Submitted by Johnny Rodrigues (johnnyrodrigues@ufcg.edu.br) on 2018-04-18T15:31:59Z No. of bitstreams: 1 VANUCIA SANTOS DIAS - DISSERTAÇÃO PPG-CEMat 2014..pdf: 3639913 bytes, checksum: 915ca6c2f3b8eced104eb3bd31c33dd3 (MD5) / Made available in DSpace on 2018-04-18T15:31:59Z (GMT). No. of bitstreams: 1 VANUCIA SANTOS DIAS - DISSERTAÇÃO PPG-CEMat 2014..pdf: 3639913 bytes, checksum: 915ca6c2f3b8eced104eb3bd31c33dd3 (MD5) Previous issue date: 2014-08-29 / Um dos grandes problemas sanitários está na disposição final dos resíduos gerados pela população e pelas indústrias. No estado da Paraíba, são coletados diariamente 2.754 toneladas de resíduos sólidos urbanos, destes 30,9% têm destinação final em aterros sanitários, 36,9% destinam-se para aterros controlados e 32,2% têm como destino final os lixões. O reaproveitamento do vidro indica 100% de reprocessamento. Além de ser 100% reciclável, o vidro, quando reaproveitado, resulta em redução do impacto ambiental e ainda contribui para diversificação da fabricação de produtos e para diminuição dos custos finais de sua produção. Este trabalho objetiva estudar o processo de recozimento de resíduos vítreos, visando contribuir para o desenvolvimento de uma tecnologia social de reciclagem de vidros para as trabalhadoras do CAVI - Associação de Catadores e Recicladores de Vidros e outros Materiais. Para isso foram utilizados resíduos de vidros planos e ocos submetidos a cinco processos de fusão e recozimento com diferentes níveis de temperatura, empregando técnicas de reciclagem de vidro a quente (vitrofusão e termoformado). Foram utilizados moldes de cerâmica para os estudos iniciais e de gesso para a confecção dos corpos de prova. A resistência após o recozimento foi analisada por meio de ensaios de impacto, em que pode ser constatado que as amostras submetidas ao tratamento térmico estudado apresentaram maior resistência ao impacto quando comparadas às amostras que não receberam tratamento térmico durante o processo de fusão. As fraturas obtidas após os ensaios foram analisadas macroscopicamente. / One of the major health problems is the disposal of waste generated by the population and industries. In the state of Paraíba, are collected daily 2,754 tons of municipal solid waste, 30.9% of these have final disposal in landfills, 36.9% intended to controlled landfills and 32.2% have a final destination landfills. Recycling of glass indicates 100% reprocessing. Besides being 100% recyclable glass, when reused, resulting in reduced environmental impact and still contributes to diversification of manufacturing products and to decrease the final cost of its production. This work aims to study the process of annealing of glassy waste, aiming to contribute to the social development of a recycling technology for glass workers CAVI - Association of Collectors and Recyclers of Glass and other Materials. For this waste flat glass and hollow undergone five mergers and annealing with different temperature levels were used, employing techniques of recycling glass hot (fusing and slumping). Ceramic molds for the initial studies and gypsum for the manufacture of test specimens were used. The resistance after annealing was examined by impact tests, it can be seen that the samples subjected to the heat treatment study had higher impact resistance compared to samples which received no heat treatment during the melting process. The fractures obtained after the tests were analyzed macroscopically.

Submitted by Maria Medeiros (maria.dilva1@ufcg.edu.br) on 2018-07-06T10:25:06Z No. of bitstreams: 1 VALDÊNIA DE SOUSA PORTO - TESE (PPGCEMat) 2016.pdf: 3526742 bytes, checksum: fea218c4b8700fd8dd39f8848fdeda24 (MD5) / Made available in DSpace on 2018-07-06T10:25:06Z (GMT). No. of bitstreams: 1 VALDÊNIA DE SOUSA PORTO - TESE (PPGCEMat) 2016.pdf: 3526742 bytes, checksum: fea218c4b8700fd8dd39f8848fdeda24 (MD5) Previous issue date: 2016-08-09 / Capes / A preocupação da sociedade com a preservação do meio ambiente vem aumentando progressivamente ao longo dos anos. A população tem se voltado para os conceitos de sustentabilidade, e, dessa forma, vários segmentos ligados à ciência e à tecnologia vêm buscando alternativas para controlar ou minimizar danos causados pelo consumo indiscriminado de matéria-prima natural e energia, além do alto volume de resíduos gerados. Diante dessa premissa, o objetivo da pesquisa foi estudar a possibilidade de utilização do resíduo de vidro de lâmpada fluorescente na composição de uma cerâmica porosa celular. Para a realização da pesquisa, as matérias-primas (argila, alumina e resíduo de vidro de lâmpada) foram submetidas aos seguintes ensaios de caracterização: Espectroscopia de Energia Dispersiva de Raio-X (EDX), Análise Granulométrica (AG), Difração de Raios-X (DRX), Espectroscopia de Infravermelho com Transformada de Fourier (FTIR), Análise Térmica Diferencial (DTA) e Termogravimetria (TG). Foram formuladas três composições de massa cerâmica porosa com diferentes proporções de argila, alumina e, posteriormente, adicionados 5%, 7% e 10% de resíduo de vidro de lâmpada fluorescente. Para conhecer as propriedades reológicas, as suspensões foram preparadas com 72% de sólido e 28% de água destilada; para as medições de viscosidade aparente, utilizou-se o silicato de sódio de 1,2g.ml-1. O processo de conformação utilizado foi o método da réplica. Os resultados sugerem a possibilidade de reutilização de resíduos de vidro de lâmpadas fluorescentes na espuma cerâmica para a composição 1, contendo 50% de argila, 40% de alumina e 10% de resíduo de lâmpada fluorescente na temperatura de queima de 1250oC, e, para a composição 2, com 43% de argila, 50% de alumina e 7% de resíduo de vidro e lâmpada fluorescente na temperatura de queima de 1300oC. Isso mostra que as peças apresentaram melhor desempenho mecânico do que as composições sem o resíduo vítreo, trazendo, assim, um benefício tecnológico e ambiental. / The concern of society with preservation of environment has been increasing steadily over the years. People have turned to concepts of sustainability and thus various segments related to science and technology have been seeking alternatives to control or minimize damage caused by the indiscriminate use of natural raw materials and energy, besides high volume of waste generated. From this premise, the objective of the research was to study the possibility of using the fluorescent lamp glass residues in cell porous ceramic composition. For conducting the survey, the raw materials (clay, alumina and glass lamp residue) were subjected to the following characterization tests: Energy Dispersive Spectroscopy X-ray (EDX), Sieve Analysis (AG)-Ray Diffraction (XRD), Infrared Spectroscopy Fourier Transform (FTIR), Differential Thermal Analysis (DTA) and thermogravimetry (TG). Three porous ceramic mass compositions were formulated with different ratios of clay, alumina; then, it was added 5%, 7% and 10% of fluorescent lamp glass residue. To know the rheological properties, the slurries were prepared with 72% solid and 28% distilled water, for apparent viscosity measurements, it was used the sodium silicate 1,2g.ml-1. The forming process used was the replica method. The forming process used was the replica method. The results suggest the possibility of reuse of fluorescent lamps glass waste in the ceramic foam to the composition 1, that contains 50% of clay, 40% of alumina and 10% of fluorescent lamp residue in a burn temperature of 1250°C; and to the composition 2, with 43% of clay, 50% of alumina and 7% of fluorescent lamp glass residue on burn temperature of 1300°C. This shows that the parts have better mechanical performance than compositions without the glassy residue, what brings a technological and environmental benefit.

