Thesis (M.S.)--Rochester Institute of Technology, 1989. / "Reference": leaves 224-227.

Thesis (Ph. D.)--University of Texas at Austin, 2002. / Vita. Includes bibliographical references. Available also from UMI Company.

Thesis (Ph.D)--Materials Science and Engineering, Georgia Institute of Technology, 2009. / Committee Chair: Speyer, Robert; Committee Co-Chair: Sanders, Thomas; Committee Member: Gerhardt, Rosario; Committee Member: Sandhage, Kenneth; Committee Member: Snyder, Robert; Committee Member: Zhang, John. Part of the SMARTech Electronic Thesis and Dissertation Collection.

Thesis (Ph. D.)--Ohio State University, 1965. / Includes bibliographical references (leaves 61-63). Available online via OhioLINK's ETD Center.

Thesis (Ph. D.)--Ohio State University, 2006. / Available online via OhioLINK's ETD Center; full text release delayed at author's request until 2007 May 23

Thesis (Ph. D.)--Oregon Graduate Center, 1987.

Thesis (Ph. D.)--University of Washington, 2006. / Vita. Includes bibliographical references (leaves 141-148).

Made available in DSpace on 2014-12-02T11:16:37Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-02-20Bitstream added on 2014-12-02T11:21:06Z : No. of bitstreams: 1 000794183.pdf: 1656380 bytes, checksum: 228ae3f387366384eb9b7265ce37a07e (MD5) / Este estudo caracterizou mecanicamente uma porcelana feldspática de aplicação convencional e uma porcelana feldspática prensada, indicadas para infraestrutura em zircônia, quanto a resistência à flexão biaxial, dureza Vickers e tenacidade à fratura. Além disso, foi investigado o efeito da taxa de resfriamento após o ciclo de sinterização do glaze da porcelana na resistência à flexão biaxial de bicamadas zircônia/porcelana. Espécimes monocamada de VM9 (n=15) e Vita PM9 (n=15) (12,0 mm de diâmetro x 1.2 mm de espessura) foram confeccionados conforme as recomendações do fabricante e submetidos ao ensaio de resistência à flexão biaxial (MPa). Um fragmento de cada espécime fraturado foi aleatoriamente selecionado para a mensuração da dureza Vickers (n=15) (VHN). A tenacidade à fratura aparente(MPa.m½) foi determinada pela técnica da indentação Vickers (n=15). Para o ensaio de flexão biaxial dos bicamadas, discos de zircônia (Vita In-Ceram YZ) foram recobertos com porcelana convencional Vita VM9 (n=30) ou com porcelana prensada Vita PM9 (n=30). Após a simulação da queima de glaze, os espécimes foram submetidos a resfriamento rápido (n=15) ou lento (n=15). Após o ensaio de resistência à flexão, os espécimes foram analisados quanto ao tipo de fratura. Teste de T-Student para espécimes monocamada mostrou que Vita PM9 apresentou valores significantemente maiores de resistência à flexão biaxial (p<0,01) e dureza (p=0,017) em relação a Vita VM9, mas não quanto a tenacidade à fratura (p= 0.41). ANOVA a dois fatores (porcelana e método de resfriamento), utilizada para análise dos bicamadas indicou significância apenas para porcelanas, com superioridade para a combinação Vita PM9/zircônia (p<0,01). Porcelanas prensadas parecem ser uma alternativa mais efetiva para recobrimento de zircônia em relação as convencionais. / This study characterized mechanically a conventional and a pressed feldspathic porcelain indicated for zirconia core in terms of biaxial flexural strength, fracture toughness, Vickers hardness. In addition it was investigated the effect of the glaze cooling rate on the biaxial flexural strength of the zirconia/porcelain bilayer. Specimens monolayers of Vita VM9 (n=15) and Vita PM9 (n=15) (12.0 mm diameter x 1.2 mm thickness) were prepared according to manufacturer’s recommendations for the biaxial flexural strength test (MPa). Afterwards, one fragment of each broken specimen was randomly selected for Vickers hardness measurements (n=15) (VHN). Apparent fracture toughness (MPa.m½) was determined by Vickers hardness indentation technique (n=15). For the biaxial flexural strength of bilayers, zirconia discs (Vita In-Ceram YZ) were veneered with the conventional porcelain Vita VM9 (n=30) or with the pressed porcelain Vita PM9 (n=30). After the glaze firing simulation, the specimens were submitted to fast (n=15) or slow cooling method (n=15). After the biaxial flexural test, the specimens were analyzed in relation to fracture pattern. T-Student tests were performed for the monolayer specimens, while two-way ANOVA (porcelain and cooling method) was used for the bilayer ones (α=.05). Vita PM9 exhibited significantly higher biaxial flexural strength (p<0.01) and hardness than VM9 (p=0.017). However, there was no significant difference (p= 0.41) in fracture toughness between the porcelains. The two-way ANOVA indicated significance only for the porcelain, with superiority for the combination Vita PM9/zirconia (p<0.01).The pressed porcelain seems to be a mechanically more effective alternative for zirconia veneering than the conventional one.

