Made available in DSpace on 2016-12-23T14:05:51Z (GMT). No. of bitstreams: 1 Ana Paula Milagres Trovao.pdf: 5557007 bytes, checksum: b2950e914a7a368c32f59e43ed00eb12 (MD5) Previous issue date: 2012-08-10 / The use of plaster in civil construction generates a large amount of waste, but it is a material that posses properties that makes it a highly competitive product. The main cause of the generation of this waste is the rapid hardening of the pastes. The incorporation of waste gypsum into the gypsum pastes results in an acceleration of the hardening process, which might increase the volume of residues generated. This dissertation aimed to develop procedure to incorporate the gypsum residue into plaster pastes without compromising the paste mechanical properties and, especially without accelerating its hardening process. Tests have been developed to evaluate the plaster pastes setting time, consistency, workability and temperature reading in the plaster pastes in the fresh state and evaluate the hardness and axial compressive strength in the hardened state. Tests results showed the viability of the incorporation of 5% gypsum waste in substitution of gypsum in the plaster paste when combined with borax retardant additive, which promoted extension of the workable time of the paste and an increase in the pastes mechanical properties / A utilização do gesso pela construção civil gera um grande volume de resíduos, no entanto é um material que apresenta propriedades que o torna altamente competitivo no mercado. A principal causa da geração desse resíduo é o rápido endurecimento das pastas. A incorporação de resíduo de gesso às pastas provoca a aceleração no processo de endurecimento, podendo aumentar ainda mais o volume de resíduos gerados. Essa dissertação teve como objetivo buscar a forma de incorporação do resíduo às pastas de gesso para revestimento de parede, sem comprometer suas propriedades mecânicas e principalmente não acelerar seu endurecimento. Foram realizados os ensaios de tempo de pega, consistência, consistência útil e leitura de temperatura nas pastas em seu estado fresco além dos ensaios de dureza e compressão axial destas no estado endurecido. Os ensaios apontaram a viabilidade da incorporação de 5% de resíduo de gesso em substituição do gesso quando associado ao aditivo retardador bórax, que promoveu ampliação do tempo de utilização da pasta e o aumento nas propriedades mecânicas ensaiadas

Made available in DSpace on 2014-06-12T17:37:02Z (GMT). No. of bitstreams: 2 arquivo2220_1.pdf: 5350178 bytes, checksum: d4a4325cd53be7393326f220a55b3d33 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2011 / Universidade Federal de Pernambuco / A influência de rotas termomecânicas na microestrutura e propriedades mecânicas do aço API 5L X70 foi estudada neste trabalho. Foram propostas 5 rotas onde todas iniciaram com aquecimento até 950°C, sendo mantidas por 15 minutos para completa austenitização, em cujas trajetórias envolviam: resfriamento em substrato metálico, resfriamento em água, deformação e banhos de chumbo. O material utilizado neste trabalho foi retirado de um tubo de aço API 5L X70 com espessura de 10,8 mm e diâmetro nominal de 20 para confecção dos corpos de prova a serem utilizados nos experimentos. Um conjunto de corpos de prova, depois de austenitizados, foram resfriados num substrato metálico a temperatura ambiente, outro resfriados em água a temperatura ambiente, outro laminados, sofrendo um redução de 15% na espessura, e em seguida resfriados em água a temperatura ambiente. Outro conjunto de corpos de prova foram laminados, reduzindo 15% na espessura, colocados em banhos de chumbo nas temperaturas de 450 e 550°C durante 15 segundos para decomposição isotérmica e, depois de tratados, sendo em seguida resfriados em água a temperatura ambiente. Amostras foram retiradas dos corpos de prova para metalografia e análise da microestrutura via microscopia óptica (MO) e microscopia eletrônica de varredura (MEV). Corpos de prova de tração e impacto Charpy foram confeccionados para realização dos ensaios mecânicos. O ensaio Charpy foi realizado em corpos de prova a 0°C e a temperatura ambiente (20°C). As fraturas geradas nos ensaios de tração e impacto Charpy foram analisadas por MEV. Na análise por MO das microestruturas produzidas, conseguiu-se visualizar apenas a presença de grãos ferríticos, todavia na análise por MEV detectou-se a formação de ferrita poligonal, ferrita acicular, ferrita granular, possíveis pontos de