O presente trabalho envolve medidas do índice de refração no MgO como função de pressão, através de um micro-interferômetro deste material, colocado no interior de uma camara de alta pressão do tipo bigornas de diamante. / In this work we measured the pressure dependence of the refractive index of MgO. A micro-interferometer of this material was inserted into a diamond anvil cell.

O presente trabalho envolve medidas do índice de refração no MgO como função de pressão, através de um micro-interferômetro deste material, colocado no interior de uma camara de alta pressão do tipo bigornas de diamante. / In this work we measured the pressure dependence of the refractive index of MgO. A micro-interferometer of this material was inserted into a diamond anvil cell.

O presente trabalho envolve medidas do índice de refração no MgO como função de pressão, através de um micro-interferômetro deste material, colocado no interior de uma camara de alta pressão do tipo bigornas de diamante. / In this work we measured the pressure dependence of the refractive index of MgO. A micro-interferometer of this material was inserted into a diamond anvil cell.

We studied dimuon events arising from trident production, for both coherent and incoherent processes, as well as relevant backgrounds, in order to predict the number of expected events observed in the lifetimes of current and forthcoming neutrino experiments. In particular, for this thesis, we focused in building the implementation of the incoherent contribution within the context of the GENIE montecarlo generator. We also developed relatively detailed GEANT4 geometries for the MINERvA detector as well as the DUNE Near Detector, for the Liquid Argon (LArTPC) and Straw Tube Tracker (STT) proposals. A very careful study of the backgrounds for the incoherent case was carried, in order to complement the study already done for the coherent contribution. Then, we combined the signals for the coherent and incoherent processes to realize a more realistic study of the expected number of events. The ROOT TMVA package for multivariate analysis was then used to filter signal from background. The results are presented in terms of number of events, and are calibrated based on the detector exposure in the lifetime of the MINERvA detector and DUNE Near Detector. / Tesis

Orientador: Jose Bellandi Filho / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-07-15T02:36:43Z (GMT). No. of bitstreams: 1 Padua_AntonioBrazde_M.pdf: 4447658 bytes, checksum: 8a2c61dedd684b8ed62764f3ab28ab28 (MD5) Previous issue date: 1986 / Resumo: Analisamos o espalhamento elástico p'p no intervalo de energias 9,78 £ Ö S £ 546 GeV e na região de pequenos -t. Os dados experimentais de ( ds/dt )p'p foram ajustados tomando-se a amplitude de espalhamento puramente imaginária e parametrizada sob a forma exponencial a( s,t ) = a( s,0 ) nSi=1 aiexp(bit) .Usando-se os parâmetros de ajuste calculamos a constante de absorção Kp'p, o fator de forma e o raio da distribuição de matéria de p' através do modelo de Chou-Yang. Pelo mesmo modelo, previmos o aparecimento de "dip" para as energias de 31 e 62 GeV em -t ~ 1.3 ( GeV/c )2 / Abstract: The p'p elastic scattering is analysed in the energy range 9.78 £ ÖS £ 546 GeV and small -t region. The experimental data of ( ds/dt )p'p were fitted under the hypothesis of apure imaginary amplitude and writted as a sum of exponentials, that is, a( s,t ) = a( s,0 ) nSi=1 aiexp(bit).Using the pararneters a( s,0 ), ai and bi we obtained the absorption constante Kp'p, the form factor and the mean square radius of the p' matter distribution by the Chou-Yang model. These calculations reveal a dip around -t ~ 1.3 ( GeV/c )2 at 31 and 62 GeV / Mestrado / Física / Mestre em Física

Tese de doutoramento. Engenharia Química. Faculdade de Engenharia. Universidade do Porto. 2005

