Fatigue life evaluation of A356 aluminum alloy used for engine\'s cylinder head / Avaliação da vida em fadiga de liga de alumínio A356 utilizada em cabeçote de motorAngeloni, Mauricio 27 April 2011 (has links)
In order to characterize mechanical components used in high responsibility applications, the knowledge of chemical composition and results from regular experiments such as traction, impact and hardness tests is important, but not sufficient. They cannot supply the necessary information that permit anticipating, in a reliable way, the components behavior in actual working conditions. As an example, there are engines cylinder head submitted to mechanical and thermal tensions that are relatively high during the in service use, and very high in same very demanding condition. During long run times and any failure in the cooling and/or lubrication the temperature may reach 300ºC. This temperature variation causes thermal shocks which may generate cracks and/or a wide ranging of plastic deformation in regions close to the pistons. Even not considering the thermal shock effects caused by failure, even so, a short number of start-up and shutdown cycles of engine, are considered the main cause of small cracks. This indicates that the generation of cracks in cylinder head may be considered as low cycle thermomechanical fatigue problem. Another problem is the microstructure heterogeneity in the component due to the casting process, leading to different physical and mechanical properties in the same piece. Besides the presence of porosity generated by gas bubbles and voids of solidification, which may be as great as short crack, reducing the nucleation life and changing the problems focus for the fatigue crack growth. The purpose of this study was to determine the isothermal and thermomechanical fatigue property through low cycle fatigue, as well as the fatigue crack growth, relaxation, microestrutural characterization and modeling of mechanical behavior by finite element for the aluminum alloy employed in the manufacture of engine cylinder head by the national automotive industry. Isothermal fatigue experiments were carried out at temperature of 120ºC and 280ºC and the thermomechanical performed in phase between the temperatures of 120ºC and 280ºC. The relaxation experiments were performed at some temperatures with trapezoidal wave loading, whereas the experiments of fatigue crack growth carried out at temperatures of 120ºC, 200ºC and 280ºC for sine and trapezoidal wave loading in displacement and load control. The microstructure analysis was also made in the specimens after the fatigue test by optical microscopy and scanning electron microscopy SEM. The results of these experiments showed that the casting defects and materials inhomogeneities, coupled long run times in high temperatures and loads, are a critical factor in the component performance. These results help us to establish accurate models for life prediction of the engine cylinder head. / Para caracterizar componentes usados em aplicações de alta responsabilidade não basta apenas conhecer a composição química e os resultados de ensaios de tração, impacto e dureza, pois estes podem não fornecer os subsídios necessários que permitam prever, de maneira confiável, o comportamento dos componentes nas condições reais de trabalho. Exemplo disto são os cabeçotes de motor automotivos, submetidos a tensões térmicas e mecânicas relativamente altas durante seu uso normal e altíssimo em condições extremas. Durante longos tempos de funcionamento e eventuais falhas na refrigeração e ou lubrificação a temperatura pode chegar a valores próximos de 300ºC. Esta variação de temperaturas provoca choques térmicos que podem gerar trincas e/ou uma grande quantidade de deformação plástica em regiões próximas aos pistões. Desconsiderando a presença de choques térmicos provocados por falhas, ainda assim, uma pequena quantidade de ciclos de acionamento e parada do motor, é considerada como os principais causadores de pequenas trincas. Isso indica que o surgimento de trincas em cabeçotes de motor deve ser considerado um problema de fadiga termomecânica de baixo ciclo. Outro problema é a heterogeneidade microestrutural no componente devido ao processo de fundição, levando a propriedades mecânicas e físicas diferentes em uma mesma peça. Além da presença de porosidade gerada por bolhas de gás e vazios de solidificação, que podem adquirir tamanho tal que se aproximem de pequenas trincas, diminuindo a vida para a nucleação e assim mudando o foco do problema para o de propagação de trinca por fadiga. A proposta deste trabalho foi a de determinar as propriedades de fadiga isotérmica e termomecânica através de ensaios de fadiga de baixo ciclo, bem como as propriedades de propagação de trinca por fadiga, relaxação, caracterização microestrutural e modelagem do comportamento mecânico por elementos finitos para a liga de alumínio utilizada na fabricação de cabeçotes de motores automotivos pela indústria nacional. Os ensaios de fadiga isotérmica foram realizados nas temperaturas de 120ºC e 280ºC e os ensaios termomecânicos foram realizados em fase entre as temperaturas de 120ºC e 280ºC. Os ensaios de relaxação foram realizados em várias temperaturas com carregamento de onda trapezoidal, enquanto que os ensaios de propagação de trinca por fadiga foram realizados nas temperaturas de 120ºC, 200ºC e 280ºC para carregamentos de onda senoidal e trapezoidal em controle de carga e de deslocamento. Foi feita também análise microestrutural nos corpos de prova, após os ensaios de fadiga, por microscopia óptica e por microscopia eletrônica de varredura MEV. Os resultados destes ensaios mostraram que os defeitos de fundição e a falta de homogeneidade no material, aliados a longos tempos de exposição a carregamentos e em altas temperaturas, constituem um fator crítico no desempenho do componente. Estes resultados ajudarão a estabelecer modelos precisos de previsão de vida para os cabeçotes de motor.