constituinte M/A e a presença de austenita retida. Os resultados de tração revelaram melhorias no limite de escoamento e ductilidade em relação ao material como recebido. Convém destacar as propriedades de tração alcançadas pelos corpos de prova austenitizados, laminados e resfriados em água, cuja microestrutura é composta principalmente de ferrita granular e ferrita acicular. Esta microestrutura proporcionou os melhores resultados de limite de escoamento e limite de resistência, onde foram verificados aumentos de 36,05 e 4,85% respectivamente, em relação ao material como recebido e assim, alcançando um valor de limite de resistência próximo àquele exigido ao aço API 5L X90. Além disso, esta rota produziu melhorias na energia absorvida no ensaio Charpy e, desta forma, propriedades otimizadas de resistência mecânica e tenacidade a fratura. Todas as rotas proporcionaram melhores valores de energia absorvida em relação ao material como recebido, exceto nos corpos de prova laminados e submetidos a banho de chumbo a 550°C. A análise de todas as fraturas revelou um mecanismo do tipo dúctil, com extensiva formação de alvéolos

Orientador: Peterson Luiz Ferrandini / Banca: Carlos Triveño Rios / Banca: Manoel Cleber de S. Alves / Resumo: A atual exigência de qualidade de grandes peças forjadas requeridas pelo mercado nos traz a necessidade de dominar completamente cada etapa do processo de produção das mesmas. O tratamento térmico de homogeneização, processo aplicado a lingotes utilizados na fabricação de cilindros de laminação de tiras a frio, tem como objetivo homogeneizar a microestrutura bruta de solidificação que irá sofrer um processo de conformação mecânica posterior, reduzindo o nível de microssegregações nas regiões interdentriticas da estrutura do lingote. Pode-se quantificar o impacto da temperatura e do tempo deste processo pela análise da microestrutura formada a partir de um resfriamento brusco em amostras retiradas de diferentes regiões do lingote. Este trabalho foi realizado a partir de um lingote de aço do tipo A2, fundido, de comprimento ~2 m e diâmetro ~1 m, a ser forjado e utilizado na fabricação de um cilindro de laminação. Foram retiradas e analisadas amostras da estrutura bruta de solidificação e também de amostras homogeneizadas e temperadas. As amostras foram retiradas na superfície do lingote, no meio raio e na região central; foram aplicados tratamentos térmicos a 1150°C e 1200°C, por 8 h, 16 h e 24 h. Foram utilizadas microscopia ótica e eletrônica de varredura. Como esperado, a estrutura bruta de solidificação apresentou altos níveis de segregação, principalmente na região central do lingote. O tempo de homogeneização de 8 h se mostrou insuficiente a despeito da temperatura utilizada. A temperatura de 1150°C é aceitável para tratamentos de 24 h e a completa homogeneização da estrutura só foi alcançada utilizando-se tratamento a 1200°C. A estrutura bruta de solidificação apresenta uma microestrutura heterogênea, caracterizada pelo aspecto dendritico. A estrutura homogeneizada e temperada apresenta microestrutura ... (Resumo completo, clicar acesso eletronico abaixo) / Abstract: The current requirement for large forgings quality required by the market brings the demand to manage completely each stage of the manufacturing process. The homogenizing heat treatment process applied in ingots used in the manufacture of cold rolling mill rolls aims to homogenize the microstructure of raw solidification that will suffer a subsequent mechanical forming process, reducing the level of microsegregations in interdentrite regions structure of the ingot. We quantified the effect of temperature and time of the process through the analysis of the microstructure formed after a sudden cooling, in samples taken from different regions of the ingot. This task was realized applying an A2 kind of steel, cast, length ~ 2 m, diameter ~ 1 m, to be forged and used in the manufacture of a rolling Mill rolls. Samples of the raw structure solidification and the homogenizations and tempered samples were taken and analyzed .The samples were taken at the ingot surface at the middle radius and the central region; Heat treatments were applied with temperatures between 1150°C and 1200°C through 8 h, 16 h and 24 h. Optical microscopy and scanning electron microscopy were used. As expected, the raw solidification structure showed high levels of segregation, especially in the central region of the ingot. The 8 h proved to be insufficient despite the temperature used. The temperature of 1150 ° C is acceptable for treatment of 24 h and complete homogenization of the structure was only achieved by using treatment at 1200 ° C. The raw structure of solidification has a heterogeneous microstructure, characterized by dendritic appearance. The homogenized and quenched structure resulted in a microstructure composed by austenite, grades of martensite, the solidification carbides and precipitates carbides during heat treatment / Mestre

