Submitted by Silvana Teresinha Dornelles Studzinski (sstudzinski) on 2016-06-15T15:50:42Z No. of bitstreams: 1 DÉBORA MAGALI HANSEN_.pdf: 2330600 bytes, checksum: 74a7605994355dc5762f8c364bddf4c9 (MD5) / Made available in DSpace on 2016-06-15T15:50:42Z (GMT). No. of bitstreams: 1 DÉBORA MAGALI HANSEN_.pdf: 2330600 bytes, checksum: 74a7605994355dc5762f8c364bddf4c9 (MD5) Previous issue date: 2016-03-30 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / PROSUP - Programa de Suporte à Pós-Gradução de Instituições de Ensino Particulares / A destinação final ambientalmente adequada para os resíduos sólidos industriais é uma problemática que veio ganhando maior importância ao longo dos anos. O setor da construção civil consome grandes quantidades de insumos, gerando paralelamente grandes quantidades de resíduos. Quando o assunto é reciclagem de resíduos industriais, o setor da construção civil exerce um papel importante, reciclando resíduos de diversos setores da economia. Tendo em vista a existência do polo cerâmico no Rio Grande do Sul, e totalidade de resíduos de cerâmica vermelha (RCV) resultante desse polo, buscou-se através deste estudo, verificar qual é o percentual de geração de RCV em uma empresa específica, devido a grande variabilidade dos dados apresentados pela literatura. E em paralelo buscou-se avaliar o potencial pozolânico do RCV e comparar o seu desempenho com o metacaulim, material já consagrado como pozolana. Os aglomerantes (cimento CP II-F-32, Ca(OH)2 – P.A., CH-I) e os materiais pozolânicos (RCV e metacaulim) empregados na pesquisa foram caracterizados quimicamente por ensaios de fluorescência de raios X (FRX) e Perda ao Fogo (PF), mineralogicamente por ensaios de difração de raios X (DRX) e fisicamente por ensaios de, granulometria a laser, massa específica e área superficial específica (BET). Além disso, o RCV e o metacaulim foram submetidos a ensaios para determinação do teor de umidade e finura. Para avaliar a atividade pozolânica do RCV e comparar seu desempenho ao metacaulim foram realizados ensaios de condutividade elétrica, termogravimetria e ensaios de resistência à compressão, orientados pelas NBR 5752:2014, NBR 5751:2015 e NBR 15894:2010. Mediante os resultados obtidos, verificou-se que o percentual de geração de RCV na empresa objeto de estudo, com os ensaios de caracterização foi possível verificar que o RCV atende aos requisitos químicos estabelecidos pela NBR 12653:2014. O procedimento de moagem conferiu ao RCV uma granulometria adequada para uso como pozolona. Quanto a atividade pozolânica, verificou-se que o RCV atendeu ao requisito da NBR 12653:2014, no que diz respeito à resistência com o aglomerante Ca(OH)2 P.A., já quando ensaiado com o aglomerante CH-I, o RCV apresentou resistência à compressão consideravelmente superior ao metacaulim. Já nas argamassas moldadas com cimento, o RCV não atingiu o índice de atividade pozolânica (IAP) exigido na NBR 12653:2014, impedindo sua classificação como material pozolânico. Nas argamassas ensaiadas sob as prescrições da NBR 15894:2010, contendo 15% de substituição do cimento pelo RCV, os resultados de resistência à compressão não apresentaram diferenças significativas em relação às argamassas referência, apontando indícios de melhor desempenho em menores teores de substituição. As análises térmicas evidenciaram o consumo de Ca(OH)2 das pastas. As pastas formuladas com 25% de substituição do cimento por metacaulim apresentaram maior consumo de Ca(OH)2 em relação as pastas formuladas com 25% de RCV, evidenciando a atividade pozolânica dos materiais. / The final destination environmentally suitable for industrial solid waste is a problem that came gaining more importance over the years. The construction industry consumes large amounts of supplies, generating parallel large quantities of waste. When it comes to recycling of industrial waste, the construction sector plays an important role, recycling waste from various sectors of the economy. Considering the existence of the ceramic polo at the Rio Grande do Sul, and all red ceramic waste (RCV) resulting from this pole, we sought through this study, find what is the percentage of RCV generation in a specific company due the great variability of the data presented in the literature. And in parallel we sought to evaluate the potential of pozzolan RCV and compare their performance with metakaolin, material already recognized as pozzolan. The binder (cement CP II-F-32, Ca(OH)2 – P.A., CH-I) and pozzolanic materials (RCV and