamente divididos em três grupos de 60 animais: grupo controle (Grupo C), composto por ratos saudáveis; grupo Diabetes descompensado, composto por animais em que foi realizada indução de Diabetes mellitus (Grupo D); e grupo Diabetes Controlado (Grupo DC) em que o diabetes induzido experimentalmente foi controlado com administração de insulina. O diabetes foi induzido em ratos por injeção de estreptozotocina. Após 4 semanas da indução, cada animal recebeu 2 implantes nas metáfises tibiais proximais, sendo 1 de superfície maquinada (M) e o outro de superfície tratada com fluoretos (F). Os animais foram sacrificados 2, 4 e 6 semanas após a instalação dos implantes. A resistência biomecânica foi avaliada ex-vivo por meio do torque de remoção, e a qualidade do tecido ósseo formado ao redor dos implantes por meio de cortes histológicos não descalcificados, aonde mediu-se a superfície de contato osso/implante (BIC) e a fração de área de tecido ósseo entre as roscas do implante (BAFO). Os dados numéricos (peso, glicemia, torque de remoção, BIC e BAFO) foram avaliados estatisticamente por meio do teste de normalidade de Shapiro-Wilk e pelos testes paramétricos ANOVA complementado pelo... / Pre-clinical and clinical studies have been showed that some systemic diseases like the diabetes mellitus may alter the bone repair process. At the oral cavity, the diabetes may be associated with poor osseointegration of dental implants and worsening of the prognosis of dental implants treatment. Thus, modifications on the dental implants surfaces that enhance the bone repair could help to offset the deleterious influences related to diabetes. The aim of this study was to evaluate, in diabetic rats, the influence of different implants surfaces on the osseointegration. A sample of 180 rats (90 for the biomechanical analysis and 90 for the histometric analysis) was randomly allocated in 3 groups of 60 rats each: Control Group (C): Healthy animals; Non-controlled diabetes Group (D): Animals with uncontrolled diabetes; Controlled Diabetes Group (DC): Animals with controlled diabetes. The diabetes was induced by injection of streptozotocin and it was controlled by injectios of insulin. After 4 weeks of the diabetes induction, all the animals received 1 implant in each tibia, one with a machined surface (M) and the other one with a fluoride surface modification. The animals were euthanized 2, 4 and 6 weeks after the implants placement. The biomechanical analysis was performed ex vivo by means of removal torque resistance, and the quality of the bone tissue formed around the implants was assessed by histometric analysis of bone / implant contact (BIC) and bone area between the threads of the implant (BAFO). The numerical data (Weight, Glicemic index, removal torque, BIC, and BAFO) were evaluated by the normality test of Shaprio-Wilk and the one-way Anova complemented by the Tukey´s test. All the statistical test were applied with a significance level of 5%. Regarding the biomechanical analysis, for the machined surface implants, the group D showed lower removal torque values (p <0.05) than the group C...

