Submitted by Reginaldo Soares de Freitas (reginaldo.freitas@ufv.br) on 2015-12-09T13:09:59Z No. of bitstreams: 1 texto completo.pdf: 640397 bytes, checksum: f236b298f8d2d17b6e27e4c07efff7fa (MD5) / Made available in DSpace on 2015-12-09T13:09:59Z (GMT). No. of bitstreams: 1 texto completo.pdf: 640397 bytes, checksum: f236b298f8d2d17b6e27e4c07efff7fa (MD5) Previous issue date: 2015-10-08 / Fundação de Amparo à Pesquisa do Estado de Minas Gerais / O objetivo deste trabalho foi avaliar o efeito do tratamento hidrotérmico de flocos (partículas do tipo strand) de pinus e eucalipto, nas propriedades físico-mecânicas de painéis OSB. Partículas strands de pinus e eucalipto, com 23 x 90 x 0,30 mm de largura, comprimento e espessura, respectivamente; foram pré-hidrolisadas a 130, 150 e 170oC por 7 e 21 minutos. Foram determinados os teores de extrativos, de lignina e de carboidratos dos flocos, assim como o pH, a umidade de equilíbrio, o ângulo de contato dos flocos com o adesivo fenol formaldeído e as propriedades colorimétricas. Em seguida foram confeccionados painéis do tipo OSB, com uma densidade nominal de 0,7 g/cm3 e um ciclo de prensagem com a temperatura de 170°C, pressão de 32 kgf/cm2 por 8 minutos. O adesivo utilizado foi o fenol-formaldeído no teor de 8% (base massa seca das partículas). Posteriormente os painéis foram mantidos em câmara climática a temperatura de 20 ± 2oC e umidade relativa de 65 ± 3%, até estabilização e em seguida determinou-se as propriedades físicas e mecânicas. A temperatura foi mais efetiva para alterar a composição química da madeira que o tempo de exposição ao tratamento. A temperatura do tratamento hidrotérmico de 170°C provocou maiores modificações químicas. O comportamento colorimétrico da madeira com a pré-hidrólise variou com o tratamento, sendo que a madeira de pinus foi mais resistente ao escurecimento que a de eucalipto. Os tratamentos hidrotérmicos a 170°C foram os mais eficientes na redução da umidade de equilíbrio higroscópico dos flocos de pinus e consequentemente aumentou a estabilidade dimensional dos painéis. O ângulo de contato do adesivo fenol-formaldeído com as superfícies dos flocos de pinus tratados apresentou uma leve diminuição, favorecendo a adesão do adesivo com a madeira, contudo a ligação interna dos painéis não foi afetada. Para a madeira de pinus o tratamento hidrotérmico causou degradação de alguns constituintes químicos principalmente de mananas, xilanas e arabinanas, o que causou uma acidificação e também perda de massa nos flocos, isso consequentemente diminuiu o inchamento em espessura e não influenciou negativamente nas propriedades mecânicas dos painéis OSB. O tratamento hidrotérmico a 170°C durante 7 minutos permitiu que o painel OSB de pinus, além da categoria 1, também se enquadre na categoria 2 da norma européia, ampliando sua gama de utilização. Para os flocos de eucalipto o tratamento hidrotérmico, principalmente com a temperatura de 170°C, causou degradação de alguns constituintes químicos principalmente galactanas, xilanas e arabinanas e diminuiu a umidade de equilíbrio higroscópico e também causou uma acidificação e perda de massa dos flocos. Os tratamentos hidrotérmicos com a temperatura de 170°C foram os mais eficientes para melhorar a estabilidade dimensional dos painéis OSB de eucalipto, uma vez que reduziu os valores de UEH (umidade de equilíbrio higroscópico), AA24h (absorção de água) e IE24h (inchamento em espessura). O tratamento hidrotérmico a 170°C durante 7 minutos, assim como a 130°C por 7 minutos e a 150°C por 21 minutos, permitiu que o painel OSB de eucalipto além da categoria 1, também se enquadre na categoria 2 da norma européia, ampliando sua gama de utilização. Além de indicados para uso geral, ou seja, quando não são submetidos a suporte de carga e painéis para uso interior em condições de ambiente seco ele passa a ser indicado também para utilização que suporte cargas. Os