Orientador: Luis Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-22T19:00:05Z (GMT). No. of bitstreams: 1 Liporoni_PriscilaChristianeSuzy_M.pdf: 2141251 bytes, checksum: a3ac5173dc3d07b4b25bd1c21f88f27b (MD5) Previous issue date: 1997 / Resumo: O acabamento e polimento de restaurações diretas são essenciais para se obter uma lisura superficial adequada. O propósito deste estudo foi avaliar "in vitro" a deposição superficial de corante em ionômeros de vidro modificados por resina quando submetidos a diferentes tratamentos superficiais de acabamento e polimento. Os materiais foram manipulados de acordo com as instruções dos fabricantes, inseridos em uma matriz de acrílico, cobertos com uma tira de poliéster e fotopolimerizados. Vinte e quatro amostras de cada material, Photac-Fil ( Espe ) e Fuji II LC ( GC Corporation ) foram divididas em três grupos: Tira matriz ( GC ); Pontas Enhance ( GI ); Discos Sof-Iex fino e extra-fino ( Gil ). Todas as amostras foram submetidas ao teste de manchamento através do corante azul de metileno e quantificados num espectrofotômetro. Foi feita a Análise de Variância para comparação entre as médias e então aplicado o Teste de Tukey ( a = 0,05% ). As médias (Jlg/ rnl) para cada material foram: Photac-Fil, GC = 0,999; GI = 1,175; Gil = 1,157 e Fuji II LC, GC = 0,0~01; GI = 0,547; GIl = 0,0001. Concluiu-se que a melhor superfície foi obtida quando os materiais polimerizaram junto à tira matriz. Entre os materiais utilizados no acabamento e polimento, os discos Sof-Iex apresentaram melhores resultados para o híbrido Fuji II LC / Abstract: Finishing is essential to obtain appropriate smooth surfaces of direct restorations increasing the longevity of them. The purpose of this study was to evaluate "in vitro" superficial dye deposition on resin modified glass-ionomer submitted to different surface finishing treatments. The materiaIs were mixed following the manufactures directions, inserted into split molds, covered with a matrix strip and polymerized. Twenty-four samples of the each material, Photac-fil ( Espe ) and Fuji 11 LC ( GC Corporation ) were divided into three finishing groups: (I) Mylar matrix ( control); (11) disks Sof-Iex ( fine and ultra-fine); (111) Enhance system. AlI samples were submitted to staining test by dye uptake and were quantified by spectrophotometry. The results were analysed by ANOV A and Tukey's test. The means Ü.lg! rnl) for each material were: Photac-Fil, GC = 0,999; GI = 1,175; GIl = 1,157 and Fuji 11 LC, GC = 0,0001; GI = 0,547; GIl = 0,0001. It was concluded that the best surface was obtained when the materiaIs were cured in contact with the Mylar matrix strip. Among the materials used for surface finishing Sof-Iex presented the best results to Fuji 11 LC / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientadores: Saide Sarkis Dominitti, Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T10:20:15Z (GMT). No. of bitstreams: 1 ArioliFilho_JoaoNeudenir_D.pdf: 3667904 bytes, checksum: af02ed1626db8a56027835c5e7ba4380 (MD5) Previous issue date: 1998 / Resumo: O objetivo deste estudo foi analisar a intluência do período de armazenagem e das técnicas de polimerização, em três marcas comerciais de resinas acrílicas, na movimentação dental de prótese total superior. As resinas acrílicas utilizadas foram LUCITONE 550 (polimerizada em banho de água a 740C por 9 horas e em microondas a 500 W por 3 minutos), QC20 (ciclo em água fervente por 20 minutos) e ACRON-MC (ciclo em microondas 500W por 3 minutos). As distâncias dentais foram mensuradas após o enceramento da prótese (To), inclusão (TI), polimerização e demutlagem (Tz) e nos períodos de 3 (T3), 7 (T4) e 30 dias (Ts) de armazenagem em água a 37°C. Os resultados obtidos foram submetidos ao teste de T~ey (p :::; 0,05) e permitindo concluir que: (1) A resina ACRONMC apresentou os maiores deslocamentos dentais~ (2) No período T3 (3 dias de armazenagem) ocorreram os maiores índices de deslocamentos dentais~ (3) Os períodos de armazenagem em água não compensaram totalmente as distorções~ e, (4) As distâncias entre pré-molares e molares mensuradas no plano horizontal nas direções látero-Iateral e ânteroposterior apresentaram contração e expansão respectivamente / Abstract: The objective of this study was to analyze the teeth movement