Yes / Poly(vinyl alcohol) (PVA)/graphene oxide (GO) nanocomposite hydrogel as artificial cartilage replacement was prepared via freezing/thawing method by introducing polyethylene glycol (PEG). Efficient grafting of PVA molecules onto GO surface was realized by formation of hydrogen bonding, resulting in exfoliation and uniform distribution of GO in PVA matrix. By introduction of appropriate content of GO, the increased crystalline regions of PVA and the formation of GO centered second network structure led to the increase of the storage modulus and effective cross-linking density. And therefore the mechanical strength and toughness of the composite hydrogel were improved simultaneously: the tensile strength, elongation at break, and compressive modulus showed approximately 200%, 40%, and 100% increase of the neat PVA hydrogel. Besides, for the sample with 1.5 wt % GO content, the maximum force retention and dynamic stiffness were improved remarkably in the process of sinusoidal cyclic compression, and the compressive relaxation stress also increased significantly, indicating the enhancement of the compressive recoverable and antifatigue ability, and resistance to compressive relaxation by formation of high load-bearing, dense, and reinforcing double network structure. Moreover, more than 50% decrease in coefficient of friction was obtained for the composite hydrogel, and the worn surface presented relative smooth and flat features with sharp decreasing furrow depth, confirming the lubrication effect of GO-PEG. This study shows promising potentials in developing new materials for cartilage replacement with simultaneous combination of high mechanical property and excellent lubrication.

Biodegradable hydrogels have become very promising materials for a number of biomedical applications, including tissue engineering and drug delivery. For optimal tissue engineering design, the mechanical properties of hydrogels should match those of native tissues as closely as possible because these properties are known to affect the behavior and function of cells seeded in the hydrogels. At the same time, high water-contents, large mesh sizes and well-tuned degradation rates are favorable for the controlled release of growth factors and for adequate transport of nutrients through the hydrogel during tissue regeneration. With these factors in mind, the goal of this research was to develop and investigate the behavior of injectable, biodegradable hydrogels with enhanced stiffness properties that persist even at high degrees of swelling. In order to do this, degradable functionalities were incorporated into photo-crosslinkable poly(ethylene glycol) and poly(acrylic acid) hydrogels, and these two components were used to make a series of double-network hydrogels. Synthesis of the precursor macromers, photopolymerization of the hydrogels, and structural parameters of the hydrogels were analyzed. The composition and the molecular weight between crosslinks (Mc) of the hydrogel components were varied, and the degradation, swelling, thermal and mechanical properties of the hydrogels were characterized over various time scales. These properties were compared to corresponding properties of the component single-network hydrogels.