|
2 |
Estudo da tenacidade e fadiga em meio assistido da liga de Al-Li de grau aeronáutico AA2050-T84 / Study toughness and fatigue in atmosphere assisted of the aircraft alloy grade AA2050-T84Maciel, Carla Isabel dos Santos 12 July 2013 (has links)
A indústria aeronáutica tem buscado melhorias no conceito de integridade estrutural, a partir do desenvolvimento de projetos mais otimizados com a produção de aeronaves mais leves e seguras. Tais projetos garantem aeronaves operacionalmente mais viáveis e redução no consumo de combustível, beneficiando o fabricante, os operadores e a população em geral, pois aplica o conceito de aeronave verde. Estruturas aeronáuticas em operação recebem solicitações de cargas típicas de vôo, como pressurização, sustentação, que por sua vez, geram esforços dos mais variados tipos e suas combinações, como tração, compressão, fadiga, torção, flexão, flambagem, cargas aeroelásticas, vibrações e flutter, associados a ambientes críticos. O conhecimento sobre o comportamento do material estrutural perante ambientes corrosivo ou de baixa temperatura, é importante para avaliação da vida útil das aeronaves. Neste contexto, o objetivo deste trabalho foi avaliar o comportamento da liga AA2050-T84 sob ponto de vista de corrosão-fadiga e tenacidade a fratura em criogenia e, correlacionar com a microestrutura e fractografia através de ensaios mecânicos e de tenacidade a fratura em temperatura ambiente e criogênica. As condições de ensaios foram determinadas próximas a de serviço a que o material será inserido sendo, para criogenia -54 ºC e para os ensaios de propagação de trinca por fadiga em atmosfera ambiente e névoa salina com concentração de solução de 3,5% e 5% NaCl, frequência de 15Hz e razões de carga R = 0,1 e 0,5. Os resultados em criogenia mostraram que há melhora nas propriedades trativas e estabilidade na tenacidade, pois o material retém dutilidade com o decréscimo da temperatura. Os ensaios de propagação de trinca por fadiga foram executados com ΔK decrescente e os parâmetros para geração de névoa salina foram determinados experimentalmente. As curvas de crescimento de trinca e determinação do fator limite foram comparadas quanto a razão de carga e atmosfera de ensaio. Observou-se que para os ensaios de propagação de trinca por fadiga a presença da névoa salina acelera a taxa de propagação e resultam em um fator limite menor. / The aviation industry has sought improvements with the concept of structural integrity, from the development of more optimized designs with production aircraft with low weight and secure. These projects ensure an aircraft more operationally doable and reduced fuel consumption, benefiting the manufacturer, operators and the people, applying the concept of green aircraft. Aerospace structures in operation receive requests loads typical of flight, how pressurization support and lift that produce several types and combinations of requests, such as tensile, compression, fatigue, torsion, bending, buckling , aeroelastic loads, vibration and flutter associated with critical environments. Knowledge about the behavior of the structural material into corrosive environments or cryogenic temperature, it is important for evaluation to the lifetime of the aircraft. Accordingly , the aim of this study was to estimate the behavior of AA2050 - T84 alloy, about corrosion-fatigue and fracture toughness at cryogenic situations and correlate with microstructure and fractography, by mechanical tests and fracture toughness at room temperature and cryogenic. The test conditions has been determined near of the service that the material will be inserted, for cryogenic temperature -54 ºC and testing of fatigue crack propagation in air and salt spray with concentration of 3.5% and 5% NaCl, frequency 15Hz and load ratios R = 0.1 and 0.5. The cryogenic results showed that there improvement in tensile properties and stability in toughness due the restraint of ductility with decreasing temperature. Tests of fatigue crack propagation were carried out with ΔK decreasing and the parameters to obtain salt spray were determined experimentally. The crack growth curves and determination of the threshold were compared the according to load ratio and test atmosphere. In the fatigue crack propagation it was observed that presence of salt spray accelerates the rate of propagation and result in a lower threshold.
|
3 |
Resistência à fadiga de tubo API 5L X65 cladeado e soldado circunferencialmente com eletrodos de Inconel® 625 / Fatigue strength of API 5L X65 cladded pipe girth welded with Inconel® 625 electrodesSantos, Elielson Alves dos 06 April 2016 (has links)
As recentes descobertas de petróleo e gás na camada do Pré-sal representam um enorme potencial exploratório no Brasil, entretanto, os desafios tecnológicos para a exploração desses recursos minerais são imensos e, consequentemente, têm motivado o desenvolvimento de estudos voltados a métodos e materiais eficientes para suas produções. Os tubos condutores de petróleo e gás são denominados de elevadores catenários ou do inglês \"risers\", e são elementos que necessariamente são soldados e possuem fundamental importância nessa cadeia produtiva, pois transportam petróleo e gás natural do fundo do mar à plataforma, estando sujeitos a carregamentos dinâmicos (fadiga) durante sua operação. Adicionalmente, um dos problemas centrais à produção de óleo e gás das reservas do Pré-Sal está diretamente associado a meios altamente corrosivos, tais como H2S e CO2. Uma forma mais barata de proteção dos tubos é a aplicação de uma camada de um material metálico resistente à corrosão na parte interna desses tubos (clad). Assim, a união entre esses tubos para formação dos \"risers\" deve ser realizada pelo emprego de soldas circunferenciais de ligas igualmente resistentes à corrosão. Nesse contexto, como os elementos soldados são considerados possuir defeitos do tipo trinca, para a garantia de sua integridade estrutural quando submetidos a carregamentos cíclicos, é necessário o conhecimento das taxas de propagação de trinca por fadiga da solda circunferencial. Assim, neste trabalho, foram realizados ensaios de propagação de trinca por fadiga na região da solda circunferencial de Inconel® 625 realizada em tubo de aço API 5L X65 cladeado, utilizando corpos de prova do tipo SEN(B) (Single Edge Notch Bending) com relações entre espessura e largura (B/W) iguais a 0,5, 1 e 2. O propósito central deste trabalho foi de obter a curva da taxa de propagação de trinca por fadiga (da/dN) versus a variação do fator de intensidade de tensão (ΔK) para o metal de solda por meio de ensaios normatizados, utilizando diferentes técnicas de acompanhamento e medição da trinca. A monitoração de crescimento da trinca foi feita por três técnicas: variação da flexibilidade elástica (VFE), queda de potencial elétrico (QPE) e análise de imagem (Ai). Os resultados mostraram que as diferentes relações B/W utilizadas no estudo não alteraram significantemente as taxas de propagação de trinca por fadiga, respeitado que a propagação aconteceu em condições de escoamento em pequena escala na frente da trinca. Os resultados de propagação de trinca por fadiga permitiram a obtenção das regiões I e II da curva da/dN versus ΔK para o metal de solda. O valor de ΔKlim obtido para o mesmo foi em torno de 11,8 MPa.m1/2 e os valores encontrados das constantes experimentais C e m da equação de Paris-Erdogan foram respectivamente iguais a 1,55 x10-10 [(mm/ciclo)/(MPa.m1/2)m] e 4,15. A propagação de trinca no metal de solda deu-se por deformação plástica, com a formação de estrias de fadiga. / Recent oil and gas discoveries in the Pre-Salt layer represent a huge exploration potential in Brazil, however, the technological challenges for the exploitation of these mineral resources are immense and therefore have motivated the development of studies looking for efficient methods and materials for their productions. The oil and gas pipellines, called risers, are elements that are necessarily welded and have fundamental importance in the production chain, since they transport oil and natural gas from the sea bed to the platforms and are subject to dynamic loads (fatigue) during operation. Additionally, one of the central problems in the production of oil and gas in the Pre-Salt reserves is directly associated with a highly corrosive media, such as H2S and CO2. A cheaper way to protect the pipelines from these medias is applying a protective layer of a corrosion resistant metal on the inner diameter of these pipes, creating a cladded pipe. Thus, a joining process of these pipes to form the risers must be carried out by the use of girth welds with a corrosion resistance material similar to the clad metal. As the welded structures are seen as potential location of \"crack like\" defects, to ensure the structural integrity of such component when subjected to repetitive loading conditions, it is necessary to know the fatigue crack growth rates for the girth weld. Therefore, in this work it was carried out fatigue crack propagation tests in the weld region of an API 5L X65 cladded pipe with Inconel® 625, girth welded using Inconel® 625 electrodes. From the welded region, Single Edge Notch Bending specimens, SEN(B), were removed with different thickness and width ratios (B/W= 0.5, 1, and 2). From the fatigue tests, the crack propagation rates (da/dN) as function of the variation of the stress intensity factor (ΔK), were determined for the weld metal, using different crack size measurement techniques: the elastic compliance (EC), electric potential drop (EPD) and image analysis (IA). The results showed that the different B/W ratios used in study did not modified significantly the fatigue crack growth rates, considering that crack propagation took place under small scale yielding conditions. The results of fatigue crack growth tests allowed to obtain the regions I and II of da/dN x ΔK curves for the weld metal. The ΔKth value obtained for the weld metal was around 11,8 MPa.m1/2 and the found values of the experimental constants C and m of Paris-Erdogan\'s equation were respectively equal to 1,55 x10-10 [(mm/cycle)/( MPa.m1/2)m] and 4.15. The micromechanism of fatigue crack growth took place by plastic deformation, with the formation of fatigue striations.
|
4 |
Resistência à fadiga de tubo API 5L X65 cladeado e soldado circunferencialmente com eletrodos de Inconel® 625 / Fatigue strength of API 5L X65 cladded pipe girth welded with Inconel® 625 electrodesElielson Alves dos Santos 06 April 2016 (has links)
As recentes descobertas de petróleo e gás na camada do Pré-sal representam um enorme potencial exploratório no Brasil, entretanto, os desafios tecnológicos para a exploração desses recursos minerais são imensos e, consequentemente, têm motivado o desenvolvimento de estudos voltados a métodos e materiais eficientes para suas produções. Os tubos condutores de petróleo e gás são denominados de elevadores catenários ou do inglês \"risers\", e são elementos que necessariamente são soldados e possuem fundamental importância nessa cadeia produtiva, pois transportam petróleo e gás natural do fundo do mar à plataforma, estando sujeitos a carregamentos dinâmicos (fadiga) durante sua operação. Adicionalmente, um dos problemas centrais à produção de óleo e gás das reservas do Pré-Sal está diretamente associado a meios altamente corrosivos, tais como H2S e CO2. Uma forma mais barata de proteção dos tubos é a aplicação de uma camada de um material metálico resistente à corrosão na parte interna desses tubos (clad). Assim, a união entre esses tubos para formação dos \"risers\" deve ser realizada pelo emprego de soldas circunferenciais de ligas igualmente resistentes à corrosão. Nesse contexto, como os elementos soldados são considerados possuir defeitos do tipo trinca, para a garantia de sua integridade estrutural quando submetidos a carregamentos cíclicos, é necessário o conhecimento das taxas de propagação de trinca por fadiga da solda circunferencial. Assim, neste trabalho, foram realizados ensaios de propagação de trinca por fadiga na região da solda circunferencial de Inconel® 625 realizada em tubo de aço API 5L X65 cladeado, utilizando corpos de prova do tipo SEN(B) (Single Edge Notch Bending) com relações entre espessura e largura (B/W) iguais a 0,5, 1 e 2. O propósito central deste trabalho foi de obter a curva da taxa de propagação de trinca por fadiga (da/dN) versus a variação do fator de intensidade de tensão (ΔK) para o metal de solda por meio de ensaios normatizados, utilizando diferentes técnicas de acompanhamento e medição da trinca. A monitoração de crescimento da trinca foi feita por três técnicas: variação da flexibilidade elástica (VFE), queda de potencial elétrico (QPE) e análise de imagem (Ai). Os resultados mostraram que as diferentes relações B/W utilizadas no estudo não alteraram significantemente as taxas de propagação de trinca por fadiga, respeitado que a propagação aconteceu em condições de escoamento em pequena escala na frente da trinca. Os resultados de propagação de trinca por fadiga permitiram a obtenção das regiões I e II da curva da/dN versus ΔK para o metal de solda. O valor de ΔKlim obtido para o mesmo foi em torno de 11,8 MPa.m1/2 e os valores encontrados das constantes experimentais C e m da equação de Paris-Erdogan foram respectivamente iguais a 1,55 x10-10 [(mm/ciclo)/(MPa.m1/2)m] e 4,15. A propagação de trinca no metal de solda deu-se por deformação plástica, com a formação de estrias de fadiga. / Recent oil and gas discoveries in the Pre-Salt layer represent a huge exploration potential in Brazil, however, the technological challenges for the exploitation of these mineral resources are immense and therefore