Orientador: Mário Fernando de Góes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T18:56:44Z (GMT). No. of bitstreams: 1 Lacerda_RenataFernandesdeSouza_M.pdf: 2496553 bytes, checksum: 8b83acbb5a024d77dc12f2bb97771b5f (MD5) Previous issue date: 2013 / Resumo: O objetivo deste estudo foi avaliar a resistência da união de cimentos resinosos autoadesivos e autocondicionantes aplicados sobre a superfície da dentina e esmalte. Foram utilizados 36 terceiros molares. Em metade destes dentes tiveram a face oclusal removida e a dentina exposta. Na outra metade, as coroas foram seccionadas longitudinalmente para obter hemi-secções de esmalte. A seguir ambas as amostras foram planificadas usando lixas de carbeto de silício de granulação #600. Restaurações de resina composta indireta (Sinfony), com 2 mm de espessura, foram confeccionadas em dois formatos circulares, de 10 e 7mm de diâmetro e jateadas com óxido de alumínio para serem cimentadas sobre a superfície da dentina e esmalte, respectivamente. Os dentes preparados foram divididos em 4 grupos para cada substrato (esmalte e dentina): Grupo I - RelyX Unicem 2 - cimento autoadesivo, Grupo II - Maxcem Elite - cimento autoadesivo, Grupo III - RelyX Unicem 2 associado ao sistema adesivo Scothbond Universal - cimento autocondicionante, Grupo IV - Multilink Automix - cimento autocondicionante. Após a cimentação os conjuntos dente/restauração foram armazenados em água destilada à 37°C por 24 horas e seccionados em formato de palitos com área transversal quadrada de 0.8±0.2mm2 para o ensaio de tração, utilizando uma máquina de ensaios universal operando com célula de carga de 50kgf e à velocidade de 1mm/min. O tipo de fratura foi observado e classificado em microscopia eletrônica de varredura (MEV). Os dados foram submetidos à análise de variância e o teste de Tukey para comparação entre os grupos (p<0,05). Os resultados da resistência de união revelaram que dentre os cimentos autoadesivos, o cimento RelyX Unicem 2 (13±4,2 e 14,3±6,8) apresentou valor significantemente maior comparado ao Maxcem (12,2±5,9 e 5,4±3,1) quando avaliado sobre a dentina. Na condição autocondicionante o cimento RelyX Unicem 2 associado ao adesivo Scothbond Universal (29,7±12,1 e 50,6±18,2) apresentou valor estatisticamente superior ao valor apresentado pelo Multilink Automix (20,5±10,4 e 20,7±10,5) para o esmalte e dentina. Na condição autocondicionante a resistência de união foi superior estatisticamente à condição autoadesiva. As análises dos padrões de fratura em MEV no substrato dentinário mostraram predominância de fraturas coesivas em cimento para a maioria dos grupos, exceto para o grupo Maxcem, que apresentou predominância de fraturas mistas (coesivas no material e coesiva na smear layer). No esmalte houve predominância de fraturas coesivas no cimento para os grupos RelyX Unicem 2, RelyX Unicem 2 associado ao sistema adesivo Scothbond Universal e Maxcem Elite, enquanto que para o Multilink Automix houve predominância de fraturas mistas (adesiva e coesiva em cimento) / Abstract: The aim of this study was to evaluate the bond strength of self-etching and self-adhesive resin cements applied on the surface of the enamel and dentin. We used 36 third molars. Half of these teeth have the occlusal face removed to expose dentin surface. The remainder teeth were longitudinally sectioned to obtain hemi-sections of enamel. All surface of the teeth were flattened using silicon carbide sandpaper granulation #600. Circular matrix shapes (10 and 7mm in diameter) were prepared to fabricate an indirect composite resin restorations (Sinfony) with 2 mm thick). The surface of the restoration was air-abrasioned using aluminum oxide to be cemented onto the dentin and enamel surfaces, following the manufacturing recommendations. The prepared teeth were divided into 4 groups for each substrate [enamel and dentin]: Group I - RelyX Unicem 2 - self-adhesive cement; Group II - Maxcem Elite - Self-adhesive cement; Group III - Multilink Automix - self-etching cement; Group IV - RelyX Unicem 2 associated with adhesive system Scothbond Universal - self-etching cement. After cementing sets tooth / restoration were stored in distilled water at 37 ° C for 24 hours and sectioned shaped sticks with square area 0.8 ± 0.2mm2 for the tensile test using a universal testing machine. The fracture mode was observed and classified by SEM (scanning electron microscopy). The results were submitted to ANOVA and Tukey's test for comparison between groups (p<0.05). The results in enamel and dentin were, respectively in MPa: self-adhesive cement RelyX Unicem 2 (13,0±4.2 and 14.3±6.8) and Maxcem Elite (12.2 ± 5.9 and 5.4±3.1); self-etching cement - RelyX Unicem 2 associated with adhesive system Scothbond Universal (29.7±12.1 and 50.6±18.2); Multilink Automix(20.5±10.4 and 20.7±10.5). The bond strength of the self-etching cements showed statistical differences compared with self-adhesive cements in both enamel and dentin tissues. The Bond strength values produced by RelyX Unicem 2 associated with adhesive system Scothbond Universal was significantly higher than all other groups in enamel and dentin. The Self-adhesive cement Rely X Unicem 2 showed statistical difference in bond strength compared with MaxCem Elite in dentin. The fracture patterns showed predominance of cohesive fractures cement for most group, in dentin, except for group Maxcem, which showed a predominance of mixed fracture (cohesive in material and cohesive in the smear layer). In enamel predominated cohesive fractures in the cement for groups RelyX Unicem 2, RelyX Unicem 2 associated with the adhesive system Scothbond Universal and Maxcem Elite, while for Multilink Automix fractures predominated mixed (adhesive and cohesive in cement) / Mestrado / Materiais Dentarios / Mestra em Materiais Dentários

