Made available in DSpace on 2015-04-22T22:08:45Z (GMT). No. of bitstreams: 1 Marcio Bartholomei.pdf: 2499347 bytes, checksum: 6b31cbfe2379597e5c48f869551b9c94 (MD5) Previous issue date: 2013-01-15 / Conselho Nacional de Desenvolvimento Científico e Tecnológico / Currently concrete performs a very important role in contemporary society´s development. Their benefits to society come from its variety of applications, being used in diverse types of constructions. Among the many kinds of existing concretes, the self-compacting one is highlighted once it is of a superior technology if compared to the ordinary one, once it doesn´t need a specific equipment to be compacted, having a self-compacting ability due to gravity. The aim of this work was studying the use of materials commercialized in Manaus and nearby locations for the production of self-compacting concrete with addition of ground glass´ waste. In this process great and tiny aggregates, cement, viscosity modifier of physical effect (ground glass´ waste) and superplasticizer additive were characterized according to Brazilian Standards (NBR). It was also analyzed the best dosage method for the ordinary concrete´s production, which also was adapted to the self-compacting production. 10 After choosing the best method for the ordinary concrete, this work developed a method so that self-compacting concrete could be produced using ground glass´ waste and local materials from Manaus city. The results showed that it is possible to obtain a self-compacting concrete from materials commercialized in Manaus and nearby locations, moreover, that the ground glass´ waste is a material which holds the self-compacting concrete properties in the cured stage having gains in resistance, and in the fresh state with viscosity increase, in which shortens its static and dynamic segregation. / Atualmente o concreto desempenha um papel muito importante no desenvolvimento de uma sociedade moderna. Seus benefícios para a sociedade vêm de sua ampla faixa de aplicações, sendo este usado em diversos tipos de construção. Dentre os diversos tipos de concretos existentes, destaca-se o concreto auto-adensável, que é uma tecnologia superior ao concreto convencional, pois o mesmo não necessita de nenhum equipamento para ser compactado, tendo uma capacidade de auto-compactação através da força da gravidade. O objetivo deste trabalho foi estudar a utilização de materiais comercializados na região de Manaus para a produção de concreto auto-adensável com adição de resíduo moído de vidro. Neste processo de estudo foram caracterizados os agregados miúdos, agregados graúdos, cimento, modificador de viscosidade de efeito físico (resíduo moído de vidro) e aditivo superplastificante conforme as Normas Brasileiras (NBR). Também foi analisado o melhor método de dosagem para a produção do concreto convencional, o qual 8 também se adaptava a produção do concreto auto-adensável. Após a escolha do melhor método para a produção do concreto convencional, foi desenvolvido neste trabalho um método para a produção do concreto auto-adensável utilizando resíduo de vidro moído e materiais regionais da cidade de Manaus. Os resultados mostraram que é possível obter um concreto auto-adensável empregando materiais comercializados na região de Manaus, além disso, que o resíduo moído de vidro é um material que mantêm as propriedades do concreto auto-adensável no estado endurecido com ganhos de resistência e no estado fresco com o aumento de viscosidade, a qual diminui a sua segregação estática e dinâmica.

Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-11T14:14:43Z No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_MaterialCompositoMatriz.pdf: 3287134 bytes, checksum: 7b7c1ee635985a997b7df99e008cd690 (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-23T12:34:35Z (GMT) No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_MaterialCompositoMatriz.pdf: 3287134 bytes, checksum: 7b7c1ee635985a997b7df99e008cd690 (MD5) / Made available in DSpace on 2014-06-23T12:34:35Z (GMT). No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Dissertacao_MaterialCompositoMatriz.pdf: 3287134 bytes, checksum: 7b7c1ee635985a997b7df99e008cd690 (MD5) Previous issue date: 2010 / Este estudo propõe avaliar o comportamento mecânico dos compósitos de matriz cimentícia reforçados com fibras de sisal e malva. Correlacionar o comportamento dos materiais com variação do tipo e do comprimento das fibras. O material base utilizado na fabricação do compósito foi cimento, areia, água e fibra de sisal e malva. Usou-se u traço 1 : 2 : 0,5 (cimento, areia e água), com adição de 1% de fibras em relação ao peso da mistura. As fibras foram previamente cortadas no comprimento de 15 mm e 25 mm e adicionadas manualmente à mistura. As correlações dos compósitos foram obtidos através do ensaio de flexão em três pontos, seguindo norma RILEM 49. As características micro-estruturais foram avaliadas através do uso do microscópio eletrônico de varredura.Os resultados obtidos indicam que a inserção de fibras na matriz cimentícia diminui a força máxima aplicada no corpo de prova, porém houve um ganho na tenacidade e na pseudo ductilidade do material após o aparecimento da 1ª trinca. As fibras mais longas mostraram melhor desempenho com um pequeno destaque às fibras de MALVA. / The purpose of this thesis is evaluate the mechanical behavior of cementitious matrix composites reinforced with sisal fibers and mauve, and correlate the material’s behavior with variations in the fibers types and lengths. The base material used in the manufacture of the composite was cement, sand, water and sisal fibers and mauve. It was used the trace 1: 2: 0,5 (cement, sand and water, respectively), with the addition of 1% in mass of fibers. The fibers had been previously cut in the length of 15mm e 25mm and manually added to the mix. The correlations of the composites were obtained by bending tests in three points, following the RILEM 49 norm. The micro-structural characteristics were evaluated with electron microscopy. The results show that the insertion of fibers in the cementitious matrix reduces the maximum force applied to the specimen, even tough there was an increase in the material toughness and pseudo-ductility after the appearance of the first fissure. The longest fibers demonstrated better performance with a small highlight on the mauve fibers.

