No description available.

During the last four decades, fiber reinforced concrete has been increasingly used in structural applications. It is generally accepted that addition of steel fibers significantly increases tensile toughness and ductility, also slightly enhances the compressive strength. Although several studies have reported previously the favorable attributes of steel fiber reinforced concrete (SFRC), little general data is related to performance modeling. There are studies on the effect of fibers on compression, tension and shear behavior of concrete. As models proposed so far can, at best, describe only a few aspect of SFRC with a given type and amount of fibers, establishing simple and accurate generalized equations to describe the behavior of SFRC in tension, compression and shear that take into account the fiber type and content is essential. Therefore, a comprehensive experimental research on SFRC is conducted in University of Canterbury to develop generalized equations to represent the characteristics of SFRC. In this research, standard material tests of SFRC are carried out in tension, compression and shear to enable the parametric characterization and modeling of SFRC to be conducted. The tests are conducted using two different propriety fiber types (NovotexTM and DramixTM) with volumetric ratios ranging from 0 to 2 percent of the Novotex fibers and with 1 percent Dramix fibers. Compression tests are conducted on small and large cylinders. For characterization of tensile behavior, several different test methods are used including: direct tension of SFRC alone; SFRC with tension applied to an embedded longitudinal rebar; and flexural bending test. Similarly direct shear tests are conducted to investigate the additional shear resistance contributed by steel fibers. Variations in the results of different specimens are reconciled through normalization of stress and strain parameters. Based on the experimental results, empirical relations are derived for modeling and analysis of SFRC.

For the manufacture of higher strength pipelines to be feasible, a better understanding of the effects of welding on toughness is necessary. Bevel submerged arc welds were performed on X80 grade steel. The subsequent Charpy V-notch (CVN) test results indicated that the notch placement in the various heat affected zone regions, and hence the bead geometry, affected the test results. A series of bead-on-plate (BOP) submerged arc welds then were performed on X70 grade steel plate to determine the effects of current, voltage, heat input, polarity, and waveform manipulation (i.e., balance, offset, and frequency) on both single and tandem weld bead geometry. A new bead profile characteristic, the SP ratio, is proposed to describe weld bead geometry, and its relationship with welding parameters is discussed. Sub-size CVN specimens, pulled from many of the BOP weld coupons, were then tested. The greatest subsize CVN fracture energies were achieved when the bead was produced using lower heat input, and when the bead profile possessed a greater SP ratio. / Materials Engineering

No description available.

No description available.

