Made available in DSpace on 2011-12-27T14:14:00Z (GMT). No. of bitstreams: 2 000386791-0.pdf: 7078042 bytes, checksum: 4c1fadb128575046216a3274f924db24 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this study was to compare, in vitro, the shear bond strength values of brackets bonded with LED and convencional halogen (QTH) light curing units with a different exposure times. One hundred and twenty six premolar teeth were equally divided into six groups according to the curing light and exposure times used. As for LED curing light, the specimens were submitted to photoactivation for 5s, 10s end 15s, whereas the exposure times to QTH curing light was 10s, 20s and 30s. The light curing units LED (Ortholux LED Curing Light, 3M-Unitek –EUA) and QTH (XL 3000, 3M Unitek – EUA) were evaluated in the beginning, right before the first bonding, and after ten brackets bonding, using specific radiometers for each light curing, registered irradiance mean values of 581 mW/cm² and 420mW/cm², respectively. The specimens were stored in water at 37°C for 24h and then subjected to a shear force with a universal testing machine, in a gingivoocclusal direction at crosshead speed of 1mm/min. According to ANOVA and Tukey, a significant difference in mean shear bond strength was detected (p<0,01).As for the LED – photoactivaded groups 5s (17,20MPa) and 10s (20,54MPa) shear bond strength values was comparable, showing statistical difference among the LED 15s (25,24MPa) group. Considering the QTH exposures, the 10s (16,97MPa) group registered differences when related to the 20s (23,61MPa) and 30s (21,33MPa), whereas these showed none between them. The LED 15s group demonstrated the higher mean shear bond strength, but showed no statistically significant differences between the QTH 20s and 30s groups. Even the lowest mean bond strength, recorded for QTH 10s and LED 5s groups, respectively, were considered to be clinically acceptable. Kruskal-Wallis analysis of ARI scores indicated that there was statistical difference (p< 0,01) among the studied groups. In LED 15s group the majority of specimens had an ARI score 0, being observed a enamel fracture in two specimens. Instead of the LED 5s and QTH 10s groups demonstrated higher frequencies of ARI score 1 and 2, respectively, in both groups, the score 3 appear frequently (QTH 10s – 10,5%; LED 5s – 9,5%). Opposing behavior was observed in groups LED 10s and 15s, where he was not registered frequency of score 3 (0%). The findings of the present study suggest that technology LED (Free Light Ortholux, 3M - Unitek) can be used, in the brackets bonding, with lesser times of cure in relation halogen light for the resin Transbond XT, being that, the minimum time of 5s with LED presented bond strength values clinically acceptable. / O objetivo do presente estudo foi comparar, in vitro, a resistência de união ao cisalhamento de bráquetes colados quando expostos à luz LED e à luz halógena (QTH) mediante diferentes tempos de exposição. Para isso 126 dentes pré-molares foram divididos em seis grupos de acordo com a fonte de luz e o tempo de exposição utilizado. Para o conjunto LED, foram usados os tempos de 5, 10 e 15s e para o conjunto QTH, 10, 20, e 30s. Os aparelhos fotopolimerizadoes LED (Ortholux LED Curing Light, 3M-Unitek –EUA) e QTH (XL 3000, 3M Unitek – EUA) tiveram suas intensidades avaliadas inicialmente e, a cada 10 colagens, por radiômetros específicos para cada natureza de luz, obtendo valores médios de 581mW/cm² e 420mW/cm², respectivamente. Após 24h de estocagem em água destilada a 37°C, os corpos - de - prova foram levados à máquina de ensaio mecânico (Emic DL 2000®) e submetidos à tensão de cisalhamento, no sentido cérvico-oclusal, à velocidade de 1mm/min. De acordo com os testes estatísticos ANOVA e Tukey, houve diferença significativa entre os grupos estudados (p< 0,01).Os grupos fotoativados por LED 5s (17,20MPa) e 10s (20,54MPa) não diferiram entre si, mostrando diferença estatisticamente significativa quando comparados ao grupo LED 15s (25,24MPa). Quanto à fonte luminosa QTH, o grupo de 10s (16,97MPa) diferiu dos 20s (23,61MPa) e 30s (21,33MPa), enquanto esses não diferiram entre 8 si. A maior média de resistência de união foi observada no grupo LED 15s, embora este grupo não tenha se diferenciado estatisticamente dos grupos QTH 20s e 30s. Verificou-se que até mesmo os grupos que tiveram as menores médias de resistência de união, QTH 10s e LED 5s, respectivamente, apresentaram valores compatíveis com o uso clínico. Segundo o teste Kruskal-Wallis, houve diferença significativa na distribuição dos resultados do IAR entre os grupos (p< 0,01).O grupo LED 15s demonstrou padrão de fratura predominantemente índice 0, sendo observado fratura de esmalte em dois corpos - de - prova. Apesar dos grupos LED 5s e QTH 10s apresentarem maior predomínio de escores 1 e 2, respectivamente, foram nesses que se observou a maior freqüência de escores 3, QTH 10s (10,5%) e LED 5s (9,5%). Comportamento oposto foi observado nos grupos LED 10s e 15s, onde não foi registrado freqüência de índice 3 (0%). Os achados do presente estudo sugerem que a tecnologia LED (Free Light Ortholux, 3M – Unitek) pode ser utilizada, na colagem de bráquetes, com tempos de cura menores em relação á luz halógena para a resina Transbond XT, sendo que, o tempo mínimo de 5s com LED apresentou valor de resistência de união clinicamente aceitável.

