Made available in DSpace on 2011-12-27T14:14:29Z (GMT). No. of bitstreams: 2 000406879-0.pdf: 817502 bytes, checksum: a388f3f8f4ce8e84782dbb5d5932a532 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this study was compare the chisel width in shear bond strength test in dental/composite interface. For the shear bond test, chisels with 0. 5, 1, 2 and 3mm width were used to test four groups (n=15). Sixty bovine incisors were used, imbedded and flattened according to the methodology of Goes (1994) in order to prepare the samples. Enamel surfaces were flattened and etched with 15% phosphoric acid (3M/ESPE) with 15%, followed by application of Single Bond (3M/ESPE) adhesive system and Z-250 (3M/ESPE) composite resins according to manufacture’s instructions. To the shear bond strength, an universal testing machine EMIC DL 2000 (EMIC) at 0. 5 mm/min cross-head speed. Obtained data were compared statistically with analysis of variance and Duncan’s test with significance level of 5% (p < 0. 05) and submitted to Pearson’s correlation test (p < 0. 01). The averages in megapascal recorded were: 0. 5 mm – 19. 66; 1. 0 mm – 18. 78; 2 mm – 16. 77; 3 mm – 16. 06.There was a significantly difference between groups, when submitted to analysis of variance (p = 0. 045) and multiple comparison of Duncan’s test. The lower average (MPa) was recorded for chisel with 3 mm (16. 06), while the highest average (MPa) was recorded for the group with 0. 05 mm chisel (19. 66), that were statistically different. The correlation between chisel width and shear bond strength was significant (p < 0. 01). The obtained results allow conclude that shear bond strength (MPa) is influenced by chisel width used in the test. / O objetivo deste estudo foi comparar diferentes larguras de cinzel utilizadas em ensaios mecânicos para avaliação da resistência de união ao cisalhamento na interface esmalte dental / resina composta. Para a realização do ensaio e cisalhamento, cinzéis com larguras de 0,5mm, 1,0 mm, 2,0 mm e 3,0 mm foram utilizados para testar 4 grupos (n=15). Foram utilizados 60 dentes bovinos do grupo incisivo que tiveram sua inclusão, preparo de superfície e confecção dos corpos de prova realizados de acordo com Goes (1994). As superfícies de esmalte foram planificadas, condicionadas com ácido fosfórico (3M/ESPE) à 15%, seguido da aplicação do sistema adesivo Single Bond (3M) e de resina composta Z-250 (3M) conforme instruções do fabricante. Para o ensaio de cisalhamento foi utilizada uma máquina de ensaio universal EMIC DL 2000 (EMIC, BRASIL) a velocidade de 0,5mm/min. Os dados obtidos foram comparados estatisticamente com análise de variância e teste de Duncan com nível de significância de 5% (p < 0,05) e submetidos ao teste de correlação de Pearson (p < 0,01). As médias obtidas em Megapascal para a resistência de união ao cisalhamento foram: 0,5mm - 19,66; 1,0mm – 18,78; 2,0 mm – 16,77; 3,0 mm – 16,06. Houve diferença estatisticamente significativa entre os grupos, quando submetidos à análise de variância (p = 0,045) e testes de comparação múltipla de Duncan. A menor média (MPa) foi registrada para o grupo com cinzel de 3,0mm (16,06), enquanto a maior média (MPa) foi verificada para o grupo com cinzel de 0,5mm (19,66), que diferiram estatisticamente. A correlação entre largura do cinzel e resistência de união foi significante (p < 0,01). Os resultados obtidos permitem concluir que os valores (MPa) de resistência de união ao cisalhamento sofrem influência da largura do cinzel utilizado no ensaio.

Made available in DSpace on 2011-12-27T14:14:41Z (GMT). No. of bitstreams: 2 000425710-0.pdf: 4733060 bytes, checksum: bc9a4ed427f2b79c5adf0d601bc1a8ca (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The objectives of the present study in vitro were to evaluate and compare the Shore A roughness and hardness of a tissue conditioner material (Ufi Gel P) submitted to abrasion test by brushing, with and without the application of surface sealer (Ufi Gel P), disinfected or not with sodium hypochlorite 2,5% up to 28 days. For the confection of the samples, the conditioner tissue material was applied in a 2 mm in thickness, over an acrylic resin bar chemically activated (JET). Thirty samples of the Ufi Gel P material (2 mm in thickness) were manufactured on the acrylic resin bar and they were randomly divided in 3 groups (n=10) according with the treatment: Ufi Gel P with control seal (Group 1); Ufi Gel P with seal, disinfected with sodium hypochlorite 2. 5% for 28 minutes, every seven days (Group 2); and Ufi Gel P without seal, disinfected with sodium hypochlorite 2. 5% for 28 minutes, every seven days (Group 3). All three groups were stored in artificial saliva in a heater at 37°C during 28 days. The Shore A rugosity and hardness were measured in time initial, 7, 14, 21 and 28 days. The measures of the average roughness (Ra) were record with a rugosimeter SJ 201 (Mitutoyo) and the ones concerning hardness, through a Teclok Shore A durometer. The results were analyzed by ANOVA and Tukey ( =0,05). Analysing the results for rugosity throughout all 28 days to groups 1, 2 and 3, we can say that no variation was statistically significant among the different amounts of time in all groups submitted to a Variance Analysis. Comparing the hardness average among the groups and the different amounts of time, a statistically significant variation was observed (p<0. 05). Thus, we can conclude that the values of rugosity were not altered a in a 28 days period (p>0,05); and also, that the tissue conditioner material increases significantly in hardness in the first 21 days, and after this period it seems to become stable (p>0,05). / Os objetivos deste estudo in vitro, foram avaliar e comparar a rugosidade e a dureza Shore A de um material reembasador resiliente (Ufi Gel P) submetido à escovação simulada com e sem aplicação de seu selante de superfície (Ufi Gel P), desinfetados ou não com hipoclorito de sódio 2,5% em até 28 dias. Para confecção das amostras, o material reembasador resiliente foi aplicado em uma espessura de 2 mm sobre uma barra de resina acrílica ativada quimicamente (JET). Foram confeccionados 30 amostras do material Ufi Gel P (2 mm de espessura) sobre a barra de resina acrílica e divididos aleatoriamente em 3 grupos (n=10) de acordo com o tratamento aplicado: Ufi Gel P com selante (Grupo 1); Ufi Gel P com selante submetido à desinfecção com hipoclorito de sódio 2,5% por 28 minutos, a cada 7 dias (Grupo 2); Ufi Gel P sem selante submetido à desinfecção com hipoclorito de sódio 2,5% por 28 minutos, a cada 7 dias (Grupo 3). Os 3 grupos foram armazenados em saliva artificial em estufa á 37°C durante 28 dias. A rugosidade e dureza Shore A foram verificados no tempo inicial, 7, 14, 21, 28 dias. As medidas da rugosidade média (Ra) foram realizadas com um rugosímetro SJ 201 (Mitutoyo) e as de dureza através de um durômetro Teclok Shore A. Os resultados foram analisados com ANOVA e Tukey ( =0,05). Analisando os resultados de rugosidade (Ra) ao longo dos 28 dias pode-se observar que não houve diferença estatisticamente significante entre os tempos e entre os grupos quando submetidos à Análise de Variância (p>0,05). Ao comparar as médias de dureza entre os grupos e entre tempos, houve diferença estatisticamente significante (p<0,05).Assim, pode-se concluir que os valores de rugosidade não se alteraram nos 28 dias (p>0,05) e que o material condicionador de tecido tem um aumento significativo nos valores de dureza nos primeiros 21 dias, não havendo diferença significante após este período (p>0,05).