Orientador: Daniela Micheline dos Santos / Coorientador: Aldiéris Alves Pesqueira / Banca: Marcelo Coelho Goiato / Banca: Valentim Adelino Ricardo Barão / Resumo: A obtenção de uma união duradoura da interface zircônia/cerâmica de cobertura é uma preocupação para sucesso clínico de restaurações livres de metal e ainda não existem evidências que indiquem uma técnica de tratamento dessa zircônia com melhor previsibilidade e durabilidade. Assim, o objetivo desse estudo foi desenvolver e caracterizar fisico-quimicamente um novo filme por vapor químico melhorado por plasma (plasma enhanced chemical vapor deposition - PECVD) na superfície da zircônia tetragonal policristalina estabilizada por óxido de ítrio (Y-TZP) para melhorar sua resistência de união com cerâmica de cobertura. Para isso, um total de 192 amostras de Y-TZP (13×5,4×5 mm) foram divididas em 6 grupos, de acordo com o tratamento de superfície: controle - sem tratamento (C), jateamento com partículas de óxido de alumínio de 27 µm (Al27), jateamento com partículas de óxido de alumínio de 110 µm (Al110), jateamento com partículas de óxido de alumínio de 250 µm (Al250), aplicação de liner para zircônia (L) e o filme por PECVD (P). A superfície da Y-TZP foi caracterizada por meio da microscopia eletrônica de varredura (MEV), espectroscopia de energia dispersiva (EED), microscopia de força atômica (MFA), perfilometria e energia livre de superfície. A resistência de união entre a Y-TZP e uma cerâmica de cobertura foi testada antes e após fadiga térmica (20.000 ciclos de 5 e 55 °C). Os dados foram submetidos à análise de variância e teste Tukey HSD (α=0,05). Como resultados, foi encont... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The obtainment of a durable zirconia/veneer ceramic interface bond is a preoccupation for clinical success of metal-free restorations and did not exist evidence indicates that the technique with the best predictability and durability. Thus, the aim of this study was to develop and to physico-chemically characterize a novel film formed after plasma enhanced chemical vapor deposition (PECVD) on the yttria stabilized tetragonal zirconia (Y-TZP) surface aiming to improve its bond strength to the veneer ceramic. For this, a total of 192 YTZP samples (13×5.4×5 mm) were divided in 6 groups, according the surface treatment: control - no treatment (C), airborne-particle with 27 µm aluminum oxide (Al27), airborneparticle with 110 µm aluminum oxide (Al110), airborne-particle with 250 µm aluminum oxide (Al250), zirconia liner (L) and the film by PECVD (P). The Y-TZP surface was characterized through scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), atomic force microscopy (AFM), surface roughness and surface free energy. The bond strength between Y-TZP and veneer ceramic was tested before and after thermal fatigue (20,000 cycles of 5 and 55ºC). The data were submitted to analysis of variance and Tukey HSD test (α=0.05). The results were that the roughness of Y-TZP surface was not modified in the P group (P>0.05 vs control), while the Al110, Al250 and L groups showed higher roughness values (P<0.05). All the treatments improved the surface free energy of Y-TZP, exc... (Complete abstract click electronic access below) / Mestre

Made available in DSpace on 2014-10-09T12:30:38Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:01:04Z (GMT). No. of bitstreams: 1 11285.pdf: 844434 bytes, checksum: 8aa5f041220f28440f0c25cd1c3d5b0f (MD5) / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP