Introduction: The aim of this study was to evaluate some of the physico-chemical properties of a new root canal sealer. Methodology: The sealers tested were Sealer Plus (MKLife, Porto Alegre, Rio Grande do Sul, Brazil), compared as AH Plus (Dentsply, DeTrey GmbH, Konstanz, Alemanha). For the radiopacity, flow, solubility and fabrication of test specimens relative to setting times the ANSI/ADA No. 57 (2000) and ISO 6876 (2012) specifications were followed. To measure the initial and final setting times the ASTM C266/2008 standard was used. pH was evaluated in the time intervals of 3, 24, 72 and 168 hours). Statistical tests were applied to the results obtained at a level of significance of 5%. Results: The results demonstrated that the Sealer Plus sealer showed a lower radiopacity value than AH Plus sealer (p<0.05), however, this was higher than the minimum value recommended by the specifications; that is 3 mm Al. Relative to flow, the value for Sealer Plus was 19.19 mm and for AH Plus, 19.81 mm (p>0.05). Sealer plus presented initial and final setting times of 138 min. and 210 min., respectively, while the values for AH Plus were 437 min. and 849 min., respectively, (p<0.05). Relative to solubility, Sealer Plus presented 0.21% and AH Plus, 0.27% (p>0.05). None of the sealers showed a significant increase in pH (p>0.05). Conclusion: Sealer Plus sealer presented physico-chemical properties in accordance with ANSI/ADA (2000) No.57 and ISO 6876 (2012) specifications. / Introdução: Este estudo objetivou avaliar algumas propriedades físico-químicas de um novo cimento obturador de canais radiculares. Metodologia: Para os testes de radiopacidade, escoamento, solubilidade e confecção dos corpos de prova para os tempos de presa foram seguidas as especificações nº57 da ANSI/ADA (2000) e ISO 6876 (2012). Para a medição dos tempos de presa, inicial e final, foi empregada a norma ASTM C266/2008. O pH foi avaliado nos períodos de 3, 24, 72 e 168 horas. Sobre os resultados foram aplicados testes estatísticos com nível de significância de 5%. Resultados: Os resultados demonstraram que o cimento Sealer Plus apresentou menor radiopacidade do que o cimento AH Plus (p<0.05), porém, superior ao mínimo recomendado pelas especificações, ou seja, de 3 mm de Al. Com relação ao escoamento, o do Sealer Plus foi 19,19 mm e do AH Plus 19,81 mm (p>0.05). O Sealer Plus apresentou tempos de presa inicial e final de 138 min. e 210 min., respectivamente, enquanto o AH Plus, 437 min. e 849 min., respectivamente, (p<0.05). Em relação à solubilidade, o Sealer Plus apresentou 0,21% e o AH Plus 0,27% (p>0.05). Nenhum dos cimentos apresentou aumento significativo do pH (p>0.05). Conclusão: O cimento Sealer Plus apresentou propriedades físico-químicas de acordo com as especificações nº 57 da ANSI/ADA (2000) e ISO 6876 (2012).

O agregado de trióxido mineral (MTA) tem-se demonstrado aplicável em diversas situações que exigem reparação dos tecidos dentais e periapicais. Contudo, desvantagens relacionadas ao seu elevado custo, propriedades físico-químicas e dificuldade de manuseio têm limitado sua utilização. Neste sentido, um novo cimento de aluminato de cálcio e aditivos (CAC+) foi desenvolvido para superar algumas características negativas do MTA, mantendo, no entanto, suas propriedades satisfatórias. O objetivo deste estudo foi avaliar a progressão de culturas de células osteogênicas e de células indiferenciadas da polpa dental (linhagem OD-21) expostas ao CAC+, utilizando MTA como controle, ou a preparações alternativas do CAC+, com maior conteúdo de cloreto de cálcio (CaCl2) e/ou com substituição do óxido de zinco por óxido de bismuto como radiopacificador. Para isso, células osteogênicas derivadas de calvárias de ratos ou células da linhagem OD-21 foram crescidas sobre Thermanox® por 24 h e expostas, por períodos de até 14 dias, a amostras dos diferentes materiais, posicionadas sobre Transwell®. Em células osteogênicas, apesar de a proximidade com as amostras de CAC+ e MTA inibir o crescimento celular, nas áreas periféricas das lamínulas, foram observados proliferação, viabilidade celular e expressão de marcadores-chave da diferenciação osteoblástica, que precederam a mineralização da matriz extracelular. Culturas expostas ao CAC+, comparativamente ao MTA, exibiram aumentos na viabilidade celular, atividade de fosfatase alcalina e na expressão de marcadores de diferenciação, o que não se repetiu para células OD-21. Além disso, demonstrou-se que os efeitos destes cimentos sobre a osteogênese in vitro variaram de acordo com o período de exposição das culturas, sendo mais favoráveis durante sua fase proliferativa. Entre as preparações de CAC+, verificou-se que o aumento no teor de CaCl2 promoveu maior disponibilização de Ca2+ no meio de cultura, o que correspondeu a maior diferenciação celular e formação de matriz mineralizada em culturas de células osteogênicas e OD-21, e à redução de efeitos negativos da adição de óxido de bismuto sobre osteoblastos. Conclui-se que o CAC+ favorece o desenvolvimento do fenótipo osteogênico, atuando principalmente em células em estágios iniciais de diferenciação e que a adição de CaCl2, independentemente do agente radiopacificador, potencializa os efeitos benéficos sobre células osteogênicas e favorece o desenvolvimento e diferenciação de células indiferenciadas derivadas do tecido pulpar, podendo ser considerado como material alternativo ao MTA. / Mineral trioxide aggregate (MTA) has been successfully applied in endodontic procedures in which dental and periapical tissue repair are required. However, some drawbacks of MTA as high cost, physicochemical properties and difficulty in handling have limited its use. In this context, a novel calcium aluminate cement plus additives (CAC+) has been developed to overcome some negative features of MTA. The aim of this study was to evaluate the progression of either osteogenic cell cultures or undifferentiated dental pulp-derived ones (OD-21 cell line) exposed to CAC+ or to alternative formulations of CAC+ with a higher content of calcium chloride (CaCl2) and/or replacement of zinc oxide by bismuth oxide as radiopacifier agent. Rat calvaria-derived cells or OD-21 cells were grown on Thermanox® coverslips for 24 h and exposed to samples of CAC+ or MTA (control) placed on Transwell® for periods of up to 14 days. In osteogenic cell cultures, the proximity to MTA or CAC+ samples inhibited cell growth, whereas at distance it was observed cell proliferation, cell viability and expression of differentition markers prior to mineralization of the extracellular matrix. Comparatively to MTA, osteogenic cell cultures exposed to CAC+ exhibited higher cell viability, alkaline phosphatase activity and expression of key osteoblast markers, contrary to what was observed for OD-21 cells. Furthermore, it was demonstrated that the effects of these cements on in vitro osteogenesis varied according to the timing of exposure, with a more favorable impact during the proliferative phase of cultures. Among the diverse formulations of CAC+, it was found that the increase in the CaCl2 content promoted greater availability of Ca2+ in the culture medium, which corresponded to higher cell differentiation and mineralized matrix formation in osteoblastic cell cultures and OD-21 cells, while reducing the negative effects of bismuth oxide on osteoblasts. In conclusion, CAC+ supported the acquisition of the osteogenic cell phenotype, mostly for cells in early stages of differentiation. Additionaly, the increase in the CaCl2 content, regardless of the radiopacifier agent, potentiates the beneficial effects on osteogenic cells and promotes the growth and differentiation of OD-21 cells, rendering CAC+ a potential alternative material to replace MTA in endodontic procedures.