Made available in DSpace on 2014-06-11T19:28:38Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-03-28Bitstream added on 2014-06-13T20:37:46Z : No. of bitstreams: 1 000738229.pdf: 1438062 bytes, checksum: 6eb2cc869f7ba5a30aaf8b01bd09ff16 (MD5) / Este estudo avaliou (1) o efeito da altura do pilar, dos diferentes cimentos e da termociclagem e (2) o efeito dos diferentes cimentos e da ciclagem mecânica sobre a resistência máxima à tração (RMT) de restaurações implantossuportadas cimentadas. Pilares de titânio (UCLA), com alturas de 4,0 e 6,0 mm (1), ou 4,0 mm (2), foram torqueados com 32 N.cm a análogos de implantes HI. Infraestruturas em Co-Cr, jateadas com óxido de alumínio 50 μm foram cimentadas com: Fosfato de Zinco- FZ; RelyX Luting 2- RXL2; C & B Cement- C&B; RelyX U100- RXU100 e RelyX Temp NE- RXTNE. Os conjuntos foram submetidos aos ensaios de tração (0,5 mm/min) após: 1- armazenagem em saliva artificial a 37 ºC durante 24 h (controle), 2- termociclagem (10.000 ciclos, 5,0 e 55 °C, 30 s de imersão), ou 3- ciclagem mecânica (106 ciclos, 140 N, 15 Hz). Os dados foram analisados por (1) 3- way ANOVA e Dunnett, e (2) 2-way ANOVA e Tukey HSD (α=0,05). Independentemente da altura do pilar, não houve diferença nos resultados dos grupos sem termociclagem (p≥0,05). Após termociclagem, houve aumento (p<0,05) na RMT nos pilares de 6,0 mm. Após ciclagem mecânica, houve diminuição (p<0,05) nos resultados de RMT produzidos por RXL2. A altura do pilar influenciou os resultados do RXL2, que produziu RMT mais elevada com os pilares de 6,0 mm. Com exceção do RXL2, a ciclagem mecânica não comprometeu a RMT das infraestruturas cimentadas. Em determinadas condições, o RXTNE produziu RMT semelhante à alguns cimentos finais. / This study evaluate (1) the effect of abutment height, different cements and thermocycling, and (2) the effect of different cements and cyclic loading on the ultimate tensile strength (UTS) of cement-retained/implant-supported cast restorations. UCLA-type abutments with 4.0 and 6.0-mm height (1), or 4.0-mm height (2) were torqued to with 32 N.cm to internal hexagon dental implant replicas. Copings casted in Co-Cr, sandblasted with 50-μm aluminum oxide particles were cemented with: Zinc Phosphate- ZP; RelyX Luting 2- RXL2; C & B Cement- C&B; RelyX U100- RXU100 and RelyX Temp NE- RXTNE. The assemblies were submitted to the tensile test (0.5 mm/min) after: 1- storage in artificial saliva at 37 °C for 24 h (control), 2- thermocycling (10,000 cycles, 5.0 and 55 ºC, 30-s dwell time), or 3- cyclic loading (106 cycles, 140 N, 15 Hz). Data were analyzed by (1) 3-way ANOVA and Dunnett tests, and (2) 2-way ANOVA and Tukey HSD tests (α=0.05). Regardless of the abutments’ heights, no significant differences were found among the UTS of the nonthermocycled groups (p≥0.05). After thermocycling, an increasing in the UTS was observed for the 6.0-mm abutments (p<0.05). After cyclic loading, the UTS values produced by RXL2 were decreased (p<0.05). The abutment’s heights used affected the RXL2 results, which produced higher results with the 6.0-mm abutments. With the exception of RXL2, cyclic loading did not detrimentally affect the UTS of the cemented castings. In some conditions, the provisional cement RXTNE produced similar UTS to some definitive cements.

Submitted by Ana Paula Simões Corrêa (paulinha_odonto@hotmail.com) on 2018-11-23T01:05:30Z No. of bitstreams: 1 FINAL- TESE Doutorado - Ana Paula APÓS CORREÇÃO.docx: 61180781 bytes, checksum: 21ce72e7304ef07d70cef0a07deeb502 (MD5) / Approved for entry into archive by Ana Paula Rimoli de Oliveira null (anapaula@foa.unesp.br) on 2018-11-23T11:22:45Z (GMT) No. of bitstreams: 1 correa_aps_dr_araca_int.pdf: 5040627 bytes, checksum: 59b1e96d9e32e4e66132171e7d64fec2 (MD5) / Made available in DSpace on 2018-11-23T11:22:46Z (GMT). No. of bitstreams: 1 correa_aps_dr_araca_int.pdf: 5040627 bytes, checksum: 59b1e96d9e32e4e66132171e7d64fec2 (MD5) Previous issue date: 2018-11-05 / Fundação de Amparo à Pesquisa do Estado do Amazonas (FAPEAM) / Modificações físicas e/ou químicas das superfícies dos implantes de titânio podem ser realizadas com intuito de facilitar e estimular o processo de osseointegração, consequentemente favorecendo um tempo de reparo mais curto. Sendo assim, o objetivo deste estudo foi avaliar as superfícies de implantes de titânio, modificadas com deposição de β-tricálcio fosfato pelo método biomimético, inseridos na maxila após levantamento de seio maxilar de coelhos, por meio da análise topográfica, biomecânica, microtomográfica, histológica