have motivated the development of studies looking for efficient methods and materials for their productions. The oil and gas pipellines, called risers, are elements that are necessarily welded and have fundamental importance in the production chain, since they transport oil and natural gas from the sea bed to the platforms and are subject to dynamic loads (fatigue) during operation. Additionally, one of the central problems in the production of oil and gas in the Pre-Salt reserves is directly associated with a highly corrosive media, such as H2S and CO2. A cheaper way to protect the pipelines from these medias is applying a protective layer of a corrosion resistant metal on the inner diameter of these pipes, creating a cladded pipe. Thus, a joining process of these pipes to form the risers must be carried out by the use of girth welds with a corrosion resistance material similar to the clad metal. As the welded structures are seen as potential location of \"crack like\" defects, to ensure the structural integrity of such component when subjected to repetitive loading conditions, it is necessary to know the fatigue crack growth rates for the girth weld. Therefore, in this work it was carried out fatigue crack propagation tests in the weld region of an API 5L X65 cladded pipe with Inconel® 625, girth welded using Inconel® 625 electrodes. From the welded region, Single Edge Notch Bending specimens, SEN(B), were removed with different thickness and width ratios (B/W= 0.5, 1, and 2). From the fatigue tests, the crack propagation rates (da/dN) as function of the variation of the stress intensity factor (ΔK), were determined for the weld metal, using different crack size measurement techniques: the elastic compliance (EC), electric potential drop (EPD) and image analysis (IA). The results showed that the different B/W ratios used in study did not modified significantly the fatigue crack growth rates, considering that crack propagation took place under small scale yielding conditions. The results of fatigue crack growth tests allowed to obtain the regions I and II of da/dN x ΔK curves for the weld metal. The ΔKth value obtained for the weld metal was around 11,8 MPa.m1/2 and the found values of the experimental constants C and m of Paris-Erdogan\'s equation were respectively equal to 1,55 x10-10 [(mm/cycle)/( MPa.m1/2)m] and 4.15. The micromechanism of fatigue crack growth took place by plastic deformation, with the formation of fatigue striations.
|
5 |
Estudo da tenacidade e fadiga em meio assistido da liga de Al-Li de grau aeronáutico AA2050-T84 / Study toughness and fatigue in atmosphere assisted of the aircraft alloy grade AA2050-T84Carla Isabel dos Santos Maciel 12 July 2013 (has links)
A indústria aeronáutica tem buscado melhorias no conceito de integridade estrutural, a partir do desenvolvimento de projetos mais otimizados com a produção de aeronaves mais leves e seguras. Tais projetos garantem aeronaves operacionalmente mais viáveis e redução no consumo de combustível, beneficiando o fabricante, os operadores e a população em geral, pois aplica o conceito de aeronave verde. Estruturas aeronáuticas em operação recebem solicitações de cargas típicas de vôo, como pressurização, sustentação, que por sua vez, geram esforços dos mais variados tipos e suas combinações, como tração, compressão, fadiga, torção, flexão, flambagem, cargas aeroelásticas, vibrações e flutter, associados a ambientes críticos. O conhecimento sobre o comportamento do material estrutural perante ambientes corrosivo ou de baixa temperatura, é importante para avaliação da vida útil das aeronaves. Neste contexto, o objetivo deste trabalho foi avaliar o comportamento da liga AA2050-T84 sob ponto de vista de corrosão-fadiga e tenacidade a fratura em criogenia e, correlacionar com a microestrutura e fractografia através de ensaios mecânicos e de tenacidade a fratura em temperatura ambiente e criogênica. As condições de ensaios foram determinadas próximas a de serviço a que o material será inserido sendo, para criogenia -54 ºC e para os ensaios de propagação de trinca por fadiga em atmosfera ambiente e névoa salina com concentração de solução de 3,5% e 5% NaCl, frequência de 15Hz e razões de carga R = 0,1 e 0,5. Os resultados em criogenia mostraram que há melhora nas propriedades trativas e estabilidade na tenacidade, pois o material retém dutilidade com o decréscimo da temperatura. Os ensaios de propagação de trinca por fadiga foram executados com ΔK decrescente e os parâmetros para geração de névoa salina foram determinados experimentalmente. As curvas de crescimento de trinca e determinação do fator limite foram comparadas quanto a razão de carga e atmosfera de ensaio. Observou-se que para os ensaios de propagação de trinca por fadiga a presença da névoa salina acelera a taxa de propagação e resultam em um fator limite menor. / The aviation industry has sought improvements with the concept of structural integrity, from the development of more optimized designs with production aircraft with low weight and secure. These projects ensure an aircraft more operationally doable and reduced fuel consumption, benefiting the manufacturer, operators and the people, applying the concept of green aircraft. Aerospace structures in operation receive requests loads typical of flight, how pressurization support and lift that produce several types and combinations of requests, such as tensile, compression, fatigue, torsion, bending, buckling , aeroelastic loads, vibration and flutter associated with critical environments. Knowledge about the behavior of the structural material into corrosive environments or cryogenic temperature, it is important for evaluation to the lifetime of the aircraft. Accordingly , the aim of this study was to estimate the behavior of AA2050 - T84 alloy, about corrosion-fatigue and fracture toughness at cryogenic situations and correlate with microstructure and fractography, by mechanical tests and fracture toughness at room temperature and cryogenic. The test conditions has been determined near of the service that the material will be inserted, for cryogenic temperature -54 ºC and testing of fatigue crack propagation in air and salt spray with concentration of 3.5% and 5% NaCl, frequency 15Hz and load ratios R = 0.1 and 0.5. The cryogenic results showed that there improvement in tensile properties and stability in toughness due the restraint of ductility with decreasing temperature. Tests of fatigue crack propagation were carried out with ΔK decreasing and the parameters to obtain salt spray were determined experimentally. The crack growth curves and determination of the threshold were compared the according to load ratio and test atmosphere. In the fatigue crack propagation it was observed that presence of salt spray accelerates the rate of propagation and result in a lower threshold.
