Submitted by ALINE SILVA FIRMINO null (linefirmino@hotmail.com) on 2017-03-27T17:54:24Z No. of bitstreams: 1 firmino_as_dissertação.pdf: 2266304 bytes, checksum: 13769bd9535af127e6fb921b1f8c1aae (MD5) / Approved for entry into archive by Luiz Galeffi (luizgaleffi@gmail.com) on 2017-03-29T19:17:16Z (GMT) No. of bitstreams: 1 firmino_as_me_sjc.pdf: 2266304 bytes, checksum: 13769bd9535af127e6fb921b1f8c1aae (MD5) / Made available in DSpace on 2017-03-29T19:17:16Z (GMT). No. of bitstreams: 1 firmino_as_me_sjc.pdf: 2266304 bytes, checksum: 13769bd9535af127e6fb921b1f8c1aae (MD5) Previous issue date: 2017-01-27 / O presente estudo teve como objetivo avaliar as características mecânicas de próteses parciais fixas adesivas, confeccionadas em resina composta de uso indireto, reforçadas por uma malha de nylon. Para a confecção da matriz dos espécimes e estudo das tensões nas estruturas, foi realizada análise qualitativa pregressa análise de elementos finitos (FEA). A pesquisa in vitro simula uma prótese parcial fixa de três elementos com inserção entre os primeiros pré-molares e os primeiros molares superiores (n = 60; 10 por grupo). Três dos seis grupos passaram por ciclagem mecânica. Os grupos experimentais foram: G1-prótese fixa convencional; G2 - prótese convencional ciclada; G3 - prótese com reforço da malha posicionada na vertical; G4 – Prótese com reforço da malha posicionada na vertical ciclada; G5 – Prótese com reforço da malha posicionada na horizontal; G6 – Prótese com reforço da malha posicionada na horizontal ciclada.Todos os grupos passaram por ensaio de carga máxima a fratura (EMIC). Os resultados não apresentaram diferença estatística entre os grupos. Concluiu-se que a utilização da malha nylon proporcionou estabilidade, mesmo após a fratura da peça, pois as partes não se separam, além disso, os resultados obtidos in vitro puderam validar os dados in sílico. / The present study aimed to evaluate the mechanical characteristics of adhesive fixed partial dentures, made from composite resin of indirect use, reinforced by a nylon mesh. A finite element analysis (FEA) was used to compile the specimen matrix and to study the stresses in the structures. In vitro research, simulated a fixed partial denture of three elements with insertion between the first premolars and the major maxillary molars (n = 60; 10 per group). Three of the six groups underwent mechanical cycling. The experimental groups were: G1 - conventional fixed prosthesis; G2 - conventional cyst prosthesis; G3 - prosthesis with reinforcement of the mesh positioned vertically; G4 - Prosthesis with reinforcement of the mesh positioned in the cycled vertical; G5 - Prosthetics with mesh reflux positioned horizontally; G6 - Prosthetics with mesh reinforcement positioned horizontally cycled. All groups underwent maximum fracture loading test (EMIC). The results do not present a statistic between the groups. It was concluded that the use of the nylon mesh provided stability, even after fracture of the part, as parts do not separate, besides, the results obtained in vitro could validate the data in silica.

Made available in DSpace on 2017-07-24T19:22:22Z (GMT). No. of bitstreams: 1 VeridianaCamilotti.pdf: 624713 bytes, checksum: f2d0756374875dd344e9aeeecdaac9cc (MD5) Previous issue date: 2005-12-15 / The following study aims to evaluate the influence between the different light sources in curing light of resin cement. The occlusal surfaces of twenty recently extractew undamaged third human molars were removed in order to expose dentine surface. Immediately after, the bond system (Adper Single Bond/3M ESPE ) and resin cement (RelyX ARC/ 3 M ESPE) was applied in accordance with manufacturer instructions. Second generation laboratory resin of 4 mm thickness was applied over tooth and light curing proceeded. According to light sources employed the teeth were divided in four groups: G1 – Control Optilux 401/ Demetron (QTH); G2 – L.E.Demetron/Demetron (LEDs ); G3 – Ultra-Lume LED5 (LEDs) e G4 – Optilight CL/ Gnatus (LEDs). Restored teeth were stored in physiologic serum for 24 h. After stored, teeth were sectioned into vestibule-tongue and mesial-distal to delimit an area with approximately 1 mm², the third cut was made on the base of the tooth in order to release the samples. The microtensile test was employed to reveal the bond strength values in MPa. The data underwent statistical analysis with p<0,05. No statistical significancent difference was found betweem the groups. In conclusion the resin cement bon strength of dual fotoative with LEDs showed similar adhesive resistance test those revelead when halogen lamp was used, and that there also were not differences among the different apparels LEDs used in that study. / Avaliou-se a influência de diferentes fontes de luz na fotoativação de um cimento resinoso dual. A superfície oclusal de 20 terceiros molares humanos hígidos foi removida para expor a superfície dentinária. Em seguida, foi aplicado sistema adesivo (Adper Single Bond/3M ESPE ) e cimento resinoso dual (RelyX ARC/ 3 M ESPE), de acordo com as recomendações do fabricante. A resina laboratorial de segunda geração (Gradia™ GC® América Inc), com espessura de 4 mm, foi adaptada sobre o dente e procedeu-se à fotoativação. De acordo com o aparelho de luz empregado, os elementos dentais foram divididos em 4 grupos: G1 – controle Optilux 401/ Demetron (QTH); G2 – L.E.Demetron 1/Demetron (LEDs ); G3 – Ultra- Lume LED5/Ultradent (LEDs) e G4 – Optilight CL/ Gnatus (LEDs). Os dentes restaurados foram armazenados em soro fisiológico por 24 h. Após o armazenamento, os dentes foram seccionados no sentido vestíbulo-lingual e mésiodistal, para delimitar uma área de 1 mm². Um terceiro corte na base do dente foi realizado com o objetivo de “soltar” os espécimes. O teste de micro-tração foi empregado para fornecer os valores da resistência adesiva em MPa. Os dados foram submetidos à análise estatística pelo teste ANOVA com p<0,05. Não houve diferenças estatisticamente significante entre os grupos testados. Concluiu-se que a resistência adesiva da interace adesiva fotoativado com LEDs foi semelhante à resistência adesiva obtida quando a lâmpada halógena foi utilizada e que também não houve diferenças entre os diferentes aparelhos LEDs empregados nesse estudo.