Orientador: João Sinézio de Carvalho Campos / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-19T08:39:45Z (GMT). No. of bitstreams: 1 Bento_RonaldoEuzebio_M.pdf: 1080016 bytes, checksum: c783e50a51346a7d89eb82f52976eb49 (MD5) Previous issue date: 2011 / Resumo: Esse trabalho concentra os estudos na investigação das propriedades de resistência a tração e alongamento do compósito de Politetrafluoretileno (PTFE) com 60% de bronze após a substituição do tipo de PTFE utilizado na formulação desse compósito. Atualmente esse compósito utiliza PTFE convencional na formulação e o objetivo é alterar para PTFE modificado. A motivação para essa alteração deveu-se ao fato que o PTFE convencional apresenta disponibilidade limitada dificultando o desenvolvimento dos segmentos que utilizam os compósitos de PTFE com 60% de bronze. A escolha do PTFE modificado para a substituição do PTFE convencional na formulação do compósito de PTFE com 60% de bronze deveu-se ao fato que polímero puro de PTFE modificado apresenta propriedades mecânicas e químicas superiores ao polímero puro de PTFE convencional, além de não apresentar limitações de disponibilidade, possibilitando a continuidade do crescimento dos segmentos industriais. A escolha do compósito de PTFE com 60% de bronze deveu-se ao fato que essa formulação é a mais empregada no segmento automobilístico para a fabricação de anéis para amortecedores e retentores. Após a substituição da resina de PTFE, os resultados demonstraram que o compósito de PTFE modificado com 60% de bronze apresentou propriedades inferiores ao compósito fabricado com PTFE convencional. A queda dessas propriedades pode estar relacionada com possíveis micros fissuras na estrutura do compósito em virtude de ar preso durante o processo de fabricação / Abstract: This work focuses on research studies of the properties of tensile strength and elongation of the composite of Polytetrafluoroethylene (PTFE) with 60% bronze after replacing the type of PTFE used in the formulation of this compound. Currently, this composite uses conventional PTFE in the formulation and the objective is to change to modified PTFE. The motivation for this change was due to the fact that the conventional PTFE has limited availability hindering the development of the segments that use the PTFE composite with 60% bronze. The choice of PTFE modified PTFE to replace the conventional formulation of the composite with 60% PTFE bronze was due to the fact that pure polymer modified PTFE has superior mechanical and chemical properties of the pure polymer PTFE conventional, and not present availability limitations, enabling the continued growth of industries. The choice of the composite with 60% PTFE bronze due to the fact that this formulation is the most used in the automotive sector for the manufacture of rings and seals for shock absorbers / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química

Orientador: Luis Alexandre Maffei Sartinni Paulillo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-21T22:09:59Z (GMT). No. of bitstreams: 1 Araujo_CintiaTerezaPimentade_D.pdf: 9367664 bytes, checksum: 6c7161dae0f158a143f829e530249b20 (MD5) Previous issue date: 2013 / Resumo: A microscopia confocal de varredura a laser (MCVL) é um recurso de visualização microscópica que permite a análise de materiais ou estruturas com requisitos mínimos de preparação de amostras de modo não destrutivo. Assim, os objetivos deste estudo foram: avaliar a influência da incorporação do corante fluorescente Rodamina B (R) nas propriedades mecânicas resistência coesiva (RC), módulo de elasticidade (ME) e resistência à flexão (RF) de 2 sistemas adesivos, o autocondicionante Clearfil SE Bond e o convencional Scotchbond Multi-Purpose (estudo 1); validar o método modificado de microtração (?TBS), em que micro-amostras de secção transversal de 0,09 mm2 foram testadas e verificar a influência da R na resistência à união a dentina e integridade interfacial através de microscopia confocal (estudo 2). Para avaliar a influência do corante, 0,16 mg/ml de R foram incorporados aos adesivos constituindo assim dois grupos para cada adesivo: grupos dos adesivos corados e não corados totalizando 4 grupos experimentais. Para a análise da RC, E e RF, os corpos de prova foram confeccionados a partir de uma matriz de silicone por adição. Sobre a matriz, foram dispensados 10 ?L de adesivo variando de acordo com cada grupo de adesivos corados e não corados. RC (n= 10), E e RF (n= 5) foram avaliadas em máquina de ensaio universal a 0,5 mm/min, até a ruptura da amostra. Para visualização em microscopia confocal e análise da resistência à união os adesivos foram aplicados