Advanced materials based on titania nanotubes for the fabrication of high performance 3D li-ion microbatteries. / Matériaux Avancés à Base des nanotubes de TiO2 pour la Fabrication de Microbatteries 3D Li-ionKyeremateng, Nana Amponsah 23 November 2012 (has links)
Le développement des dispositifs microélectroniques a dopé la recherche dans le domaine des microbatteries tout solide rechargeables. Mais actuellement, les performances de ces microbatteries élaborées par des technologies couche mince (2D) sont limitées et le passage à une géométrie 3D adoptant le concept “Li-ion” ou“rocking chair” est incontournable. Cette dernière condition implique de combiner des matériaux de cathode comme LiCoO2, LiMn2O4 or LiFePO4 avec des anodes pouvant réagir de manière réversible avec les ions lithium. Parmi tous les matériaux pouvant servir potentiellement d'anode, les nanotubes de TiO2 révèlent des propriétés intéressantes pour concevoir des microbatteries Li-ion 3D. Facilement réalisable, la nano-architecture auto-organisée a montré des résultats très prometteurs en termes de capacités à des cinétiques relativement modérées. L'utilisation des nanotubes de TiO2 en tant qu'anode conduit à des cellules présentant de faible autodéchargeet élimine le risque de surcharge grâce au haut potentiel de fonctionnement (1.72 V vs. Li+/Li). Dans ce travail de thèse, nous avons étudié la substitution des ions Ti4+ par Sn4+ et Fe2+ dans les nanotubes de TiO2. Bien que la présence d'ions Fe2+ n'ait pas amélioré les performances électrochimiques des nanotubes, nous avons pu mettre en évidence l'effet bénéfique des ions Sn4+. Nous avons aussi pu montré que la fabrication de matériaux composites à base de nanotubes de TiO2 et d'oxyde de métaux de transition électrodéposés se présentant sous forme de particules (NiO et Co3O4 ) augmentait les capacités d'un facteur 4. / The advent of modern microelectronic devices has necessitated the search for high-performance all-solid-state (rechargeable) microbatteries. So far, only lithium-based systems fulfill the voltage and energy density requirements of microbatteries. Presently, there is a need to move from 2D to 3D configurations, and also a necessity to adopt the “Li-ion” or the “rocking-chair” concept in designing these lithium-based (thin-film) microbatteries. This implies the combination of cathode materials such as LiCoO2, LiMn2O4 or LiFePO4 with the wide range of possible anode materials that can react reversibly with lithium. Among all the potential anode materials, TiO2 nanotubes possess a spectacular characteristic for designing 3D Li-ion microbatteries. Besides the self-organized nano-architecture, TiO2 is non-toxic and inexpensive, and the nanotubes have been demonstrated to exhibit very good capacity retention particularly at moderate kinetic rates. The use of TiO2 as anode provides cells with low self-discharge and eliminates the risk of overcharging due to its higher operating voltage (ca. 1.72 V vs. Li+/Li). Moreover, their overall performance can be improved. Hence, TiO2 nanotubes and their derivatives were synthesized and characterized, and their electrochemical behaviour versus lithium was evaluated in lithium test cells. As a first step towards the fabrication of a 3D microbattery based on TiO2 nanotubes, electrodeposition of polymer electrolytes into the synthesized TiO2 nanotubes was also studied; the inter-phase morphology and the electrochemical behaviour of the resulting material were studied.
|
2 |
The Development of Ni1-x-yCuxMgyO-SDC Anode for Intermediate Temperature Solid Oxide Fuel Cells (IT-SOFCs)Monrudee, Phongaksorn January 2010 (has links)
Solid oxide fuel cells (SOFCs) conventionally operate between 800 and 1000°C. The barriers for full-scale commercialization of SOFCs are the high cost and relatively poor long-term stability due to the high temperatures used in current state-of-the-art SOFCs. One solution is to decrease the operating temperature, e.g. to 550-750°C but this requires developing new electrolytes and electrode materials. Also, to increase efficiency and practicality, the anode should be able to internally reform hydrocarbon fuels especially methane because it is the most common hydrocarbon in natural gas.