Submitted by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2018-06-19T20:21:54Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação Parcial_Daiana Góes Cavalcante.pdf: 4388941 bytes, checksum: b6cd164bd266150cddd8926501d42b3b (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2018-06-19T20:22:05Z (GMT) No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação Parcial_Daiana Góes Cavalcante.pdf: 4388941 bytes, checksum: b6cd164bd266150cddd8926501d42b3b (MD5) / Made available in DSpace on 2018-06-19T20:22:05Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação Parcial_Daiana Góes Cavalcante.pdf: 4388941 bytes, checksum: b6cd164bd266150cddd8926501d42b3b (MD5) Previous issue date: 2017-10-30 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The present research presents the development and characterization of cementitious composites reinforced with jute and malva fibers textile. In order to increase the durability of these materials, a free matrix of calcium hydroxide was used, a degrading agent of natural fibers in a cementitious environment. The treatment of the textile was performed by the hornification process, aiming to reduce the fiber volume variation and consequently to improve fiber-matrix adhesion and durability. Reinforced cementitious plates with two layers of jute and malva textile were produced by a pneumatic system and exhibited double-cracked flexural tensile behavior for most experimental conditions (plates reinforced with treated and untreated textile and matrix of reference and modified by 40% metakaolin) at twenty and eight days. The composites reinforced with textile treated for 10 cycles of hornification, presented multiple cracking only in the middle third of the specimens. The durability of the composites was investigated by means of the accelerated aging process (50 wetting and drying cycles) and they were evaluated by tensile strength tests, microstructural analysis and physical characterization. In the composites with metakaolin, the hornified and untreated textile did not result a significant increase in flexural tensile strength (MOR) in relation to the reinforced reference matrix (about 6.5 MPa for all composites), however, those presented high specific energy (more than 100% increase). After aging, the matrix modified and reinforced with textile in both conditions (untreated and hornified) were efficient, since they preserved the mechanical characteristics, mainly MOR (6.5 MPa). This was not observed for the reinforced reference matrix, in this case, there was a 25% loss in resistance (MOR = 5.15 MPa). / A presente pesquisa apresenta o desenvolvimento e caracterização de compósitos cimentícios reforçados com tecido das fibras de juta e malva. Para aumentar a durabilidade destes materiais foi utilizada uma matriz livre de hidróxido de cálcio, agente degradador de fibras naturais em ambiente cimentício. O tratamento do tecido foi realizado pelo processo de hornificação, visando reduzir a variação volumétrica das fibras e consequentemente melhorar a adesão fibra-matriz e a durabilidade. Placas cimentícias reforçadas com duas camadas de tecido de juta e malva foram produzidas com o auxílio de um sistema pneumático. A durabilidade dos compósitos foi investigada por meio do processo de envelhecimento acelerado (50 ciclos de molhagem e secagem) e os mesmos foram avaliados pelos ensaios de resistência à tração na flexão, análise microestrutural e caracterização física. Para a maioria das condições experimentais (placas reforçadas com tecido não tratado e com matriz de referência e modificada por 40% de metacaulinita), as placas compósitas apresentaram comportamento à tração na flexão com dupla fissuração aos vinte e oito dias de cura. Os compósitos reforçados com tecido tratado por 10 ciclos de hornificação apresentaram múltipla fissuração apenas no terço médio dos corpos de prova. Nos compósitos com metacaulinita, os tecidos hornificados e não tratados não resultaram em um aumento significativo na resistência à tração na flexão (MOR) em relação à matriz de referência reforçada (cerca de 6,5 MPa para todos os compósitos), contudo, aqueles apresentaram alta energia específica em relação a este (acréscimo acima de 100%). Após o envelhecimento, a matriz modificada e reforçada com tecido nas duas condições (não tratado e hornificado) foram eficientes, pois preservaram as características mecânicas, principalmente o MOR (6,5 MPa). Isto não foi observado para a matriz de referência reforçada, neste caso, houve perda de 25% na resistência (MOR = 5,15 MPa).