during different cure techniques of three commercial acrylic resins and afier periods of water storage in upper complete dentures. The acrylic resins used and the cure techniques proposed were : LUCITONE 550 (cured in water 9 Hs at 74° C and energy microwave 550 W at 3 min.), QC-20 (cured in boiled water 20 min.) and ACRON-MC (cured in energy microwave 550 W at 3 min.). The teeth distances, measured in the frontal and sagital planes by linear microscopy, were taken afier denture wax (To), denture inc1usion(T 1), cureq and demuflask (T2) and in the periods of 3(T3), 7- (T4) and 30-day (Ts) water storage. The results were analysed for Tukey's test (p ~ 0,05) and permited to conc1ued that: (1) ACRON-M..Ç resin presented_the highes~h movement in all perioqs: (2) the 3-d.ro: water storage ITJJ showed--1he highest movement scores: (3) the water storage did not fully compensate the cur~ distortions in upper complete illnture anq (4) cont;rngion anq expansion occurreq among ~ ' measured frontal/sagital planes. respectively / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-26T02:35:04Z (GMT). No. of bitstreams: 1 Freitas_GersineiCarlosde_D.pdf: 4162353 bytes, checksum: 73f549d9460534321d100928321de41f (MD5) Previous issue date: 2000 / Resumo: o propósito deste estudo foi avaliar a resistência à tração da união de dois tipos de ligas metálicas (Litecast B e Pors-on 4) fixadas em dentina humana tratada sob três condições (condicionada por 1O segundos com ácido fosfórico 35%, ácido poliacrílico 25% e não condicionada). Os cimentos foram 1- de fosfato de zinco, 2- ionômero d vidro e, 3- cimento resinoso. Noventa molares humanos foram inseridos em resina acrílica e desgastados com lixas d'água de granulação nOs 120, 320 e 600 até aproximadamente 2 mm além da junção amelo-dentinária. Noventa corpos-de-prova com 6,0 mm de diâmetro por 7 mm de altura foram confeccionados, sendo quarenta e cinco com liga de níquel-cromo (Litecast B) e quarenta e cinco com liga paládio-prata (Pors-on 4). Quinze corpos-de-prova de cada liga foram fixadas com os cimentos de fosfato de zinco (55 White), ionômero de vidro (Vitremer - 3M) e cimento resinoso (3M). Antes da fixação, a dentina de cinco corpos-de-prova foi condicionada com ácido fosfórico 35%, cinco com ácido poliacrílico 25%, ambas por 1O segundos e cinco não condicionadas. Todos os corpos-de-prova foram armazenados a 37°C por 24 horas antes do ensaio. Em seguida, os corpos-de-prova foram submetidos ao ensaio de tração em uma máquina Instron a velocidade de 0,5 mm/min. até a separação entre liga metálica e dente. Os resultados foram submetidos a análise de variância e ao teste de Tukey (p<0,05). Os dados indicaram que: Para a liga Pors-on 4 o cimento de resina apresentou valores de resistência à remoção, por tração, estatisticamente superiores ao cimento de ionômero de vidro e de fosfato de zinco para as três condições de tratamento da dentina. O cimento de ionômero de vidro apresentou valores estatisticamente superior ao de fosfato de zinco, para a dentina condicionada com ácido fosfório 35% e ácido poliacrílico 25%. Nenhuma diferença estatística foi encontrada entre o cimento de ionômero de vidro e fosfato de zinco para a superfície não condicionada; Para a liga Litecast B, o cimento de resina apresentou valores de remoção, por tração, estatisticamente superiores aos cimentos de fosfato de zinco e de ionômero de vidro para a dentina condicionada com ácido fosfórico 35% e poliacrílico 25%. O cimento de fosfato de zinco foi superior ao de resina para a dentina não condicionada. Nenhuma diferença foi observada entre o cimento de fosfato de zinco e de ionômero de vidro para as três condições da dentina e entre o cimento de ionômero de vidro e de resina para a dentina não condicionada. Para as duas ligas, o cimento de resina mostrou valores de remoção, por tração, superiores aos do fosfato de zinco e ionômero de vidro. De uma maneira geral, a liga liga Pors-on 4 apresentou valores de resistência a remoção por tração estatisticamente superiores a liga Litecast B, para todos os cimentos e tratamentos da dentina / Abstract: The aim of this study was to evaluate the tensile bond strength of two alloy systems (Litecast B and Pors-on 4) luted with three cements to dentin in three conditions (etched with 35% phosphoric