Submitted by Ginamara Lima (ginaj@pucrs.br) on 2013-03-20T19:14:18Z No. of bitstreams: 1 446374.pdf: 760995 bytes, checksum: fdb1e9bc7072bab1285303e1a7f13c42 (MD5) / Made available in DSpace on 2013-03-20T19:14:18Z (GMT). No. of bitstreams: 1 446374.pdf: 760995 bytes, checksum: fdb1e9bc7072bab1285303e1a7f13c42 (MD5) / O tempo de espera para a remoção dos modelos de gesso dos moldes em relação a sua resistência mecânica é controverso. O objetivo desse trabalho foi avaliar a influência do tempo de armazenamento na rugosidade, tração diametral e compressão de gessos tipo IV. Foram confeccionadas 270 amostras, sendo 90 para cada marca comercial (Durone, Fuji Rock e Tuff Rock). Os testes de rugosidade, tração diametral e compressão para os tempos de armazenagem de 1 hora, 24 horas e 7 dias foram realizados. Para os testes de rugosidade superficial e tração diametral amostras de 6 mm de diâmetro por 3 mm de altura foram confeccionados. Para o teste de compressão amostras de 3 mm de diâmetro por 6 mm de altura foram utilizadas. Foi utilizado um rugosímetro, para a medição da rugosidade média de superfície (Ra). Os corpos de prova foram montados na máquina de ensaio universal e posteriormente realizados os testes de tração diametral e compressão nos respectivos tempos. Os resultados foram submetidos ao modelo linear geral e teste de Tukey (α=0,05). Os valores de rugosidade registrados para os diferentes tipos de gesso variaram de 0,30 μm (Durone 1 hora) à 0,64 μm (Tuff Rock 7 dias). Os valores de tração diametral registrados para os diferentes tipos de gesso variaram de 3,94 MPa (Tuff Rock 1 hora) à 9,20 MPa (Durone 7 dias). Os valores de compressão registrados para os diferentes tipos de gesso variaram de 26,67 MPa (Durone 1 hora) à 65,14 MPa (Fuji Rock 7 dias). Concluímos que houve um aumento estatisticamente significante para o fator tempo em relação a rugosidade (p=0,005), tração diametral (p=0,001) e compressão (p=0,001). O fator marca comercial influenciou significativamente na rugosidade (p=0,001), tração diametral (p=0,004) e compressão (p=0,001). O gesso Tuff Rock apresentou maior rugosidade, os gessos Durone e Fuji Rock apresentaram o maior valor à tração diametral e o gesso Fuji Rock o maior valor a compressão. / The post pouring time to remove dental stone from impression is controversial regardless to strength and roughness. The aim of this study was evaluate the influence of post pouring time in the surface roughness, compressive and diametral tensile strength (DTS) of type IV dental stone. Two hundred and seventy dental stone samples were made from three commercial brands (Durone, Fuji Rock and Tuff Rock). Surface roughness, compressive and diametral tensile strength tests were performed 1 hour, 24 hours and 7 days after pouring. Samples of 6 mm in diameter and 3 mm in height were produced for roughness and DTS tests. Samples of 3 mm in diameter and 6 mm in height were used for compressive strength. Results were submitted to the general linear model and Tukey test (α=0.05). The surface roughness (Ra) registered to different types of dental stone vary from 0.30 μm (Durone 1 hour) to 0.64 μm (Tuff Rock 7 days). The diametral tensile strength (MPa) ranged from 3.94 (Tuff Rock 1 hour) to 9.20 (Durone 7 days). For compressive strength (MPa), data vary from 26.67 MPa (Durone 1 hour) to 65.14 MPa (Fuji Rock 7 days). There was a significant increase of surface roughness (p=0.005), diametral tensile strength (p=0.001) and compressive strength (p=0.001) as time passes after pouring. Commercial brand factor influenced roughness (p=0.001), diametral tensile strength (p=0.004) and compressive strength (p=0.001). Tuff Rock showed the highest surface roughness. The highest DTS was recorded for Durone and Fuji Rock. Fuji Rock showed the highest compressive strength.