Resíduos da área de engenharia civil decorrentes da recuperação de estruturas danificadas por agentes agressivos contribuem continuadamente para impactar o meio ambiente de maneira cada vez mais preocupante. O desenvolvimento de novas tecnologias que sejam aceitáveis do ponto de vista ambiental e financeiro provou ser um grande desafio na solução desse problema quando se compara o custo original e eficaz em médio e longo prazo ao custo da demolição, destinação desse material e reconstrução da obra. Para viabilizar a utilização de compósitos de fibras sintéticas como reforço resistente a ambientes agressivos em elementos de concreto, os aparatos de ensaio e os corpos de prova foram modificados e adaptados aos sistemas operacionais descritos pelas normas técnicas vigentes, a partir da concepção do uso de filamentos de fibra contínua. Dado o caráter inovador do trabalho, não se identificou uma norma que tratasse especificamente dos ensaios de flexão nem pullout com fibras contínuas em blocos de concreto. Portanto, para se conseguir um aproveitamento desse tipo de reforço que respondesse satisfatoriamente quando comparado às armaduras metálicas, foi aplicada uma rugosidade à superfície da haste para garantir sua aderência ao bloco de concreto. Pelo método de preparo de compósitos de matriz cimentícia proposto no presente estudo, foram determinados os valores da força de arrancamento dos reforços com fibras de carbono e vidro-AR, os quais, no caso das fibras de carbono, apresentaram aumentos significativos entre 76% e 158% e 47% e 120% respectivamente para concretos de resistência à compressão de 30 MPa (fcm 30) e 40 MPa (fcm 40) comparados com valores obtidos para barras de aço. / In Civil Engineering, the waste from the recovery of structures that were damaged by aggressive agents continuously contribute to impact the environment in an increasingly concerning way. The development of new technologies that would be environmentally and financially acceptable has become a major challenge to solve that problem when one compares the medium and long term original and effective cost to the cost of demolition, destination of that material and rebuilding. To enable the use of synthetic fiber composites as a resistant reinforcement to aggressive environments in concrete elements, the test apparatus and the specimens were changed and suited to the operational systems described by current technical standards from the conception of the use of continuous fiber filaments. Given the innovative character of the present work, no standard specifically related to bending and pullout tests with continuous fibers in concrete blocks has been identified. Therefore, in order to obtain good use of that kind of reinforcement that would respond satisfactorily when compared to metallic bars, some rugosity was applied to the rod surface in order to ensure its adherence to the concrete block. The preparation method of cement matrix composites proposed in the present work has determined pullout strength values and reinforcement with carbon and AR glass fiber values, which, regarding carbon fibers, showed significant increase between 76% and 158% and 47% and 120% respectively for compression resistant concrete of 30 MPa (fcm 30) and 40 MPa (fcm 40) compared to the obtained values for steel bars.

Resíduos da área de engenharia civil decorrentes da recuperação de estruturas danificadas por agentes agressivos contribuem continuadamente para impactar o meio ambiente de maneira cada vez mais preocupante. O desenvolvimento de novas tecnologias que sejam aceitáveis do ponto de vista ambiental e financeiro provou ser um grande desafio na solução desse problema quando se compara o custo original e eficaz em médio e longo prazo ao custo da demolição, destinação desse material e reconstrução da obra. Para viabilizar a utilização de compósitos de fibras sintéticas como reforço resistente a ambientes agressivos em elementos de concreto, os aparatos de ensaio e os corpos de prova foram modificados e adaptados aos sistemas operacionais descritos pelas normas técnicas vigentes, a partir da concepção do uso de filamentos de fibra contínua. Dado o caráter inovador do trabalho, não se identificou uma norma que tratasse especificamente dos ensaios de flexão nem pullout com fibras contínuas em blocos de concreto. Portanto, para se conseguir um aproveitamento desse tipo de reforço que respondesse satisfatoriamente quando comparado às armaduras metálicas, foi aplicada uma rugosidade à superfície da haste para garantir sua aderência ao bloco de concreto. Pelo método de preparo de compósitos de matriz cimentícia proposto no presente estudo, foram determinados os valores da força de arrancamento dos reforços com fibras de carbono e vidro-AR, os quais, no caso das fibras de carbono, apresentaram aumentos significativos entre 76% e 158% e 47% e 120% respectivamente para concretos de resistência à compressão de 30 MPa (fcm 30) e 40 MPa (fcm 40) comparados com valores obtidos para barras de aço. / In Civil Engineering, the waste from the recovery of structures that were damaged by aggressive agents continuously contribute to impact the environment in an increasingly concerning way. The development of new technologies that would be environmentally and financially acceptable has become a major challenge to solve that problem when one compares the medium and long term original and effective cost to the cost of demolition, destination of that material and rebuilding. To enable the use of synthetic fiber composites as a resistant reinforcement to aggressive environments in concrete elements, the test apparatus and the specimens were changed and suited to the operational systems described by current technical standards from the conception of the use of continuous fiber filaments. Given the innovative character of the present work, no standard specifically related to bending and pullout tests with continuous fibers in concrete blocks has been identified. Therefore, in order to obtain good use of that kind of reinforcement that would respond satisfactorily when compared to metallic bars, some rugosity was applied to the rod surface in order to ensure its adherence to the concrete block. The preparation method of cement matrix composites proposed in the present work has determined pullout strength values and reinforcement with carbon and AR glass fiber values, which, regarding carbon fibers, showed significant increase between 76% and 158% and 47% and 120% respectively for compression resistant concrete of 30 MPa (fcm 30) and 40 MPa (fcm 40) compared to the obtained values for steel bars.