metakaolin) employed in the study were chemically characterized by X-ray fluorescence assays (XRF) and Loss Fire (PF), mineralogically by testing X-ray diffraction (XRD) and physically by tests of laser granulometry, specific gravity and specific surface area (BET). Furthermore, the RCV and metakaolin were subjected to tests for determination of humidity content and fineness. To evaluate the pozzolanic activity of the RCV and compare its performance to metakaolin were performed electrical conductivity tests, thermogravimetry and compressive strength tests, guided by the NBR 5752:2014, NBR 5751:2015 and NBR 15894:2010. From the results obtained, found to the percentage of RCV generation in study subject company with the characterization tests it was verified that the RCV meets chemical requirements of the NBR 12653:2014. The grinding procedure gave the RCV adequate particle size for use as pozolona. As the pozzolanic activity, it was found that the RCV met requirement the NBR 12653:2014 with regard to resistance to Ca(OH)2 P.A. agglomerating, since when tested with CH-I agglomerating, the RCV showed compression resistance the considerably higher than metakaolin. Already in the cast with cement mortar, the RCV has not reached the pozzolanic activity index (IAP) required in NBR 12653:2014 preventing classification as pozzolanic material. In mortars tested under the requirements of NBR 15894:2010, containing 15% replacement of cement by RCV, the compressive strength results showed no significant differences from the reference mortar, indicating better performance indications in lower replacement levels. The thermal analysis showed the consumption of Ca(OH)2 pastes. The pastes formulated with 25% of the cement replaced by metakaolin showed increased consumption of Ca(OH)2 relative pastes formulated with 25% RCV, showing the pozzolanic activity of the materials.

Conselho Nacional de Desenvolvimento Científico e Tecnológico / To present research has for objective investigate the technical feasibility of the job of rice husk ask ungrounded, in concretes for structural ends. This study tries the mechanical properties of axial compression strength, tensile strength by diametrical compression, elasticity modulus and total shrinkage of concretes molded with addition of RHA natural, with contents of 15% and 25% in substitution in mass of cement CP II-F, in the forms ground in mill of balls and natural (without grinding), and compared with the concrete of reference, with 0.45, 0.55, and 0.65 water/cementations materials relationships. Were tested for resistance to axial compression on the ages of 7, 28 and 91 days, resistance to diametric compression by 28 and 91 days, modulus of elasticity at 28 and 91 days and total shrinkage at 28, 91 and 300 daysThe results indicated that technical feasibility exists for the use of rice husk ash ungrounded, for the content of 15% of substitution, in structural concrete. The values from tests of concrete with 15% of RHA without grinding developed axial compression strength over the reference, lower shrinkages, tensile strength by diametrical compression and elasticity modulus lower however with not significant falls. / A presente pesquisa teve por objetivo investigar a viabilidade técnica, quanto à propriedade mecânica e de retração, do emprego de cinza de casca de arroz residual, ou seja, em seu estado natural, em concretos para fins estruturais. Este estudo trata das propriedades mecânicas de resistência por compressão axial e diametral, módulo de elasticidade e das retrações de concretos moldados com adição de CCA natural, com teores de 15% e 25% em substituição em massa de cimento CP II-F, nas formas moída em moinho de bolas e natural (sem beneficiamento), e comparadas com o concreto de referência, com três relações água/aglomerante 0,45, 0,55, e 0,65. Foram realizados ensaios de resistência por compressão axial nas idades de 7, 28 e 91 dias, resistência por compressão diametral aos 28 e 91 dias, módulo de elasticidade aos 28 e 91 dias e retração total aos 28, 91 e 300 dias.Os resultados indicaram que existe viabilidade técnica para o emprego de cinza de casca de arroz natural, sem moagem, para o teor de 15% de substituição, para emprego em concreto estrutural. Os valores obtidos nos ensaios dos concretos com 15% de CCA natural desenvolveram resistências axiais superiores ao referência, retrações inferiores, módulo de elasticidade e resistência por compressão diametral inferiores porém com quedas não significativas .

