Orientador : Renato Sussumu Nishioka / Mestre

Orientador: Osvaldo Magro Filho / Resumo: A adaptação entre a plataforma do implante e seu respectivo abutment deve ser precisa, isto é, sem nenhuma fenda, que é denominada microgap, entre as estruturas. A presença do microgap permite que microorganismos presentes na microbiota bucal migrem para o interior do implante, o que pode ocasionar problemas de natureza inflamatória e ou infecciosa, e, conseqüentemente, causar a perda do implante. Neste estudo utilizamos uma amostragem de 26 (vinte e seis) implantes e seus respectivos abutments provenientes de 5 (cinco) marcas comerciais diferentes: AS Tecnology, Conexão Sistema de Prótese, Neodent Implante Osteointegrado, Sterngold Implamed, e 3i Implant Innovation. Os abutments receberam um torque de 20Ncm. Os cortes longitudinais da interface implante/abutment foram mensurados em 6 (seis) locais com o auxílio da microscopia eletrônica de varredura. Os resultados das mensurações foram submetidos à análise estatística. Foi possível concluir que: 1) A seqüência dos grupos, em relação ao gap encontrado, do menor para o maior, foram: abutment cônico, abutment gold ucla, abutment mult unit. 2) O abutment cônico e o abutment mult unit apresentaram gaps menores que o abutment gold ucla. 3) O ponto interno apresentou gap menor em relação ao ponto médio, o qual foi menor que o ponto externo, portanto, as peças tenderam a convergir para o ponto interno. / Abstract: The adaptation of the implant platform and its respective abutment must be precise, with no space denominated microgap, between the structures. The presence of a microgap allows microorganisms that are present in the buccal microbiology to migrate into the implant, what could cause inflammatory and/or infectious problems, and consequent loss of the implant. In this study, a sample of 26 (twenty six) implants and their respective abutments was taken: conic, multi unit, and the gold ucla - together with their respective fixing screws. The abutments received a manual torque of 20Ncm. After the manual preparation, the interface implant/abutment longitudinal cuts were measured on 6 (six) different points through an Scanning Electron Microscope (SEM). The results of such measurements were statistically analyzed, and according to the experimental conditions of this study, was possible to conclude: 1) The sequential groups of implants/abutments, in relation to the gap found, from the smaller to the biggest, were: a) conic abutment , b) gold ucla abutment , c) multi unit abutment. 2) The conic and the multi unit abutments showed smaller gaps than the gold ucla abutments. 3) The internal point showed a smaller gap than the middle point, and the middle point, in return, also showed a smaller gap in relation to the external point; therefore, the pieces tended to converge to the internal point. / Mestre

Orientador: Eduardo César Almada Santos / Banca: Arnaldo Pinzan / Banca: André Luiz Fraga Briso / Banca: Marcos Rogério de Mendonça / Banca: José Luiz Cintra Junqueira / Resumo: A proposta deste estudo foi avaliar, por meio de microscopia eletrônica de varredura (MEV), a interface adesiva existente após a descolagem de acessórios ortodônticos, fixados em dentes bovinos com emprego de um sistema adesivo hidrófilo e um hidrofóbico, em distintas condições de umidade do substrato dental. Foram utilizados 20 incisivos inferiores bovinos, divididos em 4 grupos (n=5), sendo que: G I- empregou-se o sistema de colagem ortodôntica contendo o primer hidrofílico Transbond MIP e a pasta adesiva Transbond XT, aplicados em substrato úmido; G II- o sistema de colagem ortodôntica hidrofóbico composto pelo primer Transbond XT e pela pasta adesiva que completa o sistema foi aplicado nas mesmas condições. Já os espécimes dos grupos III e IV receberam a colagem dos bráquetes com os mesmos sistemas de união, no entanto o esmalte dental apresentava-se seco. Em seguida, os acessórios foram removidos e a interface adesiva, bem como a interação dos sistemas adesivos ao esmalte dental foram avaliados em microscópio eletrônico