Submitted by Emanuel Varela Cardoso (emanuel.varela@ufcg.edu.br) on 2018-06-22T18:40:01Z No. of bitstreams: 1 JOSÉ GLÊDSON DE SOUSA SILVA – TESE (UAEMa) 2015.pdf: 8998410 bytes, checksum: a46e8373d05a23d7dbcad46b391033a5 (MD5) / Made available in DSpace on 2018-06-22T18:40:01Z (GMT). No. of bitstreams: 1 JOSÉ GLÊDSON DE SOUSA SILVA – TESE (UAEMa) 2015.pdf: 8998410 bytes, checksum: a46e8373d05a23d7dbcad46b391033a5 (MD5) Previous issue date: 2015-04-29 / Voltado para prática da sustentabilidade na construção civil, propõe-se o uso de vidro plano temperado, fragmentado, em substituição à pedra britada em concretos em percentuais de substituição de 0%, 50% e 100%. O trabalho teve como objetivo a análise microestrutural de concretos com traços fixados em 1:3, fatores água/cimento de 0,45, 0,55 e 0,65, submetidos à cura em câmara úmida saturada de hidróxido de cálcio nas idades de 7, 28 e 91 dias. As matériasprimas foram caracterizadas através de análise granulométrica. Os concretos no estado fresco foram classificados através de abatimento por tronco de cone. Os concretos de referência obtiveram classes desde S10 a S160, enquanto que os concretos com adição de vidro variaram de S50 a S220. Os corpos de prova cilíndricos, com dimensões 5 cm x 10 cm, foram submetidos à ensaios de resistência à compressão simples (RCS). Os concreto de referência (0% de vidro) se classificaram com classe de resistência C20 e C25. Já os concretos com percentual de substituição de 50% tevesua classe de resistência variando do C15 ao C30, enquanto que os de 100% de vidro, classes C15 e C20. Empregou-se para o estudo do nível de adesão, na interface vidro/pasta, imagens obtidas via microscopia ótica digital USB, além de microscopia eletrônica de varredura, constatando-seinterfaces bem preservadas mesmo após ruptura sob compressão. Utilizou-se difração de Raios-X constatando-se estruturas semelhantes para os diversos valores intervenientes e média geral de cristalinidade superior a 94%. Através de microanálise por energia dispersiva constatou-se que os concretos com percentuais parcial e total tem natureza química semelhante ao concreto de referência. Os valores de RCS e o comportamento do vidro como agregado graúdo permitem o emprego desse concreto em aplicações estruturais, como lajes e pilares, e aplicações não estruturais, a exemplo de pavimentos e pisos. / Aiming at sustainability practices in civil construction, it isproposed the use of fragmented, flat tempered glass replacing the crushed stone in concrete in replacement percentages of 0%, 50% and 100%. The research aimed at the microstructural analysis in concrete with traces fixed in 1:3, water/cement factors of 0.45, 0.55 and 0.65, and replacement percentage of 0%, 50% and 100%, subjected to curing in a saturated, calcium-hydroxide humid chamber at the ages of 7, 14 and 28 days. The raw materials were characterized by particle size analysis. The concrete in the fresh state was classified in rebate by conical frustum. The concrete of reference obtained classes from S10 toS160, whereas the concrete with glass addition ranged from S50 to S220. The cylindrical specimens with dimensions of 5 cm x 10 cm underwent strength tests in simple compression(RCS). The concrete of reference(0% of glass) were qualified with resistance class of C20 and C25, and the resistance class of the concrete with replacement rate of 50% ranged from C15 to C30, whereas the class of the concrete with the rate of 100% ranged from C15 to C20. To the study of the adhesion level in the glass/pasteinterface, there were used images that were obtained via USB digital microscopy and scanning electron microscope, noting well preserved interfaces even after rupture under compression. It was used x-ray diffraction in the process, noting similar structures for the various factors and crystallinity average value greater than 94%. Using dispersive energy microanalysis, it was discovered that the concrete with partial and full percentage has its chemical nature similar to the concreteof reference. The values of RCS and the behavior of glass as coarse aggregate permit the use of concrete in structural applications such as slabs and pillars, and in non-structural ones, like in pavings and floors.