Submitted by Fabio Sobreira Campos da Costa (fabio.sobreira@ufpe.br) on 2016-07-22T13:13:31Z No. of bitstreams: 2 license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) Dissertação - Emerson Silva - Versão definitava.pdf: 2135263 bytes, checksum: 0a3cbcc3e5c3ecb44715e0fbc253bd60 (MD5) / Made available in DSpace on 2016-07-22T13:13:31Z (GMT). No. of bitstreams: 2 license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) Dissertação - Emerson Silva - Versão definitava.pdf: 2135263 bytes, checksum: 0a3cbcc3e5c3ecb44715e0fbc253bd60 (MD5) Previous issue date: 2016-02-17 / Muitos estudos acerca do aproveitamento de resíduos e sua utilização em matrizes cimentícias têm sido desenvolvidos, na busca de um destino adequado, uma vez que a construção civil é um dos maiores consumidores de materiais naturais em seus processos e produtos. As cinzas agroindustriais ocupam lugar de destaque dentre os resíduos com possibilidades de aplicação por apresentarem propriedades pozolânicas, como por exemplo, cinzas volantes, sílica ativa entre outros, contribuindo para a redução do consumo de cimento Portland e sustentabilidade da indústria de materiais cimentícios. O bagaço da cana-de-açúcar é um dos subprodutos do processo de produção da cana-de-açúcar, sendo o Brasil o maior produtor mundial. Neste trabalho foram produzidas cinzas a partir do beneficiamento por queima controlada e moagem da cinza do bagaço de cana-de-açúcar (CBCA) coletada em uma usina do estado de Pernambuco para avaliar a sua aplicação como adição mineral em matrizes de base cimentícia. A cinza coletada foi submetida a um processo prévio de secagem em estufa e peneiramento para retirada de materiais contaminantes (folhas, pedras e outros). Parte do material passante não sofreu tratamento térmico, sendo denominada CAN, o restante foi dividido em quatros frações, cada fração submetida a uma temperatura de queima: 300°C, 400°C, 500°C e 600°C, sendo denominadas CB300, CB400, CB500 e CB600, respectivamente. Após a queima, cada cinza passou por um processo de peneiramento/moagem e foi submetida a análises de fluorescência de raios X, difração de raios X, massa específica real por picnometria a gás e área superficial específica por B.E.T (Brunauer-Emmett-Teller). A reatividade das cinzas foi avaliada por meio de medições de condutividade elétrica em solução saturada de Ca(OH)2/cinzas e o índice de atividade com cal (IAC), foi baseado na ABNT NBR 5751 (2012). Os resultados por condutividade elétrica indicam tendência de reatividade do material estudado, quando comparado a pozolana de referência - MTC. O IAC das amostras com CBCA mostraram resultados satisfatórios apenas para as cinzas moídas por 7 horas. A moagem mostrou ser de fundamental importância para o aumento do potencial pozolânico da CBCA. A temperatura de calcinação se mostrou relevante quando da aplicação de 500ºC, acima deste valor ocorreu o decréscimo dos índices de pozolanicidade. / Many studies about waste recovery and your use in cement matrices have been developed on the search for a appropriate destination, since the civic construction is one of the largest consumers of natural materials in their processes and products. The agroindustrial ashes occupy prominent place among the residues with application possibilities for presenting pozzolanic properties, such as fly ash, silica fume among others, contributing for the reduction of the consumption of cement Portland and sustainability of cementitious materials industry. The bagasse of the sugarcane is one of the byproducts of the production process of sugarcane, with Brazil being the world's largest producer. In this work were produced ashes from the beneficiation by controlled burning and grinding of ash from sugarcane bagasse (CBCA) collected in a mill of Pernambuco to evaluate your application as mineral addition in cement-based matrices. The collected ash was submitted to a previous drying process in a kiln and sieving for removing contaminant material (leaves, stones and other) part of the passing material did not suffer thermal treatment, called CAN, the remainder was divided into four portions, each portion submitted to a firing temperature: 300 ° C, 400 ° C, 500 ° C and 600 ° C, called CB300, CB400, CB500 and CB600, respectively. After burning, each ash passed through a process of sieving/milling and was submitted to X-ray fluorescence analysis, X-ray diffraction, real specific mass by gas pycnometry and specific surface area by BET (Brunauer-Emmett-Teller). The reactivity of the ash was evaluated by means of electrical conductivity measurements in saturated solution of Ca(OH)2 / ashes. The activity index with lime (AIL), based on the ABNT NBR 5751 (2012). The results by electrical conductivity indicates tendency of reactivity of the studied material, when compared to the pozzolan of reference - MTC. The AIL of de samples with CBCA showed satisfactory results just for milled ashes for 7 hours. The milling showed to be of fundamental importance for improve the pozzolanic potential of the CBCA. The temperature showed to be relevant whe the application of 500ºC, above this value occurred decrease of pozzolanicity index.