Made available in DSpace on 2011-12-27T14:14:00Z (GMT). No. of bitstreams: 2 000386791-0.pdf: 7078042 bytes, checksum: 4c1fadb128575046216a3274f924db24 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this study was to compare, in vitro, the shear bond strength values of brackets bonded with LED and convencional halogen (QTH) light curing units with a different exposure times. One hundred and twenty six premolar teeth were equally divided into six groups according to the curing light and exposure times used. As for LED curing light, the specimens were submitted to photoactivation for 5s, 10s end 15s, whereas the exposure times to QTH curing light was 10s, 20s and 30s. The light curing units LED (Ortholux LED Curing Light, 3M-Unitek –EUA) and QTH (XL 3000, 3M Unitek – EUA) were evaluated in the beginning, right before the first bonding, and after ten brackets bonding, using specific radiometers for each light curing, registered irradiance mean values of 581 mW/cm² and 420mW/cm², respectively. The specimens were stored in water at 37°C for 24h and then subjected to a shear force with a universal testing machine, in a gingivoocclusal direction at crosshead speed of 1mm/min. According to ANOVA and Tukey, a significant difference in mean shear bond strength was detected (p<0,01).As for the LED – photoactivaded groups 5s (17,20MPa) and 10s (20,54MPa) shear bond strength values was comparable, showing statistical difference among the LED 15s (25,24MPa) group. Considering the QTH exposures, the 10s (16,97MPa) group registered differences when related to the 20s (23,61MPa) and 30s (21,33MPa), whereas these showed none between them. The LED 15s group demonstrated the higher mean shear bond strength, but showed no statistically significant differences between the QTH 20s and 30s groups. Even the lowest mean bond strength, recorded for QTH 10s and LED 5s groups, respectively, were considered to be clinically acceptable. Kruskal-Wallis analysis of ARI scores indicated that there was statistical difference (p< 0,01) among the studied groups. In LED 15s group the majority of specimens had an ARI score 0, being observed a enamel fracture in two specimens. Instead of the LED 5s and QTH 10s groups demonstrated higher frequencies of ARI score 1 and 2, respectively, in both groups, the score 3 appear frequently (QTH 10s – 10,5%; LED 5s – 9,5%). Opposing behavior was observed in groups LED 10s and 15s, where he was not registered frequency of score 3 (0%). The findings of the present study suggest that technology LED (Free Light Ortholux, 3M - Unitek) can be used, in the brackets bonding, with lesser times of cure in relation halogen light for the resin Transbond XT, being that, the minimum time of 5s with LED presented bond strength values clinically acceptable. / O objetivo do presente estudo foi comparar, in vitro, a resistência de união ao cisalhamento de bráquetes colados quando expostos à luz LED e à luz halógena (QTH) mediante diferentes tempos de exposição. Para isso 126 dentes pré-molares foram divididos em seis grupos de acordo com a fonte de luz e o tempo de exposição utilizado. Para o conjunto LED, foram usados os tempos de 5, 10 e 15s e para o conjunto QTH, 10, 20, e 30s. Os aparelhos fotopolimerizadoes LED (Ortholux LED Curing Light, 3M-Unitek –EUA) e QTH (XL 3000, 3M Unitek – EUA) tiveram suas intensidades avaliadas inicialmente e, a cada 10 colagens, por radiômetros específicos para cada natureza de luz, obtendo valores médios de 581mW/cm² e 420mW/cm², respectivamente. Após 24h de estocagem em água destilada a 37°C, os corpos - de - prova foram levados à máquina de ensaio mecânico (Emic DL 2000®) e submetidos à tensão de cisalhamento, no sentido cérvico-oclusal, à velocidade de 1mm/min. De acordo com os testes estatísticos ANOVA e Tukey, houve diferença significativa entre os grupos estudados (p< 0,01).Os grupos fotoativados por LED 5s (17,20MPa) e 10s (20,54MPa) não diferiram entre si, mostrando diferença estatisticamente significativa quando comparados ao grupo LED 15s (25,24MPa). Quanto à fonte luminosa QTH, o grupo de 10s (16,97MPa) diferiu dos 20s (23,61MPa) e 30s (21,33MPa), enquanto esses não diferiram entre 8 si. A maior média de resistência de união foi observada no grupo LED 15s, embora este grupo não tenha se diferenciado estatisticamente dos grupos QTH 20s e 30s. Verificou-se que até mesmo os grupos que tiveram as menores médias de resistência de união, QTH 10s e LED 5s, respectivamente, apresentaram valores compatíveis com o uso clínico. Segundo o teste Kruskal-Wallis, houve diferença significativa na distribuição dos resultados do IAR entre os grupos (p< 0,01).O grupo LED 15s demonstrou padrão de fratura predominantemente índice 0, sendo observado fratura de esmalte em dois corpos - de - prova. Apesar dos grupos LED 5s e QTH 10s apresentarem maior predomínio de escores 1 e 2, respectivamente, foram nesses que se observou a maior freqüência de escores 3, QTH 10s (10,5%) e LED 5s (9,5%). Comportamento oposto foi observado nos grupos LED 10s e 15s, onde não foi registrado freqüência de índice 3 (0%). Os achados do presente estudo sugerem que a tecnologia LED (Free Light Ortholux, 3M – Unitek) pode ser utilizada, na colagem de bráquetes, com tempos de cura menores em relação á luz halógena para a resina Transbond XT, sendo que, o tempo mínimo de 5s com LED apresentou valor de resistência de união clinicamente aceitável.