The overall goal of this research is to develop a coke-tolerant Ni1-x-yCuxMgyO-SDC anode for methane fuelled IT-SOFCs. The Ni-Cu-Mg-O-SDC anode has been chosen based on the premises that doped-ceria is suitable for intermediate operating temperatures (550-800°C), Ni is known as an active metal and good electronic conductor, Cu increases resistance to coking, MgO helps prevent agglomeration of Ni during reduction, and finally SDC improves oxide ion transport to the cell at this intermediate temperature range. In this work, these materials were characterized in three primary ways: material physical and chemical properties, methane steam reforming activity and electrochemical performance.
Two different methods have been used to add Cu to Ni1-yMgyO: a one-step co-precipitation method and a two-step co-precipitation/impregnation method. For the first method, Ni1-x-yCuxMgyO was synthesized via co-precipitation of Ni, Mg and Cu. In the two-step method, Ni0.9Mg0.1O was first prepared by co-precipitation, followed by addition of copper to Ni0.9Mg0.1O by impregnation. However, co-precipitation of all metal in one step limits the sintering temperature of the anode in the cell fabrication due to the low boiling point of CuO. Therefore, co-precipitation of Cu is not a practical method and only Cu impregnation should be considered for practical SOFC applications.
It was found that the addition of Mg (Ni0.9Mg0.1O) lowers the reducibility of NiO. Addition of Cu to Ni0.9Mg0.1O up to 5% shows similar reducibility as Ni0.9Mg0.1O. The reducibility of Ni1-x-yCuxMgyO becomes lower when the Cu content is increased to 10%. Nonetheless, all materials are fully reduced at 750ºC. The XRD patterns of pure NiO, Ni0.9Mg0.1O, and the Cu-containing material when Cu is less than 10 mol% are similar. The lower reducibility of Ni-Mg-O and Ni-Cu-Mg-O compared to NiO indicates that they form a solid solution with NiO as the matrix.
Solid oxide fuel cells (SOFCs) conventionally operate between 800 and 1000°C. The barriers for full-scale commercialization of SOFCs are the high cost and relatively poor long-term stability due to the high temperatures used in current state-of-the-art SOFCs. One solution is to decrease the operating temperature, e.g. to 550-750°C but this requires developing new electrolytes and electrode materials. Also, to increase efficiency and practicality, the anode should be able to internally reform hydrocarbon fuels especially methane because it is the most common hydrocarbon in natural gas.
The overall goal of this research is to develop a coke-tolerant Ni1-x-yCuxMgyO-SDC anode for methane fuelled IT-SOFCs. The Ni-Cu-Mg-O-SDC anode has been chosen based on the premises that doped-ceria is suitable for intermediate operating temperatures (550-800°C), Ni is known as an active metal and good electronic conductor, Cu increases resistance to coking, MgO helps prevent agglomeration of Ni during reduction, and finally SDC improves oxide ion transport to the cell at this intermediate temperature range. In this work, these materials were characterized in three primary ways: material physical and chemical properties, methane steam reforming activity and electrochemical performance.
Two different methods have been used to add Cu to Ni1-yMgyO: a one-step co-precipitation method and a two-step co-precipitation/impregnation method. For the first method, Ni1-x-yCuxMgyO was synthesized via co-precipitation of Ni, Mg and Cu. In the two-step method, Ni0.9Mg0.1O was first prepared by co-precipitation, followed by addition of copper to Ni0.9Mg0.1O by impregnation. However, co-precipitation of all metal in one step limits the sintering temperature of the anode in the cell fabrication due to the low boiling point of CuO. Therefore, co-precipitation of Cu is not a practical method and only Cu impregnation should be considered for practical SOFC applications.