O projeto desenvolvido enfocou a aplicação da difração de raios-X e método de Rietveld (DRX-Rietveld) na caracterização e quantificação do Cimento Portland, constituindo-se em contribuição pioneira sobre o tema em âmbito nacional. Foram estudadas amostras de pozolanas naturais e artificiais, subprodutos industriais de grande disponibilidade na indústria nacional, tais como escórias de alto-forno provenientes das siderúrgicas e cinzas volantes das termelétricas. Adicionalmente, foram estudadas amostras dos componentes utilizados para composição de cimentos laboratoriais, tais como clínqueres, calcários e fosfogesso, e por fim, cimento Portland com adições, preparados em laboratório. Também foram realizados ensaios para acompanhamento da hidratação do cimento Portland com uso da difração de raios-X e método de Rietveld. O cimento Portland é o material composto de clínquer, gesso e eventuais adições, tais como calcário, pozolanas e escórias. O clínquer de cimento Portland é o material sinterizado e peletizado, resultante da calcinação de uma mistura adequada de calcário e argila e, eventualmente, de componentes corretivos. O método de Rietveld, foi introduzido por Hugo Rietveld em 1969, tendo em base a simulação de todo o perfil difratométrico a partir de parâmetros estruturais das fases constituintes, permitindo refinar parâmetros de natureza instrumental e cristalográfica. A comparação do difratograma calculado com o observado e redução das diferenças através do método de mínimos quadrados permitem a obtenção de resultados quantitativos. Para desenvolvimento do projeto foram utilizadas técnicas analíticas tradicionais como apoio à difração de raios-X, tais como a microscopia óptica de luz transmitida, microscopia eletrônica de varredura (MEV-EDS), fluorescência de raios-X (FRX) e o calorímetro de condução. DRX-Rietveld apresentou-se como uma técnica de quantificação de elevada reprodutibilidade com vantagens de cunho técnico e logístico. As condições instrumentais e de coleta de difratogramas foram avaliadas, onde se verificou que a condição adequada para a obtenção de resultados de proporções de fases coerentes e em tempo reduzido pode ser obtida com coletas realizadas em 20s/passo, levando desta forma 10 minutos para sua realização, quando considerado o uso de detetores sensíveis a posição. Fendas divergentes automáticas e fixas testadas apresentaram resultados muito similares, validando a técnica nas diferentes condições. A redução no tempo de análise constitui um fator importante da técnica visando atender os interesses da indústria do cimento. A técnica estudada se mostrou adequada para a quantificação de componentes do cimento Portland tais como o calcário, materiais pozolânicos e escórias de alto-forno, e principalmente cimentos com estas adições. Com DRX-Rietveld foi possível avaliar as proporções das fases do clínquer, calcário e gipsita, e com a utilização de um padrão interno, a técnica possibilitou a quantificação de compostos com fase amorfa, o que é de grande importância para a correlação com as propriedades físico-mecânicas destes materiais. Resultados das proporções de calcário na quantificação dos cimentos apresentaram elevada correlação com as proporções dosadas em sua composição (R2=0,96-0,99), o que também foi observado com relação às proporções de fosfogesso dosadas (R2=0,99-1,0). Boas correlações também foram obtidas entre as proporções de cinzas volante e escória adicionadas nas amostras e os valores obtidos por DRX-Rietveld (R2=0,97-0,99 para cinza volante; R2=0,97 para escória). Ensaios DRX aplicados à uma pasta de cimento Portland mostraram-se adequados para o estudo quantitativo de cimentos hidratados e também para o acompanhamento das reações de hidratação. A técnica possibilitou a quantificação dos compostos hidratados como etringita, portlandita e C-S-H, o que foi aferido através de ensaios para determinação de calor de hidratação, mostrando resultados de refinamento confiáveis. / The project has focused on the application of X-ray diffraction and Rietveld method (XRD-Rietveld) on the characterization and quantification of Portland cement, and represents a pioneer scientific contribution on the theme in Brazil. Natural and artificial pozzolans, and also industrial byproducts that are highly available in the Brazilian industry were studied, as the blast furnace slags from steel works and fly ash from power stations. Furthermore components of laboratorial cements were studied, as clinker, limestone, gypsum, and finally the Portland cement with additions, prepared in laboratory. Hydration studies to follow the reactions in a cement paste were also performed using XRD-Rietveld. The Portland cement is composed by clinker, gypsum and fillers, as limestone, pozzolan and slags. Portland cement clinker is the sintered and pelletized product from calcination of an adequate mix of limestone and clay and minor corrective materials. The Rietveld method was introduced by Hugo Rietveld in 1969 and is based on the simulation of the whole diffraction spectrum from the components structural data, allowing for refining instrumental and crystallographic parameters. Quantitative values are obtained by comparing the calculated and actual diffractograms and minimizing differences mathematically through a least squares method. To develop the project several analytical traditional techniques were used with XRD: optical microscopy, electronic microscopic (SEM), X-ray fluorescence (XRF) and calorimeter. XRD-Rietveld presented as a high reproducibility technique with technical and logistics advantages. The evaluation of the instrumental conditions showed that to obtain a good quantitative result in reduced time were with a scan with 20s/step, a 10 minutes scan, possible with position sensitive detectors. Automatic (ADS) and fixed divergent slits (FDS) were tested, validating the technique in both conditions. The reduction in the time of analysis is very important to follow the cement industry interests on quality control. The technique was considered adequate to be applied on the quantification of Portland cement components such as limestone, pozzolanic materials and blast-furnace slags. With XRD-Rietveld, was possible to evaluate the clinker phases, limestone and gypsum, and using an internal standard, the technique lead to the quantification of compounds with amorphous phases, that is very important to correlate with the physic- mechanical properties of these materials. Results of limestone proportions in the quantification of cements presents a high correlation with the proportions added in the cement composition (R2=0,96-0,99), what was also observed in the case of gypsum added (R2=0,99-1,0). Good correlations were also obtained between the fly ash and slags proportions in the samples and XRD-Rietveld obtained values (R2=0,97-0,99 to fly ash; R2=0,97 to slag). XRD experiments applied to Portland cement paste were adequate to the quantitative analysis of hydrated cements and also to follow the hydration reactions. The technique permitted the quantification of hydration compounds such as ettringite, portlandite and C-S-H, that was confirmed using the calorimeter, showing good refinement results.

