Microstructure And Texture Evolution And Its Effect On Mechanical Properties In Dilute Magnesium Based AZ21 AlloyAbdul Azeem, Mohd. January 2006 (has links)
Dilute Mg alloys are exclusively identified for wrought structural applications in automotive industry. Any improvement in mechanical properties of alloys is possible only by grain size refinement and by the development of suitable texture. The grain size, grain size anisotropy and texture in these alloys affect the compatibility stresses in a very complex manner. To launch a full scale study towards understanding the complex deformation mechanisms operating in these alloys, it is necessary to understand the effect of grain size and texture on the mechanical behavior of Mg alloys in a broad or semi-quantitative manner first. Current literature lacks such broad study. In this present study, the effect of grain size, grain size anisotropy and texture evolution on the mechanical properties are examined in order to develop an understanding of the deformation mechanism that control the mechanical properties of a dilute conventionally extruded Mg alloy, AZ21.
The approach adopted was to first study the microstructure and texture evolution in this conventionally extruded alloy. Since the grain sizes in these alloys vary over a wide range, it is hence necessary to study the microstructure evolution in a highly quantitative manner. In understanding texture, the present study is only limited to qualitatively evaluating the evolution of fibre component of texture using X-Ray Diffraction spectra.
For truly quantitative microstructure evolution results in materials were grains sizes are spread over a wide range, it is critical to study a statistically enough no. of grains. Hence to avoid any sampling error, large montages (about 0.3 sq. mm) were constructed out of a series of high resolution images captured using an optical microscope. The montages so constructed are subjected to extensive image enhancement and various other operations are performed to convert these coloured to binary montages. Information like grain size, diameter etc., can be easily extracted from these binary montages and used for further analysis.
Fibre texture in these conventionally extruded dilute Mg alloys generally develops due to alignment of basal planes along the direction of extrusion. The Critical Resolved Shear Stress for basal slip is very low when compared to that of non-basal planes. And also since there are very limited primary slip systems in these dilute Mg alloys, the development of strong fibre texture drastically changes the compatibility stresses and hence the mechanical properties .
To broadly study the effect of microstructure-texture on mechanical proerties, after post extrusion annealing, heat treatments representing typical microstructure-texture combinations were identified. Effect of each microstructure-texture combination on the tensile and completely reversed cyclic fatigue properties are studied and qualitatively interpreted.
The fibre texture showed pronounced effect on tensile ductility but it hardly affected the yield strength. With just 10% reduction in BPI, the ductility reduced by about 50%. A small change in average grain size did not alter the yield strength. Unlike tensile ductility, fatigue endurance stress was not altered drastically by the change in grain size or texture. But there appeared to be a significant effect of residual stress.
In ending, a small change in microstructure-texture combination in these conventionally extruded alloys has a pronounced effect on ductility or in other words plastic properties. But a it has minimal effect on yield strength and fatigue endurance stress.
|
2 |
Effect of Li Addition on the Plasticity of AZ31 Mg-AlloyGovind, * January 2014 (has links) (PDF)
Mg-alloys, despite being the lightest structural metallic materials, find limited applications due to their poor workability, which is due to the hcp structure that does not provide sufficient number of independent slip systems for compatible deformation. Workability improves with the increase in the deformation temperature, when non-basal slip starts playing a larger role in deformation. Efforts were made to improve the workability through control of texture, grain refinement and alloying. Alloying activates non-basal slip by decreasing the critical resolved shear stress (CRSS) on non-basal planes or by promoting cross slip through an increase in the stacking fault energy (SFE) on basal planes. In this thesis, the effect of Li addition to the most widely used wrought Mg-alloy AZ31 on its workability is examined. Plastic deformation behaviour of a series of AZ31-Li alloys with temperature, T, and strain rates, ε , as variables was studied, so as to identify the optimum Li content that results in highly workable alloy. The T and ε combinations that are best suited for hot deformation of these alloys were also identified through processing maps and microstructural analysis.
