Comportamento magn?tico de comp?sitos de matriz polim?rica com adi??o de ferritas / Magnetic behavior of polymeric matrix composites with the addition of ferritesFulco, Ana Paula Pereira 06 September 2013 (has links)
Made available in DSpace on 2014-12-17T14:07:09Z (GMT). No. of bitstreams: 1
AnaPPF_DISSERT.pdf: 3895025 bytes, checksum: 139d5ed551d6922e5b7f6e67a16602fd (MD5)
Previous issue date: 2013-09-06 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Polymer matrix composites offer advantages for many applications due their combination of properties, which includes low density, high specific strength and modulus of elasticity and corrosion resistance. However, the application of non-destructive techniques using magnetic sensors for the evaluation these materials is not possible since the materials are non-magnetizable. Ferrites are materials with excellent magnetic properties, chemical stability and corrosion resistance. Due to these properties, these materials are promising for the development of polymer composites with magnetic properties. In this work, glass fiber / epoxy circular plates were produced with 10 wt% of cobalt or barium ferrite particles. The cobalt ferrite was synthesized by the Pechini method. The commercial barium ferrite was subjected to a milling process to study the effect of particle size on the magnetic properties of the material. The characterization of the ferrites was carried out by x-ray diffraction (XRD), field emission gun scanning electron microscopy (FEG-SEM) and vibrating sample magnetometry (VSM). Circular notches of 1, 5 and 10 mm diameter were introduced in the composite plates using a drill bit for the non-destructive evaluation by the technique of magnetic flux leakage (MFL). The results indicated that the magnetic signals measured in plates with barium ferrite without milling and cobalt ferrite showed good correlation with the presence of notches. The milling process for 12 h and 20 h did not contribute to improve the identification of smaller size notches (1 mm). However, the smaller particle size produced smoother magnetic curves, with fewer discontinuities and improved signal-to-noise ratio. In summary, the results suggest that the proposed approach has great potential for the detection of damage in polymer composites structures / Materiais comp?sitos polim?ricos oferecem vantagens para v?rias aplica??es pela combina??o de propriedades como baixa densidade, elevada resist?ncia mec?nica e m?dulo de elasticidade espec?ficos e resist?ncia a corros?o. Entretanto, por n?o serem magnetiz?veis, esses materiais n?o permitem a utiliza??o de t?cnicas de avalia??o n?o destrutivas que utilizem sensores magn?ticos. Ferritas s?o materiais com excelentes propriedades magn?ticas, estabilidade qu?mica e resist?ncia ? corros?o. Devido a essas propriedades esses materiais s?o promissores para o desenvolvimento de comp?sitos de matriz polim?rica com propriedades magn?ticas. Neste trabalho, discos de comp?sitos de fibra de vidro/ep?xi foram produzidos com adi??o de 10% em massa de part?culas de ferrita de cobalto ou de b?rio. A ferrita de cobalto foi sintetizada pelo m?todo Pechini. A ferrita comercial de b?rio foi submetida a um processo de moagem para se estudar o efeito do tamanho de part?cula nas propriedades magn?ticas do material. A caracteriza??o das ferritas foi realizada pelas t?cnicas de difra??o de raio x (DRX), microscopia eletr?nica de varredura (MEV-FEG) e magnetometria de amostra vibrante (MAV). Entalhes circulares com di?metros de 1, 5 e 10 mm foram introduzidos nos discos de comp?sitos com o aux?lio de uma broca para avalia??o n?o-destrutiva por meio da t?cnica de fuga de fluxo magn?tico (MFL). A abordagem apresentada permitiu identificar todos os entalhes introduzidos nos discos. Os resultados indicaram que os sinais magn?ticos medidos nos discos com a ferrita de b?rio sem moagem e de cobalto apresentaram boa correla??o com a presen?a dos entalhes. O processo de moagem por 12 h e 20 h n?o contribuiu para a melhor identifica??o de entalhes de menor dimens?o (1 mm). Entretanto, o menor tamanho de part?cula permitiu produzir curvas magn?ticas mais suaves, com menos descontinuidades e melhor rela??o sinal-ru?do. Em resumo, os resultados sugerem que a abordagem proposta tem grande potencial para a detec??o de falhas em estruturas de materiais comp?sitos polim?ricos
|
12 |
Desenvolvimento e caracteriza??o de comp?sito a partir da borra da pia?ava para constru??o da par?bola de um fog?o solar a concentra??oLion Filho, Carlos Alberto Pereira de Queiroz 02 December 2013 (has links)
Made available in DSpace on 2014-12-17T14:07:19Z (GMT). No. of bitstreams: 1
CarlosAPQLF_TESE.pdf: 7845863 bytes, checksum: f98a50dab42dcf5a759f2e7a9cf9635c (MD5)
Previous issue date: 2013-12-02 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Este trabalho apresenta um modelo de fog?o solar ? concentra??o composto de uma
par?bola obtida atrav?s da utiliza??o de fibra de borra de pia?ava, refor?o natural alternativo
aos compostos polim?ricos usualmente utilizados como a fibra de vidro, aplicada sobre um
molde cer?mico, destinado ao cozimento de alimentos para fins residenciais, urbanos e rurais.