Neste trabalho foi estudado o efeito de altas pressões, temperatura e bombardeamento de íons em ligas Invar FeNi. Analisamos os resultados destes diferentes tratamentos, principalmente através das técnicas de Efeito Mõssbauer por transmissão e por elétrons de conversão, medidas de temperatura de Curie e difração de raio-X. A investigação com pressões de até 10 GPa, para diferentes concentrações da liga FeNi, mostrou que a pressão não favorece a ordenação e separação de fases. No estudo da temperatura de Curie de ligas com concentração em torno de 30 at.% de Ni, como função do tempo de recozimento para diferentes temperaturas, observamos um aumento em Tc de mais de 20°C, em temperaturas da ordem de 340°C. A variação de T c com o tempo foi similar à observada em ligas amorfas, sendo interpretada como um rearranjo atômico, numa escala muito pequena. A energia de ativação para o processo foi estimada em torno de 1.5 eV, indicando o movimento de vacâncias congeladas como o principal mecanismo de relaxação. No estudo dos efeitos de bombardeamento com íons de Ar, Ne e Kr, para diferentes doses e temperaturas, em ligas com concentrações em torno de 30 e 40 at.% de Ni, observamos uma separação de fases, para as amostras bombardeadas com Ne e Ar, mas nenhuma evidência de ordenação, como ocorre em amostras irradiadas com elétrons e neutrons. Para o bombardeamento com Kr, não observamos nenhuma mudança, exceto para as amostras que já apresentavam separação de fases, as quais voltaram a seu estado inicial de fase única. Estes resultados indicam que existe uma predominância de mistura para bombardeamento com íons pesados, e de difusão auxiliada por irradiação para íons leves. / We studied in this work the effect of high pressure, temperature and ion bombardment in FeNi Invar alloys. The results of the different treatments were analysed mainly, by Transmission MOssbauer Spectroscopy, Conversion Electron MOssbauer Spectroscopy, measurements of Curie temperature and X-Ray diffraction. The pressure investigation until 10 GPa, for different concentrations of the FeNi alloy, showed that pressure does not favour ordering and phase separation. The study of Curie temperature of alloys near 30 at.% de Ni, as a function of the annealing time at different temperatures showed an increase in Tc of more than 20°C, with annealing at temperatures as low as 340°C. The change in Tc with time was similar to that observed in amorphous alloys, and was interpreted as an atomic rearrangement, in a very small scale. The activation energy for the process was estimated to be about 1.5 eV, indicating movement of quenched-in vacancies as the main relaxation mechanism. The study of the effect of ion bombardment at different doses and temperature, with Ar, Ne and Kr, in FeNi alloys with 30 e 40 at.% de Ni, indicated a phase separation, for samples bombarded with Ne and Ar, but no evidence of ordering, as in samples irradiated with electrons and neutrons. For bombardment with Kr, we didn't observe any change, but samples already showing a phase separation, returned to the single phase state. Our results give evidences of prevalence of mixing for bombardment with heavy ions, and of radiation enhanced diffusion for bombardment with lighter ions.