First, deformation behaviour of the base AZ31 is examined in detail. Compression tests were carried out, with T ranging between 150 and 400 °C and at ranging from 10-3 to 102 s-1, covering entire hot working range of the alloy. The results suggest that the deformation behaviour of AZ31 could be partitioned into three temperature regimes. In low T regime, twinning played an important role. It changes the orientation and increases hardening rate, θ (given by dσ/dε where σ and ε are true stress and strain respectively); material exhibits macroscopic flow localization and cracking along twin boundaries. The onset of twinning was examined in detail by examining the local maxima before ϵpeak strain in plot between d2σ/dε2 vs. ε. Twinning was found to occur at all the deformation conditions. Dynamic recrystallization (DRX) was observed at temperatures above 250 °C whereas deformation at low T (< 250 °C) led to extensive twinning at all . ε . At intermediate T of 250-300 °C, plastic strains tend to localize near grain/twin boundaries, confining DRX only to these regions. Increase in T promotes non-basal slip, which, in turn, leads to uniform deformation; DRX too becomes uniform. The dependence of critical stress (σc) for the onset of DRX and peak flow stress (σp) on Zener-Hollomon parameter (Z) indicates that these stresses increase with Z. Activation energy (Q) for the deformation of AZ31 was estimated at peak stress and steady state conditions. High values of Q (150-200 kJ/mol) indicate cross slip as the rate controlling mechanism, at the peak, in the stress-strain responses. For steady state, Q corresponds to lattice/grain boundary diffusion (90-150 kJ/mol).
Next, the effect of Li on deformation behaviour of AZ31 was examined. In addition to AZ31 without any Li (0Li), three alloys 1 (1Li), 3 (3Li) and 5 (5Li) wt% Li were prepared with the aid of a specially designed set-up for melting and casting of Li containing alloys. Experimental results on homogenized alloys show that 1Li alloy’s overall response is similar to that of 0Li alloy, but 3Li and 5Li alloys exhibit distinctly different deformation behaviour. Li addition facilitates cross slip by increasing SFE on basal planes, thus leading to change in the deformation mechanism of the alloy. Increased softening due to cross slip decreases θ and also the twin density at low ϵ (<10-2 s-1). During deformation at low ϵ and low T, high Li alloys reveal cavities along the grain boundaries in contrast to cracking along twin boundaries that was observed in AZ31. In the intermediate T range, high Li alloys reveal the presence of a small mantle, which can be attributed to the increased cross slip with increasing Li. In fact, Li addition was found to restrict DRX and promote dynamic recovery (DRY). As ϵ increases in this T regime deformation becomes more homogeneous and twinning occurs extensively in high Li alloys. This results in remarkable increase in dσ/dε (θ) in these alloys and DRX was predominantly seen at twinned regions. At high ϵ -T regime, where non-basal slip and twinning occur uniformly, DRX is observed throughout the samples. On the basis of d2σ/dε2 – ε plots, it was found that twinning occurs at almost all -T combinations examined in present study for 0Li and 1Li alloys. In high Li alloys, twinning activity was found to be insignificant at low ε , resulting in low twin density than low Li alloys. Twinning occurs at very early stages of deformation. In the low T and high ε regime, extensive twinning in high Li alloys is noted. In high T regime, presence of twins was not prominent due to the preferential occurrence of DRX at twin boundaries. Estimated values of Q in high Li alloys were found to be very low and correspond to lattice/grain boundary diffusion of Li in Mg, indicating that cross slip is no longer the rate controlling mechanism. Instead, unpinning of kinks from Li atoms appears to control the deformation. Cross slip is promoted by Li through increase in SFE at basal planes. Onset of the DRX was predicted and it was observed that high Li alloys posses lower σc at low ε , but at high ε , σc was either comparable to or higher than low Li alloys.
Processing maps were generated for all the alloys using Prasad's as well as Murty's models. Instability predictions of Prasad’s and Murty’s models are similar, except that isoefficiency contours in the latter are slightly shifted to higher ε . These maps indicate to an increase in the workability with the addition of Li to AZ31. Instability predicted by processing maps in the low ε regime in high Li alloys is attributed to underestimation of stress values due to spline interpolation. High sensitivity observed for high Li alloy at intermediate ε (10-1 – 100 s-1) is attributed to the change in the deformation mode i.e. from slip to twinning. Deformation at high T leads to dissolution of Li containing precipitates, which in turn increases the solid solution strengthening in the alloy. Hence, increase in flow stress is observed with increase in T in high Li alloys. This structural change too causes instability predictions in the high -T regime. The 0 Li alloy exhibits peak efficiency of 45% in T = 250-400 °C and ε = 10-1.25 - 100.25 s-1 regime. DRX is observed in this regime and optimum conditions for deformation predicted for this alloys are T = 350 °C and ε = 10-1 s-1. These alloys can be worked at low ε regime too (T = 250-400 °C and ε = 10-2.5 – 10-1 s-1) where the softening mechanism is DRY. Accordingly, it is concluded that the intrinsic workability of AZ31Mg-alloy increases with the addition of 3% and 5% Li.
