Made available in DSpace on 2014-06-11T19:31:04Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-04-24Bitstream added on 2014-06-13T19:40:51Z : No. of bitstreams: 1 gimenez_jma_dr_bauru_prot.pdf: 6908408 bytes, checksum: aff3f4ece05509d8087bc69b0e473e84 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Uma nova classe de rupeno-cupratos híbridos como Ru-1212 e Ru-1222 onde Ln = Sm, Eu, Gd, foi sintetizada em 1995. O Ru-1212 é isoestrutural com YBCO sendo o Y, Ba e o Cu completamente substituídos por Gd, Sr, e Ru respectivamente. Estes materiais têm despertado muito interesse devido a aparente coexistência do ferromagnetismo e a supercondutividade. Apesar da considerável atividade experimental desenvolvida neste composto, o Ru-1212 ainda apresenta vários pontos obscuros, considerando sua preparação e caracterização. O oxigênio não estequiométrico (intersticial) tem sido considerado como uma possível causa para as diferentes propriedades destes materiais. Vacâncias de oxigênio são introduzidas possivelmente nos planos de RuO2 em amostras de Ru-1212 por recozimentos em vácuo acima de 600 K. Os saltos difusivos de oxigênio intersticial e vacâncias de oxigênio são acompanhados por reorientações da distorção local e podem ser investigadas por medidas de espectroscopia mecânica. Nesta tese as amostras de Ru-1212 foram preparadas por reações de estado sólido, caracterizadas por difração de raios x, microscopia eletrônica de varredura, resistividade elétrica, susceptibilidade magnética e estudada usando medidas de espectroscopia mecânica (Pêndulo de Torção). Os resultados mostraram estruturas de relaxação que foram atribuídas à mobilidade de oxigênio intersticial (com energias de ativação de 0,13 e 0,36 eV) e vacâncias de oxigênio (com energias de ativação de 1,1 e 1,9 eV) nos octaedros de RuO6. / A new class of ruthenocuprates as Ru-1212 and Ru-1222 where Ln = Sm, Eu, Gd, was synthesized in 1995. The Ru-1212 is isoestructural with YBCO being the Y, Ba, and the Cu completely substituted by Gd, Sr and Ru respectively. These materials have attracted much interest due the apparent coexistence of the ferromagnetism and the superconductivity. Despite the considerable experimental developed acitivity in this composition, the Ru-1212 still presents some obscure points, considering its preparation and characterization. The non stoichiometric (interstitial) oxygen has been considered as a possible cause for porperties different in these materials. Oxygen vacancies are possibly introduced in the planes of RuO2 in samples of Ru-1212 for annealings in vacuum above of 600 K. The diffusive jumps of interstitial oxygen and oxygen vacancy are followed by reorientations of the local distortion and can be investigated by mechanical spectroscopy measurements. In this thesis, the samples of Ru-1212 had been prepared by solid state reactions, characterized for X-Ray Diffraction, Scanning Electronic Microscopy, Electric Resistivity, Magnetic Susceptibility had been studied using Mechanical Spectroscopy measurement in Torsional Pendulum. The results shown relaxation structures that were attributed to the mobility of interstitial oxygen (with activation energy of 0,36 and 0,13 eV) and vacancies oxygen (with activation energy of 1,1 and 1,9 eV) in the octahedral of RuO6.

Desde a descoberta dos supercondutores com alta temperatura crítica, muitos estudos têm sido realizados em tomo de suas propriedades fisicas, tentando associá-Ias à supercondutividade. Átomos de oxigênio dissolvidos intersticialmente têm um papel importante na supercondutividade destes materiais, pois são capazes de mover-se com facilidade dentro da rede além de contribuírem na criação de buracos nos planos de CUO2. As medidas de atrito interno são ferramentas sensíveis ao estudo de defeitos em sólidos, em particular a mobilidade de oxigênio intersticial. Neste trabalho, foram analisadas amostras de Bi2Sr2CaCu2O8+δ da maneira como foram recebidas, recozidas e dopadas com diferentes concentrações de oxigênio não estequiométrico. Foram efetuadas medidas de espectroscopia anelástica utilizando um pêndulo de torção invertido tipo Kê, operando com freqüência de oscilação de 11 a 30 Hz, num intervalo de temperatura compreendido entre 88 e 700 K, com taxa de aquecimento de 1 K/min e vácuo em tomo de 10-5 Torr. Foram observadas estruturas de relaxação complexas para as amostras recozidas, que são reversíveis apenas com novos tratamentos de recozimento, atribuídas a possíveis transições de fase estruturais. Para as amostras dopadas com oxigênio, foram observadas estruturas de relaxação que foram atribuídas ao movimento de átomos intersticiais de oxigênio nos planos de BiO. Foi observada também uma relação entre a intensidade dos processos de relaxação e a concentração dos intersticiais presentes nestas amostras. / Since the discovery of the high critical temperature superconductors many studies have been carried out intending to associate their physical properties to the superconductivity mechanisms. The oxygen atoms interstitially dissolved in its structure have an important role in the superconductivity of these materiaIs since they have high mobility capable to move through the net contributing to the generation of holes along the CUO2 plans. The internal friction measurements are a sensitive tool to the study of defects in solids, in particular the mobility of interstitial oxygen. In this work, it had been analyzed samples of Bi2Sr2CaCu2O8+δ in the as received condition, annealed and doped with different concentrations of not stoichiometric oxygen. The anelastic spectroscopy measurements were made using a torsional inverted pendulum of the Kê type, operating with oscillation frequency between 11 and 30 Hz, the applied temperatures are in the range between 88 and 700 K, with heating rate about 1 K/min and vacuum better than 10-5 Torr. Complex structures of relaxation had been observed for the annealed samples, they are reversible only with new annealing treatments. These structures were attributed to possible structural phase transitions. For the oxygen doped samples, the relaxation structures had been attributed to the mobility of interstitial oxygen atoms in the plans of BiO. On these measurements was also observed a relation between the intensity of the relaxation processes and the concentration ofthe interstitial oxygen in these samples.