à superfície plana da dentina oclusal de 32 pré-molares humanos. Após a realização dos procedimentos adesivos, realizaram-se as restaurações (blocos de 16 mm2) com Charisma Opal (Kulzer - cor A3). Em seguida, para a realização do teste modificado de microtração, micro-amostras em forma de palito (secção transversal 0,09 mm2) foram confeccionadas. Previamente ao ensaio mecânico, foi realizada através de MVCL a análise micromorfológica das microamostras dos grupos de adesivos corados. Posteriormente a resistência à união foi mensurada através do ensaio modificado de microtração a velocidade de 0,5 mm/min em máquina de ensaio universal. Os dados de todos os testes avaliados foram submetidos à análise de variância dois fatores. Os resultados mostraram que o comportamento dos sistemas adesivos investigados não se modificou, independente da presença do corante, pois não foram observadas diferenças significativas nas propriedades mecânicas estudadas: resistência à união, resistência coesiva, resistência flexural, módulo de elasticidade, bem como a integridade interfacial. A preparação de micro-amostras não comprometeu os resultados do ensaio de resistência adesiva. De acordo com os resultados obtidos e análise dos parâmetros: coeficiente de variação, porcentagem de padrão de fratura e incidência de falhas prematuras, concluiu-se que o teste modificado de microtração foi considerado um método confiável para a avaliação da resistência à união de sistemas adesivos. A técnica de visualização microscópica confocal produziu informações detalhadas da interface adesiva e pode ser bem indicada para a avaliação da efetividade de união de sistemas adesivos. Desta forma, é possível associar ambas as metodologias obtendo-se uma avaliação mais realista e confiável dos materiais restauradores / Abstract: The confocal laser scanning microscopic (CLSM) is a tool of visualization that allows microscopic analysis of materials or structures labeled with fluorescent dyes with minimal requirements of specimen's preparation nondestructively. The aims of this study were: to evaluate the influence of incorporation of fluorescent dye Rhodamine B (R) in the properties mechanical: cohesive strength (CS), elastic modulus (E) and flexural strength (FS) of the selfetching Clearfil SE Bond and etch-and-rinse Scotchbond Multi-Purpose (Study 1); validating the modified microtensile method using micro-specimens cross section of 0.09 mm2 (?TBS) and evaluate the influence of R in bond strength in dentin and interfacial integrity by confocal microscopy (study 2). To evaluate the influence of the dye, 0.16 mg/ml of R were incorporated into adhesives thus forming two groups for each adhesive: groups of labeled adhesives and no-labeled totaling 4 experimental groups. For the analysis of CS, E and FS the specimens were made from a silicone matrix. About the matrix were 10 ?L dispensed adhesive varying according to each group of adhesives stained or not. CS (n = 10), E and FS (n = 5) were evaluated in a universal testing machine at 0.5 mm/min until failure of the specimen. For visualization in confocal microscopy and bond strength analysis (n = 8), the adhesives were applied to the occlusal dentine surface 32 of human premolars. After procedures adhesives, composite crowns approximately (16 mm2) were built up with Charisma Opal (Kulzer - color A3). Then for testing modified microtensile, micro-specimens beam-shaped were prepared. Prior to mechanical testing micromorphological analysis of micro-sticks of the groups of labeled adhesives was performed using CLSM. Subsequently bond strength was measured using the modified microtensile test in a universal testing machine speed of 0.5 mm/min. The results showed that the behavior of the adhesive systems investigated did not change regardless of the presence of the dye, as there were no significant differences in mechanical properties studied: bond strength, tensile strength, flexural strength, modulus of elasticity, as well as interfacial integrity. The preparation of micro-specimens did not affect the results of the bond strength test. According to the analysis results and parameters: coefficient of variation percentage of fracture pattern and incidence of early failures, it is concluded that the modified microtensile test was considered a reliable method for evaluating the bond strength of adhesive systems. The confocal microscopic visualization technique yielded detailed information of the adhesive interface and can be well suited for evaluating the effectiveness of adhesive systems. Thus, it is possible to associate both methods give a more realistic and reliable adhesive restoration on the presence of fluorescent dye / Doutorado / Dentística / Doutora em Clínica Odontológica

