Orientador: Renato Sussumu Nishioka / Banca: Leonardo Buso / Banca: José Henrique Rubo / Resumo: Este trabalho avaliou a influência do tratamento superficial do metal (jateamento com óxido de alumínio e ponta de tungstênio), na resistência ao cisalhamento, entre uma liga de Co-Cr (StarLoy C - DeguDent) e duas cerâmicas (StarLight Ceram - DegunDent e Duceram Kiss - Degudent). Foram confeccionados quarenta e oito padrões metálicos de formato cilíndrico, com altura total de 4,7 mm, tendo diâmetro diferenciado entre as extremidades; a maior com 5 mm e a menor com 3,7 mm (ISO 11405), sendo doze para cada grupo: G1- superfície metálica jateada com óxido de alumínio + StarLight Ceram; G2- superfície metálica tratada com ponta de tungstênio + StarLight Ceram; G3- superfície metálica jateada com óxido de alumínio + Duceram Kiss e G4- superfície metálica tratada com ponta de tungstênio + Duceram Kiss. O ensaio de cisalhamento foi realizado em máquina de ensaio universal (Emic DL 1000, São José dos Pinhais, Brasil), com célula de carga de 100 Kg, à velocidade de 0,5 mm/min, utilizando um dispositivo específico (faca com entalhe). Após o ensaio, foi realizada a análise fractográfia e os dados obtidos analisados estatisticamente pelo teste ANOVA (2 fatores). Foram observados os seguintes valores médios de resistência de união: G1 (57,97l11,34 MPa); G2 (40,62l12,96 MPa); G3 (47,09l13,19 MPa) e G4 (36,80l8,86 MPa). Concluiu-se que o tratamento superficial com óxido de alumínio, aumentou a resistência de união entre metal e cerâmica, independente do tipo de cerâmica utilizada. / Abstract: The aim of this study was to evaluate the influence of the surface treatment (sandblasting with aluminium oxide and tungsten carbide bur), on the shear bond strength among a Co-Cr alloy (StarLoy C - DeguDent) and two ceramics (StarLight Ceram - DeguDent and Duceram Kiss - Degudent). Forty eigth metal cilindric specimens were made with 4,7 mm high, with two different diameters: one with 5,5 mm and the other with 3,7 mm (ISO 11405), with twelve specimens for each one of the four groups: G1 - sandblasting + StarLigth Ceram; G2 - tungsten carbide burs + StarLigth Ceram; G3 - sandblasting + Duceram Kiss and G4 - tungsten carbide burs + Duceram Kiss. The shear test was made with a universal testing machine (Emic DL 1000, São José dos Pinhais, Brazil), with load of 100 kg, with the crosshead speed of 0,5 mm/min, using a specific device (knife with an indent - Ultradent). The fracture analysis of the surfaces was made and the data were statistically analyzed with the ANOVA (two way). The means and the standard deviations of the shear bond strength were: G1 (57,97l11,34 MPa); G2 (40,62l12,9 MPa); G3 (47,09l13,19 MPa) e G4 (36,80l8,86 MPa). It could be concluded that the surface treatment with the tungsten carbide bur reduced the shear bond strength, independent of the ceramics used. / Mestre

Orientador: Mário Tanomaru Filho / Banca: Fábio Luis Camargo Villela Berbert / Banca: José Mauricio dos Santos Nunes Reis / Banca: Marco Antonio Hungaro Duarte / Banca: Edson Alfredo / Resumo: O presente estudo avaliou a resistência e tipo de falha de união de materiais retrobturadores à parede do canal radicular por meio do teste push-out. Capítulo 1 - Foi realizada comparação da resistência de união por compressão (push-out) e tipo de falha dos materiais retrobturadores MTA Angelus, MTA Sealer, Sealer 26 e OZE. Foram utilizadas 40 fatias de 2 mm de espessura de dentes unirradiculados humanos. Após preparo inicial do canal radicular com broca cilíndrica com 1,5 mm de diâmetro, o preparo retrógrado foi confeccionado com ponta de ultrassom CVD T0F-2. Os corpos-de-prova foram divididos aleatoriamente em 4 grupos (n=10) de acordo com o material retrobturador: Grupo 1: MTA Angelus; grupo 2: MTA Sealer; grupo 3: Sealer 26; grupo 4: OZE. Para o teste, cada espécime foi posicionado na máquina de ensaios mecânicos (EMIC DL 2000) com velocidade de 1mm/min e célula de carga de 5kN, para a realização do teste de push-out. Também foi avaliada a presença dos cimentos nas paredes radiculares por meio do microscópio confocal de varredura a laser, e análise do tipo de falha em estereomicroscópio. Os dados foram submetidos ao teste estatístico de ANOVA e Tukey, com nível de significância de 5%. Os resultados de push-out mostraram maior adesão para MTA Angelus (19,18 MPa) e MTA Sealer (19,13 MPa), seguidos do Sealer 26 (15,91 MPa). O cimento OZE (9,50 MPa) apresentou menor adesão que os demais cimentos estudados, com diferença estatisticamente significante (p<0,05). Em relação a presença de cimento, o cimento OZE (89,77%) e o MTA Sealer (83,06%) apresentaram os maiores valores, seguidos pelo Sealer 26 (59,33%), sem diferença significante entre os materiais (p>0.05). Em relação ao tipo de falha, predominou a falha adesiva, com exceção do grupo 4 (OZE), onde predominou a falha mista. Conclui-se que os materiais... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of study was to evaluate the bond strength and failure type to root-end filling materials wall by means of push-out test. Chapter 1 - the aim of this study was to evaluate the bond strength and failure type of root-end filling materials MTA Angelus, MTA Sealer, Sealer 26 and OZE. 40 slices were used 2 mm thick of human teeth. After initial root canal preparation with cylindrical drill with 1.5 mm in diameter, the root-end preparation was made with ultrasound tip CVD T0F-2. The specimens were randomly divided into 4 groups (n=10) according to the root-end filling materials: Group 1: MTA Angelus; Group 2: MTA Sealer; Group 3: Sealer 26; Group 4: OZE. For the test, each specimen was positioned in the mechanical testing machine (EMIC DL 2000) with 1mm/min speed and load cell of 5KN to the completion of the push-out test. It was also evaluated the presence of cement through the confocal scanning laser microscope and analysis of failure type in stereomicroscope. The data were submitted to ANOVA and Tukey test statistic with significance level of 5%. The results of push-out showed greater bond strength to MTA Angelus (19,18 MPa) and MTA Sealer (19,13 Mpa), followed the Sealer 26 (15,91 Mpa). OZE (9.50 Mpa) showed lower accession than other materials, with statistically significant (p 0.05). In relation to presence of cement, the OZE (89.77%) and the MTA Sealer (83.06%) showed the greatest values, followed by Sealer 26 (59.33%), no significant difference between the materials (p> 0.05). In relation to the type of failure, predominated the adhesive failed, with the exception of Group 4 (OZE), which predominated the coesive failure. It is concluded that the MTA Angelus, MTA Sealer and Sealer 26 exhibit bond strength as root-end filling materials. Chapter 2 - the aim of this study was to evaluate... (Complete abstract click electronic access below) / Doutor

Orientador: Carlos Rocha Gomes Torres / Banca: Alessandra Bühler Borges / Banca: Ricardo Amore / Resumo: O objetivo deste estudo foi avaliar a influência do tipo de resina composta com relação à viscosidade, do tipo de adesivo autocondicionante e seu modo de presa e do envelhecimento artificial, na formação de fendas marginais e microinfiltração de restaurações de resina composta. Cavidades padronizadas com 4 mm de diâmetro e 2,5 mm de profundidade foram preparadas em 240 incisivos bovinos. Eles foram divididos em 2 grupos de acordo com a viscosidade da resina composta: GC - Grandio SO (Voco - viscosidade convencional) e GF - Grandio SO Heavy Flow (Voco - baixa viscosidade), ambas com alto conteúdo de carga. Cada grupo foi dividido em seis subgrupos, de acordo com os sistemas adesivos utilizados: FM - Futura Bond M (Voco), FDCF - Futura Bond DC (Voco) - fotopolimerizado, FDCQ - Futura Bond DC (Voco) - apenas polimerização química, CS - Clearfil S3 Bond (Kuraray), CDCF - Cleafil DC (Kuraray) - fotopolimerizado e CDCQ - Clearfil DC (Kuraray) - apenas polimerização química. Metade dos espécimes foi submetida à ciclagem mecânica (300.000 ciclos) e térmica (1.000 ciclos), sendo divididos então em C - ciclados e NC - não ciclados. A maior fenda marginal presente nas margens de cada restauração foi medida em microscópio óptico, em micrometros. Para a avaliação da microinfiltração, os espécimes foram submersos em solução de nitrato de prata amoniacal 50% por 24h, lavados, colocados em revelador radiográfico por 8h sob luz fluorescente e seccionados. As interfaces foram fotografadas e a microinfiltração mensurada em milímetros. Os dados foram submetidos à ANOVA três fatores. Para fenda marginal foi encontrada diferença significativa para todos os fatores (p=0,00). Os resultados de Tukey para resina foram... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to evaluate the influence of composite viscosity, adhesive systems type of cure and artificial aging on marginal gap formation and microleakage of composite resin restorations. Cavities with 4mm in diameter and 2,5mm deep were prepared in 240 bovine incisors. Teeth were divided in two groups according to the viscosity of composite resin: GC - Grandio SO (Voco - conventional viscosity), GF - Grandio SO Heavy Flow (Voco - low viscosity), both with higher filler content. Each group was divided into 6 subgroups, according to the bonding systems: FM - Futura Bond M (Voco), FDCF - Futura Bond DC (Voco) - light cured, FDCQ - Futura Bond DC (Voco) - chemical cured only, CS - Clearfil S3 Bond (Kuraray), CDCF - Cleafil DC (Kuraray) - light cured and CDCQ - Clearfil DC (Kuraray) - chemical cured only. Half of the specimens were subjected to mechanical (300.000) and thermal cycling (1.000). So specimens were then divided into WITH and WITHOUT thermo-mechanical cycling. The biggest marginal gap for each restoration was measured in an optical microscope in microns. For microleakage evaluation, specimens were submersed in 50% ammoniacal silver nitrate for 24h, washed for 20min and placed in radiographic developer for 8h under fluorescent light. Teeth were sectioned and the interface with the deepest microleakage in millimeters was measured. Data were analyzed with three-way ANOVA and Tukey's test. For marginal gaps significant differences were shown for all factors (p=0.000). Tukey's test results for resin were GC: 28.10a e GF: 40.60b; for adhesive CDCQ: 28.67a, CDCF: 32.25b, CS: 34.12bc, FDCF: 36.10cd, FM: 36.50cd e FDCQ: 38.46d; and for artificial aging WITHOUT: 29.05a and WITH: 39.65b. For microleakage, there were also differences for all factors (p=0.000). The results of Tukey's test... (Complete abstract click electronic access below) / Mestre

Made available in DSpace on 2011-12-27T14:14:11Z (GMT). No. of bitstreams: 2 000386496-0.pdf: 391577 bytes, checksum: 23af4cf9ce3630d39442fc9f6ba06efb (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This study evaluated, in vivo, the accuracy of mettalic (Smart) and plastic (Triple Tray) dual-arch trays employed with vinyl polyxiloxane (Flexitime), in the putty/wash consistency, as well as polyether (Impregum Soft), in the regular consistency. In one patient, a transferent was parafusado on implant in the mandibular right first molar. The tranferent served as a master model. Ten impression with each tray and impression material were made. The impressions were cast in type IV die stone after 1 hour. The width and height of the master model and gypsum models were measured in a perfil projector (Nikon). The results were submitted to Student’s t-test for one sample (α=0. 05). For the width distance, the plastic dual-arch trays with vunyl polyxiloxane (4. 513 mm) and with polyether (4. 531 mm), and metallic dual-arch tray with polyether (4. 500 mm) were statistically greater than the master model (4. 489 mm). The metallic dual-arch tray with vinyl polyxiloxane (4,504 mm) did not differed statistically from the master model. For the height distance, only the metallic dual-arch tray with polyether (2. 253 mm) differed statistically from the master model (2. 310 mm). The dual-arch metallic tray with vinyl polyxiloxane reproduced models with less distortion. / Este estudo avaliou, in vivo, a fidelidade de reprodução das moldeiras de dupla arcada metálica (Smart) e plástica (Triple Tray) com os materiais de impressão silicone por adição (Flexitime), nas consistências massa e leve, e o poliéter (Impregum Soft) na consistência regular. Em um paciente com implante na região do dente 46 foi parafusado um transferente modificado, servindo este de padrão. Foram realizadas dez impressões com cada associação moldeira / material. Os moldes foram vazados com gesso tipo IV após 1 hora. As medidas de largura e altura foram realizadas no padrão e nos modelos, em um projetor de perfil (Nikon). Os resultados foram analisados pelo teste t-student para uma amostra (α=0,05). Para a medida da largura, as moldeiras plásticas com silicone por adição (4,513 mm) e com poliéter (4,531 mm), e a moldeira metálica com poliéter (4,500 mm) foram estatisticamente superiores ao padrão (4,489 mm), sendo que a moldeira metálica com silicone por adição (4,504 mm) não diferiu estatisticamente do padrão. Para a altura, somente a moldeira metálica com poliéter (2,253 mm) diferiu estatisticamente do modelo mestre (2,310 mm). A moldeira de dupla arcada metálica associada ao silicone por adição foi a que reproduziu modelos com menor distorção.