painéis de eucalipto apresentaram menores valores de inchamento em espessura e absorção de água quando comparados com os painéis de pinus, devido a menor taxa de compactação desses painéis. Os valores do módulo de elasticidade e de ruptura, dos painéis de pinus e eucalipto, foram próximos, contudo os painéis de pinus apresentaram maiores valores de ligação interna. / The aim of this study was to evaluate the effect of hydrothermal treatment in strands particles of pine and eucalyptus, on physical and mechanical properties of OSB. Eucalyptus and pine strands particles with 23 x 90 x 0.30 mm width, length and thickness, respectively; it was pre-hydrolysed at 130, 150 and 170°C for 7 and 21 minutes. The contents of extractives, lignin and carbohydrates of strands particles, as well as pH, moisture balance, the contact angle of the particles with phenol formaldehyde adhesive and colorimetric properties were detemined. OSB panels were prepared with a nominal density of 0.7 g/cm3, with a temperature of 170°C, pressure of 32 kgf/cm2 for 8 minutes. The phenol-formaldehyde adhesive was uded in 8% content (based on dry weight of the particles). Subsequently the panels were exposed to conditioning under ambient conditions of 20 ± 2°C and 65 ± 3% relative humidity, and then were determined physical and mechanical properties. The temperature was more effective to change the chemical composition of wood than the time. The prehydrolysis temperature of 170°C resulted in higher chemical modifications. The colorimetric behavior with the prehydrolysis varied with the treatment. Pine wood was more resistant to darkening than eucalyptus. The hydrothermal treatment at 170 ° C was the most efficient in reducing the moisture equilibrium moisture content of pine strand particles and consequently improving dimensional stability of the panels. The contact angle of the adhesive phenol formaldehyde with the surfaces of the treated pine strand particles showed a slight decrease in this case favoring the adhesion of the adhesive with the wood, however, the internal connection of the panels was not affected. For pinus wood the hydrothermal treatment caused degradation of some chemical constituents mainly mannans, xylans and arabinans, causing acidification as well as mass loss in the strand particles, this consequently decreased swelling in thickness and not showed negative effect on the mechanical properties of OSB. The hydrothermal treatment at 170°C for 7 minutes allowed the pine OSB panel beyond Category 1 and also met the requirements in Category 2 of the European standard, expanding its range of use. For eucalyptus strand particles the hydrothermal treatment, especially the temperature of 170°C caused degradation of some chemical constituents mainly galactans, xylans and arabinans, it decreased moisture equilibrium moisture content and also resulted in acidification as well as the loss of mass of the strand particles. The hydrothermal treatment at a temperature of 170°C was the most efficient in improving the dimensional stability of OSB from eucalyptus particles, since reduced amounts of EMC (equilibrium moisture content), and WA24h (water absorption), TS24h (thickness swelling). The hydrothermal treatment at 170°C for 7 minutes, at 150°C for 21 minutes and at 130°C for 7 minutes allowed eucalyptus OSB beyond category 1 also fits the category 2 of European standard, expanding its range of use. Besides indicated for non load-bearing boards, general purpose boards and boards for the interior fitments for use in dry conditions it is now also indicated load-bearing boards. The eucalyptus panels showed lower values of thickness swelling and water absorption when compared with pine panels, it was because of lower compression ratio of such panels. The values of elastic and rupture modulus of pine and eucalyptus panels were close, however pine panel showed higher internal bond values.