Orientadores: Mirela Sanae Shinohara, Mário Fernando de Góes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-21T23:51:52Z (GMT). No. of bitstreams: 1 Freitas_MarcelaSantiago_M.pdf: 38797129 bytes, checksum: 16869befa66eba198d1cb13ad5c9ac1d (MD5) Previous issue date: 2013 / Resumo: Estudos mostram que a resistência de união (RU) alcançada pelos sistemas adesivos autocondicionantes em superfície de esmalte pré-condicionado é significativamente maior se comparada aos valores obtidos em esmalte não condicionado. A partir destas evidências, este estudo teve como objetivo avaliar a RU e a morfologia da interface adesiva (MI) em esmalte e dentina de um adesivo autocondicionante de passo único multi-mode e um adesivo autocondicionante de dois passos com e sem pré-condicionamento ácido da superfície comparado a dois sistemas adesivos de condicionamento total, de dois e três passos. Terceiros molares humanos recém-extraídos foram seccionados para obtenção de superfícies planas em esmalte e dentina, as quais foram desgastadas com lixa SiC #600 para padronização da smear layer. Estas amostras foram divididas aleatoriamente em 6 grupos: (SBU) Scotchbond Universal; (SBUcond) SBU précondicionado; (CSE) Clearfil SE Bond; (CSEcond) CSE pré-condicionado; (SBMP) Scotchbond Multi-Purpose; e (EX) Excite F. Os grupos de condicionamento total e os autocondicionantes a serem avaliados com pré-condicionamento receberam a aplicação do ácido fosfórico por 15s em dentina e 30s em esmalte. Todos os sistemas adesivos foram aplicados de acordo com as recomendações dos fabricantes. Em seguida, um bloco de resina composta (Filtek Supreme Plus) foi construído incrementalmente sobre cada superfície preparada para o teste de RU, e para a MI, as superfícies foram restauradas com resina flow (Filtek Z-350 Flowable Restorative) formando um "sanduíche", de esmalte ou dentina. Após 24h, para avaliação da RU, as amostras foram seccionadas em palitos com área transversal de 0,8mm2 e submetidos ao teste de microtração com velocidade de 1,0mm/min. Os resultados foram analisados estatisticamente pelos testes one-way ANOVA e Fisher's PLSD (?=0.05) e os padrões de fratura analisados em Microscopia Eletrônica de Varredura (MEV). Para análise da MI, duas amostras de cada grupo foram incluídas em resina epóxica, polidas e observadas em MEV. Para esmalte, os resultados de RU mostraram que o SBUcond e CSEcond obtiveram os maiores valores, seguidos dos grupos SBMP, SBU e CSE que não apresentaram diferenças entre si. O grupo EX obteve os menores valores comparados aos outros grupos. Na análise da MI, os grupos SBUcond e CSEcond apresentaram nítidas extensões do adesivo penetrado no esmalte desmineralizado, semelhante aos sistemas de condicionamento total. Já para dentina, os resultados de RU mostraram que o condicionamento ácido prévio diminuiu significativamente os valores de RU dos sistemas autocondicionantes. Os maiores valores foram obtidos pelo SBU, CSE e SBMP, com valores de RU estatisticamente equivalentes entre si. Como em esmalte, o sistema adesivo EX obteve os menores valores. A análise em MEV da MI mostrou que o condicionamento prévio da dentina com adesivos autocondicionantes forma uma camada híbrida mais espessa com formação de tags resinosos, semelhantes aos sistemas adesivos de condicionamento total. Pode-se concluir que em esmalte, o condicionamento prévio aumentou significativamente os valores de RU para os sistemas autocondicionantes. Contudo, estes sistemas adesivos não apresentaram diferença estatística do adesivo convencional SBMP. E para dentina, o pré-condicionamento dos adesivos autocondicionantes diminuiu significativamente os valores de RU, entretanto, os valores de SBUcond não foram diferentes significativamente dos obtidos pelo sistema adesivo convencional SBMP / Abstract: Studies show that the bond strength (BS) achieved by self-etching adhesive systems on pre-etched enamel surface is significantly higher compared with the values obtained on unetched enamel. From this evidence, this study aimed to assess the BS and morphology of the adhesive interface (AI) on enamel and dentin of a one-step self-etching adhesive multi-mode and a two-step selfetching adhesive with and without pre-etching of surface compared with two totaletching adhesive systems, two and three steps. Recently extracted human third molars were sectioned to obtain flat surfaces in enamel and dentin, which were ground with #600 SiC sandpaper to standardize the smear layer. These samples were randomly assigned into 6 groups: (SBU) Scotchbond Universal; (SBU-et) SBU pre-etched; (CSE), Clearfil SE Bond, (CSE-et) CSE pre-etched; (SBMP) Scotchbond Multi-Purpose, and (EX) Excite F. The groups total-etching and selfetching to be evaluated with pre-etching received the application of phosphoric acid for 15s in dentin and 30s in enamel. All adhesive systems were applied according to manufacturers' recommendations. Then, a block of composite resin (Filtek Supreme Plus) was constructed incrementally on each surface prepared for BS testing. For AI, the areas were filled with flowable resin (Filtek Flowable Restorative Z-350) forming a "sandwich" of enamel or dentin. After 24 hours, to review the BS, the specimens were sectioned into sticks with cross-sectional area of 0.8mm² and submitted to microtensile test at a speed of 1.0mm/min. The results were statistically analyzed by one-way ANOVA test and Fisher's PLSD (?