e imunoistoquímica. Dezoitos (18) coelhos da raça Nova Zelândia (Albinus) receberam trinta e seis (36) implantes após elevação da membrana do seio maxilar bilateral. Foram divididos em dois grupos: No Grupo SBF - Implantes com superfícies modificadas pelo tratamento biomimético e preenchimento do seio maxilar esquerdo com coágulo; Grupo TCP - Implantes com superfícies modificadas com deposição de β-tricálcio fosfato pelo método biomimético e preenchimento do seio maxilar direito com coágulo. Os períodos de estudos foram de 7, 15 e 40 dias, onde foram realizadas as avaliações biomecânica, microtomográfica, histométrica e imunoistoquímica. Nas análises físico-químicas de microscopia eletrônica de varredura- MEV, espectroscopia de energia dispersiva- EDS e mapeamento da mineralização observou-se a formação de uma camada de apatita com maiores quantidades de Ca e P nos implantes com deposição biomimética com β-tricálcio fosfato. O teste de molhabilidade monstrou superfícies de alta hidrofilidade neste grupo de implantes. Na interação entre as superfícies dos implantes de Ticp e seu ambiente biológico, a análise biomecânica demonstrou aumentro da estabilidade dos implantes a partir da 2 semana. Foi observada diferença estatisticamente significante na estabilidade (ISQ) no grupo TCP período de 15 e 40 dias (p= 0,08). A análise microtomográfica demonstrou que no período de 15 dias, o grupo TCP apresentou maior volume ósseo – BV (0,16 mm3), fração do volume ósseo em porcentagem - BV/TV (24,70 mm3), número - Tb.n (2,98 mm3) e espessura do trabeculado ósseo - Tb.th (0,082 mm3), quando comparado com o grupo SBF. Foi visualizado na análise histológica a formação de tecido ósseo em ambos os grupos no período de 15 e 40 dias, maior neoformação óssea foi observada no grupo com a superfície dos implantes modificada com β-tricálcio fosfato, embora a análise histométrica da ELCOI e AON não apresentaram diferenças estatísticas (p<0,05). A imunoistoquímica aos 40 dias apresentou marcação moderada no grupo TCP (50%) e leve (25%) no grupo SBF, para a osteocalcina. A incorporação do β-tricálcio fosfato na superfície dos implantes de Ticp, através da modificação do método biomimético, mostrou-se eficiente diante dos testes de avaliação da topografia dos implantes. Observou-se a influência desse tipo de superfície bioativa ao estimular a osseointegração. Sendo assim, uma opção ao tratamento das superfícies dos implantes. / Physical and/or chemical modifications of the surfaces of the titanium implants can be performed in order to facilitate and stimulate the osseointegration process, consequently favouring a shorter repair time. Thus, the objective of this study was to evaluate the surfaces of titanium implants, modified with deposition of β-tricalcium phosphate by the biomimetic method, inserted in the maxilla after lifting the maxillary sinus of rabbits, employing topographic, biomechanical, histological and immunohistochemical analysis. Eighteen (18) New Zealand rabbits (Albinus) received thirty-six (36) implants after bilateral maxillary sinus membrane elevation. They were divided into two groups: In the SBF Group - Implants with surfaces modified by the biomimetic treatment and filling of the left maxillary sinus with clot; Group TCP - Implants with modified surfaces with deposition of β-tricalcium phosphate by the biomimetic method and filling of the right maxillary sinus with clot. The study periods were 7, 15 and 40 days, where the biomechanical, microtomographic, histometric and immunohistochemical evaluations were performed. In the physico-chemical analyzes of scanning electron microscopy (SEM), dispersive energy spectroscopy (EDS) and mapping of mineralization, the formation of an apatite layer with higher amounts of Ca and P was observed in implants with biomimetic deposition with β-tricalcium phosphate. The wettability test showed high hydrophilicity surfaces in this group of implants. In the interaction between the surfaces of the Ticp implants and their biological environment, the biomechanical analysis showed an increase of the stability of the implants from 2 weeks. Statistically significant difference in stability (ISQ) was observed in the TCP group at 15 and 40 days (p = 0.08). The microtomographic analysis showed that in the period of 15 days, the TCP group presented higher bone volume - BV (0.16 mm3), fraction of the bone volume in percentage - BV / TV (24.70 mm3), number - Tb.n ( 2.98 mm3) and bone trabecular thickness - Tb.th (0.082 mm3) when compared to the SBF