Orientador: Raquel Gonçalves / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Agricola / Made available in DSpace on 2018-08-06T00:21:33Z (GMT). No. of bitstreams: 1 Silva_SergioAugustoMelloda_D.pdf: 3060293 bytes, checksum: 3514c54e017be522e62c07231642a540 (MD5) Previous issue date: 2003 / Resumo: As tecnologias para produção das chapas denominadas ¿Medium Density Fiberboard¿ (MDF), confeccionadas com fibras de madeiras de reflorestamento de baixo custo e resinas fenólicas provenientes de uréia, representam para vários setores industriais uma possibilidade de agregar valores às espécies com pouco interesse comercial, possibilitando para os seguimentos industriais investimento promissores. Um aspecto importante a ser considerado sobre a utilização de resinas fenólicas na confecção de chapas MDF é que produzem emissões tóxicas poluidoras da natureza e nocivas ao ser humano. Dentro deste contexto, de acordo com o ¿Protocolo de Quioto¿ de 1997, os países industrializados precisam diminuir suas emissões combinadas de gases de efeito estufa em pelo menos 5 % até 2012. Considerando-se as exigências do ¿Protocolo de Quioto¿, este trabalho objetivou avaliar o desempenho de chapas MDF confeccionadas com poliuretana (PU) derivada do óleo de mamona, pois este produto apresenta baixos teores de toxidez sendo classificado como não poluente e não tóxico ao ser humano. A caracterização das chapas foi realizada considerando-se a utilização do equipamento de ultra-som da Marca Steinkamp modelo BP7 com transdutoes de 45 kHz e a realização de ensaios físicos e mecânicos propostos pela EuroMDFBoard - EMB. A avaliação desenvolveu-se em três fases distintas: 1. Na fase I foram realizados estudos exploratórios com o objetivo de verificar as características do PU sendo utilizado como adesivo para confecção de chapas de Pinus caribaea. Nesta fase foram confeccionadas chapas com 5 e 10 % de PU3070, que de acordo com a caracterização física e mecânica observou-se que as chapas apresentaram resistências compatíveis com as exigências da EMB, entretanto, a forte exalação de solvente inviabilizou seu manuseio do PU3070. 2. Na fase II foram confeccionadas chapas com fibras de Pinus caribaea e Eucalyptus grandis com uma nova síntese de adesivo, denominada neste trabalho de PU7030. A caracterização física e mecânica determinou valores de resistências compatíveis com as exigências da EMB. Entretanto, verificou-se a necessidade de se ajustar o teor de umidade a temperatura e a pressão de prensagem. 3. Na fase III novas chapas foram confeccionadas com fibras de Pinus caribea e Eucalyptus grandis modificando-se o teor de umidade, a temperatura e a pressão de prensagem. Com o resultado da caracterização física e mecânica, observou-se que as alterações nas umidades, temperatura e pressão de prensagem propiciaram resistências compatíveis com a EMB, com vantagens de utilização de menores teores de PU7030 e diminuição na temperatura de prensagem, representando economia no consumo de energia. Outro aspecto muito importante estudado neste trabalho foi a caracterização das chapas utilizando ensaios não-destrutivos. Neste caso foram realizadas medições, por meio de equipamento de ultra-som, utilizando-se transdutores de faces exponenciais e planas aplicados nas direções x, y e z das chapas. A partir das medições dos tempos de propagação das ondas ultra-sônicas determinaram-se as velocidades das ondas e as constantes dinâmicas das chapas. Estas variáveis foram comparadas com as propriedades de resistência das chapas obtidas nos ensaios estáticos. Em seguida desenvolveu-se análise estatística buscando-se avaliar as correlações entre os resultados de ensaios não-destrutivos e destrutivos tendo sido possível concluir que a utilização dos métodos de ensaios não-destrutivos é viável para inferir sobre as propriedades físicas e mecânicas das chapas. Com relação à utilização da PU7030, concluiu-se que essa poliuretana possibilita a substituição da resina fenólica na confecção das chapas MDF / Abstract: While employing low cost reforestation lumber, the technologies of the fabrication of fiber plates denominated ¿Medium Density Fiberboard¿ (MDF) offer to several industrial sectors the opportunity to aggregate worth to species with little or no commercial interest, opening to them the possibility of promising profitable investments. However, the phenolic resins used in the production of MDF plates are well-known pollutants to the environment and therefore harmful to the human beings in such a way that environmentally friendly alternatives have been eagerly sought. According to that, the present work has been aimed to evaluate the physical, chemical and mechanical properties of MDF manufactured with Polyurethane Adhesive (PU) derived from Castor Oil, due to the low toxicity and to the non-polluting characteristics of the resulting adhesive. The characterization of the plates has been accomplished with the help of Steinkamp BP7 ultrasonic equipment using 45 kHz transducers and the physical and mechanical tests recommended by Euro MDF Board - EMB. The work has been developed along three distinct phases. Initially a better