=0.05) and fracture patterns were analyzed through Scanning Electron Microscopy (SEM). For analysis of AI, two samples from each group were embedded in epoxy resin, polished and observed through SEM. For enamel, the results of BS showed that SBU-et and CSE-et obtained the highest values, followed by SBMP groups, SBU and CSE with no differences among them. The EX group obtained the lowest values of all other groups. In the analysis of AI, and CSE-et and SBU-et groups showed sharp tag extensions of the adhesive penetrated in the demineralized enamel, similar to total-etching systems. As for dentin, BS results showed that acid etching significantly reduced the BS values of self-etching systems. The highest values were obtained by the SBU, CSE and SBMP with BS values statistically equivalent to each other. As in enamel, the adhesive system EX obtained the lowest values. SEM analysis showed that BS for pre-etched dentin with selfetching adhesive forms a thicker hybrid layer with resin tags formation, similar to total-etching adhesive systems. It can be concluded that on enamel, the preetching significantly increased BS for self-etching systems. However, these adhesive systems showed no statistical difference from conventional adhesive SBMP. And to dentin, pre-etching of sel-etching adhesives significantly reduced BS, however, SBU-et values were not significantly different from those obtained by the conventional adhesive system SBMP / Mestrado / Dentística / Mestra em Materiais Dentários

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / A new generation of adhesive systems are currently available on market. They were reported on the literature as universal adhesives or multimode adhesives . These adhesives are versatile, as they can be use in either etch-and-rinse or self-etch strategy. However, only a few data is available about long-term bonding behavior of universal adhesive systems. Then, the aim of this study is to evaluate immediate and six months bond strength of different universal adhesive systems on sound and caries-affected dentin, either on etch-and-rinse or self-etch strategies. The adhesive systems tested were: Scotchbond Universal (3M ESPE), All-Bond Universal (Bisco), Prime & Bond Elect (Denstply Caulk), Adper Single Bond 2 (3M ESPE) and Clearfil SE Bond (Kuraray Noritake Dental). All adhesive systems were applied under manufacturer s instructions and a composite block was build up on dentin surfaces. Caries-affected dentin was artificially induced by pH-cycling (8h immersed on demineralizing solution and 16h on remineralizing solution, for 14 days). Stick shaped specimens (0,8 mm²) were obtained to be submitted to microtensile test at immediate time or after 6 months of storage. Bond strength data (MPa) were analyzed by three-way repeated measures ANOVA and post-hoc Tukey test (α= 5%). Analysis were performed for each substrate separately. On sound dentin, the etching strategy did not influence bond strength of universal adhesives and no significant statistical differences were found for bond strength values after 6 months of water storage. On caries-affected dentin, adhesive systems also showed similar results regardless etching strategies. However, significant reduction in bond strength values was found after six months. The etching strategy did not influence bond strength performance of universal adhesives on dentin substrate, although the long-term bond strength is decreased on caries-affected dentin. / Recentemente foram introduzidos no mercado uma nova geração de adesivos, reportados pela literatura como adesivos universais ou multi-modo . Esses adesivos são materiais versáteis, podendo ser utilizados tanto na técnica autocondicionante como na técnica com condicionamento ácido prévio. No entanto, pouco sabe-se ainda sobre o comportamento desses adesivos universais em relação à longevidade da adesão. Então, o objetivo deste estudo foi avaliar a resistência de união imediata e após 6 meses de diferentes adesivos universais em dentina hígida e afetada, usando as estratégias de condicionamento ácido prévio e autocondicionante. Os sistemas adesivos testados foram: Scotchbond Universal (3M ESPE), All-Bond Universal (Bisco), Prime & Bond Elect (Denstply Caulk), Adper Single Bond 2 (3M ESPE) e Clearfil SE Bond (Kuraray Noritake Dental). Todos os adesivos foram aplicados seguindo as recomendações dos fabricantes e um bloco de resina composta foi construído sobre a dentina. A dentina afetada foi obtida artificialmente através de ciclagem de pH (8 horas em solução desmineralizante e 16 horas em solução remineralizante, por 14 dias). Espécimes em forma de palitos foram obtidos (0,8 mm²) para serem submetidos ao teste de microtração imediatamente ou após 6 meses de armazenamento. Os dados obtidos em MPa foram analisados por análise de variância de 3 fatores e teste de contraste de Tukey (α= 5%). A análise foi realizada separadamente para cada substrato. Em dentina hígida, a estratégia de condicionamento não teve influência na resistência de união dos adesivos universais e não houve diferença estatisticamente significante entre a resistência de união imediata e após 6 meses. Em dentina afetada, os sistemas adesivos apresentaram resultados similares, independente da estratégia de condicionamento. No entanto, houve uma significativa redução na resistência de união após 6 meses. Assim, a estratégia de condicionamento não influencia a resistência de união dos adesivos universais em dentina, porém a resistência de união a longo prazo é reduzida em dentina afetada.