Orientador: Marcelo dos Santos Pereira / Banca: Cristina de Carvalho Ares Elisei / Banca: Rosinei Batista Ribeiro / Resumo: O desenvolvimento do saços avançados de alta resistência tornou-se fundamental na produção de veículos com peso reduzido, seguros e mais econômicos, dentro do contexto daindústria automobilística. Dentre os aços avançados de alta resistência destacam-se os aços de fases complexas (CP) que são caracterizados por apresentarem alta conformabilidade e alta capacidade de absorção de energia e deformação. Eles são considerados aços multifásicos por apresentarem uma microestrutura complexa formada por ferrita, bainita, martensita e austenita retida. O trabalho tem por objetivo caracterizar a microestrutura do aço de fases complexas. Foram empregadas metalografia convencional e colorida, utilizando os reagentes químicos Nital, Metabissulfito de Sódio e LePera para a identificação das fases presentes no material. As análises da microestrutura final foram feitas via microscopia óptica, utilizando-se atécnica mais clássica que é a iluminação em campo claro, mas também foram utilizadas algumas técnicas diferentes tais como, iluminação em campo escuro,contraste por interferência diferencial (DIC) e método de luz polarizada.Os resultados mostraram que, de maneira qualitativa, para os ataques químicos com os reagentes Nital, Metabissulfito de Sódio e LePera se mostrarameficientes, pois pode-se identificar as fases presentes no aço CP; de maneira quantitativa, para o ataquefeito com Nital também se mostraram eficazes para as quatro condições de microscopia óptica,tais como iluminação em campo claro; em campo escuro; DIC e método de luz polarizada, porcausa da estabilidadedos valores para o cálculo das frações de área das fases presentes neste material / Abstract: The development of advanced high-strength steels became instrumental inthe production of vehicles with reduced weight, insurance, andmore economical, within the contextof the automobile industry.Among the advanced high-strengthsteels are steels complex phase (CP) that are characterized by having high formability and high energy absorption capacity anddeformation. They are considered multiphase steels for presenting a complex microstructure consisting of ferrite, Bainite, martensiteand retained austenite. The work aims to characterize the complexphase steelmicrostructure.Were employed conventional metallography and colorful, using chemical reagentsNital, sodium metabisulfite andLePera for identification of phases present in the material. The final microstructure analyses were made via optical microscopy, usingmore classicaltechnique that is the bright field lighting, but also some different techniques were used such as lighting in dark field, differential interference contrast (DIC)and method of polarized light. The results showed that, of qualitative way, for the chemical attacks with Nital reagents,sodium metabisulfite and LePera were efficient, as it can identify the phases present in the CP steel; quantitative manner,for the attack made with Nital also proved effective for the four conditionsof optical microscopy, such as bright field lighting; in dark field; DIC and method of polarizedlight, because ofthe stability ofthe values for the calculation of area fractions ofphases present in this material / Mestre

Orientador: Luis Rogerio de Oliveira Hein / Coorientador: Peterson Luiz Ferrandini / Banca: Marcelo dos Santos Pereira / Banca: Heloisa Andréa Acciari / Banca: Mirian de Lourdes Noronha Mota Melo / Banca: Rosinei Batista Ribeiro / Resumo: Ferramentas de processamento e análise digital de imagens foram desenvolvidas com a finalidade de avaliar a evolução da textura morfológica e cristalográfica da microestrutura da liga de alumínio 7075 sob diferentes níveis de deformação plástica por compressão uniaxial. Amostras da liga de alumínio 7075-T6 passaram por um processo de recozimento pleno seguido de um estágio de compressão uniaxial, obtendo níveis de deformações entre 25 e 65%. As