de varredura em diferentes amplitudes. As imagens obtidas foram avaliadas qualitativamente, observando-se bom embricamento mecânico para o adesivo hidrófilo em quaisquer condições de substrato, enquanto que os espécimes que empregaram o sistema hidrofóbico obtiveram condições de interface favoráveis somente quando aplicado em substrato seco. Concluiu-se que o adesivo hidrofílico é menos sensível às condições de unidade, possibilitando boa interação micromecânica ao esmalte dental condicionado. / Abstract: The purpose of this study, was evaluate at the scanning electron microscopy (SEM), the interface adhesive, after the orthodontic bracket debonding, set in bovine tooth with employ adhesive system hydrophilic and hydrophobic, in different conditions the humidity of the substrate. Twenty bovine incisors were divided into four groups (n=5), since Group l: Employed is the system orthodontic bracket bonding containing the hydrophilic primer Transbond MIP and the adhesive paste Transbond XT, applied in humidity substrate. Group ll: the hydrophobic primer system Transbond XT orthodontic bonding and the adhesive paste that complete system it was applied under the same conditions. Already the specimens of the groups III and IV received the system orthodontic bracket bonding with the same bonding system, however the dental enamel presented itself dry. Then the acessories have been removed, and the interface adhesive and the interaction of adhesive systems the dental enamel was to evaluate through Scanning Electronic Microscopy (SEM), and the differents amplituds. The images obtained were evaluated qualitatively and there is good mechanical interation for hidrophylic adhesive in any conditions of substrate while the specimens we employed the system hydrophobic received favorable conditions for the interface only when applied to substrate dry. It is concluded that the adhesive hydrophilic primer is less sensitive in conditions of humidity, allowing good interaction micromechanics to dental enamel conditioning. / Doutor

Orientador: Ariel Antonio Mendes / Coorientador: Márcia Regina Fernandes Boaro Martins / Banca: José Roberto Sartori / Banca: Rodrigo Garófallo Garcia / Resumo: Com objetivo de avaliar a integridade intestinal, por meio da microscopia óptica e eletrônica de varredura (MEV), e o desempenho de frangos de corte suplementados com aditivos alternativos aos antimicrobianos foram alojados 1080 pintos machos, com densidade populacional de 12 aves/m². O delineamento experimental foi o inteiramente casualizado, com seis tratamentos e seis repetições de 30 aves cada. Os tratamentos foram: dieta basal (controle); dieta basal mais antimicrobiano; dieta basal mais probiótico; dieta basal mais prebiótico; dieta basal mais simbiótico e dieta basal mais ácidos orgânicos. Foram avaliados o ganho de peso, consumo de ração, conversão alimentar e viabilidade aos 10, 21, 35 e 42 dias de idade. Aos 42 dias, 72 aves (duas aves por repetição de cada tratamento) foram pesadas individualmente e eutanasiadas. Para avaliação da morfometria das diferentes túnicas da parede intestinal foram coletados segmentos do intestino delgado e cecos de duas aves por repetição e para as análises da integridade intestinal (MEV) foram coletados os mesmos segmentos de duas aves por tratamento. No período inicial de criação as aves suplementadas com os aditivos alternativos mostraram ganho de peso similar àquelas tratadas com antimicrobiano, porém não diferiram do grupo controle. A conversão alimentar das aves que receberam aditivos alternativos no intervalo de 1 a 10 dias foi melhor que o controle, porém para os demais períodos de criação a conversão alimentar foi similar ao antimicrobiano sem, contudo diferir do controle. A morfometria das diferentes túnicas da parede intestinal das aves não foi influenciada pelos tratamentos. No período total de criação, os aditivos alternativos avaliados não melhoraram a integridade intestinal, bem como o desempenho dos frangos de corte / Abstract: In order to evaluate the intestinal integrity, through optical microscopy and scanning