acid, 25% polyacrylic acid for 10 seconds and no etching). Ninety extracted human molars were embedded in resin with 10 mm in diameter of exposed dentin which had been grounded with 120, 320 and 600 grit SiC paper. Forty-tive specimens with 6.0 mm in diameter and 7.0 mm long, were fabricated with nickel chromium-beryllium (Litecast B) and palladium-silver (Pors-on 4) alloys. Fifteen specimens of each alloy systems were luted with zinc phosphate cement (SS White), glass ionomer cement (3M) and resin cement (3M). Prior to cementation, the dentin of five specimens were etched with 35% phosphoric acid, tive with 25% polyacrylic acid for 10 seconds and tive no etching. Ali samples were stored in distilled water at 37° C for 24 hours prior to testing. After the specimens were submitted to the tensile bond strength in an Instron at a crosshead speed of 0.5 mm/min until failure. The results were submitted to variance analysis and Tukey's test (p<0.05). The data indicated that for Pors-on 4: the resin cement showed tension bond strength values stronger than glass ionomer cement and zinc phosphate cement in three dentin conditions (p<0. 05). Glass ionomer cement showed values stronger than zinc phosphate for dentin etched with phosphoric acid and polyacrilic acid. For no etching no difference was found between glass ionomer cement and zinc phosphate cement; for Litecast B: the resin cement was signiticantly stronger than zinc phosphate and glass ionomer cement for dentin etched with two acid. Zinc phosphate was stronger than resin cement for dentin no etching. No difference was found between zinc phosphate and glass ionômero cement in three dentin conditions and between glass ionomer cement and resin cement to the dentin no etching. For the two alloy systems the resin cement showed tensile bond strength better than glass ionomer and zinc phosphate cement for three dentin conditions. In general, Pors-on 4 alloy showed tension strength values stronger than Litecast B alloy, in three dentin conditions and cements / Doutorado / Doutor em Materiais Dentários

Orientadores: Saide Sarckis Domitti, Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T01:30:57Z (GMT). No. of bitstreams: 1 Tanji_Mauricio_M.pdf: 3213490 bytes, checksum: a4c59df5e90cc9828835588aa5d0cd4a (MD5) Previous issue date: 2000 / Resumo: Este trabalho comparou a influência das variáveis resistência ao impacto, dureza de superficie, rugosidade e porosidade em 30 corpos-de-prova de resinas acrílicas termopolimerizáveis Clássico, QC-20 e Onda-Cryl, confeccionados a partir de modelos retangulares de alumínio (65xlO e 64x9 x 3,0 mm), fixados com adesivo instantâneo (Super Bonder, Loctite) em suporte de madeira. Os modelos foram moldados com silicona por condensação para uso laboratorial (Zetalabor-Labordental Ltda.) e os moldes incluídos em muflas metálicas e de fibra de vidro. A proporção póllíquido e mistura, assim como a prensagem das resinas acrílicas foram realizadas de acordo com as instruções dos fabricantes. Após a polimerização nos ciclos de água aquecida a 74°C por 9 horas, água em ebulição por 20 minutos, e por energia de microondas a 1400 W por 3 minutos, os corpos de-prova foram removidos das muflas após esftiamento em temperatura ambiente e submetidos aos processos de acabamento e polimento convencionais. Posteriormente, foram submetidos aos ensaios de resistência ao impacto, numa máquina Otto Wolpert Werke pelo sistema Charpy; de dureza, num microdurômetro Shimadzu (Modelo HMV-2000) calibrado com carga de 25 gramas por 10 segundos; de rugosidade num rugosímetro (Modelo Surfcorder SE 1700); e de porosidade, através da imersão dos corpos-de-prova em tinta Nankin (Acrilex) por 12 horas, lavados em água corrente por 10 segundos, e posteriormente quantificada e fotografada em área previamente determinada. Os resultados submetidos à análise de variância e ao teste de Tukey (5%) mostraram que a porosidade softeu influência dos tipos de resina acrílica com maiores valores para a de microondas, o mesmo ocorrendo para com a dureza. Os menores valores de rugosidade foram mostrados pela resina para microondas, enquanto as demais resinas acrílicas não mostraram diferenças estatisticamente significantes; e a resistência ao impacto não sofreu influência dos tipos de resinas acrílicas / Abstract: This study investigated the influence of the impact strenght, hardness of surface, roughness and porosity variables in 30 specimens on Clássico, QC-20 and Onda-Cryl, thermo-cured acrylic resins. The specimens were made in retangular aluminium mo dei (65xlO and 64x9 x 3,0 mm), attached to a wooden holder by Super Bonder glue (Loctite). The model were printed using a Zetalabor (Labordental Ltda.) silicone for condensation for laboratory purposes and the molds were inc1uded into metal flasks, and reinforced fiberglass flasks. The proportion powder/liquid and mixture, as well as acrylic resin pressing were done following the manufature's instructions. After hot water (74°C) for 9 hours, boiling water for 20 minutes; and microwave energy with 1400W for 3 minutes, curing cyc1es the specimens were removed form flasks after cooling at room temperature and submetted to polishing by conventional procedure. Subsequently, were submetted to impact strenght test by Charpy system in a W olpert machine; and hardness by Shimadzu microdurometer with load of 25 grams during 10 seconds; and the superficial roughness with Surfcorder SE 1700; and porousness by specimens immersion into Nankin ink (Acrilex) for 12 hours, washed into running water for 10 seconds and thererafter the porousness was counted and photographed in pre-determined areas. The results submetted to ANOV A and Tukey's test showed that the porosity was influenced by acrylic resin types with greater values for microwave, the same was showed for the hardness. The roughness and hardness smaller values had been showed for microwave resin, however the other cyc1es didn't show difference statistical significant; and the impact strenght hadn't influence of the acrylic resins types / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Orientador: Lourenço Correr Sobrinho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T09:59:32Z (GMT). No. of bitstreams: 1 Borges_GilbertoAntonio_M.pdf: 3479582 bytes, checksum: 48667180de177d8d86f6c782a513e22b (MD5) Previous issue date: 2000 / Resumo: O propósito deste estudo foi avaliar a resistência ao cisalhamento de bráquetes fixados à cerâmica dental, utilizando as variáveis: materiais para colagem, tratamento superficial e aplicação do silano. Foram confeccionados 192 discos de cerâmica (Duceram) com 5 mm de diâmetro por 2 mm de espessura. Os discos foram embutidos com resina acrílica ativada quimicamente em tubos de P.V.C. e divididos em 4 grupos de 48 discos de acordo com o tratamento de superfície: Grupo I - condicionamento com ácido fosfórico 37%, por 30 segundos; Grupo 11 - condicionamento com ácido hidrofluorídrico a 10%, por 2,0 minutos; Grupo 111 - jateado com óxido de alumínio por 4 segundos; e, Grupo IV submetido apenas a profilaxia com pedra pomes e água por 30 segundos. Vinte e quatro corpos-de-prova de cada grupo receberam aplicação de silano e vinte e quatro não. Três materiais para colagem Transbond XT, Concise e Fuji Ortho LC foram utilizados para fixação dos bráquetes à cerâmica para cada grupo (com e sem silano) perfazendo um total de 64 fixações por material. Todas as amostras foram armazenadas em água destilada a 37° C, por 24 horas. Em seguida, as amostras foram submetidas ao teste de resistência ao cisalhamento numa máquina Instron a velocidade de 1,0 mm/min. Os resultados foram submetidos a análise de variância e ao teste de Tukey 5% de significância. Os resultados mostraram que independente do tratamento superficial da cerâmica e silanização o Transbond XT mostrou valores de resistência ao cisalhamento superiores em relação ao Concise e Fuji Ortho LC (p<0,05); o tratamento superficial da cerâmica com ácido hidrofluorídrico mostrou valores de resistência ao cisalhamento superiores em relação ao jateamento com óxido de alumínio, com condicionamento com ácido fosfórico e profilaxia com pedra pomes e água, independente do material para colagem e silanização (p<O,O5); e, a aplicação do silano aumentou a resistência da união cerâmicalbráquete para os três materiais e tratamentos superficiais, exceto para os bráquetes fixados na cerâmica com o Concise em superfícies submetidas à profilaxia com pedra pomes e água / Abstract: The purpose of this study was to evaluate the shear bond strength of brackets fixed on dental ceramic using