This study focuses on the evolving microstructure and its associated mechanical properties during each step of a seven step manufacturing process for 1010 steel tubing. For the microstructural analysis, we employed optical microscopy to quantify the ferrite grain size and pearlite grain size at each material step. To determine the mechanical properties, we used a Vickers hardness indenter and performed both tension and compression tests at varying strain rates and temperatures. Mechanical tests results indicate decreasing strength with increasing grain size, agreeing with the Hall-Petch relation and were used to correlate hardness and yield strength with grain size. Additionally, tensile and compression tests were performed at different strain rates to examine the effect of microstructural features on the mechanical properties of the steel tubing. Understanding the structure/property relationships of 1010 steel tubing during different processing conditions allows tubing to be manufactured more efficiently with desirable mechanical properties.

No description available.

No description available.

Trefilação é um dos processos de fabricação para a obtenção de arames, tubos e barras. Este processo consiste na redução da área de seção transversal de um material cilíndrico, fazendo-o atravessar uma matriz cônica de menor seção de área transversal, chamada fieira. Destacam-se o excelente acabamento superficial, a boa precisão dimensional e o aumento na resistência mecânica do material como vantagens e, como desvantagens, deformações heterogêneas ocorrem quando atravessam a ferramenta de trefilação (fieira). As deformações heterogêneas provocam retorno elástico também heterogêneo das camadas da barra trefilada, o que induz o aparecimento das tensões residuais relacionadas às distorções de forma, empenamentos e variações dimensionais, causando desperdício de material e energia, tanto no caso de geração de refugo, quanto em tentativas de correção das não conformidades. Desta forma, neste trabalho estudou-se a influência da geometria da fieira no valor da força necessária para realizar a trefilação e no gradiente das tensões residuais em barras de aço, através de experimentos físicos e computacionais. Após a caracterização de um processo de trefilação de um aço SAE 1045 foram desenvolvidos modelos computacionais no software Simufact.forming GP ®, e obtidos os resultados para: a força de trefilação, as tensões residuais das direções principais, as deformações plásticas, o limite de escoamento e o retorno elástico do material após a realização do processo para uma determinada redução. Os modelos foram validados através da comparação dos resultados simulados com experimentos físicos e equações encontradas na literatura. Após a validação, o modelo computacional foi utilizado para simular a variação da geometria da fieira: número de regiões de trabalho, raios de convergência entre as diferentes regiões da ferramenta, diferentes materiais e áreas de seção transversal. Os resultados das simulações computacionais foram correlacionados e utilizados para projetar e fabricar uma fieira em escala reduzida e um dispositivo mecânico para a simulação física do processo de trefilação em uma máquina universal de ensaios Emic ®. Duas diferentes geometrias de fieira foram testadas experimentalmente F1: a fieira convencional, e F4, a fieira modificada a partir das sugestões obtidas a partir da metodologia escolhida para correlacionar os resultados das simulações computacionais. As novas barras trefiladas foram caracterizadas mecanicamente através de ensaios de microdureza e rugosidade para análise das propriedades mecânicas, difração de raios-X para obtenção das tensões residuais superficiais e força de trefilação, que foi medida durante a realização do ensaio. Este trabalho contribuiu cientificamente com uma melhor compreensão do comportamento do escoamento de um material trefilado e através da análise de uma nova geometria de fieira que permitiu uma redução no valor das tensões residuais, um pequeno aumento na força de trefilação, mantendo as propriedades mecânicas do material trefilado quando comparadas com o processo original objeto desta pesquisa. / The wire drawing is a manufacturing process used to produce wires, tubes and rods. It consists in a reduction in cross sectional area by plastic deformation where the raw material (wire rod) is pulled through a die. Some of the main features of the wire drawing process are the achievement of an excellent surface finishing and good dimensional accuracies and increase in mechanical strength. However, this process generates inhomogeneous deformation due to the different flowing of the material into the drawing tool (die). The inhomogeneous deformation generates residual stress, stresses present in a material free from the action of external loads and temperature gradients. Residual stresses are commonly related to distortions of shape and dimensional variations of the final products, appearing after heat treatments which are related to shape distortions, warping and dimensional variations, causing material and energy waste, in the case of waste generation and in attempts to correct nonconformities. Thus, the influence of die geometry to reducing the residual stresses and the drawing force of bars manufactured by a cold-drawing process was studied. After the characterization of a drawing process of an SAE 1045 steel, computer models were developed in the software Simufact.forming GP ®, and the results were obtained for: drawing force, residual stresses of the main directions, plastic deformations, flow and the elastic return of the material after the process was carried out. The models were validated by comparing simulated results with physical experiments and equations found in the literature. Different die geometries were simulated as: number of tool regions, fillets between different tool regions, different materials and cross-sectional areas. The results of the computational simulations were correlated and used to design and manufacture a scale die and a mechanical device to develop the physical drawing tests in an Emic ® testing machine. Two different die geometries were experimentally tested F1: the conventional die, and F4, the modified from suggestions obtained in the computational simulations correlation F. The mechanical characterization of the new drawn bars were carried out by Vickers microhardness and roughness tests, X-ray diffraction to obtain surface residual stresses and the drawing force was taken during the test. This work contributes scientifically with a better understanding of the behavior of the flow of a drawn material by the analysis of a new die geometry that allowed a reduction in the value of the residual stresses, an increase in the drawing force and maintaining the mechanical properties of the drawn material when compared to the original process object of this research.