understanding of the characteristics of the polyurethane adhesive derived from castor oil has been acquired. It has been learnt that the adhesive exhibits the main characteristic of a monocomponent synthesis, stabilized by air humidity. During that phase, plates with 5% and 10% of polyurethane adhesive have been manufactured, called Adhesive PU3070 in this work, corresponding to 30% of solids and 70% of solvents. The properties of the plates manufactured with this synthesis have been determined and it has been found that although they have met EMB demands, the strong exhalation of solvent has ruled out its usage for MDF manufacture. As for the second phase, fiber plates have been produced with a new synthesis, called Adhesive PU7030, that is, 70% of solids and 30% of solvents. Again mechanical properties have satisfied EMB regulations. However, during the tests, it has been noticed that in order to control the quality of the final product, a fine adjusting to the values of some important Variables in the manufacture process, such as humidity level, temperature and pressing pressure, would be necessary. Accordingly, in the last phase, using Pinus caribea as fiber material, three experimental conditions have been elaborated, one for each controlled Variable, and repeated again for Eucalyptus gandis. Resulting from the adjusting of the variables, it has been observed that during the manufacture process, plates using much less adhesive than the former standards still have satisfied EMB demands fully, with advantages of a significant decrease in the pressing temperature and the corresponding energy savings. The characterization of the plates using non-destructive tests has been an important feature of the present work. Measurements have been performed in the plates by means of ultrasound equipment, using exponential as well as plane face transducers. From the readings, the propagation times of the ultrasonic waves have been evaluated, allowing to the determination of the propagation velocity of the ultrasonic waves through the material and consequently its dynamic parameters, which have been correlated to the mechanical properties of the plates, by means of a suitable statistic model. It has been concluded from the results that non-destructive test methods could as well be employed for the characterization of the physical and mechanical properties of the plates / Doutorado / Construções Rurais / Doutor em Engenharia Agrícola

Submitted by Lúcia Brandão (lucia.elaine@live.com) on 2015-07-17T19:17:36Z No. of bitstreams: 1 Dissertacao - Álefe Lopes Viana.pdf: 4010509 bytes, checksum: 4ad1d7c025d9ac2ae1bf19ac3d1b9fa0 (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2015-07-20T12:58:04Z (GMT) No. of bitstreams: 1 Dissertacao - Álefe Lopes Viana.pdf: 4010509 bytes, checksum: 4ad1d7c025d9ac2ae1bf19ac3d1b9fa0 (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2015-07-20T13:01:37Z (GMT) No. of bitstreams: 1 Dissertacao - Álefe Lopes Viana.pdf: 4010509 bytes, checksum: 4ad1d7c025d9ac2ae1bf19ac3d1b9fa0 (MD5) / Made available in DSpace on 2015-07-20T13:01:37Z (GMT). No. of bitstreams: 1 Dissertacao - Álefe Lopes Viana.pdf: 4010509 bytes, checksum: 4ad1d7c025d9ac2ae1bf19ac3d1b9fa0 (MD5) Previous issue date: 2014-06-17 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The low attractiveness of forestry activities has been one of several factors responsible for the lack of competitiveness in the sector. Performance improvement of manufacturing processes depends on the identification of technological and organizational factors responsible for production efficiency in mobile industries. Problems such as lack of designer in product design, raw material waste, product quality, marketing strategies and inefficient manufacturing has raised the cost of production of products. One way to improve is to know the costs related to processes to tangible solutions. Based on this premise, the research used the method of activity-based costing (ABC) to analyze the factors involved in the production of two wooden artifacts case: center table and armchair, both produced with tauari wood. The ABC operates as a management tool, which employs the costs of activities to determine product costs, avoiding problems with apportionment of indirect costs. For this we used the technique chronoanalysis which allowed the preparation of the map of the process flow for both products, indicating the main bottlenecks of production characterized as activities that do not add value to the product, contributing only to the increase in unit cost. The activities that add value to both products were sanding, gluing / mounting and application of sealer. Activities that add value less characterized by its high setup time and measurements, to the table, were drilling, squaring and sewing rabbet; for the chair was the squaring, drilling and production of spikes. Material costs were higher in workmanship. Regarding the materials, to the table, the raw materials with the greatest cost was wood, MDF and the blade. For the armchair, costs and foam corvin were the highest. The share of share of costs with the wood compared to