Made available in DSpace on 2011-12-27T14:14:03Z (GMT). No. of bitstreams: 2 000389582-0.pdf: 4751378 bytes, checksum: 96556d08ded117c5d6139618402559ab (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This in situ study evaluated the degradation of tissue conditioners as a function of the timespan of clinical use measuring the variables Shore A hardness and quantity of plasticizer phthalate. The three tissue conditioners evaluated were Coe-Comfort, Dura Conditioner, and Softone. The materials were prepared according to each manufacturer’s instructions and inserted into grooves (5x15x2 mm) made in the palatal inner surface of maxillary complete dentures of nine patients at the FO-PUCRS Complete Dentures Clinics. These patients were selected following the inclusion and exclusion criteria and used their dentures during the evaluation period. Data collection was performed at baseline and 3, 7, and 14 days after the insertion of the materials into the dentures grooves. Shore A hardness was recorded by using an analogical Shore A durometer. The quantity of plasticizer phthalate was measured by means of infrared spectroscopy. One specimen of each material was randomly chosen at each test-time for observation of surface topography in scanning electron microscope. Data were analyzed by ANOVA for repeated measures followed by Tukey test, and by simple linear regression, at the 5% significance level.All tested tissue conditioners showed decrease of quantity of phthalate and increase of hardness over time. The overall degradation was similar for all tissue conditioners but the pattern of phthalate lixiviation and of hardness alteration was material-specific. The largest changes of phthalate concentration and Shore A hardness of the tested tissue conditioners occurred in the first three days of clinical use. Comparing baseline and day 3 data, Coe-Comfort showed 25% decrease of initial phthalate concentration, which was statistically different from the other materials with reduction of 50%. No significant alteration of phthalate concentration was detected between days 3 and 7. The quantity of plasticizer in the material is inversely related to the hardness of the tissue conditioner. / Este estudo in situ avaliou a degradação de condicionadores de tecido em função do tempo de uso clínico, mensurando a dureza Shore A e a quantidade do agente plastificante ftalato. Três materiais condicionadores de tecido foram avaliados: Coe-Comfort, Dura Conditioner e Softone. Os três materiais foram manipulados de acordo com as instruções dos fabricantes e inseridos em canaletas (5x15x2 mm) preparadas na região palatal da superfície interna de próteses totais superiores de nove pacientes da Clínica de Prótese Total da FO-PUCRS selecionados de acordo com os critérios de inclusão e exclusão, que permaneceram utilizando suas próteses durante o período de avaliação. As análises foram realizadas no baseline, no terceiro, sétimo e décimo-quarto dias, após a inserção dos condicionadores em boca. As mensurações da dureza foram registradas por meio de um aparelho durômetro Shore A analógico e a quantidade de plastificante foi mensurada por espectrofotometria de infravermelho. Foram selecionadas aleatoriamente espécimes dos três condicionadores de cada intervalo de tempo para análise em microscópio eletrônico de varredura.Os dados foram analisados por ANOVA utilizando o delineamento em medidas repetidas seguida pelo Teste de Comparações Múltiplas de Tukey e por regressão linear simples, ao nível de significância de 5%. Todos os condicionadores de tecido testados apresentaram redução da quantidade de plastificante ftalato e aumento da dureza ao longo do tempo do estudo. O comportamento geral de degradação dos condicionadores de tecido testados foi similar mas o padrão de lixiviação de ftalato e de aumento de dureza foi específico para cada material. As maiores alterações de concentração de ftalato e de dureza Shore A dos condicionadores de tecido estudados ocorreram nos primeiros três dias de uso clínico. Entre o baseline e o dia 3 o Coe- Comfort apresentou redução de aproximadamente 25% da concentração inicial de ftalato, sendo estatisticamente diferente dos demais materiais que apresentaram perda de 50%. Não houve alteração significativa da quantidade de ftalato entre os dias 3 e 7. A quantidade de plastificante no material está inversamente relacionada com a dureza dos condicionadores de tecido.

Made available in DSpace on 2011-12-27T14:14:07Z (GMT). No. of bitstreams: 2 000421649-0.pdf: 1087640 bytes, checksum: faee9bfd7959d4a4a23ff18aca62f774 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This in vitro study evaluated the fracture strength of endodontically treated, weakened root canals, which were restored with either cast metallic or glass fiber-reinforced resin posts (Exacto, Angelus Indústria de Produtos Odontológicos S/A, Londrina, PR, Brazil) and submitted or not to mechanical fatigue. Twenty extracted human teeth with standardized dimensions and no visible structural defects were used. The crowns were cut below the enamel-cement junction to result in 14-16 mm-length roots. The endodontic treatment was performed by using the stepwise technique; the canals were prepared for post insertion with a bur of the glass fiber-reinforced resin post system (# 1. 6 mm-diameter). The roots were weakened by removing intracanal dentin with a tapered diamond bur (4 mm-length) and randomly divided into four groups (n=5/group) according to the type of post (metallic or glass fiber-reinforced resin post) and type of treatment (with or without mechanic cycling). For the metallic posts, the intracanal portion was modeled and cast in Ni-Cr alloy. The resin posts had the crown portion built with nanoparticle composite Z250 (ESPE, 3M) using prefabricated polyesther crowns of standardized shape according to the cast posts. All posts and metallic crowns were cemented with RelyX Unicem. The roots were covered with impression material to simulate the periodontal ligament and embedded in acrylic resin. Two groups were submitted to mechanic cycling with 300,000 cycles, 50 N of load corresponding to a pressure of 1. 13 bars, and frequency of 1 Hz. Specimens were loaded at 45 degrees in a universal testing machine at a crosshead speed of 0. 5 mm/min until failure. The mode of failure was classified as repairable or nonrepairable. The results showed that the metallic posts with no mechanic fatigue had the highest fracture strength (484 N); the resin posts with mechanic cycling showed the lowest values (259. 