Made available in DSpace on 2014-06-11T19:27:13Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-03-31Bitstream added on 2014-06-13T19:55:32Z : No. of bitstreams: 1 nogueira_fc_me_ilha.pdf: 11300968 bytes, checksum: d1398bf3ab23244ed728edf3d9404283 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O ensaio de impacto Charpy convencional é um ensaio mecânico consagrado no meio científico e industrial. Sua função é determinar a energia total absorvida para causar a fratura completa de um corpo-de-prova entalhado, padronizado segundo a norma ASTM E?23. Entretanto, a energia global absorvida possui um valor de uso muito limitado. Ela normalmente não é aceita como um indicador quantitativo da resistência à fratura do material. Assim, através da instrumentação adequada, pode-se aumentar a quantidade de informações obtidas a partir do ensaio de impacto Charpy clássico. No presente trabalho, estudou-se a influência do raio de ponta do entalhe, do tipo de carregamento e da microestrutura dos corpos-de-prova no processo à fratura dinâmica do aço ABNT-4340 a partir do ensaio Charpy Instrumentado. As diferentes condições microestruturais foram resultantes de diferentes condições de tratamentos térmicos: como-recebido, como-temperado e revenido nas seguintes temperaturas: 473K, 573K, 673K e 773K. Para cada microestrutura foram confeccionados corpos-de-prova com dois tipos de raio de ponta - pré-trincado e entalhe arredondado (0,25mm). Os corpos-de-prova assim preparados foram submetidos ao ensaio Charpy Instrumentado e tiveram seus sinais digitalizados. O sinal capturado com tal cadeia de medição foi utilizado na determinação dos valores de tenacidade à fratura dinâmica. Os resultados experimentais foram obtidos através dos ensaios de dureza, monotônicos (em três pontos), dinâmicos (Ensaio de Impacto Charpy). Os ensaios de dureza foram realizados com objetivo de ratificar a qualidade dos tratamentos térmicos. Os ensaios monotônicos servirão como referências para auxiliar o entendimento dos dados obtidos com os ensaios dinâmicos. / The proof of conventional impact Charpy is a mechanic proof consecrated in scientific in industry. Its function is determinate the absorb total energy in order to the complete fracture in a indented proof body, standardized according to the ASTM E- 23 pattern. Therefore, the absorb global energy has a very limited value. It is not accepted a quantities indicator of resistance to the matter fracture. Thus, though adequate instrumentation, it can increase the quantity of information obtained from the proof of the classic impact Charpy. In this paper, we intend to study the influence of the ray of intende tip, of the loading type and of the microstructure of proof bodies in process the fracture of the structural steel ABNT-4340 from the instrumented proof Charpy. The different microstructure conditions are resulted of different conditions of thermal treatments: drawgeting, draw tempering, drawing in following temperatures: 473 K, 573 K, 673 K and 773 K. For each microstructures prepared proof body with two types of tip ray - sharp rack and rounding indented (0,25 mm). Proof bodies prepared this way are submitted the instrumented proof Charpy and have your signal digitalized. The signal capturing with such ranger of measurement will de used in determination of values of toughness to dynamic fracture. The experimental result were obtained through the rehearsals of hardness, almost-static (in three points), dynamic (instrumented proof Charpy). The rehearsals of hardness were accomplished with objective of ratifying the quality of the thermal treatments. The rehearsals almost-static will serve as references for to aid the understanding of the data obtained with the dynamic rehearsals.

Made available in DSpace on 2014-06-11T19:28:34Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-02-07Bitstream added on 2014-06-13T18:57:57Z : No. of bitstreams: 1 gallo_gb_me_guara.pdf: 1706567 bytes, checksum: 597ea250f08f8ddc714ee7df53e7829b (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Estudos de novos materiais, mais resistentes, econômicos e de menor densidade, são de grande interesse para aplicações estruturais em projetos de Engenharias. Propriedades mecânicas antes obtidas principalmente por meio de adição de elementos de ligas, como por exemplo elevada dureza, tenacidade e resistência mecânica, podem ser atingidas atualmente com variações no processamento térmico e termomecânico. Estas alterações têm proporcionado a formação de estruturas multifásicas nos aços, e como elemento deste estudo, os aços bifásicos. Neste trabalho, buscou-se entender os efeitos que processamentos térmicos possuem sobre as microestruturas dos aços de médio teor de carbono (SAE 1045), assim como a sua influência sobre as propriedades mecânicas, especialmente sobre a tenacidade, evidenciada por meio de ensaios de impacto. O material tratado termicamente obteve, sua estrutura transformada, visando à formação de estrutura bifásica (ferrita e martensita) e de estrutura formada por martensita revenida, sendo comparadas com a condição do material como fornecido (ferrita e perlita). A caracterização microestrutural foi realizada para determinação das fases presentes, assim como das frações volumétricas respectivas. Ensaios de tração e de impacto foram realizados visando a determinação das propriedades mecânicas do aço. Os resultados mostraram que a interação entre ferrita e martensita, gerada na condição bifásica, possue forte influência nos resultados referentes à tenacidade, assim como a temperatura em que o material foi ensaiado. Comparando-se três estruturas, comprova-se que a estrutura bifásica possui resistência mecânica e tenacidade mais elevadas que os aços temperados e revenidos, e tenacidade proxima a do aço com médio teor de carbono, sem tratamento térmico. / Studies of new materials, more resistance, cheaper costs and lower density, have high interest for structural use in engineering projects. Mechanical properties adquired in the past by alloyes adition, for example igher hardness, toughness and mechanical strenght, nowadays can be reached using controlled thermo mechanical process. These changes have provided the multiphase structures formation in steels, for example the dual phase steel, subject of the present study. In this work it was researched the effects of heat process in microestructure of medium carbon steels (SAE 1045) and the influence over mechanical properties, specially in toughers, realized by impact analysis. The heat treatment material has its structure transformed in dual-phase structure (ferrite and martensite) and compared with supplied material (ferrite and perlite). The microestructural characterization was done to determine the present phase, and the respective volumetric fraction of martensite. Tension and impact analysis were done to determine the steel mechanical properties. Results have shown that the interaction between ferrite and martensite generated in dual-phase condition, has higher influence, related the materials toughness, so the temperature that material was analysed comparing the three structures, verifies that the dual-phase struture has level of mechanical resistence and toughness, higher than quenched and tempered steels, and toughness near of medium carbon steel that has not received heat treatment in higher or lower temperatures.