the final cost of the product did not exceed 14% to 24% for armchair and coffee table. As a recommendation, it is suggested that an ongoing study for the improvement of processes, reviewing and verifying the level of importance of activities, developing new processes that can give speed to the flow of production. / A baixa atratividade das atividades florestais tem sido uma das várias causas responsáveis pela ausência de competitividade no setor. A melhoria do desempenho dos processos de fabricação depende da identificação dos fatores tecnológicos e organizacionais responsáveis pela eficiência produtiva nas indústrias de móveis. Problemas como ausência de designer no projeto de produtos, desperdícios de matéria-prima, qualidade dos produtos, estratégias comerciais e fabricação ineficiente tem elevado os custos do processo de produção de produtos. Uma das formas de melhoria é conhecer os custos relacionados aos processos, visando soluções palpáveis. Baseado nesta premissa, a pesquisa usou o método de custeio baseado em atividades (ABC) para analisar os fatores envolvidos no processo de produção de dois artefatos de madeira: mesa de centro e poltrona, ambos produzidos com madeira de tauari. O ABC atua como uma ferramenta de gerenciamento, que emprega os custos das atividades para determinar os custos do produto, evitando problemas com rateio dos custos indiretos. Para isso foi usada a técnica de cronoanálise que permitiu a elaboração do mapa do fluxo do processo para os dois produtos, apontando os principais gargalos da produção caracterizadas como atividades que não agregam valor ao produto, contribuindo apenas para o aumento do custo unitário. As atividades que mais agregaram valor, para ambos os produtos, foram lixamento, colagem/montagem e aplicação de selador. As atividades que menos agregaram valor, caracterizadas por seu alto tempo de setup e medições, para a mesa, foram furação, esquadrejamento e confecção das sambladuras; para a poltrona foi o esquadrejamento, furação e confecção de espigas. Custos com materiais foram superiores à mão de obra. Em relação aos materiais, para a mesa, as matérias-primas que obtiveram maior custo foi a madeira, o painel MDF e o disco de serra. Para a poltrona, os custos com espuma e corvin foram os mais elevados. A participação de participação dos custos com a madeira em relação ao custo final do produto não ultrapassou 14% para a poltrona e 24% para a mesa de centro. Como recomendação, sugere-se um estudo contínuo para a melhoria dos processos, reavaliando e verificando o nível de importância das atividades, desenvolvendo novos processos que possam dar velocidade ao fluxo de produção.

Submitted by Lúcia Brandão (lucia.elaine@live.com) on 2015-07-20T18:11:59Z No. of bitstreams: 1 Dissertação - Renata do Nascimento Melo.pdf: 3167649 bytes, checksum: 8c000ab4581071b3faa10277883a36b9 (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2015-07-22T13:27:12Z (GMT) No. of bitstreams: 1 Dissertação - Renata do Nascimento Melo.pdf: 3167649 bytes, checksum: 8c000ab4581071b3faa10277883a36b9 (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2015-07-22T13:29:55Z (GMT) No. of bitstreams: 1 Dissertação - Renata do Nascimento Melo.pdf: 3167649 bytes, checksum: 8c000ab4581071b3faa10277883a36b9 (MD5) / Made available in DSpace on 2015-07-22T13:29:55Z (GMT). No. of bitstreams: 1 Dissertação - Renata do Nascimento Melo.pdf: 3167649 bytes, checksum: 8c000ab4581071b3faa10277883a36b9 (MD5) Previous issue date: 2014-01-17 / CNPq - Conselho Nacional de Desenvolvimento Científico e Tecnológico / Due the need of improving the management of both products as processes in the production chain of wood in the Amazon came the urgent need to meet the technological factors that influence decision making. Among the success criteria for the sector are quality management, production capacity and cost management. The present study sought to determine the relationship between the costs of raw wood and machining costs in the process of cutting, milling and drilling to find out which factors critical to machining costs in the manufacture of wood products in city of Manaus, the assumption that the raw material is not a critical success for the product cost factor because there is a cultivated by the local productive sector that the availability of wood provides a competitive advantage over other producing regions belief. Through the work of the company, required for calculation of costing data, using a product with two different models were listed. After identifying the data and the calculations, it was possible through tables and graphs, comparing the results obtained on the transactions analyzed, the results between product models and the relationship between the costs. The analyzes showed that there were differences between the variables in the model I, pointing the cutting process as the most costly and model II, both pointing the cutting process as the milling process with greater results, with the drilling process, presenting lower results for both models. Among the costs, the analysis showed that machining costs are higher chair by the cost per timber chair. The