Assim, o trabalho ? iniciado com a caracteriza??o da microestrutura da fibra da borra da
pia?ava seguido da caracteriza??o do comp?sito utilizando como matriz resina ortoft?lica
refor?ada com fibras de borra de pia?ava. O Estado da Bahia, na regi?o do baixo-sul, ? o
?nico produtor de fibras de pia?ava da esp?cie Attalea funifera Martius, sendo a fibra da
borra de pia?ava muito utilizada na cobertura de quiosques em ?reas de lazer como s?tios,
clubes e pra?as, diferentemente da fibra propriamente dita utilizada na confec??o de
vassouras. O comp?sito, que tem em sua estrutura resina poli?ster ortoft?lica refor?ada
somente com fibras da borra da pia?ava, foi desenvolvido usando o processo de molde
fechado por compress?o. As amostras com diferentes percentuais de fibras, 5%, 10% e 15%,
sendo metade delas tratadas com NaOH a 3%, e dimens?es de 150x25x3 mm, foram cortadas
a laser na placa do comp?sito obtido para os ensaios mec?nicos e posterior an?lise
microestrutural e finalizando com a constru??o da par?bola. Ser?o apresentados detalhes
t?cnicos dos processos de caracteriza??o das fibras da casca de pia?ava, caracteriza??o do
comp?sito, fabrica??o e montagem do fog?o, uma an?lise das viabilidades, t?rmica,
econ?mica e de materiais de tal prot?tipo, que tem uma conota??o social importante e um
aspecto primordial, que ? o combate a danos ecol?gicos proporcionados pela utiliza??o, ainda
em larga escala, da lenha para o cozimento dos alimentos
|
13 |
Fibras de licuri: um refor?o vegetal alternativo de comp?sitos polim?ricosLe?o, Mirt?nia Antunes 27 September 2009 (has links)
Made available in DSpace on 2014-12-17T14:57:46Z (GMT). No. of bitstreams: 1
MirtaniaAL.pdf: 1813042 bytes, checksum: 3d26a66f383220285205f479f11b4656 (MD5)
Previous issue date: 2009-09-27 / This research is based, at first, on the seeking of alternatives naturals reinforced in place of polymeric composites, also named reinforced plastics. Therein, this work starts with a whole licuri fiber micro structural characterization, as alternative proposal to polymeric composites. Licuri fiber is abundant on the Bahia state flora, native from a palm tree called Syagrus Coronata (Martius) Beccari. After, it was done only licuri fiber laminar composite developing studies, in order to know its behavior when impregnated with thermofix resin. The
composite was developed in laminar structure shape (plate with a single layer of reinforcement) and produced industrially. The layer of reinforcement is a fabric-fiber
unidirectional of licuri up in a manual loom. Their structure was made of polyester resin ortofit?lica (unsaturated) only reinforced with licuri fibers. Fiber characterization studies were based on physical chemistry properties and their constitution. It was made by tension, scanning electron microscopy (SEM), x-ray diffraction (RDX) and thermal analyses (TG and DTA) tests, besides fiber chemistry analyses. Relating their mechanical properties of strength and hardness testing, they were determined through unit axial tension test and flexion in three
points. A study in order to know fiber/matrix interface effects, in the final composites results, was required. To better understand the mechanical behavior of the composite, macroscopic and microscopic optical analysis of the fracture was performed / Esta investiga??o baseia-se, em principio, na busca de refor?os naturais alternativos aos comp?sitos polim?ricos, tamb?m denominados de pl?sticos refor?ados. Neste sentido, o presente trabalho de pesquisa se inicia com um completo estudo de caracteriza??o micro estrutural da fibra de licuri, essa como proposta alternativa de refor?o aos comp?sitos polim?ricos. A fibra de licuri ? abundante na flora do estado da Bahia e origin?ria da palmeira