9 N). The teeth with cast posts had higher strength than the ones with resin posts, but they also showed more nonrepairable failure. Mechanical cycling reduced the fracture strength but did not affect the failure mode. / Este estudo in vitro avaliou a resistência à fratura de raízes enfraquecidas, tratadas endodonticamente, que foram restauradas com pinos metálicos fundidos e pinos de fibra de vidro Exacto (Angelus Indústria de Produtos Odontológicos S/A, Londrina, PR, Brasil) e submetidos à fadiga mecânica. Foram utilizados 20 dentes humanos unirradiculares, extraídos, com dimensões padronizadas e sem defeitos estruturais visíveis. As coroas foram removidas abaixo da junção amelo-cementária, mantendo-se comprimento da raiz entre 14 e 16 mm. O tratamento endodôntico foi realizado pela técnica escalonada; os canais foram desobturados para o preparo intra-radicular padronizado com a broca do sistema de pino de fibra de vidro Exacto (no 1,6 mm de diâmetro). O enfraquecimento radicular foi realizado com remoção de dentina dos condutos com uma broca diamantada tronco-cônica (4 mm de comprimento). As raízes foram aleatoriamente divididas em quatro grupos (n=5/grupo) conforme o tipo de pino (metálico ou pino de fibra de vidro) e o tipo de tratamento realizado (com ciclagem mecânica ou sem ciclagem mecânica). Para os pinos metálicos, a região intra-radicular foi modelada e fundida em peça única em liga de níquel-cromo. Os pinos de fibra de vidro receberam complemento coronário confeccionado com resina nanoparticulada Z250 (ESPE, 3M) com o uso de coroas de poliéster pré-fabricadas com a forma padronizada pelos núcleos fundidos. Todos os pinos e coroas totais metálicas foram cimentadas com o cimento RelyX Unicem. As raízes foram revestidas com uma camada de poliéter simulando o ligamento periodontal e foram embutidas em resina acrílica autopolimerizável. Dois grupos foram submetidos à ciclagem mecânica no Simulador de Fadiga Mecânica ERIOS, modelo ER – 11000, com protocolo de 300. 000 ciclos, carga de 50 N correspondente a pressão de trabalho de 1,13 bars e frequência de 1 Hz.O ensaio mecânico para registro dos valores de resistência à fratura foi realizado com a aplicação de uma carga compressiva a 450 com a face palatina dos corpos-de-prova em máquina de ensaio universal à velocidade de 0,5 mm/min até que houvesse algum tipo de ruptura. O tipo de falha após o ensaio foi classificado como reparável ou irreparável. Os dados de força máxima de ruptura (N) obtidos foram preliminarmente analisados pelos testes de Lilliefors (D) e Shapiro-Wilk (W) quanto à normalidade de sua distribuição para aplicação de testes estatísticos paramétricos. Posteriormente, foram analisados pelo teste ANOVA de acordo com o delineamento de experimento em blocos casualizados com repetições, ao nível de significância de 0,05. Os resultados mostraram que pinos metálicos sem ciclagem mecânica tiveram a maior resistência à fratura (484 N); os pinos de fibra de vidro submetidos à ciclagem mecânica mostraram os menores valores (259,9 N). Os pinos metálicos fundidos apresentaram maiores valores de resistência à fratura que os pinos de fibra de vidro; entretanto, apresentaram maior número de falhas irreparáveis. A ciclagem mecânica reduziu a força máxima de ruptura, mas não afetou o tipo de falha.

Made available in DSpace on 2011-12-27T14:14:12Z (GMT). No. of bitstreams: 2 000347433-0.pdf: 2385324 bytes, checksum: b30cdf7cb8df14803e76ba57e57535bb (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The purpose of this study was to assess the effect of a horizontally transfixed fiber glass post on the fracture resistance of molar teeth endodontically treated with MOD preparations, restored or not with composite resin. Seventy-five sound human third molars were extracted and mounted on acrylic resin blocks and were randomly assigned to five groups (n=15). In Group A, the teeth remained sound (control). Groups B, C, D and E, treated endodontically, were subjected to the following procedures: Group B – MOD preparation, group C – MOD preparation and transfixed post, group C – MOD preparation and resin composite restoration, group E – MOD preparation, transfixed post, and composite resin. The samples were stored in physiological serum at 37ºC for 24 hours. Later, a compressive force was applied parallely to the long axis of the teeth to fracture, performed by means of a universal testing machine (EMIC DL-2000) at 1 mm/min speed. The means in Newtons (N) of the results (standard deviation) followed by the same letter did not show a statistic difference for ANOVA and Tukey, p=0. 05: Group A = 4289. 8 (± 1128. 9)a, Group B = 549. 6 (± 120. 7)b, Group C = 1474. 8 (± 338. 1)c, Group D = 1224. 7 (± 236. 0)c, Group E = 2645. 4 (± 675. 1)d. In the analysis of qualitative variables, cusp fracture prevailed in 56%, a recoverable diagnosis was found in all groups, except for Group C, and the palatal cusp preparation prevailed in all Groups, except for Group A. It was concluded that a fiber glass post transfixed horizontally to the walls of a MOD cavity significantly increased fracture resistance, and when associated to the composite resin restoration, it established a fracture pattern compatible with the recovery of the dental specimen. / A proposta deste estudo foi avaliar o efeito, na resistência à fratura, de um pino de fibra de vidro transfixando horizontalmente as paredes, de um preparo MOD, de dentes molares tratados endodonticamente restaurados ou não com resina composta. Setenta e cinco dentes terceiros molares humanos hígidos foram extraídos e montados em blocos de resina acrílica, sendo distribuídos aleatoriamente em cinco grupos (n=15). No Grupo A, os dentes foram mantidos hígidos (controle). Os Grupos B, C, D e E, com tratamento endodôntico, receberam os seguintes procedimentos: Grupo B – preparo MOD; Grupo C – preparo MOD e pino transfixado; Grupo D – preparo MOD e restauração com resina composta; Grupo E – preparo MOD, pino transfixado e restauração com resina composta. As amostras foram armazenadas em soro fisiológico a 37ºC durante 24 horas. Após o procedimento, foi aplicada uma força compressiva paralela ao longo eixo dos dentes até a fratura, conduzida por meio de uma máquina de ensaio universal (EMIC DL-2000) com velocidade de 1mm/min. As médias em Newtons dos resultados (desvio padrão) seguidas de mesma letra não apresentaram diferença estatística para ANOVA e Tukey, p=0,05: Grupo A = 4289,8 (± 1128,9)a, Grupo B = 549,6 (±120,7)b, Grupo C = 1474,8 (± 338,1)c, Grupo D = 1224,7 (± 236,0)c, Grupo E = 2645,4 (±675,1)d. Na análise das variáveis qualitativas, predominou a fratura de cúspide em 56%, o diagnóstico recuperável em todos os grupos, com exceção do Grupo C e o preparo da cúspide palatina predominou em todos os grupos, a exceção do Grupo A. Concluiu-se que um pino de fibra de vidro transfixando horizontalmente as paredes de uma cavidade MOD elevou significativamente a resistência à fratura e quando associado à restauração de resina composta determinou um padrão de fratura compatível com a recuperação da peça dentária.