It was found that the addition of Mg (Ni0.9Mg0.1O) lowers the reducibility of NiO. Addition of Cu to Ni0.9Mg0.1O up to 5% shows similar reducibility as Ni0.9Mg0.1O. The reducibility of Ni1-x-yCuxMgyO becomes lower when the Cu content is increased to 10%. Nonetheless, all materials are fully reduced at 750ºC. The XRD patterns of pure NiO, Ni0.9Mg0.1O, and the Cu-containing material when Cu is less than 10 mol% are similar. The lower reducibility of Ni-Mg-O and Ni-Cu-Mg-O compared to NiO indicates that they form a solid solution with NiO as the matrix.
Addition of Mg also lowers the BET specific surface area from 11.5 m2/g for NiO:SDC to 10.4 m2/g for Ni0.9Mg0.1O. The surface area is further reduced when Cu is added; for example, at 10% Cu, the surface area is 8.2 m2/g.
The activity of 50wt% Ni1-x-yCuxMgyO/50wt% SDC samples for methane steam reforming (SMR) and water-gas-shift reaction (WGS) was evaluated in a fully automated catalytic fixed-bed reactor where the exiting gases were analyzed online by a gas chromatograph (GC). The tests were performed at steam-to-carbon ratios (S/C) of 3, 2 and 1, and at temperatures of 750°C and 650°C for twenty hours. Higher methane conversions were obtained at the higher temperature and higher S/C ratio.
Higher methane conversion are obtained using NiO:SDC and Ni0.9Mg0.1O:SDC than Ni-Cu-Mg-O. The conversion decreases with increasing Cu content. Over NiO:SDC and Ni0.9Mg0.1O:SDC the methane conversions are the same; for example 85% at 750°C for S/C of 3. At the same conditions, impregnation of 5%Cu and 10%Cu yields lower conversions: 62% and 48%, respectively.
The activity for the WGS reaction was determined by mornitoring CO2/(CO+CO2) ratio. As expected because WGS is a moderately exothermic reaction, this ratio decreases when increasing the temperature. However, the CO2/(CO+CO2) ratio increases with higher S/C. The results indicate that adding Mg does not affect the WGS activity of NiO. The WGS activity of Ni0.9Mg0.1O:SDC is higher when Cu is added. The effect of additional Cu is more pronounced at 650ºC. At 750°C, changing the amount of Cu does not change the WGS activity because the WGS reaction rapidly reaches equilibrium at this high temperature.
At 750°C for S/C of 1, carbon filaments were found in all samples. At 650ºC, different types of deposited carbon were observed: carbon fibers and thin graphite layers. Spent NiO:SDC had the longest carbon fibers. Addition of Mg significantly reduced the formation of carbon fibers. Impregnating 5% Cu on Ni0.9Mg0.1O:SDC did not change the type of deposited carbon. Monitoring the amount of deposited carbon on Ni0.9Mg0.1O:SDC, 3%Cu and 5%Cu impregnated on Ni0.9Mg0.1O:SDC for S/C of 0 at 750ºC showed that Cu addition deactivated methane cracking causing a reduction in the amount of carbon deposited.
Electrochemical performance in the presence of dry and humidified hydrogen was determined at 600, 650, 700 and 750ºC. Electrolyte-supported cells constructed with four different anodes were tested using polarization curve and electrochemical impedance spectra. The four anodes were NiO:SDC, Ni0.9Mg0.1O:SDC, 3%Cu and 5%Cu on Ni0.9Mg0.1O:SDC. Adding Mg improved the maximum power density from 356 mW.cm-2 with NiO:SDC to 369 mW.cm-2 with Ni0.9Mg0.1O:SDC at 750ºC in dry hydrogen. Addition of Cu, on the other hand, lowered the maximum power density to 325 mW.cm-2 with 3%Cu impregnated and to 303 mW.cm-2 with 5% Cu impregnated.