three different materials with or without silane. One hundred ninety two specimens with 5 mm in diameter and 2 mm thickness were made with ceramic (Duceram). The specimens were divided into four groups according to surface treatments: Group I - acid etching with 37% phosphoric acid for 30 seconds; Group 11 - acid etching 10% hydrofluoridric acid for 2,0 minutes; Group 111 - Sandblasting with aluminum oxide for 4 seconds; and, Group IV - cleaned with pumice slurry. Twenty-four specimens of each group was treated with silane agents and twenty-four remained untreated. The brackets were bonded to ceramic with Transbond XT, Concise and Fuji Ortho LC. Ali specimens were stored in distilled water 37° C for 24 hours. After that the specimens were submitted to shear bond strength in an Instron at a crosshead speed of 1,0 mm/min. The results were submitted to variance analyses and Tukey's test (p<0.05). The date indicated that the Transbond XT showed higher values of shear bond strength than Concise and Fuji Ortho LC independent of the treatment on ceramic surface (p<0.05); the ceramic etching with hydrofluoridric acid of the ceramic showed higher values shear bond strength than the others three treatments for ali specimens (p<0.05); and the treatement with silane increased the shear bond strength of ceramic/bracket interface for ali materials, except Concise cleaned with pumice slurry on surface ceramic / Mestrado / Mestre em Materiais Dentários

Orientador: Marcelo Ferraz Mesquita / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Campinas / Made available in DSpace on 2018-07-27T09:42:09Z (GMT). No. of bitstreams: 1 CarmoFilho_JoseLopesdo_M.pdf: 2851043 bytes, checksum: 65b6ca0779ecc240d74dba3e452b088c (MD5) Previous issue date: 2000 / Resumo: Este trabalho teve como objetivo avaliar "in vitro", o efeito da ação de diferentes escovas na manutenção das características superficiais de reembasadores resilientes. Foram confeccionadas 30 amostras, divididas em 6 grupos de variáveis, com 5 amostras para cada variável. Para a confecção das amostras, foram utilizadas matrizes acrílicas incluídas em muflas, obtendo um molde impresso no gesso e posteriormente preenchido com os materiais resilientes Dentuflex (ativado quimicamente) ou Eversoft (ativado termicamente). Os materiais foram manuseados seguindo as orientações dos fabricantes. As amostras foram submetidas à leitura de rugosidade superficial num rugosímetro Prazis modelo Rug-03 (AROTEC­Argentina). Em seguida, foram fixadas no recipiente metálico da máquina de escovação (Equilabor) e submetidas ao ensaio de escovação mecânica. Foram utilizadas as escovas: 1- Te_ de cerdas duras; 2- Johnson's 30, de cerdas extra macias; e 3- Phb, de cerdas ultra-suaves. As escovas foram presas a um dispositivo da máquina de escovação. No recipiente de escovação da máquina, foi colocada uma solução contendo 6g de dentifrício para 6ml de água. As amostras foram submetidas à movimentos lineares de escovação, totalizando 30.000 ciclos, sob carga estática de 200g. Após a escovação, foram realizadas novas leituras dos valores de rugosidade superficial, e os valores obtidos submetidos à análise de variância e ao teste de Tukey, com 5% de significância. O material Dentuflex apresentou valores de rugosidade superficial estatisticamente superiores aos apresentados pelo material Eversoft, antes da escovação. Após a escovação, o material Dentuflex apresentou valores estatisticamente semelhantes aos apresentados pelo Eversoft. Para o material Eversoft, a escova Tek provocou maior rugosidade superficial, seguida pela escova Johnson's, sendo que a escova Phb não alterou estatisticamente os valores de _rugosidade superficial. Para o material Dentuflex, as escovas Te_ Johnson's e Phb produziram valores estatisticamente semelhantes, entretanto a escova Phb parece ter provocado polimento na sua superficie, diminuindo seus valores de rugosidade superficial / Abstract: The aim ofthis study was to evaluate "in vitro" the effect ofbrushing on the surface features of resilient lining materiaIs. TIrirty samples were prepared and divided into 6 groups of variables with 5 test repetitions for each variable. The samples were made with acrylic matrixes placed in a flask to obtain a cast pressed molel, later filled with resilient lining