Made available in DSpace on 2011-12-27T14:14:13Z (GMT). No. of bitstreams: 2 000411472-0.pdf: 3421246 bytes, checksum: 2de63642b6d6b46a8c8709c79bb57f6a (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Article 1 - Aims: To compare the surface roughness of four resin composites with different organic matrix compositions applying the abrasion testing by tooth brushing until 20,000 cycles. Methods and materials: One hundred and sixty samples were buildup and divided into 16 groups (n=10) according to the type of composite resin, source of light and energy density. The resin composites used were Charisma, Z250, ROK and Filtek LS, being photo activated with LED or halogen unit, receiving 8 or 16 J/cm2. After 24h, the samples were submitted to a simulated wear test with a dentifrice and a soft toothbrush by periods of 6 months (5000 cycles), 12 months (10. 000 cycles) e 24 months (20. 000 cycles). After each period was realized the surface roughness measurement. Results: The factors as energy density (p=0. 0001), source of light (p=0. 0047), resin composites (p=0. 0001) and cycles (p=0. 0001) influenced the results. The mean roughness values obtained were (means followed by the same letter are not significantly different according to Tukey (α=5%)): 0. 07μm (A) - ROK; 0. 08μm (B) - Z250; 0. 12μm (C) - Charisma; 0,17μm (D) - Filtek LS. Conclusion: The UDMA-based resin composites present higher surface abrasion resistance. The silorane-based composites present lower surface abrasion resistance. The resin composites photo activated by 16J/cm2 present lower roughness than composites cured by 8J/cm2.Article 2 - Aim: To evaluate the surface roughness of two resin composites with different organic phase when submitted to a simulated wear test with tooth brushing and whitening dentifrices. Materials and methods: Forty-eight samples were built and divided into 6 groups (n=8) according to composite resin (ROK (SDI) or Z250 (3MESPE) and dentifrice used (Colgate Total 12, Colgate Max White or Close up Extra Whitening). The resins were submitted to cycles of simulated tooth brushing until 24 months. After each simulated period, the surface roughness of the resins was measured. Results: The surface roughness(Ra) average, in μm, to the Colgate total 12 (control), Colgate Max White and Close up Extra Whitening dentifrices were, respectively (means followed by the same letter are not statistically different to ANOVA and Tukey (p<0,05)): 1) ROK: 0. 09(B), 0. 12(B) and 0. 11(B); 2) Z250: 0. 09(B), 0. 21(A) and 0. 21(A). Conclusions: The ROK composite resin presented lower surface roughness (0. 11) than Z250 (0. 17). The resin composites ROK and Z250 have its abrasion resistance decreased when the whitening dentifrices Colgate Max-White and Close Up Extra-Whitening are applied. / Artigo 1 - Objetivo: Comparar a rugosidade de superfície de quatro resinas compostas com diferentes composições de matriz orgânica, através do ensaio de abrasão por escovação simulada até 20. 000 ciclos. Materiais e Métodos: Cento e sessenta corpos de prova foram confeccionados e divididos em 16 grupos (n=10) conforme o tipo de resina, fonte de luz e quantidade de energia. As resinas utilizadas foram Charisma, Z250, ROK e Filtek LS, sendo fotopolimerizadas com LED ou Luz halógena, recebendo 8 ou 16 J/cm². Após 24 horas, os corpos de prova foram submetidos à escovação simulada com dentifrício e escova macia por períodos de tempo equivalentes à 6 meses (5000 ciclos), 12 meses (10. 000 ciclos) e 24 meses (20. 000 ciclos). Após cada período foi realizada a medição da rugosidade de superfície. Resultados: Fatores como energia (p=0,0001), tipo de fonte (p=0,0047), resinas (p=0,0001) e ciclo (p=0,0001) influenciaram nos resultados obtidos. Os valores de rugosidade média obtidos foram (médias seguidas de mesma letra não apresentam diferença estística para Tukey (α=5%): 0,07μm (A) para ROK; 0,08µm (B) para Z250; 0,12μm (C) para Charisma e 0,17μm (D) para filtek LS. Conclusão: as resinas compostas que contém UDMA apresentam maior resistência à abrasão de superfície; resinas baseadas em Siloranos apresentam a menor resistência ao desgaste por abrasão e resinas compostas fotoativadas com 16J/cm² apresentam menor rugosidade de superfície do que as polimerizadas com 8J/cm².Artigo 2 - Objetivos: O objetivo deste estudo foi comparar a rugosidade de superfície de duas resinas compostas, com diferentes composições orgânicas, quando submetidas ao ensaio de abrasão por escovação com dentifrícios clareadores. Materiais e métodos: Quarenta e oito corpos-de-prova foram confeccionados, divididos em 6 grupos (n=8) conforme tipo de resina e dentifrício utilizado. As resinas foram submetidas a ciclos de escovação os quais simularam até 24 meses. Após cada período simulado, as resinas compostas tiveram a rugosidade de superfície mensurada. Resultados: as médias finais de rugosidade de superfície (Ra), em μm, para os dentifrícios Colgate total 12 (controle), Colgate Max White e Close up Extra Whitening foram, respectivamente (médias seguidas de mesma letra não apresentam diferença estatística significante para ANOVA e Tukey (p<0,05)): 0,09 (B), 0,12 (B) e 0,11 (B) para a resina ROK; e 0,09 (B), 0,21 (A) e 0,21(A) para Z250. Conclusões: A resina composta ROK apresentou menor rugosidade de superfície do que a resina Z250. As resinas compostas ROK e Z250 tem a sua resistência ao desgaste superficial diminuída com o uso de dentifrícios mais abrasivos e utilizados para clareamento dos dentes: Colgate Max-White e Close Up Extra-Whitening.