The cell with Ni0.9Mg0.1O:SDC was also tested under dry methane. To minimize methane cracking under this extreme condition, a current density of 0.10 A.cm-2 was always drawn when methane was present in the feed. The voltage decreased during the first hour from 0.8 to 0.5 V, then remained stable for 10 hours, and then started to drop again. Many small cracks were observed on the anode after completion of the electrochemical test, but there was no evidence of much carbon being deposited. In addition to dry methane, tests were also carried out, using the same material, with a H2O/CH4 mixture of 1/6 in order to generate a polarization curve at 750°C. Under these conditions, the maximum power density was 226 mW.cm-2. This is lower than the maximum power density obtained with humidified hydrogen, which was 362 mW.cm-2.
|
3 |
Mild Preparation of Anode Materials for Lithim Ion Batteries: from Gas-Phase Oxidation to Salt-free Green MethodHolze, Rudolf, Wu, Yuping 27 November 2009 (has links) (PDF)
Natural graphite from cheap and abundant natural sources is an attractive anode material for lithium ion batteries. We report on modifications of such a common natural graphite, whose electrochemical performance is very poor, with solutions of (NH4)2S2O8, concentrated nitric acid, and green chemical solutions such of e.g. hydrogen peroxide and ceric sulfate. These treatments resulted in markedly im-proved electrochemical performance (reversible capacity, coulombic efficiency in the first cycle and cycling behavior). This is attributed to the effective removal of active defects, formation of a new dense surface film consisting of oxides, improvement of the graphite stability, and introduction of more nanochannels/micropores. These changes inhibit the decomposition of electrolyte solution, pre-vent the movement of graphene planes along a-axis direction, and provide more passage and storage sites for lithium. The methods are mild, and the uniformity of the product can be well controlled. Pilot experiments show promising results for their application in industry.
|
4 |
The Development of Ni1-x-yCuxMgyO-SDC Anode for Intermediate Temperature Solid Oxide Fuel Cells (IT-SOFCs)Monrudee, Phongaksorn January 2010 (has links)
Solid oxide fuel cells (SOFCs) conventionally operate between 800 and 1000°C. The barriers for full-scale commercialization of SOFCs are the high cost and relatively poor long-term stability due to the high temperatures used in current state-of-the-art SOFCs. One solution is to decrease the operating temperature, e.g. to 550-750°C but this requires developing new electrolytes and electrode materials. Also, to increase efficiency and practicality, the anode should be able to internally reform hydrocarbon fuels especially methane because it is the most common hydrocarbon in natural gas.
The overall goal of this research is to develop a coke-tolerant Ni1-x-yCuxMgyO-SDC anode for methane fuelled IT-SOFCs. The Ni-Cu-Mg-O-SDC anode has been chosen based on the premises that doped-ceria is suitable for intermediate operating temperatures (550-800°C), Ni is known as an active metal and good electronic conductor, Cu increases resistance to coking, MgO helps prevent agglomeration of Ni during reduction, and finally SDC improves oxide ion transport to the cell at this intermediate temperature range. In this work, these materials were characterized in three primary ways: material physical and chemical properties, methane steam reforming activity and electrochemical performance.
Two different methods have been used to add Cu to Ni1-yMgyO: a one-step co-precipitation method and a two-step co-precipitation/impregnation method. For the first method, Ni1-x-yCuxMgyO was synthesized via co-precipitation of Ni, Mg and Cu. In the two-step method, Ni0.9Mg0.1O was first prepared by co-precipitation, followed by addition of copper to Ni0.9Mg0.1O by impregnation. However, co-precipitation of all metal in one step limits the sintering temperature of the anode in the cell fabrication due to the low boiling point of CuO. Therefore, co-precipitation of Cu is not a practical method and only Cu impregnation should be considered for practical SOFC applications.