denominada Syagrus Coronata (Martius) Beccari. Em seguida, foi realizado um estudo do desenvolvimento de um comp?sito laminar somente a base de fibras de licuri, de forma a se conhecer o comportamento da fibra quando impregnada com resina termofixa. O comp?sito foi desenvolvido na forma de estrutura laminar (placa com uma ?nica l?mina de refor?o) e fabricado industrialmente. A l?mina de refor?o ? de um tecido unidirecional de fibras de licuri confeccionado em um tear manual. O comp?sito tem em sua estrutura resina poli?ster ortofit?lica (insaturada) refor?ada somente com fibras de licuri. O estudo da caracteriza??o da fibra teve como base a determina??o das propriedades f?sicas, qu?micas e de constitui??o. As mesmas foram realizadas atrav?s dos ensaios de: tra??o uniaxial, an?lise por microscopia
eletr?nica de varredura (MEV), ensaio de difra??o de raios X (RDX), an?lises t?rmicas (TG e DTA), al?m da an?lise qu?mica das fibras. Com rela??o ?s propriedades mec?nicas de resist?ncia e rigidez do comp?sito, estas foram determinadas atrav?s dos ensaios de tra??o
uniaxial e flex?o em tr?s pontos. Um estudo com o objetivo de conhecer a influ?ncia da ader?ncia da interface fibra/matriz, na resposta final do comp?sito, se fez necess?rio. Para melhor entendimento do comportamento mec?nico do comp?sito, an?lises macrosc?picas e microsc?picas ?pticas da fratura foram realizadas
|
14 |
Descontinuidade na se??o transversal em laminados comp?sitos polim?ricos: efeitos e propriedadesTin?, S?rgio Renan Lopes 26 February 2010 (has links)
Made available in DSpace on 2014-12-17T14:57:58Z (GMT). No. of bitstreams: 1
SergioRLT_DISERT.pdf: 4299592 bytes, checksum: e9cf5f819b0edce432f2bda3973896ee (MD5)
Previous issue date: 2010-02-26 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The growing demand in the use of composite materials necessitates a better understanding its behavior to many conditions of loading and service, as well as under several ways of connections involved in mechanisms of structural projects. It is know that most of the structural elements are designed with presence of geometric discontinuities (holes, notches, etc) in their longitudinal sections and / or transversals, and that these discontinuities affect the mechanical response of these elements. This work has aims to analyze a study of the mechanical response, when in the presence geometric discontinuity, of polymer matrix composite laminates (orthophthalic polyester) to the uniaxial tensile test. The geometric discontinuity is characterized by the presence of a center hole in the transversal section of the composite. In this study, different kinds of stacking sequences are tested, with and without the presence of the hole, so as to provide better understanding of the mechanical properties. This sense, two laminates were studied: the first is only reinforced by with seven layers short mats of fiberglass-E (CM) and the second where the reinforcement of fiberglass-E comes in the form of bidirectional fabric (CT), with only four layers. The laminate CT has the presence of anisotropy (sense of continuous fibers with respect to the applied load) as the main parameter influencing its mechanical behavior, behavior this, not observed for the CM. In addition to the mechanical properties was also studied the fracture characteristics developed in each composite laminated. The results also showed that the presence of the hole in the transversal section decreased the ultimate strength of laminates and changed the final characteristic of fracture in all kinds of composite laminated studied / A crescente demanda na utiliza??o de materiais comp?sitos torna imprescind?vel uma melhor compreens?o do seu comportamento frente ?s mais diversas condi??es de carga e servi?o, bem como sob as variadas formas de conex?es (fixa??es) envolvendo mecanismos nos projetos estruturais. Sabe-se que a maioria dos elementos estruturais ? projetada com presen?a de descontinuidades geom?tricas (furos, entalhes, ranhuras, etc) em suas se??es longitudinais e/ou transversais, e que essas descontinuidades alteram a resposta mec?nica desses elementos. Este trabalho tem como objetivo analisar um estudo da resposta mec?nica, quando em presen?a de descontinuidade geom?trica, de laminados comp?sitos de matriz polim?rica/fibras de