Made available in DSpace on 2011-12-27T14:14:03Z (GMT). No. of bitstreams: 2 000389582-0.pdf: 4751378 bytes, checksum: 96556d08ded117c5d6139618402559ab (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This in situ study evaluated the degradation of tissue conditioners as a function of the timespan of clinical use measuring the variables Shore A hardness and quantity of plasticizer phthalate. The three tissue conditioners evaluated were Coe-Comfort, Dura Conditioner, and Softone. The materials were prepared according to each manufacturer’s instructions and inserted into grooves (5x15x2 mm) made in the palatal inner surface of maxillary complete dentures of nine patients at the FO-PUCRS Complete Dentures Clinics. These patients were selected following the inclusion and exclusion criteria and used their dentures during the evaluation period. Data collection was performed at baseline and 3, 7, and 14 days after the insertion of the materials into the dentures grooves. Shore A hardness was recorded by using an analogical Shore A durometer. The quantity of plasticizer phthalate was measured by means of infrared spectroscopy. One specimen of each material was randomly chosen at each test-time for observation of surface topography in scanning electron microscope. Data were analyzed by ANOVA for repeated measures followed by Tukey test, and by simple linear regression, at the 5% significance level.All tested tissue conditioners showed decrease of quantity of phthalate and increase of hardness over time. The overall degradation was similar for all tissue conditioners but the pattern of phthalate lixiviation and of hardness alteration was material-specific. The largest changes of phthalate concentration and Shore A hardness of the tested tissue conditioners occurred in the first three days of clinical use. Comparing baseline and day 3 data, Coe-Comfort showed 25% decrease of initial phthalate concentration, which was statistically different from the other materials with reduction of 50%. No significant alteration of phthalate concentration was detected between days 3 and 7. The quantity of plasticizer in the material is inversely related to the hardness of the tissue conditioner. / Este estudo in situ avaliou a degradação de condicionadores de tecido em função do tempo de uso clínico, mensurando a dureza Shore A e a quantidade do agente plastificante ftalato. Três materiais condicionadores de tecido foram avaliados: Coe-Comfort, Dura Conditioner e Softone. Os três materiais foram manipulados de acordo com as instruções dos fabricantes e inseridos em canaletas (5x15x2 mm) preparadas na região palatal da superfície interna de próteses totais superiores de nove pacientes da Clínica de Prótese Total da FO-PUCRS selecionados de acordo com os critérios de inclusão e exclusão, que permaneceram utilizando suas próteses durante o período de avaliação. As análises foram realizadas no baseline, no terceiro, sétimo e décimo-quarto dias, após a inserção dos condicionadores em boca. As mensurações da dureza foram registradas por meio de um aparelho durômetro Shore A analógico e a quantidade de plastificante foi mensurada por espectrofotometria de infravermelho. Foram selecionadas aleatoriamente espécimes dos três condicionadores de cada intervalo de tempo para análise em microscópio eletrônico de varredura.Os dados foram analisados por ANOVA utilizando o delineamento em medidas repetidas seguida pelo Teste de Comparações Múltiplas de Tukey e por regressão linear simples, ao nível de significância de 5%. Todos os condicionadores de tecido testados apresentaram redução da quantidade de plastificante ftalato e aumento da dureza ao longo do tempo do estudo. O comportamento geral de degradação dos condicionadores de tecido testados foi similar mas o padrão de lixiviação de ftalato e de aumento de dureza foi específico para cada material. As maiores alterações de concentração de ftalato e de dureza Shore A dos condicionadores de tecido estudados ocorreram nos primeiros três dias de uso clínico. Entre o baseline e o dia 3 o Coe- Comfort apresentou redução de aproximadamente 25% da concentração inicial de ftalato, sendo estatisticamente diferente dos demais materiais que apresentaram perda de 50%. Não houve alteração significativa da quantidade de ftalato entre os dias 3 e 7. A quantidade de plastificante no material está inversamente relacionada com a dureza dos condicionadores de tecido.

Made available in DSpace on 2011-12-27T14:14:07Z (GMT). No. of bitstreams: 2 000421649-0.pdf: 1087640 bytes, checksum: faee9bfd7959d4a4a23ff18aca62f774 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This in vitro study evaluated the fracture strength of endodontically treated, weakened root canals, which were restored with either cast metallic or glass fiber-reinforced resin posts (Exacto, Angelus Indústria de Produtos Odontológicos S/A, Londrina, PR, Brazil) and submitted or not to mechanical fatigue. Twenty extracted human teeth with standardized dimensions and no visible structural defects were used. The crowns were cut below the enamel-cement junction to result in 14-16 mm-length roots. The endodontic treatment was performed by using the stepwise technique; the canals were prepared for post insertion with a bur of the glass fiber-reinforced resin post system (# 1. 6 mm-diameter). The roots were weakened by removing intracanal dentin with a tapered diamond bur (4 mm-length) and randomly divided into four groups (n=5/group) according to the type of post (metallic or glass fiber-reinforced resin post) and type of treatment (with or without mechanic cycling). For the metallic posts, the intracanal portion was modeled and cast in Ni-Cr alloy. The resin posts had the crown portion built with nanoparticle composite Z250 (ESPE, 3M) using prefabricated polyesther crowns of standardized shape according to the cast posts. All posts and metallic crowns were cemented with RelyX Unicem. The roots were covered with impression material to simulate the periodontal ligament and embedded in acrylic resin. Two groups were submitted to mechanic cycling with 300,000 cycles, 50 N of load corresponding to a pressure of 1. 13 bars, and frequency of 1 Hz. Specimens were loaded at 45 degrees in a universal testing machine at a crosshead speed of 0. 5 mm/min until failure. The mode of failure was classified as repairable or nonrepairable. The results showed that the metallic posts with no mechanic fatigue had the highest fracture strength (484 N); the resin posts with mechanic cycling showed the lowest values (259. 