A aderência de filmes de diamante depositados por CVD (deposição química a partir da fase vapor) ao metal duro (WC-Co) é de vital importância para a viabilidade da fabricação de ferramentas de corte de alto desempenho com esse tipo de recobrimento. O diamante CVD não é utilizado extensivamente para produção de ferramentas porque a adesão entre o filme e o substrato ainda representa um desafio tecnológico a ser superado. Neste trabalho, após um ataque químico para remover o cobalto da superfície de deposição, pastilhas de metal duro foram recobertas com um filme de diamante CVD usando um reator de plasma ativado por micro-ondas. Estas pastilhas foram posteriormente processadas em alta pressão (7,7 GPa) e altas temperaturas (500 ºC e 1000 ºC). O objetivo foi investigar o efeito desse processamento nas propriedades mecânicas e estruturais das amostras. Para realizar o processamento em alta pressão foi utilizada uma câmara do tipo toroidal em uma prensa hidráulica com capacidade para gerar 1000 toneladas-força. Ensaios de adesão, desgaste abrasivo, testes instrumentados de dureza e ensaios eletroquímicos, aliados a técnicas de análise por espectroscopia Raman, microscopia óptica e microscopia eletrônica de varredura, foram utilizados para avaliar os efeitos desses processamentos sobre as amostras produzidas. Os resultados mostraram um incremento considerável na aderência. Entre os mecanismos que poderiam contribuir para esse efeito, três parecem desempenhar um papel chave em decorrência do efeito do processamento em alta pressão e alta temperatura: (a) a recuperação do substrato na interface, a partir da reinfiltração de cobalto, sem degradação do filme de diamante; (b) o aumento do ancoramento mecânico do filme no substrato; (c) transformações microestruturais no filme associadas a dois fatores: a eliminação de fases carbonáceas fracas retidas na interface de deposição e nos contornos de grão, que podem ser deletérias para a adesão entre filme e substrato e para a coesão entre os grãos de diamante, e o aumento da tenacidade do filme provocado pelo preenchimento de defeitos com cobalto. / The adhesion of CVD diamond film on cemented carbide (WC-Co) substrate plays a key role on the production of diamond coated cutting tools. CVD diamond films are not yet widely used for coating of cutting tools because of the not reliable adhesion between the film and the substrate. Thus, the improvement of the adhesion represents a technological challenge to be achieved. In this work hard metal discs have been coated with a CVD diamond film after a previous chemical etching to remove the cobalt from the surface. After coating these discs were processed at high-pressure (7.7 GPa) and high temperature (500ºC and 1000ºC). The main aim was to investigate the effect of this processing conditions on the mechanical and structural properties of diamond coated cutting tools. The high-pressure processing was performed using toroidal-type high-pressure chambers driven by a 1000 tonf hydraulic press. Adhesion, abrasive wear and corrosion tests as well as Raman spectroscopy, optic and electronic microscopy analyses were performed to investigate the effects of these processing conditions on the samples. The results showed a significant improvement of the film adhesion and reduction of the wear coefficient. Three mechanisms have been identified as the main responsible for this effect related to the high pressure and high temperature processing: (a) the re-sintering of the substrate in the region previously affected by the chemical etching; (b) the increase of the mechanical pinning promoted by the compression of the film in the substrate; (c) the enhancement of the film quality associated to: the elimination of weak carbon phases retained in the deposition interface and grain boundaries that can be deleterious to the film-substrate adhesion and to the cohesion between diamond grains, and the increment of film toughness promoted by the filling of defects with cobalt from the substrate.

A aderência de filmes de diamante depositados por CVD (deposição química a partir da fase vapor) ao metal duro (WC-Co) é de vital importância para a viabilidade da fabricação de ferramentas de corte de alto desempenho com esse tipo de recobrimento. O diamante CVD não é utilizado extensivamente para produção de ferramentas porque a adesão entre o filme e o substrato ainda representa um desafio tecnológico a ser superado. Neste trabalho, após um ataque químico para remover o cobalto da superfície de deposição, pastilhas de metal duro foram recobertas com um filme de diamante CVD usando um reator de plasma ativado por micro-ondas. Estas pastilhas foram posteriormente processadas em alta pressão (7,7 GPa) e altas temperaturas (500 ºC e 1000 ºC). O objetivo foi investigar o efeito desse processamento nas propriedades mecânicas e estruturais das amostras. Para realizar o processamento em alta pressão foi utilizada uma câmara do tipo toroidal em uma prensa hidráulica com capacidade para gerar 1000 toneladas-força. Ensaios de adesão, desgaste abrasivo, testes instrumentados de dureza e ensaios eletroquímicos, aliados a técnicas de análise por espectroscopia Raman, microscopia óptica e microscopia eletrônica de varredura, foram utilizados para avaliar os efeitos desses processamentos sobre as amostras produzidas. Os resultados mostraram um incremento considerável na aderência. Entre os mecanismos que poderiam contribuir para esse efeito, três parecem desempenhar um papel chave em decorrência do efeito do processamento em alta pressão e alta temperatura: (a) a recuperação do substrato na interface, a partir da reinfiltração de cobalto, sem degradação do filme de diamante; (b) o aumento do ancoramento mecânico do filme no substrato; (c) transformações microestruturais no filme associadas a dois fatores: a eliminação de fases carbonáceas fracas retidas na interface de deposição e nos contornos de grão, que podem ser deletérias para a adesão entre filme e substrato e para a coesão entre os grãos de diamante, e o aumento da tenacidade do filme provocado pelo preenchimento de defeitos com cobalto. / The adhesion of CVD diamond film on cemented carbide (WC-Co) substrate plays a key role on the production of diamond coated cutting tools. CVD diamond films are not yet widely used for coating of cutting tools because of the not reliable adhesion between the film and the substrate. Thus, the improvement of the adhesion represents a technological challenge to be achieved. In this work hard metal discs have been coated with a CVD diamond film after a previous chemical etching to remove the cobalt from the surface. After coating these discs were processed at high-pressure (7.7 GPa) and high temperature (500ºC and 1000ºC). The main aim was to investigate the effect of this processing conditions on the mechanical and structural properties of diamond coated cutting tools. The high-pressure processing was performed using toroidal-type high-pressure chambers driven by a 1000 tonf hydraulic press. Adhesion, abrasive wear and corrosion tests as well as Raman spectroscopy, optic and electronic microscopy analyses were performed to investigate the effects of these processing conditions on the samples. The results showed a significant improvement of the film adhesion and reduction of the wear coefficient. Three mechanisms have been identified as the main responsible for this effect related to the high pressure and high temperature processing: (a) the re-sintering of the substrate in the region previously affected by the chemical etching; (b) the increase of the mechanical pinning promoted by the compression of the film in the substrate; (c) the enhancement of the film quality associated to: the elimination of weak carbon phases retained in the deposition interface and grain boundaries that can be deleterious to the film-substrate adhesion and to the cohesion between diamond grains, and the increment of film toughness promoted by the filling of defects with cobalt from the substrate.