microestruturas das amostras foram avaliadas em função dos parâmetros morfológicos dos precipitados, da reorientação dos planos cristalográficos dos grãos e da orientação das subestruturas formadas durante o processo de deformação. Para a caracterização foram utilizadas técnicas de difração de raios-X, microscopia eletrônica, microscopia óptica utilizando técnicas de polarização linear e circular, microscopia correlativa e processamento digital de imagens. Os resultados de difração de raios-X indicaram uma reorientação do plano cristalográficos (200) para o (220) após a deformação, e as técnicas de microscopia eletrônica identificaram precipitados de Mg2Si, Al7Cu2Fe e Al6(FeCu) na liga. A análise morfológica dos precipitados indicou uma maior fragmentação dos precipitados devido à maior ativação do plano (331) a partir de 39% de deformação. Por meio do processamento de imagens foi encontrada uma tendência de correlação entre os planos cristalográficos e a fração de área das fases, enquanto que os parâmetros morfológicos das subestrutur... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Digital image processing and analysis tools were developed to perform the AA 7075 crystallographic and morphologic texture evaluation under different level of plastic deformation by uniaxial compression. Samples of AA 7075-T6 were submitted to full annealing process followed by uniaxial compression, thus obtaining deformations between 25 and 65% of thickness. The samples microstructure evaluation was performed considering: precipitates morphological parameters, crystallographic lattices reorientation and deformation substructure orientation. The characterization technics were: X-ray diffraction, electron microscopy, optical microscopy with polarization light, correlative microscopy and digital images processing. Xray diffraction results showed that the crystallographic plane (200) was reoriented to (220) after compression. The EDS analysis identified precipitates of Mg2Si, Al7Cu2Fe e Al6(FeCu). The precipitates morphological analysis showed an increase in fragmentation due to plane (331) at 39% of deformation. The digital image process of the samples etched with Barker reagents indicated a correlation between area fraction and the diffraction peaks, and the deformation substructures analysis made viable a qualitative characterization of the hardening process / Doutor

Orientador: Ana Paula Rosifini Alves Claro / Coorientador: Luiz Rogério de Oliveira Hein / Banca: Angelo Caporalli Filho / Banca: Maria Ismênia Sodero Toledo Farria / Resumo: Ligas de titânio são utilizadas para aplicações biomédicas devido as excelentes propriedades como a alta resistência à corrosão, biocompatibilidade e propriedades mecânicas. No presente trabalho, foram analisadas as microestruturase as propriedades mecânicas daliga Ti-30Ta e em amostras deformadas com diferentes graus de compressão. A liga foi obtida pela fusão dos metais puros em um forno a arcovoltaico com atmosfera inerte de argônio. O material obtido foi homogeneizado em um forno tubular a 1000 °C por 24 h e deformadas a friopelo processodeforjamento rotativo para obter barras de 13 mm de diâmetro. A liga foi avaliada utilizadastécnicas de difração de raios-X (DRX) em temperatura ambiente e com aquecimento, calorimetria diferencial de varredura(DSC), microscopia eletrônica de transmissão (TEM), microdureza e compressão de corpos de provas em diferentes graus de deformação. As amostras foram deformadas com taxas graus de 19%, 22% e 43% e analisadas, usando as técnicas de DRX,microscopia óptica, microdureza. A liga apresentou transformação alotrópica a uma temperatura próxima de 650°C, e microestrutura do tipo α', a deformação da amostra resultou em cisalhamento na amostra de 43%, as amostras apresentaram microdureza de 250, 269, 286 e 280HV para as amostras sem deformação, 19%, 22%e 43% de deformação / Abstract: Titanium and its alloys have been used for biomedical applications due their excellent properties, such as high corrosion resistance, biocompatibility and mechanical proprieties. In this work, the microstructure and mechanical proprieties of Ti-30Taand deformeds amples with different degrees of compression were analyzed The in gots were obtained in a arc melting furnace inan argon atmosphere. In gots were homogenized at 1000 ºCin a tubular furnace with argon atmosphere for 24 hours and than they were cold worked by swaging. and samples with 13 m mindiameter were obtained. The alloy was evaluated by