It was found that the addition of Mg (Ni0.9Mg0.1O) lowers the reducibility of NiO. Addition of Cu to Ni0.9Mg0.1O up to 5% shows similar reducibility as Ni0.9Mg0.1O. The reducibility of Ni1-x-yCuxMgyO becomes lower when the Cu content is increased to 10%. Nonetheless, all materials are fully reduced at 750ºC. The XRD patterns of pure NiO, Ni0.9Mg0.1O, and the Cu-containing material when Cu is less than 10 mol% are similar. The lower reducibility of Ni-Mg-O and Ni-Cu-Mg-O compared to NiO indicates that they form a solid solution with NiO as the matrix.
Solid oxide fuel cells (SOFCs) conventionally operate between 800 and 1000°C. The barriers for full-scale commercialization of SOFCs are the high cost and relatively poor long-term stability due to the high temperatures used in current state-of-the-art SOFCs. One solution is to decrease the operating temperature, e.g. to 550-750°C but this requires developing new electrolytes and electrode materials. Also, to increase efficiency and practicality, the anode should be able to internally reform hydrocarbon fuels especially methane because it is the most common hydrocarbon in natural gas.
The overall goal of this research is to develop a coke-tolerant Ni1-x-yCuxMgyO-SDC anode for methane fuelled IT-SOFCs. The Ni-Cu-Mg-O-SDC anode has been chosen based on the premises that doped-ceria is suitable for intermediate operating temperatures (550-800°C), Ni is known as an active metal and good electronic conductor, Cu increases resistance to coking, MgO helps prevent agglomeration of Ni during reduction, and finally SDC improves oxide ion transport to the cell at this intermediate temperature range. In this work, these materials were characterized in three primary ways: material physical and chemical properties, methane steam reforming activity and electrochemical performance.
Two different methods have been used to add Cu to Ni1-yMgyO: a one-step co-precipitation method and a two-step co-precipitation/impregnation method. For the first method, Ni1-x-yCuxMgyO was synthesized via co-precipitation of Ni, Mg and Cu. In the two-step method, Ni0.9Mg0.1O was first prepared by co-precipitation, followed by addition of copper to Ni0.9Mg0.1O by impregnation. However, co-precipitation of all metal in one step limits the sintering temperature of the anode in the cell fabrication due to the low boiling point of CuO. Therefore, co-precipitation of Cu is not a practical method and only Cu impregnation should be considered for practical SOFC applications.
It was found that the addition of Mg (Ni0.9Mg0.1O) lowers the reducibility of NiO. Addition of Cu to Ni0.9Mg0.1O up to 5% shows similar reducibility as Ni0.9Mg0.1O. The reducibility of Ni1-x-yCuxMgyO becomes lower when the Cu content is increased to 10%. Nonetheless, all materials are fully reduced at 750ºC. The XRD patterns of pure NiO, Ni0.9Mg0.1O, and the Cu-containing material when Cu is less than 10 mol% are similar. The lower reducibility of Ni-Mg-O and Ni-Cu-Mg-O compared to NiO indicates that they form a solid solution with NiO as the matrix.
Addition of Mg also lowers the BET specific surface area from 11.5 m2/g for NiO:SDC to 10.4 m2/g for Ni0.9Mg0.1O. The surface area is further reduced when Cu is added; for example, at 10% Cu, the surface area is 8.2 m2/g.
The activity of 50wt% Ni1-x-yCuxMgyO/50wt% SDC samples for methane steam reforming (SMR) and water-gas-shift reaction (WGS) was evaluated in a fully automated catalytic fixed-bed reactor where the exiting gases were analyzed online by a gas chromatograph (GC). The tests were performed at steam-to-carbon ratios (S/C) of 3, 2 and 1, and at temperatures of 750°C and 650°C for twenty hours. Higher methane conversions were obtained at the higher temperature and higher S/C ratio.