O projeto desenvolvido enfocou a aplicação da difração de raios-X e método de Rietveld (DRX-Rietveld) na caracterização e quantificação do Cimento Portland, constituindo-se em contribuição pioneira sobre o tema em âmbito nacional. Foram estudadas amostras de pozolanas naturais e artificiais, subprodutos industriais de grande disponibilidade na indústria nacional, tais como escórias de alto-forno provenientes das siderúrgicas e cinzas volantes das termelétricas. Adicionalmente, foram estudadas amostras dos componentes utilizados para composição de cimentos laboratoriais, tais como clínqueres, calcários e fosfogesso, e por fim, cimento Portland com adições, preparados em laboratório. Também foram realizados ensaios para acompanhamento da hidratação do cimento Portland com uso da difração de raios-X e método de Rietveld. O cimento Portland é o material composto de clínquer, gesso e eventuais adições, tais como calcário, pozolanas e escórias. O clínquer de cimento Portland é o material sinterizado e peletizado, resultante da calcinação de uma mistura adequada de calcário e argila e, eventualmente, de componentes corretivos. O método de Rietveld, foi introduzido por Hugo Rietveld em 1969, tendo em base a simulação de todo o perfil difratométrico a partir de parâmetros estruturais das fases constituintes, permitindo refinar parâmetros de natureza instrumental e cristalográfica. A comparação do difratograma calculado com o observado e redução das diferenças através do método de mínimos quadrados permitem a obtenção de resultados quantitativos. Para desenvolvimento do projeto foram utilizadas técnicas analíticas tradicionais como apoio à difração de raios-X, tais como a microscopia óptica de luz transmitida, microscopia eletrônica de varredura (MEV-EDS), fluorescência de raios-X (FRX) e o calorímetro de condução. DRX-Rietveld apresentou-se como uma técnica de quantificação de elevada reprodutibilidade com vantagens de cunho técnico e logístico. As condições instrumentais e de coleta de difratogramas foram avaliadas, onde se verificou que a condição adequada para a obtenção de resultados de proporções de fases coerentes e em tempo reduzido pode ser obtida com coletas realizadas em 20s/passo, levando desta forma 10 minutos para sua realização, quando considerado o uso de detetores sensíveis a posição. Fendas divergentes automáticas e fixas testadas apresentaram resultados muito similares, validando a técnica nas diferentes condições. A redução no tempo de análise constitui um fator importante da técnica visando atender os interesses da indústria do cimento. A técnica estudada se mostrou adequada para a quantificação de componentes do cimento Portland tais como o calcário, materiais pozolânicos e escórias de alto-forno, e principalmente cimentos com estas adições. Com DRX-Rietveld foi possível avaliar as proporções das fases do clínquer, calcário e gipsita, e com a utilização de um padrão interno, a técnica possibilitou a quantificação de compostos com fase amorfa, o que é de grande importância para a correlação com as propriedades físico-mecânicas destes materiais. Resultados das proporções de calcário na quantificação dos cimentos apresentaram elevada correlação com as proporções dosadas em sua composição (R2=0,96-0,99), o que também foi observado com relação às proporções de fosfogesso dosadas (R2=0,99-1,0). Boas correlações também foram obtidas entre as proporções de cinzas volante e escória adicionadas nas amostras e os valores obtidos por DRX-Rietveld (R2=0,97-0,99 para cinza volante; R2=0,97 para escória). Ensaios DRX aplicados à uma pasta de cimento Portland mostraram-se adequados para o estudo quantitativo de cimentos hidratados e também para o acompanhamento das reações de hidratação. A técnica possibilitou a quantificação dos compostos hidratados como etringita, portlandita e C-S-H, o que foi aferido através de ensaios para determinação de calor de hidratação, mostrando resultados de refinamento confiáveis. / The project has focused on the application of X-ray diffraction and Rietveld method (XRD-Rietveld) on the characterization and quantification of Portland cement, and represents a pioneer scientific contribution on the theme in Brazil. Natural and artificial pozzolans, and also industrial byproducts that are highly available in the Brazilian industry were studied, as the blast furnace slags from steel works and fly ash from power stations. Furthermore components of laboratorial cements were studied, as clinker, limestone, gypsum, and finally the Portland cement with additions, prepared in laboratory. Hydration studies to follow the reactions in a cement paste were also performed using XRD-Rietveld. The Portland cement is composed by clinker, gypsum and fillers, as limestone, pozzolan and slags. Portland cement clinker is the