electronic (SE), and the performance of broilers receiving diets supplemented with additives instead of antimicrobial growth promoters 1080 male chicks were allocated in a population density of 12 birds / m2. The experimental design was a completely randomized arrangement with six treatments and six replications of thirty birds each. The treatments were: basal diet (control); basal diet + antimicrobial growth promoter (AGP); basal diet + probiotic; basal diet + prebiotic; basal diet + symbiotic; and basal diet + organic acids. The weight gain, feed intake, feed:gain ratio and the viability at days 10, 21, 35 and 42 were evaluated. At 42th day, 72 birds (two birds per replicate of each treatment) were individually weighted and sacrificed. For morphometric evaluation of different tunics of intestinal wall, small intestine and caecum fragments from 2 birds per repetition were collected and for intestinal integrity analysis (SE) the same fragments were collected from 2 birds per treatment. At the first period of breeding alternative additives-fed chickens showed similar weight gain compared to AGP-fed chickens, but they did not differ from control group. The feed:gain of alternative additives-fed chickens from 1st to 10th days was better than control group, but for the others periods the feed:gain ratio was similar to AGP-fed birds, without differing from control group. The morphometric of different tunics of intestinal wall was not influenced by treatments. The alternative additives did not improve the intestinal integrity, neither the broiler performance during the whole breeding period / Mestre

Orientador: Antonio Carlos Ferreira Seridonio / Co-orientador: Ezequiel Costa Siqueira / Banca: João Carlos Silo Moraes / Banca: Eduardo Miranda / Resumo: Foi estudado teóricamente a densidade local de estados (LDOS), por meio de uma ponta de STM, de sistemas bidimensionais hospedando um adatom e uma segunda impureza localizada abaixo da superfície hospedeira, ambos capacitivamente acoplados a pontas de AFM e atravessados por campos magnético antiparalelos. São analisados dois sistemas, uma monocamada de grafeno e um gás de elétrons bidimensional (2DEG). As pontas de AFM ajustam os níveis das impurezas com respeito à energia de Fermi, onde dois comportamentos constrastantes emergem: o fator de Fano para o grafeno diverge, enquanto no 2DEG ele se aproxima de zero. Como resultado, a degenerescência de spin da LDOS é levantada exclusivamente no sistema do grafeno, em particular para o regime assimétrico da interferência Fano. O resultado deste limite é um fenômeno não intuitivo, que consiste de um fator de Fano dominante devido à impureza que se encontra abaixo do plano de grafeno, mesmo com um forte acoplamento entre a ponta do STM e o adatom. Assim, foi obtida uma condutância completamente polarizada, por meio do deslocamento vertical da posição da ponta de STM. Para melhor conhecimento, este trabalho é a primeira proposta que utiliza o efeito Fano como mecanismo para filtrar spins no grafeno. Esta característica surge a partir de elétrons de Dirac que se comportam como se não tivessem massa, por conta da estrutura de bandas do grafeno, e nos permite empregá-lo como um filtro de spins relativístico Fano / Abstract: We explore theoretically the density of states (LDOS) probed by an STM tip of 2D systems hosting an adatom and a subsurface impurity, both capacitively coupled to AFM tips and traversed by antiparallel magnetic fields. Two kinds of setups are analyzed, a monolayer of graphene and a two-dimensional electron gas (2DEG). The AFM tips set the impurity levels at the Fermi energy, where two contrasting behaviors emerge: the Fano factor for the graphene diverges, while in the 2DEG it approaches zero. As result, the spin-degeneracy of the LDOS is lifted exclusively in the graphene system, in particular for the asymmetric regime of Fano interference. The aftermath of this limit is a counterintuitive phenomenon, which consists of a dominant Fano factor due to the subsurface impurity even with a stronger STMadatom coupling. Thus we find a full polarized conductance, achievable just by displacing vertically the position of the STM tip. To the best knowledge, our work is the first to propose the Fano effect as the mechanism to filter spins in graphene. This feature arises from the massless Dirac electrons within the band structure and allows us to employ the graphene host as a relativistic Fano spin-filter / Mestre