Higher methane conversion are obtained using NiO:SDC and Ni0.9Mg0.1O:SDC than Ni-Cu-Mg-O. The conversion decreases with increasing Cu content. Over NiO:SDC and Ni0.9Mg0.1O:SDC the methane conversions are the same; for example 85% at 750°C for S/C of 3. At the same conditions, impregnation of 5%Cu and 10%Cu yields lower conversions: 62% and 48%, respectively.
The activity for the WGS reaction was determined by mornitoring CO2/(CO+CO2) ratio. As expected because WGS is a moderately exothermic reaction, this ratio decreases when increasing the temperature. However, the CO2/(CO+CO2) ratio increases with higher S/C. The results indicate that adding Mg does not affect the WGS activity of NiO. The WGS activity of Ni0.9Mg0.1O:SDC is higher when Cu is added. The effect of additional Cu is more pronounced at 650ºC. At 750°C, changing the amount of Cu does not change the WGS activity because the WGS reaction rapidly reaches equilibrium at this high temperature.
At 750°C for S/C of 1, carbon filaments were found in all samples. At 650ºC, different types of deposited carbon were observed: carbon fibers and thin graphite layers. Spent NiO:SDC had the longest carbon fibers. Addition of Mg significantly reduced the formation of carbon fibers. Impregnating 5% Cu on Ni0.9Mg0.1O:SDC did not change the type of deposited carbon. Monitoring the amount of deposited carbon on Ni0.9Mg0.1O:SDC, 3%Cu and 5%Cu impregnated on Ni0.9Mg0.1O:SDC for S/C of 0 at 750ºC showed that Cu addition deactivated methane cracking causing a reduction in the amount of carbon deposited.
Electrochemical performance in the presence of dry and humidified hydrogen was determined at 600, 650, 700 and 750ºC. Electrolyte-supported cells constructed with four different anodes were tested using polarization curve and electrochemical impedance spectra. The four anodes were NiO:SDC, Ni0.9Mg0.1O:SDC, 3%Cu and 5%Cu on Ni0.9Mg0.1O:SDC. Adding Mg improved the maximum power density from 356 mW.cm-2 with NiO:SDC to 369 mW.cm-2 with Ni0.9Mg0.1O:SDC at 750ºC in dry hydrogen. Addition of Cu, on the other hand, lowered the maximum power density to 325 mW.cm-2 with 3%Cu impregnated and to 303 mW.cm-2 with 5% Cu impregnated.
The cell with Ni0.9Mg0.1O:SDC was also tested under dry methane. To minimize methane cracking under this extreme condition, a current density of 0.10 A.cm-2 was always drawn when methane was present in the feed. The voltage decreased during the first hour from 0.8 to 0.5 V, then remained stable for 10 hours, and then started to drop again. Many small cracks were observed on the anode after completion of the electrochemical test, but there was no evidence of much carbon being deposited. In addition to dry methane, tests were also carried out, using the same material, with a H2O/CH4 mixture of 1/6 in order to generate a polarization curve at 750°C. Under these conditions, the maximum power density was 226 mW.cm-2. This is lower than the maximum power density obtained with humidified hydrogen, which was 362 mW.cm-2.