Made available in DSpace on 2011-12-27T14:14:11Z (GMT). No. of bitstreams: 2 000425717-0.pdf: 985525 bytes, checksum: 1409745d664f74c4d1969f3e154f3926 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The elastic chains are used extensively in orthodontics treatments because they are comfortable to the patient, easy to use, hygienic and low cost. However, when stretched in the oral environment, due to the absorption of water and temperature changes, the elastic chains undergo a permanent deformation and degradation of the initial force. The technology employed by the elastic chain manufacturer and the material used defines how fast and how much the force degradation of this material occurs when in oral environment. To evaluate the force degradation in elastic chain from six different commercial brands, the elastic elements were stretched upon jigs fixed to the brackets of 20 patients under orthodontic treatment. The elastic chains stayed with an initial force of 150 grammas during 3 weeks and the force displayed by the chains measured in the first 24 hours, one week and 3 weeks. All samples suffered relaxation of the initial force. In the first 24 hours, the degradation measured was from 5. 5% to 37. 66%. In one week, from 8. 16% to 44. 5% and in three weeks, from 12. 33 to 47. 33%. In the end of the evaluation, all the elastic chains presented necessary forces to move teeth. / As cadeias elásticas são amplamente utilizadas pelos ortodontistas devido à sua facilidade de uso, ao conforto ao paciente, à praticidade na higienização e ao baixo custo. No entanto, por causa da absorção de líquidos e de outros fatores, como mudanças na temperatura, elas sofrem deformação permanente e degradação das forças geradas inicialmente. As tecnologias empregadas para a fabricação das cadeias elásticas e os materiais utilizados definem a velocidade e a quantidade de degradação de força que estes materiais irão sofrer quando distendidos em meio bucal. A fim de avaliar a degradação de força de cadeias elásticas de seis fabricantes, foi colocado um dispositivo preso ao aparelho fixo de 20 pacientes em tratamento ortodôntico, onde segmentos, com quatro elos cada, destas cadeias elásticas ficaram distendidos com uma força inicial de 150 gramas pelo período de 3 semanas. Mediu-se a força alcançada pelas cadeias no intervalo de 24 horas, uma semana e três semanas. Todas as marcas comerciais avaliadas sofreram degradação de força estatisticamente significante já na primeira medição, que variou de 5,5% a 37,66%. No final da primeira semana, a variação foi de 8,16% a 44,5% e, no final das três semanas, de 12,33% a 47,33%. Ao término do experimento, todos apresentavam forças suficientes para a movimentação dentária.

Made available in DSpace on 2011-12-27T14:14:22Z (GMT). No. of bitstreams: 2 000387549-0.pdf: 9945748 bytes, checksum: 2dfadcd5259cb6d75417400392f79458 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The purpose of this study was evaluate selected mechanical properties (compressive strength, diametral tensile strength, flexural strength e flexural moduli) of four differents nanofilled composite and a microhybrid composite, in dentin e enamel A2 shades. Were maded ten samples for each group of each test. The flexural moduli was calculated by the results of the flexural strength`s test. The results were compared statistically with ANOVA e Tukey (p<0,01). There was no statistical difference for compressive strength, with values that range into 141. 04 MPa for 4 Seasons A2E and 206. 08 MPa Grandio A2O. For flexural strength, there was statistical difference for the tested groups, and the values range into 59. 16 MPa for 4 Seasons A2E and 122 MPa for Supreme XT A2E. There was statistical difference for flexural moduli and in this test the values range between 3. 4 GPa for 4 Seasons A2E and 13. 30 GPa for Grandio A2O. For diametral tensile strength, Esthet-X A2O showed value (34. 87 MPa) statiscally lower than the others groups, and Supreme XT A2E (50. 26 MPa), statiscally higher than the others tested groups; between the others groups there was no statistical difference. Even with differences for the values between the tested groups for flexural strength, flexural moduli and diametral tensile strength, the nanofiller composites, based in the results of this study, present mechanical properties similar from microhibrid resin. / Este estudo teve como objetivo avaliar as propriedades mecânicas selecionadas (resistência à compressão, resistência à tração diametral, resistência flexural de trêspontos e módulo flexural) de quatro marcas diferentes de resina composta nanoparticuladas e uma resina composta microhíbrida, nas cores A2 esmalte e dentina. Foram confeccionadas dez amostras para cada grupo de cada teste. O módulo flexural foi calculado a partir dos resultados do teste de resistência flexural. Os resultados obtidos nos ensaios foram comparados estatisticamente com análise de variância e teste de Tukey (p < 0,01). Não houve diferença estatisticamente significante para os grupos testados no teste de resistência à compressão, sendo que as médias variaram entre 141,04 MPa para a resina 4 Seasons A2E e 206,08 MPa para a resina Grandio A2O. No teste de resistência flexural, houve diferença estatisticamente significativa entre os grupos, onde as medias variaram entre 59,16 MPa para a resina 4 Seasons A2E e 122 MPa para a resina Supreme XT A2E. Houve diferença estatisticamente significante para módulo flexural e neste teste as médias variaram entre 3,4 GPa para a resina 4 Seasons A2E e 13,30 GPa para a resina Grandio A2O. No teste de resistência à tração diametral, a resina Esthet-X A2O apresentou média (34,87 MPa) estatisticamente menor que os demais grupos, e a resina Supreme XT A2E (50,26 MPa), estatisticamente maior que os demais grupos testados; entre os demais grupos não houve diferença estatisticamente significante. Apesar de diferenças nos valores entre os grupos testados nos testes de resistência flexural, módulo flexural e resistência à tração diametral, as resinas nanoparticuladas, baseados nos resultados obtidos neste estudo, apresentam propriedades mecânicas semelhantes da resina microhíbrida.

