Spelling suggestions: "subject:"robocasting"" "subject:"robocastingu""
1 |
Three-dimensional plotted hydroxyapatite scaffolds with predefined architecture: comparison of stabilization by alginate cross-linking versus sinteringKumar, Alok, Akkineni, Ashwini R., Basu, Bikramjit, Gelinsky, Michael 11 October 2019 (has links)
Scaffolds for bone tissue engineering are essentially characterized by porous three-dimensional structures with interconnected pores to facilitate the exchange of nutrients and removal of waste products from cells, thereby promoting cell proliferation in such engineered scaffolds. Although hydroxyapatite is widely being considered for bone tissue engineering applications due to its occurrence in the natural extracellular matrix of this tissue, limited reports are available on additive manufacturing of hydroxyapatite-based materials. In this perspective, hydroxyapatite-based three-dimensional porous scaffolds with two different binders (maltodextrin and sodium alginate) were fabricated using the extrusion method of three-dimensional plotting and the results were compared in reference to the structural properties of scaffolds processed via chemical stabilization and sintering routes, respectively. With the optimal processing conditions regarding to pH and viscosity of binder-loaded hydroxyapatite pastes, scaffolds with parallelepiped porous architecture having up to 74% porosity were fabricated. Interestingly, sintering of the as-plotted hydroxyapatite–sodium alginate (cross-linked with CaCl₂ solution) scaffolds led to the formation of chlorapatite (Ca₉.₅₄P₅.₉₈O₂₃.₈Cl₁.₆₀(OH)₂.₇₄). Both the sintered scaffolds displayed progressive deformation and delayed fracture under compressive loading, with hydroxyapatite–alginate scaffolds exhibiting a higher compressive strength (9.5±0.5 MPa) than hydroxyapatite–maltodextrin scaffolds (7.0±0.6 MPa). The difference in properties is explained in terms of the phase assemblage and microstructure
|
2 |
In vitro evaluation of cell-material interactions on bioinert ceramics with novel surface modifications for enhanced osseointegration / Evaluation in vitro des intéractions cellules-matériaux sur des céramiques bioinertes avec des modifications de la surface nouvelles pour une osseointegration améliorréeStanciuc, Ana-Maria 23 June 2017 (has links)
Cette thèse porte sur l'évaluation de la réponse cellulaire in vitro vis-à-vis de différentes stratégies de modification de surface pour améliorer la capacité d’ostéointégration de céramiques bioinertes pour implants orthopédiques et dentaires. Premièrement des surfaces l'alumine-zircone avec différentes micro-rugosités obtenues par moulage par injection ont été étudiées. Le comportement d'ostéoblastes primaires humains (obtenus à partir de têtes de fémurs soumis à arthroplastie) a été étudié sur les surfaces telles quelles ou modifiées par traitement avec acide hydrofluorique. La micro-rugosité a eu seulement un effet mineur sur la réponse ostéoblastique tandis que la combinaison de micro- et nano-rugosité a eu un effet synergique sur la maturation ostéoblastique. Cette stratégie de modification de surface ouvre la voie vers des cupules acétabulaires céramiques monoblocs directement ostéo-intégrées. Deuxièmement, le robocasting (une technique d’impression 3D) a été exploré pour la production de structures macroporeuses en alumine-zircone avec une haute reproductibilité et contrôle architectural. Les structures imprimées ont présentées une topographie aux multiples niveaux grâce au design et les conditions de frittage. Les ostéoblastes ont pu s'attacher sur les structures 3D mais la préservation des cellules à l’intérieur des scaffolds sur le long terme reste à améliorer. Des techniques de sélection rapide de modifications de surface ont fait l'objet de la dernière partie de cette thèse. Deux différentes stratégies ont été utilisées sur la zircone: laser femtoseconde pour la production de multiples motifs sur un échantillon unique et échantillons avec un gradient de rugosité via le contrôle du temps d’attaque chimique. La morphologie des cellules souches humaines a permis d'avoir un indicateur précoce de la lignée de différentiation cellulaire. En conclusion, les différentes techniques de modification de surface de zircone et alumine-zircone utilisées à travers la thèse peuvent moduler l’interaction cellule-matériau en stimulant la différentiation ostéoblastique de cellules souches et la maturation des ostéoblastes. / The focus of this PhD thesis is the in vitro evaluation of cell-material interactions on bioinert ceramics with novel surface modifications for enhanced osseointegration of orthopaedic and dental implants. Firstly, alumina-zirconia surfaces with different micro-roughnesses obtained by injection moulding were studied. The behaviour of human primary osteoblasts (hObs) obtained from patients undergoing total hip replacements was studied on the different micro-rough ZTA surfaces and on combined micro-/nano-rough surfaces modified by hydrofluoric acid treatment. Micro-roughness alone had minor effects on hOb response while the combination micro-/nano-roughness induced a synergic effect on hOb maturation. This latter surface modification technique opens the way to the fabrication of ceramic acetabular cups with direct implantation capabilities. Secondly, robocasting (a 3D printing technique) was explored for the fabrication of a alumina-zirconia macroporous structures with high reproducibility and control of the architecture. Roughness at different scales was observed for the 3D structures due to the scaffold design and to the low temperature sintering conditions. Osteoblasts were able to attach on the 3D structures but cell retention at long term needs further optimization. Rapid screening of cell-material interactions was the subject of the last part of the thesis. Two different strategies were tested on zirconia: femtosecond laser to produce multiple patterns on a single sample and samples with a roughness gradient by the control of chemical etching time. Stem cell morphology was used as an early marker of cell differentiation lineage. In conclusion, the different surface modification techniques of zirconia and alumina-zirconia surfaces used in the thesis allow the modulation of cell-material interactions by stimulating stem cells osteogenesis and osteoblast maturation.