Made available in DSpace on 2014-06-11T19:23:29Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-06-30Bitstream added on 2014-06-13T19:50:18Z : No. of bitstreams: 1 nascimento_rm_me_bauru.pdf: 3217433 bytes, checksum: 4db978f65eff59d8b027881dac872d0f (MD5) / Secretaria de Educação do Estado de São Paulo / Desde a descoberta dos supercondutores com alta Tc, vários trabalhos têm sido efetuados sobre as diferentes propriedades destes materiais. As cerâmicas Y'BA IND.2' C IND.U 'IND.3' 'O IND. 7-'delta' mostraram que tem suas propriedades supercondutoras fortemente afetadas pela quantidade de oxigênio. Mais recentemente, medidas de relaxações anelásticas em 'LA IND.2'CU 'O IND. 4+'delta' mostraram que a remoção deste elemento pode ser relacionada com dois eventos. Um deles é o decréscimo na mobilidade entre dois planos adjacentes CuO e o outro, é o aumento no número de padrões de mobilidade para os octaedros CU 'O IND. 6'. Para SM'BA IND.2' C IND.U 'IND.3' 'O IND. 7-'delta' (SBCO), a possibilidade de uma estequiometria de oxigênio variável e sua alta mobilidade nos planos... / Since the discovery of the high Tc superconductors, several works have been made about the different propoerties of these materials. Y'BA IND.2' C IND.U 'IND.3' 'O IND. 7-'delta' ceramic showed to have its superconducting properties strongly affected by the oxygen content. More recently, anelastic relaxation measurements in 'LA IND.2'CU 'O IND. 4+'delta', showed that the remotion of this element can be related to two events. One is the decrease in mobility between two adjacent CuO planes, and the other is the increase in the number of tilting patterns of the Cu 'O IND. 6' octahedra. For SM'BA IND.2' C IND.U 'IND.3' 'O IND. 7-'delta' (SBCO), the possibility of variable stoichiometry and the high mobility of oxygen in the... (Complete abstract, click electronic access below)

Desde a descoberta dos supercondutores com alta temperatura crítica, muitos estudos têm sido realizados em tomo de suas propriedades fisicas, tentando associá-Ias à supercondutividade. Átomos de oxigênio dissolvidos intersticialmente têm um papel importante na supercondutividade destes materiais, pois são capazes de mover-se com facilidade dentro da rede além de contribuírem na criação de buracos nos planos de CUO2. As medidas de atrito interno são ferramentas sensíveis ao estudo de defeitos em sólidos, em particular a mobilidade de oxigênio intersticial. Neste trabalho, foram analisadas amostras de Bi2Sr2CaCu2O8+δ da maneira como foram recebidas, recozidas e dopadas com diferentes concentrações de oxigênio não estequiométrico. Foram efetuadas medidas de espectroscopia anelástica utilizando um pêndulo de torção invertido tipo Kê, operando com freqüência de oscilação de 11 a 30 Hz, num intervalo de temperatura compreendido entre 88 e 700 K, com taxa de aquecimento de 1 K/min e vácuo em tomo de 10-5 Torr. Foram observadas estruturas de relaxação complexas para as amostras recozidas, que são reversíveis apenas com novos tratamentos de recozimento, atribuídas a possíveis transições de fase estruturais. Para as amostras dopadas com oxigênio, foram observadas estruturas de relaxação que foram atribuídas ao movimento de átomos intersticiais de oxigênio nos planos de BiO. Foi observada também uma relação entre a intensidade dos processos de relaxação e a concentração dos intersticiais presentes nestas amostras. / Since the discovery of the high critical temperature superconductors many studies have been carried out intending to associate their physical properties to the superconductivity mechanisms. The oxygen atoms interstitially dissolved in its structure have an important role in the superconductivity of these materiaIs since they have high mobility capable to move through the net contributing to the generation of holes along the CUO2 plans. The internal friction measurements are a sensitive tool to the study of defects in solids, in particular the mobility of interstitial oxygen. In this work, it had been analyzed samples of Bi2Sr2CaCu2O8+δ in the as received condition, annealed and doped with different concentrations of not stoichiometric oxygen. The anelastic spectroscopy measurements were made using a torsional inverted pendulum of the Kê type, operating with oscillation frequency between 11 and 30 Hz, the applied temperatures are in the range between 88 and 700 K, with heating rate about 1 K/min and vacuum better than 10-5 Torr. Complex structures of relaxation had been observed for the annealed samples, they are reversible only with new annealing treatments. These structures were attributed to possible structural phase transitions. For the oxygen doped samples, the relaxation structures had been attributed to the mobility of interstitial oxygen atoms in the plans of BiO. On these measurements was also observed a relation between the intensity of the relaxation processes and the concentration ofthe interstitial oxygen in these samples.