X-raydiffraction (XRD), Heat treatment X ray diffraction (HTXRD)and differential scanning calorimetrical (DSC), transmission electron microscopy(TEM), micro hard nessand compression test with different deformations. The samples were forging at reductionratiosof 19%, 22% and 43%. After this deformation,its microstructure were evaluated by optical microscopy, X-ray diffraction(XRD)and micro hardness in each condition. The alloy show a allotropic transformation at 650 °C, and α' microstructure. The sample that was compressed with 43% shear and the others samples ( 19%, 22%) don't change their microstructure. the samples without deformation, 19%, 22% and 43% result 250, 269, 286, 280 HV / Mestre

Orientador: Élson de Campos / Coorientador: Francisco Cristóvão Lourenço de Melo / Banca: Miguel Angel Ramirez Gil / Banca: José Vitor Candido de Souza / Banca: Luis Antonio Genova / Banca: Sebastião Ribeiro / Resumo: O objetivo deste trabalho foi a produção e caracterização microestrutural, mecânica e fractografica de rochas sintéticas, obtidas por fabricação, a partir da mistura de resíduos dos pós de granito e vidro comercial. Esta pesquisa foi dividida em duas etapas. Na primeira etapa, a meta foi determinar a composição a ser utilizada na mistura e a temperatura de sinterização que produzisse uma rocha sintética com maior resistência mecânica e menor consumo de energia. Nesta fase foram definidas duas composições para produção das amostras: a primeira com massa de 1/3 de pó de granito, 1/3 de pó de vidro âmbar e 1/3 de pó de vidro transparente e uma segunda composição, com 60% de pó de granito, 30% de pó de vidro âmbar e 10% de pó de vidro transparente. Tais amostras foram sinterizadas em temperaturas que variaram de 800ºC a 1100ºC, e com base nos resultados obtidos pelo ensaio de flexão de três pontos, foi determinada para primeira composição, uma temperatura de sinterização de 850ºC e para a segunda 1050ºC. Na segunda etapa da pesquisa, aprofundou-se os estudos com relação às rochas sintéticas obtidas, realizando-se medidas de rugosidade, resistência a flexão, tenacidade a fratura pelo método SEVNB (Single-edge V-notch Beam), microdureza, molhabilidade e porosidade aparente. Além de difração de raios X, microscopia eletrônica de varredura e análise termogravimétrica e calorimetria diferencial de varredura. Os resultados obtidos nesta segunda etapa foram comparados com o granito comercial "andorinha" e mostraram que as rochas sintéticas obtidas são altamente promissoras e viáveis. As rochas sintéticas produzidas a partir das duas composições, apresentam menores valores de molhabilidade e porosidade e maiores valores de tensão de ruptura à flexão e microdureza, quando comparados as amostras do gra... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: This paper was intended to produce and characterize synthetic rocks in a microstructural, mechanical and fractographic way. Such rocks were obtained from the mixture of commercial glass waste and granite powder. This research was divided in two steps: in the first one it was to determined the amount of materials used in the mixture and the sintering temperature in order to produce synthetic rocks with higher mechanical strength and lower energy consumption, while in the second the synthetic rocks were submited to some tests, such as roughness measurement, flexural strength, fracture toughness by the SEVNB method, hardness, wettability and apparent porosity. In this first step two compositions were defined in order to produce the samples. The first composition contained 1/3 of granite powder, 1/3 of ambar glass waste and 1/3 of transparent glass waste; the second one contained 60% of granite powder, 30% of ambar glass waste and 10% of transparent glass waste. It was also determined the sintering temperature: 850ºC for the first composition and 1050ºC for the second one. Other tests, such as: X-ray diffraction, scanning electron microscopy, thermogravimetric analysis and differential scanning calorimetry were also performed. The results of the experiments in the second step were compared to "andorinha", an ordinary kind of Brazilian gray granite and showed that synthetic rocks are very promising and viable. Synthetic rocks presented lower wettability and porosity values and higher flexural strength and hardness values, when compared to the samples of "andorinha". It could be concluded that the first composition was the most relevant from the commercial point of view (1/3 of granite powder, 1/3 of ambar glass waste and 1/3 of transparent glass waste) for it presents higher flexural strength value and lower sintiring temperature value. This represents a considerable economic gain / Doutor