Trefilação é um dos processos de fabricação para a obtenção de arames, tubos e barras. Este processo consiste na redução da área de seção transversal de um material cilíndrico, fazendo-o atravessar uma matriz cônica de menor seção de área transversal, chamada fieira. Destacam-se o excelente acabamento superficial, a boa precisão dimensional e o aumento na resistência mecânica do material como vantagens e, como desvantagens, deformações heterogêneas ocorrem quando atravessam a ferramenta de trefilação (fieira). As deformações heterogêneas provocam retorno elástico também heterogêneo das camadas da barra trefilada, o que induz o aparecimento das tensões residuais relacionadas às distorções de forma, empenamentos e variações dimensionais, causando desperdício de material e energia, tanto no caso de geração de refugo, quanto em tentativas de correção das não conformidades. Desta forma, neste trabalho estudou-se a influência da geometria da fieira no valor da força necessária para realizar a trefilação e no gradiente das tensões residuais em barras de aço, através de experimentos físicos e computacionais. Após a caracterização de um processo de trefilação de um aço SAE 1045 foram desenvolvidos modelos computacionais no software Simufact.forming GP ®, e obtidos os resultados para: a força de trefilação, as tensões residuais das direções principais, as deformações plásticas, o limite de escoamento e o retorno elástico do material após a realização do processo para uma determinada redução. Os modelos foram validados através da comparação dos resultados simulados com experimentos físicos e equações encontradas na literatura. Após a validação, o modelo computacional foi utilizado para simular a variação da geometria da fieira: número de regiões de trabalho, raios de convergência entre as diferentes regiões da ferramenta, diferentes materiais e áreas de seção transversal. Os resultados das simulações computacionais foram correlacionados e utilizados para projetar e fabricar uma fieira em escala reduzida e um dispositivo mecânico para a simulação física do processo de trefilação em uma máquina universal de ensaios Emic ®. Duas diferentes geometrias de fieira foram testadas experimentalmente F1: a fieira convencional, e F4, a fieira modificada a partir das sugestões obtidas a partir da metodologia escolhida para correlacionar os resultados das simulações computacionais. As novas barras trefiladas foram caracterizadas mecanicamente através de ensaios de microdureza e rugosidade para análise das propriedades mecânicas, difração de raios-X para obtenção das tensões residuais superficiais e força de trefilação, que foi medida durante a realização do ensaio. Este trabalho contribuiu cientificamente com uma melhor compreensão do comportamento do escoamento de um material trefilado e através da análise de uma nova geometria de fieira que permitiu uma redução no valor das tensões residuais, um pequeno aumento na força de trefilação, mantendo as propriedades mecânicas do material trefilado quando comparadas com o processo original objeto desta pesquisa. / The wire drawing is a manufacturing process used to produce wires, tubes and rods. It consists in a reduction in cross sectional area by plastic deformation where the raw material (wire rod) is pulled through a die. Some of the main features of the wire drawing process are the achievement of an excellent surface finishing and good dimensional accuracies and increase in mechanical strength. However, this process generates inhomogeneous deformation due to the different flowing of the material into the drawing tool (die). The inhomogeneous deformation generates residual stress, stresses present in a material free from the action of external loads and temperature gradients. Residual stresses are commonly related to distortions of shape and dimensional variations of the final products, appearing after heat treatments which are related to shape distortions, warping and dimensional variations, causing material and energy waste, in the case of waste generation and in attempts to correct nonconformities. Thus, the influence of die geometry to reducing the residual stresses and the drawing force of bars manufactured by a cold-drawing process was studied. After the characterization of a drawing process of an SAE 1045 steel, computer models were developed in the software Simufact.forming GP ®, and the results were obtained for: drawing force, residual stresses of the main directions, plastic deformations, flow and the elastic return of the material after the process was carried out. The models were validated by comparing simulated results with physical experiments and equations found in the literature. Different die geometries were simulated as: number of tool regions, fillets between different tool regions, different materials and cross-sectional areas. The results of the computational simulations were correlated and used to design and manufacture a scale die and a mechanical device to develop the physical drawing tests in an Emic ® testing machine. Two different die geometries were experimentally tested F1: the conventional die, and F4, the modified from suggestions obtained in the computational simulations correlation F. The mechanical characterization of the new drawn bars were carried out by Vickers microhardness and roughness tests, X-ray diffraction to obtain surface residual stresses and the drawing force was taken during the test. This work contributes scientifically with a better understanding of the behavior of the flow of a drawn material by the analysis of a new die geometry that allowed a reduction in the value of the residual stresses, an increase in the drawing force and maintaining the mechanical properties of the drawn material when compared to the original process object of this research.