|
3 |
Výzkum nových elektrokeramických struktur pro nové aplikace senzorů / An investigation of novel electroceramic structures for new sensor applicationsNan, Bo Unknown Date (has links)
Piezoelektrické keramické materiály jsou široce používány v mnoha aplikacích a průmyslových odvětvích, nicméně tradiční materiály obvykle obsahují olovo, které je toxické vůči životnímu prostředí. Většina zemí proto zavedla zákony a omezení, které postupně minimalizují spotřebu olova a podporují výzkum v oblasti bezolovnatých kompozic, které by nahradily olověné protějšky. Bezolovnatá piezoelektrická keramika se tak stala žhavým tématem v posledních letech. Nicméně výzkumy na praktické využití bezolovnatých piezoelektrických materiálů jsou jen zřídka publikovány. V této diplomové práci byl vybrán jeden z nadějných kandidátů na piezoelektrickou bezolovnatou keramiku (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 za účelem zkoumání metody snížení jeho vysoké teploty slinování pomocí dotování uhličitanem lithným, kde syntéza prášku byla připravená pomocí techniky sol-gel. Výsledky byly srovnány s konvenčním práškem syntetizovaným v pevné fázi. Vzorky vyrobené ze sol-gel prášku dopovaného 0.5% hmotn. uhličitanem lithným a slinované při 1300 °C po dobu 2 hodin vykazovaly d33 = 447 ± 9 pC N–1, teplotu Curie 98.7 °C a velikost zrn 7.0 ± 0.3 m. Další důležitou otázkou pro aplikace bezolovnatého piezoelektrického keramického materiálu je jeho výroba v různých konfiguracích. Použitím techniky odlévání pásky a aditivních výrobních postupů byla piezoelektrická keramika zpracována do tří různých konfigurací (2-2, 3-3 a 1-3), aby se překlenula mezera mezi materiálovými vědami a materiálovým inženýrstvím. Pro dolévání pásky byly použity suspenze na bázi oleje a vody. Pro přípravu neslinutých keramických fólií bez trhlin, byly pro odlévání na bázi oleje vyvinuty uhlíkové suspenze s obsahem pevných látek 25% hmotn. a BCZT suspenze s obsahem pevných látek 65% hmotn. Problém práškové hydrolýzy ve vodných suspenzích byl vyřešen povrchovou úpravou prášku Al(H2PO4)3, což umožnilo, aby byly tlusté vrstvy bez trhlin odlety v jednom kroku. Tlusté vrstvy slinované při 1500 °C vykazovaly relativní dielektrickou konstantu 1207, dielektrickou ztrátu 0.018 při 1 kHz, remanentní polarizaci 7.54 µC/cm2 a koercitivní síla intenzity pole (Ec) 0.23 kV/mm při 3 kV/mm. Pro tvarování BCZT v konfiguraci 3-3 a 1-3 byla použita přímá metoda tisknutí inkoustu. Pro správnou úpravu tiskového procesu byla použita inkoustová náplň s viskoelastickým chováním obsahující 41.6% obj. pevných látek BCZT a se zpracovatelskými přísadami (HPMC ~ 2.4% a PEI ~ 0.03%). Vzorky v konfiguraci 3-3, slinované při 1500 °C, vykazovaly nejvyšší dielektrické a piezoelektrické vlastnosti, kde Curieho teplota = 86 °C, tan = 0.021, remanentní polarizace = 4.56 µC/cm2 a d33 = 100 ± 4 pC/N. Vzorky v konfiguraci 1-3 slinované při 1500 °C, které byly smíchány s epoxidem, vykazovaly dielektrickou konstantu 144 a dielektrickou ztrátu 0.035 při 1 kHz. Tato práce popisuje tvarování bezolovnaté piezoelektrické keramiky s vynikajícími vlastnostmi v pokročilých strukturách jako krok k návrhu pro moderní senzorické a energy harvesting aplikace.
|
Page generated in 0.0398 seconds