|
6 |
Fatigue life evaluation of A356 aluminum alloy used for engine\'s cylinder head / Avaliação da vida em fadiga de liga de alumínio A356 utilizada em cabeçote de motorMauricio Angeloni 27 April 2011 (has links)
In order to characterize mechanical components used in high responsibility applications, the knowledge of chemical composition and results from regular experiments such as traction, impact and hardness tests is important, but not sufficient. They cannot supply the necessary information that permit anticipating, in a reliable way, the components behavior in actual working conditions. As an example, there are engines cylinder head submitted to mechanical and thermal tensions that are relatively high during the in service use, and very high in same very demanding condition. During long run times and any failure in the cooling and/or lubrication the temperature may reach 300ºC. This temperature variation causes thermal shocks which may generate cracks and/or a wide ranging of plastic deformation in regions close to the pistons. Even not considering the thermal shock effects caused by failure, even so, a short number of start-up and shutdown cycles of engine, are considered the main cause of small cracks. This indicates that the generation of cracks in cylinder head may be considered as low cycle thermomechanical fatigue problem. Another problem is the microstructure heterogeneity in the component due to the casting process, leading to different physical and mechanical properties in the same piece. Besides the presence of porosity generated by gas bubbles and voids of solidification, which may be as great as short crack, reducing the nucleation life and changing the problems focus for the fatigue crack growth. The purpose of this study was to determine the isothermal and thermomechanical fatigue property through low cycle fatigue, as well as the fatigue crack growth, relaxation, microestrutural characterization and modeling of mechanical behavior by finite element for the aluminum alloy employed in the manufacture of engine cylinder head by the national automotive industry. Isothermal fatigue experiments were carried out at temperature of 120ºC and 280ºC and the thermomechanical performed in phase between the temperatures of 120ºC and 280ºC. The relaxation experiments were performed at some temperatures with trapezoidal wave loading, whereas the experiments of fatigue crack growth carried out at temperatures of 120ºC, 200ºC and 280ºC for sine and trapezoidal wave loading in displacement and load control. The microstructure analysis was also made in the specimens after the fatigue test by optical microscopy and scanning electron microscopy SEM. The results of these experiments showed that the casting defects and materials inhomogeneities, coupled long run times in high temperatures and loads, are a critical factor in the component performance. These results help us to establish accurate models for life prediction of the engine cylinder head. / Para caracterizar componentes usados em aplicações de alta responsabilidade não basta apenas conhecer a composição química e os resultados de ensaios de tração, impacto e dureza, pois estes podem não fornecer os subsídios necessários que permitam prever, de maneira confiável, o comportamento dos componentes nas condições reais de trabalho. Exemplo disto são os cabeçotes de motor automotivos, submetidos a tensões térmicas e mecânicas relativamente altas durante seu uso normal e altíssimo em condições extremas. Durante longos tempos de funcionamento e eventuais falhas na refrigeração e ou lubrificação a temperatura pode chegar a valores próximos de 300ºC. Esta variação de temperaturas provoca choques térmicos que podem gerar trincas e/ou uma grande quantidade de deformação plástica em regiões próximas aos pistões. Desconsiderando a presença de choques térmicos provocados por falhas, ainda assim, uma pequena quantidade de ciclos de acionamento e parada do motor, é considerada como os principais causadores de pequenas trincas. Isso indica que o surgimento de trincas em cabeçotes de motor deve ser considerado um problema de fadiga termomecânica de baixo ciclo. Outro problema é a heterogeneidade microestrutural no componente devido ao processo de fundição, levando a propriedades mecânicas e físicas diferentes em uma mesma peça. Além da presença de porosidade gerada por bolhas de gás e vazios de solidificação, que podem adquirir tamanho tal que se aproximem de pequenas trincas, diminuindo a vida para a nucleação e assim mudando o foco do problema para o de propagação de trinca por fadiga. A proposta deste trabalho foi a de determinar as propriedades de fadiga isotérmica e termomecânica através de ensaios de fadiga de baixo ciclo, bem como as propriedades de propagação de trinca por fadiga, relaxação, caracterização microestrutural e modelagem do comportamento mecânico por elementos finitos para a liga de alumínio utilizada na fabricação de cabeçotes de motores automotivos pela indústria nacional. Os ensaios de fadiga isotérmica foram realizados nas temperaturas de 120ºC e 280ºC e os ensaios termomecânicos foram realizados em fase entre as temperaturas de 120ºC e 280ºC. Os ensaios de relaxação foram realizados em várias temperaturas com carregamento de onda trapezoidal, enquanto que os ensaios de propagação de trinca por fadiga foram realizados nas temperaturas de 120ºC, 200ºC e 280ºC para carregamentos de onda senoidal e trapezoidal em controle de carga e de deslocamento. Foi feita também análise microestrutural nos corpos de prova, após os ensaios de fadiga, por microscopia óptica e por microscopia eletrônica de varredura MEV. Os resultados destes ensaios mostraram que os defeitos de fundição e a falta de homogeneidade no material, aliados a longos tempos de exposição a carregamentos e em altas temperaturas, constituem um fator crítico no desempenho do componente. Estes resultados ajudarão a estabelecer modelos precisos de previsão de vida para os cabeçotes de motor.