materiaIs like Dentuflex ( chemically activated) or Eversoft ( thermally activated). The materiaIs were handled according to the manufacturer's directions. The samples were subjected to surface roughness readings in a roughness reOOing machine (prazis, model RUg-03, AROTEC- Argentine). They were fixed to the brushing machine (Equilabor) and submited to a mechanical brushing simulation. Three different brushes were used in the experiment: "l-Tek" with thick filaments, "2-Johnson's 30" with extra-soft filaments and "3-Phb " with ultra-soft filaments. The brushes were attached to a device in the brushing machine and a solution of 6g. of toothpaste/ 6 ml of water was placed in the brushing recipient of the machine. The samples were submited to linear brushing movements, totaling 30,000 cycles, under a 200g. static 1000 pressure. After the brushing, new readings of the surface roughness were made and the values obtained were subjected to variance analysis and the Tukey test, with 5% of significance. Before brushing, Dentuflex showed values of surface roughness statistically higher than the values obtained with Eversoft. After brushing, Dentuflex showed values statistically equivalent to the ones obtained with _Eversoft. The use ofEversoft with the three different brushes had the following results: the "PHb" brush did not statistically change the values of surface roughness. The use of "Tek" brush caused higher roughness, followed by the "Johnson's" brush, however, the Dentuflex with the "Tek", "Johnson's" and "PHb" brushes showed similar statistical values, however, the "Phb" brush seems to have polished the surface, thus decreasing the surface roughness values / Mestrado / Protese / Mestre em Clínica Odontológica

Orientador : Marcelo Ferraz Mesquita / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T15:44:52Z (GMT). No. of bitstreams: 1 Pinto_JoseRenatoRibeiro_M.pdf: 2240755 bytes, checksum: bba30074db6c533e3f9e02730326069b (MD5) Previous issue date: 2001 / Mestrado

Orientadores : Saide Sarckis Domitti, Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T17:36:03Z (GMT). No. of bitstreams: 1 Borges_LuizHenrique_D.pdf: 3778776 bytes, checksum: e1a8e978c93c200285af8af68e063845 (MD5) Previous issue date: 2001 / Resumo: Este trabalho teve o objetivo de avaliar o efeito do tempo pós-prensagem sobre a rugosidade, dureza superficial e porosidade da resina acrilica QC-20, em diferentes ciclos de polimerização. Para a confecção dos 81 corpos-de-prova foram utilizadas matrizes circulares de silicona de condensação medindo 30 mm de diâmetro e 5 mm de espessura, obtidas através de um molde padrão. As matrizes foram incluídas em muflas metálicas emuflas com reforço de fibra de vidro. A proporção pó/líquido, e a prensagem da resina acrílica foram feitas de acordo com as instruções do fabricante. As muflas foram deixadas em descanso por 30 minutos, 12 e 24 horas antes da polimerização que foi realizada nos ciclos de água aquecida a 74°C por 9 horas, 20 minutos em água em ebulição, e energia de microondas por 3 minutos a 500 W. Após o resfriamento em temperatura ambiente, os corpos-de-prova foram submetidos aos processos de acabamento e polimento em politriz, e submetidos aos testes de rugosidade superficial média, através do rugosímetro Surfcorder SE 1700, dureza superfical em um microdurômetro Shimadzu, e porosidade superficial, através da imersão dos corpos-de-prova em tinta nankin por 8 horas, contados em área determinada. Os resultados obtidos foram submetidos à análise de variânci_ e ao teste de Tukey ao nível de significância de 5%. Concluiu-se que não houve diferenças significativas entre as médias obtidas pelos métodos para as variáveis rugosidade e porosidade. Para a variável dureza superficial, houve diferenças significativas entre o método convencional e os outros dois métodos, mostrando que o método convencional apresentou menor dureza em relação aos demais / Abstract: The purpuse of this study was to investigate the effect of post-pressing step time on the roughness, surface hardness Knoop and porosity of a QC-20 acrylic resin in different polymerization cycles. Specimens were manufactured using 30 mm high and 5 mm thick round condensation silicone matrices, obtained through a standard method. The matrices were placed in metallic and in