This study was undertaken to prepare polystyrene (PS)/montmorillonite (MMT) nanocomposites by different methods, including melt intercalation, in-situ polymerization and masterbatch methods. The in-situ polymerization method consisted of dispersing the styrene monomer into the galleries of MMT followed by subsequent polymerization. The PS/MMT nanocomposites formed by melt intercalation method were prepared on a twin-screw extruder. The masterbatch method was in fact a two-step process. As the first step, a high clay content composite of polystyrene (masterbatch) was prepared by in-situ polymerization, and then the prepared masterbatch was diluted to desired compositions with commercial polystyrene in a twin-screw extruder.The structural, thermal and mechanical properties of the nanocomposites were examined. X-Ray diffraction (XRD) analysis showed that the d-spacing of the in-situ formed nanocomposites containing 0.73 and 1.6 wt. %organoclay increased from 32.9 &amp / #506 / to 36.3 and 36.8 &amp / #506 / respectively, indicating intercalation while the dspacing of the other prepared materials remained nearly unchanged compared to pure organoclay. At low clay content, (&lt / 1 wt.%), in-situ formed nanocomposites showed the best improvement in mechanical properties including tensile, flexural, impact strength and Young&rsquo / s modulus. In all the three methods, the addition of organoclay increased the Young&rsquo / s modulus compared to neat resin, but the maximum improvement was 88.5 %, obtained at 0.73 wt. % organoclay in the in-situ formed material. In-situ polymerization method did not prove to be efficient at high clay loadings in terms of mechanical properties. At high clay loadings, the effects of the three methods on promoting mechanical properties were not significantly different from each other. The glass transition temperature increased from 105.5 oC in the pure polystyrene to 108.4 oC in the in-situ formed nanocomposite at 0.73 wt % organoclay due to the restricted mobility of the polymer chains within the organoclay layers.

The master's thesis deals with risk prevention in the production of masterbatches in company Lifocolor, s.r.o. The theoretical part is focused on the overall risk management process, specifying individual methods of risk analysis. The following section pertains masterbatch production process. Analysis of history of disagreeable products, application of methods described in theoretical parts, their evaluation and design of corrective precautions are described in the practical part.

El presente y el futuro de la industria textil están íntimamente ligados al concepto de textil técnico, artículos éstos concebidos para su aplicación en diferentes segmentos de mercado: salud y ámbito hospitalario, industria naval, aeronáutica y de automoción, sector de construcción e ingeniería civil, defensa e industria militar, etc. En el presente proyecto de investigación se ha contemplado la funcionalización de fibras de polipropileno mediante la aditivación de nanopartículas de plata. De esta forma, se persigue la funcionalización de este material textil con el objetivo de que estas fibras exhiban propiedades antibacterianas y antifúngicas intrínsecas, aumentando así sus posibilidades de aplicación en el campo de textiles de uso médico. El desarrollo de hilos de polipropileno aditivados con nanopartículas de plata ha requerido de un proceso previo de aditivación de la granza polimérica mediante la utilización de un sistema de extrusión de doble husillo co-rotante. Se ha evaluado la influencia de la velocidad de extrusión, de la concentración de nanoplata y de la naturaleza y concentración de diferentes agentes compatibilizantes sobre la homogeneidad de la mezcla polímero-nanopartícula. Se ha optimizado la mezcla polipropileno-nanoplata con vistas a su aplicación en el proceso de hilatura por fusión de hilos multifilamento. Se ha estudiado la influencia de la relación de estirado y de la concentración de nanopartículas de plata en las propiedades térmicas, mecánicas y bioactivas de los hilos funcionales desarrollados. Los hilos multifilamento objeto de estudio presentan configuración monocomponente y bicomponente con sección corteza-núcleo. En el estudio del grado de dispersión de las nanopartículas de plata en la matriz de polipropileno se ha hecho uso de los siguientes técnicas analíticas: difracción de rayos X (XRD), microscopía electrónica de barrido (SEM) y microscopía electrónica de transmisión (TEM). Igualmente, se ha caracterizado la estabilidad térmica / Fages Santana, E. (2012). INVESTIGACIÓN DE FIBRAS DE POLIPROPILENO ADITIVADAS CON NANOPARTÍCULAS DE PLATA PARA LA MEJORA DE PROPIEDADES BIOACTIVAS EN EL SECTOR TEXTIL [Tesis doctoral no publicada]. Universitat Politècnica de València. https://doi.org/10.4995/Thesis/10251/21065 / Palancia