|
7 |
Fatigue life evaluation of A356 aluminum alloy used for engine cylinder head / Evaluation de la durée de vie en fatigue d'un alliage d'aluminium A356 uytilisé pour réaliser des têtes de cyclindresAngeloni, Mauricio 27 April 2011 (has links)
Le matériau étudié est un alliage Al A356, utilisés pour produire des têtes de cylindres pour l'industrie automobile par fonderie. Le matériau présente une microstructure dendritique assez grossière dans une matrice eutectique, avec une taille moyenne de grains de 25 microns, des précipités intermetalliques et des porosités. Les propriétés de traction sont fortement affectées par la température d'essai, avec une baisse assez sensible du module de Young, de la limite d'élasticité lorsque la température augmente. La durée de vie de fatigue isotherme chute de façon marquée (approximativement d'un facteur 10) lorsque la température d'essai est portée de 120 à 280 °C, en déformation imposée. Du essais thermomecaniques cycliques en phase, avec une température variant de 120 à 280 °C, on montré que la durée de vie en anisotherme est assez similaire à celle obtenue en conditions isothermes à 280 oC. Dans ce cas, les dommages causés par le chargement thermomécanique cyclique se produisent à la température la plus élevée du cycle. Les essais de relaxation ont montré l'existence de deux comportements distincts. À basse température, le matériau présente de l'écrouissage cyclique tandis qu'il s'adoucit cycliquement à des températures plus élevées. A partir des résultats de croissance des fissures de fatigue, on a observé que la température et la forme du cycle de fatigue a une forte influence sur la vitesse de fissuration par fatigue ainsi que sur le facteur d'intensité des contraintes seuil. Une loi de comportement élastique visco-plastique non-isotherme a été identifiée pour le matériau. Les paramètres de comportement mécanique sont statistiquement distribués du fait de la fabrication du matériau par fonderie. Toutefois, il a été démontré que le modèle était capable de se reproduire, avec une approximation raisonnable, les essais contrainte-déformation à des températures différentes, pour le cas isotherme et anisotherme. / The studied material is an A356 Al alloy, used to produce engine cylinder heads for the automotive industry by die casting process. The material displays a quite coarse dendritic microstructure in a eutectic matrix, with a mean grains size of 25 microns, intemetallic precipitates and porosities. The tensile properties are strongly affected by testing temperature, with a quite sensitive drop of the Young's modulus, the Yield stress as the temperature was raised. The isothermal fatigue life dropped of markedly (approximately 10 times) when the testing temperature is raised from 120 to 280 °C, under strain control. From the themomechanical in-phase cyclic tests, with temperature varying from (120 to 280 oC), it was possible to observe that life is quite similar to the isothermal fatigue test at 280 oC. In this case, the more sensitive damage caused the in-phase mechanical and thermal cycle take place at the highest temperature. Relaxation tests indicated two distinct behaviors, with the temperature of 240°C being a threshold. At lower temperatures, the material hardens cyclically whereas it softens cyclically at higher temperatures. From the fatigue crack growth results, it was observed that temperature and wave shape has a strong influence on the crack growth rate as well as on the stress intensity threshold. Considering sinusoidal wave shape (10 Hz), as the temperature increased the DKth decreased and the crack propagation rate increased. However, the rate as da/dN change with temperature is quite similar, as an indicative that the micromechanism of crack growth has not changed due to the high frequency used, and it was due only to loss of mechanical strength. An elastic-visco-plastic non-isothermal constitutive law was identified for the material. For the cast material studied in this work, the mechanical behavior parameters are statistically distributed. However, it was shown that the model was able to reproduce, with a reasonable approximation, the stress – strain relationship at different temperatures, for the isothermal and anisothermal cases. / Para caracterizar componentes usados em aplicações de alta responsabilidade não basta apenas conhecer a composição química e os resultados de ensaios de tração, impacto e dureza, pois estes podem não fornecer os subsídios necessários que permitam prever, de maneira confiável, o comportamento dos componentes nas condições reais de trabalho. Exemplo disto são os cabeçotes de motor automotivos, submetidos a tensões térmicas e mecânicasrelativamente altas durante seu uso normal e altíssimo em condições extremas. Durante longos tempos de funcionamento e eventuais falhas na refrigeração e ou lubrificação a temperatura pode chegar a valores próximos de 300ºC. Esta variação de temperaturas provoca choques térmicos que podem gerar trincas e/ou uma grande quantidade de deformação plástica em regiões próximas aos pistões. Desconsiderando a presença de choques térmicos provocadospor falhas, ainda assim, uma pequena quantidade de ciclos de acionamento e parada do motor, é considerada como os principais causadores de pequenas trincas. Isso indica que o surgimento de trincas em cabeçotes de motor deve ser considerado um problema de fadiga termomecânica de baixo ciclo. Outro problema é a heterogeneidade microestrutural no componente devido ao processo de fundição, levando a propriedades mecânicas e físicas diferentes em uma mesma peça. Além da presença de porosidade gerada por bolhas de gás e vazios de solidificação, que podem adquirir tamanho tal que se aproximem de pequenas trincas, diminuindo a vida para a nucleação e assim mudando o foco do problema para o de propagação de trinca por fadiga. A proposta deste trabalho foi a de determinar as propriedades de fadiga isotérmica e termomecânica através de ensaios de fadiga de baixo ciclo, bem como as propriedades de propagação de trinca por fadiga, relaxação, caracterização microestrutural e modelagem do comportamento mecânico por elementos finitos para a liga de alumínio utilizada na fabricação de cabeçotes de motores automotivos pela indústria nacional. Todos os ensaios e análises computacionais foram realizados nos laboratórios da Universidade de São Paulo (EESC-USP) e da École Normale Supérieure de Cachan (ENS-LMT). Os ensaios de fadiga isotérmica foram realizados nas temperaturas de 120ºC e 280ºC e os ensaios termomecânicos foram realizados em fase entre as temperaturas de 120ºC e 280ºC. Os ensaios de relaxação foram realizados em várias temperaturas com carregamento de onda trapezoidal, enquanto que os ensaios de propagação de trinca por fadiga foram realizados nas temperaturas de 120ºC, 200ºC e 280ºC para arregamentos de onda senoidal e trapezoidal em controle de carga e de deslocamento. Foi feita também análise microestrutural nos corpos de prova, após os ensaios de fadiga, por microscopia óptica e por microscopia eletrônica de varredura MEV.Os resultados destes ensaios mostraram que os defeitos de fundição e a falta de homogeneidade no material, aliados a longos tempos de exposição a carregamentos e em altas temperaturas, constituem um fator crítico no desempenho do componente. Estes resultados ajudarão a estabelecer modelos precisos de previsão de vida para os cabeçotes de motor.