Submitted by Juliana Cristine de Sousa Teixeira (jullysousa@gmail.com) on 2018-05-18T20:34:21Z No. of bitstreams: 1 Tese de Mestrado_Juliana Cristine de Sousa Teixeira_Final.pdf: 5778909 bytes, checksum: 048e61d5039f6fe8cb5e93a20b68b791 (MD5) / Rejected by Pamella Benevides Gonçalves null (pamella@feg.unesp.br), reason: Solicitamos que realize correções na submissão seguindo as orientações abaixo: • A capa e a ficha catalográfica não são consideradas para contagem de páginas. a paginação deve aparecer no canto superior direito a partir da introdução, realizei a contagem das páginas e seu trabalho deve com o número (17)*, após você precisa atualizar a numeração na ficha catalográfica, nas listas e no sumário • Referências. A palavra Referências deve ser centralizada, e não conter numeração de seção; As referencias devem ser justificadas, espaço simples com um espaço simples(enter) entre elas. • Será necessário revisar suas referências, logo, sobre a elaboração das referencias e citações favor solicitar ajuda com a bibliotecária Juciene (juciene@feg.unesp.br) ou consultar os modelos de referências nas diretrizes http://www.feg.unesp.br/Home/Biblioteca21/diretrizes-2016.pdf A identificação deve ser feita por letras maiúsculas, consecutivas seguidas de travessão e seus respectivos títulos. Exemplo: ANEXO A - Modelo de formulário Agradecemos a compreensão. on 2018-05-21T12:20:53Z (GMT) / Submitted by Juliana Cristine de Sousa Teixeira (jullysousa@gmail.com) on 2018-05-30T01:46:04Z No. of bitstreams: 1 Tese de Mestrado_Juliana Cristine de Sousa Teixeira_29052018.pdf: 5816923 bytes, checksum: 39d3338ac2cdd4e61f96dc8b8bde5084 (MD5) / Approved for entry into archive by Pamella Benevides Gonçalves null (pamella@feg.unesp.br) on 2018-06-11T12:25:10Z (GMT) No. of bitstreams: 1 teixeira_jcs_me_guara.pdf: 6341115 bytes, checksum: 44f465e9d11d884cc4f765165da772f7 (MD5) / Made available in DSpace on 2018-06-11T12:25:10Z (GMT). No. of bitstreams: 1 teixeira_jcs_me_guara.pdf: 6341115 bytes, checksum: 44f465e9d11d884cc4f765165da772f7 (MD5) Previous issue date: 2018-04-06 / O ensaio de queda de peso DWTT (Drop Weigth Tear Test) é um método amplamente utilizado pela indústria de óleo e gás para determinar a capacidade de um material em impedir a propagação de uma trinca. Esse método foi desenvolvido pelo Battelle Memorial Institute, e é realizado em conformidade com a especificação API RP 5L3 "Práticas Recomendadas para a Condução de Testes de Queda de Peso". Com o desenvolvimento dos aços ARBL, o comportamento dos aços vem mostrando algumas particularidades resultantes do processamento termomecânico, e por esse motivo, podem não apresentar o mesmo comportamento à fratura que aços mais antigos, como delaminações ou inclusões não metálicas. Atualmente são propostos dois tipos de entalhe, sendo o tipo prensado, obtido pela estampagem de uma matriz na amostra, e o tipo Chevron, que deve ser usinado. A correlação entre ambos os entalhes pode ser realizada apenas para a análise da porcentagem da superfície dúctil da fratura. Outros tipos de correlação como energia absorvida para impacto, não são recomendados, uma vez que a concentração de tensão para o entalhe Chevron é muito maior, facilitando o rompimento da amostra, enquanto que o entalhe prensado demanda maior energia, uma vez que possui maior encruamento na região. No presente trabalho foram realizados os levantamentos de curvas de temperatura de transição dúctil e frágil (TTDF) do material base do tubo com dimensões de 762 mm x 38,1 mm de aço carbono com grau API X60, através da análise da porcentagem de fratura dúctil resultante cujo os resultados se mostraram equivalentes tanto para o entalhe Prensado como Chevron; energia absorvida pela leitura do equipamento de DWTT com cutelo instrumentado, apresentando resultados não comparativos, sendo necessário maior energia para fraturar um CP com entalhe Prensado e menor energia para fraturar um CP com entalhe usinado Chevron; e expansão lateral, resultante das amostras para ambos os tipos de entalhes, cujo os resultados possuem similaridade, entretanto não equivalentes. Para correlacionar a energia absorvida, também foi realizada a TTDF por ensaio de impacto (CVN), contudo a correção não foi possível, devido ao tamanho da amostra ser distinta ao DWTT / The Drop Weigth Tear Test (DWTT) is a method widely used by the oil and gas industry to determine the ability of a material to prevent the propagation of a crack. This method was developed by the Battelle Memorial Institute, and is performed in accordance with API RP 5L3 "Drop-Weight Tear Tests on Line Pipe" specification. With the development of ARBL steels, the behavior of steels has shown some particularities resulting from thermomechanical processing, and for this reason, they may not present the same fracture behavior as older steels, such as delamination or nonmetallic inclusions. Currently two types of notch are proposed, being the type pressed, obtained by the stamping of a matrix in the sample, and the type Chevron, that must be machined. The correlation between both notches can be performed only for the analysis of the percentage of the ductile surface of the fracture. Other types of correlation as energy absorbed for impact are not recommended, since the stress concentration for the Chevron notch is higher, facilitating the rupture of the sample, while the notched press demands greater energy, since it has greater hardening in the region. In the present study, the ductile and brittle transition temperature (TTDF) curves of the base material of the pipe with dimensions of 762 mm x 38.1 mm of carbon steel with API grade X60 were carried out, through the analysis of the percentage of ductile fracture resulting whose results were shown to be equivalent for both notch: Pressed and Chevron; energy absorbed by reading DWTT equipment with instrumented cleaver, presenting non-comparative results, requiring greater energy to fracture a sample with notched Press and lower energy to fracture a sample with Chevron machined notch; and lateral expansion, resulting from the samples for both types of notches, whose results have similarity, however not equivalent. In order to correlate absorbed energy, TTDF was also performed by impact test (CVN), however correction was not possible, because the sample size was distinct from DWTT