9 N). The teeth with cast posts had higher strength than the ones with resin posts, but they also showed more nonrepairable failure. Mechanical cycling reduced the fracture strength but did not affect the failure mode. / Este estudo in vitro avaliou a resistência à fratura de raízes enfraquecidas, tratadas endodonticamente, que foram restauradas com pinos metálicos fundidos e pinos de fibra de vidro Exacto (Angelus Indústria de Produtos Odontológicos S/A, Londrina, PR, Brasil) e submetidos à fadiga mecânica. Foram utilizados 20 dentes humanos unirradiculares, extraídos, com dimensões padronizadas e sem defeitos estruturais visíveis. As coroas foram removidas abaixo da junção amelo-cementária, mantendo-se comprimento da raiz entre 14 e 16 mm. O tratamento endodôntico foi realizado pela técnica escalonada; os canais foram desobturados para o preparo intra-radicular padronizado com a broca do sistema de pino de fibra de vidro Exacto (no 1,6 mm de diâmetro). O enfraquecimento radicular foi realizado com remoção de dentina dos condutos com uma broca diamantada tronco-cônica (4 mm de comprimento). As raízes foram aleatoriamente divididas em quatro grupos (n=5/grupo) conforme o tipo de pino (metálico ou pino de fibra de vidro) e o tipo de tratamento realizado (com ciclagem mecânica ou sem ciclagem mecânica). Para os pinos metálicos, a região intra-radicular foi modelada e fundida em peça única em liga de níquel-cromo. Os pinos de fibra de vidro receberam complemento coronário confeccionado com resina nanoparticulada Z250 (ESPE, 3M) com o uso de coroas de poliéster pré-fabricadas com a forma padronizada pelos núcleos fundidos. Todos os pinos e coroas totais metálicas foram cimentadas com o cimento RelyX Unicem. As raízes foram revestidas com uma camada de poliéter simulando o ligamento periodontal e foram embutidas em resina acrílica autopolimerizável. Dois grupos foram submetidos à ciclagem mecânica no Simulador de Fadiga Mecânica ERIOS, modelo ER – 11000, com protocolo de 300. 000 ciclos, carga de 50 N correspondente a pressão de trabalho de 1,13 bars e frequência de 1 Hz.O ensaio mecânico para registro dos valores de resistência à fratura foi realizado com a aplicação de uma carga compressiva a 450 com a face palatina dos corpos-de-prova em máquina de ensaio universal à velocidade de 0,5 mm/min até que houvesse algum tipo de ruptura. O tipo de falha após o ensaio foi classificado como reparável ou irreparável. Os dados de força máxima de ruptura (N) obtidos foram preliminarmente analisados pelos testes de Lilliefors (D) e Shapiro-Wilk (W) quanto à normalidade de sua distribuição para aplicação de testes estatísticos paramétricos. Posteriormente, foram analisados pelo teste ANOVA de acordo com o delineamento de experimento em blocos casualizados com repetições, ao nível de significância de 0,05. Os resultados mostraram que pinos metálicos sem ciclagem mecânica tiveram a maior resistência à fratura (484 N); os pinos de fibra de vidro submetidos à ciclagem mecânica mostraram os menores valores (259,9 N). Os pinos metálicos fundidos apresentaram maiores valores de resistência à fratura que os pinos de fibra de vidro; entretanto, apresentaram maior número de falhas irreparáveis. A ciclagem mecânica reduziu a força máxima de ruptura, mas não afetou o tipo de falha.

Made available in DSpace on 2011-12-27T14:14:12Z (GMT). No. of bitstreams: 2 000347433-0.pdf: 2385324 bytes, checksum: b30cdf7cb8df14803e76ba57e57535bb (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The purpose of this study was to assess the effect of a horizontally transfixed fiber glass post on the fracture resistance of molar teeth endodontically treated with MOD preparations, restored or not with composite resin. Seventy-five sound human third molars were extracted and mounted on acrylic resin blocks and were randomly assigned to five groups (n=15). In Group A, the teeth remained sound (control). Groups B, C, D and E, treated endodontically, were subjected to the following procedures: Group B – MOD preparation, group C – MOD preparation and transfixed post, group C – MOD preparation and resin composite restoration, group E – MOD preparation, transfixed post, and composite resin. The samples were stored in physiological serum at 37ºC for 24 hours. Later, a compressive force was applied parallely to the long axis of the teeth to fracture, performed by means of a universal testing machine (EMIC DL-2000) at 1 mm/min speed. The means in Newtons (N) of the results (standard deviation) followed by the same letter did not show a statistic difference for ANOVA and Tukey, p=0. 05: Group A = 4289. 8 (± 1128. 9)a, Group B = 549. 6 (± 120. 7)b, Group C = 1474. 8 (± 338. 1)c, Group D = 1224. 7 (± 236. 0)c, Group E = 2645. 4 (± 675. 1)d. In the analysis of qualitative variables, cusp fracture prevailed in 56%, a recoverable diagnosis was found in all groups, except for Group C, and the palatal cusp preparation prevailed in all Groups, except for Group A. It was concluded that a fiber glass post transfixed horizontally to the walls of a MOD cavity significantly increased fracture resistance, and when associated to the composite resin restoration, it established a fracture pattern compatible with the recovery of the dental specimen. / A proposta deste estudo foi avaliar o efeito, na resistência à fratura, de um pino de fibra de vidro transfixando horizontalmente as paredes, de um preparo MOD, de dentes molares tratados endodonticamente restaurados ou não com resina composta. Setenta e cinco dentes terceiros molares humanos hígidos foram extraídos e montados em blocos de resina acrílica, sendo distribuídos aleatoriamente em cinco grupos (n=15). No Grupo A, os dentes foram mantidos hígidos (controle). Os Grupos B, C, D e E, com tratamento endodôntico, receberam os seguintes procedimentos: Grupo B – preparo MOD; Grupo C – preparo MOD e pino transfixado; Grupo D – preparo MOD e restauração com resina composta; Grupo E – preparo MOD, pino transfixado e restauração com resina composta. As amostras foram armazenadas em soro fisiológico a 37ºC durante 24 horas. Após o procedimento, foi aplicada uma força compressiva paralela ao longo eixo dos dentes até a fratura, conduzida por meio de uma máquina de ensaio universal (EMIC DL-2000) com velocidade de 1mm/min. As médias em Newtons dos resultados (desvio padrão) seguidas de mesma letra não apresentaram diferença estatística para ANOVA e Tukey, p=0,05: Grupo A = 4289,8 (± 1128,9)a, Grupo B = 549,6 (±120,7)b, Grupo C = 1474,8 (± 338,1)c, Grupo D = 1224,7 (± 236,0)c, Grupo E = 2645,4 (±675,1)d. Na análise das variáveis qualitativas, predominou a fratura de cúspide em 56%, o diagnóstico recuperável em todos os grupos, com exceção do Grupo C e o preparo da cúspide palatina predominou em todos os grupos, a exceção do Grupo A. Concluiu-se que um pino de fibra de vidro transfixando horizontalmente as paredes de uma cavidade MOD elevou significativamente a resistência à fratura e quando associado à restauração de resina composta determinou um padrão de fratura compatível com a recuperação da peça dentária.