Made available in DSpace on 2011-12-27T14:14:13Z (GMT). No. of bitstreams: 2 000387554-0.pdf: 6424305 bytes, checksum: eede53bc1323d5be8d0e3d939fde81ca (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Seventeen extracted healthy third molars were used in order to evaluate dentine as to: microtensile bond strength (μTBS) with Z250 resin composite (CR), and 3M Single Bond 2 adhesive; appearance previous to adhesive treatment (APTA); adhesive union (UA); type of fracture by Scanning Electron Microscope (SEM), and energy dispersion spectroscopy (EDS), comparing the treatment with a KGSorensen diamond bur (PD) and a CVDentus (UT) ultrasound tips with (c/a) and without (s/a) etching. Four groups (n=40) were divided according to the dentin processing (PDs/a - diamond bur without etching); (PDc/a - diamond bur with etching); (UTs/a - ultrasound tip without etching); (UTc/a - ultrasound tip with etching) were restored, embedded in politetrafluoretilene tube using chemically activated acrylic resin, and sectioned into samples for μTBS testing in an EMIC DL-2000 universal machine (0. 5 mm/min). Samples were analyzed by SEM and EDS for fracture classification UA and APTA. Statistical tests were: Kolmogorov- Smirnov Test; Two way Variance Analysis; Tukey and Fisher's Exact Test (p≤0,05). Failures were classified as: cohesive in dentine (CD); cohesive in CR (CM); cohesive interfacial on the base or top of hybrid layer (CBT); adhesive cohesive interfacial (CA); mixed (M); interfacial on smear layer (S). Results showed (group, average μTBS in MPa - standard deviation): (UTc/a, 45. 31-8. 16); (PDc/a, 34. 04-9. 29); (UTs/a, 15. 17-3. 71); (PDs/a, 9. 86-3. 80).The PD method is associated to CBT, and the UT method is associated to CA and CM; c/a is associated to CBT and CM, and s/a is associated to S. APTA showed: PDs/a - total obstruction of dentinal tubules (cd); UTs/a - partial disobstruction of cd and irregular surface appearance; PDc/a - complete disobstruction of cd; UTc/a - complete disobstruction of cd, and irregular surface appearance. UA showed: PDs/a rectilinear hybrid layer occurred without tags penetration (PT); UTs/a, curvilinear with a few PT; PDc/a, rectilinear with PT; UTc/a, curvilinear with PT. It was concluded that the association of UTc/a treatment promotes higher values of μTBS. There is an association between CBT failure and the PD method, failures CA and CM and the UT method, failures CBT and CM and the c/a method, and failure S and the s/a method. The failures that caused higher resistance to its rupture were, in a decreasing order: CD; CM; CBT; CA; M, and S. / Dezessete terceiros molares hígidos extraídos foram utilizados com objetivo de avaliar a dentina quanto: resistência à união por microtração (μTBS) com resina composta (CR) Z250 e adesivo Single Bond 2 (3M); aspecto prévio ao tratamento adesivo (APTA); união adesiva (UA); tipo de fratura por microscopia eletrônica de varredura (MEV) e espectroscopia por dispersão de energia (EDS) comparando o tratamento com ponta diamantada KGSorensen (PD) e haste ultra-sônica CVDentUS (UT) com (c/a) ou sem (s/a) condicionamento ácido. Quatro grupos (n=40) divididos conforme processamento dentinário (PDs/a; PDc/a; UTs/a; UTc/a) foram restaurados, incluídos em resina acrílica autopolimerizável e transformados em pequenas barras por máquina de corte seriado para posterior ensaio de μTBS em máquina universal EMIC DL-2000 (0,5 mm/min). As amostras foram analisadas por MEV e EDS para classificação de fratura, UA e APTA. Os testes estatísticos foram: Kolmogorov-Smirnov; Análise de Variância fatorial; Tukey e Exato de Fisher (p≤0,05). As falhas foram classificadas em: Coesiva em dentina (CD); coesiva em CR (CM); interfacial coesiva na base ou topo de camada híbrida (CBT); interfacial coesiva adesiva (CA); mista (M); interfacial no smear layer (S). Os resultados mostraram (grupo, média μTBS em MPa - desvio padrão): (UTc/a, 45,31-8,16); (PDc/a, 34,04-9,29); (UTs/a, 15,17-3,71); (PDs/a, 9,86-3,80). O método PD está associado à CBT e o método UT às CA e CM, c/a está associado às CBT e CM e s/a à S. O APTA mostrou: PDs/a total obstrução dos canalículos dentinários (cd); UTs/a parcial desobstrução dos cd e aspecto irregular de superfície; PDc/a completa desobstrução dos cd; UTc/a completa desobstrução dos cd e aspecto irregular de superfície. Em PDs/a ocorreu camada híbrida retilínea sem penetrações de tags (PT); UTs/a, curvilínea com algumas PT; PDc/a, retilínea com PT; UTc/a, curvilínea com PT. Concluiu-se que a associação do tratamento UTc/a promove valores maiores de μTBS. Existe associação entre falha CBT com o método PD, falhas CA e CM com o método UT, falhas CBT e CM com o método c/a e falha S com o método s/a. As falhas que ofereceram maior resistência para seu rompimento são, em ordem decrescente: CD; CM; CBT; CA; M; S.