Orientador: Marcelo Giannini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T02:35:57Z (GMT). No. of bitstreams: 1 Ayres_AnaPaulaAlmeida_M.pdf: 3452977 bytes, checksum: c1245f8af84e3e9b42ae18f3eb096ed8 (MD5) Previous issue date: 2013 / Resumo: O objetivo desse estudo foi avaliar a resistência de união à dentina de sistemas restauradores contendo ou não fluoretos em sua composição e o comportamento do esmalte e da dentina adjacentes às restaurações, quando submetidos ao desafio cariogênico in vitro. Adicionalmente, durante o desafio cariogênio foi mensurada a liberação de fluoreto dos adesivos. Para o estudo foram utilizados 64 dentes terceiros molares humanos e quatro sistemas restauradores: FL-Bond II/Beautifil II, Bond Force/Estelite Sigma, GC Fuji II LC e Adper Easy Bond/Filtek Z350 XT. No estudo de resistência da união à dentina, utilizou-se a dentina coronária, onde foram aplicados os materiais restauradores (n=8). Os dentes foram seccionados para obtenção dos espécimes e o teste de microtração foi realizado em dois tempos: imediato e após um ano de armazenamento em saliva artificial. Para o estudo da microdureza longitudinal, foram confeccionadas cavidades na região cervical, as quais foram restauradas com os quatro sistemas propostos, de acordo com as recomendações dos fabricantes (n=8). Os dentes restaurados foram submetidos à ciclagem térmica (3.000 ciclos) e, posteriormente, à ciclagem de pH durante oito dias. A mensuração da microdureza subsuperficial foi realizada em esmalte e em dentina, em três distâncias da parede cavitária e em seis profundidades em relação à superfície submetida à ciclagem de pH. As soluções desmineralizantes e remineralizantes utilizadas nessa ciclagem foram utilizadas para análise de concentração catiônica de flúor. A análise estatística de resistência de união dentinária mostrou que os valores médios não foram afetados após um ano de armazenamento em saliva artificial para nenhum dos sistemas restauradores. Os resultados de microdureza longitudinal em esmalte apresentaram diferença estatística significativa apenas para a distância 50 ?m. Mas os valores médios de microdureza Knoop em esmalte foram semelhantes para os quatro sistemas restauradores quando avaliados nas mesmas distâncias e profundidades. O mesmo padrão de resultado foi encontrado na dentina, mas os valores médios de microdureza não apresentaram diferença estatística entre as distâncias da restauração. A análise catiônica de flúor detectou liberação de fluoreto nos espécimes restaurados com GC Fuji LC II e FL-Bond II/Beautifil II. A partir dos resultados desse estudo in vitro é possível afirmar que os sistemas restauradores avaliados apresentaram estabilidade da união por um ano, porém apresentaram pouca capacidade de inibição de cárie secundária em esmalte e em dentina, independentemente da liberação ou não de fluoretos / Abstract: The aim of this study was to evaluate the bond strength to dentin of restorative systems containing or not fluoride in their compositions and the performance of enamel and dentin around the restorations, when submitted to cariogenic challenge in vitro. Additionally, the fluoride released was measured during the pH cycling. This study used 64 third molars human teeth and four restorative systems were selected: FL-Bond II/Beautifil II, Bond Force/Estelite Sigma, GC Fuji II LC and Adper Easy Bond/Filtek Z350 XT. For the bond strength evaluation, it was used oclusal dentin in which the restorative materials were applied (n=8). The "restored" teeth were sectioned for obtaining bonded beam specimens and the microtensile test was performed in two times: imediate and after one year of storage in artificial saliva. For the cross-sectional microhardness test, cervical cavities were prepared and filled with the restorative systems according to the manufacturer's instructions (n=8). The restored teeth were submitted to thermo cycling (3.000 cycles) and subsequent pH-cycling during eight days. The cross-sectional microhardness analysis was performed in enamel and dentin, at three distances from cavity wall and at six depths regarding the surface submitted to pH-cycling. The desmineralizing and remineralizing solutions of this pH-cycling regimen was used for fluor cationic concentration analysis. The statistical analysis of bond strength to dentin showed that means were not reduced after one year of storage in artificial saliva for no restorative systems. The results of cross-sectional microhardness measurements in enamel presented significant statistical difference only at the distance of 50 ?m. However, means of Knoop microhardness measurements were similar for the four restorative systems when compared to the same distances and depths. The same pattern of results was found in dentin, but the means of microhardness measurements showed no significant statistical differences between the distances from the restorations. Fluor cationic concentration analysis detected fluoride releasing by the specimens restored GC Fuji LC II and FL-Bond II/Beautifil II. The results of this in vitro study suggest that the restorative products tested presented bond stability after one year, but showed little ability to inhibit secondary caries around restoration, independently on fluoride releasing or not / Mestrado / Dentística / Mestra em Clínica Odontológica

Orientador: Luís Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-24T07:41:05Z (GMT). No. of bitstreams: 1 Coppini_ErickKamiya_M.pdf: 3349153 bytes, checksum: e0323d6512c30cee2e8ea17128a4c6e6 (MD5) Previous issue date: 2013 / Resumo: The aim of this study was to evaluate the cavosuperficial enamel acid-etching influence in class I cavities, filled with composites on microtensile bond strength, Knoop microhardness and nanoleakage after thermomechanic ageing. It was selected 76 sound molar splitted on: 32 teeth to microtensile test (n=8); 32 teeth to Knoop microhardness (n=8); and 12 teeth (n=3) to nanoleakage analysis. The cavities were prepared on a standard cavity preparation machine. Half of the teeth had the cavosuperficial enamel etched with 35% phosphoric acid and restored with a Silorane restorative system or a Methacrylate restorative system. After the conclusion of the restoration procedures, the teeth were taken to a thermomechanic cycling machine where the artificial ageing was performed with 200.000 mechanical cycles with an 80 N load in a 2HZ frequency and thermocycling by filling the chambers for 30 seconds and 15 seconds drainage with the temperatures varying between 5ºC and 55ºC. The samples were submitted to the microtensile bond strength test, Knoop microhardness and nanoleakage evaluation. To statistical analysis it was performed the ANOVA two-way and Tuckey test (p ? 