|
8 |
Fatigue crack propagation in AA 7050-T7451 alloy considering environment, stress ratio, rolling direction and waveform effects / Propagação de trinca por fadiga na liga AA7050-T7451 considerando o efeito do meio ambiente, razão de tensões, direção de laminação e forma de ondaCárdenas Barbosa, José Fernando 17 March 2017 (has links)
Main extrinsic and intrinsic modifiers factors of crack growth rate in AA7050-T7451 were assessed in order to provide tools for aeronautical structures designers. These tools cover most necessary information to project aircraft\'s structures using the studied alloy, under damage tolerance philosophy. The experimental methodology consisted of use CT specimens, on TL and LT rolling direction to test its behavior under different conditions of stress ratio, force waveform, and the environment. The stress ratio values were 0.1 and 0.5, the force waveform used were sine and trapezoidal or Dwell under normal air laboratory conditions and salt fog 3.5%NaCl weight in order to simulate the marine environment. In Dwell tests, results were checked with the electrical potential drop technique (DCPD) in addition to the crack opening displacement (COD) method. Using the Walker coefficients, calculated on the present research, could be projected accurately the crack propagation behavior on Paris region and do fatigue life predictions using da/dN and S-N diagrams for different stress ratio values. The corrosion environment increases both crack growth rate and ΔKth due to oxides formation on the crack path that generates a crack closure effect. Dwell carrying makes decrease the crack growth rate by decreasing the slope of the Paris line on log (da/dN) versus log (ΔK) curve, instead of shifting down the line as occurs on titanium alloys. Rolling direction change from LT to TL increase the FCG rate in both threshold and Paris region, where the rate change use to be small. / Os principais fatores modificadores extrínsecos e intrínsecos da taxa de propagação de trincas na liga AA7050-T7451 foram avaliados para fornecer subsídios para projetistas de estruturas aeronáuticas, com base na filosofía de tolerância ao dano. A metodologia experimental consistiu em ensaiar corpos de prova do tipo compact tension (CT) da liga nas direções de laminação TL e LT, para verificar seu comportamento sob diferentes razões de tensões, forma de onda e condição ambiente. Os valores de razão de tensão estudados foram 0,1 e 0,5, as formas de onda foram senoidal e trapezoidal ou de Dwell, em condições normais de laboratório, ao ar, e névoa salina 3,5% NaCl, em massa, para simular um ambiente marinho. No caso dos ensaios Dwell, os resultados foram conferidos pelo método de queda de potencial eléctrico (QPE), além do método de flexibilidade elástica. Usando os coeficientes de Walker calculados a partir dos resultados obtidos, pôde-se projetar com precisão o comportamento da propagação de trinca na região de Paris e prever a vida em fadiga usando os diagramas da/dN e S-N para diferentes valores da razão de tensões. O ambiente corrosivo aumenta tanto a taxa de propagação de trinca, quanto o valor de ΔKth por causa da formação de óxidos na trajetória da trinca, que geram um efeito de fechamento sobre a mesma. Quanto à forma de onda, verificou-se que o carregamento Dwell diminui a taxa de propagação de trinca, diminuindo a inclinação das curvas log (da/dN) versus log (ΔK) na região de Paris, ao invés de deslocá-la paralelamente como ocorre com ligas de titânio. A mudança da direção de laminação de LT para TL aumenta a taxa de propagação de trinca por fadiga (PTF) tanto na região de threshold, quanto na região de Paris, onde a mudança de taxa é pequena.
