Cement bonded particleboards contain organic base and as they are set outside, extreme weather condition, such as frost, chemical defrosting substances or sulphates, cause their degradation. The presence of the organic base in the matrix of the material could be the reason why there is higher probability of degrading when compared with materials containing an inorganic base. It could be partially eliminated by an appropriate surface modification of the slab, which main goal is to weaken the impact of an aggressive environment and to extend the lifespan of the board. On the other hand, the surface modifications based on a polymer base are prone to degrade because of other unfavourable conditions such as UV radiation when compared with the cement bonded particleboard. The classification of the surface modifications and the way of their degradation caused by the aggressive environment in real applications are presented in the theoretical part of the thesis. In the experimental part, appropriate methodical ways of testing the resistance of cement bonded particleboard’s coating system were chosen. Then, the testing and comparing of the physical, mechanical and aesthetic properties of different types of coatings were done. Moreover, a spectrophotometric analysis of the colour shade changes for the different aggressive environment were carried out. Furthermore, microstructures of chosen surface modifications were assessed by using an optical and an electron microscope.

In line with the current focus on utilizing side products of various production processes, this dissertation thesis analyzes the process of alkali activation of particular side products: fly ash and brick fragments. This activation produces geopolymeric materials widely used in civil engineering. The thesis aims to optimize the geopolymerization process so that the resulting geopolymer is both ecologically and economically viable. To that end, the thesis studies the course of geopolymeric reaction between the alkali activator and fly ash from: (i) the Chvaletice power plant, (ii) the Dětmarovice power plant, and (iii) biomass combustion, as well as (iv) fluid fly ash from the Hodonín power plant. All experiments of geopolymeric reaction have focused on the factors influencing the synthesis of geopolymers—that is: composition of the alkali activator, the ratio of alumino-silicate to the activator, and the impact of temperature on structure of the synthesized geopolymer. Further, the thesis analyzed the synthesized polymer’s microstructure, phase composition, resistance against corrosive conditions, and compressive strength, as well as mechanical-fracture properties of selected fly-ash geopolymers. The thesis finds that the most suitable for geopolymeric synthesis appears to be the fly ash from the Chvaletice power plant in which case the obtained geopolymers showed best properties in the studied areas. The fly ash from the Dětmarovice power plant, biomass fly ash, and fluid fly ash have failed to reach acceptable properties. Separately, the thesis studies the geopolymerization of brick body that could be suitable input for alkali activation. The geopolymers synthesized from brick fragments resulted in materials of supperior mechanical strength. A mixed use of fly ash and brick fragments failed to show a synergetic effect. Properties of the resulting geopolymers have been inferior to the properties of geopolymers produced using just fly ash or just brick body.

No description available.

The diploma thesis aims to analyze bent FRP reinforcements. It describes the method of production of bent FRP reinforcement, examples of application of FRR reinforcement in structures and mentions aggressive influences influencing the durability of FRP reinforcement. Furthermore, an experiment is proposed to monitor changes in straight and bent FRP reinforcement stored in an aqueous environment at 20 °C and an alkaline environment at 20 °C and 40 °C. The output of the diploma thesis is the evaluation of changes in mechanical properties and durability. The condition of the FRP reinforcement is documented using optical and electron mocroscopy.