fiberglass-reinforced mufles. Powderlliquid ratio and acrylic resin pressing were carried as recommended by the manufacturer. Mufles were allowed to rest in the 0011 press for 30 minutes, 12 and 24 hours before being polymerized in heated water, boiling water and microwave energy cycles at 74°C for 9 hours. Afier cooling in room temperature, specimens were fmished and polished with politriz. Afterwords, specimens were submitted to superficial roughness test, using roughness tester Surfcorder SE 1700; to a superficial hardness test in a microdurometer Shimadzu 2000, and apparent porosity in which specimens were immersed in Nankin ink for 8 hours, being sectioned in a determined area later. The results were submitted to variance analysis and Tukey's test 5% significance leveI. 1t was concluded that there were no significant differences between the averages obtained by the methods used for roughness and porosity. For superficial hardness, there were significant differences between the conventional method and the other two used, showing that the conventional method demonstrated less hardness when compared to the others / Doutorado / Protese / Doutor em Clínica Odontológica

Orientador : Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T00:32:05Z (GMT). No. of bitstreams: 1 Cunha_MarciaReginaBernardida_M.pdf: 2234174 bytes, checksum: d5064ae556f27764bd71a1f2aca5f61e (MD5) Previous issue date: 2001 / Resumo: O objetivo deste estudo foi avaliar a resistência de união à tração de sistemas adesivos dentinários convencionais e autocondicionantes aos 10 minutos e 24 horas pós-polimerização. Superfícies dentinárias planas foram preparadas nas faces superfícies vestibulares de 120 incisivos inferiores bovinos e sobre as quais foi delimitada a área de união de 4mm de diâmetro com fita adesiva. Nos grupos citados foram aplicados os seguintes sistemas adesivos seguidos da aplicação da resina composta Z 100: Grupo A e B - ScotchBond Multi-Uso Plus; Grupos C e D - Single Bond; Grupos E e F- Clearfil Liner Bond 2Ve Grupos G e H - Clearfil SE Bond. Nos Grupos A, B, C e D foi efetuado condicionamento com ácido fosfórico a 35% sobre a dentina por 15 segundos, seguida da lavagem e remoção do excesso de água. Um cilindro de resina composta foi posicionado sobre a área de união delimitada e fotoativado por 20 segundos em três pontos da interface para a realização do ensaio de tração, que foi conduzido após 10 minutos da união para os Grupos A, C, E e G. Os grupos B, D, F e H foram armazenados em água destilada a 37°C e o teste foi realizado após 24 horas em máquina de ensaio universal Instron com velocidade de 0,5mm/minuto, após o qual, o padrão de fratura foi observado sob Microscopia Eletrônica de Varredura. Os resultados foram submetidos à análise de variância e teste de Tukey (p< 0,05). Os resultados do ensaio de tração expressos em MPa foram: Grupo A- 7,69 +/- 1,40; Grupo B- 7,86 +/- 2,66; Grupo C- 8,56 +/- 2,97, Grupo D- 7,99 +/- 2,12; Grupo E­ 11,46 +/- 1,96; Grupo F- 12,97 +/- 2,86, Grupo G-11 ,73 +/- 3,01 e Grupo H- 13,04 +/- 3,57. Não houve diferença estatística significativa entre 10 minutos e 24 horas (p<O,05) para todos os grupos testados e os sistemas adesivos autocondicionantes foram estatisticamente superiores aos demais sistemas adesivos (p<O,05). O padrão de fratura predominante para os grupos de ScotchBond Multi-Uso e Single Bond foi coesivo no adesivo! Camada híbrida e nos grupos dos sistemas autocondicionantes foi coesiva em dentina. Os sistemas adesivos convencionais ScotchBond Multi-Uso e Single Bond, e os sistemas autocondicionantes Clearfil Liner Bond 2V e Clearfil SE Bond, apresentaram zonas de interdifusão resina! dentina com características morfológicas distintas, tanto em relação à espessura quanto na formação dos prolongamentos resinosos decorrentes da penetração do adesivo nos túbulos dentinários / Abstract: The purpose of this study was to evaluate the tensile bond strength of conventional dentin adhesive systems and self-etching primers at 10 minute and 24 hours. Flat dentin surfaces were prepared on labial surface of 120 bovine lower incisor teeth and a 4-mm-diameter bonding area was demarcated on each prepared surface with adhesive vinyl tape. In the following groups were applied the dentin systems and the composite resin Z 