O agregado de trióxido mineral (MTA) tem-se demonstrado aplicável em diversas situações que exigem reparação dos tecidos dentais e periapicais. Contudo, desvantagens relacionadas ao seu elevado custo, propriedades físico-químicas e dificuldade de manuseio têm limitado sua utilização. Neste sentido, um novo cimento de aluminato de cálcio e aditivos (CAC+) foi desenvolvido para superar algumas características negativas do MTA, mantendo, no entanto, suas propriedades satisfatórias. O objetivo deste estudo foi avaliar a progressão de culturas de células osteogênicas e de células indiferenciadas da polpa dental (linhagem OD-21) expostas ao CAC+, utilizando MTA como controle, ou a preparações alternativas do CAC+, com maior conteúdo de cloreto de cálcio (CaCl2) e/ou com substituição do óxido de zinco por óxido de bismuto como radiopacificador. Para isso, células osteogênicas derivadas de calvárias de ratos ou células da linhagem OD-21 foram crescidas sobre Thermanox® por 24 h e expostas, por períodos de até 14 dias, a amostras dos diferentes materiais, posicionadas sobre Transwell®. Em células osteogênicas, apesar de a proximidade com as amostras de CAC+ e MTA inibir o crescimento celular, nas áreas periféricas das lamínulas, foram observados proliferação, viabilidade celular e expressão de marcadores-chave da diferenciação osteoblástica, que precederam a mineralização da matriz extracelular. Culturas expostas ao CAC+, comparativamente ao MTA, exibiram aumentos na viabilidade celular, atividade de fosfatase alcalina e na expressão de marcadores de diferenciação, o que não se repetiu para células OD-21. Além disso, demonstrou-se que os efeitos destes cimentos sobre a osteogênese in vitro variaram de acordo com o período de exposição das culturas, sendo mais favoráveis durante sua fase proliferativa. Entre as preparações de CAC+, verificou-se que o aumento no teor de CaCl2 promoveu maior disponibilização de Ca2+ no meio de cultura, o que correspondeu a maior diferenciação celular e formação de matriz mineralizada em culturas de células osteogênicas e OD-21, e à redução de efeitos negativos da adição de óxido de bismuto sobre osteoblastos. Conclui-se que o CAC+ favorece o desenvolvimento do fenótipo osteogênico, atuando principalmente em células em estágios iniciais de diferenciação e que a adição de CaCl2, independentemente do agente radiopacificador, potencializa os efeitos benéficos sobre células osteogênicas e favorece o desenvolvimento e diferenciação de células indiferenciadas derivadas do tecido pulpar, podendo ser considerado como material alternativo ao MTA. / Mineral trioxide aggregate (MTA) has been successfully applied in endodontic procedures in which dental and periapical tissue repair are required. However, some drawbacks of MTA as high cost, physicochemical properties and difficulty in handling have limited its use. In this context, a novel calcium aluminate cement plus additives (CAC+) has been developed to overcome some negative features of MTA. The aim of this study was to evaluate the progression of either osteogenic cell cultures or undifferentiated dental pulp-derived ones (OD-21 cell line) exposed to CAC+ or to alternative formulations of CAC+ with a higher content of calcium chloride (CaCl2) and/or replacement of zinc oxide by bismuth oxide as radiopacifier agent. Rat calvaria-derived cells or OD-21 cells were grown on Thermanox® coverslips for 24 h and exposed to samples of CAC+ or MTA (control) placed on Transwell® for periods of up to 14 days. In osteogenic cell cultures, the proximity to MTA or CAC+ samples inhibited cell growth, whereas at distance it was observed cell proliferation, cell viability and expression of differentition markers prior to mineralization of the extracellular matrix. Comparatively to MTA, osteogenic cell cultures exposed to CAC+ exhibited higher cell viability, alkaline phosphatase activity and expression of key osteoblast markers, contrary to what was observed for OD-21 cells. Furthermore, it was demonstrated that the effects of these cements on in vitro osteogenesis varied according to the timing of exposure, with a more favorable impact during the proliferative phase of cultures. Among the diverse formulations of CAC+, it was found that the increase in the CaCl2 content promoted greater availability of Ca2+ in the culture medium, which corresponded to higher cell differentiation and mineralized matrix formation in osteoblastic cell cultures and OD-21 cells, while reducing the negative effects of bismuth oxide on osteoblasts. In conclusion, CAC+ supported the acquisition of the osteogenic cell phenotype, mostly for cells in early stages of differentiation. Additionaly, the increase in the CaCl2 content, regardless of the radiopacifier agent, potentiates the beneficial effects on osteogenic cells and promotes the growth and differentiation of OD-21 cells, rendering CAC+ a potential alternative material to replace MTA in endodontic procedures.