vidro frente ao ensaio de tra??o uniaxial. A descontinuidade geom?trica ? caracterizada pela presen?a de um furo conc?ntrico na se??o transversal do comp?sito. Nesse estudo, diferentes tipos de configura??es s?o testados, com e sem a presen?a do furo, de forma a proporcionar melhor entendimento das propriedades mec?nicas. Neste sentido, dois laminados comp?sitos polim?ricos foram estudados: o primeiro ? unicamente refor?ado com sete camadas de mantas de fibras curtas de vidro-E (CM) e o segundo onde o refor?o de fibras de vidro-E vem na forma de tecido bidirecional (CT), com apenas quatro camadas. O laminado CT tem a presen?a da anisotropia (sentido das fibras cont?nuas com rela??o ? carga aplicada) como principal par?metro influenciando no comportamento mec?nico do mesmo, comportamento este, n?o observado para o CM. Al?m das propriedades mec?nicas, tamb?m foi estudado as caracter?sticas da fratura desenvolvidas em cada laminado comp?sito. Os resultados mostraram que, em um estudo comparativo, a presen?a do furo conc?ntrico na se??o transversal diminuiu a resist?ncia ?ltima dos laminados e alterou a caracter?stica final da fratura em todos os tipos de laminados comp?sitos estudados
|
15 |
Estudo das propriedades mec?nicas de biocomp?sitos de polipropileno refor?ados com fibras naturaisBispo, Sistanley Jones Lima 20 June 2011 (has links)
Made available in DSpace on 2014-12-17T14:58:07Z (GMT). No. of bitstreams: 1
SistanleyJLB_DISSERT.pdf: 3362424 bytes, checksum: 30d67bc0b13dba47c7002133ab1bb63d (MD5)
Previous issue date: 2011-06-20 / This research presents an approach to the addition of curau? fibers and licuri fibers in
a polypropylene resin matrix, such as an alternative proposal to reinforce the polymeric
composites. Fiber content of 0 %, 5 %, 10 %, and 20% were analyzed for verification of their
mechanical properties comparing them, inclusive with the properties of polypropylene. The
grainulated biocomposites had been prepared in an extrusora. The test bodies had been
molded by injection and submitted to the mechanical essays uniaxial traction, flexion on three
points, impact, in addition to thermal tests (HDT). These biocomposites had been also
subjected the essay physicist-chemistry index of fluidity (IF). It was observed that the
biocomposites of PP with 20% curau?, obtained bigger increase in the modulus of elasticity
and a bigger reduction in the resistance to the impact. In the mechanical behavior, for all the
biocomposites, these were increases in values of the limit of drainage and tension of rupture,
when tested by uniaxial traction, as they added the fibers. Another important point was the
increase of the resistance the flexion. It was also noted that the addition of fibers reduced the
thermal degradation of the mixture natural fibers / polypropylene. / Esta pesquisa apresenta uma abordagem da adi??o de fibras de licuri e curau? em uma
matriz de resina de polipropileno, essa como uma proposta alternativa de refor?o aos
comp?sitos polim?ricos. Teores de fibras de 0 %, 5 %, 10 %, e 20 % foram analisados para
verifica??o de suas propriedades mec?nicas comparando-as, inclusive com as propriedades do
polipropileno. Os biocomp?sitos granulados foram preparados em uma extrusora. Os corpos
de prova foram moldados por inje??o e submetidos aos ensaios mec?nicos de tra??o uniaxial,
flex?o em tr?s pontos, impacto, al?m de ensaios t?rmicos (HDT). Estes biocomp?sitos
tamb?m foram submetidos a ensaio f?sico-qu?mico de ?ndice de fluidez (IF). Observou-se que
os biocomp?sitos de PP com 20% curau? obteve maior aumento no m?dulo de elasticidade, e
uma maior diminui??o na resist?ncia ao impacto. No comportamento mec?nico, para todos os
biocomp?sitos, houve acr?scimos nos valores do limite de escoamento e tens?o de ruptura
quando ensaiados por tra??o uniaxial, ? medida que se adicionavam as fibras. Outro ponto
importante foi o aumento da resist?ncia ? flex?o. Verificou-se tamb?m que a adi??o de fibras
reduziu a degrada??o t?rmica da mistura fibras naturais / polipropileno.