group. Bone tissue formation in both groups was visualized in histological analysis in the 15- and 40-day periods, with a greater tendency for bone neoformation to be observed in the group with implants surface modified with β-tricalcium phosphate, although histological analysis of ELCOI and AON did not present statistical differences (p <0.05). The incorporation of β-tricalcium phosphate on the surface of the Ticp implants, through the modification of the biomimetic method, proved to be efficient in the evaluation of the topography of the implants. The influence of this type of bioactive surface on osseointegration was observed. Thus, an option to the treatment of implant surfaces. / FAPEAM: 062.03159.2014; Decisão do conselho: 202/2015

Made available in DSpace on 2014-06-11T19:25:20Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-08-22Bitstream added on 2014-06-13T18:53:16Z : No. of bitstreams: 1 munhoz_fc_me_araca.pdf: 428760 bytes, checksum: 52e5bedbe2781e905f522cced7cbd981 (MD5) / O sucesso dos implantes dentários depende de um cuidadoso planejamento préoperatório. O exame radiográfico é de fundamental importância na avaliação da morfologia, inclinação óssea e localização de estruturas anatômicas críticas durante os procedimentos de implantação, quando é necessário medir a quantidade de osso disponível. A Tomografia convencional é um exame de extrema importância, pois permite a mensuração da altura e espessura do rebordo alveolar, determinantes na escolha do tamanho do implante. Poucos autores estudaram a influência da variação do movimento tomográfico na qualidade da imagem. O objetivo deste trabalho foi elucidar precisamente as áreas avaliadas pelas imagens fornecidas por tomografias realizadas pelo tomógrafo espiral X-MIND TOME, fabricado em 2005 pela SOREDEX, Helsink, Finlândia. Foram utilizadas dez mandíbulas humanas secas, desdentadas na região dos pré-molares e molares. Os implantes foram posicionados bilateralmente em oito mandíbulas e unilateralmente em duas, com a distância de 4 mm um do outro. Em seguida, cada mandíbula foi adaptada ao tomógrafo, onde foi realizada uma radiografia panorâmica prévia, com magnificação de 50%. Sobre esta radiografia foi colocado um template que determina a região a ser avaliada, sendo realizados cortes de 4mm de largura, nos dois lados da mandíbula. Comparou-se então a solicitação ao tomógrafo com os resultados obtidos, quanto à distância e a ordem dos cortes solicitados. Foram realizadas 19 tomografias que foram avaliadas utilizando-se o programa Radioimp RADIO MEMORY – Belo Horizonte – Brasil. Em seguida, os dados foram tabulados, analisados e estudados estatisticamente, com nível de significância 5%. Através do teste de Wilcoxon, não foram evidenciadas diferenças estatisticamente significantes nos dados obtidos pelas tomografias, sendo, portanto, precisas. / The success of dental implants depends on a carefull pre-opertative planning. The radiographic exam is of main importance for a correct evaluation of morphology, bone inclination and location of critical anatomical structures during the surgical procedures for dental implants, when it’s necessary to measure the amount of available bone. The conventional Tomography is a very important exam, because it allows the measurement of height and thickness of the alveolar bone for the determination of the implant’s size. Few authors studied the influence of the tomographic movement variation in the quality of the image. The aim of the present paper is to clarify the precision of the areas evaluated by the images given by the spiral scanning X-MIND TOME, made in 2005 by SOREDEX, Helsink, Finland. There were used 10 dried mandibles, toothless in the region of pre-molars and molars. The implants were placed in both sides in eight mandibles and in one side in two, with the distance of 4mm one from another. After this, each mandible was placed in the scanning, where a previous panoramic radiograph was taken, with magnification of 50%. Upon this radiograph, it was placed a template to determine the region to be evaluated, where there were made cuts of 4mm of width, in both sides of the mandible. The scanning request was then compared to the obtained results. It was made 19 radiographs that were evaluated using the Radioimp program (RADIO MEMORY – Belo Horizonte – Brazil). The data were then analyzed and studied statistically, with significance of 5%. Throught wilcoxon test, there were not noticed statistical differences in the data obtained in the tomographies, that showed to be precise.