Orientador: Marcelo dos Santos Pereira / Resumo: O ensaio de queda de peso DWTT (Drop Weigth Tear Test) é um método amplamente utilizado pela indústria de óleo e gás para determinar a capacidade de um material em impedir a propagação de uma trinca. Esse método foi desenvolvido pelo Battelle Memorial Institute, e é realizado em conformidade com a especificação API RP 5L3 "Práticas Recomendadas para a Condução de Testes de Queda de Peso". Com o desenvolvimento dos aços ARBL, o comportamento dos aços vem mostrando algumas particularidades resultantes do processamento termomecânico, e por esse motivo, podem não apresentar o mesmo comportamento à fratura que aços mais antigos, como delaminações ou inclusões não metálicas. Atualmente são propostos dois tipos de entalhe, sendo o tipo prensado, obtido pela estampagem de uma matriz na amostra, e o tipo Chevron, que deve ser usinado. A correlação entre ambos os entalhes pode ser realizada apenas para a análise da porcentagem da superfície dúctil da fratura. Outros tipos de correlação como energia absorvida para impacto, não são recomendados, uma vez que a concentração de tensão para o entalhe Chevron é muito maior, facilitando o rompimento da amostra, enquanto que o entalhe prensado demanda maior energia, uma vez que possui maior encruamento na região. No presente trabalho foram realizados os levantamentos de curvas de temperatura de transição dúctil e frágil (TTDF) do material base do tubo com dimensões de 762 mm x 38,1 mm de aço carbono com grau API X60, através da análise da porce... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The Drop Weigth Tear Test (DWTT) is a method widely used by the oil and gas industry to determine the ability of a material to prevent the propagation of a crack. This method was developed by the Battelle Memorial Institute, and is performed in accordance with API RP 5L3 "Drop-Weight Tear Tests on Line Pipe" specification. With the development of ARBL steels, the behavior of steels has shown some particularities resulting from thermomechanical processing, and for this reason, they may not present the same fracture behavior as older steels, such as delamination or nonmetallic inclusions. Currently two types of notch are proposed, being the type pressed, obtained by the stamping of a matrix in the sample, and the type Chevron, that must be machined. The correlation between both notches can be performed only for the analysis of the percentage of the ductile surface of the fracture. Other types of correlation as energy absorbed for impact are not recommended, since the stress concentration for the Chevron notch is higher, facilitating the rupture of the sample, while the notched press demands greater energy, since it has greater hardening in the region. In the present study, the ductile and brittle transition temperature (TTDF) curves of the base material of the pipe with dimensions of 762 mm x 38.1 mm of carbon steel with API grade X60 were carried out, through the analysis of the percentage of ductile fracture resulting whose results were shown to be equivalent for both notch: ... (Complete abstract click electronic access below) / Mestre