Made available in DSpace on 2011-12-27T14:14:26Z (GMT). No. of bitstreams: 2 000402872-0.pdf: 99141 bytes, checksum: 5dc4125b2c78cb76226d6ed213f92959 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This study aimed to evaluate the toxicity of silver solder used in Orthodontics through an “in vitro” cytotoxicity test as well as to determine the “in situ” concentration of component ions of the silver solder released in human saliva. The cytotoxicity assay was performed by fibroblast culture, line NIH/3T3, being divided in 4 groups (n=10, each): control, negative control (stainless steel wire), positive control (amalgam discs) and silver solder. After the cell culture in complete D-MEM and obtained a confluence of 80% the suspension was added on the plaques of 24 wells with the samples and incubated at 37° C for 24 hours. The plaques were then evaluated in an inverted optical microscope and micrographs were taken. Results were recorded in answer indexes according to modifications in the Stanford parameters (1980), based on the size of the diffusion halo of the toxic substance and amount of cell lysis. The results showed a maximum rate response to the silver solder group, as well as severe inhibition of the proliferation and cell growth, more circular cells and, most of them having with a darkened and granular aspect, suggesting lysis with cell death, results comparable to the positive control. In the “in situ” study the sample consisted of 60 subjects, aged from 8 to 14 years, divided in 2 groups (n=30, each): control and test (patients requiring the use of Hyrax appliances). To analyze the release of metallic ions, saliva samples were collected from each patient at 6 different moments for both groups: initial, 10 minutes, 24 hours, 7, 30 and 60 days after the insertion of the Hyrax appliance. Saliva was examined through Atomic Absorption Spectrophotometry with Graphite Furnace as to the presence of ions cadmium, copper, zinc and silver. The non-parametric Friedman and Mann-Whitney tests were used for the statistical analysis (p<0. 05). In the control group the ionic concentrations showed low values for cadmium, copper and zinc (p>0. 05), while the silver ion wasn’t detected. As for the test group, all subjects showed significant concentrations at 10 minutes post- insertion of the appliance (p<0. 01), higher averages for copper were detected, tending to reduce after 24 hours. The comparison between the groups showed significant differences for copper (all moments), zinc (10 minutes, 24 hours, 7days and 30 days) and for cadmium, only for 10 minutes. It was concluded that the silver solder was a material of high cytotoxicity to the studied cells. The differences in ionic concentrations in the groups and between them showed clearly the influence of individual physiological and metabolic characteristics of the human oral cavity on the alloys used in orthodontic appliances and corrosive process; as well as there was great release of ions with high concentrations immediately after the appliance insertion, representing risk of absorption and retention of these ions by the human body despite the decline in concentrations during the period studied. / Propôs-se neste trabalho avaliar a toxicidade da solda de prata utilizada em Ortodontia por meio do teste de citotoxicidade "in vitro", bem como pela determinação "in situ" da concentração dos íons componentes da solda de prata, liberados na saliva humana. O ensaio de citotoxicidade foi por meio de cultura de fibroblastos, linhagem NIH/3T3, sendo montados 4 grupos (n=10, cada): controle, controle negativo (fio de aço inoxidável), controle positivo (discos de amálgama) e (solda de prata). Após o cultivo das células em meio D-MEM completo e obtida confluência de 80%, a suspensão foi adicionada sobre as placas de 24 poços, contendo os corpos de prova, sendo incubados em estufa a 37ºC, por 24 horas. Após esse período, as placas foram avaliadas em microscópio óptico invertido, fotomicrografadas e os resultados registrados em índices de resposta, a partir de modificações nos parâmetros de Stanford (1980), baseados no tamanho do halo de difusão da substância tóxica e quantidade de lise das células. Os resultados mostraram índice de resposta máximo para o grupo da solda de prata, bem como severa inibição da proliferação e crescimento celular, células mais circulares e, em grande parte, com aspecto escurecido e granular, sugerindo lise com morte celular, resultados comparáveis ao controle positivo. No estudo "in situ", a amostra foi composta por 60 indivíduos entre 8 e 14 anos, divididos em 2 grupos (n=30, cada): controle e teste (necessidade de uso do aparelho de Hyrax).Para análise da liberação dos íons metálicos, foram coletadas amostras da saliva de cada paciente, em 6 tempos, para ambos os grupos: inicial, 10 minutos, 24 horas, 