Made available in DSpace on 2014-06-11T19:31:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-08-30Bitstream added on 2014-06-13T18:41:42Z : No. of bitstreams: 1 souza_fa_dr_araca.pdf: 2491659 bytes, checksum: 017388e8b7b826e5dad08553556571ca (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Proposição: O objetivo deste estudo foi comparar o comportamento biológico e mecânico do tecido ósseo ao redor de implantes de superfícies comerciais modificada por condicionamento ácido (SA), e usinada (SU), com implantes de superfícies experimentais modificada por laser (SL), e modificada por laser com depósito de sílica (SS), empregando-se as análises biomecânica, topográfica e histométrica. Material e Métodos: Trinta coelhos receberam 120 implantes de 3,75x10mm em suas tíbias direita e esquerda, sendo dois implantes de cada superfície por tíbia. O implante localizado mais superior, instalado na metáfise tibial foi utilizado para o ensaio biomecânico, descrito no capítulo I; e o implante localizado abaixo deste, instalado na epífise tibial foi utilizado para o estudo histométrico, descrito no capítulo II. A morfologia das superfícies dos implantes foi analisada por microscopia eletrônica de varredura (MEV), e por espectroscopia de energia dispersiva de raios X (EDS) antes, e após 4 semanas de implantação e remoção por torque reverso. Medidas de rugosidade e secção transversal foram obtidas. Após períodos de 4, 8, e 12 semanas realizou-se o ensaio biomecânico, e após os animais sofreram eutanásia. As peças do implante localizado na epífise tibial foram levadas ao micrótomo para corte sem descalcificação. A análise histométrica foi realizada empregando-se microscopia óptica. Foi mensurada a extensão linear de contato entre osso e implante (ELCOI), e a área óssea (AO). Uma lâmina de cada superfície do período de 4 semanas foi metalizada para realização da análise do mapeamento elementar por MEV-EDS. Resultados: A caracterização topográfica mostrou diferenças entre as superfícies analisadas, e os valores de rugosidade média das SL e SS foram estatisticamente superiores (p<0,05) a SA. Na comparação estatística dos valores obtidos... / Purpose: The aim of this study was to compare the biologic and mechanical behavior of bone tissue around implants with commercially available surfaces, modified by acid etching (SA), and machined surfaces (SU), with the experimental surfaces modified by laser (SL), and modified by laser with silica deposition (SS), using biomechanical, topographic and histometric analyses. Materials and Methods: Thirty rabbits received 120 implants measuring 3,75x10mm in their right and left tibias, being two implants of each type of surface per tibia. The implant located in the uppermost position, inserted in the tibial metaphysis, was used for the biomechanical test, described in Chapter I; and the implant located below this, inserted in the tibial epiphysis, was used for the histometric study, described in Chapter II. The morphology of the implant surfaces was analyzed by scanning electron microscopy (SEM) and by energy dispersive X-ray spectrometry (EDS) before and after 4 weeks of implantation and removal by reverse torque. Mean roughness and cross-sectional measurements were obtained. After periods of 4, 8, and 12 weeks the biomechanical test was performed, and after this the animals were euthanized. The parts of the implant located in the tibial epiphysis were taken for cutting nondecalcified on a microtome. Histometric analysis was performed using an optical microscope. The bone interface contact (BIC), and the bone area (AO) were measured in percentages. A slide of each surface in the period of 4 weeks was metalized in order to analyze the element mapping by means of SEM-EDS. Results: The topographic characterization showed differences between the analyzed surfaces, and the mean roughness values of SL and SS were statistically higher (p<0,05) than those of SA. In the statistical comparison of the values obtained by the biomechanical test, it was... (Complete abstract click electronic access below)