Made available in DSpace on 2011-12-27T14:14:13Z (GMT). No. of bitstreams: 2 000411472-0.pdf: 3421246 bytes, checksum: 2de63642b6d6b46a8c8709c79bb57f6a (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Article 1 - Aims: To compare the surface roughness of four resin composites with different organic matrix compositions applying the abrasion testing by tooth brushing until 20,000 cycles. Methods and materials: One hundred and sixty samples were buildup and divided into 16 groups (n=10) according to the type of composite resin, source of light and energy density. The resin composites used were Charisma, Z250, ROK and Filtek LS, being photo activated with LED or halogen unit, receiving 8 or 16 J/cm2. After 24h, the samples were submitted to a simulated wear test with a dentifrice and a soft toothbrush by periods of 6 months (5000 cycles), 12 months (10. 000 cycles) e 24 months (20. 000 cycles). After each period was realized the surface roughness measurement. Results: The factors as energy density (p=0. 0001), source of light (p=0. 0047), resin composites (p=0. 0001) and cycles (p=0. 0001) influenced the results. The mean roughness values obtained were (means followed by the same letter are not significantly different according to Tukey (α=5%)): 0. 07μm (A) - ROK; 0. 08μm (B) - Z250; 0. 12μm (C) - Charisma; 0,17μm (D) - Filtek LS. Conclusion: The UDMA-based resin composites present higher surface abrasion resistance. The silorane-based composites present lower surface abrasion resistance. The resin composites photo activated by 16J/cm2 present lower roughness than composites cured by 8J/cm2.Article 2 - Aim: To evaluate the surface roughness of two resin composites with different organic phase when submitted to a simulated wear test with tooth brushing and whitening dentifrices. Materials and methods: Forty-eight samples were built and divided into 6 groups (n=8) according to composite resin (ROK (SDI) or Z250 (3MESPE) and dentifrice used (Colgate Total 12, Colgate Max White or Close up Extra Whitening). The resins were submitted to cycles of simulated tooth brushing until 24 months. After each simulated period, the surface roughness of the resins was measured. Results: The surface roughness(Ra) average, in μm, to the Colgate total 12 (control), Colgate Max White and Close up Extra Whitening dentifrices were, respectively (means followed by the same letter are not statistically different to ANOVA and Tukey (p<0,05)): 1) ROK: 0. 09(B), 0. 12(B) and 0. 11(B); 2) Z250: 0. 09(B), 0. 21(A) and 0. 21(A). Conclusions: The ROK composite resin presented lower surface roughness (0. 11) than Z250 (0. 17). The resin composites ROK and Z250 have its abrasion resistance decreased when the whitening dentifrices Colgate Max-White and Close Up Extra-Whitening are applied. / Artigo 1 - Objetivo: Comparar a rugosidade de superfície de quatro resinas compostas com diferentes composições de matriz orgânica, através do ensaio de abrasão por escovação simulada até 20. 000 ciclos. Materiais e Métodos: Cento e sessenta corpos de prova foram confeccionados e divididos em 16 grupos (n=10) conforme o tipo de resina, fonte de luz e quantidade de energia. As resinas utilizadas foram Charisma, Z250, ROK e Filtek LS, sendo fotopolimerizadas com LED ou Luz halógena, recebendo 8 ou 16 J/cm². Após 24 horas, os corpos de prova foram submetidos à escovação simulada com dentifrício e escova macia por períodos de tempo equivalentes à 6 meses (5000 ciclos), 12 meses (10. 000 ciclos) e 24 meses (20. 000 ciclos). Após cada período foi realizada a medição da rugosidade de superfície. Resultados: Fatores como energia (p=0,0001), tipo de fonte (p=0,0047), resinas (p=0,0001) e ciclo (p=0,0001) influenciaram nos resultados obtidos. Os valores de rugosidade média obtidos foram (médias seguidas de mesma letra não apresentam diferença estística para Tukey (α=5%): 0,07μm (A) para ROK; 0,08µm (B) para Z250; 0,12μm (C) para Charisma e 0,17μm (D) para filtek LS. Conclusão: as resinas compostas que contém UDMA apresentam maior resistência à abrasão de superfície; resinas baseadas em Siloranos apresentam a menor resistência ao desgaste por abrasão e resinas compostas fotoativadas com 16J/cm² apresentam menor rugosidade de superfície do que as polimerizadas com 8J/cm².Artigo 2 - Objetivos: O objetivo deste estudo foi comparar a rugosidade de superfície de duas resinas compostas, com diferentes composições orgânicas, quando submetidas ao ensaio de abrasão por escovação com dentifrícios clareadores. Materiais e métodos: Quarenta e oito corpos-de-prova foram confeccionados, divididos em 6 grupos (n=8) conforme tipo de resina e dentifrício utilizado. As resinas foram submetidas a ciclos de escovação os quais simularam até 24 meses. Após cada período simulado, as resinas compostas tiveram a rugosidade de superfície mensurada. Resultados: as médias finais de rugosidade de superfície (Ra), em μm, para os dentifrícios Colgate total 12 (controle), Colgate Max White e Close up Extra Whitening foram, respectivamente (médias seguidas de mesma letra não apresentam diferença estatística significante para ANOVA e Tukey (p<0,05)): 0,09 (B), 0,12 (B) e 0,11 (B) para a resina ROK; e 0,09 (B), 0,21 (A) e 0,21(A) para Z250. Conclusões: A resina composta ROK apresentou menor rugosidade de superfície do que a resina Z250. As resinas compostas ROK e Z250 tem a sua resistência ao desgaste superficial diminuída com o uso de dentifrícios mais abrasivos e utilizados para clareamento dos dentes: Colgate Max-White e Close Up Extra-Whitening.