100: Groups A and B ¿ ScotchBond Multi-Purpose Plus and Z 100; Groups C and O - Single Bond; Groups E and F­ Clearfil Liner Bond 2V and Groups G and H - Clearfil SE Bond. In the groups A, B, C and O ali dentin was etched with 35% phosphoric acid, washed and the excess of water was removed. A resin composite rod was positioned on the bonding area and cured for 20 s at the three points of the interface to perform the tensile bond strength (TBS). The TBS was tested at 10 minute to groups A, C, E and G. The groups B, O, F and H were stored in distilled water at 37°C and the TBS was performed after 24 h. An Instron testing machine was used with a cross-head speed of 0,5 mm/min for the tensile test. After the TBS, the fracture pattern was observed by SEM. The results were analysed by ANOVA and Tukey's test (p<0,05). The TBS results expressed by MPa were: Group A- 7.69 +/- 1.40; Group B­ 7.86+/- 2.66; Group C- 8.56+/- 2.97, Group 0- 7.99+/- 2.12; Group E- 11.46+/- 1.96; Group F- 12.97 +/- 2.86, Group G-11.73 +/-3.01 and Group H- 13.04 +/- 3.57. There was no statistically significant difference among the 10 min and 24h groups. The more frequently fracture pattern was cohesive on the adhesive system for the A,B, C and o; and the Groups E, F, G and H showed cohesive fracture of dentin. The TBS of ali dentin bonding systems were similar at 10 min and 24 h and the self etching primers showed the highest values of TBS. The conventional adhesive systems, ScotchBond Multi-Use Plus and Single Bond, and the self etching primers, Clearfil Liner Bond 2V and Clearfil SE Bond, showed distinct morphological characteristics at resin dentin interdifusion zones about their thickness and resin tags created because of the infiltration of the adhesive resin into the dentin tubules / Mestrado / Mestre em Materiais Dentários

Orientador : Lourenço Correr Sobrinho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T10:57:54Z (GMT). No. of bitstreams: 1 Fortuna_Sergio_M.pdf: 1973517 bytes, checksum: cf09d7d0d7be76d3db2c070c8f277af0 (MD5) Previous issue date: 2000 / Resumo: O propósito deste estudo foi avaliar a abrasividade de três dentifrícios comerciais sobre a região cervical (junção cemento-esmalte) de dentes pré-molares, provocada pela escovação mecânica. Foram utilizados 24 pré-molares superiores e inferiores, divididos em três grupos de oito. O terço apical da raiz foi seccionada com disco de diamante a fim de obter um corpo-de-prova com 15 mm de comprimento. Em seguida, os corpos-de-prova foram submetidos a 30.000 ciclos numa máquina de escovação Equilabor com os dentifrícios (Sorriso, Sensodyne e Colgate branqueador) e escova Oral-B 30. A rugosidade foi verificada com o aparelho (Suf-corder, SE 1700), antes e após os corpos-de-prova serem submetidos à escovação. Os resultados foram submetidos à análise de variância e ao teste de Tukey (5%) e indicaram que a escovação promoveu nos corpos-de-prova maior rugosidade com diferença estatística em relação aos corpos-de-prova sem escovação, para os três d_ntifrícios; os dentifrícios apresentaram diferentes. índices médios de abrasão, quando associados à escovação mecânica dos dentes; e, os dentifrícios Colgate branqueador e Sorriso foram significantemente mais abrasivos do que o dentifrício Sensodyne (p<0,05) / Abstract: The purpose of this study was to investigate the abrasivity of three dentifriees on the eervieal surfaee Ounetion eement-enamel) of the premolar teeth, by meehanie bruehing. Twenty four premolar were using in this study. The root was eut to got samples with 15 mm long. Afterwards the samples were submitted to 30,000 eycling in a brushing meehanie Equilabor with dentifriees (Sorriso, Sensodyne and Colgate branqueador) and toothbrushe Oral - B. Roughness was verified using (Surf-eorder, SE 1700) before and after toothbrushing. The results were submitted to varianee analyses and Tukey's test (p<0.05). The data indieated that the meehanie brushing showed more roughness with differenee statistieally in relation speeimens without brushing for the three dentifriees; the dentifriees showed differents abrasion when assoeiated to meehaniebrushing to the teeth; and, the dentifriees Colgate branqueador and Sorriso were signifieantly more abrasive than Sensodyne (p<0.05) / Mestrado / Mestre em Materiais Dentários