The purpose of this study was to investigate the process optimization of combined high pressure acid leaching (HPAL) and mixed hydroxide precipitation (MHP) route for the extraction of nickel and cobalt from &Ccedil / aldag lateritic nickel ore. In order to extract nickel and cobalt values into pregnant leach solution (PLS), several process parameters of HPAL including acid load, temperature, leaching duration and particle size were investigated in comparative manner at constant solid concentration and agitation speed. After HPAL trials, it has been found that more than one combination of parameters offered higher than 90% extraction efficiencies for both nickel and cobalt. Among them, 0.325 kg/kg acid load, 250&deg / C, 1 hour duration and 100% -1 mm particle size was selected as the optimum conditions with 94.1% Ni and 94.0% Co extractions. A stock of PLS was prepared under the stated conditions that was treated by downstream operations in order to obtain MHP. Initially by two-stage iron removal of downstream operations major impurities iron, chromium and aluminum were nearly completely removed with acceptable nickel and cobalt losses from PLS. Then, the nickel and cobalt were precipitated by two-stage mixed hydroxide precipitation. In the first step of MHP, the optimum conditions were chosen as pH=7.10, 60&deg / C and 1 hour duration. The intermediate product obtained at these conditions contained 44.3% Ni, 3.01% Co with 3.06% Mn contamination. In summary, it was found that &Ccedil / aldag nickel laterite ore was readily leachable under HPAL conditions and PLS obtained was easily treatable in order to produce saleable MHP.

Actuellement, les supercondensateurs sont au centre de beaucoup de recherches. Ils offrent une solution potentielle pour le stockage réversible de l´énergie que ce soit pour le domaine spatial, aéronautique ou encore le transport (véhicules hybrides). Un axe de recherche important, visant à augmenter les densités d'énergie et de puissance, est consacré aux systèmes oxydes de métaux de transition /charbon actif (C) asymétriques. Les systèmes à base de RuO2 présentent les capacités les plus élevées, supérieures à 700 F/g, mais leur coût et leur toxicité limitent leur application aux petits appareils électroniques. Des oxydes moins coûteux tels que les oxydes de cobalt (notamment Co3O4), MnO2, V2O5, Fe3O4, NiO, Ni(OH)2, ainsi que des polymères conducteurs électroniques, ont été étudiés de manière approfondie au cours des dernières décennies jusqu’à être utilisés, pour certains, dans des dispositifs commerciaux. Mais aucun système n’a été aussi étudié que le C / MnO2. En effet, il a été démontré que ce dernier est particulièrement intéressant car il peut fonctionner dans des milieux aqueux à des tensions pouvant aller jusqu’à 2V tout en gardant une bonne stabilité électrochimique durant le vieillissement. Néanmoins, les performances du système, en particulier en termes de densité de puissance, sont limitées à cause de la mauvaise conductivité électronique du MnO2. Il est possible de surmonter ce problème en ajoutant à l’oxyde de manganèse, des matériaux conducteurs à base de carbone (noir de carbone, nanotubes de carbone…) ou encore, en développant des stratégies de greffage ou de décoration plus élaborées. La combinaison d’oxydes avec des espèces carbonées est très largement rapportée dans la littérature alors que le mélange d’oxydes de différente nature l’est beaucoup moins. Nous proposons dans ce projet de synthétiser et de développer des matériaux originaux améliorant, par un effet synergique, les propriétés intéressantes du manganèse, du cobalt et de l'oxyde / hydroxyde de nickel. Les inconvénients de chaque composant étant compensés par les bonnes propriétés complémentaires des autres. Nous cherchons à réunir en un seul matériau (ou composite), le bon comportement pseudocapacitif du manganèse, la bonne conductivité électronique associée aux oxydes de cobalt, la grande capacité de l'hydroxyde de nickel ainsi que les propriétés de conduction du carbone. Ce projet de doctorat vise à concevoir et à fabriquer de nouvelles classes d'électrodes composites hybrides basées sur des assemblages de graphène (pour la capacitance renforcée à double couche) et d'oxydes poreux de métaux de transition (pour une capacité faradique supplémentaire due à de multiples processus rédox réversibles). Les avantages combinés du graphène et des oxydes de métaux de transition permettront aux supercondensateurs à haute densité d'énergie de travailler dans des électrolytes aqueux respectueux de l'environnement ce qui est, aujourd’hui, un besoin reconnu. / Supercapacitors are the focus of much research at the present time. They offer a potential solution for reversible energy storage in the fields of space, aircrafts or transportation (hybrid vehicles). An important research line, aiming at increasing both energy and power densities, is devoted to asymmetric transition metal oxides / activated carbon (C) systems. RuO2-based devices exhibit the highest capacitance, more than 700 F/g, but their cost limits the applications to small electronic devices. Less expensive oxides such as cobalt oxides (especially Co3O4), MnO2, V2O5, Fe3O4, NiO, Ni(OH)2, as well as electrically conducting polymers, have been extensively studied in the past decades, or used in commercial devices; they EACH exhibit each drawbacks and advantages with regard to applications. But no system has been