Made available in DSpace on 2011-12-27T14:14:18Z (GMT). No. of bitstreams: 2 000385863-0.pdf: 11730392 bytes, checksum: be18f24f5772871dae60f25e74a3ef0b (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This study evaluated the influence of different surface treatments to dentin with pre-cured adhesive layer when the immediate dentin sealing technique (IDS) was applied in different storage time with provisional cement on microtensile bond strength of two adhesive systems, classified the failure pattern and measured the adhesive layer thickness. The dentin bonding agent (DBS) Single Bond 2 (SB2) (3M ESPE) e Prime&Bond NT (PB) (Dentsply) were tested in two storage times: 48 hours (A) and 4 months (B). Freshly prepared flat dentin surfaces of extracted human molars were coated with the adhesive systems according to the surface treatments groups: G1) aluminum-oxide - SB2; G2) 37% phosphoric acid - SB2; G3) oxide+acid - SB2; G4) aluminum-oxide - PB; G5) 37% phosphoric acid - PB; G6) oxide+acid - PB; G7) control - SB2; G8) control - PB. After curing the DBA, the provisional cement RelyXTemp NE (3M ESPE) was applied to the bonded dentin surface of the groups 1, 2, 3, 4, 5 and 6, and the teeth were stored for 48 hour or 4 months. After the storage, provisional cement layer was scaled off and the different surface treatments were applied followed by a second DBS layer. The control groups (7 and 8) didn’t received the provisional cement neither the second DBS layer, however were stored for the same times.The composite crown restoration was built with direct resin and, after 24h, the prepared teeth were serially sectioned in sticks. The specimens (n=20 per group) were submitted to microtensile strength test using the universal testing machine EMIC DL-2000. The average values (MPa) were (means followed by different letters are statistically different to General Linear Model and Turkey’s test (p<0,05)): G1A - 23,79±5,92(AB); G1B - 23,93±5,49(AB); G2A - 28,47±6,57(B); G2B - 27,84±3,31(B); G3A - 44,84±10,49(C); G3B - 44,37±9,07(C); G4A - 19,14±4,76(A); G4B - 18,51±4,64(A); G5A - 30,60±5,48(B); G5B - 28,30± 3,95(B); G6A - 47,22±10,11(C); G6B - 46,02±10,33(C); G7A - 41,57±6,91(C); G7B - 41,21±9,32(C); G8A - 40,17±10,35(C) e G8B - 41,04±11,21(C). The fractures specimens were analyzed by SEM and the mixed failure was predominant (92%) followed by interfacial failure (21%). The adhesive thickness range in increasing order: G8< G7< G4< G1< G6< G3< G5< G2. These results suggested that: the surface treatment with aluminum-oxide + 37% phosphoric acid provided the highest bond strength values, however the storage times and the DBS didn’t affect these values; the mixed failure was predominant followed by interfacial failure; and the surface treatments affected significantly the bonding layer thickness for both tested DBS. / Este estudo avaliou a influência de diferentes tratamentos de superfície na dentina pré-hibridizada com a técnica do selamento dentinário imediato (SDI) e armazenada por diferentes períodos na resistência de união à microtração de dois sistemas adesivos. Os agentes de união dentinária (AUD) utilizados, Single Bond 2 (SB2) (3M ESPE) e Prime&Bond NT (PB) (Dentsply), foram testados em dois períodos de armazenagem: 48 horas (A) e 4 meses (B). Superfícies planas de dentina foram preparadas em molares humanos extraídos e foram cobertas com o sistema adesivo de acordo com o tratamento de superfície de cada grupo: G1) óxido de alumínio - SB2; G2) ácido fosfórico 37% - SB2; G3) óxido+ácido - SB2; G4) óxido de alumínio - PB; G5) ácido fosfórico 37% - PB; G6) óxido+ácido - PB; G7) controle - SB2; G8) controle - PB. Após a polimerização do sistema adesivo o cimento provisório RelyXTemp NE (3M ESPE) foi aplicado sobre as superficies dentinárias previamente tratadas com adesivo dos grupos 1, 2, 3, 4, 5 e 6 e estes foram armazenados por 48 horas ou 4 meses. Após o período de armazenagem a camada de cimento provisório foi removida e os diferentes tratamentos de superfície foram empregados seguidos de uma segunda camada de AUD. Os grupos controle (7 e 8) não receberam o cimento provisório nem a segunda camada adesiva, sendo no entanto armazenados pelos mesmos períodos de tempo. Coroas de resina composta direta foram construídas e, após 24h, os dentes preparados foram seccionados em palitos. As amostras (n=20 por grupo) foram submetidas ao teste de resistência de união à microtração na máquina de ensaios universal EMIC DL-2000.Os valores médios (MPa) foram (médias seguidas de letras diferentes são estatisticamente diferentes para Modelo Linear Geral e teste de Tukey (p<0,05)): G1A - 23,79±5,92(AB); G1B - 23,93±5,49(AB); G2A - 28,47±6,57(B); G2B - 27,84±3,31(B); G3A - 44,84±10,49(C); G3B -44,37±9,07(C); G4A - 19,14±4,76(A); G4B - 18,51±4,64(A); G5A - 30,60±5,48(B); G5B - 28,30± 3,95(B); G6A - 47,22±10,11(C); G6B - 46,02±10,33(C); G7A - 41,57±6,91(C); G7B - 41,21±9,32(C); G8A - 40,17±10,35(C) e G8B - 41,04±11,21(C). O tipo de fratura foi analisado através de MEV e a falha do tipo mista foi predominante (92%) seguida da falha interfacial (21%). A espessura de adesivo variou em ordem crescente nos grupos: G8< G7< G4< G1< G6< G3< G5< G2. Os resultados sugerem que: o tratamento de superfície com óxido de alumínio + ácido fosfórico 37% proporcionou os maiores valores de resistência de união, no entanto o tempo de armazenagem e o AUD utilizado não afetaram estes valores; a falha mista foi predominante seguida da falha interfacial; e os tratamentos de superfície utilizados afetaram significativamente a espessura da camada adesiva para ambos os AUD testados.