Trefilação é um dos processos de fabricação para a obtenção de arames, tubos e barras. Este processo consiste na redução da área de seção transversal de um material cilíndrico, fazendo-o atravessar uma matriz cônica de menor seção de área transversal, chamada fieira. Destacam-se o excelente acabamento superficial, a boa precisão dimensional e o aumento na resistência mecânica do material como vantagens e, como desvantagens, deformações heterogêneas ocorrem quando atravessam a ferramenta de trefilação (fieira). As deformações heterogêneas provocam retorno elástico também heterogêneo das camadas da barra trefilada, o que induz o aparecimento das tensões residuais relacionadas às distorções de forma, empenamentos e variações dimensionais, causando desperdício de material e energia, tanto no caso de geração de refugo, quanto em tentativas de correção das não conformidades. Desta forma, neste trabalho estudou-se a influência da geometria da fieira no valor da força necessária para realizar a trefilação e no gradiente das tensões residuais em barras de aço, através de experimentos físicos e computacionais. Após a caracterização de um processo de trefilação de um aço SAE 1045 foram desenvolvidos modelos computacionais no software Simufact.forming GP ®, e obtidos os resultados para: a força de trefilação, as tensões residuais das direções principais, as deformações plásticas, o limite de escoamento e o retorno elástico do material após a realização do processo para uma determinada redução. Os modelos foram validados através da comparação dos resultados simulados com experimentos físicos e equações encontradas na literatura. Após a validação, o modelo computacional foi utilizado para simular a variação da geometria da fieira: número de regiões de trabalho, raios de convergência entre as diferentes regiões da ferramenta, diferentes materiais e áreas de seção transversal. Os resultados das simulações computacionais foram correlacionados e utilizados para projetar e fabricar uma fieira em escala reduzida e um dispositivo mecânico para a simulação física do processo de trefilação em uma máquina universal de ensaios Emic ®. Duas diferentes geometrias de fieira foram testadas experimentalmente F1: a fieira convencional, e F4, a fieira modificada a partir das sugestões obtidas a partir da metodologia escolhida para correlacionar os resultados das simulações computacionais. As novas barras trefiladas foram caracterizadas mecanicamente através de ensaios de microdureza e rugosidade para análise das propriedades mecânicas, difração de raios-X para obtenção das tensões residuais superficiais e força de trefilação, que foi medida durante a realização do ensaio. Este trabalho contribuiu cientificamente com uma melhor compreensão do comportamento do escoamento de um material trefilado e através da análise de uma nova geometria de fieira que permitiu uma redução no valor das tensões residuais, um pequeno aumento na força de trefilação, mantendo as propriedades mecânicas do material trefilado quando comparadas com o processo original objeto desta pesquisa. / The wire drawing is a manufacturing process used to produce wires, tubes and rods. It consists in a reduction in cross sectional area by plastic deformation where the raw material (wire rod) is pulled through a die. Some of the main features of the wire drawing process are the achievement of an excellent surface finishing and good dimensional accuracies and increase in mechanical strength. However, this process generates inhomogeneous deformation due to the different flowing of the material into the drawing tool (die). The inhomogeneous deformation generates residual stress, stresses present in a material free from the action of external loads and temperature gradients. Residual stresses are commonly related to distortions of shape and dimensional variations of the final products, appearing after heat treatments which are related to shape distortions, warping and dimensional variations, causing material and energy waste, in the case of waste generation and in attempts to correct nonconformities. Thus, the influence of die geometry to reducing the residual stresses and the drawing force of bars manufactured by a cold-drawing process was studied. After the characterization of a drawing process of an SAE 1045 steel, computer models were developed in the software Simufact.forming GP ®, and the results were obtained for: drawing force, residual stresses of the main