|
3 |
Evolution of Microstructure and Texture during Severe Plastic Deformation of a Magnesium-Cerium AlloySabat, Rama Krushna January 2014 (has links) (PDF)
Magnesium alloys have poor formability at room temperature, due to a limited number of slip systems owing to the hexagonal closed packed structure of magnesium. One possibility to increase the formability of magnesium alloys is to refine the grain size. A fine grain magnesium alloy shows high strength and high ductility at room temperature, hence an improved formability. In addition to grain refinement, the formability of Mg alloys can be improved by controlling crystallographic texture. Severe plastic deformation (SPD) processes namely, equal channel angular pressing (ECAP) and multi-axial forging (MAF) have led to improvement in room temperature mechanical property of magnesium alloys. Further, it has been reported that by adding rare earth elements, room temperature ductility is enhanced to nearly 30%. The increase in property is attributed to crystallographic texture. Many rare earth elements have been added to magnesium alloys and new alloy systems have been developed. Amongst these elements, Ce addition has been shown to enhance the tensile ductility in rolled sheets at room temperature by causing homogeneous deformation. It has been observed that processing of rare-earth containing alloys below 300°C is difficult. Processing at higher temperatures leads to grain growth which ultimately leads to low strength at room temperature. The present thesis is an attempt to combine the effect SPD and rare earth addition, and to examine the overall effect on microstructure and texture, hence on room temperature mechanical properties. In this thesis, Mg-0.2%Ce alloy has been studied with regard to the two SPD processes, namely, ECAP and MAF. The thesis has been divided into six chapters. Chapter 1 is dedicated to introduction and literature review pertaining to different severe plastic deformation processes as applied to different Mg alloys. Chapter 2 includes the details of experimental techniques and characterization procedures, which are commonly employed for the entire work.
Chapter 3 addresses the effect of ECAP on the evolution of texture and microstructure in Mg-0.2%Ce alloy. ECAP has been carried out on two different initial microstructure and texture in the starting condition, namely forged and extruded. ECAP has been successfully carried out for the forged billets at 250°C while cracks get developed in the extruded billet when ECAP was done at 250°C. The difference in the deformation behaviour of the two alloys has been explained on the basis of the crystallographic texture of the initial materials. The microstructure of the ECAP materials indicates the occurrence of recrystallization. The recrystallization mechanism is identified as “continuous dynamic recovery and recrystallization” (CDRR) and is characterized by a rotation of the deformed grains by ~30⁰ along c-axis. The yield strengths and ductility of the two ECAP materials have been found quite close. However, there is a difference in the yield strength as well as ductility values when the materials were tested under compression. The extruded billet has the tension compression asymmetry ~1.7 while the forged material has the asymmetry as ~2.2. After ECAP, the yield asymmetry reduces to ~1 for initially extruded billet, while for the initially forged billet the yield asymmetry value reduces to ~1.9.
In chapter 4, the evolution of microstructure and texture was examined using another severe plastic deformation technique, namely multi axial forging (MAF). In this process, the material was plastically deformed by plane strain compression subsequently along all three axes. In this case also two different initial microstructures and texture were studied, namely the material in as cast condition and the extruded material. The choice of initial materials in this case was done in order to examine the effect of different initial grain size in addition to different textures. By this method, the alloy Mg-0.2%Ce could be deformed without fracture at a minimum temperature of 350⁰C leading to fine grain size (~3.5 µm) and a weak texture. Grain
refinement was more in the initial cast billets compared to the initial extruded billet after processing. The mechanism of grain refinement has been identified as twin assisted dynamic recrystallization (TDRX) and CDRR type. The mechanical properties under tension as well as under compression were also evaluated in the present case. The initially extruded billet has shown low tension compression asymmetry (~1.2) than cast billet (~1.9), after MAF. Chapter 5 addresses the exclusive effect of texture on room temperature tensile properties of the alloy. Different textures were the outcomes of ECAP and MAF processes. In this case, in order to obtain an exact role of texture, a third of deformation mode, rolling, was also introduced. All the processed materials were annealed to obtain similar grain size but different texture. A similar strength and ductility for ECAP and MAF, where the textures were qualitatively very different, was attributed to the fact that texture of both the ECAP and MAF processed materials, was away from the ideal end orientation for tensile tests. In chapter 7, the final outcomes of the thesis have been summarized and scope for the future work has been presented.
|