The diploma thesis is focused on the development of composites from alkali activated materials (AAM) and their resistance to extreme temperatures. The theoretical part describes alkaline activation and precursors for the production of AAM. Furthermore, the problem of the effect of extreme temperatures on these materials is described. In the experimental part, the optimal silicate modulus with respect to the properties of AAM was gradually determined, and the effect of extreme temperatures on the AAM matrix was verified. In the next stage, the effect of the filler with respect to the behavior at extreme temperatures was tested and then the final formulation was optimized.

Nowadays, the waste sands from the water glass production have no utilization and due to high alkali content are considered as a dangerous waste. So the aim of this thesis is to find and study some possibilities of their utilization in the building industry. First of all, some necessary analysis of these sands were performed and then some advantages and disadvantages of their application for production of materials based on portland cement and alkali activated materials were studied. Characteristics of fresh and hardened pastes, mortars and concretes containing these waste sands were determined. The most tested properties were their workability and their compressive and flexural strength. Close attention for the risks of alkali-silica reaction and for options of its suppressing by the mineral admixtures was paid.

This paper reports the development of an Alkali Activated Binder (AAB) with an emphasis on the performance and the durability of the AAB-matrix. For the development of the matrix, the reactive components granulated slag and coal fly ash were used, which were alkali activated with a mixture of sodium hydroxide (2 - 10 mol/l) and aqueous sodium silicate solution (SiO2/Na2O molar ratio: 2.1) at ambient temperature. A sodium hydroxide concentration of 5.5 mol/l revealed the best compromise between setting time and mechanical strengths of the AAB. With this sodium hydroxide concentration, the compressive and the 3-point bending tensile strength of the hardened AAB were 53.4 and 5.5 MPa respectively after 14 days. As a result of the investigation of the acid resistance, the AAB-matrix showed a very high acid resistance in comparison to ordinary Portland cement concrete. In addition, the AAB had a high frost resistance, which had been validated by the capillary suction, internal damage and freeze thaw test with a relative dynamic E-Modulus of 93% and a total amount of scaled material of 30 g/m2 after 28 freeze-thaw cycles (exposure class: XF3).

This dissertation deals with the study of electric and dielectric properties of composite structures on the base of alkali-activated aluminosilicates with admixtures of various carbon particles. These materials fabricated from alkali-activated blast furnace slag, quarz sand, natrium water glass as alkali activator, water, dispersant and small amount of carbon admixture (carbon black, graphite powder, carbon fibers or carbon nanotubes) to increase electric conductivity may be used for example to construction of snow-melting, deicing and self-monitoring systems. Their current-voltage characteristics and impedance spectra were used for determination of electric and dielectric properties of these structures. The equivalent circuits were used for evaluation of impedance spectra. The results were correlated with thermal properties of these structures.

Předložená magisterská práce se zabývá možným použitím vitrifikovaného lignitového lóžového popele jako náhrada slinku v kompozitních cementech. Byly zkoumány vlivy přidaného vitrifikovaného lóžového popele, jeho jemnosti, alkalických roztoků a jejich koncentrací. Byly připraveny kompozitní cementy v souladu s normou DIN EN 197 – 1. V těchto cementech bylo nahrazeno 30 % slinku vitrifikovaným lóžovým popelem. Konkrétně byly připraveny kompozitní cementy s vitrifikovaným lóžovým popelem o jemnosti 5549 cm2/g a 8397 cm2/g. Dále byly přidány alkalické roztoky hydroxidů a síranů vždy o dvou různých koncentracích, za účelem stimulace pucolánové a/nebo geopolymerní reakce. Mechanické vlastnosti připravených vzorků byly charakterizovány mechanickým testováním na prizmách s rozměry 40×40×160 mm, jak je specifikováno v normě DIN EN 196 – 1. Byla provedena nedestruktivní měření dynamického elastického modulu a destruktivní testovaní na pevnosti v tlaku a v ohybu. Distribuce velikosti částic a chemická analýza vstupních materiálů byla vykonána pomocí laserové granulometrie a rentgenové fluorescence. U zatvrdlých kompozitů bylo dále zkoumáno po 2 a 28 dnech hydratace fázové složení s využitím metody rentgenové difrakce a mikrostruktura s využitím skenovací elektronové mikroskopie. Výsledky ukázaly, že mechanické vlastnosti jsou nezávislé na množství přidaných alkálií stejně jako na jemnosti přidaného vitrifikovaného lóžového popele. Nicméně, znatelně nižší mechanické pevnosti byly pozorovány pro vzorky, které byly aktivovány hydroxidy, pravděpodobně kvůli brzké tvorbě silikátového hydrogelu. Vzorky aktivované sírany nedosáhly pevností jako referenční malta.

The topic of this master's thesis is the development of composite materials based on inorganic binders for use in extreme conditions. It means especially geopolymeric or alkali activated materials (AAM) based composites. The theoretical part of this thesis summarizes knowledges about the development and use of alkali-activated materials, their structure and mechanisms of their formation. It also deals with the applicable raw materials for AAM and their exciters, which are in particular water glass and sodium hydroxide. There also have been a summary of the effects of high temperatures and chemicals on the mechanical properties of AAM and the requirements of standard EN 1504-3 for repairing materials. The task of the practical part was to develop a repair mortar for concrete structures based on AAM so that its production was as simple as possible, ie one-component materials. Gradually six recipes have been develeoped. Test specimens made from these recipes have been putted to selected tests according to the requirements of ČSN EN 1504-3.