Made available in DSpace on 2011-12-27T14:14:13Z (GMT). No. of bitstreams: 2 000387554-0.pdf: 6424305 bytes, checksum: eede53bc1323d5be8d0e3d939fde81ca (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Seventeen extracted healthy third molars were used in order to evaluate dentine as to: microtensile bond strength (μTBS) with Z250 resin composite (CR), and 3M Single Bond 2 adhesive; appearance previous to adhesive treatment (APTA); adhesive union (UA); type of fracture by Scanning Electron Microscope (SEM), and energy dispersion spectroscopy (EDS), comparing the treatment with a KGSorensen diamond bur (PD) and a CVDentus (UT) ultrasound tips with (c/a) and without (s/a) etching. Four groups (n=40) were divided according to the dentin processing (PDs/a - diamond bur without etching); (PDc/a - diamond bur with etching); (UTs/a - ultrasound tip without etching); (UTc/a - ultrasound tip with etching) were restored, embedded in politetrafluoretilene tube using chemically activated acrylic resin, and sectioned into samples for μTBS testing in an EMIC DL-2000 universal machine (0. 5 mm/min). Samples were analyzed by SEM and EDS for fracture classification UA and APTA. Statistical tests were: Kolmogorov- Smirnov Test; Two way Variance Analysis; Tukey and Fisher's Exact Test (p≤0,05). Failures were classified as: cohesive in dentine (CD); cohesive in CR (CM); cohesive interfacial on the base or top of hybrid layer (CBT); adhesive cohesive interfacial (CA); mixed (M); interfacial on smear layer (S). Results showed (group, average μTBS in MPa - standard deviation): (UTc/a, 45. 31-8. 16); (PDc/a, 34. 04-9. 29); (UTs/a, 15. 17-3. 71); (PDs/a, 9. 86-3. 80).The PD method is associated to CBT, and the UT method is associated to CA and CM; c/a is associated to CBT and CM, and s/a is associated to S. APTA showed: PDs/a - total obstruction of dentinal tubules (cd); UTs/a - partial disobstruction of cd and irregular surface appearance; PDc/a - complete disobstruction of cd; UTc/a - complete disobstruction of cd, and irregular surface appearance. UA showed: PDs/a rectilinear hybrid layer occurred without tags penetration (PT); UTs/a, curvilinear with a few PT; PDc/a, rectilinear with PT; UTc/a, curvilinear with PT. It was concluded that the association of UTc/a treatment promotes higher values of μTBS. There is an association between CBT failure and the PD method, failures CA and CM and the UT method, failures CBT and CM and the c/a method, and failure S and the s/a method. The failures that caused higher resistance to its rupture were, in a decreasing order: CD; CM; CBT; CA; M, and S. / Dezessete terceiros molares hígidos extraídos foram utilizados com objetivo de avaliar a dentina quanto: resistência à união por microtração (μTBS) com resina composta (CR) Z250 e adesivo Single Bond 2 (3M); aspecto prévio ao tratamento adesivo (APTA); união adesiva (UA); tipo de fratura por microscopia eletrônica de varredura (MEV) e espectroscopia por dispersão de energia (EDS) comparando o tratamento com ponta diamantada KGSorensen (PD) e haste ultra-sônica CVDentUS (UT) com (c/a) ou sem (s/a) condicionamento ácido. Quatro grupos (n=40) divididos conforme processamento dentinário (PDs/a; PDc/a; UTs/a; UTc/a) foram restaurados, incluídos em resina acrílica autopolimerizável e transformados em pequenas barras por máquina de corte seriado para posterior ensaio de μTBS em máquina universal EMIC DL-2000 (0,5 mm/min). As amostras foram analisadas por MEV e EDS para classificação de fratura, UA e APTA. Os testes estatísticos foram: Kolmogorov-Smirnov; Análise de Variância fatorial; Tukey e Exato de Fisher (p≤0,05). As falhas foram classificadas em: Coesiva em dentina (CD); coesiva em CR (CM); interfacial coesiva na base ou topo de camada híbrida (CBT); interfacial coesiva adesiva (CA); mista (M); interfacial no smear layer (S). Os resultados mostraram (grupo, média μTBS em MPa - desvio padrão): (UTc/a, 45,31-8,16); (PDc/a, 34,04-9,29); (UTs/a, 15,17-3,71); (PDs/a, 9,86-3,80). O método PD está associado à CBT e o método UT às CA e CM, c/a está associado às CBT e CM e s/a à S. O APTA mostrou: PDs/a total obstrução dos canalículos dentinários (cd); UTs/a parcial desobstrução dos cd e aspecto irregular de superfície; PDc/a completa desobstrução dos cd; UTc/a completa desobstrução dos cd e aspecto irregular de superfície. Em PDs/a ocorreu camada híbrida retilínea sem penetrações de tags (PT); UTs/a, curvilínea com algumas PT; PDc/a, retilínea com PT; UTc/a, curvilínea com PT. Concluiu-se que a associação do tratamento UTc/a promove valores maiores de μTBS. Existe associação entre falha CBT com o método PD, falhas CA e CM com o método UT, falhas CBT e CM com o método c/a e falha S com o método s/a. As falhas que ofereceram maior resistência para seu rompimento são, em ordem decrescente: CD; CM; CBT; CA; M; S.