sintered and pelletized product from calcination of an adequate mix of limestone and clay and minor corrective materials. The Rietveld method was introduced by Hugo Rietveld in 1969 and is based on the simulation of the whole diffraction spectrum from the components structural data, allowing for refining instrumental and crystallographic parameters. Quantitative values are obtained by comparing the calculated and actual diffractograms and minimizing differences mathematically through a least squares method. To develop the project several analytical traditional techniques were used with XRD: optical microscopy, electronic microscopic (SEM), X-ray fluorescence (XRF) and calorimeter. XRD-Rietveld presented as a high reproducibility technique with technical and logistics advantages. The evaluation of the instrumental conditions showed that to obtain a good quantitative result in reduced time were with a scan with 20s/step, a 10 minutes scan, possible with position sensitive detectors. Automatic (ADS) and fixed divergent slits (FDS) were tested, validating the technique in both conditions. The reduction in the time of analysis is very important to follow the cement industry interests on quality control. The technique was considered adequate to be applied on the quantification of Portland cement components such as limestone, pozzolanic materials and blast-furnace slags. With XRD-Rietveld, was possible to evaluate the clinker phases, limestone and gypsum, and using an internal standard, the technique lead to the quantification of compounds with amorphous phases, that is very important to correlate with the physic- mechanical properties of these materials. Results of limestone proportions in the quantification of cements presents a high correlation with the proportions added in the cement composition (R2=0,96-0,99), what was also observed in the case of gypsum added (R2=0,99-1,0). Good correlations were also obtained between the fly ash and slags proportions in the samples and XRD-Rietveld obtained values (R2=0,97-0,99 to fly ash; R2=0,97 to slag). XRD experiments applied to Portland cement paste were adequate to the quantitative analysis of hydrated cements and also to follow the hydration reactions. The technique permitted the quantification of hydration compounds such as ettringite, portlandite and C-S-H, that was confirmed using the calorimeter, showing good refinement results.

Made available in DSpace on 2014-12-17T14:08:34Z (GMT). No. of bitstreams: 1 TiagoRS.pdf: 224853 bytes, checksum: a7ecf3c3cba57ff6b3ea1ac7c4fb7f05 (MD5) Previous issue date: 2009-06-02 / Petr?leo Brasileiro SA - PETROBRAS / Cementation operation consists in an extremely important work for the phases of perforation and completion of oil wells, causing a great impact on the well productivity. Several problems can occur with the cement during the primary cementation, as well as throughout the productive period. The corrective operations are frequent, but they are expensive and demands production time. Besides the direct cost, prejudices from the interruption of oil and gas production till the implementation of a corrective operation must be also taken into account. The purpose of this work is the development of an alternative cement paste constituted of Portland cement and porcelainized stoneware residue produced by ceramic industry in order to achieve characteristics as low permeability, high tenacity, and high mechanical resistance, capable of supporting various operations as production or oil wells recuperation. Four different concentration measures of hydrated paste were evaluated: a reference paste, and three additional ones with ceramic residue in concentrations of the order of 10%, 20% and 30% in relation to cement dough. High resistance and low permeability were found in high concentration of residues, as well as it was proved the pozolanic reactivity of the residue in relation to Portland cement, which was characterized through x-ray and thermogravimetry assays. It was evident the decrease of calcium hydroxide content, once it was substituted by formation of new hydrated products as it was added ceramic residue / A opera??o de cimenta??o consiste em um trabalho de extrema import?ncia para as fases de perfura??o e completa??o de po?os de petr?leo e tem grande impacto sobre a produtividade do po?o. Muitos problemas podem ocorrer com o cimento, tanto durante a cimenta??o prim?ria do po?o como tamb?m durante seu per?odo produtivo. As opera??es para corre??o destes problemas s?o freq?entes, por?m onerosas e demandam tempo de produ??o. Al?m do custo direto da opera??o corretiva, deve m ser ontabilizados, ainda, preju?zos devidos ? interrup??o da produ??o de ?leo e g?s at? que uma opera??o de corre??o seja realizada. Este trabalho tem como objetivo o desenvolvimento de