directions, plastic deformations, flow and the elastic return of the material after the process was carried out. The models were validated by comparing simulated results with physical experiments and equations found in the literature. Different die geometries were simulated as: number of tool regions, fillets between different tool regions, different materials and cross-sectional areas. The results of the computational simulations were correlated and used to design and manufacture a scale die and a mechanical device to develop the physical drawing tests in an Emic ® testing machine. Two different die geometries were experimentally tested F1: the conventional die, and F4, the modified from suggestions obtained in the computational simulations correlation F. The mechanical characterization of the new drawn bars were carried out by Vickers microhardness and roughness tests, X-ray diffraction to obtain surface residual stresses and the drawing force was taken during the test. This work contributes scientifically with a better understanding of the behavior of the flow of a drawn material by the analysis of a new die geometry that allowed a reduction in the value of the residual stresses, an increase in the drawing force and maintaining the mechanical properties of the drawn material when compared to the original process object of this research.

As tensões residuais podem atuar de forma benéfica ou maléfica no desempenho dos componentes mecânicos. Elas representam um dos principais potenciais para o aparecimento de distorções, empenamentos e mudanças dimensionais em componentes mecânicos durante o processo de manufatura. Por estes motivos a determinação da distribuição e o controle destas tensões residuais em cada etapa do processo de manufatura são de grande importância. Neste trabalho, foram realizadas análises da variação das tensões residuais em barras trefiladas de aço AISI 1048 em decorrência do processo de fabricação. As barras foram retiradas de quatro diferentes etapas do processo de trefilação combinada guardando-se a orientação inicial do fio-máquina, sendo elas: pré-endireitada, jateada, trefilada (com ângulos de 15°, 16°, 18° e 20°), endireitada e polida por rolos cruzados (PTN) (com ângulos de 15°, 16° e 18°). Estas barras foram ensaiadas através do método do furo cego (hole-drilling), método da deflexão (slitting) e difração de raios-X. Os ensaios foram realizados até uma profundidade de 1 mm para o método do furo cego e chegando até profundidades de 5,6mm para a técnica de difração de raios-X com remoção de camadas em diferentes posições periféricas para caracterizar heterogeneidades impostas pelo processo. A partir dos valores de deformações obtidos, foram calculadas as tensões residuais nas direções longitudinais e tangenciais para cada posição ensaiada. Com este trabalho foi obtida uma visão completa do desenvolvimento de tensões na região superficial da barra após as etapas do processo e assim foram determinadas quais etapas do processo tem maior influência no produto final (barras trefiladas). Após o préendireitamento as tensões são compressivas, aumentando seu nível após o jateamento. Na saída da trefilação as tensões mudam para trativas e após o endireitamento final (PTN) tornam-se menos trativas ou compressivas dependendo do ângulo de endireitamento (PTN) e o ângulo de fieira utilizado. A partir deste estudo foram propostas mudanças nos ângulos de ferramenta (fieira) e também nos rolos de polimento e endireitamento final, objetivando-se um produto final com tensões residuais mais favoráveis a processos subseqüentes de manufatura. Outro aspecto importante verificado é a variação das tensões residuais em relação à posição periférica: diferenças de até 200MPa foram verificadas até antes da etapa de endireitamento final PTN, após a qual as diferenças são reduzidas a quase zero. / The residual stresses can affect positively or negatively the behavior of mechanical components. These residual stresses also represent one of the main potentials for distortion (i.e. bending and dimensional changes) in mechanical components during the manufacturing. Therefore the determination of the distribution and the control of these residual stresses in each stage of the manufacturing process are of great importance. In this work the variation of residual stresses in cold-drawing of AISI 1048 steel bars due to the production process was analyzed. Samples were taken from five different stages of the process of combined cold-drawing with special care to keep the information about initial orientation. The process steps from where samples were taken were: pre-straightening, shot-blasting, drawing, straightening and polishing in crossed rolls (PTN) with angles of 16° and 18°. The determination of residual stresses was accomplished by the hole drilling method. The measurements were done until a depth of 1 mm in different angular positions on the periphery to characterize heterogeneities imposed by the process. Starting with the obtained strains, the residual stresses were calculated in the longitudinal and tangential directions for each measurement position. With this work a