|
5 |
Development and characterisation of an A-site deficient perovskite as alternative anode material for solid oxide fuel cellsAljaberi, Ahmed D. A. January 2013 (has links)
The research presented in this thesis is a collection of many different, yet connected, parts that stemmed from the development of a new alternative material intended to be utilised as anode material in solid oxide fuel cells. The main part is the research conducted in the development and characterisation of the novel A-site deficient La₀.2₂Sr₀.₇₋ₓCaₓTiO₃. Calcium introduction resulted in reducing this perovskite unit cell volume which, at the beginning, enhanced its electrical conductivity in reducing conditions. However, the ideal cubic symmetry coud not be maintained, as in the starting material LA₀.₂Sr₀.₇TiO₃, as a result of the increased A-site ionic radius mismatch and two lower symmetries were observed at room temperature. These were the tetragonal I4/mcm for 0.1 ≤ x ≤ 0.35 and orthorhombic Pbnm for 0.4 ≤ x ≤ 0.7. Higher temperature NPD data showed that the orthorhombic samples transformed into higher symmetries with Pbnm → I4/mcm → Pm3-m phase transitions. Detailed crystallographic analysis is discussed; where the different unit cells showed changes to the tilts of the BO₆ octahedra, along with distortions to these octahedra. DC conductivity measurements showed a high electrical conductivity of 27.5 S/cm for a pre-reduced composition La₀.₂Sr₀.₂₅Ca₀.₄₅TiO₃ at 900°C and pO₂ = 10⁻¹⁹ atm. This material showed very encouraging features; which makes it a very promising anode material for SOFCs. A study was also done which explores the best renewable energy options for the United Arab Emirates given its local climate and other aspects. The reliance on seawater desalination is argued to by unsustainable for different reasons. Thus, water security should be a main element in the planning process for adopting renewable energy technologies. A system that combines different technologies; with a focus on fuel cells technology; is outlined which is thought of to be a very promising basis for a broader system that will secure power and water in a very environment friendly way. Different compositions of the system La₀.₂Sr₀.₇₋ₓCaₓTiO₃ were also studied using AC impedance spectroscopy in order to establish whether or not this system can show a ferroelectric behaviour. Results showed a variation in the dielectric constant of different samples with temperature; however, no Curie point was observed. Nonetheless, the results did show that the different compositions were very homogeneous when fully oxygenated and there were some indications of possible symmetry changes at sub-ambient temperatures. The final part of this thesis outlined the work done towards the development of a new analytical instrument. An existing TGA instrument was altered in order to provide a simultaneous thermogravimetric analysis and DC conductivity measurement for solid solutions at controlled temperature and oxygen partial pressure. Results were obtained for different samples of the system La₀.₂Sr₀.₇₋ₓCaₓTiO₃ which showed a great dependence of the electrical conductivity on the oxygen stoichiometry in these oxides. Also, a direct method is possible with this instrument to estimate the oxygen chemical diffusion coefficient using the electrical conductivity relaxation method. This new setup will be very useful for different electrochemical and thermal studies which can broaden the understanding of the different mechanisms that affect the performance of different solid state materials.
|
6 |
Mild Preparation of Anode Materials for Lithim Ion Batteries: from Gas-Phase Oxidation to Salt-free Green MethodHolze, Rudolf, Wu, Yuping 27 November 2009 (has links)
Natural graphite from cheap and abundant natural sources is an attractive anode material for lithium ion batteries. We report on modifications of such a common natural graphite, whose electrochemical performance is very poor, with solutions of (NH4)2S2O8, concentrated nitric acid, and green chemical solutions such of e.g. hydrogen peroxide and ceric sulfate. These treatments resulted in markedly im-proved electrochemical performance (reversible capacity, coulombic efficiency in the first cycle and cycling behavior). This is attributed to the effective removal of active defects, formation of a new dense surface film consisting of oxides, improvement of the graphite stability, and introduction of more nanochannels/micropores. These changes inhibit the decomposition of electrolyte solution, pre-vent the movement of graphene planes along a-axis direction, and provide more passage and storage sites for lithium. The methods are mild, and the uniformity of the product can be well controlled. Pilot experiments show promising results for their application in industry.