7, 30 e 60 dias pós-instalação do aparelho. A avaliação da saliva foi realizada por meio de Espectrofotometria de Absorção Atômica com Forno de Grafite, determinando-se a concentração dos íons cádmio, cobre, zinco e prata. Para análise estatística, foram utilizados os testes não-paramétricos de Friedman e Mann-Whitney, com p<0,05. As concentrações iônicas, no grupo controle, mostraram valores baixos para o cádmio, cobre, zinco (p>0,05) e, principalmente para a prata, onde não atingiram limite de detecção. No grupo teste, todos os íons mostraram concentrações expressivas aos 10 minutos pós- instalação do aparelho (p<0,01), maiores médias para o cobre, com tendência à redução após 24 horas. A comparação entre os grupos mostrou diferenças significativas para o cobre (todos os tempos), zinco (10 minutos, 24 horas, 7 e 30 dias) e, para o cádmio, apenas aos 10 minutos. Concluiu-se que a solda de prata representa um material de alta toxicidade para as células estudadas; as diferenças nas concentrações iônicas intragrupos e intergrupos mostraram, nitidamente, a influência das características fisiológicas e metabólicas individuais da cavidade oral humana sobre as ligas utilizadas nos aparelhos ortodônticos e processo corrosivo desencadeado, assim como foi perceptível a grande liberação dos íons, com concentrações elevadas imediatamente após a instalação do aparelho, representando risco de absorção e retenção desses íons pelo organismo humano, apesar da regressão nas concentrações, ainda no período estudado.

Tese (doutorado)-Universidade de Brasília, Faculdade de Ciências da Saúde, 2010. / Submitted by Shayane Marques Zica (marquacizh@uol.com.br) on 2011-03-18T18:48:09Z No. of bitstreams: 1 2010_DeboraFerreiraCarneiro.pdf: 2035586 bytes, checksum: ee9d140bc73a527e588a16ce8b998da1 (MD5) / Approved for entry into archive by Daniel Ribeiro(daniel@bce.unb.br) on 2011-03-19T19:55:48Z (GMT) No. of bitstreams: 1 2010_DeboraFerreiraCarneiro.pdf: 2035586 bytes, checksum: ee9d140bc73a527e588a16ce8b998da1 (MD5) / Made available in DSpace on 2011-03-19T19:55:48Z (GMT). No. of bitstreams: 1 2010_DeboraFerreiraCarneiro.pdf: 2035586 bytes, checksum: ee9d140bc73a527e588a16ce8b998da1 (MD5) / Perfurações radiculares podem ser seladas com auxílio de materiais endodônticos, que ficam em contato direto com as células do ligamento periodontal, podendo causar danos que retardem ou impeçam o processo de reparo. Os objetivos deste trabalho foram avaliar a citocompatibilidade dos extratos dos materiais endodônticos (Endofill, Sealer 26, cimento de Portland branco e Cimento de óxidos bioativos), recém espatulados e após 24 horas de presa, em contato com células do ligamento periodontal humano. Foram utilizados como parâmetros de análise a capacidade de proliferação, o potencial transmembrânico mitocondrial, as alterações morfológicas, o potencial genotóxico e as alterações no ciclo celular. As células do ligamento periodontal foram obtidas a partir da extração de quatro terceiros molares e cultivadas em laboratório, conforme protocolos de cultura de células. As análises dos efeitos foram realizadas por meio do teste MTT de viabilidade celular, análise microscópica e a citometria de fluxo utilizando como fluorocromos rodamina 123 e iodeto de propídio. O pH foi avaliado pela medição imediata do meio de cultura com extrato do cimento endodôntico com auxílio de pHmetro calibrado. Os resultados obtidos, após análise estatística (ANOVA a três fatores, com nível de significância p<0,05), revelaram que a composição dos materiais é o fator mais influente nas alterações celulares. Todos os materiais demonstraram algum grau de toxicidade para as células do ligamento periodontal dependendo da análise realizada. Somente o Endofill demonstrou toxicidade em todos os testes. Cimento de óxidos bioativos e o cimento de Portland branco não causaram alterações no potencial transmembrânico mitocondrial. Sealer 26, Sealer  e Cimento de Portland branco aumentaram o pH do meio e os dois primeiros também provocaram alterações morfológicas. Cimento de óxidos bioativos foi o que causou os menores danos ao DNA celular e, portanto, as menores alterações em ciclo celular. A citotoxicidade tende a diminuir à medida que a reação presa se completa. Apesar dos resultados, faz-se necessário continuar as pesquisas, com organismos vivos, para predizer e estabelecer a compatibilidade dos materiais. _______________________________________________________________________________ ABSTRACT / Root perforations can be sealed with the aid of endodontic materials, which are in direct contact with the periodontal ligament cells, may cause damage to slow or prevent the repair process. Our objectives were to evaluate the cytocompatibility of the extracts of endodontic materials (Endofill, Sealer 26, white Portland cement and bioactive oxides-based sealer), after contact for 24 hours with human periodontal ligament cells. The cell viability, the mitochondrial transmembrane potential, the morphological changes, the genotoxic potential and changes in the cell cycle were evaluated by MTT assay and flow cytometry. The periodontal ligament cells were obtained from the extraction of four third molars and cultured in the laboratory by cell culture protocols. The pH was measured at the material extract at varying time intervals with calibrated pHmeter. The results, after statistical analysis (ANOVA with three factor interaction, p <0.05), revealed that the composition of materials is the most influential factor in the cellular changes. All materials showed some degree of toxicity to the cells of periodontal ligament depending on the analysis. Only Endofill demonstrated toxicity in all tests. Bioactive oxides-based sealer and white Portland cement did not cause changes in mitochondrial transmembrane potential. Sealer 26, Sealer  and white Portland cement increased the pH of the medium and the first and second also caused morphological changes. Bioactive oxide-based sealer was what caused the least damage to cellular DNA and thus the smallest changes in the cell cycle. The cytotoxicity tends to decrease as the set reaction is complete. Despite the results, it is necessary to continue research with living organisms to predict and establish the compatibility of materials.

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-21T06:06:54Z (GMT). No. of bitstreams: 1 Almeida_RenatoCastrode_D.pdf: 2877178 bytes, checksum: be0449278267396730bbcd25c53cdc1a (MD5) Previous issue date: 1995 / Resumo: Este trabalho teve como objetivo verificar o efeito do meio bucal simulado sobre a força de tração exercida por 15 cadeias elastoméricas coloridas, de fabricação brasileira (Tecnident), em função do tempo de distensão. As amostras foram constituídas de 10 módulos, de 4 anéis, para cada cor, selecionados ao acaso. Os módulos foram distendidos à distância constante de 25 mm., imersos em saliva artificial (Oralub) e mantidos em estufa, à temperatura constante de 37°C ± 1 °C. As leituras de força de tração foram efetuadas com um dinamômetro Correx (Suíça), obedecendo a 10 períodos de tempo: inicial, 1 hora, 6 horas, 12 horas, 24 horas, 72 horas, 1 semana, 2 semanas, 3 semanas e 4 semanas. Os resultados mostraram, que as cadeias elastoméricas se comportaram diferentemente entre si, quanto à força de tração, variando de intensidade conforme a sua cor. Assim, a força inicial variou de 459,0 gramas (verde 1) a 345,0 gramas (verde 3) e a força remanescente, ao final de 4 semanas de teste, variou de 162,0 gramas (cinza) a 94,0 gramas (verde 3). Ao final de 4 semanas de teste, a maior porcentagem de força remanescente foi apresentada pelo elastômero de cor pink, com 41,14%, enquanto a menor foi apresentada pelo elastômero de cor verde 1, com apenas 22,77% de força remanescente. Portanto, após a análise estatística dos resultados, foi possível concluir que o meio bucal simulado exerceu efeito significativo sobre o desempenho da força de tração das cadeias elastoméricas pigmentadas, de fabricação brasileira, após distensão / Abstract: This work has as goal to check the effect of simulated buccal surrounding on the traction force made by 15 colorful elastomeric chains, Brazilian production (Tecnident), in function of distension time. The samples were made from 10 modules, of 4 rings for each color, selected at random. The modules were distended to the constant distance of 25 mm., immersed in artificial saliva (Oralube) and kept in sterilizer at the constant temperature of 35°C ± 1°C. The traction force readings were with a dynamometer Correx (Swiss), following the 10 time periods: initial, 1 hour, 6 hours, 12 hours, 24 hours, 72 hours, 1 week, 2 weeks, 3 weeks and 4 weeks. The results showed that the elastomeric chains behaved differently among themselves, as the traction force, changing of intensity, depending on its color. In this way, the initial force varied from 459,0 grams (green 1) to 345,0 grams (green 3) and the remaining force, at the end of 4 week's test varied from 162,0 grams (gray) to 94,0 grams (green 3). At the end of 4 week's test, the higher percentage of remaining force was showed by the pink elastomer, with 41,14% while the lowest one was showed by the green 1 elastomer, with just 22,77% of remaining force. Therefore, after the result statistical analyze, was possible to verify that the simulated buccal surrounding made meaningful effect over the traction force performance of pigmented elastomeric chains, Brazilian production, after distension / Doutorado / Ortodontia / Doutor em Ciências

Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-21T10:40:31Z (GMT). No. of bitstreams: 1 Garcia_KelleCristina_M.pdf: 2436383 bytes, checksum: 22ffa406fcb76451d2889ccc9e282115 (MD5) Previous issue date: 1996 / Resumo: A proposta deste trabalho foi verificar a microdureza superficial e a resistência compressão de cimentos de ionômero de vidro, Tipo lI, conhecidos comercialmente como VIDRION R (SS WHITE) e VITREMER (3M), em intervalos de armazenagem de 15 minutos, 1 hora e 24 horas à temperatura de 37°C e 100% de umidade relativa. Para o ensaio de microdureza superficial foram confeccionados cinco corpos de prova para cada material, em ambiente controlado de temperatura (23 '+ OU ¿' 2°C) e umidade relativa do ar (50 '+ OU ¿' 10%). Os materiais foram proporcionados e espatulados de acordo com as instruções dos fabricantes e colocados em matrizes plásticas cilíndricas, com 6 mm de diâmetro interno por 1,8 mm de altura. Os corpos de prova foram confeccionados e armazenados em estufa a 37°C e 100% de umidade relativa. Os valores de microdureza Knoop (KHN) foram determinados utilizando um microdurômetro (DURIMET). As penetrações foram feitas sob carga de 50 gramas, por 30 segundos, totalizando cinco penetrações em cada corpo de prova. Para o ensaio de resistência à compressão foram confeccionados 10 corpos de prova para cada intervalo proposto, de acordo com a especificação n09 da Associação Dentária Americana, proporcionados e confeccionados em ambiente de trabalho com temperatura e umidade controladas. A espatulação e a proporção pó/líquido foram realizadas de acordo com as instruções dos fabricantes. Os corpos de prova do cimento de ionômero de vidro VITREMER (ativação tripla) foram polimerizados pela luz visível por meio de um fotopolimerizador VISILUX 2 (3M), por 40 segundos e, em seguida, armazenados em estufa a 37°C e 100% de umidade relativa. A resistência à compressão foi obtida através de uma máquina universal LOS (Alemanha), com carga de 100 kg/minuto e os resultados obtidos em kg/cm2 foram transformados em unidade MPa. Após a realização do teste de microdureza superficial e resistência à compressão, os valores obtidos foram submetidos ao Teste de Tukey ao nível de 5% de significância. O tempo de armazenagem aumentou os valores de microdureza superficial para os dois materiais, com resultados estatisticamente significativos ao nível de 5% de probabilidade. Em cada período de armazenagem, os valores de microdureza superficial não apresentaram diferenças estatisticamente significativas para os dois materiais. Com relação aos valores de resistência à compressão, o tempo de armazenagem aumentou os valores de resistência dos cimentos com resultados estatisticamente significativos ao nível de 5% de probabilidade. Porém, em todos os períodos, os valores apresentados pelo cimento de ionômero de vidro VITREMER foram estatisticamente superiores aos do cimento VIDRION R / Abstract: The purpose of this work was to verify the superficial microhardness and the compressive strenght of VIDRION R (SS WHITE) and VITREMER (3M) glass ionomer cements, Type II, stored at 37°C and 100 % relative humidity for 15 minutes, 1 hour and 24 hours. For the superficial microhardness test were made five samples from each material, in temperature (23 '+ OU ¿' 2°C) and relative humidity (50 '+ OU ¿' 10 %) in controled environmental. The materiais were ratio and mixing in accordance with the manufacturer's instructions and placed in plastic mold with 6 mm in diameter and 1.8 mm in height. The samples were stored in dissecator at 37°C and 100 % relative humitidity. The values of superficial microhardness (KHN) were determined by indentations (DURIMET) with load of 50 weight by 30 seconds, totalizing five indentations in each sample. For the compressive strength test were made ten samples for each intervals purpose, according to Association Dental American especification n# 9, in temperature and humidity controled environmental. The mixing of the powder/líquid ratio was realized according to manufacturer's instructions. The samples of VITREMER glass ionomer cement (activaction triple) were polimerized by visible light with a VISILUX 2 (3M) unit, by 40 seconds and after stored in a dissecator at 37°C and 100 % relative humidity. The compressive strength was obtained by LOS machine (GERMANY), with load of 100 kg/min. The superficial microhardness and compressive strength values were submited to Tukey's test at 5 % confidence leveI. The storage time increased the values of superficial microhardness for the two materiais ( p < 0.05). In each storage period, the values of superficial microhardness did not show difference statistically significant for the two materiais. The storage time increased the values of compressive strenght of cements (p < 0.05). However, the values presented by VITREMER glass ionomer cement were statistically higher than the VIDRION R cement, in alI periods / Mestrado / Materiais Dentarios / Mestre em Ciências