nÃo hà / CoordenaÃÃo de AperfeiÃoamento de Pessoal de NÃvel Superior / Ce travail a pour but principal la construction d'une base de donnÃes de collocations du portugais brÃsilien. Soutenu par la phrasÃologie thÃorique, qui traite de l'Ãtude des combinaisons polilexicais d'une langue naturelle cristallisÃe par tradition culturelle et stockÃe en bloc par les locuteurs de cette langue sans rÃgles de valeurs gÃnÃrales nÃcessairement qu'ils sont appliquÃs, nous avons choisi de rÃflÃchir spÃcifiquement sur ces phrasÃologismes qui se comportent comme le linguiste britannique Firth (1957) a appelà le collocations, catÃgorie phrasÃologique qui est, en fin de compte, les co-occurrences lexicales-syntaxiques habituelles, dont l'association est donnÃe de faÃon arbitraire et idiosyncratique. De cet objectif plus large, il y a des prÃoccupations de divers ordres. Parmi les consÃquences les plus immÃdiates, nous nous concentrons d'une part a ce qui concerne la typologie syntaxique consolidÃe dans la littÃrature (notamment Mel'čuk (1995), Tutin et Grossmann (2002), Corpas Pastor, Koike (2001), le cÃtà dâici l'Atlantique, FulgÃncio (1998), Tagnin (1989; 2005; 2011), AraÃjo Vale (2001)), qui a abouti à notre proposition pour l'organisation de la macrostructure syntaxique du CPB en simple, superposà et complexe. Nous pensons que les ÃlÃments collocationelles ne sont pas prÃsents de maniÃre homogÃne de faÃon à recevoir le mÃme traitement thÃorique et descriptive en termes structurels, le positionnement construit à partir de la confrontation entre les instances collectÃes. D'autre part, les ÃvÃnements signalÃs caractÃristiques de composition d'ordre syntaxique-sÃmantique-discursive qui a organisà en termes de 19 propriÃtÃs microstructurales de CPB. Le retour à la dÃfinition du phÃnomÃne prÃsentà comme rÃsultat impÃratif de la physiologie des occurrences compris ici comme collocations, de sorte que, en Ãlargissant le champ d'horizon du phÃnomÃne collocationlle en termes d'expression, redÃfini leur plan conceptuel, le point axial dont il dÃrive la classe de l'unitÃ. En tant que rÃsultat d'un travail thÃorique et descriptive, nous avons ouvert la base de donnÃes des emplacements des Portugais du BrÃsil. / O presente trabalho tem por fito maior a construÃÃo de uma base de dados de colocaÃÃes do portuguÃs brasileiro. Sustentado pela catedral teÃrica da Fraseologia, a qual se ocupa do estudo das combinaÃÃes polilexicais de uma lÃngua natural cristalizadas pela tradiÃÃo cultural e memorizadas em bloco pelos falantes dessa lÃngua sem que necessariamente lhes sejam aplicadas regras de valores gerais, elegemos para reflexÃo especificamente aquelas unidades fraseolÃgicas que se comportam como o que o linguista britÃnico Firth (1957) chamou de colocaÃÃo (collocations), categoria fraseolÃgica que trata, em Ãltima instÃncia, de coocorrÃncias lÃxico-sintÃticas habituais, cuja associaÃÃo se dà arbitrÃria e idiossincraticamente. Desse objetivo maior, surgem inquietaÃÃes de vÃrias ordens. Entre os desdobramentos mais imediatos, concentramo-nos, de uma parte, naquele respeitante à tipologia sintÃtica consolidada na literatura especializada (notadamente Melâčuk (1995), Tutin e Grossmann (2002), Corpas Pastor, Koike (2001); do lado de cà do atlÃntico, FulgÃncio (1998), Tagnin (1989; 2005; 2011), AraÃjo Vale (2001)), que culminou em nossa proposta de organizaÃÃo sintÃtica macroestrutural das CPB em simples, superposta e complexa. Sustentamos que os elementos colocacionais nÃo se apresentam homogeneamente a ponto de receberem o mesmo tratamento teÃrico-descritivo em termos estruturais, posicionamento construÃdo a partir do confronto entre as ocorrÃncias coletadas. De outra parte, as ocorrÃncias sinalizavam particularidades composicionais de ordem sintÃtico-semÃntico-discursiva as quais organizamos em termos de 19 propriedades microestruturais das CPB. O retorno à definiÃÃo do fenÃmeno se nos apresentou como imperativo, consequÃncia da fisiologia das ocorrÃncias entendidas aqui como colocaÃÃes, de modo que, ao alargar o horizonte de escopo do fenÃmeno colocacional no plano da expressÃo, redefinimos seu plano conceitual, ponto axial donde se deriva a unidade da classe. Como resultado desse trabalho teÃrico-descritivo, inauguramos a base de dados das colocaÃÃes do portuguÃs do Brasil.