|
16 |
Desenvolvimento e caracteriza??o de comp?sitos poli(tereftalato de etileno) reciclado (PET reciclado) com flocos de vidro.Moura, M?rcio Cleto Soares de 29 July 2011 (has links)
Made available in DSpace on 2014-12-17T14:07:07Z (GMT). No. of bitstreams: 1
MarcioCSM_TESE.pdf: 957118 bytes, checksum: 7c10d815ada900ecb0efde8936a6064e (MD5)
Previous issue date: 2011-07-29 / The growing concern with the solid residues management, observed in the last
decade, due to its huge amount and impact, has motivated the search for recycling
processes, where these residues can be reprocessed to generate new products,
enlarging the cycle of materials and energy which are present. Among the polymeric
residues, there is poly (ethylene terephthalate) (PET). PET is used in food
packaging, preferably in the bottling of carbonated beverages. The reintegration of
post-consumer PET in half can be considered a productive action mitigation of
environmental impacts caused by these wastes and it is done through the
preparation of several different products at the origin, i.e. food packaging, with
recycling rates increasing to each year. This work focused on the development and
characterization mechanical, thermal, thermo-mechanical, dynamic mechanical
thermal and morphology of the pure recycled PET and recycled PET composites with
glass flakes in the weight fraction of 5%, 10% and 20% processed in a single screw
extruder,
using the following analytical techniques: thermogravimetry (TG), differential
scanning calorimetry (DSC), tensile, Izod impact, Rockwell hardness, Vicat softening
temperature, melt flow rate, burn rate, dynamic mechanical thermal analysis (DMTA)
and scanning electron microscopy (SEM). The results of thermal analysis and
mechanical properties leading to a positive evaluation, because in the thermograms
the addition of glass flakes showed increasing behavior in the initial temperatures of
thermal decomposition and melting crystalline, Furthermore was observed growing
behavior in the mechanical performance of polymer composites, whose
morphological structure was observed by SEM, verifying a good distribution of glass
flakes, showing difference orientation in the center and in the surface layer of test
body of composites with 10 and 20% of glass flakes. The results of DMTA Tg values
of the composites obtained from the peak of tan ? showed little reductions due to
poor interfacial adhesion between PET and recycled glass flakes. / A crescente preocupa??o com a gest?o de res?duos s?lidos, observada na ?ltima
d?cada, em virtude de sua enorme quantidade e impacto ambiental, tem motivado a
busca por processos de reciclagem, onde estes res?duos podem ser reprocessados
de modo a gerarem novos produtos, ampliando o ciclo dos materiais e energia neles
contidos. Dentre os res?duos polim?ricos, destaca-se o poli(tereftalato de etileno)
(PET). O PET ? utilizado em embalagens de alimentos, preferencialmente, no
envase de bebidas carbonatadas. A reintegra??o do PET p?s-consumo ao meio
produtivo pode ser considerada uma a??o mitigat?ria dos impactos ambientais
causados por estes res?duos e j? ? realizada por meio da obten??o de diversos
produtos diferentes ao da origem, ou seja, embalagens para alimento, com taxas de
reciclagem crescente a cada ano. Este trabalho focou o desenvolvimento e a
caracteriza??o mec?nica, t?rmica, termo-mec?nica, termo-din?mico-mec?nica e
morfol?gica do PET reciclado processado e dos comp?sitos de PET reciclado com
flocos de vidro na fra??o em peso de 5%, 10% e 20% processados em uma
extrusora rosca simples, utilizando as seguintes t?cnicas de an?lise:
termogravimetria (TG), calorimetria explorat?ria diferencial (DSC), tra??o uniaxial,
impacto Izod, dureza Rockwel, temperatura de amolecimento Vicat, ?ndice de fluidez,
taxa de queima, an?lise termo-din?mico-mec?nica (DMTA) e microscopia eletr?nica
de varredura (MEV). Os resultados das an?lises t?rmicas e das propriedades
mec?nicas conduziram a uma avalia??o positiva, pois nos termogramas as adi??es
dos flocos de vidro mostraram comportamento crescente nas temperaturas inicial de
decomposi??o t?rmica e de fus?o cristalina, al?m disso, observou-se
comportamento crescente no desempenho mec?nico dos comp?sitos polim?ricos,
cuja estrutura morfol?gica foi observada por MEV, verificando uma boa distribui??o
dos flocos de vidro, apresentando diferen?a na orienta??o no centro e na camada
superficial do corpo de prova dos comp?sitos com 10 e 20% de flocos de vidro. Nos
resultados de DMTA os valores de Tg dos comp?sitos obtidos a partir do pico de tan
?, apresentaram pequenas redu??es, devido a pobre ades?o interfacial entre o PET
reciclado e os flocos de vidro.