Made available in DSpace on 2011-12-27T14:14:18Z (GMT). No. of bitstreams: 2 000385863-0.pdf: 11730392 bytes, checksum: be18f24f5772871dae60f25e74a3ef0b (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / This study evaluated the influence of different surface treatments to dentin with pre-cured adhesive layer when the immediate dentin sealing technique (IDS) was applied in different storage time with provisional cement on microtensile bond strength of two adhesive systems, classified the failure pattern and measured the adhesive layer thickness. The dentin bonding agent (DBS) Single Bond 2 (SB2) (3M ESPE) e Prime&Bond NT (PB) (Dentsply) were tested in two storage times: 48 hours (A) and 4 months (B). Freshly prepared flat dentin surfaces of extracted human molars were coated with the adhesive systems according to the surface treatments groups: G1) aluminum-oxide - SB2; G2) 37% phosphoric acid - SB2; G3) oxide+acid - SB2; G4) aluminum-oxide - PB; G5) 37% phosphoric acid - PB; G6) oxide+acid - PB; G7) control - SB2; G8) control - PB. After curing the DBA, the provisional cement RelyXTemp NE (3M ESPE) was applied to the bonded dentin surface of the groups 1, 2, 3, 4, 5 and 6, and the teeth were stored for 48 hour or 4 months. After the storage, provisional cement layer was scaled off and the different surface treatments were applied followed by a second DBS layer. The control groups (7 and 8) didn’t received the provisional cement neither the second DBS layer, however were stored for the same times.The composite crown restoration was built with direct resin and, after 24h, the prepared teeth were serially sectioned in sticks. The specimens (n=20 per group) were submitted to microtensile strength test using the universal testing machine EMIC DL-2000. The average values (MPa) were (means followed by different letters are statistically different to General Linear Model and Turkey’s test (p<0,05)): G1A - 23,79±5,92(AB); G1B - 23,93±5,49(AB); G2A - 28,47±6,57(B); G2B - 27,84±3,31(B); G3A - 44,84±10,49(C); G3B - 44,37±9,07(C); G4A - 19,14±4,76(A); G4B - 18,51±4,64(A); G5A - 30,60±5,48(B); G5B - 28,30± 3,95(B); G6A - 47,22±10,11(C); G6B - 46,02±10,33(C); G7A - 41,57±6,91(C); G7B - 41,21±9,32(C); G8A - 40,17±10,35(C) e G8B - 41,04±11,21(C). The fractures specimens were analyzed by SEM and the mixed failure was predominant (92%) followed by interfacial failure (21%). The adhesive thickness range in increasing order: G8< G7< G4< G1< G6< G3< G5< G2. These results suggested that: the surface treatment with aluminum-oxide + 37% phosphoric acid provided the highest bond strength values, however the storage times and the DBS didn’t affect these values; the mixed failure was predominant followed by interfacial failure; and the surface treatments affected significantly the bonding layer thickness for both tested DBS. / Este estudo avaliou a influência de diferentes tratamentos de superfície na dentina pré-hibridizada com a técnica do selamento dentinário imediato (SDI) e armazenada por diferentes períodos na resistência de união à microtração de dois sistemas adesivos. Os agentes de união dentinária (AUD) utilizados, Single Bond 2 (SB2) (3M ESPE) e Prime&Bond NT (PB) (Dentsply), foram testados em dois períodos de armazenagem: 48 horas (A) e 4 meses (B). Superfícies planas de dentina foram preparadas em molares humanos extraídos e foram cobertas com o sistema adesivo de acordo com o tratamento de superfície de cada grupo: G1) óxido de alumínio - SB2; G2) ácido fosfórico 37% - SB2; G3) óxido+ácido - SB2; G4) óxido de alumínio - PB; G5) ácido fosfórico 37% - PB; G6) óxido+ácido - PB; G7) controle - SB2; G8) controle - PB. Após a polimerização do sistema adesivo o cimento provisório RelyXTemp NE (3M ESPE) foi aplicado sobre as superficies dentinárias previamente tratadas com adesivo dos grupos 1, 2, 3, 4, 5 e 6 e estes foram armazenados por 48 horas ou 4 meses. Após o período de armazenagem a camada de cimento provisório foi removida e os diferentes tratamentos de superfície foram empregados seguidos de uma segunda camada de AUD. Os grupos controle (7 e 8) não receberam o cimento provisório nem a segunda camada adesiva, sendo no entanto armazenados pelos mesmos períodos de tempo. Coroas de resina composta direta foram construídas e, após 24h, os dentes preparados foram seccionados em palitos. As amostras (n=20 por grupo) foram submetidas ao teste de resistência de união à microtração na máquina de ensaios universal EMIC DL-2000.Os valores médios (MPa) foram (médias seguidas de letras diferentes são estatisticamente diferentes para Modelo Linear Geral e teste de Tukey (p<0,05)): G1A - 23,79±5,92(AB); G1B - 23,93±5,49(AB); G2A - 28,47±6,57(B); G2B - 27,84±3,31(B); G3A - 44,84±10,49(C); G3B -44,37±9,07(C); G4A - 19,14±4,76(A); G4B - 18,51±4,64(A); G5A - 30,60±5,48(B); G5B - 28,30± 3,95(B); G6A - 47,22±10,11(C); G6B - 46,02±10,33(C); G7A - 41,57±6,91(C); G7B - 41,21±9,32(C); G8A - 40,17±10,35(C) e G8B - 41,04±11,21(C). O tipo de fratura foi analisado através de MEV e a falha do tipo mista foi predominante (92%) seguida da falha interfacial (21%). A espessura de adesivo variou em ordem crescente nos grupos: G8< G7< G4< G1< G6< G3< G5< G2. Os resultados sugerem que: o tratamento de superfície com óxido de alumínio + ácido fosfórico 37% proporcionou os maiores valores de resistência de união, no entanto o tempo de armazenagem e o AUD utilizado não afetaram estes valores; a falha mista foi predominante seguida da falha interfacial; e os tratamentos de superfície utilizados afetaram significativamente a espessura da camada adesiva para ambos os AUD testados.