0,05). The group restored with methacrylate without acid-etching showed the lowest values of microtensile bond strength and it was statistically different to the other groups that have no difference between them. The methacrylate composite presented statistically higher values on Knoop microhardness compared to silorane composite. The nanoleakage analysis showed low infiltration to silorane restorative system and moderate infiltration to the methacrylate restorative system. The methacrylate group restored without enamel acid-etching showed the formation of Water Trees. It can be concluded that the acid-etching improved the bond strength to the methacylate system. The methacrylate composite has bigger Knoop microhardness than silorane composite. The methacrylate restorative system showed moderate infiltration on nanoleakage analysis / Abstract: The aim of this study was to evaluate the cavosuperficial enamel acid-etching influence in class I cavities, filled with composites on microtensile bond strength, Knoop microhardness and nanoleakage after thermomechanic ageing. It was selected 76 sound molar splitted on: 32 teeth to microtensile test (n=8); 32 teeth to Knoop microhardness (n=8); and 12 teeth (n=3) to nanoleakage analysis. The cavities were prepared on a standard cavity preparation machine. Half of the teeth had the cavosuperficial enamel etched with 35% phosphoric acid and restored with a Silorane restorative system or a Methacrylate restorative system. After the conclusion of the restoration procedures, the teeth were taken to a thermomechanic cycling machine where the artificial ageing was performed with 200.000 mechanical cycles with an 80 N load in a 2HZ frequency and thermocycling by filling the chambers for 30 seconds and 15 seconds drainage with the temperatures varying between 5ºC and 55ºC. The samples were submitted to the microtensile bond strength test, Knoop microhardness and nanoleakage evaluation. To statistical analysis it was performed the ANOVA two-way and Tuckey test (p ? 0,05). The group restored with methacrylate without acid-etching showed the lowest values of microtensile bond strength and it was statistically different to the other groups that have no difference between them. The methacrylate composite presented statistically higher values on Knoop microhardness compared to silorane composite. The nanoleakage analysis showed low infiltration to silorane restorative system and moderate infiltration to the methacrylate restorative system. The methacrylate group restored without enamel acid-etching showed the formation of Water Trees. It can be concluded that the acid-etching improved the bond strength to the methacylate system. The methacrylate composite has bigger Knoop microhardness than silorane composite. The methacrylate restorative system showed moderate infiltration on nanoleakage analysis / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientadores: Simonides Consani, Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-28T00:04:36Z (GMT). No. of bitstreams: 1 Dantas_LucasCostadeMedeiros_D.pdf: 1456971 bytes, checksum: 92555fabf5fb3ce889e0f529fd098830 (MD5) Previous issue date: 2015 / Resumo: Diferentes métodos de ensaio para verificação da resistência de união entre materiais odontológicos são descritos na literatura como meios de predizer o comportamento destes materiais em meio oral. Entre os métodos utilizados, os mais mencionados são os de microtração e microcisalhamento. Apesar de amplamente estudados, existe uma grande variação nos protocolos de confecção de espécimes e de ensaio mecânico, dificultando a comparação entre os estudos. O objetivo neste estudo foi avaliar o comportamento da interface de união entre cerâmica odontológica e dois cimentos resinosos sob influência de diferentes ensaios de resistência de união, potências de fotoativação e realização de ciclagem térmica. Utilizando o método de elementos finitos, no capítulo 1, dois modelos, um simulando o ensaio de microcisalhamento e o outro o ensaio de microtração, foram analisados quanto à distribuição de tensões na região de união dos espécimes. Assim, no capítulo 2, o ensaio de microcisalhamento foi utilizado para avaliar a resistência de união entre dois cimentos resinosos e uma cerâmica odontológica variando a potência do aparelho fotoativador, e a simulação de envelhecimento por meio de ciclagem térmica. Por meio de teste in vitro, os ensaios de microtração e microcisalhamento foram utilizados para avaliar a resistência de união entre os mesmos materiais e com os mesmos protocolos de confecção, variando o tipo de cimento resinoso e a potência do foto ativador. O método de elementos finitos revelou a presença de uma tensão uniaxial para o modelo de microtração. Nos ensaios laboratoriais o ensaio de microcisalhamento resultou em maiores valores de resistência de união. O método de envelhecimento de amostras diminuiu a resistência de união. Desta forma, conclui-se que a utilização da baixa potência de fotoativação favoreceu o resultado de resistência de união imediato e que o ensaio de microtração performado neste estudo apresentou tensões melhores distribuídas indicando melhor utilização no ensaio / Abstract: Different test methods to verify the bond strength of dental materials are described in the literature as a means to predict the behaviour of these materials in the oral environment. Among the methods used, the most mentioned are the microtensile and microshear. Although widely studied, there is a large variation in the preparation of specimens and mechanical testing protocols, making it difficult to compare studies. The aim of this study was to evaluate the behaviour of the adhesive interface with two resin cements and curing powers and performing thermal cycling, assessed by two different tests of bond strength. Using the finite element method, in chapter 1, two models were made, one