[pt] Durante as ultimas três décadas, as pesquisas cientificas sobre bambu como material de engenharia concentraram-se na caracterização física e mecânica nos níveis macro, meso, micro e alguns trabalhos no nível nanoestructural. As praticas de uso de bambu inteiro mostram ao longo do tempo trincas na superfície que são provocadas por razão da variação da umidade, da temperatura e entalhes gerados durante o processo de fabricação de peças estruturais. A presença das trincas tem grande influenciam na resistência desses elementos. Este aspecto do comportamento do bambu ainda é assunto de estudo na fase inicial. O presente trabalho apresenta os resultados da pesquisa teórico-experimental realizada para a determinação dos valores característicos dos fatores de intensidade de tensões, K(C), e as taxas de dissipação de energia, G(C), para os modos I e II, utilizando metodologias experimentais aplicadas aos materiais compósitos. Foi estudada a espécie Dendrocalamus Giganteus da parte basal do bambu do campus da PUC-Rio. A dimensão do corpo-de-prova tinha seção transversal retangular de 10x10mm e 100 mm de comprimento do vão livre com entalhes induzidos. Os corpos-deprova foram submetidos à flexão em quatro pontos para diferentes valores de tamanho de entalhe. São apresentados os resultados de carga-deslocamento na metade do comprimento e as deformações relativas nas faces externa, interna e lateral dos corpos-de-prova. Os valores das taxas dissipação de energia e fatores de intensidade de tensões foram calculados a partir da curva de carga - deslocamento. / [en] During the last three decades, the research on bamboo as engineering material was carried on through the physical and mechanic characterizations in the levels macro, meso, micro and some works in the nano-structural level. In practice, the use of entire bamboo shows cracks on the surface throughout the time, that are provoked by variation of the moisture, the temperature and notches generated during the process of manufacture of structural parts. The crack presence has influences on the resistance of these elements. This aspect of the bamboo behaviour is still subject of study in the initial phase. This work presents the results of a theoretical and experimental research for the determination of the characteristic values of the intensity stress factors, K(C), and the release energy, G(C), for modes I and II, using methodologies applied to the composites materials. It was studied the basal part of the specie Dendrocalamus Giganteus of the Pontifícia Universidade Católica do Rio de Janeiro campus (PUC-Rio). The specimens had rectangular shape with transversal section of 10x10mm and 100mm of length with notch; each one was tested in four points bend for different values of notch size. The results correspond to curves load-displacement in the half span; and strain in the external, internal and lateral sides of the specimen. The values of release energy and intensity stress factors have been calculated from the curve loaddisplacement.