pastas cimentantes alternativas, constitu?das por cimento Portland e um res?duo de porcelanato produzido pela ind?stria cer?mica, a fim de obter caracter?sticas como baixa permeabilidade, alta tenacidade e alta resist?ncia mec?nica, capazes de suportar as diversas opera??es, tanto de produ??o como de recupera??o de po?os de petr?leo. Foram avaliadas quatro concentra??es diferentes de pastas hidratadas: uma pasta de refer?ncia e tr?s pastas contendo res?duo cer?mico nas concentra??es de 10%, 20% e 30%, em rela??o ? massa do cimento. Foram encontradas, para as maiores concentra??es de res?duo, maior resist?ncia mec?nica e menor permeabilidade, al?m de ser comprovada a reatividade pozol?nica do res?duo com o cimento Portland. Esta foi caracterizada atrav?s dos ensaios de Difra??o de Raios X e Termogravimetria, ficando clara a diminui??o do teor de hidr?xido de c?lcio, substitu?do pela forma??o de novos produtos hidratados ? medida que se adicionava o res?duo cer?mico

Orientador: Jorge Luís Akasaki / Resumo: A indústria cimenteira tem passado por pressões cada vez mais constantes, referentes aos impactos ambientais causados pela emissão de gases na produção de cimento Portland e, atualmente, pela crise econômica que o setor da construção civil vem passando. Estes acontecimentos têm levado pesquisadores a investigarem novas formas de se obter aglomerantes alternativos, de maneira mais sustentável e econômica. Aliada a este problema, está a geração de resíduos de biomassa provenientes da atividade agroindustrial. Uma das alternativas criadas para a redução da emissão de CO2 e do consumo de cimento Portland é a produção de novos aglomerantes à base de argilas calcinadas. Além de reduzir significativamente o teor de cimento em matrizes cimentantes, a utilização destes aglomerantes proporciona economia de energia e menor temperatura de queima, liberando menos CO2 que o cimento durante sua produção. Assim, o objetivo desta pesquisa foi produzir e caracterizar um novo aglomerante formado pela mistura da cinza do bagaço da cana-de-açúcar e argila calcinada, denominada de CBA. A proporções entre bagaço, argila e água foram de 1,000:0,150:0,125, em massa, respectivamente. Após a calcinação, a cinza passou por processo de peneiramento e moagem. O estudo foi divido em três principais etapas: produção e caracterização da CBA; estudo da reatividade da CBA em pastas e; análise do comportamento mecânico de argamassas produzidas com substituição parcial de cimento por CBA. Inicialmente, a cinza p... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Cement industry has been suffering pressure increasing, related to environments impacts due gas emission promoted by Portland cement production and, furthermore, due the currently crisis in civil construction sector that has been passing through. These events have lad researchers to investigate new forms of obtaining alternative binders more sustainable and economic. Allied to this problem, there is to biomass residues generation from agro-industry activity. One of the alternatives created to reduce the CO2 emissions and Portland cement consumption is the manufacturing of new binders based on thermally calcined clay. Besides it to reduce significantly cement content in cementitious matrix, these binders provides energy saving and lower calcination temperature, realizing less CO2 than Portland cement related to its production. Thus, the main of this objective of this study was to produce and characterize a new binder, composed by sugar-cane bagasse ash and calcined clay (SCA). The content of sugarcane bagasse, clay and water in mixture was 1/0.15/0.125, by mass, respectively. After calcination procedure, SCA passed through sieving and mill process. The study was separated in three stages: characterization of SCA; SCA reactivity study in pastes and; mechanical behavior analysis in cement mortars produced with partial cement replacement by SCA. Initially, SCA was characterized by physicochemical tests, being X-ray diffraction, thermogravimetric analysis, scanning electron micros... (Complete abstract click electronic access below) / Mestre