|
7 |
Synthèse et caractérisations électrochimiques de nouveaux matériaux pour anodes d'électrolyseurs à haute température / Synthesis and electrochemical characterizations of new materials for high temperature electrolyser anodesChauveau, Florent 15 December 2009 (has links)
L’électrolyse de la vapeur d’eau à haute température (EHT) est une voie permettant de produire de l’hydrogène d’une grande pureté et avec un fort rendement, ceci sans émission de CO2. Un des verrous actuels de cette technologie est la forte surtension associée à la réaction d’oxydation des ions O2- qui se déroule à l’électrode à oxygène (anode). L’objectif de ce travail était de concevoir de nouveaux matériaux d’anode possédant des propriétés de conductivité mixte (i.e. électronique et ionique), dans le but d’obtenir des surfaces de réaction plus importantes afin de diminuer cette surtension. A cet effet, une étude comparative a été réalisée sur huit oxydes (ferrites et nickelates de terres rares). Après synthèse et mise en forme, ces matériaux ont fait l’objet de caractérisations physico-chimiques puis électrochimiques en demi-cellules symétriques sous atmosphère unique afin de déterminer ceux présentant les meilleures propriétés sous courant nul et sous polarisation anodique. Quatre composés de structure dérivée de type K2NiF4 ont ainsi été sélectionnés pour être caractérisés de façon plus approfondie en cellules complètes à électrolyte support en conditions EHT (750 - 850°C). Il a ainsi été possible d’obtenir, pour une tension de cellule de 1,3 V une densité de courant de 0,9 A/cm² à 850°C, soit près de deux fois plus qu’avec une cellule identique comportant comme matériau d’anode un composite commercial optimisé à base de LaMnO3 substitué au strontium. / High temperature steam electrolysis (HTSE) is a way to produce hydrogen with a high purity, with noteworthy efficiency and without CO2 emission. Nowadays, a blocking point concerning this technology is the high overvoltage related to the oxidation of the O2- ions occurring at the oxygen electrode (anode). The aim of this work was to design new anode materials with mixed conducting properties (i.e. electronic and ionic), in order to obtain larger reaction areas and to lessen this overvoltage. In this aim, eight compounds (ferrites and rare earth nickelates) were investigated. After synthesis and shaping, these compounds were characterized using physical, chemical and electrochemical analyses in symmetrical half cells, under single atmosphere, in order to determine which ones have the best properties under zero current and under anodic polarization. Four compounds of structure derived from K2NiF4-type were then selected to be more accurately characterized in complete electrolyte supported cells, under HTSE conditions (750 - 850°C). It was then possible to obtain, for a 1.3 V cell voltage, a current density of 0.9 A/cm² at 850°C, which is nearly two times larger than the one obtained with a same cell including a commercial composite material based on strontium substituted LaMnO3 as anode.
|
8 |
Studie vlastností pokročilých materiálů pro katody lithno-iontových akumulátorů / Study of the properties of the advanced materials for the cathodes of the lithium-ion accumulatorsPustowka, Pavel January 2016 (has links)
This thesis in its first part deals especially with characteristic of lithium ion accumulators in terms of their structure, electrochemical properties and also features of the most commonly used cathode materials. Especial attention is given to the high-voltage cathode material LiNi0,5Mn1,5O4 which cell voltage is close to 5V. The second practical part deals with the preparation of cathode materials based on LiNi0,5Mn1,5O4 with different temperatures in the second stage of annealing and analyzing them in terms of structure and electrochemical properties using appropriate measuring methods.
|
9 |
A Lithium-ion Test Cell for Characterization of Electrode Materials and Solid Electrolyte InterphaseGoel, Ekta 03 May 2008 (has links)
The research discussed is divided into two parts. The first part discusses the background work involved in preparation of the Li-ion cell testing stage. This includes the preparation of anodes using the doctor blade and a calendar mill, electrolyte preparation, test cell assembly, the Li-ion test cell design, and experiments performed to troubleshoot the cell. The second part deals with the cell testing experiments. Li-ion batteries are amongst the most promising rechargeable battery technology because of their high capacity and low weight. Current research aims at improving the anode quality to increase the capacity. The experiments discussed evaluate the traditional anode materials like SFG44 graphite and conducting grade graphite against the novel ones– and tin oxide (SnO2) based and carbon encapsulated tin based anodes. The solid electrolyte interphase formed on each anode was analyzed to understand the initial capacity fade leading to conditioning of the cell thus stabilizing its performance.
|