results also showed that the causes of low production efficiency in machining woods are mainly related to the lack of cost of improvement of the product, lack of research being directed at meeting demand, lack of skilled manpower, organization of company poor, no metric information that may assist in planning costs. The work contributed to the generation of knowledge about the analysis of machining costs, providing better utilization of resources and demystifying the belief that the availability of wood is a critical success for the production of wood products in Amazon factor. / Devido à necessidade de melhorar a gestão tanto de produtos quanto de processos na cadeia produtiva da madeira no Amazonas, surgiu a urgente necessidade de conhecer os fatores tecnológicos que influenciam nas tomadas de decisão. Entre os critérios de sucesso para o setor estão a gestão da qualidade, da capacidade produtiva e a gestão de custos. O presente estudo buscou determinar a relação entre os custos da matéria prima madeira e os custos de usinagem e os custos de usinagem nos processos de corte, fresamento e furação para saber quais os fatores críticos para os custos de usinagem na confecção de produtos de madeira na cidade de Manaus, do pressuposto de que a matéria prima não é um fator crítico de sucesso para os custos do produto, pois há uma crença cultivada pelo setor produtivo local de que a disponibilidade de madeira proporciona vantagens competitivas em relação a outras regiões produtoras. Mediante o trabalho desenvolvido na empresa, foram coletados os dados necessários para os cálculos da determinação dos custos, usando-se um produto com dois diferentes modelos. Após a identificação dos dados e realização dos cálculos, foi possível fazer por meio de tabelas e gráficos, a comparação entre os resultados obtidos nas operações analisadas, os resultados entre os modelos do produto e a relação entre os custos. As análises mostraram que houve diferença entre as variáveis no modelo I, apontando o processo de corte como o mais oneroso e no modelo II, apontando tanto o processo de corte como o processo de fresamento com resultados maiores, sendo o processo de furação, apresentando menor resultado para ambos os modelos. Entre os custos, a análise mostrou que os custos de usinagem por cadeira são maiores que o custo da madeira por cadeira. Os resultados obtidos também mostraram que as causas da baixa eficiência produtiva na usinagem de madeiras estão relacionadas, principalmente, ao desconhecimento dos custos do beneficiamento do produto, ausência de pesquisas mais direcionadas ao atendimento da demanda, falta de mão de obra qualificada, organização da empresa deficiente, ausência de informações métricas que possam auxiliar no planejamento dos custos. O trabalho contribuiu com a geração de conhecimento sobre a análise dos custos de usinagem, propiciando o melhor aproveitamento dos recursos e desmistificando a crença de que a disponibilidade de madeira é um fator crítico de sucesso para a produção de produtos de madeira na Amazônia.

Conselho Nacional do Desenvolvimento Científico e Tecnológico (CNPq) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação Araucária de Apoio ao Desenvolvimento Científico e Tecnológico do Paraná / Devido a preocupações com o meio ambiente e aos avanços tecnológicos na área química e florestal, alternativas tecnológicas são buscadas para o desenvolvimento de novos produtos. Os painéis de madeira colados lateralmente, EGP, possibilitam a otimização do uso de recursos florestais e são compostos por sarrafos de madeira unidos através de ligação adesiva nas laterais e de topos, sendo avaliados segundo a norma EN-13353. Esses painéis podem ser fabricados com adesivo poliacetato de vinila, PVAc e emulsão polimérica de isocianato, EPI, que são provenientes do petróleo. O adesivo de poliuretano derivado do óleo da mamona é uma alternativa para substituir estes adesivos, pois é um material que não possui solvente, é biodegradável e procedente de matéria-prima renovável. O objetivo deste trabalho foi avaliar o adesivo poliuretano que procede do óleo de mamona para a produção de painéis colados lateralmente. Foram utilizadas as espécies de Pinus taeda e Tectona grandis para a colagem com o adesivo de poliuretano e comparados com os adesivos PVAc e EPI, com prensagens em diferentes tempos, proporções de poliol e pré- polímero e diferentes gramaturas submetidas a condicionamentos de acordo com a norma EN-13353 para a avaliação da qualidade de colagem de painéis de madeira sólida. Todos os corpos de prova foram avaliados pelo ensaio de cisalhamento na linha de cola. Observou-se que o tempo mais indicado para a produção de EGP com o adesivo PU para a espécie Pinus taeda foi de 4 horas, com proporção de 1:0,7 e gramatura de 180 g/m² e para espécie Tectona grandis foi de 4 horas, com proporção de 1:0,7 e gramatura de 120 g/m², sendo que todos os valores atenderam à norma para painéis colados lateralmente EN-13353 e foram superiores aos valores obtidos com adesivos PVAc e EPI. / Due to concerns about the environment and technological advances in the chemical and forestry