simulating the test microshear and the other microtensile test were analysed for the stress distribution in the adhesive region of the specimens. Thus, microshear test, in chapter 2, was used to evaluate the bond strength of two resin cements and dental ceramics by varying the power of curing unit device and the simulation of ageing by thermal cycling. By the means of in vitro assay tests microtensile and microshear were used to evaluate the bond strength of the same materials and with the same protocols of specimens preparation by varying the type of resin cement and the power of the photoactivator. The finite element analysis revealed the microtensile model a uniaxial stress. In laboratory, microshear results in higher values of bond strength. The ageing method promoted reducing in bond strength values, while the low power of photoactivation increases these values. It may be concluded, that low intensity of photoactivation leads to an immediately higher bond strength and microtensile bond strength test performed in this study showed the stresses distributed in correct axis indicating better use to bond strength evaluation / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Rebeca [Unesp] Di Nicoló / Resumo: O objetivo desse estudo foi avaliar as propriedades de um sistema adesivo modificado com a incorporação de partículas de vidro bioativas (SCHOTT Bioactive Glass) em duas diferentes concentrações (0,5 e 1%). Foram avaliados a resistência de união da interface adesiva, o grau de conversão e a atividade antibacteriana, além da análise por meio do Estereomicroscópio e Microscópio Eletrônico de Varredura (MEV). Os adesivos foram divididos em três grupos: ASB - Adesivo Single Bond 2 (3M-ESPE) sem a incorporação de partículas bioativas, ASB0,5 – Adesivo Single Bond 2 com a incorporação de partículas bioativas na concentração de 0,5% e ASB1 – Adesivo Single Bond 2 com a incorporação de partículas bioativas na concentração de 1%. Para o teste de resistência de união foram utilizados 30 molares humanos hígidos (n=10) que posteriormente foram observados em Estereomicroscópio para análise do padrão da fratura. O grau de conversão foi feito no FTIR, onde foram feitas três leituras das gotas do adesivo dos diferentes grupos. A atividade antibacteriana foi feita através dos testes de difusão em ágar e contagem da unidade formadora de colônia (UFC), onde foram utilizados discos de adesivos polimerizados dos diferentes grupos. Os testes antibacterianos foram repetidos por três vezes. Os dados foram analisados estatisticamente quanto à sua normalidade. Como estes apresentaram distribuição normal, realizou-se o teste de análise de variância (ANOVA) paramétrica um fator (sistema adesivo) e o tes... (Resumo completo, clicar acesso eletrônico abaixo) / Mestre

To develop a project sizing concrete pavement is necessary to know the mechanical properties and the different treatment processes of material to be used. This study aimed to analyze the mechanical properties such as flexural strenght, compressive strength, indirect tensile strength and static modulus of concrete paving. The three types of concrete were studied: An actual reference (typically used in paving, one with the addition of polypropylene fibers (common practice for floors), and a high strength concrete used to rapidly release the traffic. Different methods of curing were applied: chemical cure with and without the use of wet burlap bags (widely applied in pavements) and curing in a moist chamber (as recommended by standard). This evaluation of the mechanical properties for the concrete studied in different curing methods applied, showed that the microstructure of concrete is significantly interfering with the results, especially in cured concrete to track conditions (chemical cure without and with the placement of burlap sacks). Where factors such as the absorption and reabsorption of water evaporation to cement hydration, cracking the interface folder / aggregate, ambient conditions related to temperature and humidity, are interfering with the tensile strength in bending, compressive strength, indirect tensile strength and particularly in the static modulus and still, from the results obtained in this study and those reported by other authors who studied a high-strength concrete, it is possible to verify that there are particularities still unknown about the behavior of high strength concrete. / Para o desenvolvimento de um projeto de dimensionamento de pavimentos de concreto é necessário conhecer as propriedades mecânicas e os diferentes processos de tratamento do material a ser utilizado. Este trabalho teve por objetivo analisar as propriedades mecânicas, tais como, resistência à tração na flexão, resistência à compressão axial, resistência à tração por compressão diametral e módulo de elasticidade estático em concretos para pavimentação. Foram estudados os três tipos de concretos: um concreto referência, (tipicamente empregado em pavimentação, outro com a adição de fibras de polipropileno (prática comum em pavimentos) e um concreto de alta resistência, utilizado para rápida liberação ao tráfego. Diferentes métodos de cura foram aplicados: cura química com e sem a utilização de sacos de aniagem úmidos (largamente aplicados em pavimentos) e cura em câmara úmida (conforme preconizado por norma). A avalição das propriedades mecânicas para os concretos estudados, nos diferentes métodos de cura aplicados, mostrou que a microestrutura dos concretos, está interferindo de forma significativa nos resultados obtidos, principalmente nos concretos curados para condições de pista (cura química sem e com a colocação de sacos de aniagem), onde fatores como a absorção e reabsorção da água de evaporação para hidratação do cimento, a fissuração da interface pasta/agregado, as condições ambientes relacionadas à temperatura e umidade, estejam interferindo na resistência à tração na flexão, resistência à compressão axial, resistência à tração por compressão diametral e principalmente no módulo de elasticidade estático e ainda, a partir dos resultados obtidos na presente pesquisa e daqueles apresentados por outros autores que estudaram um concreto de alta resistência, é possível verificar que existem particularidades ainda desconhecidas sobre o comportamento do concreto de alta resistência.