|
17 |
Biocomp?sitos polim?ricos obtidos a partir da fra??o lignocelul?sica e amil?cea do caro?o de manga (mangifera indica), Tommy atkinsCordeiro, Edna Maria Silva 19 July 2013 (has links)
Made available in DSpace on 2014-12-17T14:07:16Z (GMT). No. of bitstreams: 1
EdnaMSC_DISSERT.pdf: 4754889 bytes, checksum: 7ba8ec4a5f3d11921ca74b85b2fe0b3b (MD5)
Previous issue date: 2013-07-19 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / This employment has the function the utilization of mango seeds Tommy Atkins, like starch source to obtain biopolymers and fibers source and nanowhiskers cellulose also, that will be use like reinforcing fillers in micro and nanobiocomposites polymeric. The fibers in natura removed from tegument mango seed were characterized, as weel as the treated fibers and nanowhiskers of cellulose extracted from them. The starch extracted from seed s almond showed a good performance (32%) and a high purity. The chemicals analyzes, of crystallinity and morphological of the fibers in natura, treated fibers and nanowhiskers of cellulose confirmed the efficacy of the chemical treatement performed to remove amorphous constituents (hemicellulose and lignina). The thermoplastic starch (TPS) obtained from two sources, corn starch and starchy material mango, was produced in a twin screw extruder with compositon mass of 62,5% of starch, 9,4% of water and 28,1% of glycerol. The starch material mango was the main objective of this work for the production of biodegradable materials, and the starch corn was utilized during the production stage to evaluate the processability of the starch and use as parameter for comparison, according of being a conventional source for obtaining conventional comercial starch. The incorporation of fibers (6% in mass) and nanowhiskers cellulose (1% in mass) in matrix of TPS to obtain composite and nanocomposite, respectively, it was performed in single screw extruder. The biocomposites and bionanocomposites polymeric were obtained and the TPS from starchy material mango presented better results of thermal and mechanicals properties when compared to TPS corn starch. Concludes that the sediment generated of the agroindustrial processing mango used presents potencial to producing of biodegradables materials / Este trabalho apresenta como objetivo a utiliza??o de caro?os da manga Tommy Atkins, como fonte de amido para obten??o de biopol?meros e, tamb?m, como fonte de fibras e nanowhiskers de celulose, que foram utilizadas como cargas refor?antes em micro e nanobiocomp?sitos polim?ricos. As fibras in natura removidas do tegumento do caro?o de manga foram caracterizadas, bem como as fibras tratadas e nanowhiskers de celulose extra?dos a partir delas. O amido extra?do das am?ndoas do caro?o apresentou um bom rendimento (32%) e elevado grau de pureza. As an?lises qu?micas, de cristalinidade e morfol?gicas das fibras in natura, fibras tratadas e nanowhiskers de celulose confirmaram a efic?cia do tratamento qu?mico realizado em remover os constituintes amorfos (hemicelulose e lignina). O amido termopl?stico (TPS) obtido de duas fontes, amido de milho e material amil?ceo de manga, foi produzido em extrusora rosca dupla com a composi??o em massa de 62,5% de amido, 9,4% de ?gua e 28,1% de glicerol. O material amil?ceo de manga foi o objetivo principal deste trabalho para produ??o de materiais biodegrad?veis, e o amido de milho foi utilizado durante a etapa de produ??o para avaliar a processabilidade do amido e utilizar como par?metro de compara??o, em fun??o de ser uma fonte convencional de obten??o de amido comercial. A incorpora??o das fibras (6% em massa) e nanowhiskers de celulose (1% em massa) em matriz de TPS para obter comp?sitos e nanocomp?sitos, respectivamente, foi realizada em extrusora monorosca. Os biocomp?sitos e bionanocomp?sitos polim?ricos foram obtidos e os TPS do material amil?ceo de manga apresentaram melhores resultados de propriedades t?rmicas e mec?nicas quando comparados aos TPS de amido de milho. Concluiu-se que os res?duos gerados do processamento agroindustrial da manga utilizados apresentaram potencial para a produ??o de materiais biodegrad?veis
|
18 |
Comp?sito Polim?rico H?brido: Comportamento Mec?nico, Descotinuidade Geom?trica e Resist?ncia ResidualFontes, Raphael Siqueira 12 April 2013 (has links)