investigated as much as the C/MnO2 one, which is particularly interesting because it can work in aqueous media at tensions up to 2 V, and high stability in ageing has been demonstrated. Nevertheless, the performances of the system, especially in terms of power density, are limited by the poor electronic conductivity of MnO2. This problem is usually solved by simply mixing conductive carbon materials (carbon black, CNTs…) with MnO2 or by developing more elaborated grafting or decoration strategies. The combination of oxide and carbonaceous species is widely reported in the literature, whereas combining oxides with different natures is less frequently encountered. We propose in this project to synthesize and develop original materials enhancing, through a synergistic effect, the interesting properties of manganese, cobalt and nickel oxide/hydroxide, the drawbacks of each component being overbalanced by the good complementary properties of the other components. We aim at gathering in one single material (or composite), the good pseudocapacitive behavior of manganese, the good electronic conductivity associated to cobalt oxides, the high capacity of nickel hydroxide, as well as the enhanced conduction properties of carbon. The present PhD project aims at designing and manufacturing new classes of hybrid composite electrodes based on assemblies of graphene (for enhanced double layer capacitance) and porous transition metals oxides (for additional faradaic capacitance due to multiple reversible redox processes) directly applied on metallic current collectors. The combined advantages of graphene with those of transition metals oxides will enable supercapacitors with high energy density, working in environmentally friendly aqueous electrolytes, which are an acknowledged need. / A procura crescente de energia em setores distintos, como residencial, transporte e industrial, bem como a proliferação de fontes renováveis de produção de energia, exigem novos e mais eficientes dispositivos de armazenamento de energia. Consequentemente, tem-se observado um interesse crescente na produção e engenharia de materiais para armazenamento de energia. Muito dos esforços de R&D estão centrados no desenvolvimento de materiais nanoestruturados que possam responder aos requisitos da aplicação, tais como densidade de energia, densidade de potência e estabilidade face à ciclagem do dispositivo. Presentemente são muitos os materiais investigados como potenciais candidatos para elétrodos para dispositivos de armazenamento de energia por via eletroquímia, nomeadamente baterias, condensadores, pseudocondensadores ou supercondensadores. O objetivo do presente trabalho é produzir e estudar novos materiais com uma resposta eletroquímica intermédia entre um elétrodo típico de supercondensador e um elétrodo típico de bateria, também conhecidos como elétrodos híbridos. Por essa razão, selecionaram-se hidróxidos e óxidos de níquel e cobalto devido à sua elevada atividade eletroquímica e baixo custo. Estes materiais foram combinados com derivados de grafeno, que exibem alta condutividade e elevada área superficial ativa. Portanto, este trabalho foca a síntese e caracterização fisico química e eletroquímica de hidróxidos e óxidos de níquel-cobalto nanoestruturados e sua combinação com óxido de grafeno reduzido para aplicações de armazenamento de energia. A síntese foi efectuada por duas vias distintas: eletrodeposição e exfoliação. A eletrodeposição é usada para obter hidróxidos e óxidos de níquel-cobalto em combinação com óxido de grafeno reduzido. Os resultados evidenciam um efeito sinérgico quando o óxido de grafeno reduzido é combinado com o (hidr)óxido de níquel- cobalto, isto é, um aumento na capacidade, condutividade e estabilidade do compósito quando comparado com o (hidr)óxido de níquel-cobalto. Neste trabalho é dada especial atenção à espectroscopia de impedância eletroquímica que foi utilizada para avaliar os fenômenos que ocorrem durante a carga e descarga contínua e compreender os processos que ocorrem no material ativo e que resultam na sua degradação. O hidróxido de níquel-cobalto é também preparado por exfoliação, em meio aquoso, por meio da intercalação de lactato, enquanto o tetra-butilamónio é utilizado na exfoliação do óxido de níquel-cobalto. A resposta eletroquímica é avaliada em diferentes eletrólitos após reconstrução. Os resultados revelam a influência das espécies intercaladas durante o processo de exfoliação: quando a exfoliação é realizada para fins de armazenamento de energia, as espécies intercaladas e a força da interação com o material ativo devem ser consideradas de antemão para evitar o bloqueio superficial ou inibição da interação elétrodo-eletrólito. Os resultados mostraram que a exfoliação é uma rota promissora para aumentar a área de superfície ativa dos materiais, um parâmetro crítico no desempenho eletroquímico dos materiais dos eletrodos. Nesta dissertação é também estudado o mecanismo de carga-descarga do hidróxido de níquel-cobalto, que ainda não está completamente entendido. Assim, compreender esse mecanismo é um passo crítico para otimizar a morfologia e o desempenho do material e para projetar futuros dispositivos de armazenamento de energia. Para esclarecer os processos que ocorrem durante a carga, aplica-se o modelo de Mott-Schottky foi aplicado parade modo a avaliar a variação da conductividade do material e da sua capacidade na interface elétrodo-eletrólito. [...]