Submitted by Alan Henrique Vicentini (vicentini.alanh@gmail.com) on 2018-07-19T12:54:56Z No. of bitstreams: 1 ALAN HENRIQUE VICENTINI - DISSERTAÇÃO - ENGENHARIA CIVIL.pdf: 4878364 bytes, checksum: 78fb1552972193124495e015f63d3b91 (MD5) / Approved for entry into archive by Cristina Alexandra de Godoy null (cristina@adm.feis.unesp.br) on 2018-07-19T13:49:52Z (GMT) No. of bitstreams: 1 vicentini_ah_me_ilha.pdf: 4878364 bytes, checksum: 78fb1552972193124495e015f63d3b91 (MD5) / Made available in DSpace on 2018-07-19T13:49:52Z (GMT). No. of bitstreams: 1 vicentini_ah_me_ilha.pdf: 4878364 bytes, checksum: 78fb1552972193124495e015f63d3b91 (MD5) Previous issue date: 2018-06-04 / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / A indústria cimenteira tem passado por pressões cada vez mais constantes, referentes aos impactos ambientais causados pela emissão de gases na produção de cimento Portland e, atualmente, pela crise econômica que o setor da construção civil vem passando. Estes acontecimentos têm levado pesquisadores a investigarem novas formas de se obter aglomerantes alternativos, de maneira mais sustentável e econômica. Aliada a este problema, está a geração de resíduos de biomassa provenientes da atividade agroindustrial. Uma das alternativas criadas para a redução da emissão de CO2 e do consumo de cimento Portland é a produção de novos aglomerantes à base de argilas calcinadas. Além de reduzir significativamente o teor de cimento em matrizes cimentantes, a utilização destes aglomerantes proporciona economia de energia e menor temperatura de queima, liberando menos CO2 que o cimento durante sua produção. Assim, o objetivo desta pesquisa foi produzir e caracterizar um novo aglomerante formado pela mistura da cinza do bagaço da cana-de-açúcar e argila calcinada, denominada de CBA. A proporções entre bagaço, argila e água foram de 1,000:0,150:0,125, em massa, respectivamente. Após a calcinação, a cinza passou por processo de peneiramento e moagem. O estudo foi divido em três principais etapas: produção e caracterização da CBA; estudo da reatividade da CBA em pastas e; análise do comportamento mecânico de argamassas produzidas com substituição parcial de cimento por CBA. Inicialmente, a cinza passou por ensaios de caracterização físico-química, sendo realizados os ensaios de difração de raios-X, termogravimetria, microscopia eletrônica de varredura, espectroscopia de infravermelho por transformada de Fourier, fluorescência de raios-X e granulometria a laser. A segunda etapa consistiu em avaliar a ação da cinza em pastas de cal e de cimento, através dos ensaios de espectroscopia de infravermelho por transformada de Fourier, microscopia eletrônica de varredura e termogravimetria. A última etapa baseou-se em avaliar a consistência e o comportamento mecânico de resistência à compressão de argamassas produzidas com substituição de cimento por CBA nos teores de 10%, 20%, 30% 40% e 50%. Foi possível substituir cimento por CBA em até 50% em massa, mostrando que o material possui grande potencial de ser utilizado na produção de aglomerantes, além de ser energeticamente viável, devido à geração de calor durante sua produção. / Cement industry has been suffering pressure increasing, related to environments impacts due gas emission promoted by Portland cement production and, furthermore, due the currently crisis in civil construction sector that has been passing through. These events have lad researchers to investigate new forms of obtaining alternative binders more sustainable and economic. Allied to this problem, there is to biomass residues generation from agro-industry activity. One of the alternatives created to reduce the CO2 emissions and Portland cement consumption is the manufacturing of new binders based on thermally calcined clay. Besides it to reduce significantly cement content in cementitious matrix, these binders provides energy saving and lower calcination temperature, realizing less CO2 than Portland cement related to its production. Thus, the main of this objective of this study was to produce and characterize a new binder, composed by sugar-cane bagasse ash and calcined clay (SCA). The content of sugarcane bagasse, clay and water in mixture was 1/0.15/0.125, by mass, respectively. After calcination procedure, SCA passed through sieving and mill process. The study was separated in three stages: characterization of SCA; SCA reactivity study in pastes and; mechanical behavior analysis in cement mortars produced with partial cement replacement by SCA. Initially, SCA was characterized by physicochemical tests, being X-ray diffraction, thermogravimetric analysis, scanning electron microscope, Fourier transform infrared spectroscopy analysis, X-ray fluorescence spectroscopy and laser granulometry analysis. The second stage consisted of to evaluate SCA behavior in lime/SCA pastes and Portland cement/SCA pastes systems, through Fourier transform infrared spectroscopy, scanning electron microscope and thermogravimetric analysis. The third and last stage consisted of to evaluate the plastic consistence and mechanical behavior by compressive strength in mortars produced with partial cement replacement by SCA in 10%, 20%, 30%, 40% and 50% contents, by mass. It was possible replace cement by SCA in up to 50% content, showing that this material has potential to be widely utilized in production of binders, besides being energetically viable, due to the heat generation during SCA production. / CNPq: 830017/2001-1