Neste trabalho foi estudado o efeito de altas pressões, temperatura e bombardeamento de íons em ligas Invar FeNi. Analisamos os resultados destes diferentes tratamentos, principalmente através das técnicas de Efeito Mõssbauer por transmissão e por elétrons de conversão, medidas de temperatura de Curie e difração de raio-X. A investigação com pressões de até 10 GPa, para diferentes concentrações da liga FeNi, mostrou que a pressão não favorece a ordenação e separação de fases. No estudo da temperatura de Curie de ligas com concentração em torno de 30 at.% de Ni, como função do tempo de recozimento para diferentes temperaturas, observamos um aumento em Tc de mais de 20°C, em temperaturas da ordem de 340°C. A variação de T c com o tempo foi similar à observada em ligas amorfas, sendo interpretada como um rearranjo atômico, numa escala muito pequena. A energia de ativação para o processo foi estimada em torno de 1.5 eV, indicando o movimento de vacâncias congeladas como o principal mecanismo de relaxação. No estudo dos efeitos de bombardeamento com íons de Ar, Ne e Kr, para diferentes doses e temperaturas, em ligas com concentrações em torno de 30 e 40 at.% de Ni, observamos uma separação de fases, para as amostras bombardeadas com Ne e Ar, mas nenhuma evidência de ordenação, como ocorre em amostras irradiadas com elétrons e neutrons. Para o bombardeamento com Kr, não observamos nenhuma mudança, exceto para as amostras que já apresentavam separação de fases, as quais voltaram a seu estado inicial de fase única. Estes resultados indicam que existe uma predominância de mistura para bombardeamento com íons pesados, e de difusão auxiliada por irradiação para íons leves. / We studied in this work the effect of high pressure, temperature and ion bombardment in FeNi Invar alloys. The results of the different treatments were analysed mainly, by Transmission MOssbauer Spectroscopy, Conversion Electron MOssbauer Spectroscopy, measurements of Curie temperature and X-Ray diffraction. The pressure investigation until 10 GPa, for different concentrations of the FeNi alloy, showed that pressure does not favour ordering and phase separation. The study of Curie temperature of alloys near 30 at.% de Ni, as a function of the annealing time at different temperatures showed an increase in Tc of more than 20°C, with annealing at temperatures as low as 340°C. The change in Tc with time was similar to that observed in amorphous alloys, and was interpreted as an atomic rearrangement, in a very small scale. The activation energy for the process was estimated to be about 1.5 eV, indicating movement of quenched-in vacancies as the main relaxation mechanism. The study of the effect of ion bombardment at different doses and temperature, with Ar, Ne and Kr, in FeNi alloys with 30 e 40 at.% de Ni, indicated a phase separation, for samples bombarded with Ne and Ar, but no evidence of ordering, as in samples irradiated with electrons and neutrons. For bombardment with Kr, we didn't observe any change, but samples already showing a phase separation, returned to the single phase state. Our results give evidences of prevalence of mixing for bombardment with heavy ions, and of radiation enhanced diffusion for bombardment with lighter ions.