Made available in DSpace on 2014-06-11T19:32:40Z (GMT). No. of bitstreams: 0 Previous issue date: 2011-09-09Bitstream added on 2014-06-13T20:04:02Z : No. of bitstreams: 1 scala_a_dr_araca.pdf: 881800 bytes, checksum: e5815e800d5d9d273ba4ee24380c2131 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Objetivo: Avaliar a influência da plataforma Switching sobre a remodelação dos tecidos peri-implantares. Material e métodos: Em 6 cães labradores, foram extraídos os pré-molares e primeiro molares inferiores bilateralmente. Após 3 meses de cicatrização, na região correpondente ao 1º molar, foi instalado um implante cônico em cada lado da mandíbula, com o ombro do mesmo posicionado ao nível da crista óssea alveolar vestibular. No lado direito da mandíbula, foi utilizado um pilar de diâmetro reduzido em relação à plataforma do implante, criando uma incompatibilidade de 0,85 milímetros (grupo teste), enquanto no lado esquerdo selecionou-se um pilar do mesmo diâmetro da plataforma do implante (grupo controle). Os retalhos foram suturados permitindo a cicatrização não-submersa. Após 4 meses, os animais foram eutanasiados para obtenção dos cortes histológicos para avaliação histométrica. Resultados: Todos os implantes apresentaram-se completamente osseointegrados. No grupo teste foram observados que os níveis ósseos apresentaram-se superiores ao grupo controle. No entanto, a diferença estatisticamente significativa foi encontrada apenas na região vestibular e na região proximal. A dimensão vertical dos tecidos moles foi maior no grupo controle em comparação ao grupo teste. No entanto, foi encontrada diferença estatisticamente significativa apenas na vestibular. Conclusões: O presente estudo demonstrou diferenças nas dimensões dos tecidos duros e moles peri-implantares (vestibular e proximal) como resultado da incompatibilidade do implante / pilar de 0,85 milímetros, quando o ombro do implante foi posicionado ao nível da crista óssea vestibular / Aim: to evaluate the effect of platform switching on the peri-implant tissue remodeling. Material & methods: Mandibular premolars and first molars of 6 Labrador dogs were extracted bilaterally. After 3 months of healing, 1 tapered implant was installed on each side of the mandibular molar region with the implant shoulder placed at the level of the alveolar buccal bony crest. On the right side of the mandible, an abutment of reduced diameter in relation to the platform of the implant was used creating a mismatch of 0.85mm (test), while an abutment of the same diameter of the implant platform was affixed in the left side of the mandible (control). The flaps were sutured to allow a non-submerged healing. After 4 months, the animals were sacrificed and ground sections were obtained for histometric assessment. Results: All implants were completely osseointegrated. Bone levels were superior at the test than at the control sites. However, statistically significant differences were found only at the buccal and proximal aspects. The soft tissue vertical dimension was higher at the control compared to the test sites. However, statistically significant differences were demonstrated only or at the buccal aspects. Conclusions: The present study demonstrated differences in peri-implant (buccal and proximal) hard and soft tissue dimensions as a result of an implant/abutment mismatch of 0.85mm, when the implant shoulder was placed at the level of the buccal bony crest