Made available in DSpace on 2014-12-17T14:58:19Z (GMT). No. of bitstreams: 1
RaphaelSF_DISSERT.pdf: 3572126 bytes, checksum: c44c0bf716695541147f2e019fde49de (MD5)
Previous issue date: 2013-04-12 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / The growing demand in the use of hybrid composite materials makes it essential a better understanding of their behavior face of various design conditions, such as the presence of geometric discontinuities in the cross section of structural elements. This way, the purpose of this dissertation is a study of the mechanical response (strength and stiffness), modes (characteristics) of fracture and Residual Strength of an hybrid polymeric composite with and without a geometric discontinuity in its longitudinal section (with a reduction in the cross section) loaded by uniaxial tension. This geometric discontinuity is characterized by central holes of different diameters. The hybrid composite was fabricated as laminate (plate) and consisting of ortho-tereftalic polyester matrix reinforced by 04 outer layers of Jute fibers bidirectional fabrics and 01 central layer of E-glass bidirectional fabric. The laminate was industrially manufactured (Tecniplas Nordeste Ind?stria e Com?rcio Ltda.), obtained by the hand lay-up technique. Initially, a study of the volumetric density of the laminate was made in order to verify its use in lightweight structures. Also were performed comparative studies on the mechanical properties and fracture modes under the conditions of the specimens without the central hole and with the different holes. For evaluating the possible influence of the holes in the structural stability of the laminate, the Residual Strength of the composite was determined for each case of variation in hole diameter. As a complementary study, analyses of the macroscopic final fracture characteristic of the laminates were developed. The presence of the central hole of any sizes, negatively changed the ultimate tensile strength. Regarding the elastic modulus, moreover, the difference found between the specimens was within the range of tests displacement, showing the laminate stability related to the stiffness / A crescente demanda na utiliza??o dos materiais comp?sitos h?bridos torna imprescind?vel uma melhor compreens?o do seu comportamento frente ?s mais diversas condi??es de projeto, como a presen?a de descontinuidades geom?tricas nos elementos estruturais. Nesse sentido, a proposta desta disserta??o ? um estudo envolvendo a resposta mec?nica (resist?ncia e rigidez), os modos (caracter?sticas) da fratura e Resist?ncia Residual de um laminado comp?sito h?brido de matriz polim?rica com e sem presen?a de descontinuidade geom?trica em sua se??o longitudinal (com redu??o da se??o transversal), sob a a??o de tra??o uniaxial. Essa descontinuidade geom?trica ? caracterizada por furos centrais de diferentes di?metros. O laminado comp?sito h?brido foi confeccionado na forma de placa e composto por matriz poli?ster orto-tereft?lica refor?ada por 04 camadas externas de tecidos bidirecionais de fibras de juta e 01 camada central de tecidos bidirecionais de fibras de vidro-E. O laminado foi fabricado industrialmente (Tecniplas Nordeste Ind?stria e Com?rcio Ltda.), obtido atrav?s do processo de lamina??o manual (hand lay-up). Inicialmente, foi feito um estudo da densidade volum?trica do laminado, de modo a comprovar sua aplica??o em estruturas leves. Foram realizados estudos comparativos entre as propriedades mec?nicas nas condi??es dos corpos de prova sem o furo e com os diferentes di?metros do furo. Para a avalia??o de poss?vel influ?ncia da presen?a dos furos centrais na estabilidade estrutural do laminado, a Resist?ncia Residual foi determinada para cada caso de varia??o do di?metro do furo. Como estudo complementar, an?lises macrosc?picas da caracter?stica de fratura final dos laminados foram desenvolvidas. A presen?a do furo central, independente do di?metro, influiu de forma danosa, principalmente na resist?ncia ?ltima ? tra??o. Quanto ao m?dulo de elasticidade, por outro lado, a diferen?a encontrada entre os corpos de prova apresentou-se dentro da faixa da dispers?o dos ensaios, mostrando estabilidade com rela??o ? rigidez do laminado
|