Orientador : Estevão Tomomitsu Kimpara / Doutor

Orientador: Marcelo Ferrarezi de Andrade / Banca: Hugo Henrique Alvim / Banca: Victor Humberto Orbegoso Flores / Banca: Edson Alves de Campos / Banca: José Roberto Cury Saad / Resumo: O presente trabalho propõe avaliar a utilização de clorexidina e laser de Er,Cr:YSGG no processo de adesão em cavidades mistas hígidas e afetadas por cárie em relação a adaptação externa de restaurações classe V submetidas a ciclagem térmica. Foram realizados preparos cavitários mistos de classe V vestibular em 36 molares humanos, dos quais metade foram induzidos artificialmente à cárie. Foi feita a remoção da cárie com broca esférica em baixa rotação, permanecendo a dentina afetada. Os dentes foram subdivididos em 6 grupos, cavidade hígida: sem tratamento prévio, utilização de clorexidina e utilização de laser de Er,Cr:YSGG e cariados: sem tratamento prévio, utilização de clorexidina e utilização de laser de Er,Cr:YSGG. Foi empregado o sistema adesivo e restaurador da resina a base de silorano Filtek P90 (3M ESPE, St. Paul, MN, EUA). Os espécimes foram submetidos a 5000 ciclos térmicos (5-55° C em banhos de 60 minutos). Para caracterização da adaptação externa foram obtidas réplicas de epóxi pela impressão da superfície das restaurações. Foi realizada a análise quantitativa da adaptação externa, tanto em dentina hígida quanto afetada, por meio de réplicas de epóxi, utilizando Microscopia Eletrônica de Varredura. Os valores médios em porcentagem de margen não-adaptadas foram 5,41% em esmalte e 6,49% em dentina antes da termociclagem e 25% e 33,7% respectivamente após. As amostras do grupo com cavidade cariada que foram irradiados com laser apresentaram os maiores valores de margem não-contínua. A clorexidina não afetou os resultados na adaptação marginal / Abstract: This study evaluates the use of chlorhexidine and laser Er,Cr:YSGG in the adesion in cavities mixed healthy and carie affected, in relation to external adaptation on class V restorations subjected to thermal cycling. Cavity preparations were performed mixed class V buccal 36 human molars, half of which were artificially carie induced. Was removed from the cavity with round bur at low speed, the remaining affected dentin. The teeth were divided into 6 groups, cavity healthy: without previous treatment, use of chlorhexidine and the use of Er,Cr:YSGG and carie afected: no previous treatment, use of chlorhexidine and the use of Er,Cr:YSGG. We used adhesive system and restorative resin-based silorano Filtek P90 (3M ESPE, St. Paul, MN, USA). The specimens were subjected to 5000 thermal cycles (5-55° C 60 minutes). To characterize the external adaptation of epoxy replicas were obtained by printing the surface of the restorations. We performed quantitative analysis of external adaptation, both in healthy female and affected dentin, using epoxy replicas, using SEM. The average percentage of non-adapted were 5.41% and 6.49% in enamel dentine before thermal cycling and 25% and 33.7% respectively after. And the group they were carious cavity laser irradiated showed higher non-continuous margin. The clorexidine does not affected the result / Doutor