This work solves creation of calibration relations to determine cube compressive strength, dynamic and static elastic modulus of alkali-activated concrete by non-destructive methods. Alkali-activated concrete is spoken of as a new material used in civil engineering. It shows different properties than normal concrete based on Portland cement. That's why the modification of common calibration relation seems necessary. Fresh concrete was made in the concrete plan ŽPSV a.s., Uherský Ostroh in three mixtures and always in the number of 18 cubes and 3 prisms. The samples were tested by impact hammer Schmidt type L, type N, SilverSchmidt PC-N and by ultrasound in 6 time periods of three specimens. After that, the cube compressive strength was determined. Status of static elastic modulus was determined in a time period of 28 days. The results are calibration relations to determine the progress of compressive strength and modulus of elasticity for each method and their combination.

Since their inception, building materials are constantly improving. New ways to explore and improve the material's properties are constantly investigated (especially to improve the mechanical and deformation characteristics of the materials). This thesis is focused on identifying and comparing values of the modulus of elasticity of fine-grained composites. These features are compared with respect to water cement ratio, ageing and compressive strength of the investigated materials. Afterwards, the values of the modulus of elasticity are studied in the relation to the tested materials.

Tesis por compendio / [ES] Esta tesis englobada dentro del programa de doctorado en ingeniería de la construcción sigue la línea de investigación en sostenibilidad y gestión de la construcción. Las investigaciones se han centrado en el desarrollo de cementos de activación alcalina (CAA) obtenidos a partir de residuos con el fin de reducir tanto el coste económico como medioambiental. Este hecho implicaría la reducción en el uso tanto de materias primas, en el caso de los precursores, como de reactivos químicos en el caso de los activadores. La tesis doctoral que se presenta estudia el uso de diferentes mezclas de residuos como precursores: cerámica sanitaria, catalizador gastado de craqueo catalítico, escoria de alto horno y ceniza volante de central térmica en la preparación de morteros. Así mismo, utiliza también CAA, obtenidos a partir de residuos en la estabilización de suelos. En este último caso también se han usado residuos en la preparación de activadores como son las cenizas obtenidas en la combustión de biomasa. Los resultados obtenidos ponen de manifiesto la viabilidad en el uso de residuos para la preparación de CAA, y la posibilidad incluso de ser usados en contextos de subdesarrollo. / [CA] Aquesta tesi englobada dins del programa de doctorat en enginyeria de la construcció segueix la línia d'investigació en sostenibilitat i gestió de la construcció. Les investigacions s'han centrat en el desenvolupament de ciments d'activació alcalina (CAA) obtinguts a partir de residus amb la finalitat de reduir tant el cost econòmic com mediambiental. Aquest fet implicaria la reducció en l'ús tant de matèries primeres, en el cas dels precursors, com de reactius químics en el cas dels activadors. La tesi doctoral que es presenta estudia l'ús de diferents mescles de residus com a precursors: ceràmica sanitària, catalitzador gastat de craqueig catalític, escòria d'alt forn i cendra volant de central tèrmica en la preparació de morters. Així mateix, utilitza també CAA, obtinguts a partir de residus en l'estabilització de sòls. En aquest últim cas també s'han usat residus en la preparació d'activadors com són les cendres obtingudes en la combustió de biomassa. Els resultats obtinguts posen de manifest la viabilitat en l'ús de residus per a la preparació de CAA, i la possibilitat de ser usats fins i tot en contextos de subdesenvolupament. / [EN] This doctoral thesis encompassed within the doctoral program in construction engineering follows the research line in sustainability and construction management. The research has focused on the development of alkaline activated cements (AAC) obtained from waste to reduce the economic and environmental cost. This fact would imply a reduction in the use of raw materials in the case of precursors, and chemical reagents in the case of activators. The doctoral thesis that is presented studies the use of different waste mixtures as precursors: sanitary ceramics, spent fluid cracking catalyst, blast furnace slag and fly ash from thermal power plants in the preparation of mortars. Likewise, also is used CAA obtained from residues in soil stabilization. In the latter case, residues have also been used in the activators preparation, such as the ashes obtained in the combustion of biomass. The results obtained show the viability in the use of residues for CAA preparation, and the possibility of being used even in underdeveloped contexts. / Agradecer al Ministerio de Ciencia e Innovación por el soporte a mi investigación, mediante los fondos del proyecto APLIGEO BIA2015-70107-R y los fondos FEDER. También a las empresas: Ideal Standard por suministrar residuos de cerámica sanitaria, Omya Clariana S.A. por suministrar catalizador gastado del craqueo catalítico, a Balalva S.L. por suministrar cenizas volantes, a Cementval por suministrar escorias de alto horno, a Heineken España S.A. por el suministro de residuo del filtrado de cerveza (tierras diatomeas), a DACSA GROUP por la ceniza de cáscara de arroz, y a PAVASAL por suministrar suelo de tipo dolomítico. Támbien al servicio de Microscopía electrónica y al Instituto de Ciencia y Técnología del Hormigón de la Universitat Politècnica de València. / Cosa Martínez, J. (2022). Utilización de mezclas de residuos para la obtención de cementos de activación alcalina: aplicación en morteros y suelos estabilizados [Tesis doctoral]. Universitat Politècnica de València. https://doi.org/10.4995/Thesis/10251/185221 / Compendio