Made available in DSpace on 2018-08-01T23:58:51Z (GMT). No. of bitstreams: 1 tese_11406_Guilherme Cunha20180522-110439.pdf: 13274017 bytes, checksum: 85bc8b1f4cf1b40df18e294e850377a3 (MD5) Previous issue date: 2017-08-12 / Resumo da dissertação (apenas copie e cole na célula) O desempenho das estruturas de concreto está relacionado com a conservação das propriedades mecânicas e propriedades vinculadas com a durabilidade. No que tange à durabilidade, identificam-se os íons cloreto como um dos principais agentes responsáveis pela redução da vida útil das estruturas de concreto armado, pois ao ingressar no interior das estruturas, são capazes de despassivar a armadura ocasionando corrosão, comprometendo a capacidade de carga. Uma importante solução para mitigar o ingresso destes agentes agressivos é a utilização de sistemas compostos por cimento Portland e pozolanas, capazes de interagir com os compostos do cimento melhorando o seu desempenho. Neste contexto, pesquisas têm identificado avanços com relação à utilização de resíduos de vidro em matrizes cimentícias, favorecendo destinação sustentável para o resíduo e redução do consumo de cimento, em função de sua substituição parcial. Constatam-se benefícios com relação às propriedades mecânicas e aquelas relacionadas com a durabilidade, entretanto tem-se observado, em alguns casos, suscetibilidade a processos expansivos relacionados à reação álcali-sílica, podendo ser atenuada com a utilização conjunta de outros materiais suplementares, como por exemplo o metacaulim. O objetivo deste trabalho é avaliar o desempenho de concretos produzidos com resíduos da lapidação do vidro. Para a produção dos concretos, utilizou-se como substituição parcial ao cimento, resíduo de vidro com e sem moagem e metacaulim. Foram realizados ensaios de penetração de cloretos (ASTM C 1202), difusão por imersão (NT Build 443), migração em regime estacionário (UNE 83987) e não estacionário (NT Build 492), além da análise da ocorrência de reação álcali-sílica pelo método ASTM C 1260. Os resultados demostraram que os resíduos da lapidação do vidro, utilizados em substituição ao cimento em até 20%, quando moídos em dimensões de partículas adequadas, podem melhorar o desempenho de concretos, beneficiando os aspectos mecânicos, elevando de modo significativo a resistência aos íons cloretos e ainda mitigar reações álcali-sílica.

The use of residues, as the rice husk ash (RHA) in the concrete s production reduces the environmental impact caused in its productive chain. It means fewer energy s consumption, fewer natural resources waste, less environmental pollution and lower aggregated cost. In the present study, the viability of using residual RHA, in natura (non-ground) or ground, on structural concrete, in partial substitution to the Portland cement was investigated, starting from the durability chloride ions analysis. In such a way, five cementitious blends, two composed by natural RHA, two with crushed RHA and one as a reference sample were tested. The substitution s rates were 15% and 25%. The water/binder relations used were 0.45, 0.55 and 0.65. The samples were tested for chloride penetration according to ASTM C 1202 (Rapid Chloride Permeability Test) and for long-term test (colorimetric method). Additionally, the tests of axial compressive strength and water absorption by immersion, according to the ABNT prescriptions were conducted. The obtained results showed that is viable to use residual non-ground RHA as partial substitution to Portland cement in structural concretes. For the axial compressive strength at 91 days and to the same relation w/b, in general, the residual non-ground RHA blends showed higher performance than those presented by the reference mixture. In the RCPT the use of RHA resulted in decreases in the passing charges that, in general, promoted improvement in the mixtures ratings on the chloride penetrability, compared with the reference mixtures. In long-term test, the use of RHA burnt without temperature control, also promoted improvements in the mixture performances, compared to the reference mixtures, with reductions in the chloride penetration coefficients. But the mixtures were dissimilar when compared to those presented by the RCPT. In the case of water absorption by immersion, it was found that the use of RHA, in general, increased the concrete water absorption, however, the results presented by mixtures composed with RHA were close to those of reference ones. / A utilização de resíduos como a cinza da casca do arroz produzida sem controle da temperatura na fabricação de concretos reduz o impacto ambiental gerado na cadeia produtiva deste material, significando menor consumo de energia, menor desperdício de recursos naturais, menor poluição do meio ambiente e menor custo agregado. No presente trabalho investiga-se a viabilidade de se utilizar a CCA residual, ao natural ou moída, em concretos estruturais, em substituição parcial ao cimento Portland, a partir da análise da durabilidade aos ions cloretos. Para isso, foram testadas cinco misturas aglomerantes: duas compostas com CCA ao natural, duas com CCA moída e uma mistura de referência com 100% cimento Portland, a qual se confrontaram os resultados. Adotaram-se os teores de substituição de 15% e 25%, e as relações a/ag de 0,45; 0,55 e 0,65. Procederam-se os ensaios de resistência à penetração de cloretos segundo o método de penetração acelerada ASTM C 1202 (EAPC) e também, segundo o método de imersão em solução salina (EPCI). Adicionalmente, foram realizados os ensaios de resistência à compressão axial e de absorção de água por imersão, segundo prescrições da ABNT. Os resultados obtidos na investigação confirmam que é viável utilizar a CCA residual, ao natural ou moída, como substituição parcial ao cimento Portland, em concretos para uso estrutural. Quanto à resistência a compressão axial, aos 91 dias, as misturas compostas CCA, em geral, apresentaram desempenhos superiores aos das misturas de referência. No EAPC a utilização de CCA resultou em decréscimos nos valores das cargas passantes que, em geral, promoveram melhoria nas classificações das misturas quanto à penetrabilidade aos cloretos, em comparação as misturas de referência. No EPCI a utilização da CCA, queimada sem controle de temperatura, também promoveu melhorias no desempenho da maioria das misturas, em comparação às misturas de referência, com reduções nos coeficientes de penetração de cloretos. Porém as misturas apresentaram comportamentos diferenciados quando comparados ao apresentado no EAPC. No caso da absorção de água por imersão, constatou-se que a utilização de CCA, em geral, aumentou a absorção de água dos concretos, entretanto, os valores apresentados pelas misturas compostas com CCA foram próximos aos de referência.