Tendo em vista o alto índice de criminalidade com armas de fogo no Brasil, é imperativo que a perícia forense tenha mais subsídios sobre resíduos de tiro e alterações provocadas por tiros em têxteis comumente encontrados em cenas de crime. Neste trabalho foram utilizadas munições do maior fabricante de cartuchos no Brasil (Companhia Brasileira de Cartuchos CBC). Foram comparados resíduos de munição convencional (Sinoxid) e de munição não-tóxica (Sintox) em tiros disparados a diversas distâncias, mostrando suas diferenças de composição e morfologia e que o resíduo Sintox contém partículas com composição semelhante àquelas encontradas no ambiente livre de tiros. A análise de fases do resíduo Sinoxid permitiu identificar uma nova categoria de partículas características, com composição e cristalografia específica (BaAl2O4), além das características (PbSbBa, PbBa) e consistentes (PbSb, PbBa, Pb, Sb, Ba) previstas pela norma. Nos resíduos de munição Sintox foram observadas composições contendo AlSiK, AlSi, Pb e AlSiCa. Destas categorias três tem composição semelhante a minerais abundantes na crosta terrestre (aluminossilicatos em geral). Nesta munição se propõe a presença de microesferulitos de chumbo, detectados com microscopia eletrônica de varredura, como evidência de disparo, com validade para os casos de armas em que se supõe o uso anterior ou concomitante de munição convencional, pois a origem provável destes esferulitos é a contaminação da arma com tiros anteriores (enchumbamento do cano). Exceto pela presença dos esferulitos de Pb, não se tem indicativo seguro para afirmar a origem de disparo de arma de fogo nestes resíduos. Do universo de fibras têxteis foram selecionadas fibras de vestimentas comuns entre vítimas de homicídio no Estado do Rio Grande do Sul e foram analisadas as alterações em fibras de tecidos submetidas a tiros, disparados em diferentes distâncias. Fibras de poliéster no tecido alvejado permitiram estimar distâncias de tiro tipo "encostadas" (contact) por fusão das fibras (fiber fusing), tipo "distâncias curtas", por apresentarem rompimento por fusão (fiber melting), enquanto que em distâncias maiores ocorre o rompimento mecânico. Fibras de algodão apresentaram apenas rompimento mecânico. Foi desenvolvida uma medida quantitativa através da medida com MEV do recobrimento de fibras com GSR, que mostra um decaimento exponencial em função da distância radial do furo do projétil, cuja constante de decaimento apresenta dependência da distância de disparo. / Given the high crime rate with firearms in Brazil, it is imperative to supply forensic laboratories with more subsidies on gunshot residues (GSR) from Brazilian ammunition and to analyze changes caused by firearm projectiles in textiles most commonly found at crime scenes. In this work we used ammunition from the leading supplier of cartridges in Brazil (Companhia Brasileira de Cartuchos CBC), and analyzed GSR from conventional ammunition (Sinoxid) and from non-toxic ammunition (Sintox), originated from shots fired at various distances from the target. Elemental analysis showed that both GSR are fundamentally different and that Sintox GSR is similar in composition to common environmental dust. The residue of the Sinoxid phase analysis identified a new category of characteristics particles, with specific composition and crystallography (BaAl2O4), next to the characteristic (PbSbBa, PbBa) and consistent (PBSB, PbBa, Pb, Sb, Ba) particles enumerated by the standard. In Sintox ammunition residue containing AlSiK, AlSi, Pb, and AlSiCa were found. Three of these categories have similar composition to abundant minerals in the earth's crust (aluminosilicates). To identify GSR from this ammunition, the presence of lead micro-spherulites detected with scanning electron microscopy, is proposed as evidence of shooting, valid for cases of weapons which had previous usage of conventional ammunition (weapon fouling). Among the many possible textile fibers, we selected those common on clothing of homicide victims in Southern Brazil (State of Rio Grande do Sul). Fiber modifications due to shots fired at different distances were analyzed. Polyester fibers in the targeted textiles allowed to estimate the firing distance of contact shots by fiber fusing, while at short distances fiber melting occurred. A higher distance only mechanical breakage was observed. Cotton fibers showed only mechanical disruption. The GSR-coverage of the fibers as a function of radial distance from the hole margin showed an exponential decay and the reciprocal decay constant showed a linear dependence on firing distance.