global view of the developed stresses in the surface of the bar after each process stage was obtained. After the pre-straightening the residual stresses are compressive, and increase their level after the shot blasting, at the end of drawing the residual stresses change for tensile and after the polishing with crossed rolls (PTN) they become less tensile or slightly compressive depending on the PTN - angle and draw angle used. Based on this study, changes were proposed in the tool (draw) angles and also in the PTN, being aimed at a final product with more favorable residual stresses to subsequent manufacturing operations. Another verified important aspect is the variation of the residual stresses in relation to the peripheral position: differences of up to 200MPa were verified before the stage of polishing in crossed rolls (PTN), after which the differences are almost reduced to nearly zero.

As tensões residuais podem atuar de forma benéfica ou maléfica no desempenho dos componentes mecânicos. Elas representam um dos principais potenciais para o aparecimento de distorções, empenamentos e mudanças dimensionais em componentes mecânicos durante o processo de manufatura. Por estes motivos a determinação da distribuição e o controle destas tensões residuais em cada etapa do processo de manufatura são de grande importância. Neste trabalho, foram realizadas análises da variação das tensões residuais em barras trefiladas de aço AISI 1048 em decorrência do processo de fabricação. As barras foram retiradas de quatro diferentes etapas do processo de trefilação combinada guardando-se a orientação inicial do fio-máquina, sendo elas: pré-endireitada, jateada, trefilada (com ângulos de 15°, 16°, 18° e 20°), endireitada e polida por rolos cruzados (PTN) (com ângulos de 15°, 16° e 18°). Estas barras foram ensaiadas através do método do furo cego (hole-drilling), método da deflexão (slitting) e difração de raios-X. Os ensaios foram realizados até uma profundidade de 1 mm para o método do furo cego e chegando até profundidades de 5,6mm para a técnica de difração de raios-X com remoção de camadas em diferentes posições periféricas para caracterizar heterogeneidades impostas pelo processo. A partir dos valores de deformações obtidos, foram calculadas as tensões residuais nas direções longitudinais e tangenciais para cada posição ensaiada. Com este trabalho foi obtida uma visão completa do desenvolvimento de tensões na região superficial da barra após as etapas do processo e assim foram determinadas quais etapas do processo tem maior influência no produto final (barras trefiladas). Após o préendireitamento as tensões são compressivas, aumentando seu nível após o jateamento. Na saída da trefilação as tensões mudam para trativas e após o endireitamento final (PTN) tornam-se menos trativas ou compressivas dependendo do ângulo de endireitamento (PTN) e o ângulo de fieira utilizado. A partir deste estudo foram propostas mudanças nos ângulos de ferramenta (fieira) e também nos rolos de polimento e endireitamento final, objetivando-se um produto final com tensões residuais mais favoráveis a processos subseqüentes de manufatura. Outro aspecto importante verificado é a variação das tensões residuais em relação à posição periférica: diferenças de até 200MPa foram verificadas até antes da etapa de endireitamento final PTN, após a qual as diferenças são reduzidas a quase zero. / The residual stresses can affect positively or negatively the behavior of mechanical components. These residual stresses also represent one of the main potentials for distortion (i.e. bending and dimensional changes) in mechanical components during the manufacturing. Therefore the determination of the distribution and the control of these residual stresses in each stage of the manufacturing process are of great importance. In this work the variation of residual stresses in cold-drawing of AISI 1048 steel bars due to the production process was analyzed. Samples were taken from five different stages of the process of combined cold-drawing with special care to keep the information about initial orientation. The process steps from where samples were taken were: pre-straightening, shot-blasting, drawing, straightening and polishing in crossed rolls (PTN) with angles of 16° and 18°. The determination of residual stresses was accomplished by the hole drilling method. The measurements were done until a depth of 1 mm in different angular positions on the periphery to characterize heterogeneities imposed by the process. Starting with the obtained strains, the residual stresses were calculated in the longitudinal and tangential directions for each measurement position. With this work a global view of the developed stresses in the surface of the bar after each process stage was obtained. After the pre-straightening the residual stresses are compressive, and increase their level after the shot blasting, at the end of drawing the residual stresses change for tensile and after the polishing with crossed rolls (PTN) they become less tensile or slightly compressive depending on the PTN - angle and draw angle used. Based on this study, changes were proposed in the tool (draw) angles and also in the PTN, being aimed at a final product with more favorable residual stresses to subsequent manufacturing operations. Another verified important aspect is the variation of the residual stresses in relation to the peripheral position: differences of up to 200MPa were verified before the stage of polishing in crossed rolls (PTN), after which the differences are almost reduced to nearly zero.