Made available in DSpace on 2011-12-27T14:14:19Z (GMT). No. of bitstreams: 2 000425713-0.pdf: 1781396 bytes, checksum: 7eeb594432bb477d3935d002b3c3bfbb (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this in vitro study was to evaluate the bond strength interface between the veneering and core zirconia ceramic of a system metal free compared to metal-ceramic system. For this, 40 blocks were made of zirconia (Procera Zirconia), where 32 without color and 8 color have A2) and 8 blocks of metal (alloy Viron 99), all the dimensions (10 x 10 x 2 mm). Samples of zirconia were divided into 5 groups (8 each), and received different preparations: Group 1 (zirconia without color): application of the dentin; Group 2 (zirconia A2 color): application of the dentin; Group 3 (zirconia without color): application of liner + dentin; Group 4 (zirconia without color): application of dentin + liner on the inner surface; Group 5 (zirconia without color): wear diamond drill + liner + dentin. As a control group: metal-ceramic (IPS Dsign Viron 99 + dentin A2). After sintering of ceramics according to the manufacturer, the samples were subjected to analysis of shear strength tests performed on machine EMIC DL 2000, where results were obtained in MPa. Through photographs and SEM with magnitude of 37X, 200X and 2000X as the type of failure that occurred at the interface core and veneering ceramic. When submitting the results to the ANOVA, it was possible to observe that there were statistically significant differences between groups (p=0,000). According to Tukey's test, the control group had the highest values of tensile bond strength, statistically different (P<0. 05) than other groups of zirconia. The groups of zirconia showed no statistical difference between them (p>0. 05). Group 2 had the highest average among the zirconia and group 4 had the lowest average of all groups. The flaws found in the joint interface were 100% in all samples and only 1 sample of group 2 it was cohesive failures in the core of zirconia. It was concluded that the control group showed a tensile bond strength approximately 50% higher than all groups of zirconia tested. / O objetivo deste estudo in vitro foi avaliar a resistência de união entre infraestrutura de zircônia e cerâmica de cobertura de um sistema livre de metal comparado com um sistema metalo-cerâmico. Para isso, foram confeccionados 40 blocos de zircônia (Procera Zirconia), onde 32 não possuíam cor e 8 possuíam cor A2) e 8 blocos metálicos (liga Viron 99), todos nas dimensões (10 x 10 x 2 mm). As amostras de zircônia foram divididas em 5 grupos (8 em cada), e receberam diferentes tratamentos: Grupo 1 (zircônia s/ cor): aplicação da dentina; Grupo 2 (zircônia c/ cor): aplicação da dentina; Grupo 3 (zircônia s/ cor): aplicação do liner + dentina; Grupo 4 (zircônia s/ cor): aplicação do liner + dentina na superfície interna; Grupo 5 (zircônia s/ cor): desgaste com broca diamantada + liner + dentina. Como Grupo Controle: metalo-cerâmica (viron 99 + IPS Dsign dentina A2). Após sinterização das cerâmicas de acordo com o fabricante, as amostras foram submetidas ao teste de resistência ao cisalhamento realizados em máquina de ensaios EMIC DL 2000, onde os resultados foram obtidos em MPa. Através de fotografias e de MEV com magnitude de 37X, 200X e 2000X foi verificado o tipo de falha que ocorreu na interface infra-estrutura e cerâmica de cobertura. Ao submeter os resultados ao teste ANOVA, foi possível observar que houve diferenças estatisticamente significantes entre os grupos (p=0,000). De acordo com teste de Tukey, o grupo controle obteve os maiores valores de resistência de união, estatisticamente diferente (p<0,05) aos demais grupos de zircônia. Os grupos de zircônia não apresentaram diferença estatística entre si (p>0,05). O grupo 2 apresentou a maior média entre os grupos de zircônia e o grupo 4 apresentou a menor média de todos os grupos testados. As falhas encontradas na interface foram 100% mistas em todas amostras e apenas 1 amostra do grupo 2 constatou-se falhas coesivas na infra-estrutura de zircônia. Concluiu-se que o grupo controle mostrou uma resistência de união aproximadamente 50% maior que todos os grupos de zircônia testados.

Made available in DSpace on 2011-12-27T14:14:20Z (GMT). No. of bitstreams: 2 000427785-0.pdf: 701572 bytes, checksum: 6d68289fb0a8c4a345e9c231cfaa8675 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Objective: Firstly, to evaluate correlation between load and dwell time in composite resin microhardness tests, using Vickers and Knoop mechanic test methods. Secondly, to correlate time and load on Knoop microhardness test over a composite resin, and to show, with the obtained results, whether composite resin conversion degree comparison is possible through the tests. Materials and Methods: Resin Grandio (Voco, Cuxhaven, Germany), shade A2, was used to make the samples. Ninety (90) samples were made on a six-(6)-mm-diameter by three-(3)-mm-deep polytetrafluorethylene matrix, where two equidistant increments were each photocured for 20s by the LED device (Celalux, Voco, Cuxhaven, Germany, with 800 mW/cm2). The samples were randomly divided into three groups according to the load factor. Groups I, II and III received loads at 50g, 100g and 500g respectively. These groups were divided into nine subgroups according to the deal time (15s, 30s, 45s). Each sample received indentations from a Shimadzu HMV tester (Shimadzu, Kyoto, Japan). The results were submitted to a two-way ANOVA with fixed factors (load and dwell time), and to the post-hoc Tukey multiple comparison test at α = 0. 05.Results: Significant differences were recorded between groups for each methodology, Vickers and Knoop (p<0. 001). Among the Vickers (VHN) tested samples, the average recorded ranged from 164. 94 (50g for 45s) to 210. 33 (100g for 45s). Knoop microhardness (KHN) ranged from 128. 92 (500g 45s) to 184. 26 (100g 15s). For both methodologies, both load and dwell time were statistically significant (p<0. 