Os aços da classe SAE 5120 são largamente utilizados para a produção de eixos e engrenagens de caixas de transmissão. As adições de nióbio e boro neste aço visam modificar a microestrutura e, consequentemente, alteram as propriedades metalúrgicas e mecânicas deste aço. Adições de nióbio ancoram o crescimento de grão austenítico, permitindo um aumento de produtividade no processamento visto que temperaturas de laminação e de tratamento térmico mais elevadas podem ser aplicadas sem que ocorra o crescimento de grão austenítico. O boro encontra-se tanto na forma solúvel como nãosolúvel nos aços. O boro solúvel aumenta a temperabilidade, devido à segregação deste elemento durante a solidificação nos contornos de grãos, retardando a nucleação da ferrita. O boro não-solúvel (combinado) também contribui para o ancoramento dos contornos de grãos austeníticos, visto que este se combina com o nitrogênio formando o BN cuja temperatura de solubilização é por volta de 1360ºC. O objetivo principal foi avaliar a cinética de transformação do aço SAE 5120 com a adição simultânea de boro e nióbio por meio da curva de transformação por resfriamento contínuo (CCT) a partir do campo austenítico (930oC). As amostras foram caracterizadas por microscopia óptica e microscopia eletrônica de varredura e por ensaios de dureza, possibilitando a construção da curva CCT para diferentes taxas de resfriamento. Na análise metalográfica observou-se a segregação de manganês e cromo da matéria-prima (estrutura bandeada) e a forte tendência de formação da bainita. Com o auxílio do programa de simulação termodinâmica computacional Thermocalc, foi possível simular as fases termodinamicamente estáveis, verificando que o boro e o nióbio formam precipitados estáveis em altas temperaturas (acima de 1150ºC), sendo os principais responsáveis pelo refino de grão. A temperabilidade e comportamento mecânico foram avaliados pelos ensaios Jominy e o ensaio de impacto Brugger, respectivamente. A influência dos elementos de liga nestes ensaios foi avaliada através de método de regressão linear por meio do software Minitab. / SAE 5120-alloyed steel is largely used to manufacture transmission gears and shafts for automotive industry. Alloying with niobium and boron is intentionally made to modify the microstructure and, consequently, promoting changes in metallurgical and mechanical proprieties. Alloying with niobium prevents austenitic grain growth (pinning effect), leading to an increase of productivity since higher rolling mill and heat treatment temperatures can be achieved. Boron can be found either soluble or insoluble in steels. Soluble B increases hardness, because it segregates to grain boundaries retarding the nucleation of ferrite. Insoluble B, on the other hand, also plays a role on avoiding austenitic grain growth due to its chemical reaction with N forming BN whose solubility temperature is around 1360ºC. The main target of this work was to evaluate the kinetics of phase transformations by continuous cooling transformation (CCT) from the austenitic field (930oC). The microstructure was analyzed by optical microscope, scanning eléctron microscope (SEM), and hardness testing, allowing building the CCT diagram with different cooling rates. It was observed by means of conventional metallography the segregation of Mn and Cr (banding) during solidification of the raw material and a strong propensity to form bainite. Using the Thermocalc software, it was possible to predict the thermodynamically stable phases, proving that boron and niobium form stable precipitates at high temperatures (above 1150ºC) responsible to decrease austenitic grain size. The hardenability and mechanical properties were investigated by Jominy and Brugger impact tests, respectively. The effect alloy adding in these tests were analyzed by linear regression in the software Minitab.