As tensões residuais podem atuar de forma benéfica ou maléfica no desempenho dos componentes mecânicos. Elas representam um dos principais potenciais para o aparecimento de distorções, empenamentos e mudanças dimensionais em componentes mecânicos durante o processo de manufatura. Por estes motivos a determinação da distribuição e o controle destas tensões residuais em cada etapa do processo de manufatura são de grande importância. Neste trabalho, foram realizadas análises da variação das tensões residuais em barras trefiladas de aço AISI 1048 em decorrência do processo de fabricação. As barras foram retiradas de quatro diferentes etapas do processo de trefilação combinada guardando-se a orientação inicial do fio-máquina, sendo elas: pré-endireitada, jateada, trefilada (com ângulos de 15°, 16°, 18° e 20°), endireitada e polida por rolos cruzados (PTN) (com ângulos de 15°, 16° e 18°). Estas barras foram ensaiadas através do método do furo cego (hole-drilling), método da deflexão (slitting) e difração de raios-X. Os ensaios foram realizados até uma profundidade de 1 mm para o método do furo cego e chegando até profundidades de 5,6mm para a técnica de difração de raios-X com remoção de camadas em diferentes posições periféricas para caracterizar heterogeneidades impostas pelo processo. A partir dos valores de deformações obtidos, foram calculadas as tensões residuais nas direções longitudinais e tangenciais para cada posição ensaiada. Com este trabalho foi obtida uma visão completa do desenvolvimento de tensões na região superficial da barra após as etapas do processo e assim foram determinadas quais etapas do processo tem maior influência no produto final (barras trefiladas). Após o préendireitamento as tensões são compressivas, aumentando seu nível após o jateamento. Na saída da trefilação as tensões mudam para trativas e após o endireitamento final (PTN) tornam-se menos trativas ou compressivas dependendo do ângulo de endireitamento (PTN) e o ângulo de fieira utilizado. A partir deste estudo foram propostas mudanças nos ângulos de ferramenta (fieira) e também nos rolos de polimento e endireitamento final, objetivando-se um produto final com tensões residuais mais favoráveis a processos subseqüentes de manufatura. Outro aspecto importante verificado é a variação das tensões residuais em relação à posição periférica: diferenças de até 200MPa foram verificadas até antes da etapa de endireitamento final PTN, após a qual as diferenças são reduzidas a quase zero. / The residual stresses can affect positively or negatively the behavior of mechanical components. These residual stresses also represent one of the main potentials for distortion (i.e. bending and dimensional changes) in mechanical components during the manufacturing. Therefore the determination of the distribution and the control of these residual stresses in each stage of the manufacturing process are of great importance. In this work the variation of residual stresses in cold-drawing of AISI 1048 steel bars due to the production process was analyzed. Samples were taken from five different stages of the process of combined cold-drawing with special care to keep the information about initial orientation. The process steps from where samples were taken were: pre-straightening, shot-blasting, drawing, straightening and polishing in crossed rolls (PTN) with angles of 16° and 18°. The determination of residual stresses was accomplished by the hole drilling method. The measurements were done until a depth of 1 mm in different angular positions on the periphery to characterize heterogeneities imposed by the process. Starting with the obtained strains, the residual stresses were calculated in the longitudinal and tangential directions for each measurement position. With this work a global view of the developed stresses in the surface of the bar after each process stage was obtained. After the pre-straightening the residual stresses are compressive, and increase their level after the shot blasting, at the end of drawing the residual stresses change for tensile and after the polishing with crossed rolls (PTN) they become less tensile or slightly compressive depending on the PTN - angle and draw angle used. Based on this study, changes were proposed in the tool (draw) angles and also in the PTN, being aimed at a final product with more favorable residual stresses to subsequent manufacturing operations. Another verified important aspect is the variation of the residual stresses in relation to the peripheral position: differences of up to 200MPa were verified before the stage of polishing in crossed rolls (PTN), after which the differences are almost reduced to nearly zero.