|
9 |
Estudo sobre o tratamento térmico de envelhecimento interrompido T6I4-65 e influência na propagação de trinca por fadiga em uma liga de alumínio AA7050Lima, Luis Otavio Ribas de 18 June 2014 (has links)
Made available in DSpace on 2017-07-21T20:43:45Z (GMT). No. of bitstreams: 1
Luis Otavio Ribas Lima.pdf: 8124964 bytes, checksum: d16bc8c64f9e15d57f770b1b271d6b3b (MD5)
Previous issue date: 2014-06-18 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Aluminum alloys have been the primary material of choice for the aircraft due to their properties such as low density, high mechanical and corrosion resistance. Commercial aircraft apply aluminum alloys for the fuselage, wings and supporting structure due to the extensive knowledge in design and production of aluminum components, and most importantly, aluminum alloys continue to be developed, keeping it highly competitive. A great development happen with the heat-treatable alloys, which allow improvement of the mechanical properties. Among this alloys stand out the Al-Zn-Mg-Cu series, known for high strength, toughness and corrosion resistance. The improvement of those alloys occurs by the precipitation of nanometric particles MgZn2, called η phase. This study’s aim was to promote an interrupted heat treatment T6I4-65 in an AA7050 aluminum alloy, with fatigue crack growth resistance as priority. Interrupted heat treatments’ goal is optimizing the consumption of solute atoms during process of nucleation and growth of precipitates as a finely dispersion. The T6I4-65 condition obtained was analyzed by differential scanning calorimetry, DSC, optical and electronic microscopy, mechanical tests as hardness, tensile and fatigue crack growth. The T6I4-65 treatment results in a microstructure with a fine dispersion of precipitated phase η’, about 75% smaller than those resulting from in current use, T7451. This microstructure resulted in a reduction of up to 24% in fatigue crack growth rate compared to that resulting from T7451 treatment, keeping the ductility of 17% of area reduction and yield strength higher than 400MPa. / Ligas de alumínio são o principal material de uso na indústria aeronáutica devido a suas propriedades como baixa densidade, alta resistência mecânica e a corrosão. Aeronaves comerciais utilizam ligas de alumínio em sua fuselagem, asas e na estrutura de suporte devido ao extenso conhecimento no projeto e produção de componentes em alumínio, e mais importante, as ligas de alumínio continuam a serem desenvolvidas, mantendo-se altamente competitivas. Ocorreu um grande avanço com o desenvolvimento das ligas tratáveis termicamente, que permitiram a otimização das propriedades mecânicas. Entre estas ligas tratáveis, destaca se a família Al-Zn-Mg-Cu, conhecidas pela alta resistência mecânica, tenacidade e resistência a corrosão. O aperfeiçoamento destas ligas ocorre pela precipitação de partículas nanométricas de MgZn2, conhecida como fase η. O objetivo deste trabalho foi obter um tratamento térmico interrompido T6I4-65 em uma liga de alumínio AA7050 com prioridade ao aumento de resistência à propagação de trinca por fadiga. Tratamentos interrompidos tem por objetivo otimizar o consumo de átomos de soluto durante os processos de nucleação e crescimento dos precipitados endurecedores na liga na forma de dispersão finamente dispersa. A condição T6I4-65 obtida foi analisada por meio de calorimetria diferencial de varredura, DSC, microscopia ótica e eletrônica de varredura e transmissão, ensaios mecânicos dureza, tração e propagação de trinca por fadiga. Este tratamento resultou em uma microestrutura com uma dispersão de finos precipitados de fase η’, cerca de 75% menores que os resultantes de tratamentos de uso corrente, T7451. Esta microestrutura promoveu a redução de até 24% na taxa de propagação de trinca por fadiga em comparação à resultante do tratamento T7451, mantendo grande ductilidade, até 17% de redução de área e limite de escoamento superior a 400MPa.
|
10 |
Fatigue crack propagation in AA 7050-T7451 alloy considering environment, stress ratio, rolling direction and waveform effects / Propagação de trinca por fadiga na liga AA7050-T7451 considerando o efeito do meio ambiente, razão de tensões, direção de laminação e forma de ondaJosé Fernando Cárdenas Barbosa 17 March 2017 (has links)
Main extrinsic and intrinsic modifiers factors of crack growth rate in AA7050-T7451 were assessed in order to provide tools for aeronautical structures designers. These tools cover most necessary information to project aircraft\'s structures using the studied alloy, under damage tolerance philosophy. The experimental methodology consisted of use CT specimens, on TL and LT rolling direction to test its behavior under different conditions of stress ratio, force waveform, and the environment. The stress ratio values were 0.1 and 0.5, the force waveform used were sine and trapezoidal or Dwell under normal air laboratory conditions and salt fog 3.5%NaCl weight in order to simulate the marine environment. In Dwell tests, results were checked with the electrical potential drop technique (DCPD) in addition to the crack opening displacement (COD) method. Using the Walker coefficients, calculated on the present research, could be projected accurately the crack propagation behavior on Paris region and do fatigue life predictions using da/dN and S-N diagrams for different stress ratio values. The corrosion environment increases both crack growth rate and ΔKth due to oxides formation on the crack path that generates a crack closure effect. Dwell carrying makes decrease the crack growth rate by decreasing the slope of the Paris line on log (da/dN) versus log (ΔK) curve, instead of shifting down the line as occurs on titanium alloys. Rolling direction change from LT to TL increase the FCG rate in both threshold and Paris region, where the rate change use to be small. / Os principais fatores modificadores extrínsecos e intrínsecos da taxa de propagação de trincas na liga AA7050-T7451 foram avaliados para fornecer subsídios para projetistas de estruturas aeronáuticas, com base na filosofía de tolerância ao dano. A metodologia experimental consistiu em ensaiar corpos de prova do tipo compact tension (CT) da liga nas direções de laminação TL e LT, para verificar seu comportamento sob diferentes razões de tensões, forma de onda e condição ambiente. Os valores de razão de tensão estudados foram 0,1 e 0,5, as formas de onda foram senoidal e trapezoidal ou de Dwell, em condições normais de laboratório, ao ar, e névoa salina 3,5% NaCl, em massa, para simular um ambiente marinho. No caso dos ensaios Dwell, os resultados foram conferidos pelo método de queda de potencial eléctrico (QPE), além do método de flexibilidade elástica. Usando os coeficientes de Walker calculados a partir dos resultados obtidos, pôde-se projetar com precisão o comportamento da propagação de trinca na região de Paris e prever a vida em fadiga usando os diagramas da/dN e S-N para diferentes valores da razão de tensões. O ambiente corrosivo aumenta tanto a taxa de propagação de trinca, quanto o valor de ΔKth por causa da formação de óxidos na trajetória da trinca, que geram um efeito de fechamento sobre a mesma. Quanto à forma de onda, verificou-se que o carregamento Dwell diminui a taxa de propagação de trinca, diminuindo a inclinação das curvas log (da/dN) versus log (ΔK) na região de Paris, ao invés de deslocá-la paralelamente como ocorre com ligas de titânio. A mudança da direção de laminação de LT para TL aumenta a taxa de propagação de trinca por fadiga (PTF) tanto na região de threshold, quanto na região de Paris, onde a mudança de taxa é pequena.
|