Neste trabalho estudou-se a síntese de nanotubos de Ta2O5 (NTs Ta2O5) fabricados pelo processo de anodização e sua aplicação na fotogeração de hidrogênio (H2). A otimização dos parâmetros de síntese e fotocatálise levou a uma maximização na fotoprodução de H2. O controle da temperatura do eletrólito da anodização proporcionou a escolha da obtenção de NTs de Ta2O5 aderidos ou livres do substrato de tântalo metálico. Os NTs de Ta2O5 formados foram caracterizados por microscopia eletrônica de varredura (MEV), microscopia eletrônica de transmissão (TEM), espectroscopia de energia dispersiva de raios X (EDX), difração de raios X (DRX), refinamento Rietveld, espectroscopia de fotoelétrons induzidos por raios X (XPS), área superficial específíca (BET) e espectroscopia ultravioleta visível (UV-Vis). A fotogeração de hidrogênio utilizando os NTs de Ta2O5 foi avaliada pela fotólise da água. A difratometria de raios X revelou que os NTs de Ta2O5 como anodizados são amorfos, necessitando de tratamento térmico para se obter uma fase cristalina necessária para uma mais eficiente produção de hidrogênio. A combinação entre a elevada cristalinidade, superfície química e área superficial influenciou na atividade fotocatalítica dos NTs. A amostra com 33 % de cristalinidade apresentou uma elevada atividade fotocatalítica na fotogeração de H2. A utilização de etanol como agente de sacrifício fez aumentar a fotogeração de H2 em 12,5 vezes quando comparado com água pura. Para o nosso sistema, as condições de “otimização” para a concentração de massa de NTs e etanol como agente de sacrifício foram de 1,0 mg/mL e 25 %, respectivamente. Pelo uso de etanol como agente de sacrifício, foram produzidos além de H2, outros gases minoritários como CO, CO2, CH4, C2H4 e C2H6. No entanto, a formação desses produtos foi de apenas 3 % para uma produção de H2 de 97 %. A eficiência quântica aparente para a fotogeração de H2 foi de 5,18 ± 0,3%. Na tentativa de aumentar a produção de H2 foi realizado um carregamento de nanopartículas de NiO sobre a superfície dos NTs, fazendo aumentar a eficiência em 8,4±0,7 % com uma taxa de produção de H2 de 56 % maior que a de NTs livres de nanopartículas. / In this work the synthesis of Ta2O5 nanotubes (Ta2O5 NTs) fabricated by anodizing process and its application in hydrogen (H2) photogeneration was studied. The optimization of the synthesis and photocatalytic parameters led to maximization the H2 production. Temperature control of the anodizing electrolyte afforded the choice of obtaining Ta2O5 NTs freestanding or adhered on tantalum metal substrate. The Ta2O5 NTs formed has been characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy X-ray (EDX), X-ray diffraction (XRD), Rietveld refinement, induced photoemission spectroscopy X-ray (XPS), specific surface area (BET) and ultraviolet visible spectroscopy (UV-Vis). The photogeneration hydrogen using the Ta2O5 NTs was evaluated by photolysis of water. The X-ray diffractometry revealed that the as-anodized Ta2O5 NTs are amorphous, requiring heat treatment to obtain a crystalline phase necessary for a more efficient hydrogen production. The combination of high crystallinity, surface chemistry and surface area influence the photocatalytic activity of NTs. The sample with 33 % of crystallinity had a high photocatalytic activity for H2 photogeneration. The use of ethanol as a sacrificial agent has increased the H2 photogeneration in 12.5 times compared with pure water. For our system, the optimization conditions for the mass concentration of NTs and ethanol as the sacrificial agent were 1.0 mg/mL and 25 %, respectively. By the use of ethanol as a sacrificial agent, other trace gases such as CO, CO2, CH4, C2H4 and C2H6 in addition to H2 were produced. However, the formation of these products was only 3 %, for a generation of 97 % of H2. The quantum efficiency apparent to photogeneration of H2 was 5.18 ± 0.3 %. In an attempt to increase production of H2 was performed a NiO nanoparticle loading on the surface of NTs, increasing efficiency of 8.4 ± 0.7% with a production rate of 56 % H2 greater than NTs free of nanoparticles.