Este trabalho tem como objetivo caracterizar as mudanças microestruturais durante o recozimento isotérmico de um fio de ferro trefilado a frio e de pureza comercial com ênfase no crescimento de grão. Os recozimentos foram realizados no intervalo de 823-1173 K por diversos tempos. As informações estatísticas do tamanho de grão foram obtidas por meio do método dos interceptos lineares. O mapeamento das orientações foi obtido por meio de difração de elétrons retroespalhados (EBSD). O material apresenta uma microestrutura ferrítica e totalmente recristalizada a partir de 873 K. Foram encontrados indícios de crescimento normal de grão a partir de 1023 K, porém este crescimento não evoluiu consideravelmente ao longo do tempo de tratamento. Os resultados obtidos a partir do método dos interceptos lineares demonstram que a distribuição de tamanho de grão segue uma curva próxima à log-normal. Nas amostras recozidas a partir de 1123 K, verificou-se a ocorrência de crescimento anormal de grão. O crescimento anormal de alguns grãos inicia-se na região central do fio, estendendo-se até uma região próxima à superfície do fio. Algumas modificações na dimensão da amostra e na atmosfera de recozimento foram realizadas a fim de se estudar a interação destas variáveis no desenvolvimento dos grãos anormais. Foram identificados indícios morfológicos de que o mecanismo para ocorrência de crescimento anormal foi o molhamento de contornos no estado sólido (solid-state wetting) que depois foram confirmados pelas análises de micro e mesotexturas. A análise de microtextura também revela que o material apresenta duas componentes preferenciais, as fibras || DT e || DT, onde DT é a direção axial de trefilação. A primeira orientação é a mais intensa, sendo que seu fortalecimento parece ser impulsionado pelo crescimento anormal de grão. A segunda é menos intensa e parece estar relacionada com as orientações dos grãos oriundos da recristalização primária. Aspectos teóricos e analíticos sobre o crescimento de grão são apresentados e associados aos resultados experimentais e à literatura. / This Dissertation aims follow the microstructural changes occurring during isothermal annealing of commercially-pure cold-drawn iron wire, with emphasys on grain growth phenomena. The grain size data were obtained by means of the linear intercept method. The orientations scanning were done by means of electron backscatter diffraction patterns (EBSD). Isothermal annealing was performed within the temperature range 823 - 1173 K for several times. The material displays full recrystallization at temperatures above 873 K. Normal grain growth was observed above 1023 K, although this growth did not evolve through longer annealing times. The results of the linear intercept method show the grain size distribution has a log-normal shape. For samples annealed above 1123 K, abnormal grain growth occurs. The first signs of secondary recrystallization appear close to the center of the wire, growing towards the surface. Changes in the wire diameter and annealing atmosphere were performed to assess the effect of these variables on abnormal grain growth. Results point out that abnormal grain growth is driven by solid-state wetting. These morphological observations were also confirmed by micro and mesotexture analyses. The microtexture also shows the presence of two major fiber texture components || WD and || WD, were WD is the axial wire-drawn direction. The first one is the most intense and its strengthening seems to be related with abnormal grain growth. The second one is weaker and it seems to be most related with small primary recrystallized grains. Theoretical and analytical features about grain growth are presented and discussed in light of literature and experimental results.