001), this way showing that different loads and dwell time influence the microhardness of resins. Conclusion: Firstly, this study demonstrated that correlating both Vickers and Knoop microhardness test results is not recommended, and similar protocols must be applied to allow comparisons among the different studies that use the same kind of test. Secondly, this study demonstrated that Knoop microhardness test results is not recommended for composite resin conversion degree comparisons, and similar protocols should be applied to allow this kind of correlation. / OBJETIVO: Primeiramente, avaliar, em uma resina composta, a correlação existente, em testes de microdureza, entre os fatores carga e tempo de aplicação, utilizando-se os métodos de ensaio mecânico Vickers e Knoop. Em segundo lugar, avaliar, em uma resina composta, os fatores carga e tempo de aplicação no teste de microdureza Knoop, e mostrar, com os resultados obtidos, quando é possível, através dos testes, fazer uma comparação com o grau de conversão da resina composta. MATERIAIS E MÉTODOS: Resina Grandio (Voco, Cuxhaven, Alemanha), cor A2, foi utilizada para confeccionar as amostras. Noventa (90) amostras foram feitas em uma matriz de politetrafluoretileno com seis (6) mm de diâmetro por três (3) mm de profundidade, onde dois incrementos equidistantes foram fotopolimerizados por 20s cada um através de um dispositivo LED (Celalux, Voco, Cuxhaven, Alemanha, com 800 mW/cm2). As amostras foram divididas aleatoriamente em três grupos de acordo com o fator carga. Os grupos I, II e III receberam cargas de 50g, 100g e 500g, respectivamente. Estes grupos foram divididos em nove subgrupos de acordo com o fator tempo de aplicação (15s, 30s, 45s). Cada amostra recebeu edentações de um dispositivo Shimadzu HMV tester (Shimadzu, Kioto, Japão). Os resultados foram analisados estatisticamente através de ANOVA com fatores fixos (carga e tempo de aplicação), e ao teste de comparações múltiplas de Tukey (α = 0. 05).RESULTADOS: Diferenças significativas foram encontradas entre os grupos para cada metodologia, Vickers e Knoop (p<0. 001). Entre as amostras testadas com a metodologia Vickers (VHN), a média encontrada variou de 164. 94 (50g 45s) até 210. 33 (100g 45s). Os valores de microdureza para a metodologia Knoop (KHN) variaram de 128. 92 (500g 45s) até 184. 26 (100g 15s). Para ambas as metodologias, tanto o fator tempo e o fator tempo de aplicação foram estatisticamente significantes (p<0. 001), isto mostra que diferentes cargas e tempos de aplicação influenciam na microdureza das resinas. CONCLUSÃO: Primeiramente, este estudo demonstrou que correlacionar os resultados de testes de microdureza Vickers and Knoop não é recomendado, e protocolos similares devem ser aplicados a fim de permitir comparações entre diferentes estudos que utilizam o mesmo tipo de teste. Em Segundo lugar, este estudo demonstrou que os resultados de microdureza Knoop não são recomendados para comparações com o grau de conversão das resinas compostas, e protocolos similares devem ser aplicados a fim de permitir este tipo de correlação.

Made available in DSpace on 2011-12-27T14:14:20Z (GMT). No. of bitstreams: 2 000425443-0.pdf: 137763 bytes, checksum: 07c751d4d7073c523bf8aaedf5f3b302 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Aims: to evaluate the bond strength of fibre-posts luted with two kind of resin cements to dentin of the root canal treated or not with Nd:YAG laser associated to phosphoric acid. Materials and methods: Sixty one-root teeth with similar morphology and length were submitted to the endodontic treatment with manual instrumentation. After, it were divided into six groups according to the luting protocol of the fibre post (n=10): G1 –RelyX Unicem; G2 – Nd:YAG laser + self-etching luting cement RelyX Unicem; G3 – 37% phosphoric acid gel (AG37%) + RelyX ARC; G4 – Nd:YAG laser + AG37% + RelyX ARC; G5 – etching with the Experimental Solution (ES): Patent number BRPI0903355-6) + RelyX ARC; e G6 – Nd:YAG laser + SS solution + RelyX ARC. The Nd:YAG laser were irradiated with the following protocol: 1064 nm, 60 mJ, 15 Hz and 47. 77 mJ/cm2, 1 min. Afterwards, the teeth with the luted fibre posts were stored in distilled water at 37ºC for 1 week. Next, the roots were sectioned in thirds – cervical, medial and apical – being the slices submitted to the push-out bond strength test. Results: the SS solution group associated to RelyX ARC presented together with the Nd:YAG laser associated to the RelyX Unicem the higher bond strength considering all thirds. Notwithstanding, the phosphoric acid gel associated to the RelyX ARC presented the lower bond strength together with the Relyx Unicem control group. Conclusion: The use of the ES solution increased significantly the bond strength of the RelyX Arc to dentin of the root canal. / Objetivos: Avaliar a resistência de união de pinos de fibra de vidro cimentados à dentina radicular tratada com laser de Nd:YAG, ácido fosfórico gel a 37% ou com uma solução experimental (PATENTE solicitada ao INPI nº PI0903355-6), utilizando dois tipos de cimentos resinosos. Materiais e métodos: Sessenta dentes unirradiculares com morfologia e comprimentos semelhantes foram submetidos ao tratamento endodôntico tradicional ou com laser de Nd:YAG, com instrumentação manual. Após, os dentes foram divididos em seis grupos de acordo com o protocolo de cimentação do pino de fibra de vidro (n=10): G1 –RelyX Unicem; G2 –laser Nd:YAG + RelyX Unicem; G3 –ácido fosfórico gel a 37% (AG37%) + RelyX ARC; G4 –laser Nd:YAG + AG37% + RelyX ARC; G5 – condicionamento com solução experimental (PATENTE solicitada ao INPI nº PI0903355- 6) + RelyX ARC; e G6 – laser Nd:YAG + solução experimental (PATENTE solicitada ao INPI nº PI0903355-6) + RelyX ARC. O laser de Nd:YAG foi irradiado com o seguinte protocolo: 1064 nm, 60 mJ, 15 Hz, 47,77 mJ/cm2 durante 1 min. Os dentes com os pinos cimentados foram armazenados em água destilada a 37ºC por 7 dias. Após esse período, as raízes foram seccionadas em terços cervical, médio e apical, sendo as fatias submetidas ao ensaio de resistência de união por push-out. Ainda, seis dentes foram submetidos aos tratamentos de superfície e levados à microscopia eletrônica de varredura e análise EDS. Resultados: o grupo da solução experimental (PATENTE solicitada ao INPI nº PI0903355- 6) associada ao cimento resinoso RelyX ARC apresentou juntamente com o grupo do laser 4 de Nd:YAG associado ao cimento RelyX Unicem a maior resistência de união considerando todos os terços radiculares. Por sua vez, o ácido fosfórico gel associado ao cimento RelyX ARC apresentou a menor resistência de união juntamente com o grupo do RelyX Unicem. Conclusão: O uso da solução experimental (PATENTE solicitada ao INPI nº PI0903355-6) aumentou significativamente a resistência de união do cimento resinoso RelyX ARC à superfície dentinária do conduto radicular, assim como a irradiação por laser, de uma maneira geral, também aumentou a resistência de união particularmente nos grupos G2 e G4.