A Medida de Corrente Induzida por Feixe de Elétrons (EBIC - do inglês Electron Beam-induced Current ) é uma técnica focada nas propriedades de transporte dos portadores de carga minoritários em materiais semicondutores, permitindo a medição direta de propriedades elétricas tais como comprimento de difusão e vida média dos portadores, localização de defeitos e caracterização de zonas de depleção em junções p-n. O contraste EBIC depende da eficiência da coleção de corrente na amostra, permitindo assim a direta visualização de características eletricamente ativas. A avaliação da metodologia de medida EBIC foi realizada através da caracterização de amostras de silício tipo-p e tipo-n, e comparação dos resultados com dados da literatura. Uma vez que a profundidade de penetração do feixe de elétrons do MEV na amostra depende da tensão de aceleração utilizada, foram realizadas medidas EBIC com diferentes tensões de aceleração para avaliar a resolução em profundidade da posição de uma junção p-n formada em uma amostra de silício tipo n implantada com íons de Ga com energia de 5 keV.A medida EBIC na seção transversal de células solares é promissora para a caracterização destes dispositivos, considerando a habilidade da técnica de resolver espacialmente regiões menores do que o tamanho de grão típicos (em torno de 1 m), fornecendo informações que seriam inacessíveis através das técnicas usualmente empregadas, como luminescência e curvas I-V, cujos resultados constituem valores médios representativos de escalas maiores do que a da camada ativa das células. Embora imagens EBIC sejam comumente utilizadas para a análise de defeitos em células solares, poucos trabalhos aplicam a técnica para a caracterização de seções transversais de células solares, especialmente células de terceira geração sensibilizadas por corante (DSSC) do tipo estado sólido. A estabilidade dos dispositivos durante as medições foi verificada, apoiando a aplicação da técnica EBIC na caracterização desse tipo de DSSC. Foram analisadas células com diferentes estruturas e espessuras da camada ativa, e caracterizações complementares com as técnicas EDS e GID foram feitas. Observou-se também a possibilidade de utilização da técnica no controle de qualidade e avaliação dos métodos de produção das células. Diferentes métodos de deposição da camada intermediária na estrutura das DSSCs foram testados, de forma a melhorar a adesão insatisfatória desta camada. A técnica EBIC mostrou-se adequada para a distinção entre células com boa adesão desta camada e células com defeitos de construção, permitindo a introdução de melhorias significativas na fabricação destes dispositivos. / Electron Beam-induced Current (EBIC) measurement is a technique focused on minority carrier transport properties in semiconductor materials, allowing direct measurements of several electrical properties, such as diffusion lengths and lifetime of the carriers, location of defects and depletion zone characterization in p-n junctions. EBIC contrast depends on the current collection efficiency in the sample, thus permitting a direct visualization of electronically active features. The evaluation of the EBIC measuring methodology was performed by the characterization of p- and n-type silicon and the comparison with results from the literature. Since the penetration depth of the electron beam in a sample depends on its acceleration voltage, the EBIC signal was acquired for variable voltage in order to evaluate the depth-resolved location of the p-n junction formed in the n-type silicon implanted with gallium at 5 keV. Direct measurement of EBIC profiles in cross-sections of solar cells is a promising method for device characterization, considering its spatial resolution is smaller than the typical grain sizes (about 1 m), providing informations otherwise inaccessible by the usually employed techniques, such as luminescence and V-I curves, that yield results that represent mean values of scales larger than that of the cell’s active layer. Although the EBIC imaging method is commonly used for defect analysis of solar cells, very few works have applied the thechnique to 3rd. generation solid state dye sensitized solar cell (DSSC) cross-sections. The stability of the devices during the measurement was verified in this work, supporting the application of the EBIC technique for the characterization of this type of DSSCs. DSSCs with different structures and active layer thickness were analyzed, and complementary characterizations with EDS and GID techniques were performed. The applicability of the EBIC thecnique in device quality control, as well as production methods evaluation was observed. Different deposition methods of the intermediate layer of the DSSC structure were tested, in orde to improve the unsatisfactory adhesion of this layer. EBIC showed to be the adequate thechnique to differentiate between well adhered and poorly constructed DSSCs, allowing to introdenuce significant improvements in the device fabrication.