Superligas à base de níquel vêm sendo extensivamente utilizadas em diversas aplicações nas indústrias devido ao excelente comportamento mecânico e anticorrosivo. No entanto, essas ligas possuem certas particularidades que levam à necessidade de desenvolvimento de técnicas de inspeção e caracterização metalúrgica, como forma de garantir a integridade estrutural dos componentes fabricados com essas ligas. Neste trabalho, a técnica de correntes parasitas foi aplicada à superligas à base de níquel com duas propostas distintas: 1) Em um primeiro momento foi realizado o estudo da evolução microestrutural da liga Inconel 718 durante o processo de envelhecimento através da combinação do ensaio por correntes parasitas, análise de difração de raios-X, análise metalográfica, medidas de dureza e tamanho de grão. As medidas foram realizadas em amostras submetidas a diferentes ciclos de tratamentos térmicos variando entre 620-1035°C. Os resultados mostraram que as diferentes microestruturas do Inconel 718 têm efeitos distintos na condutividade elétrica quando medidos através da técnica de correntes parasitas. A influência da microestrutura na condutividade pode ser mostrada sendo devido à competição de dois efeitos sobre o espalhamento de elétrons: a purificação da matriz e a morfologia, distribuição e tamanho dos precipitados. A combinação dos valores de dureza e condutividade elétrica provou ser uma forma rápida e prática de determinar o nível de envelhecimento da liga; 2) Em um segundo momento foi desenvolvido um processo de otimização de sensores através de modelagem por elementos finitos (MEF). Através de uma metodologia de otimização, os parâmetros de construção e operação de um sensor foram otimizados para inspeção de defeitos superficiais e subsuperficiais esperados em materiais cladeados com Inconel 625. O sensor com a geometria ótima foi construído e testado a fim de verificar a eficiência do processo de otimização. Uma ótima correlação entre os resultados numéricos e experimentais foi encontrada e o sensor ótimo se mostrou eficiente na inspeção de pequenos defeitos superficiais e subsuperficiais na liga Inconel 625 quando operado nas frequências apropriadas. / Nickel-based superalloys have been extensively used in various industries due to its unique mechanical and corrosion behavior. However, these alloys show particular characteristics which lead to the need for specific inspection and metallurgical characterization techniques in order to ensure the structural integrity of components manufactured from these alloys. In this work , the eddy current technique was applied to nickel-base superalloys with two aims: 1 ) Firstly, the microstructural evolution of Inconel 718 during aging processes has been studied through a combination of eddy current testing, X-ray diffraction analysis, metallography, hardness and grain size measurements. Measurements were carried out in samples subjected to different heat treatment cycles between 620-1035°C. Results show that different microstructures of Inconel 718 have a distinguishable effect on electrical conductivity when this is measured through an appropriately sensitive technique (i.e. eddy current testing). The influence of microstructure on conductivity could be shown to be due to the competition between two effects on the scattering of electrons: matrix purification and precipitate size, distribution and morphology. A combination of hardness values and electrical properties proved to be a fast and practical way of determining the stage of aging of the alloy; 2) An optimization method of eddy current sensor design was developed through finite element modeling (FEM). Through a methodology of optimization, the construction and operation parameters of the sensor were optimized for inspection of superficial and subsuperficial defect, commonly found in weld overlay Inconel 625 claddings. A prototype of this sensor with the optimum geometry was built and tested on blocks identical to those considered in the models in order to verify the efficiency of the optimization process. A very good agreement between numerical and experimental results was found. Moreover, the optimal sensor was efficient to detect small surface and subsurface defects in Inconel 625 when operated at appropriate frequencies.