area, technological alternatives are sought for the development of new products. The Edge Glued Panels, EGP, enable the optimization of the use of forest resources and are composed of wood joints joined by adhesive bonding on the sides and tops and evaluated according to EN-13353.These panels can be manufactured with vinyl polyacetate adhesive, PVAc and emulsion polymer isocyanate, epoxy, which are derived from petroleum. The polyurethane adhesive derived from castor oil is an alternative to replace these adhesives, since it is a material that has no solvent, is biodegradable and derived from renewable raw material. The objective of this work was to evaluate the polyurethane adhesive derived from castor oil for the production of Edge Glued Panels. The Pinus taeda and Tectona grandis species were used for bonding with the polyurethane adhesive and compared with the PVAc and EPI adhesives, with pressings at different times, proportions of polyol and prepolymer and different weights subjected to conditioning according to standard EN-13353 for the evaluation of the bonding quality of solid wood panels. All the specimens were evaluated by the shear test on the glue line. It was observed that the time most suitable to produce EGP with the PU adhesive for Pinus taeda was 4 hours, with a ratio of 1: 0.7 and weight of 180 g / m² and for Tectona grandis species it was 4 hours, with a ratio of 1: 0.7 and 120 g / m², where all values met the standard for laterally bonded panels EN-13353, and were higher than the values obtained with PVAc and EPI adhesives.

O uso da Avaliação do Ciclo de Vida (ACV) permite identificar oportunidades de melhoria de desempenho ambiental, gerar aprendizagem sobre produtos e processos e apoiar decisões para alcançar vantagens competitivas. O processo de tomada de decisão baseado nos resultados da ACV envolve, além dos aspectos e impactos ambientais, outros critérios importantes para um processo decisório. Neste sentido, esta tese objetivou desenvolver um modelo multicritério para apoio à decisão baseado em avaliação de ciclo de vida e indicadores corporativos. O modelo desenvolvido possui caráter interativo, pode ser generalizado e foi validado utilizando dados de diferentes cenários do ciclo de vida da produção do painel MDF. O modelo avalia par a par as opções de cenários distintos e identifica a opção mais atrativa de acordo com um índice final. O índice final é composto por dimensões específicas, subdimensões e indicadores. A dimensão ambiental do modelo é baseada em ACV, a qual foi modelada no software Umberto e utilizou a base de dados Eco-Invent 2.2. Para a estrutura decisória do modelo e a construção de escalas cardinais foi utilizado o método MACBETH, através do software M-MACBETH. A validação do modelo ocorreu por meio da avaliação de três situações decisórias da produção do painel MDF (variações no processo produtivo, variações em parâmetros de processo e variações em espessura do produto). Os resultados apresentados contribuíram para avanços acadêmicos em construções de modelos de apoio à decisão baseados em ACV e multicritérios. Permitiram, ainda, interpretar e gerar aprendizados acerca do processo produtivo, do ciclo de vida do produto e da gestão da produção da indústria pesquisada. Neste sentido, concluiu-se que o modelo mostrou-se apto para apoiar e gerar aprendizagem em processos decisórios multicritérios baseados em ACV e em outros indicadores corporativos. / Life Cycle Assessment (LCA) allows identify opportunities to improve environmental performance, providing knowledge about products and processes and supporting decision-making in order to achieve advantages. Decision-making based on LCA results involves, in addition to the environmental aspects and impacts, others important criteria. In this sense, this thesis aimed to develop a multi-criteria model for decision-making based on life cycle assessment and corporate indicators. The model developed has interactive nature and can be generalized. The model was validated using data for different scenarios of MDF panel production life cycle. The pairwise model evaluates the options for different scenarios and identifies the most attractive option in accordance with a final index. The final index is composed of specific, sub-dimensions and indicators. The environmental dimension is based on an LCA, which was modeled in Umberto software and used Eco-Invent 2.2 as database. For the model structure and construction of cardinal scale was used MACBETH method using M-MACBETH software. The model validation was made by evaluation of three decision-making scenarios in MDF panel production (changes in production processes, changes in process parameters and changes in product thickness variations). The results allowed to reach academic advances in order to support decision models structures based on LCA and multi-criteria. The results allowed interpreting and generating knowledge about production process, product life cycle and industrial management. In this sense, it is concluded that the model is able to support and generate knowledge on decision-making processes based on LCA and other corporate indicators.